JP2005304877A - Skin sticking adhesive sheet - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To provide a skin sticking adhesive sheet having good skin touch, superior in manual cutting performance. <P>SOLUTION: The skin sticking adhesive sheet is composed of a base material of mixture fiber including pulp fiber free from thermal sticking fiber occurring at 150°C, having holes at predetermined intervals. The openings of the holes are blocked with chemical binders. The holes have preferably a diameter of 0.5mm-1.5mm. This chemical binder has a glass transition temperature of preferably 0-30°C. <P>COPYRIGHT: (C)2006,JPO&NCIPI

Description

  TECHNICAL FIELD The present invention relates to a pressure-sensitive adhesive sheet for skin application, and particularly relates to a pressure-sensitive adhesive sheet for skin application having hand cutting properties and good touch.

  A medical pressure-sensitive adhesive sheet generally has a structure in which a pressure-sensitive adhesive layer is formed on one side of a base material, and there are many pressure-sensitive adhesive sheets in which a nonwoven fabric is used as the base material. Thus, the adhesive sheet which a base material consists of a nonwoven fabric is economically cheap, and the thing excellent in characteristics, such as mechanical strength and adhesiveness, exists. However, there are many cases where the medical pressure-sensitive adhesive sheet is required to have a hand-cut property that can be cut by hand. Various reports have been made on pressure-sensitive adhesive sheets with improved hand-cutting properties.

  In JP-T-7-503290, pattern embossing is performed on a fibrous web in which stretchable non-destructive staple fibers and binder fibers are irregularly woven and knitted, and internally bonded uniformly by a chemical binder. Discloses a nonwoven sheet material that exhibits wet, dry strength, and excellent hand measurements, and can be easily torn with a finger in a direction perpendicular to the web direction. Japanese Patent Publication No. 9-502111 discloses a series of about 0.2-5 mm perforations divided by connecting segments of about 0.1-1 mm on an adhesive tape having a binder-containing nonwoven web as a support. It is disclosed that it can be easily torn by hand. Japanese Patent Laid-Open No. 2002-526667 proposes a laminated composite material in which a nonwoven fiber, a scrim in contact with a filament stretched vertically and horizontally, and a binder are combined. In JP-A-2002-360625, the support is a polyolefin nonwoven fabric, and a large number of through or non-penetrating micropores are formed, and the nonwoven fabric fibers around each micropore are melted to form a film. An adhesive tape for skin application is disclosed.

  In the pressure-sensitive adhesive tape provided with the above-mentioned hand cutting property, the cut surface is often cut in an irregular state when cut by hand. Ideally, a plastic film that has been perforated is cut linearly and the cut surface is clean, such as when a perforated process is cut. There is no adhesive tape to fill.

Japanese National Patent Publication No. 7-503290 Japanese National Patent Publication No. 9-502111 JP-T-2002-526667 JP 2002-360625 A

  The present invention has been made to solve the above-described problems, and an object of the present invention is to provide a pressure-sensitive adhesive sheet for skin application that is excellent in hand cutting properties and in touch.

The pressure-sensitive adhesive sheet for skin application of the present invention comprises a mixed fiber having a pulp fiber and a fiber that is not thermally fused at 150 ° C., and has pores at regular intervals. The opening is closed with a chemical binder.
Here, the holes preferably have a diameter of 0.5 mm to 1.5 mm.
The chemical binder preferably has a glass transition temperature of 0 ° C. or higher and 30 ° C. or lower.

In the present invention, in the adhesive sheet for skin application, the fiber that is not heat-sealed at 150 ° C. may be a polyester fiber.
The mixed fiber is preferably formed by a wet method.

  ADVANTAGE OF THE INVENTION According to this invention, the adhesive sheet for skin sticking which was excellent in hand cutting property and was balanced with the touch etc. can be provided.

BEST MODE FOR CARRYING OUT THE INVENTION

  The pressure-sensitive adhesive sheet for skin application of the present invention has a pressure-sensitive adhesive layer on at least one surface of a substrate. The base material is a non-woven fabric made of a mixed fiber having pulp fibers and fibers that are not thermally fused at 150 ° C. The nonwoven fabric is provided with pores, and a chemical binder and an adhesive layer are provided so as to close the pores.

The pulp fiber used in the present invention is not particularly limited, such as fiber length.
In the present invention, the fibers that are not heat-sealed at 150 ° C. are formed using a material having a high melting point that is not easily heat-sealed. The fiber that is not heat-sealed at 150 ° C. may be a chemical synthetic fiber or other fiber, and is not particularly limited. Specific examples include wood pulp, rug pulp, linter pulp, and linen pulp. For example, it is preferable to use a polyester fiber or the like from the viewpoint of easiness of procurement and stability.

  Although a nonwoven fabric is formed using the mixed fiber which has a pulp fiber and the fiber which is not heat-seal | fused at 150 degreeC, a general nonwoven fabric manufacturing method is employable, without being specifically limited. For example, a wet method, a dry method, a chemical bond method in which fiber webs are bonded with an adhesive, a thermal bond method in which self-adhesion or bonded fibers are bonded, a spun bond method, a melt blow method, a needle punch method, and the like can be employed. In the present invention, it is preferable to employ a wet method using water. Specifically, for example, pulp fibers and fibers that are not heat-sealed at 150 ° C. are uniformly dispersed in water, and this is poured onto a wire to form a sheet, followed by dehydration and drying to form a nonwoven fabric. it can.

The blending ratio of the pulp fiber and the fiber not thermally fused at 150 ° C. is preferably determined in consideration of mechanical strength, texture, and the like. For example, the blending ratio of the pulp fiber and the fiber not thermally fused at 150 ° C. is preferably in the range of pulp fiber / fiber not thermally fused at 150 ° C. = 40/60 to 80/20. . The basis weight of the whole nonwoven fabric ^is preferably ^{20g / m 2 ~60g / m 2} , in consideration of the texture and mechanical strength, it is particularly preferable basis weight is 25 to 50 g / ^{m 2.}

  Nonwoven fabrics formed using mixed fibers have pores at regular intervals. This hole may be a through hole or a concave recess, but is preferably a through hole. The shape of the holes may be a polygon such as a triangle, a quadrangle, or a hexagon, or a circle, a semicircle, an ellipse, or the like. Further, the length ratio of the holes in the vertical and horizontal directions can also be designed as appropriate. For example, the holes may be long rectangles or vertically long ellipses. The size of the holes in each shape is preferably designed as appropriate, but the diameter of the holes is preferably in the range of 0.5 mm to 1.5 mm. In the present invention, the “diameter” represents the longest length in the hole. For example, in the case of a quadrangular shape, the longer one of the diagonal lines is within a range of 0.5 mm to 1.5 mm. In the case of a circle, the diameter is preferably in the range of 0.5 mm to 1.5 mm. In the case of an ellipse, the major axis is in the range of 0.5 mm to 1.5 mm. It is preferable.

The hole pattern of the nonwoven fabric used for the adhesive tape for skin sticking of this invention is demonstrated concretely using drawing. (A) of FIG. 1 is a figure which shows the 1st aspect of the void | hole pattern of a nonwoven fabric, and arrange | positions so that a square may be arrange | positioned now in the row | line | column vertically and horizontally, and a corner may be located vertically and horizontally Has been. (B) of FIG. 1 is a diagram showing a second aspect of the pore pattern of the nonwoven fabric, and here is arranged in rows and columns so that the sides of the quadrangle are vertically and horizontally. (C) of FIG. 1 is a figure which shows the 3rd aspect of the void | hole pattern of a nonwoven fabric, and is arrange | positioned so that a semicircle may form a row | line | column in the width direction. (D) of FIG. 1 is a figure which shows the 4th aspect of the void | hole pattern of a nonwoven fabric, Here, the triangle is arrange | positioned so that it may form a row | line | column in the width direction, and one side of each triangle is located in 1 row. ing.
In addition, in (a) of FIG. 1-(d) of FIG. 1, although the aspect arrange | positioned in the state which the space | interval and the void | hole separated | separated was shown, the void | hole and the void | hole contacted It may be arranged in a state.

The pores are formed on the nonwoven fabric at regular intervals. For example, the pores and voids are arranged in at least one of the columns (flow direction and longitudinal direction of the nonwoven fabric) and rows (direction perpendicular to the flow direction and width direction). The distance between the holes is constant. The interval (pitch) between the non-cut portions between the holes in the row where hand cutting properties are required is preferably determined as appropriate depending on the shape, size, etc. of the holes. For example, FIG. ), When the square holes are arranged, the pitch (X or Y) of the rows requiring hand cutting properties is preferably in the range of about 0.25 mm to 1.25 mm. . In the present invention, the interval (pitch) between the non-cut portions between the holes is a portion indicated by X ₁ or Y ₁ in FIG. 1B, and is Y ₂ in FIG. a portion shown, a portion indicated by the the (d) Y ₃ FIG.

  In the present invention, a metal roll having a hole-shaped protrusion (a perforated roll) and a pressure roll (a metal roll having a smooth surface) are arranged to face each other, and a nonwoven fabric is placed between the contact surfaces of both rolls. By letting it pass, holes can be formed in the nonwoven fabric. The metal roll is provided with protrusions for forming holes at regular intervals and may have a sharp tip, for example, a square pyramid with a bottom surface or a circular cone with a bottom surface. The metal roll is preferably heated to about 120 ° C. to about 180 ° C., and the pressure roll is preferably heated to about 50 ° C. to about 150 ° C.

The pressure applied between the metal roll and the pressure roll (crimping force) and the speed at which the nonwoven fabric passes (flow velocity) are appropriate for the nonwoven fabric, taking into consideration the shape of the projection, the temperature of the projection, the thickness of the nonwoven fabric, etc. However, in general, the crimping force is preferably about 50 kg / cm to about 200 kg / cm at the linear pressure, and the speed of passing the nonwoven fabric is about 1 m. / Min to about 20 m / min.
As the pressure roll, a stainless steel roll having a smooth surface, a rubber roll having a smooth surface obtained by coating a core metal with silicone rubber, and the like can be used.

  In the formed holes, the opening side and the bottom side of the holes are closed with a chemical binder and an adhesive layer, etc., but the opening side of the holes is preferably closed with a chemical binder. As the chemical binder, a general chemical binder can be used, there is little chemical skin irritation, flexibility that does not give a sense of incongruity when in contact with the skin, and moisture permeability is possible. If it has, it can be used without being specifically limited. In the present invention, a chemical binder having a glass transition temperature (Tg) higher than 0 ° C. and lower than 30 ° C. is preferably used. When the glass transition temperature (Tg) is 0 ° C. or less, a sticky feeling is generated, handling becomes difficult, and production problems may occur. When the glass transition temperature (Tg) exceeds 30 ° C., the adhesive sheet May become stiff, and texture may worsen.

Examples of the chemical binder used include acrylic resin, vinyl acrylic resin, acetate / ethylene, and polyvinyl acetate. Also, latexes bonded with acrylic resins, styrene / butadiene rubber, vinyl acetate / ethylene, vinyl acetate / acrylates, polyvinyl chloride, polyvinyl alcohols, polyurethanes, vinyl acetates, acrylic / vinyl acetate, and similar Examples of water-based chemical binders include acrylic latex binders, styrene / butadiene rubber latex, acrylic / vinyl acetate copolymer latex, and the like.
For example, the pores can be closed by applying a water-based chemical binder to the nonwoven fabric using a wire wound rod, reverse roll, air knife, spray or the like.
The amount of the chemical binder used is preferably appropriately determined according to the desired properties, for example, mechanical strength (dry strength, wet strength), tear properties, etc., but generally about 3 g is preferably in the range of / ^{m 2} ~ about 30 g / ^{m 2,} and still more preferably in the range of about ^{5g / m 2 ~20g / m 2} .

  In the present invention, it is preferable to perform a back surface treatment after applying a chemical binder. By performing the back surface treatment, even when the pressure-sensitive adhesive sheet for skin application of the present invention is wound, that is, stored in the form of a scroll, it can be smoothly rewound. For example, the back treatment is preferably performed by applying a back treatment agent such as silicone or fluorine. The amount of the back surface treatment agent used is preferably determined as appropriate in consideration of the type of pressure-sensitive adhesive.

  The pressure-sensitive adhesive sheet for skin application of the present invention has a pressure-sensitive adhesive layer on one surface of a substrate. For example, an adhesive layer is provided on the surface opposite to the surface coated with the chemical binder of the nonwoven fabric. The pressure-sensitive adhesive layer is flexible enough to follow the skin, has little irritation to the skin (chemical irritation, physical irritation), and preferably has moisture permeability, and uses an adhesive that satisfies such requirements. It is preferable to be formed. As an adhesive, the adhesive generally used for the adhesive tape for skin sticking etc. can be used without being specifically limited. For example, synthetic rubber-based adhesives, polyurethane-based adhesives, polysiloxane-based adhesives, natural rubber-based adhesives, polyether-based adhesives, acrylic-based adhesives and the like mainly composed of a styrene-isobutylene-styrene copolymer One kind or a mixture of two or more kinds can be used.

  For the adhesive, water-soluble or water-absorbing resins such as plasticizers typified by polyhydric alcohols such as glycerin, polyethylene glycol, and polypropylene glycol, polyacrylic acid, cross-linked polyacrylic acid, and polyvinylpyrrolidone are used as necessary. Various additives such as rosin-based, terpene-based, petroleum-based tackifiers, various softeners, fillers, pigments and the like can be blended.

  The thickness of the pressure-sensitive adhesive layer is preferably 10 to 100 μm, and preferably 20 to 70 μm. When the thickness of the pressure-sensitive adhesive layer is less than 10 μm, sufficient adhesiveness may not be exhibited during sticking to the skin. On the other hand, if the thickness exceeds 80 μm, the water vapor permeability required for the adhesive sheet for skin application may not be obtained. May be expressed.

The pressure-sensitive adhesive layer may be provided directly on one side of the substrate, for example, the side opposite to the side to which the nonwoven fabric chemical binder is applied, or may be provided indirectly. Here, “indirect” does not directly contact the adhesive layer to the base material, for example, after applying a primer to the surface of the base material in order to improve anchorage with the adhesive layer, This refers to forming an adhesive layer.
Moreover, the adhesive layer may be provided in the whole surface of one side of a nonwoven fabric, and may be provided partially. When a pressure-sensitive adhesive layer is partially provided, it may be provided in a streak shape having a constant width or may be provided in a wavy shape. The pressure-sensitive adhesive layer may be a laminate of two or more layers. In this case, for example, one of the pressure-sensitive adhesive layers having different adhesive forces can be provided on the entire surface, and the other pressure-sensitive adhesive can be partially provided on the surface.
The pressure-sensitive adhesive layer may be formed by applying a pressure-sensitive adhesive in a solution, or by emulsion coating or hot-melt coating.

  In order to protect the adhesive layer, the adhesive sheet for skin application of the present invention may have a release sheet on the adhesive layer. As the release sheet, it is possible to use a release sheet that has been subjected to release treatment with silicone or the like on the side in contact with the pressure-sensitive adhesive layer. Or an adhesive sheet can also be made into a roll state. In this case, it is preferable to perform surface treatment on the surface to which the chemical binder is applied as described above.

  Since the adhesive sheet for skin application of the present invention has the above-described configuration, it can be torn by hand without using a cutting tool such as scissors, and the skin is less irritating and stuffy. Absent. Therefore, it is effective for medical use.

In the present invention, a medical tape or sheet such as a bandage can be formed using this adhesive sheet for skin application. For example, cut an adhesive sheet for skin application to an appropriate size to form a bandage, taping tape, etc., or a covering material covering the wound part, a post-surgical patch, a catheter needle insertion part, gauze, etc. Form medical tapes or sheets such as cover materials, or combine other supports with adhesive sheets for skin application to form medical products such as fixing tapes, bathing pouch fixing tapes, instrument holding tapes, etc. can do. Needless to say, the adhesive tape for skin application of the present invention can be used other than the medical application as long as it is applied to the skin.

  The present invention will be described more specifically with reference to the following examples. However, the present invention is not limited to these examples, and various applications are possible without departing from the technical idea of the present invention. In the following examples, “part” means “part by weight”, and “%” means “% by weight”. The measurement methods and evaluation methods used in the following examples are shown below.

<Measurement method and evaluation method>
(1) Hand cutting property The adhesive sheet for skin application was torn with a finger to a length of 25 mm in the flow direction and in a direction perpendicular to the flow direction (width direction). The tear direction was assumed to be an ideal cutting line, and the distance at which the cut edge of this cut surface was farthest from the ideal cutting line was determined. That is, for example, when tearing in the flow direction, the maximum length was measured among the lengths to the cutting edge of the adhesive sheet extending in the direction perpendicular to the flow direction. The shorter this length, the better the hand cutting ability. The said operation was performed 5 times and the average value was calculated | required.

(2) Touch The surface on the opposite side of the pressure-sensitive adhesive layer of the adhesive sheet for skin application, that is, the surface of the nonwoven fabric fixed with a chemical binder was touched by hand to examine whether or not there was a sticky feeling. Those with a sticky feeling are indicated by a symbol “×”, and those without a sticky feeling are indicated by a symbol “◯”.

(Example 1)
Pulp fibers and polyester fibers were mixed at a weight ratio of 60:40 to obtain mixed fibers. This mixed fiber was made into paper by a wet method to produce a nonwoven fabric. However, in order to add strength, 12 / m ^{2 of} acrylic resin was contained. The obtained nonwoven fabric had a basis weight of 35 g / m ² .

  Next, pores were formed in the produced nonwoven fabric. That is, a metal roll (square length is 1.0 mm and pitch (Y in FIG. 1) is 0.5 mm) provided with rectangular protrusions having vertical and horizontal corners as shown in FIG. 1 is set to 150 ° C. Then, the pressure roll having a smooth surface was set to 100 ° C., and the nonwoven fabric was passed between the metal roll and the pressure roll under pressure at a linear pressure of 180 kg / cm and a speed of 2.0 m / min. . Thereby, holes having a diameter of 0.8 mm were formed in the nonwoven fabric.

On the other hand, in a nitrogen gas atmosphere, a monomer mixture consisting of 95 parts of 2-ethylhexyl acrylate and 5 parts of acrylic acid was dissolved and mixed uniformly in 80 parts of ethyl acetate. To this, 0.2 part of benzoyl peroxide (BPO) was added as a polymerization initiator and a copolymerization reaction was carried out to obtain an acrylic copolymer.
For 100 parts of this acrylic copolymer, 67 parts of sorbitan trioleate and 0.14 part of a trifunctional isocyanate compound (manufactured by Nippon Polyurethane Industry Co., Ltd., Coronate HL) as a crosslinking agent are placed in an ethyl acetate solvent. Mixed and dissolved. The resulting solution was applied to the silicone-treated surface of a release paper having a silicone treatment on one side so that the thickness after drying was 50 μm, dried at 100 ° C. for 3 minutes, and then a crosslinked adhesive. A layer was formed.

Next, a chemical binder having a glass transition temperature (Tg) of 10 ° C. (trade name “Boncoat R3360N”, manufactured by Dainippon Ink & Chemicals, Inc.) is applied to the opening side surface of the formed nonwoven fabric pores. The hole was closed. Further, the pressure-sensitive adhesive layer formed was bonded to the other surface of the non-woven fabric, pressure-bonded, and then aged (aged) at 60 ° C. for 72 hours to prepare the pressure-sensitive adhesive sheet for skin application of the present invention.
The obtained adhesive sheet for skin application was measured and evaluated for hand tearability and touch. The results are shown in Table 1.

(Example 2)
In Example 1, holes (1.3 mm) were obtained in the same manner as in Example 1 except that the metal roll was changed to a metal roll having a diameter of 1.5 mm (diagonal length: 1.5 mm, pitch: 0.5 mm). A nonwoven fabric having a diameter) was produced. Moreover, the adhesive layer was formed like Example 1 using the obtained nonwoven fabric, and then the adhesive sheet for skin sticking was produced.
About the obtained adhesive sheet for skin sticking, the same measurement and evaluation as Example 1 were performed. The results are shown in Table 1.

(Example 3)
Using a metal roll having a diameter of 1.0 mm (diagonal length: 1.0 mm, pitch between holes: 0.5 mm), a nonwoven fabric having holes having a diameter of 0.8 mm was prepared in the same manner as in Example 1. . Next, the pores were closed in the same manner as in Example 1 using a chemical binder having a glass transition temperature of 30 ° C. (trade name “Dick Fine Q-500”, manufactured by Dainippon Ink & Chemicals, Inc.). A pressure-sensitive adhesive layer was formed on the other surface in the same manner as in Example 1 to prepare a pressure-sensitive adhesive sheet for skin application.
About the obtained adhesive sheet for skin sticking, the same measurement and evaluation as Example 1 were performed. The results are shown in Table 1.

(Comparative Example 1)
Using a metal roll having a diameter of 1.0 mm (diagonal length: 1.0 mm, pitch between holes: 0.5 mm), a nonwoven fabric having holes having a diameter of 0.8 mm was prepared in the same manner as in Example 1. . Moreover, the adhesive layer was formed and the adhesive sheet for skin sticking was produced like Example 1 except not performing a binder process using the obtained nonwoven fabric.
About the obtained adhesive sheet for skin sticking, the same measurement and evaluation as Example 1 were performed. The results are shown in Table 1.

(Comparative Example 2)
In Example 1, a polypropylene nonwoven fabric (trade name “P03025”, manufactured by Dainichi Kasei Co., Ltd.) was used in place of the nonwoven fabric composed of pulp fiber / polyester fiber. A nonwoven fabric having pores with a diameter of 0.8 mm was produced on this polypropylene nonwoven fabric in the same manner as in Example 1. Moreover, the adhesive layer was formed like Example 1 using the obtained nonwoven fabric, and then the adhesive sheet for skin sticking was produced.
About the obtained adhesive sheet for skin sticking, the same measurement and evaluation as Example 1 were performed. The results are shown in Table 1.

(Comparative Example 3)
A pressure-sensitive adhesive sheet for skin application was prepared in the same manner as in Example 1 except that pore formation was not performed with a metal roll.
About the obtained adhesive sheet for skin sticking, the same measurement and evaluation as Example 1 were performed. The results are shown in Table 1.

As is apparent from Table 1, the adhesive sheets for skin application of Examples 1 to 3 exhibited excellent hand cutting properties in both length and width, and the touch was also good. Also, these adhesive sheets for skin application hardly gave any physical or chemical irritation to the skin surface at the time of peeling.
On the other hand, it was found that the adhesive sheets for skin application of Comparative Examples 2 to 3 were both inferior in hand cutting properties because both the hand cutting properties in the vertical direction and the horizontal direction were 2.0 or more. Moreover, it turned out that the adhesive sheet for skin sticking of the comparative example 1 is inferior in evaluation of the touch.

  The pressure-sensitive adhesive sheet for skin application of the present invention can be used in the form of various sizes of sheets, tapes, etc., and can also be stored in a roll form. These adhesive sheets for skin application can be used in the fields of skin application, for example, medical hygiene field, external application, etc., and specifically, suitable for bandages, adhesive bandages, dressing materials, taping tapes, etc. used.

(A) is a figure which shows the 1st aspect of the void | hole pattern of the nonwoven fabric which concerns on this invention, (b) is a figure which shows the 2nd aspect of the void | hole pattern of the nonwoven fabric which concerns on this invention, (c (A) is a figure which shows the 3rd aspect of the void | hole pattern of the nonwoven fabric which concerns on this invention, (d) is a figure which shows the 1st aspect of the void | hole pattern of the nonwoven fabric which concerns on this invention.

Explanation of symbols

X, Y, X ₁ , Y ₁ , Y ₂ , Y ₃ Non-cut portion spacing (pitch)

Claims (5)

  The base material is a mixed fiber having pulp fibers and fibers that are not thermally fused at 150 ° C., and has pores at regular intervals, and the openings of the pores are blocked with a chemical binder. A pressure-sensitive adhesive sheet for application to skin.   The pressure-sensitive adhesive sheet for skin application according to claim 1, wherein the hole has a diameter of 0.5 mm to 1.5 mm.   The adhesive sheet for skin application according to claim 1 or 2, wherein the chemical binder has a glass transition temperature of 0 ° C or higher and 30 ° C or lower.   The pressure-sensitive adhesive sheet for skin application according to any one of claims 1 to 3, wherein the fiber not thermally fused at 150 ° C is a polyester fiber. The pressure-sensitive adhesive sheet for skin application according to claim 1 or 2, wherein the mixed fiber is formed by a wet method.

Images