WO2012081429A1 - 擬ポリロタキサンの製造方法 - Google Patents

擬ポリロタキサンの製造方法 Download PDF

Info

Publication number
WO2012081429A1
WO2012081429A1 PCT/JP2011/078015 JP2011078015W WO2012081429A1 WO 2012081429 A1 WO2012081429 A1 WO 2012081429A1 JP 2011078015 W JP2011078015 W JP 2011078015W WO 2012081429 A1 WO2012081429 A1 WO 2012081429A1
Authority
WO
WIPO (PCT)
Prior art keywords
pseudopolyrotaxane
aqueous dispersion
producing
cyclodextrin
drying
Prior art date
Application number
PCT/JP2011/078015
Other languages
English (en)
French (fr)
Inventor
山崎　智朗
慎哉 岡崎
宏紀 岡崎
茂生 濱本
長明 趙
Original Assignee
住友精化株式会社
アドバンスト・ソフトマテリアルズ株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 住友精化株式会社, アドバンスト・ソフトマテリアルズ株式会社 filed Critical 住友精化株式会社
Priority to CA2821887A priority Critical patent/CA2821887C/en
Priority to ES11848923.6T priority patent/ES2552210T3/es
Priority to KR1020137018129A priority patent/KR101817379B1/ko
Priority to JP2012548734A priority patent/JP6013189B2/ja
Priority to US13/994,515 priority patent/US9938382B2/en
Priority to CN201180059389.1A priority patent/CN103249743B/zh
Priority to EP11848923.6A priority patent/EP2653481B1/en
Publication of WO2012081429A1 publication Critical patent/WO2012081429A1/ja

Abstract

本発明は、高い包接率を有する粉末状擬ポリロタキサンを工業的に有利な方法で製造することができる擬ポリロタキサンの製造方法を提供することを目的とする。 本発明は、ポリエチレングリコールとシクロデキストリンとを水性媒体中で混合し、シクロデキストリン分子の開口部に前記ポリエチレングリコールが串刺し状に包接された擬ポリロタキサン粒子を含有する水性分散体を得る包接工程と、前記包接工程で得られた擬ポリロタキサン水性分散体を乾燥して擬ポリロタキサンを得る乾燥工程とを有する擬ポリロタキサンの製造方法であって、前記乾燥工程において、擬ポリロタキサン水性分散体を噴霧し、加熱した気流中で乾燥することを特徴とする擬ポリロタキサンの製造方法である。

Description

擬ポリロタキサンの製造方法
本発明は、擬ポリロタキサンの製造方法に関する。
架橋ポリロタキサンは、擬ポリロタキサンの両末端に封鎖基を導入したポリロタキサンを複数架橋することで得られる。例えば、擬ポリロタキサンが、ポリエチレングリコール（以下、「ＰＥＧ」ともいう）と該ＰＥＧを包接するシクロデキストリンとからなる場合、得られる架橋ポリロタキサンは、ＰＥＧの直鎖分子上に串刺し状に貫通されているシクロデキストリンが、当該直鎖分子に沿って移動可能（滑車効果）なために、張力が加わっても滑車効果によりその張力を均一に分散させることができる。そのため、架橋ポリロタキサンは、クラックや傷が生じにくいなど、従来の架橋ポリマーにない優れた特性を有する。
架橋ポリロタキサンの製造に用いられる擬ポリロタキサンは、通常、ＰＥＧとシクロデキストリンとを水性媒体中で混合することにより生成するため、水性分散体として得られる。効率よく、しかも化学的に安定な結合により擬ポリロタキサンの両末端に封鎖基を導入してポリロタキサンを得るには、ＰＥＧの両末端を－ＣＯＯＨ基とし、封鎖基を該－ＣＯＯＨ基と反応する基、例えば－ＮＨ２基、－ＯＨ基などとして反応させることが有効である。
しかしながら、このような擬ポリロタキサンの両末端に封鎖基を導入する反応においては系内の水分が反応を失活させるため、反応を効率よく進行させるには、反応系中に水が存在しないかまたは水分量を極めて微量に制御する必要があり、擬ポリロタキサンの水性分散体を遠心分離、濾過などにより固液分離した後、または水性分散体をそのまま乾燥し、充分に水を除去する必要があった。
特許文献１には、ＰＥＧ／α－シクロデキストリン包接化合物（擬ポリロタキサン）の沈殿を水中に懸濁し、７０℃以上の温度に加熱すると、包接力が弱まりシクロデキストリンが遊離することが開示されている。そのため、擬ポリロタキサンの水分散体を７０℃以上の温度で乾燥させることは、包接率の低下を招く可能性があった。包接率が低下すると、架橋ポリロタキサンの滑車効果が損なわれ、所望の特性が得られなくなるため、従来、擬ポリロタキサン水性分散体の乾燥には、主に凍結乾燥法や７０℃以下での減圧乾燥が行われてきた。
例えば、特許文献２には、擬ポリロタキサン水性分散体をアセトンの中で沈殿させ、ろ別した後、室温で真空乾燥する方法が開示されている。しかしながら、アセトンによる媒体置換とろ別では擬ポリロタキサン中の水を充分に除去することができないため、室温下での乾燥では水分が残留し、擬ポリロタキサンの両末端に封鎖基を導入する反応を阻害するという問題があった。
さらに、凍結乾燥法や７０℃以下での減圧乾燥といった従来公知の乾燥方法では、得られた擬ポリロタキサンが塊状となるため、両末端に封鎖基を導入する反応の前に、粉砕、分級などにより粉末状にする必要があり、工程が煩雑となるという問題があった。
特開平３－２３７１０３号公報 特開２００５－２７２６６４号公報
従来公知の乾燥方法では分散媒である水の沸点以下での乾燥となるため、非常に長い乾燥時間を要するだけでなく、凍結乾燥方式においては大きな設備コスト、ランニングコストが掛かる。
また、７０℃以下の乾燥温度であっても含水状態で長時間加熱するとシクロデキストリンが遊離してしまうという問題があった。
さらに、乾燥後に粉砕、分級などの煩雑な工程を要さず、粉末状の擬ポリロタキサンが得られる乾燥方法が望まれていた。
本発明の目的は、上記の課題を解決し、高い包接率を有する粉末状擬ポリロタキサンを工業的に有利な方法で製造することができる擬ポリロタキサンの製造方法を提供することにある。
本発明は、ＰＥＧとシクロデキストリンとを水性媒体中で混合し、シクロデキストリン分子の開口部に前記ＰＥＧが串刺し状に包接された擬ポリロタキサン粒子を含有する水性分散体を得る包接工程と、前記包接工程で得られた擬ポリロタキサン水性分散体を乾燥して擬ポリロタキサンを得る乾燥工程とを有する擬ポリロタキサンの製造方法であって、前記乾燥工程において、擬ポリロタキサン水性分散体を噴霧し、加熱した気流中で乾燥する擬ポリロタキサンの製造方法である。
以下に本発明を詳述する。
本発明者らは、乾燥工程において、擬ポリロタキサン水性分散体を噴霧し、加熱した気流中で乾燥する方法を用いれば、高い包接率を有する粉末状擬ポリロタキサンを工業的に有利な方法で製造することができることを見出し、本発明を完成させるに至った。
本発明の擬ポリロタキサンの製造方法は、ＰＥＧとシクロデキストリンとを水性媒体中で混合し、シクロデキストリン分子の開口部に前記ＰＥＧが串刺し状に包接された擬ポリロタキサン粒子を含有する水性分散体を得る包接工程を有する。
前記ＰＥＧの重量平均分子量は１０００～５０万であることが好ましく、１万～３０万であることがより好ましく、１万～１０万であることがさらに好ましい。前記ＰＥＧの重量平均分子量が１０００未満であると、得られる架橋ポリロタキサンが特性の低いものとなることがある。前記ＰＥＧの重量平均分子量が５０万を超えると、擬ポリロタキサン水性分散体の流動性が低く、乾燥工程において噴霧できない場合がある。
なお、本明細書において、前記重量平均分子量は、ゲルパーミエーションクロマトグラフィー（ＧＰＣ）で測定を行い、ポリエチレングリコール換算により求められる値である。ＧＰＣによってポリエチレングリコール換算による重量平均分子量を測定する際のカラムとしては、例えば、ＴＳＫｇｅｌ　ＳｕｐｅｒＡＷＭ－Ｈ（東ソー社製）等が挙げられる。
前記ＰＥＧは、好ましくは、両末端に反応性基を有する。前記ＰＥＧの両末端は、従来公知の方法により反応性基を導入することが出来る。
前記ＰＥＧの両末端に有する反応性基は、採用する封鎖基の種類により適宜変更することができ、特に限定されないが、水酸基、アミノ基、カルボキシル基、チオール基などが挙げられ、とりわけ、カルボキシル基が好ましい。前記ＰＥＧの両末端にカルボキシル基を導入する方法としては、例えば、ＴＥＭＰＯ（２，２，６，６－テトラメチル－１－ピペリジニルオキシラジカル）と次亜塩素酸ナトリウムとを用いてＰＥＧの両末端を酸化させる方法等が挙げられる。
前記包接工程において、ＰＥＧとシクロデキストリンとの重量比は１：２～１：５であることが好ましく、１：２．５～１：４．５であることがより好ましく、１：３～１：４であることがさらに好ましい。シクロデキストリンの重量がＰＥＧの重量の２倍未満であると、ＰＥＧを包接するシクロデキストリンの個数（包接量）が低下する場合がある。シクロデキストリンの重量がＰＥＧの重量の５倍を超えても、包接量は増加せず経済的でない。
前記シクロデキストリンとしては、例えば、α－シクロデキストリン、β－シクロデキストリン、γ－シクロデキストリン、およびこれらの誘導体などが挙げられる。とりわけ、包接性の観点より、α－シクロデキストリンが好ましい。これらのシクロデキストリンは、１種を単独で使用してもよいし、２種以上を組み合わせて使用してもよい。
前記水性媒体としては、例えば、水、水とＤＭＦ、ＤＭＳＯなどの水性有機溶媒との水性混合物などが挙げられ、とりわけ水が好ましく用いられる。
包接工程におけるＰＥＧとシクロデキストリンとの混合条件としては、両者を前記水性媒体中に添加して混合すればよいが、ＰＥＧとシクロデキストリンとを水性媒体に溶解させることが好ましい。具体的には、通常５０～１００℃、好ましくは６０～９０℃、より好ましくは７０～８０℃に加熱、溶解することによりほぼ透明な混合溶液を得ることが出来る。
ＰＥＧとシクロデキストリンとの混合溶液を冷却することにより、ＰＥＧとシクロデキストリンからなる擬ポリロタキサン粒子が析出し、概ね白色状の擬ポリロタキサン水性分散体が得られる。
前記混合溶液を冷却する際に、混合溶液を流動させながら連続的または断続的に冷却し、擬ポリロタキサン粒子を析出させることにより、流動性がよく、経時的に流動性が低下しない擬ポリロタキサン水性分散体を得ることができるため、乾燥工程において擬ポリロタキサン水性分散体を容易に噴霧することが出来る。
なお、前記混合溶液を冷却する際に、静置下で冷却して擬ポリロタキサン粒子を析出させた場合には、極めて流動性の低いペースト状やクリーム状、または流動性のないゲル状の擬ポリロタキサン水性分散体が得られる。ペースト状やクリーム状で得られた擬ポリロタキサン水性分散体であっても経時的に流動性を失うため、乾燥工程において噴霧する前に適当な条件下で攪拌、混合するなどにより、流動性を付与しておくことが好ましい。
前記混合溶液を冷却する際、冷却後の到達温度は、０～３０℃であることが好ましく、１～２０℃であることがより好ましく、１～１５℃であることがさらに好ましい。０℃未満まで冷却した場合、凍結などにより得られる擬ポリロタキサン水性分散体の流動性が低下することがある。３０℃を超える場合、擬ポリロタキサン粒子が充分に析出しないことがある。
前記混合溶液を冷却する際の冷却速度は、０．０１～３０℃／分であることが好ましく、０．０５～２０℃／分であることがより好ましく、０．０５～１０℃／分であることがさらに好ましい。前記混合溶液を冷却する際の冷却速度が０．０１℃／分未満であると、析出する擬ポリロタキサン粒子が微細となりすぎるため、得られる擬ポリロタキサン水性分散体の流動性が低下する場合がある。前記混合溶液を冷却する際の冷却速度が３０℃／分を超えると、擬ポリロタキサン粒子が大きくなるため分散安定性が低下し、沈降分離する場合がある。
上述したように、擬ポリロタキサン粒子をより完全に析出させるため、断続的に冷却することも可能であり、また、冷却の過程で冷却速度や前記混合溶液の流動状態を変化させることも可能である。
前記混合溶液を冷却し、所望の温度に到達した後、得られた擬ポリロタキサン水性分散体の流動状態を保持する時間は、通常数秒～１週間、好ましくは数時間～３日である。
前記混合溶液を冷却する際に、混合溶液を流動させる方法としては、攪拌翼による攪拌、超音波照射など従来公知の方法を使用することができる。
混合溶液を流動させる程度は特に限定されず、緩やかな攪拌により混合溶液が僅かに流動する程度からホモジナイザー等での強攪拌による激しい流動状態まで任意に選択することが出来るが、過小な流動状態では析出する擬ポリロタキサン粒子が大きくなるため分散安定性が低下し、沈降分離する場合があり、過大な流動状態では析出する擬ポリロタキサン粒子が微細となりすぎるため得られる擬ポリロタキサン水性分散体の流動性が低下する場合がある。
一方、混合溶液を流動させない状態で冷却した場合、極めて流動性が低いか流動性のないゲル状の擬ポリロタキサン水性分散体となる。
擬ポリロタキサン水性分散体中の粒子の体積平均粒子径は、冷却速度、冷却後の到達温度、冷却する際の混合溶液の流動状態などにより変化するが、擬ポリロタキサン水性分散体の流動性、分散安定性の観点より、１～２００μｍであることが好ましく、１～１００μｍであることがより好ましく、１～５０μｍであることがさらに好ましい。擬ポリロタキサン水性分散体中の粒子の体積平均粒子径が１μｍ未満であると、分散体の流動性が低下するか流動性を示さない場合がある。擬ポリロタキサン水性分散体中の粒子の体積平均粒子径が２００μｍを超えると、擬ポリロタキサン水性分散体中の粒子が沈降分離することがある。
なお、本明細書において前記擬ポリロタキサン水性分散体中の粒子の体積平均粒子径は、レーザー回折式粒度分布測定装置により分析することが出来る。
擬ポリロタキサン水性分散体に占める擬ポリロタキサンの濃度（以下、固形分濃度という）は、５～２５ｗｔ％であることが好ましく、５～２０ｗｔ％であることがより好ましく、１０～２０ｗｔ％であることがさらに好ましい。前記擬ポリロタキサン水性分散体の固形分濃度が５ｗｔ％未満であると、経済的でない。前記擬ポリロタキサン水性分散体の固形分濃度が２５ｗｔ％を超えると、擬ポリロタキサン水性分散体の流動性が低下するため、乾燥工程において噴霧することが難しくなる場合がある。
本発明の擬ポリロタキサンの製造方法は、前記包接工程で得られた擬ポリロタキサン水性分散体を乾燥して擬ポリロタキサンを得る乾燥工程を有する。本発明の擬ポリロタキサンの製造方法によれば、当該乾燥工程により、粉末状の擬ポリロタキサンを得ることができる。
前記乾燥工程では、擬ポリロタキサン水性分散体を噴霧し、加熱した気流中で乾燥する。
前記乾燥工程において、擬ポリロタキサン水性分散体を噴霧する方法としては、例えば、圧力ノズル、二流体ノズル、四流体ノズル、超音波ノズルなどを用いるノズル法や、回転ディスク法などが挙げられる。
前記ノズル法は、擬ポリロタキサン水性分散体の流動性が高い場合に好適に用いることができる。
前記ノズル法に用いられる装置としては、例えば、ノズルアトマイザー式噴霧乾燥装置などが挙げられる。前記ノズルアトマイザー式噴霧乾燥装置では、熱風の吹き出し方向に対向して擬ポリロタキサン水性分散体を噴霧する並向流式、熱風の吹出し方向と同一方向に擬ポリロタキサン水性分散体を噴霧する並流式に大別され、並向流式では噴霧した擬ポリロタキサン水性分散体の滞留時間を長く、並流式では噴霧した擬ポリロタキサン水性分散体の滞留時間を短くすることが出来る。ノズルアトマイザー式噴霧乾燥装置では、ノズル径を変化させるなどにより、噴霧する液滴径を調整し、得られる擬ポリロタキサンの粒子径を任意に調整することが出来る。
前記回転ディスク法は、擬ポリロタキサン水性分散体の流動性が低かったり、擬ポリロタキサン水性分散体中の擬ポリロタキサン粒子が比較的大きかったりする場合に好適に用いることができる。
前記回転ディスク法に用いられる装置としては、例えば、ロータリーアトマイザー式噴霧乾燥装置が挙げられる。前記ロータリーアトマイザー式噴霧乾燥装置では、ディスクの回転数を変化させることにより、噴霧する液滴径を調整し、得られる粉末状擬ポリロタキサンの粒子径を任意に調整することが出来る。
前記乾燥工程において、気流には空気、または窒素などのガスを使用することが出来る。
前記乾燥工程における気流の温度は７０～２００℃であることが好ましく、７０～１８０℃であることがより好ましく、７０～１７０℃であることがさらに好ましい。前記乾燥工程における気流の温度が７０℃未満であると、乾燥が不充分となる場合がある。前記乾燥工程における気流の温度が２００℃を超えると、擬ポリロタキサンが分解し、包接率が低下するおそれがある。
前記乾燥工程における系の圧力は特に限定されないが、通常、大気圧に近い圧力で乾燥を行う。また、減圧下で乾燥することも可能であり、大気圧以下の圧力で乾燥を行うことが好ましい。
噴霧した擬ポリロタキサン水性分散体の滞留時間は、通常数秒から数分であり、シクロデキストリンの遊離を抑制するため、３分以下であることが好ましく、２分以下であることがより好ましい。また、噴霧した擬ポリロタキサン水性分散体の滞留時間が短すぎると、乾燥が不充分となる。
擬ポリロタキサン水性分散体を噴霧する際の液滴の直径は、１～２０００μｍであることが好ましく、５～５００μｍであることがより好ましい。上記液滴の直径が１μｍ未満であると、気流との同伴により乾燥収率が低下する場合がある。上記液滴の直径が２０００μｍを超えると、全液滴の総表面積が小さくなり、乾燥速度が遅くなることがある。
得られる粉末状擬ポリロタキサンや架橋ポリロタキサンの用途、使用目的によるが、本発明によれば、当該粉末状擬ポリロタキサンの包接率を６～６０％とすることができる。前記包接率が６％未満であると、滑車効果が発現しないことがある。前記包接率が６０％を超えると、環状分子であるシクロデキストリンが密に配置され過ぎてシクロデキストリンの可動性が低下することがある。シクロデキストリンが適度な可動性を有し、より高い包接率とするためには、包接率は１５～４０％が好ましく、２０～３０％がより好ましい。
なお、本明細書において前記包接率とは、ＰＥＧへのシクロデキストリンの最大包接量に対するＰＥＧを包接しているシクロデキストリンの包接量の割合であり、ＰＥＧとシクロデキストリンの混合比、水性媒体の種類などを変化させることにより、任意に調整することが出来る。また、前記最大包接量とは、ＰＥＧ鎖の繰り返し単位２つに対し、シクロデキストリンが１つ包接された最密包接状態とした場合のシクロデキストリンの個数をいう。
前記包接率は、１Ｈ－ＮＭＲにより測定することが出来るが、得られた粉末状擬ポリロタキサンを溶解させ分析した場合、シクロデキストリンが遊離し正確な包接率を得ることが出来ないため、通常、シクロデキストリンが遊離しないように当該擬ポリロタキサンの両末端に封鎖基を導入したポリロタキサンに変性した後、分析され、得られた包接率は、作製した粉末状擬ポリロタキサンの包接率とみなすことが出来る。具体的には、包接率は、ＤＭＳＯ－ｄ６に擬ポリロタキサンの両末端に封鎖基を導入したポリロタキサンを溶解し、ＮＭＲ測定装置（ＶＡＲＩＡＮ　Ｍｅｒｃｕｒｙ－４００ＢＢ）により測定し、４～６ｐｐｍのシクロデキストリン由来の積分値と３～４ｐｐｍのシクロデキストリン及びＰＥＧの積分値の比較で算出することができる。
本発明の擬ポリロタキサンの製造方法により得られる粉末状擬ポリロタキサンの体積平均粒子径は１～３００μｍであることが好ましく、５～７０μｍであることがより好ましく、５～５０μｍであることがさらに好ましい。得られる粉末状擬ポリロタキサンの体積平均粒子径が１μｍ未満であると、気流との同伴により乾燥収率が低下する場合がある。得られる粉末状擬ポリロタキサンの体積平均粒子径が３００μｍを超えると、乾燥装置内に付着が生じるおそれがある。
本発明の擬ポリロタキサンの製造方法により得られる粉末状擬ポリロタキサンの含水率は、１０ｗｔ％以下であることが好ましく、７ｗｔ％以下であることがより好ましく、５ｗｔ％以下であることがさらに好ましい。得られる粉末状擬ポリロタキサンの含水率が１０ｗｔ％を超えると、シクロデキストリンが遊離しないように擬ポリロタキサンの両末端に封鎖基を導入する反応において、反応系中の水分が多くなるため、反応が進行しないか、または封鎖基の導入率が低下する場合がある。
本発明によれば、高い包接率を有する粉末状擬ポリロタキサンを工業的に有利な方法で製造することができる擬ポリロタキサンの製造方法を提供することができる。
以下に実施例を掲げて本発明をさらに詳しく説明するが、本発明はこれら実施例のみに限定されない。以下、ＰＥＧを酸化して両末端にカルボキシル基を有するＰＥＧの製造方法について、国際公開第０５／０５２０２６号パンフレットに記載された方法を参考にして行った。
（製造例１）
１Ｌ容のフラスコ内で、ＰＥＧ（重量平均分子量３５０００）１００ｇ、ＴＥＭＰＯ（２，２，６，６－テトラメチル－１－ピペリジニルオキシラジカル）１ｇ、臭化ナトリウム１０ｇを水１Ｌに溶解させた。次いで、次亜塩素酸ナトリウム水溶液（有効塩素濃度５％）５０ｍＬを添加し、室温で３０分間撹拌した。余った次亜塩素酸ナトリウムを分解させるために、エタノールを５０ｍＬ添加して反応を終了させた。
分液ロートを用い、５００ｍＬの塩化メチレンを用いた抽出を３回繰り返して有機層を分取した後、エバポレーターで塩化メチレンを留去し、２Ｌの温エタノールに溶解させてから冷凍庫（－４℃）中で一晩静置し、両末端にカルボキシル基を有するＰＥＧのみを析出させ、回収し、減圧乾燥することにより両末端にカルボキシル基を有するＰＥＧ１００ｇを得た。
（製造例２）
１Ｌ容のフラスコ内で、高分子量ＰＥＧ（重量平均分子量１０万）１００ｇ、ＴＥＭＰＯ（２，２，６，６－テトラメチル－１－ピペリジニルオキシラジカル）１ｇ、臭化ナトリウム１０ｇを水１Ｌに溶解させた。次いで、次亜塩素酸ナトリウム水溶液（有効塩素濃度５％）５０ｍＬを添加し、室温で３０分間撹拌した。余った次亜塩素酸ナトリウムを分解させるために、エタノールを５０ｍＬ添加して反応を終了させた。
分液ロートを用い、５００ｍＬの塩化メチレンを用いた抽出を３回繰り返して有機層を分取した後、エバポレーターで塩化メチレンを留去し、２Ｌの温エタノールに溶解させてから冷凍庫（－４℃）中で一晩静置し、両末端にカルボキシル基を有するＰＥＧのみを析出させ、回収し、減圧乾燥することにより両末端にカルボキシル基を有するＰＥＧ１００ｇを得た。
（実施例１）
（１）両末端にカルボキシル基を有するＰＥＧとα－シクロデキストリンとを用いた擬ポリロタキサン水性分散体の調製
攪拌機付きの１Ｌ容のフラスコ内に、水６５０ｍＬを加え、製造例１で調製した両末端にカルボキシル基を有するＰＥＧ２０ｇ及びα－シクロデキストリン８０ｇを７０℃まで加熱し、溶解させた。
攪拌翼を用い、７００ｒｐｍの回転速度で攪拌しながら、０．４℃／分の冷却速度にて５℃まで冷却し、さらに同温度にて１０時間攪拌し続けることにより、流動性のよい乳液状の擬ポリロタキサン水性分散体（固形分濃度１３ｗｔ％）を得た。
レーザー回折式粒径測定装置を用いて測定した結果、擬ポリロタキサン水性分散体中の粒子の体積平均粒子径は１０μｍであった。
（２）擬ポリロタキサン水性分散体の乾燥
調製した擬ポリロタキサン水性分散体７５０ｇをノズルアトマイザー式噴霧乾燥装置（大川原化工機社製、「Ｌ－８」）を用いて、乾燥機気流入口温度１６０℃、出口温度７０℃にて常圧下で乾燥し（滞留時間１分）、粉末状擬ポリロタキサン９３ｇを得た。得られた粉末状擬ポリロタキサンの含水率は２．２ｗｔ％、体積平均粒子径は３５μｍであった。
（実施例２）
擬ポリロタキサン水性分散体の調製において、溶解させる水の量を５００ｍｌ（擬ポリロタキサン水性分散体の固形分濃度１７ｗｔ％）とした以外は実施例１と同様にして粉末状擬ポリロタキサンを得た。調製した擬ポリロタキサン水性分散体は、流動性のある乳液状であり、中位粒子径は１８μｍであった。得られた粉末状擬ポリロタキサンの含水率は１．４ｗｔ％、体積平均粒子径は４６μｍであった。
（実施例３）
擬ポリロタキサン水性分散体の乾燥において、乾燥機気流入口温度を１８８℃、出口温度を９０℃、滞留時間を２０秒とした以外は実施例１と同様に粉末状擬ポリロタキサンを得た。得られた粉末状擬ポリロタキサンの含水率は０．９ｗｔ％、体積平均粒子径は２８μｍであった。
（実施例４）
擬ポリロタキサン水性分散体の乾燥において、乾燥機気流入口温度を１２０℃、出口温度を７０℃、滞留時間を１分とした以外は実施例１と同様に粉末状擬ポリロタキサンを得た。得られた粉末状擬ポリロタキサンの含水率は４．８ｗｔ％、体積平均粒子径は３２μｍであった。
（実施例５）
擬ポリロタキサン水性分散体の調製において、冷却速度を０．０５℃／分、擬ポリロタキサン水性分散体の乾燥において、乾燥機気流入口温度を１７０℃、出口温度を８０℃とした以外は、実施例１と同様にして粉末状擬ポリロタキサンを得た。調製した擬ポリロタキサン水性分散体は、流動性のある乳液状であり、中位粒子径は５μｍであった。
得られた粉末状擬ポリロタキサンの含水率は１．７ｗｔ％、体積平均粒子径は４０μｍであった。
（実施例６）
擬ポリロタキサン水性分散体の調製において、攪拌翼の攪拌速度を６００ｒｐｍ、冷却速度を１０℃／分とした以外は、実施例１と同様にして粉末状擬ポリロタキサンを得た。調製した擬ポリロタキサン水性分散体は、やや流動性のある乳液状であり、中位粒子径は３８μｍであった。得られた粉末状擬ポリロタキサンの含水率は２．１ｗｔ％、体積平均粒子径は３５μｍであった。
（実施例７）
擬ポリロタキサン水性分散体の調製において、攪拌翼の攪拌速度を７５ｒｐｍ、冷却速度を０．１℃／分とした以外は、実施例１と同様にして粉末状擬ポリロタキサンを得た。調製した擬ポリロタキサン水性分散体は、流動性のよい乳液状であり、中位粒子径は５０μｍであった。得られた粉末状擬ポリロタキサンの含水率は１．９ｗｔ％、体積平均粒子径は３３μｍであった。
（実施例８）
擬ポリロタキサン水性分散体の調製において、攪拌翼の攪拌速度を７０００ｒｐｍ、冷却速度を２０℃／分とした以外は、実施例２と同様にして粉末状擬ポリロタキサンを得た。調製した擬ポリロタキサン水性分散体は、やや流動性のある乳液状であり、中位粒子径は２μｍであった。得られた粉末状擬ポリロタキサンの含水率は１．３ｗｔ％、体積平均粒子径は９μｍであった。
（実施例９）
擬ポリロタキサン水性分散体の調製において、攪拌することなく静置下で冷却した以外は、実施例１と同様にして擬ポリロタキサン水性分散体を得た。調製した擬ポリロタキサン水性分散体は、僅かな流動性しかなく、ペースト状であったため水１５０ｇで希釈後（擬ポリロタキサン水性分散体の固形分濃度１１ｗｔ％）、スパチュラで攪拌し、流動性のある状態とした後、実施例１と同様にして乾燥し、粉末状擬ポリロタキサンを得た。得られた粉末状擬ポリロタキサンの含水率は３．６ｗｔ％、体積平均粒子径は１１μｍであった。
（実施例１０）
製造例２で調製した両末端にカルボキシル基を有するＰＥＧを使用した以外は、実施例１と同様にして粉末状擬ポリロタキサンを得た。調製した擬ポリロタキサン水性分散体は、やや流動性のある乳液状の分散体であり、中位粒子径は１５μｍであった。得られた粉末状擬ポリロタキサンの含水率は１．６ｗｔ％、体積平均粒子径は３３μｍであった。
（実施例１１）
擬ポリロタキサン水性分散体の調製において、攪拌することなく静置下で冷却した以外は、実施例１０と同様にして擬ポリロタキサン水性分散体を得た。調製した擬ポリロタキサン水性分散体は、全く流動性を示さなかったため水２５０ｇで希釈後（擬ポリロタキサン水性分散体の固形分濃度１０ｗｔ％）、スパチュラで攪拌し、やや流動性のある状態とした後、実施例１と同様にして乾燥し、粉末状擬ポリロタキサンを得た。得られた粉末状擬ポリロタキサンの含水率は３．５ｗｔ％、体積平均粒子径は１４μｍであった。
（比較例１）
擬ポリロタキサン水性分散体を凍結乾燥（－１０～２０℃にて４８時間乾燥）した以外は、実施例１と同様にして擬ポリロタキサンを得た。得られた擬ポリロタキサンは多孔質の塊状物であり、含水率は１．２ｗｔ％であった。
（比較例２）
擬ポリロタキサン水性分散体を２０℃にて９６時間減圧乾燥した以外は、実施例１と同様にして擬ポリロタキサンを得た。得られた擬ポリロタキサンは硬い塊状物であり、含水率は４．０ｗｔ％であった。
＜評価＞
実施例及び比較例で得られた擬ポリロタキサンについて、以下の方法により包接率を測定した。結果を表１に示した。
（１）アダマンタンアミンとＢＯＰ試薬反応系を用いた擬ポリロタキサンの封鎖
１Ｌ容のフラスコ内で、室温でジメチルホルムアミド（ＤＭＦ）１７０ｍＬにアダマンタンアミン０．５ｇを溶解し、得られた擬ポリロタキサン５０ｇに添加した後、速やかによく振りまぜた。
続いて、ＢＯＰ試薬（ベンゾトリアゾール－１－イル－オキシ－トリス（ジメチルアミノ）ホスホニウム・ヘキサフルオロフォスフェート）１．３ｇをＤＭＦ８０ｍＬに溶解したものを添加し、速やかによく振りまぜた。
さらに、ジイソプロピルエチルアミン０．５０ｍＬをＤＭＦ８０ｍＬに溶解したものを添加し、速やかによく振り混ぜた。得られた混合物を冷蔵庫中で一晩静置した。
（２）ポリロタキサンの精製と包接率の測定
その後、ＤＭＦ３００ｍＬを加えてよく混ぜ、遠心分離して上澄みを捨てる洗浄操作を行った。このＤＭＦによる洗浄操作を合計２回繰り返した後、得られた沈澱を２０００ｍＬの熱水（７０℃）に分散させ、よく攪拌し濾過する洗浄操作を行った。
この熱水による洗浄操作を合計４回繰り返し、回収した沈殿を凍結乾燥させ最終的に精製ポリロタキサンを得た。
得られたポリロタキサンの包接率は、１Ｈ－ＮＭＲで同定した。得られた包接率は、擬ポリロタキサンの包接率とみなすことが出来る。
Figure JPOXMLDOC01-appb-T000001
本発明によれば、高い包接率を有する粉末状擬ポリロタキサンを工業的に有利な方法で製造することができる擬ポリロタキサンの製造方法を提供することができる。

Claims (9)

  1. ポリエチレングリコールとシクロデキストリンとを水性媒体中で混合し、シクロデキストリン分子の開口部に前記ポリエチレングリコールが串刺し状に包接された擬ポリロタキサン粒子を含有する擬ポリロタキサン水性分散体を得る包接工程と、前記包接工程で得られた擬ポリロタキサン水性分散体を乾燥して擬ポリロタキサンを得る乾燥工程とを有する擬ポリロタキサンの製造方法であって、
    前記乾燥工程において、擬ポリロタキサン水性分散体を噴霧し、加熱した気流中で乾燥する
    ことを特徴とする擬ポリロタキサンの製造方法。
  2. ポリエチレングリコールの重量平均分子量が１０００～５０万である請求項１記載の擬ポリロタキサンの製造方法。
  3. ポリエチレングリコールとシクロデキストリンとの重量比が１：２～１：５である請求項１または２記載の擬ポリロタキサンの製造方法。
  4. 包接工程において、ポリエチレングリコールとシクロデキストリンとを、水性媒体中に溶解して混合溶液を調製した後、前記混合溶液を流動させながら連続的または断続的に冷却し、擬ポリロタキサン粒子を析出させることにより、擬ポリロタキサン水性分散体を得る請求項１、２または３記載の擬ポリロタキサンの製造方法。
  5. 冷却速度が０．０１～３０℃／分である請求項４記載の擬ポリロタキサンの製造方法。
  6. 擬ポリロタキサン水性分散体の固形分濃度が５～２５ｗｔ％である請求項１、２、３、４または５記載の擬ポリロタキサンの製造方法。
  7. 擬ポリロタキサン水性分散体中の粒子の体積平均粒子径が１～２００μｍである請求項１、２、３、４、５または６記載の擬ポリロタキサンの製造方法。
  8. 乾燥工程における気流の温度が７０～２００℃である請求項１、２、３、４、５、６または７記載の擬ポリロタキサンの製造方法。
  9. 乾燥工程における系の圧力が大気圧以下である請求項１、２、３、４、５、６、７または８記載の擬ポリロタキサンの製造方法。
PCT/JP2011/078015 2010-12-16 2011-12-05 擬ポリロタキサンの製造方法 WO2012081429A1 (ja)