CN101798472A - 一种黑、蓝分散染料组合物 - Google Patents
一种黑、蓝分散染料组合物 Download PDFInfo
- Publication number
- CN101798472A CN101798472A CN201010133539A CN201010133539A CN101798472A CN 101798472 A CN101798472 A CN 101798472A CN 201010133539 A CN201010133539 A CN 201010133539A CN 201010133539 A CN201010133539 A CN 201010133539A CN 101798472 A CN101798472 A CN 101798472A
- Authority
- CN
- China
- Prior art keywords
- dye
- black
- formula
- monomer
- blue
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
本发明公开了一种黑、蓝分散染料组合物，按重量百分比计，包括：30％～70％至少一种如式(1)所示的染料单体A；15％～40％至少一种如式(2)所示的染料单体B；5％～50％至少一种如式(3)所示的染料单体C；5％～50％至少一种如式(4)所示的染料单体D。本发明的分散染料组合物pH值的适用范围广，配伍性好，染深性强，得色量高，均匀性佳，升华牢度、水洗牢度、日晒牢度均好，更为重要的是此黑、蓝分散染料组合物的价格便宜，使用方便，弥补了分散橙288#拼得黑、蓝分散染料配伍性、染深性、寅色性的不足。
Description
技术领域
本发明涉及一种环保型黑、蓝分散染料组合物，适用于涤纶及其混纺织物的染色和印花。
背景技术
目前市场上环保型的黑、蓝系列分散染料，一般由分散橙288#、分散紫93:1和分散蓝291:3组成，此组合物其中一个组份分散橙288#虽然为环保染料，弥补了分散橙76#的不足，而且成本也比同样环保的分散橙61#偏低不少，但分散橙288#的缺点就是配伍性、染深性、遮盖性不及分散橙76#和分散橙61#，而且寅色性比较严重，对寅色性要求比较的高档进口聚酯纤维，只能用分散橙61#拼的黑、蓝分散染料组合物。但分散橙61#拼的黑、蓝分散染料组合物的成本太高，寻找一只既环保、性能又好、成本又低的黑、蓝分散染料组合物，迫在眉睫。
发明内容
本发明提供一种环保的、染深性、遮盖性、寅色性均较好的黑、蓝分散染料组合物，弥补了分散橙288#拼得黑、蓝分散染料配伍性、染深性、寅色性的不足。此分散染料组合物pH值的适用范围广，配伍性好，染深性强，得色量高，均匀性佳，升华牢度、水洗牢度、日晒牢度均好，更为重要的是此黑、蓝分散染料组合物的价格便宜，使用方便。
一种黑、蓝分散染料组合物按重量百分比计，包括：
30％～70％至少一种如式(1)所示的染料单体A：
X1为H、卤素、NO2或CN；
R1、R2各自独立为C1～C4的烷基；
R3、R4各自独立为C1～C4的烷基或为C1～C4烷基中的一个氢被苯环、烷氧基、CN取代或为CH2CH＝CH2或为烷酰氧烷基；
15％～40％至少一种如式(2)所示的染料单体B：
X2、X3各自独立为H、卤素、NO2或CN；
R5为C1～C4的烷基；
R6、R7各自独立为C1～C4的烷基或C1～C4烷基中的一个氢被苯环、烷氧基、CN取代或为烷酰氧烷基或为CH2CH＝CH2；
5％～50％至少一种如式(3)所示的染料单体C：
X3、X4各自独立为H、卤素、CN或NO2；
5％～50％至少一种如式(4)所示的染料单体D：
X5、X6各自独立为H、卤素、CN或NO2。
所述染料单体A优选由以下一种或一种以上成份组成，
所述染料单体B优选由以下一种或一种以上成份组成，
所述染料单体C优选由以下一种或一种以上成份组成，
所述染料单体D优选由以下一种或一种以上成份组成，
本发明所述的黑、蓝分散染料组合物优选为35％～55％至少一种如式(1)所示的染料单体A，20％～35％至少一种如式(2)所示的染料单体B，6％～30％至少一种如式(3)所示的染料单体C，6％～30％至少一种如式(4)所示的染料单体D。
本发明所述的黑、蓝分散染料组合物，应用时一般需要加入助剂。所述的助剂为分散染料复配时常用的分散剂、扩散剂及其表面活性剂等.优选包括下列之一或其混合物：萘磺酸甲醛缩合物、木质素磺酸盐、烷基萘磺酸甲醛缩合物。如甲基萘磺酸甲醛缩合物(分散剂MF)、萘磺酸甲醛缩合物(扩散剂NNO)、苄基萘磺酸甲醛缩合物(扩散剂CNF)、木质素磺酸钠(木质素85A、83A)等。通常，助剂与原染料重量之比为1.5～3.2∶1。
本发明所述的黑、蓝分散染料组合物可用以下方法制备：将染料单体的原染料按比例混合后，在助剂、水或其它表面活性剂存在下，用砂磨机或研磨机等粉碎机进行微粒子化，然后喷雾干燥。上述染料单体均可采用市售产品。
本发明所述的黑、蓝分散染料组合物，微粒子化后可为液状、膏状，喷雾干燥后可为粉状、颗粒状。本发明所述的黑、蓝分散染料组合物为环保型的，因其染深性好、遮盖性强，可减少染料用量，提高染料的利用率；因其得色量高、吸尽率高，可减少染色时的污水；因其染色时的各组份的相溶性、均染性、配伍性均好、pH值的适用范围极广，所以使用起来比较方便。并且本发明所述的黑、蓝分散染料组价格便宜，寅色性少，升华牢度、水洗牢度、日晒牢度均好。
具体实施方式
下面结合实施例对本发明作进一步说明，但本发明的保护范围并不限于此。
实施例1～18
根据表1所示数据，将染料单体A、染料单体B、染料单体C、染料单体D按一定的配比与甲基萘磺酸甲醛缩合物(分散剂MF)、萘磺酸甲醛缩合物(扩散剂NNO)、木质素磺酸钠(木质素85A、83A)加水拼混后，用砂磨进行研磨分散，然后进行喷雾干燥。
其中染料单体A中的(1-1)可选用浙江闰土股份有限公司生产的C.I.DISP BLUE 291：1#；(1-2)可选用浙江闰土股份有限公司生产的C.I.DISP BLUE 291：2#；(1-3)为2，4-二硝基氯化苯胺重氮化与2-甲氧基-5-乙酰氨基-N-乙基-N-烯丙基苯胺偶合制得；(1-4)为2，4-二硝基氯化苯胺重氮化与2-甲氧基-5-乙酰氨基-N-乙基-N-氰乙基苯胺偶合制得；(1-5)为2，4-二硝基氯化苯胺重氮化与2-甲氧基-5-乙酰氨基-N-苄基-N-氰乙基苯胺偶合制得；(1-6)可选用浙江闰土股份有限公司生产的C.I.DISP BLUE 291#；(1-7)可选用浙江闰土股份有限公司生产的C.I.DISP BLUE 301#；(1-8)可选用浙江闰土股份有限公司生产的C.I.DISP BLUE 79#。
其中染料单体B中的(2-1)可选用浙江闰土股份有限公司生产的C.I.DISP VIOLET 93#；(2-2)可选用浙江闰土股份有限公司生产的C.I.DISP VIOLET 93：1#；(2-3)可选用浙江闰土股份有限公司生产的C.I.DISP BLUE 183：1#；(2-4)可选用浙江闰土股份有限公司生产的C.I.DISP BLUE 165：1#；(2-5)可选用浙江闰土股份有限公司生产的C.I.DISP BLUE 165#；(2-6)可选用浙江闰土股份有限公司生产的C.I.DISPVIOLET 63#；(2-7)可选用浙江闰土股份有限公司生产的C.I.DISP VIOLET33#；(2-8)可选用浙江闰土股份有限公司生产的C.I.DISP VIOLET 77#。
其中染料单体C中的(3-1)可选用浙江闰土股份有限公司生产的C.I.DISP ORANGE 288#；(3-2)可选用浙江闰土股份有限公司生产的C.I.DISP ORANGE 30：2#；(3-3)可选用浙江闰土股份有限公司生产的C.I.DISP ORANGE 298#。
其中染料单体D中的(4-1)可选用浙江闰土股份有限公司生产的C.I.DISP ORANGE 279#；(4-2)可选用浙江闰土股份有限公司生产的C.I.DISP ORANGE 278#。
表1：
将上述实施例制得的分散染料组合物与45％(重量)分散蓝291:1、30％(重量)分散紫93#、25％(重量)分散橙288#拼制的组合物进行性能对比测试，测试方法如下：
各取0.5克实施例1～20制得的分散染料，用水分别配制成浓度为1g/500ml的分散染料悬浮液，取10ml、50ml、80ml的悬浮液与90ml、50ml、20ml的水混合，用醋酸调节染浴pH到5，然后升温到60℃，同时分别放入2g聚酯纤维进行高温高压染色，在35分钟内升温到130℃，保温30分钟，冷却到80℃时取样。
观察布样色光并采用GB/T2400-1980、GB/T2397-2003、GB/T3921-1997、GB/T3920-1997、GB/T5718-1997测定其染色牢度。测定结果见表2。
表2
| 实施例名称 | 配伍性 | 提升力 | 水洗牢度 | 摩擦牢度 | 升华牢度(180℃) |
| 实施例1 | A | A | 4-5 | 4-5 | 4-5 |
| 实施例2 | A-B | A | 4-5 | 4-5 | 4-5 |
| 实施例3 | A | A | 4-5 | 4-5 | 4-5 |
| 实施例4 | A-B | A | 4 | 4-5 | 4-5 |
| 实施例5 | A-B | A- | 4-5 | 4-5 | 4-5 |
| 实施例6 | A-B | A | 4-5 | 4-5 | 4-5 |
| 实施例7 | A | A- | 4-5 | 4-5 | 4-5 |
| 实施例8 | A-B | A-B | 4-5 | 4-5 | 4-5 |
| 实施例9 | A-B | A | 4 | 4-5 | 4-5 |
| 实施例10 | A | A | 4 | 4-5 | 4-5 |
| 实施例11 | A | A | 4 | 4-5 | 4-5 |
| 实施例12 | A-B | A | 4-5 | 4-5 | 4-5 |
| 实施例13 | A | A | 4-5 | 4-5 | 4-5 |
| 实施例14 | A- | A | 4 | 4-5 | 4-5 |
| 实施例15 | A | A- | 4-5 | 4-5 | 4-5 |
| 实施例16 | A | A- | 4-5 | 4-5 | 4-5 |
| 实施例名称 | 配伍性 | 提升力 | 水洗牢度 | 摩擦牢度 | 升华牢度(180℃) |
| 实施例17 | A | A | 4 | 4-5 | 4-5 |
| 实施例18 | A- | A | 4-5 | 4-5 | 4-5 |
| 实施例19 | A | A | 4 | 4-5 | 4-5 |
| 实施例20 | A | A | 4-5 | 4-5 | 4-5 |
| 对比例 | B | B | 4-5 | 4-5 | 4-5 |
Claims (6)
1.一种黑、蓝分散染料组合物，按重量百分比计，包括：
30％～70％至少一种如式(1)所示的染料单体A：
X1为H、卤素、NO2或CN；
R1、R2各自独立为C1～C4的烷基；
R3、R4各自独立为C1～C4的烷基或为C1～C4烷基中的一个氢被苯环、烷氧基、CN取代或为CH2CH＝CH2或为烷酰氧烷基；
15％～40％至少一种如式(2)所示的染料单体B：
X2、X3各自独立为H、卤素、NO2或CN；
R5为C1～C4的烷基；
R6、R7各自独立为C1～C4的烷基或C1～C4烷基中的一个氢被苯环、烷氧基、CN取代或为烷酰氧烷基或为CH2CH＝CH2；
5％～50％至少一种如式(3)所示的染料单体C：
X3、X4各自独立为H、卤素、CN或NO2。
5％～50％至少一种如式(4)所示的染料单体D：
X5、X6各自独立为H、卤素、CN或NO2。
2.如权利要求1所述的黑、蓝分散染料组合物，其特征在于：所述染料单体A由以下一种或一种以上成份组成，
3.如权利要求1所述的黑、蓝分散染料组合物，其特征在于：所述染料单体B由以下一种或一种以上成份组成，
4.如权利要求1所述的黑、蓝分散染料组合物，其特征在于：所述染料单体C由以下一种或一种以上成份组成，
5.如权利要求1所述的黑、蓝分散染料组合物，其特征在于：所述染料单体D由以下一种或一种以上成份组成，
6.如权利要求1所述的黑、蓝分散染料组合物，其特征在于：按重量百分比计，包括：35％～55％至少一种如式(1)所示的染料单体A，20％～35％至少一种如式(2)所示的染料单体B，6％～30％至少一种如式(3)所示的染料单体C，6％～30％至少一种如式(4)所示的染料单体D。