WO2012063846A1 - アンモニア酸化・分解触媒 - Google Patents

アンモニア酸化・分解触媒 Download PDF

Info

Publication number
WO2012063846A1
WO2012063846A1 PCT/JP2011/075775 JP2011075775W WO2012063846A1 WO 2012063846 A1 WO2012063846 A1 WO 2012063846A1 JP 2011075775 W JP2011075775 W JP 2011075775W WO 2012063846 A1 WO2012063846 A1 WO 2012063846A1
Authority
WO
WIPO (PCT)
Prior art keywords
catalyst
temperature
group
ammonia
ammonia oxidation
Prior art date
Application number
PCT/JP2011/075775
Other languages
English (en)
French (fr)
Inventor
日数谷　進
匠磨 森
貞夫 荒木
Original Assignee
日立造船株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Family has litigation
First worldwide family litigation filed litigation Critical https://patents.darts-ip.com/?family=46050987&utm_source=google_patent&utm_medium=platform_link&utm_campaign=public_patent_search&patent=WO2012063846(A1) "Global patent litigation dataset” by Darts-ip is licensed under a Creative Commons Attribution 4.0 International License.
Application filed by 日立造船株式会社 filed Critical 日立造船株式会社
Priority to US13/883,302 priority Critical patent/US20130288890A1/en
Priority to CN201180053907.9A priority patent/CN103338862B/zh
Priority to EP11839746.2A priority patent/EP2638962A4/en
Publication of WO2012063846A1 publication Critical patent/WO2012063846A1/ja
Priority to US15/047,797 priority patent/US9896332B2/en

Abstract

触媒が常温起動性を有するようにするために必要な担体の還元温度を低減させることができ、かつ、常温よりも低い温度で起動性を持たせることができるような、アンモニア酸化・分解触媒を提供する。本発明のアンモニア酸化・分解触媒は、酸化セリウムと酸化ジルコニウムとの複合酸化物からなる触媒担体に、触媒活性金属として第６Ａ族、第７Ａ族、第８族、および第１Ｂ族からなる群から選ばれる少なくとも１種の金属を担持させたアンモニア酸化・分解触媒であって、前記触媒担体中の酸化ジルコニウムのモル濃度が１０～９０％であることを特徴とするものである。

Description

アンモニア酸化・分解触媒
　本発明は、燃料としてアンモニアを用いるアンモニアエンジンの助燃剤や燃料電池などで水素生成反応に供されるアンモニア酸化・分解触媒に関する。
　アンモニアを分解して水素を製造するためには、従来、ルテニウム系のアンモニア分解触媒の存在下に下記式(I)の反応を進行させる必要がある。
　ＮＨ３　⇔　３／２Ｈ２　＋　１／２Ｎ２　　　　　　　　　　・・・（I）
　　　　　　　　　　　　　　　　ΔＨ２９８Ｋ＝４６．１ｋＪ／ｍｏｌ
　式(I)の反応は、吸熱反応であるため、安定したアンモニア分解率を得るためには反応系に熱を与えて反応温度３５０℃以上にする必要がある。
　そこで、吸熱反応によるガス温度降下を抑制するために従来は外部から熱を供給していた。しかし、この方法では伝熱速度が反応速度より遅いため十分な伝熱速度を得るには伝熱面積を大きくせざるを得ず、装置のコンパクト化が難しい。
　外部からの熱供給の熱源としてエンジンなどの排ガスを利用する方法も考えられるが、この方法では熱源の温度が３５０℃以下である場合は触媒が作動する温度より低いため、熱供給を行うことができず、所定量の水素を製造することができないという難点がある。
　熱供給の熱源としては、外部からの供給以外に下記式(II)に示されるように、アンモニアと酸素との触媒反応により熱を発生させ、この熱を利用する方法がある。
　ＮＨ３　＋　３／４Ｏ２　⇔　１／２Ｎ２　＋　３／２Ｈ２Ｏ　・・・（II）
　　　　　　　　　　　　　　　　ΔＨ２９８Ｋ＝－３１５．１ｋＪ／ｍｏｌ
　式(I)と式(II)の反応を同一の反応管内で起こさせると式(I)の吸熱分を式(II)で発生する熱で補うことが可能となる。また、式(II)の酸素量を制御することで触媒層温度を制御することができる。例えば、エンジン排ガスの廃熱を熱交換して予熱された供給ガス温度が変動する場合において、安定して水素を製造することが可能となる。
　式（II）を進行させるために用いられるアンモニア酸化用触媒としては、通常、白金系触媒が用いられる。例えば特許文献１には、耐火性金属酸化物、この耐火性金属酸化物上に設けられた白金層、およびこの白金上に設けられたバナジア層を含んでなる多層化アンモニア酸化触媒が提案されている。
　しかし、この触媒の作動温度は２００℃程度であり、それ以下の温度では酸化反応を進行させることができず、電気ヒータ等でガス温度を２００℃程度まで上げる必要がある。
　特許文献２には、セリウム及びプラセオジムから選択される少なくとも１種の元素の酸化物と、イットリウムを含む原子価非可変性希土類元素から選択される少なくとも１種の元素の酸化物と、コバルトの酸化物を含むアンモニア酸化触媒が提案され、また特許文献３には、本質的に白金、ロジウム、随時パラジウムからなるフィラメントを含み、該フィラメントが白金コーティングを有するアンモニア酸化触媒が提案されているが、これらも特許文献１と同じ問題を有する。
特表2007-504945号公報 特許4165661号公報 特開昭63-72344号公報
　本願の発明者らは、酸化還元可能な金属酸化物からなる担体に触媒活性金属が担持されてなるアンモニア酸化・分解触媒を開発した。
　このアンモニア酸化・分解触媒によると、（i）常温でアンモニアおよび空気をこの触媒と接触させることにより、まず還元状態にある担体が酸素と反応して酸化熱が発生し、瞬時に触媒層温度が上昇し、触媒層温度がアンモニアと酸素とが反応する温度にまで達する；（ii）その後は発熱反応であるアンモニア酸化反応が自立的に進行し、発熱反応により生じた熱が、上述の式（I）に従って触媒活性金属の存在下にアンモニアを分解する過程で使われ、これにより水素が生成する。
　したがって、上記触媒を用いることにより、電気ヒータ等での予備加熱が不要となり、水素の製造コストを削減することができる。
　上記触媒では、担体を予め還元しておくことにより、常温で還元された状態の担体と酸素が接触した時に担体が酸素と反応して酸化熱が発生し、常温起動性を有することとなる。
　担体として単独のＣｅＯ２を用いた場合、常温起動性を有するようにするためには、６００℃以上もの高温で担体を還元する必要があった。
　また、上記触媒は常温起動性を有するものであるが、常温より低い温度では起動性を発現させることができなかった。そこで常温よりもさらに低い温度で起動させることができれば、上記触媒の適用範囲を広くすることができるので便宜である。
　本発明は、上記事情に鑑みてなされたものであり、触媒が常温起動性を有するようにするために必要な担体の還元温度を低減させることができ、かつ、常温よりも低い温度で起動性を持たせることができるような、アンモニア酸化・分解触媒を提供することを目的とする。
　上記課題を解決するため、本発明のアンモニア酸化・分解触媒は、酸化セリウムと酸化ジルコニウムとの複合酸化物からなる触媒担体に、触媒活性金属として第６Ａ族、第７Ａ族、第８族、および第１Ｂ族からなる群から選ばれる少なくとも１種の金属を担持させたアンモニア酸化・分解触媒であって、前記触媒担体中の酸化ジルコニウムのモル濃度が１０～９０％であることを特徴とする。
　好ましくは、上記アンモニア酸化・分解触媒はハニカム形状を有する。
　好ましくは、上記アンモニア酸化・分解触媒はペレットもしくはラッシヒリング状を有する。
　本発明のアンモニア酸化・分解触媒に用いられる酸化還元可能な触媒担体は、酸化セリウムと酸化ジルコニウムとの複合酸化物からなるものであり、この触媒担体中の酸化ジルコニウムのモル濃度は１０～９０％、より好ましくは２０～７０％である。
　触媒担体に担持される触媒活性金属は、好ましくは、Ｍｏ、Ｃｒ等の第６Ａ族、Ｍｎ等の第７Ａ族、Ｒｕ、Ｐｔ、Ｒｈ、Ｐｄ、Ｃｏ、Ｎｉ、Ｆｅ等の第８族、およびＣｕ、Ａｇ等の第１Ｂ族からなる群から選ばれる少なくとも１種の金属である。
　本発明によるアンモニア酸化・分解触媒は、水素気流中若しくはアンモニア気流中で２００～４００℃で加熱処理することにより、以下の反応により触媒担体を構成する金属酸化物の一部または全部が還元される。
　ＣｅＯ２＋ｘＨ２→ＣｅＯ２－ｘ＋ｘＨ２Ｏ　（０＜ｘ＜２）
　ＣｅＯ２＋２ｘ／３ＮＨ３→ＣｅＯ２－ｘ＋ｘＨ２Ｏ＋ｘ／３Ｎ２（０＜ｘ＜２）
　上記還元後の触媒がアンモニア酸化・分解反応に供される。アンモニア酸化・分解触媒の還元処理は、同触媒反応器に充填する前に行っても後に行ってもよい。
　触媒担体が還元された状態にあるアンモニア酸化・分解触媒は、常温若しくはそれ以下の温度である－１５～－３０℃の温度でアンモニアおよび空気と接触させると、まず、還元状態にある触媒担体が酸素と反応することによって酸化熱が発生し、瞬時に触媒層温度が上昇する。一旦、触媒層温度がアンモニアと酸素が反応する温度（２００℃）まで上昇すると、その後は自立的に上述した式（II）に従ってアンモニア酸化反応が進行する。この発熱反応（II）で生じた熱が、上述した式（I）に従って触媒活性金属の存在下にアンモニアを分解する過程で使われ、水素が生成する。
　本発明は、触媒活性金属として第６Ａ族、第７Ａ族、第８族、および第１Ｂ族からなる群から選ばれる少なくとも１種の金属を担持させたアンモニア酸化・分解触媒において、酸化セリウムと酸化ジルコニウムとの複合酸化物からなる触媒担体を用い、この触媒担体中の酸化ジルコニウムのモル濃度を１０～９０％とすることにより、触媒が常温起動性を有するようにするために必要な担体の還元温度を低減させることができ、かつ、常温よりも低い温度で起動性を持たせることができる。
低温時起動性試験を行った時の触媒層温度の経時変化を示すグラフである。 実施例１７の触媒を用いた場合の各気体の濃度の経時変化を示すグラフである。
　以下、本発明を具体的に説明するために、本発明の実施例およびこれとの比較を示すための比較例をいくつか挙げる。
　ａ）触媒担体
　触媒担体として、ＺｒＯ２のモル濃度が１０、２０、５０、８０％である４種の市販のＣｅＯ２－ＺｒＯ２（第一稀元素化学工業（株）製）を用いた。
　ｂ）触媒活性金属の担持
　上記の触媒担体に触媒活性金属を担持させた。触媒活性金属は、貴金属であるＲｕ、Ｐｔ、Ｒｈ、Ｐｔ－Ｒｈおよび卑金属であるＣｏ、Ｎｉ、Ｆｅ、Ｃｕ、Ｍｏ、Ｍｎを用いた。触媒担持量はすべて２重量％となるようにした。
　（ペレット形状の触媒の調製）
　上記各金属の触媒担体上への担持は、各金属の前駆体である各金属塩を純水に溶解させ、この溶液に、上記の触媒担体を、触媒活性金属の担持量が２重量％（金属として）になるように分散させた。
　この分散液を加熱し、水を緩やかに蒸発させた（蒸発乾固法）。
　得られた粉末状物を３００℃の空気中で３時間にわたって焼成した。
　焼成後の粉末状物を圧縮成型し、１～０．８５ｍｍに篩い分けして使用に供した。
　（ハニカム状触媒の調製）
　６００ｃｐｉのコーディエライト上にウォッシュコート法を用いて約２５０ｇ／Ｌの触媒担持量になるまで触媒活性金属を担持させた。
　比較例のための触媒担体として、市販のＣｅＯ２（第一稀元素化学工業（株）製）を用いた。この触媒担体にＲｕ、ＣｏおよびＮｉの各触媒活性金属を担持させた。触媒担持量は、２重量％となるようにした。
　ｃ）常温起動性試験
　（触媒の還元処理）
　得られた各ペレット状触媒１ｇまたはハニカム状触媒４ｍＬを流通型反応管に充填した後、水素気流中還元処理温度を１５０℃から８００℃までにわたって５０℃刻みとして処理した。還元処理時間は２時間とした。
　（常温起動性の確認）
　上記の反応管に充填された各温度で還元処理された触媒を、窒素雰囲気下、２５℃で保持し、その後、酸素（空気）とアンモニアを同時に触媒層に供給した。アンモニア供給量は２．５ＮＬ／分と一定にし、空気供給量は空気／アンモニアの体積比１．０とした。触媒層温度と出口ガス組成を、それぞれ、熱電対と質量分析計により計測した。
　上記の結果、触媒層の温度が上昇すること、水素の生成が認められること、および３０分間以上にわたって安定に水素が生成すること、の３つの要件を満たした触媒を、常温起動性を発現する触媒とし、そのような触媒について還元処理に要した温度を還元温度とした。
　各実施例および比較例の触媒の形状および組成および還元温度を以下の表１に示す。
Figure JPOXMLDOC01-appb-T000001
　上記表１から明らかなように、触媒担体がＣｅＯ２であった場合（比較例１～３）、常温起動性が発現するには還元温度は６００℃以上であることが必要であったのに対して、ＣｅＯ２にＺｒを１０ｍｏｌ％添加した場合（実施例１）には常温起動性を発現させるための還元温度は４００℃であり、比較例１に比べて還元温度を２００℃低減させることができた。
　アンモニアの酸化・分解が進行し触媒層温度が６００℃以上であれば反応が停止時にアンモニアを触媒層へ吹き込むだけで発熱反応である担体触媒の酸化反応が進行することにより触媒層温度が上昇し、再び常温起動性を有することが確認された。したがって、より温和な条件で再起動が可能となった。
　上記結果から、Ｚｒの添加は望ましくは２０～７０ｍｏｌ％であり、貴金属であるＲｕを触媒活性金属として用いた場合には２００℃の還元温度で常温起動性を発現し、卑金属であるＮｉやＣｏを触媒活性金属として用いた場合には、３００℃の還元温度で常温起動性を発現させることができた。
　ｄ）低温時の起動性試験
　（触媒の還元処理）
　得られた各ペレット状触媒１ｇまたはハニカム状触媒４ｍＬを流通型反応管に充填した後、水素気流中６００℃で２時間にわたって還元処理を行った。
　（低温起動性の確認）
　上記の反応管に充填された還元処理された触媒を、窒素雰囲気下に冷却し、所定の温度に達した後に、酸素（空気）とアンモニアを同時に供給した。アンモニア供給量は１ＮＬ／分と一定にし、空気供給量は空気／アンモニアの体積比１．０とした。触媒層の温度と触媒層出口における水素発生量を、それぞれ、熱電対と質量分析計により計測した。
　各実施例および比較例の触媒の形状および組成および還元温度を以下の表２に示す。
Figure JPOXMLDOC01-appb-T000002
　上記の低温時起動性試験を行った時の触媒層温度の経時変化について実施例１７の触媒（Ｒｕ／ＣｅＯ２－ＺｒＯ２（５０ｍｏｌ％））を用いた場合と比較例４の触媒（Ｒｕ（２ｗｔ％）／ＣｅＯ２）を用いた場合とを図１に示す。また、実施例１７の触媒を用いた場合の各気体の濃度の経時変化を図２に示す。
　図１から明らかなように、触媒担体がＣｅＯ２である比較例１では、初期触媒層温度が－１５℃では起動性は発現せず、アンモニアは発生しなかった。
　これに対して、実施例１５～３２では、ＣｅＯ２にＺｒＯ２を１０～９０ｍｏｌ％、望ましくは２０～７０ｍｏｌ％の割合で添加することにより、室温より低い温度であってもアンモニアの生成が見られ、起動性を発現することが分かった。
　特に、Ｐｔ、Ｒｈ、Ｐｔ－Ｒｈ合金などの貴金属、Ｃｏ、Ｆｅ、Ｎｉ、Ｃｕ、Ｍｏ、Ｍｎ等の卑金属などの種類を問わず、低温時の起動性を発現することができた。

Claims (3)

  1. 　酸化セリウムと酸化ジルコニウムとの複合酸化物からなる触媒担体に、触媒活性金属として第６Ａ族、第７Ａ族、第８族、および第１Ｂ族からなる群から選ばれる少なくとも１種の金属を担持させたアンモニア酸化・分解触媒であって、前記触媒担体中の酸化ジルコニウムのモル濃度が１０～９０％であることを特徴とするアンモニア酸化・分解触媒。
  2. 　ハニカム形状を有する、請求項１に記載のアンモニア酸化・分解触媒。
  3. 　ペレットもしくはラッシヒリング状を有する、請求項１に記載のアンモニア酸化・分解触媒。
PCT/JP2011/075775 2010-11-09 2011-11-09 アンモニア酸化・分解触媒 WO2012063846A1 (ja)