WO2019230132A1 - 光造形用組成物セット - Google Patents

光造形用組成物セット Download PDF

Info

Publication number
WO2019230132A1
WO2019230132A1 PCT/JP2019/010942 JP2019010942W WO2019230132A1 WO 2019230132 A1 WO2019230132 A1 WO 2019230132A1 JP 2019010942 W JP2019010942 W JP 2019010942W WO 2019230132 A1 WO2019230132 A1 WO 2019230132A1
Authority
WO
WIPO (PCT)
Prior art keywords
composition
support material
mass
parts
model
Prior art date
Application number
PCT/JP2019/010942
Other languages
English (en)
French (fr)
Inventor
浩史 太田
圭介 奥城
Original Assignee
マクセルホールディングス株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by マクセルホールディングス株式会社 filed Critical マクセルホールディングス株式会社
Publication of WO2019230132A1 publication Critical patent/WO2019230132A1/ja

Abstract

本発明は、モデル材用組成物とサポート材用組成物とを含んでなるマテリアルジェット光造形法に使用される光造形用組成物セットであって、前記モデル材用組成物が、単官能モノマー（Ａ）と、分子内に炭素－炭素二重結合を含む重合性官能基を複数有する多官能モノマー（Ｂ）とを含んでなり、前記単官能モノマー（Ａ）と前記多官能モノマー（Ｂ）とのモル分率（単官能モノマー（Ａ）／多官能モノマー（Ｂ））が９９．９／０．１～９２／８であり、前記単官能モノマー（Ａ）として、分子量が１５０以上４００未満であり、かつ、ホモポリマーとしてのガラス転移温度が５℃以下である（メタ）アクリレート（Ａ１）を、前記単官能モノマー（Ａ）の全質量に対して８５質量％以上含有し、　前記サポート材用組成物が、該サポート材用組成物１００質量部に対して、１５質量部以上７５質量部以下の、オキシブチレン基を含み、かつ、重量平均分子量が３００以上であるポリアルキレングリコール（ａ）、１９質量部以上８０質量部以下の水溶性単官能エチレン性不飽和単量体（ｂ）、および、光重合開始剤を含有する、光造形用組成物セットに関する。

Description

光造形用組成物セット
　本発明は、マテリアルジェット光造形法に用いられるモデル材用組成物とサポート材用組成物を組み合わせた光造形用組成物セット、およびそれを用いた光造形物の製造方法に関する。
　ノズルから光硬化性樹脂組成物を吐出させ、その直後に紫外線等を照射して硬化させることにより、所定の形状を有する硬化層を形成するマテリアルジェット（インクジェット）方式による光造形法（以下、「マテリアルジェット光造形法」ともいう）が知られている。マテリアルジェット光造形法は、ＣＡＤ（Ｃｏｍｐｕｔｅｒ　Ａｉｄｅｄ　Ｄｅｓｉｇｎ）データに基づいて、自由に立体造形物を作成可能な３Ｄプリンタによって実現される造形法として、注目されている。
　マテリアルジェット光造形法は、液体状の光硬化性組成物に光を照射し、その照射部分を硬化させ、積層させることにより光造形物を得る従来の方法に比べて複雑な形状を造形しやすい。また、必要となる光硬化性組成物の量が少なく、複数のノズルから性質の異なる光硬化性組成物を同時に出射することで機械的特性を調整しやすい等のメリットもあるため、様々な試作用途に使用されている。
　近年、ゴム状材料を用いた試作用途に対する要望が高まっており、ゴムのような伸びと弾性を有し、かつ、経時的な寸法安定性にも優れた、マテリアルジェット光造形法に用いることができる種々のモデル材用組成物が提案されている（特許文献１～３）。
特開２０１５－７８２５５号公報 国際公開第２０１５／０５６６１４号 国際公開第２０１５／０４９８７３号
　モデル材用組成物は、通常、サポート材用組成物とともにマテリアルジェット光造形法に用いられる。近年、取扱性や環境的な観点から、水溶性のサポート材用組成物が開発されており、上記特許文献にも、該文献に記載されるモデル材用組成物を水溶性のサポート材用組成物と組み合わせて用い得ることが記載されている。しかしながら、上記特許文献において例示されるような従来広く知られているサポート材用組成物は、親水性の高いポリプロピレングリコール等の水溶性高分子を含んでおり、このようなサポート材用組成物に含まれる成分の種類や含有量によっては、得られるサポート材の自立性が劣ることから、そのようなサポート材用組成物を用いて造形された光造形品の寸法精度が低下するという問題があった。特に、ゴムのような伸びや弾性を有するモデル材用組成物から形成されるモデル材は寸法精度が低下しやすい傾向にあり、組み合わせるサポート材用組成物によって、その造形精度に大きな影響が及びやすい。
　そこで、本発明は、ゴムのような伸びと弾性を有するモデル材用組成物と、該モデル材用組成物に対する高いサポート力と優れた水除去性を併せ持つサポート材用組成物との組み合わせを提案し、ゴムのような伸びと弾性を有する光造形物を高い精度で造形し得る光造形用組成物セットを提供することを目的とする。
　本発明者等は、上記課題を解決するために鋭意検討した結果、本発明を完成するに至った。すなわち、本発明は、以下の好適な態様を提供するものである。
［１］モデル材用組成物とサポート材用組成物とを含んでなるマテリアルジェット光造形法に使用される光造形用組成物セットであって、
　前記モデル材用組成物が、単官能モノマー（Ａ）と、分子内に炭素－炭素二重結合を含む重合性官能基を複数有する多官能モノマー（Ｂ）とを含んでなり、前記単官能モノマー（Ａ）と前記多官能モノマー（Ｂ）とのモル分率（単官能モノマー（Ａ）／多官能モノマー（Ｂ））が９９．９／０．１～９２／８であり、
　前記単官能モノマー（Ａ）として、分子量が１５０以上４００未満であり、かつ、ホモポリマーとしてのガラス転移温度が５℃以下である（メタ）アクリレート（Ａ１）を、前記単官能モノマー（Ａ）の全質量に対して８５質量％以上含有し、
　前記サポート材用組成物が、該サポート材用組成物１００質量部に対して、
１５質量部以上７５質量部以下の、オキシブチレン基を含み、かつ、重量平均分子量が３００以上であるポリアルキレングリコール（ａ）、
１９質量部以上８０質量部以下の水溶性単官能エチレン性不飽和単量体（ｂ）、および、
光重合開始剤
を含有する、光造形用組成物セット。
［２］モデル材用組成物の硬化物のガラス転移温度は５℃以下である、前記［１］に記載の光造形用組成物セット。
［３］モデル材用組成物を構成する多官能モノマー（Ｂ）が有する重合性官能基は、アクリル基、メタクリル基、ビニルエーテル基およびアリルエーテル基からなる群から選択される、前記［１］または［２］に記載の光造形用組成物セット。
［４］モデル材用組成物は２種以上の前記（メタ）アクリレート（Ａ１）を含有する、前記［１］～［３］のいずれかに記載の光造形用組成物セット。
［５］モデル材用組成物は光重合開始剤をさらに含有する、前記［１］～［４］のいずれかに記載の光造形用組成物セット。
［６］モデル材用組成物の２５℃における粘度は１５０ｍＰａ・ｓ以下である、前記［１］～［５］のいずれかに記載の光造形用組成物セット。
［７］サポート材用組成物における光重合開始剤の含有量は、サポート材用組成物１００質量部に対して、１質量部以上１５質量部以下である、前記［１］～［６］のいずれかに記載の光造形用組成物セット。
［８］サポート材用組成物は、サポート材用組成物１００質量部に対して０．００５質量部以上３質量部以下の表面調整剤をさらに含有する、前記［１］～［７］のいずれかに記載の光造形用組成物セット。
［９］サポート材用組成物が水溶性有機溶剤を含有し、前記水溶性有機溶剤の含有量は、サポート材用組成物１００質量部に対して３０質量部以下である、前記［１］～［８］のいずれかに記載の光造形用組成物セット。
［１０］サポート材用組成物は保存安定化剤をさらに含有する、前記［１］～［９］のいずれかに記載の光造形用組成物セット。
［１１］マテリアルジェット光造形法により、前記［１］～［１０］のいずれかに記載の光造形用組成物セットに含まれるモデル材用組成物を光硬化させて得られるモデル材を含む、光造形物。
［１２］マテリアルジェット光造形法により、前記［１］～［１０］のいずれかに記載の光造形用組成物セットを用いて光造形物を製造する方法であって、
　モデル材用組成物を光硬化させてモデル材を得るとともに、サポート材用組成物を光硬化させてサポート材を得る工程（Ｉ）、および、
　前記サポート材を除去する工程（ＩＩ）
を有する、光造形物の製造方法。
　本発明によれば、ゴムのような伸びと弾性を有する光造形物を高い精度で造形し得る光造形用組成物セットを提供することができる。
本実施形態に係る光造形物の製造方法におけるモデル材用組成物及びサポート材用組成物を吐出してエネルギー線を照射している状態を示す模式側面図である。 本実施形態に係る光造形物の製造方法におけるモデル材用組成物及びサポート材用組成物を吐出している状態を示す模式側面図である。 本実施形態に係る光造形物の製造方法におけるモデル材用組成物及びサポート材用組成物にエネルギー線を照射している状態を示す模式側面図である。 サポート材とモデル材からなる光造形品前駆体（光造形物）の模式側面図である。 光造形品の模式側面図である。
　以下に、実施形態を挙げて本発明を説明するが、本発明は以下の実施形態に限定されるものではない。
　＜モデル材用組成物＞
　本発明の光造形用組成物セットは、モデル材用組成物を含む。本発明の光造形用組成物セットに含まれるモデル材用組成物は、単官能モノマー（Ａ）と、分子内に炭素－炭素二重結合を含む重合性官能基を複数有する多官能モノマー（Ｂ）とを含む。
　単官能モノマー（Ａ）は、紫外線等の活性エネルギー線の照射により重合して硬化する特性を有する成分であり、分子内に１つのラジカル重合性基を有する重合性化合物である。単官能モノマー（Ａ）が有するラジカル重合性基としては、（メタ）アクリル基、ビニルエーテル基、アリルエーテル基、スチレン基、（メタ）アクリルアミド基、アセチルビニル基、ビニルアミド基などのエチレン基およびアセチレン基等が挙げられる。なお、本発明において「（メタ）アクリレート」とは、アクリレートおよびメタクリレートの総称であり、アクリレートおよびメタクリレートの一方または両方を意味するものである。「（メタ）アクリロイル」、「（メタ）アクリル」等についても同様である。
　本発明において、モデル材用組成物は、単官能モノマー（Ａ）として、分子量が１５０以上４００未満であり、かつ、ホモポリマーとしてのガラス転移温度が５℃以下である（メタ）アクリレート（Ａ１）を含有する。モデル材用組成物が、（メタ）アクリレート（Ａ１）を含むことにより、該モデル材用組成物を硬化して得られるモデル材（光造形物）にゴムのような伸びと弾性を付与することができる。
　（メタ）アクリレート（Ａ１）は、ホモポリマーとした際に５℃以下のガラス転移温度を有する。ガラス転移温度が上記上限以下であることにより、モデル材用クリア組成物を光硬化して得られるモデル材にゴム状特性を付与することができる。（メタ）アクリレート（Ａ１）におけるガラス転移温度の下限は、特に限定されるものではないが、通常、－５５℃以上であり、好ましくは－５０℃以上である。
　上記分子量およびガラス転移温度を有する前記（メタ）アクリレート（Ａ１）の具体例としては、イソアミルアクリレート、ラウリル（メタ）アクリレート、オクチルアクリレート、イソオクチル（メタ）アクリレート、イソノニルアクリレート、デシルアクリレート、イソデシルアクリレート、トリデシル（メタ）アクリレート、イソミリスチルアクリレート、イソステアリルアクリレート、２－エチルヘキシルアクリレート、２－エチルヘキシル－ジグリコールアクリレート、４－ヒドロキシブチルアクリレート、メトキシジエチレングリコールアクリレート、メトキシトリエチレングリコールアクリレート、エトキシジエチレングリコールアクリレート、２－（２－エトキシエトキシ）エチルアクリレート、２－エチルヘキシルカルビトールアクリレート、フェノキシエチルアクリレート、フェノキシエトキシエチルアクリレート等が挙げられる。
　モデル材用組成物における前記（メタ）アクリレート（Ａ１）の含有量は、モデル材用組成物が含む単官能モノマー（Ａ）の全質量に対して８５質量％以上であり、好ましくは９０質量％以上である。（メタ）アクリレート（Ａ１）の含有量が８５質量％以上であると、得られるモデル材に十分なゴム状特性を付与しながら、寸法安定性を向上させることができる。本発明において、モデル材用組成物に含まれる（メタ）アクリレート（Ａ１）の含有量の上限は特に限定されず、単官能モノマー（Ａ）の全て（すなわち、全質量に対して１００質量％）が（メタ）アクリレート（Ａ１）であってもよいが、弾性を付与する観点から、例えば９８質量％以下であり、好ましくは９５％以下である。
　モデル材用組成物は、（メタ）アクリレート（Ａ１）を１種のみ含んでいてもよいが、硬化速度に幅が出て硬化収縮の原因となる応力緩和を促進することにより、寸法安定性の向上が期待できるため、２種以上の（メタ）アクリレート（Ａ１）を含むことが好ましい。
　本発明においてモデル材用組成物は、（メタ）アクリレート（Ａ１）以外の他の単官能モノマーを含んでいてもよい。そのような他の単官能モノマーとしては、前記（メタ）アクリレート（Ａ１）以外の（メタ）アクリレート（Ａ２）が挙げられ、例えば、メチル（メタ）アクリレート、エチルアクリレート、プロピルアクリレート、ブチルアクリレート、ペンチルアクリレート、ｎ－ステアリルアクリレート、シクロヘキシルアクリレート、ベンジルアクリレート、２－（メタ）アクリロイルオキシエチルヘキサヒドロフタル酸、ブトキシエチル（メタ）アクリレート、テトラヒドロフルフリル（メタ）アクリレート、イソボルニル（メタ）アクリレート、メトキシエチルアクリレート、２－ヒドロキシエチル（メタ）アクリレート、２－ヒドロキシプロピル（メタ）アクリレート、２－ヒドロキシブチル（メタ）アクリレート、２－ヒドロキシ－３－フェノキシプロピル（メタ）アクリレート、２－（メタ）アクリロイロキシエチルフタル酸、２－（メタ）アクリロイロキシエチル－２－ヒドロキシエチル－フタル酸、ｔ－ブチルシクロヘキシル（メタ）アクリレートなどが挙げられる。
　また、前記他の単官能モノマーは、ビニルエーテル基を有する単官能モノマー、アリルエーテル基を有する単官能モノマー、アセチルビニル基を有する単官能モノマー、（メタ）アクリルアミド基を有する単官能モノマー、ビニルアミド基を有する単官能モノマー、アセチレン基を有する単官能モノマーなどであってもよい。
　ビニルエーテル基を有する単官能モノマーとしては、例えば、ブチルビニルエーテル、ブチルプロペニルエーテル、ブチルブテニルエーテル、ヘキシルビニルエーテル、エチルヘキシルビニルエーテル、フェニルビニルエーテル、ベンジルビニルエーテル、エチルエトキシビニルエーテル、アセチルエトキシエトキシビニルエーテル、シクロヘキシルビニルエーテル、アダマンチルビニルエーテルなどが挙げられる。
　アリルエーテル基を有する単官能モノマーとしては、例えば、フェニルアリルエーテル、ｏ－，（ｍ－，ｐ－クレゾールモノアリルエーテル、ビフェニル－２－オールモノアリルエーテル、ビフェニル－４－オールモノアリルエーテル、ブチルアリルエーテル、シクロヘキシルアリルエーテル、シクロヘキサンメタノールモノアリルエーテル等が挙げられる。
　アセチルビニル基を有する単官能モノマーとしては、例えば、酢酸ビニルなどが挙げられる。（メタ）アクリルアミド基を有する単官能モノマーとしては、アクリルアミド、Ｎ，Ｎ－ジメチルアクリルアミド、Ｎ－イソプロピルアクリルアミド、メタクリルアミドなどが挙げられる。ビニルアミド基を有する単官能モノマーとしては、例えば、Ｎ－ビニル－ε－カプロラクタム、Ｎ－ビニルホルムアミド、Ｎ－ビニルピロリドンなどが含まれる。アセチレン基を有する単官能モノマーとしては、アセチレンなどが含まれる。
　多官能モノマー（Ｂ）は、紫外線等の活性エネルギー線の照射により重合して硬化する特性を有する成分であり、その分子内に炭素－炭素二重結合を含む重合性官能基を複数有する重合性モノマーである。多官能モノマー（Ｂ）が有する炭素－炭素二重結合を含む重合性官能基としては、（メタ）アクリル基、ビニルエーテル基、アリルエーテル基、スチレン基及び（メタ）アクリルアミド基などが挙げられる。中でも、光重合感度が良好となるため、多官能モノマー（Ｂ）はアクリル基、メタクリル基、ビニルエーテル基およびアリルエーテル基からなる群から選択される重合性官能基を含むことが好ましい。分子内にある複数の炭素－炭素二重結合を含む重合性官能基は、互いに同一であっても、異なっていてもよい。多官能モノマー（Ｂ）として、１種のみを単独で用いてもよく、複数種を組み合わせて用いてもよい。
　多官能（メタ）アクリレートとしては、例えば、
　トリエチレングリコールジ（メタ）アクリレート、テトラエチレングリコールジ（メタ）アクリレート、ポリエチレングリコールジ（メタ）アクリレート、トリプロピレングリコールジ（メタ）アクリレート、ポリプロピレングリコールジ（メタ）アクリレート、１，４－ブタンジオールジ（メタ）アクリレート、１，６－ヘキサンジオールジ（メタ）アクリレート、１，９－ノナンジオールジ（メタ）アクリレート、ネオペンチルグリコールジ（メタ）アクリレート、ジメチロール－トリシクロデカンジ（メタ）アクリレート、ビスフェノールＡのＰＯ付加物ジ（メタ）アクリレート、ヒドロキシピバリン酸ネオペンチルグリコールジ（メタ）アクリレート、ポリテトラメチレングリコールジ（メタ）アクリレート等の二官能モノマー；
　トリメチロールプロパントリ（メタ）アクリレート、ペンタエリスリトールトリ（メタ）アクリレート、ペンタエリスリトールテトラ（メタ）アクリレート、ジペンタエリスリトールヘキサ（メタ）アクリレート、ジトリメチロールプロパンテトラ（メタ）アクリレート、グリセリンプロポキシトリ（メタ）アクリレート、ペンタエリスリトールエトキシテトラ（メタ）アクリレート等の三官能以上の多官能モノマーなど
が挙げられる。
　（メタ）アクリレート化合物は、変性物であってもよい。変性物としては、例えば、エチレンオキサイド変性トリメチロールプロパントリ（メタ）アクリレート、エチレンオキサイド変性ペンタエリスリトールテトラアクリレート等のエチレンオキサイド変性（メタ）アクリレート化合物；カプロラクトン変性トリメチロールプロパントリ（メタ）アクリレート等のカプロラクトン変性（メタ）アクリレート化合物；およびカプロラクタム変性ジペンタエリスリトールヘキサ（メタ）アクリレート等のカプロラクタム変性（メタ）アクリレート化合物等が挙げられる。
　多官能ビニルエーテル化合物は、二官能、三官能、四官能またはそれ以上であってもよい。
　二官能ビニルエーテルとしては、例えば、エチレングリコールジビニルエーテル、ジエチレングリコールジビニルエーテル、トリエチレングリコールジビニルエーテル、プロピレングリコールジビニルエーテル、ジプロピレングリコールビニルエーテル、ブチレンジビニルエーテル、ジブチレングリコールジビニルエーテル、ネオペンチルグリコールジビニルエーテル、シクロヘキサンジオールジビニルエーテル、シクロヘキサンジメタノールジビニルエーテル、ノルボルニルジメタノールジビニルエーテル、イソバイニルジビニルエーテル、ジビニルレゾルシン、ジビニルハイドロキノンなどが挙げられる。
　三官能ビニルエーテルとしては、例えば、グリセリントリビニルエーテル、グリセリンエチレンオキシド付加物トリビニルエーテル（エチレンオキシドの付加モル数６）、トリメチロールプロパントリビニルエーテル、トリビニルエーテルエチレンオキシド付加物トリビニルエーテル（エチレンオキシドの付加モル数３）などが含まれる。四官能以上のビニルエーテルの例には、ペンタエリスリトールトリビニルエーテル、ジトリメチロールプロパンヘキサビニルエーテル、それらのオキシエチレン付加物などが挙げられる。
　多官能アリルエーテルは、二官能、三官能またはそれ以上であってもよい。
　二官能アリルエーテルとしては、例えば、１，４－シクロヘキサンジメタノールジアリルエーテル、アルキレン（炭素数２～５）グリコールジアリルエーテル、及びポリエチレングリコール（重量平均分子量：１００～４０００）ジアリルエーテルなどが挙げられる。また、グリセリンジアリルエーテル、トリメチロールプロパンジアリルエーテル、ペンタエリスリトールジアリルエーテル及びポリグリセリン（重合度２～５）ジアリルエーテルなどが挙げられる。
　三官能以上のアリルエーテルとしては、例えば、トリメチロールプロパントリアリルエーテル、グリセリントリアリルエーテル、ペンタエリスリトールテトラアリルエーテル及びテトラアリルオキシエタンなどが含まれる。また、ペンタエリスリトールトリアリルエーテル、ジグリセリントリアリルエーテル、ソルビトールトリアリルエーテルおよびポリグリセリン（重合度３～１３）ポリアリルエーテルなどが挙げられる。
　さらに、他の多官能モノマーとしては、例えば、フタル酸ジアリル、イソフタル酸ジアリル、ジビニルベンゼン、Ｎ，Ｎ－エチレンビスアクリルアミドなどが挙げられる。
　本発明において、モデル材用組成物に含まれる単官能モノマー（Ａ）と多官能モノマー（Ｂ）とのモル分率（単官能モノマー（Ａ）／多官能モノマー（Ｂ））が９９．９／０．１～９２／８となることが好ましい。単官能モノマー（Ａ）の含有量と、多官能モノマー（Ｂ）の含有量とのモル分率が上記範囲内であると、多官能モノマー（Ｂ）が架橋剤として機能し、線状ポリマー同士を適度に架橋することにより、得られるモデル材に高い伸びや弾性を付与することができる。本発明において、上記モル分率は、より好ましくは９９．５／０．５～９２／８である。
　本発明においては、特に、（メタ）アクリレート（Ａ１）をモデル材用組成物が含む単官能モノマー（Ａ）の全質量に対して８５質量％以上含有し、かつ、多官能モノマー（Ｂ）を単官能モノマー（Ａ）との関係で上記モル分率の範囲となるよう含有することで、得られるモデル材の伸び性（ゴム弾性）と寸法安定性とを両立させることができる。これは、限定されるわけではないが、例えば、その硬化物のガラス転移温度が低い単官能モノマーは、そのホモポリマーのガラス転移温度が高い単官能モノマーよりも、硬化反応中における粘度の増加速度は遅く、そのため、ホモポリマーとしてのガラス転移温度が低い単官能モノマーを含むモデル材用組成物を硬化させる際に、その硬化収縮を緩和するための時間が確保できる。硬化収縮を緩和する時間が確保できると、ゴム弾性と寸法安定性とを両立するモデル材が得られると考えられる。
　モデル材用組成物は、光重合開始剤をさらに含んでいてもよい。通常、活性光線が電子線である場合には光重合開始剤を含まなくてもよいが、活性光線が紫外線である場合には光重合開始剤を含むことが好ましい。
　光重合開始剤には、開裂型と水素引き抜き型とがある。本発明においてモデル材用組成物は、少なくとも開列型の光重合開始剤を含むことが好ましい。すなわち、モデル材用組成物は、（ｉ）開裂型と水素引き抜き型の両方の光重合開始剤を含有していてもよく、（ｉｉ）開裂型の光重合開始剤のみを含有していてもよい。所望の効果に応じて、光重合開始剤の態様を適宜使い分ければよい。
　モデル材用組成物が、（ｉ）開裂型と水素引き抜き型の両方の光重合開始剤を含有している場合には、開裂型の開始剤を質量比として多く含有していることが好ましい。光重合開始剤における水素引き抜き型開始剤の割合は、光重合開始剤の総質量に対して３０質量％以下であることが好ましく、２０質量％以上３０質量％以下であることがより好ましい。
　モデル材用組成物中に光重合開始剤として開裂型と水素引き抜き型の両方の種類の重合開始剤を含有していると、光造形用組成物の硬化速度が上昇する傾向にある。理由は明らかではないが、開裂型と水素引き抜き型の光重合開始剤が並存すると、水素引き抜き型開始剤が増感剤のような役割を果たすために重合速度が向上するものと考えられる。重合速度の向上は、通常の二次元の印刷（インクジェットプリント）に比べてはるかに長い時間を要する三次元立体を造形するマテリアルジェット光造形法において、より有利となる。
　モデル材用組成物が、（ｉｉ）開裂型の光重合開始剤のみを含有している（水素引き抜き型の開始剤を含有していない）場合には、開裂型と水素引き抜き型の両方の光重合開始剤を含有している場合と比較して、モデル材用組成物から形成されるモデル材の伸び性または弾性が向上することがある。この理由は明らかではないが、以下のように推察される。単官能モノマーの重合により得られる線状高分子間で、水素引き抜き型開始剤によってグラフト反応が発生すると不規則な架橋が起きることがある。架橋が規則的である場合には、硬化物を伸長させた際に均一に力を受けるため、高い伸縮性を維持することができるが、硬化物中に不規則な架橋がある場合、硬化物を伸長させた際に硬化物中の特定の部位に応力が集中する。このため、架橋部位または線状高分子鎖の破断が生じやすくなり、かえって伸び性や弾性が低下すると考えられる。
　したがって、三次元立体の光造形物の造形速度を向上させるためには、モデル材用組成物に（ｉ）開裂型と水素引き抜き型の両方の種類の重合開始剤を含有させることが好ましい。一方、硬化物の耐久性を重視する場合には、（ｉｉ）開裂型の光重合開始剤のみを含有させる（水素引き抜き型を実質的に含有させない）ことが好ましい。
　開裂型の光重合開始剤の例としては、ジエトキシアセトフェノン、２－ヒドロキシ－２－メチル－１－フェニルプロパン－１－オン、ベンジルジメチルケタール、１－（４－イソプロピルフェニル）－２－ヒドロキシ－２－メチルプロパン－１－オン、４－（２－ヒドロキシエトキシ）フェニル－（２－ヒドロキシ－２－プロピル）ケトン、１－ヒドロキシシクロヘキシル－フェニルケトン、２－メチル－２－モルホリノ（４－チオメチルフェニル）プロパン－１－オン、２－ベンジル－２－ジメチルアミノ－１－（４－モルホリノフェニル）－ブタノン等のアセトフェノン系；ベンゾイン、ベンゾインメチルエーテル、ベンゾインイソプロピルエーテル等のベンゾイン類；２，４，６－トリメチルベンゾインジフェニルホスフィンオキシド等のアシルホスフィンオキシド系；ベンジルおよびメチルフェニルグリオキシエステルなどが挙げられる。
　水素引き抜き型の光重合開始剤の例としては、ベンゾフェノン類（ベンゾフェノン、Ｎ，Ｎ－ジエチルベンゾフェノン、等）、チオキサントン類（２，４－ジエチルチオキサントン、イソプロピルチオキサントン、クロロチオキサントン、イソプロポキシクロロチオキサントン等）、アントラキノン類（エチルアントラキノン、ベンズアントラキノン、アミノアントラキノン、クロロアントラキノン等）、アクリジン類（９－フェニルアクリジン、１，７－ビス（９，９’－アクリジニル）ヘプタン等）等が挙げられる。
　モデル材用組成物における光重合開始剤の含有量は、モデル材用組成物を構成する重合性化合物の種類やその量、用いる開始剤の種類、活性光線の種類等に応じて適宜選択すればよいが、モデル材用組成物の総質量に対して、０．０１質量％～１０質量％であることが好ましい。
　モデル材用組成物は、本発明の効果を阻害しない範囲で、必要により、その他の添加剤を含有させることができる。その他の添加剤としては、例えば、光重合開始助剤、保存安定剤、表面調整剤、酸化防止剤、着色剤、紫外線吸収剤、光安定剤、連鎖移動剤、充填剤、希釈溶媒、増粘剤等が挙げられる。
　光重合開始助剤は、例えば、第３級アミン化合物であり、芳香族第３級アミン化合物が好ましい。芳香族第３級アミン化合物としては、例えば、Ｎ，Ｎ－ジメチルアニリン、Ｎ，Ｎ－ジエチルアニリン、Ｎ，Ｎ－ジメチル－ｐ－トルイジン、Ｎ，Ｎ－ジメチルアミノ－ｐ－安息香酸エチルエステル、Ｎ，Ｎ－ジメチルアミノ－ｐ－安息香酸イソアミルエチルエステル、Ｎ，Ｎ－ジヒドロキシエチルアニリン、トリエチルアミンおよびＮ，Ｎ－ジメチルヘキシルアミン等が挙げられる。中でも、Ｎ，Ｎ－ジメチルアミノ－ｐ－安息香酸エチルエステル、Ｎ，Ｎ－ジメチルアミノ－ｐ－安息香酸イソアミルエチルエステルが好ましい。これらの化合物は、１種のみを用いてもよく、２種以上を組み合わせて用いてもよい。
　表面調整剤は、モデル材用組成物の表面張力を適切な範囲に調整する成分であり、その種類は特に限定されない。モデル材用組成物の表面張力を適切な範囲にすることで、吐出性を安定化させることができるとともに、モデル材用組成物とサポート材用組成物との界面混じりを抑制することができる。その結果、寸法精度が良好な造形物を得ることができる。
　表面調整剤としては、例えば、シリコーン系化合物等が挙げられる。シリコーン系化合物としては、例えば、ポリジメチルシロキサン構造を有するシリコーン系化合物等が挙げられる。具体的には、ポリエーテル変性ポリジメチルシロキサン、ポリエステル変性ポリジメチルシロキサン、ポリアラルキル変性ポリジメチルシロキサン等が挙げられる。これらとして、商品名でＢＹＫ－３００、ＢＹＫ－３０２、ＢＹＫ－３０６、ＢＹＫ－３０７、ＢＹＫ－３１０、ＢＹＫ－３１５、ＢＹＫ－３２０、ＢＹＫ－３２２、ＢＹＫ－３２３、ＢＹＫ－３２５、ＢＹＫ－３３０、ＢＹＫ－３３１、ＢＹＫ－３３３、ＢＹＫ－３３７、ＢＹＫ－３４４、ＢＹＫ－３７０、ＢＹＫ－３７５、ＢＹＫ－３７７、ＢＹＫ－ＵＶ３５００、ＢＹＫ－ＵＶ３５１０、ＢＹＫ－ＵＶ３５７０（以上、ビックケミー社製）、ＴＥＧＯ－Ｒａｄ２１００、ＴＥＧＯ－Ｒａｄ２２００Ｎ、ＴＥＧＯ－Ｒａｄ２２５０、ＴＥＧＯ－Ｒａｄ２３００、ＴＥＧＯ－Ｒａｄ２５００、ＴＥＧＯ－Ｒａｄ２６００、ＴＥＧＯ－Ｒａｄ２７００（以上、デグサ社製）、グラノール１００、グラノール１１５、グラノール４００、グラノール４１０、グラノール４３５、グラノール４４０、グラノール４５０、Ｂ－１４８４、ポリフローＡＴＦ－２、ＫＬ－６００、ＵＣＲ－Ｌ７２、ＵＣＲ－Ｌ９３（共栄社化学社製）等を用いてもよい。また、シリコーン系化合物以外の表面調整剤（例えば、フッ素系表面調整剤等、ノニオン系表面調整剤）を用いてもよい。これらは単独で用いてもよいし、２種以上を併用してもよい。
　モデル材用組成物が表面調整剤を含有する場合、その含有量は、モデル材用組成物１００質量部に対して、好ましくは０．００５～３質量部であり、より好ましくは０．０１～１質量部である。表面調整剤の含有量が上記の範囲内である場合、モデル材用組成物の表面張力を適切な範囲に調整しやすい。
　保存安定剤は、モデル材用組成物の保存安定性を高めることができる成分である。また、熱エネルギーにより重合性化合物が重合することで生じるヘッド詰まりを防止することができる。保存安定剤としては、例えば、ヒンダードアミン系化合物（ＨＡＬＳ）、フェノール系酸化防止剤、リン系酸化防止剤、ニトロソアミン系化合物等が挙げられる。具体的には、ハイドロキノン、メトキノン、ベンゾキノン、ｐ－メトキシフェノール、ハイドロキノンモノメチルエーテル、ハイドロキノンモノブチルエーテル、ＴＥＭＰＯ、４－ヒドロキシ－ＴＥＭＰＯ、ＴＥＭＰＯＬ、クペロンＡｌ、ＩＲＧＡＳＴＡＢ　ＵＶ-１０、ＩＲＧＡＳＴＡＢ　ＵＶ-２２、ＦＩＲＳＴＣＵＲＥ　ＳＴ－１（ＡＬＢＥＭＡＲＬＥ社製）、ｔ－ブチルカテコール、ピロガロール、ＢＡＳＦ社製のＴＩＮＵＶＩＮ　１１１　ＦＤＬ、ＴＩＮＵＶＩＮ　１４４、ＴＩＮＵＶＩＮ　２９２、ＴＩＮＵＶＩＮ　ＸＰ４０、ＴＩＮＵＶＩＮ　ＸＰ６０、ＴＩＮＵＶＩＮ　４００等が挙げられる。これらは単独で用いてもよいし、２種以上を併用してもよい。
　モデル材用組成物が保存安定剤を含有する場合、上記効果を得やすい観点から、その含有量はモデル材用組成物１００質量部に対して、好ましくは０．０５～３質量部であり、より好ましくは０．１～２質量部である。
　本発明のモデル材用組成物の粘度は、マテリアルジェットノズルからの吐出性を良好にする観点から、２５℃において１５０ｍＰａ・ｓ以下であることが好ましい。上記粘度の測定は、ＪＩＳ　Ｚ　８８０３に準拠し、回転粘度計を用いて行うことができる。モデル材用組成物の粘度は、重合性化合物の種類およびその配合比率、希釈溶媒や増粘剤の種類およびその添加量等を調整することにより制御することができる。
　本発明のモデル材用組成物の硬化物のガラス転移温度（Ｔｇ）は、５℃以下であることが好ましい。モデル材用組成物の硬化物のガラス転移温度を５℃以下とすることで、低温下においても良好な弾性を維持することができる。モデル材用組成物の硬化物のガラス転移温度は、より好ましくは３℃以下である。ガラス転移温度は、例えば、示差熱分析（ＤＴＡ）または示差走査熱量測定（ＤＳＣ）により測定することができる。
　本発明のモデル材用組成物の製造方法は特に限定されず、例えば、混合攪拌装置、分散機等を用いて、モデル材用組成物を構成する成分を均一に混合することにより製造することができる。
　＜サポート材用組成物＞
　本発明の光造形用組成物セットは、サポート材用組成物を含む。本発明の光造形用組成物セットを構成するサポート材用組成物は、該サポート材用組成物１００質量部に対して、
　１５質量部以上７５質量部以下の、オキシブチレン基を含み、かつ、重量平均分子量が３００以上であるポリアルキレングリコール（ａ）、および、
　１９質量部以上８０質量部以下の水溶性単官能エチレン性不飽和単量体（ｂ）
を含有する組成物である。サポート材用組成物が、オキシブチレン基を含むポリアルキレングリコール（ａ）を上記含有量で含有していることにより、優れた水除去性とサポート力とを兼ね備えたサポート材を提供することができ、また、低温安定性に優れたサポート材組成物を提供することができる。上記オキシブチレン基を含むポリアルキレングリコール（ａ）は水溶性ではあるが、サポート材を形成した際にサポート材のサポート力を低下させるほどの親水性を有さない一方で、上記オキシブチレン基を含むポリアルキレングリコール（ａ）が水溶性であることにより、サポート材を形成した際のサポート材の水による除去性に優れている。ここで、水溶性とは、水に溶解し得るまたは水に分散し得る特性を意味する。また、上記サポート材用組成物は、低温時に凝固（固化）し難く、流動性が低下し難いため、低温安定性にも優れている。
　より具体的には、本発明においてサポート材用組成物は、上記オキシブチレン基を含むポリアルキレングリコール（ａ）と、水溶性単官能エチレン性不飽和単量体（ｂ）と、光重合開始剤とを含有している。これにより、優れた水除去性とサポート力とを兼ね備えたサポート材を実現可能で、かつ、低温安定性に優れたサポート材用組成物を提供することができる。
　サポート材用組成物に含まれ得るオキシブチレン基を含むポリアルキレングリコール（ａ）としては、直鎖型、多鎖型のいずれであってもよい。また、水に溶解するものであれば、末端にアルキル基を含んでいてもよく、例えば、好ましくは炭素数６以下のアルキル鎖を含んでいてもよい。これらは単独で用いてもよいし、２種以上を組み合わせて用いてもよい。
　オキシブチレン基を含むポリアルキレングリコール（ａ）は、サポート材に適度の親水性を付与するための水溶性樹脂であり、これを添加することによりに水除去性とサポート力とを兼ね備えたサポート材を得ることができる。上記オキシブチレン基を含むポリアルキレングリコールは、オキシブチレン基を含んでいれば、特にそのアルキレン部分の構造は限定されず、例えば、オキシブチレン基（オキシテトラメチレン基）のみ有するポリブチレングリコール単体であってもよく、また、オキシブチレン基と他のオキシアルキレン基とを共に有するポリブチレンポリオキシアルキレングリコール（例えば、ポリブチレンポリエチレングリコール）であってもよい。
　例えば、上記ポリブチレングリコールは、下記化学式（１）で示され、上記ポリブチレンポリエチレングリコールは、下記化学式（２）で示される。
Figure JPOXMLDOC01-appb-C000001
　上記化学式（２）において、ｍは５～３００の整数であることが好ましく、ｎは２～１５０の整数であることが好ましい。より好ましくは、ｍは６～２００、ｎは３～１００である。また、化学式（１）および化学式（２）中のオキシブチレン基は、直鎖であってもよいが、分岐していてもよい。これらは単独で用いてもよいし、２種以上を組み合わせて用いてもよい。
　サポート材用組成物が、オキシブチレン基を含むポリアルキレングリコール（ａ）を含むことにより、サポート材のサポート力を低下させずに水による除去性をより向上させることができ、ゴム状の伸びや弾性を有するモデル材を支持し、精度の高いモデル材を造形するのに適したサポート材となる。特に、ゴムのような伸びや弾性を有し、成形時に寸法精度が低下しやすいモデル材に対して、光造形中にサポート材がモデル材を十分に支えることができるため光造形の段階における造形精度を向上させることができる。さらに、その後、サポート材を除去する段階においてはサポート材の容易な除去が可能であるため、光造形中に高い精度で成形した立体モデルの微細構造においてもその精度の低下を抑えながらサポート材を除去することができる。これにより、サポート材の水による除去性を向上させることによりサポート材除去時における寸法精度の低下を抑制するだけでなく、サポート材の自立性を向上させることにより光造形中におけるモデル材の寸法精度を高めることで、より良好な寸法精度を有する光造形物を得ることができる。
　オキシブチレン基を含むポリアルキレングリコール（ａ）の重量平均分子量（Ｍｗ）は、３００以上である。前記ポリアルキレングリコール（ａ）の重量平均分子量が３００未満であると、サポート材用組成物を構成する成分との相溶性が低下し、ブリーディングが生じやすくなる。したがって、オキシブチレン基を含むポリアルキレングリコール（ａ）の重量平均分子量は、より好ましくは４００以上、さらに好ましくは５００以上である。また、オキシブチレン基を含むポリアルキレングリコール（ａ）の重量平均分子量の上限は特に限定されるものではないが、通常、３０００以下であり、好ましくは２０００以下である。重量平均分子量が上記範囲であると、硬化前の組成物中で水溶性単官能エチレン性不飽和単量体（ｂ）と相溶しやすくなる一方、光照射後の水溶性単官能エチレン性不飽和単量体の硬化物とは相溶し難くなり、サポート材の水または水溶性溶剤による除去が容易になる。
　上述したとおり、サポート材用組成物におけるオキシブチレン基を含むポリアルキレングリコール（ａ）の含有量は、サポート材用組成物１００質量部に対して、１５質量部以上７５質量部以下であり、好ましくは１７質量部以上であり、より好ましくは２０質量部以上であり、好ましくは７２質量部以下であり、より好ましくは７０質量部以下である。オキシブチレン基を含むポリアルキレングリコール（ａ）の含有量が、１５質量部未満であると、サポート材の親水性が低下するため、サポート材の水除去性が低下し、上記含有量が７５質量部を上回ると、重合性成分の水溶性単官能エチレン性不飽和単量体（ｂ）の添加量が低下し、サポート材が軟化して自立性が低下するため、サポート材のサポート力が低下する。
　本発明において、サポート材用組成物に含まれる水溶性単官能エチレン性不飽和単量体（ｂ）としては、例えば、炭素数５～１５の水酸基含有（メタ）アクリレート〔例えば、ヒドロキシエチル（メタ）アクリレート、ヒドロキシプロピル（メタ）アクリレート、４－ヒドロキシブチル(メタ)アクリレート等〕、数平均分子量（Ｍｎ）２００～１，０００の水酸基含有（メタ）アクリレート〔例えばポリエチレングリコールモノ（メタ）アクリレート、モノアルコキシ（炭素数１～４）ポリエチレングリコールモノ（メタ）アクリレート、ポリプロピレングリコールモノ（メタ）アクリレート、モノアルコキシ（炭素数１～４）ポリプロピレングリコールモノ（メタ）アクリレート、ＰＥＧ－ＰＰＧブロックポリマーのモノ（メタ）アクリレート等〕、（メタ）アクリルアミド誘導体〔例えば（メタ）アクリルアミド、Ｎ－メチル（メタ）アクリルアミド、Ｎ－エチル（メタ）アクリルアミド、Ｎ－プロピル（メタ）アクリルアミド、Ｎ－ブチル（メタ）アクリルアミド、Ｎ，Ｎ’－ジメチル（メタ）アクリルアミド、Ｎ，Ｎ’－ジエチル（メタ）アクリルアミド、Ｎ－ヒドロキシエチル（メタ）アクリルアミド、Ｎ－ヒドロキシプロピル（メタ）アクリルアミド、Ｎ－ヒドロキシブチル（メタ）アクリルアミド等〕、（メタ）アクリロイルモルホリン等が挙げられる。これらは単独で用いてもよいし、２種以上を併用してもよい。
　サポート材用組成物に含まれる水溶性単官能エチレン性不飽和単量体（ｂ）の含有量は、上記サポート材用組成物１００質量部に対して、１９質量部以上８０質量部以下であり、好ましくは２２質量部以上であり、より好ましくは２５質量部以上であり、好ましくは７６質量部以下であり、より好ましくは７３質量部以下である。水溶性単官能エチレン性不飽和単量体（ｂ）の含有量が上記範囲内であると、サポート材のサポート力を低下させることなく、水によるサポート材の除去性を向上させることができる。
　さらに、サポート材用組成物は、水溶性有機溶剤を含んでいてもよい。水溶性有機溶剤は、サポート材用組成物を光硬化させて得られるサポート材の水への溶解性を向上させる成分である。また、サポート材用組成物を低粘度に調整する機能も有する。
　水溶性有機溶剤としては、グリコール系溶剤を用いることが好ましく、具体的には、例えば、エチレングリコールモノアセテート、プロピレングリコールモノアセテート、ジエチレングリコールモノアセテート、ジプロピレングリコールモノアセテート、トリエチレングリコールモノアセテート、トリプロピレングリコールモノアセテート、テトラエチレングリコールモノアセテート、テトラプロピレングリコールモノアセテート、エチレングリコールジアセテート、プロピレングリコールジアセテートなどのグリコールエステル系溶剤；エチレングリコールモノメチルエーテル、プロピレングリコールモノメチルエーテル、トリエチレングリコールモノメチルエーテル、エチレングリコールモノエチルエーテル、プロピレングリコールモノエチルエーテル、エチレングリコールモノプロピルエーテル、プロピレングリコールモノプロピルエーテル、エチレングリコールモノブチルエーテル、プロピレングリコールモノブチルエーテル、テトラプロピレングリコールモノブチルエーテル、エチレングリコールジメチルエーテル、プロピレングリコールジメチルエーテル、エチレングリコールジエチルエーテル、プロピレングリコールジエチルエーテル、エチレングリコールジプロピルエーテル、プロピレングリコールジプロピルエーテル、エチレングリコールジブチルエーテル、プロピレングリコールジブチルエーテル、ジエチレングリコールジエチルエーテルなどのグリコールエーテル系溶剤；エチレングリコールモノメチルエーテルアセテート、プロピレングリコールモノメチルエーテルアセテート、ジプロピレングリコールモノメチルエーテルアセテート、エチレングリコールモノエチルエーテルアセテート、プロピレングリコールモノエチルエーテルアセテート、エチレングリコールモノプロピルエーテルアセテート、プロピレングリコールモノプロピルエーテルアセテート、エチレングリコールモノブチルエーテルアセテート、プロピレングリコールモノブチルエーテルアセテートなどのグリコールモノエーテルアセテート系溶剤等が挙げられる。これらは単独で用いてもよいし、２種以上を組み合わせて用いてもよい。
　中でも、低粘度のサポート材用組成物を調製しやすく、また、硬化して得られるサポート材が水溶解性に優れる点から、水溶性有機溶剤としては、トリエチレングリコールモノメチルエーテル、ジエチレングリコールジエチルエーテルおよびジプロピレングリコールモノメチルエーテルアセテートが好ましい。
　サポート材用組成物における水溶性有機溶剤の含有量は、サポート材用組成物１００質量部に対して、３０質量部以下であることが好ましく、より好ましくは２８質量部以下であり、さらに好ましくは２５質量部以下である。水溶性有機溶剤の含有量が、上記範囲内であると、サポート材のサポート力を低下させずにサポート材の水または水溶性溶媒による除去性を向上させることができる。サポート材用組成物が水溶性有機溶剤を含む場合、その含有量は、サポート材用組成物を低粘度に調整し得る観点から、サポート材用組成物１００質量部に対して、好ましくは３質量部以上である。
　光重合開始剤としては、モデル材用組成物に含有され得る光重合開始剤として上記に述べた化合物を同様に使用することができる。サポート材用組成物における光重合開始剤の含有量は、サポート材用組成物１００質量部に対して、好ましくは１質量部以上２０質量部以下であり、より好ましくは２質量部以上であり、また、より好ましくは１８質量部以下、さらに好ましくは１５質量部以下である。光重合開始剤の含有量が上記範囲内であると、未反応の重合成分を十分に低減させて、サポート材の硬化性を十分に高めやすい。
　上記各成分を上記範囲の含有量で含むことにより、優れた水溶解性とサポート力とを兼ね備えたサポート材用組成物を得ることができる。特に、サポート力に優れるため造形中に空気中の水分を取り込みサポート力が低下するという懸念がなく、寸法精度が良好な光造形品が得られる。
　上記サポート材用組成物には、必要により、その他の添加剤を含有させることができる。その他の添加剤としては、例えば、表面調整剤、酸化防止剤、着色剤、顔料分散剤、保存安定剤、紫外線吸収剤、光安定剤、連鎖移動剤、充填剤等が挙げられる。
　サポート材用組成物に、表面調整剤を配合することによりサポート材用組成物の表面張力を適当な範囲に制御することができ、モデル材用組成物とサポート材用組成物がその界面で混合することを抑制することができる。これにより、寸法精度の良好な光造形物を得ることができる。サポート材用組成物が含み得る表面調整剤としては、先のモデル材用組成物に用い得る表面調整剤として例示したものと同様のものを用いることができ、その含有量は、サポート材用組成物１００質量部に対して０．００５質量部以上３質量部以下であることが好ましい。
　また、サポート材用組成物に保存安定剤を配合することにより保存安定性を向上させることができる。サポート材用組成物が含み得る保存安定剤としては、先のモデル材用組成物に用い得る保存安定剤として例示したものと同様のものを用いることができ、その含有量は、サポート材組成物１００質量部に対して０．０５質量部以上３質量部以下であることが好ましい。
　本発明において、サポート材用組成物の粘度は、マテリアルジェットノズルからの吐出性を良好にする観点から、２５℃において３０～２００ｍＰａ・ｓであることが好ましく、より好ましくは３５ｍＰａ・ｓ以上、さらに好ましくは４０ｍＰａ・ｓ以上であり、より好ましくは１７０ｍＰａ・ｓ以下、さらに好ましくは１５０ｍＰａ・ｓ以下である。なお、上記粘度の測定は、ＪＩＳ　Ｚ　８８０３に準拠し、Ｒ１００型粘度計を用いて行うことができる。
　本発明において、サポート材用組成物の表面張力は、好ましくは２４～３０ｍＮ／ｍであり、より好ましくは２４．５～２９．５ｍＮ／ｍであり、さらに好ましくは２５～２９ｍＮ／ｍである。表面張力が上記範囲内であると、ノズルからの吐出液滴を正常に形成することができ、適切な液滴量や着弾精度を確保することやサテライトの発生を抑制することが可能であり、高い造形精度を確保しやすくなる。なお、サポート材用組成物の表面張力は、モデル材用組成物における表面張力の測定方法と同様の方法に従い測定することができる。
　本発明のサポート材用組成物の製造方法は特に限定されず、例えば、混合攪拌装置、分散機等を用いて、サポート材用組成物を構成する成分を均一に混合することにより製造することができる。
　＜光造形用組成物セット＞
　本発明の光造形用組成物セットは、サポート材が自立性および除去性に優れるために光造形物の寸法精度を損なわないので、高い伸びや弾性を有する立体造形物（モデル材）を優れた精度で造形し得る。
　＜光造形品およびその製造方法＞
　本発明の光造形物の製造方法は、本発明の光造形用組成物セットを用いた光造形物の製造方法であり、マテリアルジェット（インクジェット）方式プリンタを用いてモデル材用組成物およびサポート材用組成物を吐出した後、モデル材用組成物を光硬化させてモデル材を得るとともに、水溶性サポート材用組成物を光硬化させて水溶性サポート材を得る工程と、前記水溶性サポート材を水に接触させることにより除去する工程とを備えている。
　本発明の製造方法は、上記本発明の光造形用組成物セットを用いているため、高い造形精度でゴム状特性を有する光造形物を形成することができる。
　以下、本発明の光造形物の製造方法について図面に基づき説明する。図１は、マテリアルジェット造形法によりサポート材用組成物およびモデル材用組成物を吐出してエネルギー線を照射している状態を示す模式側面図である。図１において、三次元造形装置１０は、インクジェットヘッドモジュール１１と、造形テーブル１２とを備えている。また、インクジェットヘッドモジュール１１は、光造形用インクユニット１１ａと、ローラー１１ｂと、光源１１ｃとを備えている。さらに、光造形用インクユニット１１ａは、モデル材用組成物１３が充填されたモデル材用インクジェットヘッド１１ａＭと、サポート材用組成物１４が充填されたサポート材用インクジェットヘッド１１ａＳとを備えている。
　モデル材用インクジェットヘッド１１ａＭからは、モデル材用組成物１３が吐出され、サポート材用インクジェットヘッド１１ａＳからは、サポート材用組成物１４が吐出され、光源１１ｃからエネルギー線１５が照射され、吐出されたモデル材用組成物１３およびサポート材用組成物１４を硬化させて、モデル材１３ＰＭとサポート材１４ＰＳを形成している。図１では、一層目のモデル材１３ＰＭおよびサポート材１４ＰＳを形成する状態を示している。
　次に、本発明の光造形物の製造方法について図面に基づき更に詳細に説明する。本発明の光造形物の製造方法では、先ず、図２に示すように、インクジェットヘッドモジュール１１を造形テーブル１２に対してＸ方向（図２では右方向）に走査させる共に、モデル材用インクジェットヘッド１１ａＭからモデル材用組成物１３を吐出し、サポート材用インクジェットヘッド１１ａＳからサポート材用組成物１４を吐出する。これにより、造形テーブル１２の上に、モデル材前駆体１３Ｍからなる層とサポート材前駆体１４Ｓからなる層とを、それぞれの界面同士が接触するように隣接して配置する。
　次に、図３に示すように、インクジェットヘッドモジュール１１を造形テーブル１２に対して逆Ｘ方向（図３では左方向）に走査させると共に、ローラー１１ｂでモデル材前駆体１３Ｍおよびサポート材前駆体１４Ｓからなる層の表面を平滑にした後、光源１１ｃからエネルギー線１５を照射し、モデル材前駆体１３Ｍおよびサポート材前駆体１４Ｓからなる層を硬化させて、一層目のモデル材１３ＰＭおよびサポート材１４ＰＳからなる層を形成す
る。
　続いて、造形テーブル１２をＺ方向に一層分だけ下降させて、上記と同様の工程を行い、二層目のモデル材およびサポート材からなる層を形成する。その後、上記の工程を繰り返すことにより、図４に示すように、モデル材１３ＰＭとサポート材１４ＰＳからなる光造形品前駆体１６が形成される。
　最後に、図４に示した光造形品前駆体１６を水に接触させる、例えば、水に浸漬することによりサポート材１４ＰＳを溶解して除去し、図５に示すような光造形品１７が形成される。
　本発明の光造形物の製造方法において、光源として、例えば、高圧水銀灯、メタルハライドランプ、ＵＶ-ＬＥＤ等を使用できる。三次元造形装置１０の小型化が可能であり、消費電力が小さいという観点から、ＵＶ-ＬＥＤが好ましい。光量は、造形品の硬度および寸法精度の観点から、２００～５００ｍＪ/ｃｍ２が好ましい。光源としてＵＶ-ＬＥＤを用いる場合、光が深層まで届きやすくなり、光造形品の硬度および寸法精度を向上させることができることから、中心波長が３８５～４１５ｎｍのものを用いることが好ましい。また、光源１１ｃから照射するエネルギー線１５についは、紫外線、近紫外線、可視光線、赤外線、遠赤外線、電子線、α線、γ線およびエックス線等を使用することができるが、硬化作業の容易性及び効率性の観点から、紫外線又は近紫外線が好ましい。
　本発明の製造方法において、例えば、作製する物体の３次元ＣＡＤデータをもとに、マテリアルジェット方式で積層して立体造形物を構成するモデル材用組成物のデータ、および、作製途上の立体造形物を支持するサポート材用組成物のデータを作製し、さらにマテリアルジェット方式の３Ｄプリンタで各組成物を吐出するスライスデータを作製し、作製したスライスデータに基づきモデル材用およびサポート材用の各組成物を吐出後、光硬化処理を層ごとに繰り返し、モデル材用組成物の硬化物（モデル材）およびサポート材用組成物の硬化物（サポート材）からなる光造形物を作製することができる。
　立体造形物を構成する各層の厚みは、造形精度の観点からは薄いほうが好ましいが、造形速度とのバランスからは５～３０μｍが好ましい。
　得られた光造形物は、モデル材とサポート材とが組み合わされたものである。かかる光造形物からサポート材を除去してモデル材である光造形品を得る。サポート材の除去は、例えば、サポート材を溶解させる除去溶剤に得られた光造形物を浸漬し、サポート材を柔軟にした後、ブラシなどでモデル材表面からサポート材を除去して行うことが好ましい。サポート材の除去溶剤には水、水溶性溶剤、例えばグリコール系溶剤、アルコール系溶剤などを用いてもよい。これらは、単独で、あるいは複数用いてもよい。
　上記光造形品は、水に接触した場合の吸水及び膨潤が抑制されており、微細構造部分の破損及び変形を起こしにくいものである。また、上記光造形品は撥水撥油性に優れ、汚染されにくいものである。
　以上の工程により得られた光造形品は、ある実施形態においては、比較的高い表面硬度を有する。例えば、上記光造形品は、ショア－Ｄ硬度で５０以上、好ましくは６０以上、より好ましくは７０以上の表面硬度を有する。上記光造形品は、サポート材を除去する際に水に接触する時間が短時間で済むために吸水及び膨潤が抑制されており、寸法精度が高いものである。
　以下、本実施形態をより具体的に開示した実施例を示す。なお、本発明はこれらの実施例のみに限定されるものではない。
　以下、実施例により本発明をさらに詳細に説明する。例中の「％」及び「部」は、特記ない限り、質量％及び質量部である。
１．モデル材用組成物
　実施例において用いたモデル材用組成物を構成する成分の詳細を表１に示す。
　［表１］
Figure JPOXMLDOC01-appb-I000002
（１）モデル材用組成物の調製
　表２に示す配合で、各モデル材用組成物を構成する成分を、それぞれ、混合攪拌装置を用いて均一に混合し、実施例Ｍ１～Ｍ６並びに比較例ｍ１およびｍ２のモデル材用組成物を製造した。
　［表２］
Figure JPOXMLDOC01-appb-I000003
（２）モデル材用組成物の物性
　＜粘度の測定＞
　各モデル材用組成物の粘度は、回転粘度計を用いて測定した。結果を表２に示す。
（３）モデル材の特性
　ガラス板上に、縦１００ｍｍ、横２０ｍｍ、厚さ１ｍｍの額縁状のシリコンゴムにより枠を形成し、その枠の中に各モデル材用組成物を流し込み、メタルハライドランプにより積算光量６００ｍＪ／ｃｍ2の紫外線を照射して、モデル材を得た。得られたモデル材について下記特性を、測定、評価した。結果を表２に示す。
　＜ガラス転移温度（Ｔｇ）＞
　ガラス転移度はＤＳＣ（示差走査熱量測定）で測定した。
　＜ゴム特性＞
　室温で、引張速度５００ｍｍ／分で一定荷重をかけて破断強度および破断伸びを測定した。Ｘ軸を伸び（％）、Ｙ軸を破断強度（ＭＰａ）としたときに、曲線Ａ（４０％、６．８ＭＰａ）、（１００％、３ＭＰａ）、（３００％、１．１ＭＰａ）、曲線Ｂ（４０％、５．２ＭＰａ）、（１００％、２．２ＭＰａ）、（３００％、０．７５ＭＰａ）を結ぶ線を基準にして、以下の評価基準により評価した。
　評価基準：
　○：曲線Ａから原点の反対側
　△：曲線Ａと曲線Ｂの間
　×：曲線Ｂから原点の間
　＜寸法安定性＞
　硬化物の硬化直後の寸法と、７日後の寸法とを測定した。
　評価基準：
　○：寸法の差が１％未満
　△：寸法の差が１～３％未満
　×：寸法の差が３％以上
２．サポート材用組成物
　実施例において用いたサポート材用組成物を構成する成分の詳細を表３に示す。
　［表３］
Figure JPOXMLDOC01-appb-I000004
（１）サポート材用組成物の調製
　表４に示す配合で、各サポート材用組成物を構成する成分を、それぞれ、混合攪拌装置を用いて均一に混合し、実施例Ｓ１～Ｓ１３および比較例ｓ１のサポート材用組成物を製造した。
　［表４］
Figure JPOXMLDOC01-appb-I000005
（２）サポート材用組成物およびその硬化物の特性
　上記実施例Ｓ１～Ｓ１３および比較例ｓ１のサポート材用組成物について、下記に示す方法によって、サポート材用組成物の低温安定性、サポート材組成物を硬化したサポート材硬化物の高温高湿条件安定性（サポート力）および水除去性を評価した。
　＜サポート材用組成物の低温安定性＞
　低温でのサポート材用組成物の安定性について評価した。各サポート材用組成物をガラス瓶に入れ、そのサポート材用組成物入りガラス瓶を温度１０℃に設定した恒温槽中で２４時間保管した。その後、保管後のサポート材用組成物の状態を目視で確認して、下記基準でサポート材用組成物の低温安定性を評価した。
　サポート材用組成物が液体状を維持している場合：低温安定性Ａ（優良）
　サポート材用組成物が一部凝固（固化）している場合：低温安定性Ｂ（良）
　サポート材用組成物が凝固（固化）している場合：低温安定性Ｃ（不良）
　＜サポート材硬化物のサポート力＞
　ガラス板上に、縦３０ｍｍ、横３０ｍｍ、厚さ５ｍｍの額縁状のシリコンゴムにより枠を形成し、その枠の中に各サポート材組成物を流し込み、メタルハライドランプにより積算光量５００ｍＪ／ｃｍ2の紫外線を照射し、サポート材硬化物を作製した。続いて、上記硬化物をガラス製シャーレに入れ、その硬化物入りシャーレを温度４０℃、相対湿度９０％の恒温槽中に２時間放置した。その後、放置後の上記硬化物の状態を目視で確認して、下記基準でサポート材硬化物のサポート力を評価した。
　硬化物の表面に液体状物質の発生がなく、硬化物の軟化も確認されない場合：サポート力Ａ（優良）
　硬化物の表面に液体状物質がわずかに発生し、硬化物の軟化が若干確認された場合：サポート力Ｂ（良）
　硬化物の表面に液体状物質が発生し、硬化物の軟化が確認された場合：サポート力Ｃ（不良）
　＜サポート材硬化物の水除去性＞
　上記サポート材硬化物のサポート力の評価の場合と同様にして、サポート材硬化物を作製した。次に、上記硬化物を、５０ｍＬのイオン交換水を満たしたビーカーに入れ、水温を２５℃に維持しながら超音波洗浄機で処理し、上記硬化物が溶解するまでの時間を測定し、下記基準でサポート材硬化物の水除去性を評価した。
　硬化物が完全に溶解するまでの時間が１時間未満であった：水除去性Ａ（優良）
　硬化物が完全に溶解するまでの時間が１時間以上２時間未満であった：水除去性Ｂ（良）
　硬化物が完全に溶解するまでの時間が２時間以上であった：水除去性Ｃ（不良）
　上記結果を表５に示す。
　［表５］
Figure JPOXMLDOC01-appb-I000006
　実施例Ｓ１～Ｓ１３のサポート材用組成物は、全ての評価項目で満足できる結果（優良または良）を得たことが分かる。
３．光造形用組成物セット
　表６に示す通りに上記モデル材用組成物およびサポート材用組成物を組み合わせることにより、実施例１～３並びに比較例１および２を調製した。
　ガラス板（商品名「ＧＬＡＳＳ　ＰＬＡＴＥ」、アズワン社製、２００ｍｍ×２００ｍｍ×厚さ５ｍｍ）の上面四辺に厚さ１ｍｍのスペーサーを配し、１０ｃｍ×１０ｃｍの正方形に仕切った。該正方形内にサポート材用組成物を注型した後、照射手段として紫外線ＬＥＤ（ＮＣＣＵ００１Ｅ、日亜化学工業株式会社製）を用い、全照射光量が５００ｍＪ／ｃｍ２となるように紫外線を照射して硬化させ、サポート材を得た。
　次に、上記サポート材の上面四辺に厚さ１ｍｍのスペーサーを配し、１０ｃｍ×１０ｃｍの正方形に仕切った。該正方形内にモデル材用組成物を注型した後、照射手段として紫外線ＬＥＤ（ＮＣＣＵ００１Ｅ、日亜化学工業株式会社製）を用い、全照射光量が５００ｍＪ／ｃｍ２となるように紫外線を照射して硬化させ、モデル材を得た。
　＜密着性の評価＞
　この状態で３０℃の恒温槽に１２時間放置し、モデル材とサポート材との密着性の様子を目視にて確認し、下記の基準において評価した。結果を表９に示す。
○：モデル材とサポート材とは密着していた。
△：モデル材とサポート材とは密着していたが、モデル材とサポート材との界面を爪でひっかくと剥がれが生じた。
×：モデル材とサポート材との界面で剥がれが生じ、モデル材の硬化収縮でモデル材が反るように剥がれた。
　　［表６］
Figure JPOXMLDOC01-appb-I000007
　表６の結果から分かるように、本発明の要件を満たす実施例１～３の光造形用組成物のセットは、モデル材とサポート材との界面に剥がれが生じず、モデル材とサポート材とがより密着していた。このように、モデル材とサポート材とが密着していれば、寸法精度が良好な光造形品が得られる。
　１０　三次元造形装置
　１１　インクジェットヘッドモジュール
　１１ａ　光造形用インクユニット
　１１ａＭ　モデル材用インクジェットヘッド
　１１ａＳ　サポート材用インクジェットヘッド
　１１ｂ　ローラー
　１１ｃ　光源
　１２　造形テーブル
　１３　モデル材用組成物
　１３Ｍ　モデル材前駆体
　１３ＰＭ　モデル材
　１４　サポート材用組成物
　１４Ｓ　サポート材前駆体
　１４ＰＳ　サポート材
　１５　エネルギー線
　１６　光造形品前駆体（光造形物）
　１７　光造形品

Claims (12)

  1. 　モデル材用組成物とサポート材用組成物とを含んでなるマテリアルジェット光造形法に使用される光造形用組成物セットであって、
    　前記モデル材用組成物が、単官能モノマー（Ａ）と、分子内に炭素－炭素二重結合を含む重合性官能基を複数有する多官能モノマー（Ｂ）とを含んでなり、前記単官能モノマー（Ａ）と前記多官能モノマー（Ｂ）とのモル分率（単官能モノマー（Ａ）／多官能モノマー（Ｂ））が９９．９／０．１～９２／８であり、
    　前記単官能モノマー（Ａ）として、分子量が１５０以上４００未満であり、かつ、ホモポリマーとしてのガラス転移温度が５℃以下である（メタ）アクリレート（Ａ１）を、前記単官能モノマー（Ａ）の全質量に対して８５質量％以上含有し、
    　前記サポート材用組成物が、該サポート材用組成物１００質量部に対して、
    １５質量部以上７５質量部以下の、オキシブチレン基を含み、かつ、重量平均分子量が３００以上であるポリアルキレングリコール（ａ）、
    １９質量部以上８０質量部以下の水溶性単官能エチレン性不飽和単量体（ｂ）、および、
    光重合開始剤
    を含有する、光造形用組成物セット。
  2. 　モデル材用組成物の硬化物のガラス転移温度は５℃以下である、請求項１に記載の光造形用組成物セット。
  3. 　モデル材用組成物を構成する多官能モノマー（Ｂ）が有する重合性官能基は、アクリル基、メタクリル基、ビニルエーテル基およびアリルエーテル基からなる群から選択される、請求項１または２に記載の光造形用組成物セット。
  4. 　モデル材用組成物は２種以上の前記（メタ）アクリレート（Ａ１）を含有する、請求項１～３のいずれかに記載の光造形用組成物セット。
  5. 　モデル材用組成物は光重合開始剤をさらに含有する、請求項１～４のいずれかに記載の光造形用組成物セット。
  6. 　モデル材用組成物の２５℃における粘度は１５０ｍＰａ・ｓ以下である、請求項１～５のいずれかに記載の光造形用組成物セット。
  7. 　サポート材用組成物における光重合開始剤の含有量は、サポート材用組成物１００質量部に対して、１質量部以上１５質量部以下である、請求項１～６のいずれかに記載の光造形用組成物セット。
  8. 　サポート材用組成物は、サポート材用組成物１００質量部に対して０．００５質量部以上３質量部以下の表面調整剤をさらに含有する、請求項１～７のいずれかに記載の光造形用組成物セット。
  9. 　サポート材用組成物が水溶性有機溶剤を含有し、前記水溶性有機溶剤の含有量は、サポート材用組成物１００質量部に対して３０質量部以下である、請求項１～８のいずれかに記載の光造形用組成物セット。
  10. 　サポート材用組成物は保存安定化剤をさらに含有する、請求項１～９のいずれかに記載の光造形用組成物セット。
  11. 　マテリアルジェット光造形法により、請求項１～１０のいずれかに記載の光造形用組成物セットに含まれるモデル材用組成物を光硬化させて得られるモデル材を含む、光造形物。
  12. 　マテリアルジェット光造形法により、請求項１～１０のいずれかに記載の光造形用組成物セットを用いて光造形物を製造する方法であって、
    　モデル材用組成物を光硬化させてモデル材を得るとともに、サポート材用組成物を光硬化させてサポート材を得る工程（Ｉ）、および、
    　前記サポート材を除去する工程（ＩＩ）
    を有する、光造形物の製造方法。
PCT/JP2019/010942 2018-05-29 2019-03-15 光造形用組成物セット WO2019230132A1 (ja)