TWI710543B - 用於針對鐘錶或珠寶硬焊鈦合金零件與氧化鋯基的陶瓷零件之方法 - Google Patents

用於針對鐘錶或珠寶硬焊鈦合金零件與氧化鋯基的陶瓷零件之方法 Download PDF

Info

Publication number
TWI710543B
TWI710543B TW108140066A TW108140066A TWI710543B TW I710543 B TWI710543 B TW I710543B TW 108140066 A TW108140066 A TW 108140066A TW 108140066 A TW108140066 A TW 108140066A TW I710543 B TWI710543 B TW I710543B
Authority
TW
Taiwan
Prior art keywords
component
brazing
bearing surface
brazing material
groove
Prior art date
Application number
TW108140066A
Other languages
English (en)
Other versions
TW202024001A (zh
Inventor
達曼 拉布杜伊爾
亞歷山卓 內圖斯奇爾
Original Assignee
瑞士商柯瑪豆股份有限公司
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 瑞士商柯瑪豆股份有限公司 filed Critical 瑞士商柯瑪豆股份有限公司
Publication of TW202024001A publication Critical patent/TW202024001A/zh
Application granted granted Critical
Publication of TWI710543B publication Critical patent/TWI710543B/zh

Abstract

用於硬焊第一陶瓷部件(10)和第二金屬合金部件(20)以製造結構或外部時計元件(100)的方法，選擇氧化鋯基的陶瓷作為第一部件(10)和鈦合金作為第二部件(20)，第一凹槽(4)在第一部件(10)內被形成，從第一表面(1)在與第二部件(20)的第二表面(2)的接合區域(3)中被設定後退，將硬焊材料(5)沉積在該第一表面(1)上，並在每個凹槽(4)內，將第二表面(2)與第一表面(1)對準以形成組件， 組件在受控的氣氛中加熱到高於硬焊材料(5)的熔化溫度，以便在接合區域(3)中形成硬焊。

Description

用於針對鐘錶或珠寶硬焊鈦合金零件與氧化鋯基的陶瓷零件之方法
本發明關於一種用於硬焊第一陶瓷部件和第二金屬合金部件以製造結構和/或外部時計元件的方法。
本發明還關於一種包括至少一個藉由根據本發明的方法製作的結構和/或外部元件的手錶。
本發明關於特別是用於手錶的結構和/或外部時計元件的製造。它更具體地關於由幾種材料的組裝產生的複合元件的領域，並且更具體地，還包括陶瓷材料成分。
在鐘錶學中，將陶瓷部件與其他金屬類型的部件組裝仍然是難以正確管理以確保隨時間推移完美黏附的困難操作。實際上，通常存在組裝三維部件的問題：其為幾十毫米至幾毫米的厚度，其連接表面主要是傾斜表面，通常具有精確的定位和對中，特別是在對稱性方面，例如，殼體的軸向對稱性或錶鍊元件的橫向對稱性。
用於組裝用於這種時計應用的陶瓷，特別是氧化鋯基的陶瓷和金屬合金的當前技術是壓配合、黏合劑結合(聚合物黏合劑)和螺釘配合。這些技術會削弱部件，並且不能保證隨時間推移的黏附性。
各種文件解決了這個問題： JP S63249085A SEIKO EPSON KYOCERA公開了一種用於時計應用的將氧化鋯基陶瓷部件與另一種金屬合金部件，特別是鈦合金硬焊的方法； -WO99/58332A1太平洋海岸技術公開了使用鈦/鎳硬焊材料在由金屬材料例如含鈦材料製作的界面上密封由諸如氧化鋯的陶瓷材料製作的界面表面的方法。較佳的陶瓷包括穩定的氧化鋯材料。較佳的金屬包括鈦和鈮的合金。較佳的鈦/鎳硬焊材料是50:50的鈦/鎳合金。含鈦，鎳和鈮的硬焊材料用於將陶瓷材料連接到不含鈮的金屬材料上。將至少一個界面放置成與鈦/鎳硬焊材料接觸，並在真空條件下在900至1200℃的溫度範圍內進行密封，同時向接頭施加壓力。該方法適用於可植入醫療設備、電連接器、電子箱、運動用品、結構部件中的氣密密封應用； -WO2017/129705A1 MORGAN高級陶瓷公司公開了一種用於對燒結的氧化鋯陶瓷體進行硬焊的方法，該方法包括以下步驟：提供具有表面的燒結的氧化鋯陶瓷體，對燒結的氧化鋯陶瓷體進行整體或部分化學還原以形成相對於燒結後的還原表面。氧化鋯陶瓷體，將釬料施加到減小的表面的至少一部分上以形成包括所述釬料和燒結的氧化鋯陶瓷體的組件，將所述組件加熱到足以至少部分地熔化釬料的溫度，以使硬焊材料潤濕縮小的表面，並冷卻組件以使硬焊材料固化； -EP3243593A1 PNL HOLDING公開了一種用於在氧化鋯零件的表面上硬焊金屬元素的方法，該方法包括以下步驟：-降低零件的表面狀況，以允許第一金屬化層的黏附力；-清洗零件以去除雜質。-在零件的表面上沉積主要包含鈦的第一金屬化層，-在第一金屬化層上沉積主要包含鈮的第二金屬化層，-在第二金屬化層上放置元素，-在其上沉積金硬焊元件和第二金屬化層，-以受控的溫度冷卻硬焊區域，-在硬焊之前在金屬元件的負載下進行應力消除熱處理； FR2862246A1 EADS SPACE TRANSP GmbH公開了一種方法，該方法包括在硬焊之前藉由使用Nd/Yag雷射束或機械方式在陶瓷表面中形成一系列孔來對至少一個陶瓷表面進行結構化。孔的平均直徑大於550 mcm，分為兩類，它們的幾何形狀，直徑或深度不同。每個類別中的多個孔組成一個幾何組，一組中的孔中心之間的間距小於另一組中的孔中心之間的間距。當對陶瓷表面進行纖維增強和層壓時，將孔的深度製作至少等於層壓層的深度。 -EP2789597 ALSTOM TECHNOLOGY Ltd.公開了一種用於獲得用於將包括隔熱材料的陶瓷層接合到金屬層的構造的方法，該構造包括由金屬材料製作的位於陶瓷層和金屬層之間的界面層，包括在其面對陶瓷層的一側上的多個互鎖元件，陶瓷層包括多個空腔，該多個空腔旨在連接到界面層的相應互鎖元件，該構造還包括硬焊層，藉由該硬焊層，界面層與金屬層連接； -EP2799411A1 COMADUR公開了一種製造亮橙色氧化鋯基製品的方法，其特徵在於，它包括以下連續步驟：製備包含氧化鋯粉末的第一混合物，該混合物中按重量計從3％至20％的至少一個穩定劑中選擇包括氧化釔、氧化鎂和氧化鈣的氧化物，單獨或組合使用，按重量計0.1％至5％，至少一種旨在形成玻璃相的元素，並選自氧化矽、氧化鋁、氧化鋰氧化釔粉末，單獨或組合使用，按重量計佔氧化鈰粉末的1％至6％。製備包含所述第一混合物和黏合劑的第二混合物，藉由將所述第二混合物造粒而製得顆粒混合物；藉由使第二粒狀混合物具有所需物品的形狀來形成生坯；在還原性氣氛中在1,250至1,500℃之間的溫度下空氣燒結至少30分鐘，並在700℃至1,350℃之間的溫度下退火所需產品，持續30分鐘至20小時。並拋光所述燒結的生坯。 Sonia Simoes於2018年10月26日發表的文章“金屬合金與陶瓷的鈦合金的最新進展”提供了其他指示。
本發明提出在不使用機械應力或聚合物黏合劑的情況下解決金屬合金時計部件組裝到陶瓷部件的問題，從而使組裝件具有更好的機械性能。
為了控制生產成本，本發明還提出了藉由直接硬焊而沒有任何相對部件的在先的薄膜金屬化來製造這樣的組件的目的。
本發明的目的是藉由受控氣氛硬焊處理將由這種合金製作的部件與陶瓷部件組裝在一起。原理是： -在陶瓷基板中製造至少形成一個(底切)凹槽； -在該凹槽內以及希望硬焊的整個表面上沉積釬料； -添加希望硬焊的金屬合金部件，並精確定位； -將組件加熱到合適的溫度，以熔化硬焊材料並在兩個部件之間形成硬焊。
為此，根據請求項1，本發明關於一種用於硬焊第一陶瓷部件和第二金屬合金部件以製造結構和/或外部時計元件的方法。
更具體地，本發明關於根據請求項2所述的一種硬焊方法，用於在至少一個接合區域中硬焊在第一氧化鋯基陶瓷部件中包含的至少一個第一軸承表面與第二鈦金屬合金部件中包含的至少一個第二軸承表面之間，以製造用於鐘錶或珠寶的結構和/或外部元件。
本發明還關於一種包括至少一個藉由根據本發明的方法製作的結構和/或外部元件的手錶。
本發明關於一種用於硬焊第一陶瓷部件10和第二金屬合金部件20以製造結構和/或外部時計元件100的方法。
根據本發明，選擇氧化鋯基的陶瓷作為第一陶瓷部件10，並且選擇鈦合金作為第二金屬合金部件20。
的確，在適於外部時計部件的陶瓷和金屬合金之間進行硬焊是困難的操作，並且所進行的大量測試已突顯了陶瓷和金屬合金之間緊密的熱行為的本質。
下文中說明的方法可以用於其他陶瓷，例如基於氮化矽的陶瓷或其他，和/或用於其他合金，例如不銹鋼或其他合金，但是其膨脹和收縮行為非常不同，這損害了硬焊操作的原理之品質，這說明了將氧化鋯基陶瓷與鈦合金配對的刻意選擇，以產生高品質的硬焊，尤其是隨著時間的流逝特別出色的黏附力。
氧化鋯是具有許多有利特性的材料，但是與其他元素完全不反應。因此，執行硬焊的原理非常困難，硬焊的原理是基於元素(硬焊材料和部件)之間的反應。在健康安全性、強度、耐老化性、外觀品質等方面，要選擇與鐘錶限制條件相容的合適金屬合金並不明顯。因為硬焊發生在硬焊材料的熔化溫度下，所以兩個組裝的元件的熱膨脹係數必須非常接近，如氧化鋯和鈦的情況，以避免部件破裂或變形的任何風險。
根據本發明，至少那些不含鎳的鈦合金滿足上述條件，並且適合於與氧化鋯基的陶瓷組裝在一起的硬焊。
儘管在下文中公開的方法的操作模式在理論上對於其他陶瓷/金屬合金對的情況是可行的，對於其他陶瓷和其他金屬合金，問題是相似的，但是在大多數情況下不可能藉由硬焊進行組裝，或者至少很難實施。
更具體地，根據本發明，至少第一凹槽4在第一部件10內製作，相對於第一軸承表面1在與第二部件20的第二軸承表面2的接合區域3中相對於第一軸承表面1被設定後退，硬焊材料5沉積在該第一軸承表面1上並且在每個凹槽4內，第二表面2與第一表面1對準以形成組件，並且在受控氣氛中將該組件加熱到高於硬焊材料5的熔化溫度的溫度，以在接合區域3中在第二部件20和第一部件10之間形成硬焊。
更具體地，為了產生這種元件100，該硬焊方法在第一氧化鋯基陶瓷部件10中包含的至少一個第一軸承表面1與第二鈦合金構件20中包含的至少一個第二軸承表面2之間的至少一個接合區域3中實施。第二軸承表面2至少部分地與第一軸承表面1互補。
根據本發明，第一部件10和/或第二部件20藉由使從其第一軸承表面1和/或其第二軸承表面2被設定後退的錐形鑽、狹縫或凹槽類型的至少一個第一凹槽4，和/或分別形成第二凹槽7的形成接收器而佈置，該接收器佈置成允許硬焊材料5從第一軸承表面1和/或第二軸承表面2被設定後退，深深穿透第一部件10和/或第二部件20內，並促進在第一部件10和/或第二部件20內部的硬焊材料5的機械黏附易於硬焊。
為此，選擇至少與第二部件的鈦合金相容的硬焊材料5，特別是但不限於5級鈦合金。
藉由將硬焊材料5沉積在第一軸承表面1上以及從第一軸承表面1被設定後退的每個第一凹槽4內和/或分別在第二軸承表面2上和從第二軸承表面2被設定後退的每個第二凹槽7內製備第一部件10和/或第二部件20。
第二部件20的第二表面2定位成與第一部件10的第一表面1對準，以形成組件。然後將該組件在受控氣氛中加熱到高於或等於硬焊材料5的熔化溫度的溫度，以在接合區域3中的第二部件20和第一部件10之間形成硬焊。
有利地，製造多個凹槽4，其在接合區域3中幾何分佈，以執行第二部件20到第一部件10的一種裝訂。例如，為了在殼體中部的肩部周圍硬焊​​環，至少三個或更具體地至少四個這樣的凹槽4被製作以確保兩個部件的良好相對黏附。
在一種變型中，在接合區域3中製作多個不連續的第一凹槽4和/或第二凹槽7。
在另一個變體中，在接合區域3中製作單個連續凹槽4。更具體地說，該單個凹槽4依循圍繞第一部件10的第一表面1的封閉輪廓。
在特定的實施方式中，僅在第一部件10中製造第一凹槽4，以便將第二部件20的最可能的材料保持在接合區域3中。然後，藉由製造從第一軸承表面1被設定後退的錐形鑽孔、狹縫或凹槽類型的至少一個第一凹槽4來佈置第一部件10，第一凹槽4形成設置成允許硬焊材料5穿透第一部件10內深處之接收器，從第一軸承表面1被設定後退的，以促進硬焊材料5在第一部件10內的機械黏合。選擇與鈦合金相容的硬焊材料5。藉由在第一軸承表面1上和從第一軸承表面1被設定後退的每個第一凹槽4內沉積硬焊材料5來製備第一部件10。因此，第二部件20的第二表面2與第一部件10的第一表面1定位對準，以準備好形成一個組件。在受控的氣氛中將該組件加熱到高於或等於硬焊材料5的熔化溫度的溫度，以在接合區域3中在第二部件20和第一部件10之間形成硬焊。
更具體地，製作第一部件1的至少第一軸承表面1，具有至少兩個第一基本表面11、基本表面12，它們在至少第一交叉線13上是正割的，並且至少是第一凹槽4在第一交叉線13上製作。例如，如圖8和圖9所示，第一基本表面11是平面表面，第二基本表面12是圓柱形，並且交叉線13是圓形，並且凹槽圖4中的曲線圖同時侵占第一基本表面11、第二基本表面12和交叉線13。
同樣，如圖5所示，至少第二支撐表面12可以以正割在位於交界區域3中的至少第二交叉線23上的至少兩個基本表面21、基本表面22在第二部件20中製作。
在第二部件20還設置有一個或多個第二凹槽7的替代方案中，更具體地，在第二交叉線上23製作至少一個這樣的第二凹槽7。
更具體地，當可能時，選擇硬焊材料5以與鈦合金和氧化鋯基的陶瓷兩者都相容。
更具體地，在硬焊操作之前對第一部件10和第二部件20進行超聲波清洗。
更具體地，在硬焊操作期間，組件被機械地緊密地保持在接合區域3附近。
更具體地，選擇硬焊膏作為硬焊材料5，其在壓力下至少插入每個第一凹槽4內和/或分別插入每個第二凹槽7的適當位置，並從第一表面1和/或分別從第二表面2退回。
更具體地，如圖13所示，至少第一凹槽4靠近第一表面1製作有頸部6，其中頸部6的橫截面小於與第一表面1相對的第一凹槽4的底部8的橫截面，以在硬焊操作之後形成將第二部件20保持到第一部件10的機械鍵。更具體地，每個第一凹槽4在靠近第一表面1處製作有這樣的頸部6，其中頸部6的橫截面小於與第一表面1相對的第一凹槽4的底部8的橫截面，以在硬焊操作之後形成將第二部件20保持到第一部件10的機械鍵。
在一種變型中，確定第二部件20的單一插入方向DI以使其與第一部件10對準，並且使至少第一凹槽4傾斜或垂直於插入方向DI。更具體地，每個第一凹槽4被製作傾斜或垂直於插入方向DI。
在另一變型中，確定第二部件20的單個插入方向DI以使其與第一部件10對準，並且在插入方向DI上至少形成第一凹槽4。
更具體地，確定第二部件20的單一插入方向DI以使其與第一部件10對準，並且在沉積硬焊材料5之前的自由狀態下，第一表面1和第二表面2之間製造有徑向間隙JR在它們之間；所述徑向間隙JR在垂直於插入方向DI的半徑處被包含在0.010mm至0.040mm之間。又更具體地，在沉積硬焊材料5之前的自由狀態下，第一表面1和第二表面2之間製造有徑向間隙JR在第一表面1和第二表面2之間；所述徑向間隙JR在垂直於插入方向DI的半徑處被包含在0.015mm至0.025mm之間。
更具體地，藉由注射器將硬焊材料5插入每個第一凹槽4中。
更具體地，選擇適合於在鋼上硬焊碳化鎢的硬焊材料作為硬焊材料5。
更具體地，選擇硬焊材料5以包括銅、錳和鎳，並且是無鎘的，具有超細的晶粒尺寸，並且包括用於在受控氣氛爐中以介於1000℃和1100℃之間的溫度硬焊的黏合劑。
更具體地，在包括帶的氬氣可控氣氛爐中，針對硬焊操作以進入該爐的速度包括在0.15m/mn至0.25m/mn之間進行可控氣氛加熱。
更具體地，在硬焊操作之後，在帶速度為0.05m/mm至0.15m/mm之間的帶上進行第一冷卻操作。
更具體地，硬焊和/或第一次冷卻是用機械工具固定組件的固體工具和/或至少與放置並保持在組件上的組件的重量相等的重量進行的，以減慢硬焊操作後冷卻組件的速度。
更具體地，在硬焊之後，將組件放置在石墨支撐件上以進行快速冷卻而沒有熱衝擊。
更具體地，在硬焊和/或第一次冷卻操作之後，將組件放置在石墨支撐件上以進行快速冷卻而沒有熱衝擊。
更具體地，如圖10所示，硬焊材料5以波型8沉積在第一表面1和/或第二表面2上。
更具體地，在製造第一陶瓷部件10的期間，製造至少第一凹槽4，特別是在模具中製造該第一凹槽4。
更具體地，至少一個第一凹槽4被使用雷射精完全機械加工，或精加工。
更具體地，至少一個第一凹槽4被使用工具或砂輪完全地機械加工或精加工。
更具體地，選擇5級鈦作為鈦合金。根據ASTM F136，該5級鈦的%含量包括從0.00至0.08 C、從0.0至0.3 Fe、從0.0000至0.0125 H、從0.00至0.05 N、從0.0至0.2 O、從5.50至6.75 Al、從3.5至4.5 V、從0.0至0.1 OE(每個其他元素)、從0.0至0.4 TO(所有其他元素)，其餘為Ti。
更具體地，選擇氧化鋯基陶瓷以包括： -單獨或組合地選自氧化釔、氧化鎂和氧化鈣的氧化物的群組之至少一個穩定劑； -旨在產生玻璃相，並單獨或組合地選自氧化矽、氧化鋁、氧化鋰和氧化釔的群組之至少一種元素； -用作顏料的氧化物粉末； -和形成剩餘物至100重量％之氧化鋯粉末。
更具體地，選擇氧化鋯基的陶瓷以包含： -3至20重量％的至少一個穩定劑，其單獨或組合地選自包含氧化釔、氧化鎂和氧化鈣的氧化物的群組； -0.1至5重量％的旨在產生玻璃相的至少一個元件，其單獨或組合地選自包含氧化矽、氧化鋁、氧化鋰和氧化釔的群組； -1至10重量％的用作顏料的氧化物粉末； -和形成剩餘物至100重量％之氧化鋯粉末。
更具體地以在氧化鋯基的陶瓷殼體中部上的鈦合金環的硬焊組件，特別是5級鈦的硬焊組件來說明本發明。試驗表明，一個重要的參數是殼體中部和環之間在硬焊之前的間隙，這對於允許適當的熱膨脹而不產生不希望的變形是必要的。特別地，對於具有大約37mm的組件肩部的殼體中部，在殼體中部與環之間的半徑處的間隙有利地包括在0.01mm與0.04mm之間，並且較佳地接近於0.02mm。當然，這種低間隙值要求降低加工公差，這與成本同義。
可以用雷射製造底切凹槽。這些底切凹槽4的目的是產生機械黏合的區域，其增強硬焊。底切凹槽4可以僅位於某些區域，例如，靠近殼體中部的角部，如圖8所示。
用CF CuMn3硬焊材料和氬氣可控氣氛爐正確地進行硬焊。
良好的硬焊條件如下： -進入熔爐的速度：20厘米/分鐘(所需速度)； -冷卻速度：10厘米/分鐘(所需速度)； -在氬氣氛下硬焊； -爐溫：期望溫度為1050℃。
操作規程包括執行以獲得最終產品的所有步驟。
硬焊材料基於環20的位置沉積在殼體中部10上，並沉積至壁，並沉積在先前製作的凹槽4內。此外，如圖10所示，它有利地以波浪8的形式沉積。
然後，將環20定位在硬焊材料上。
當進入爐子時，為了避免環20在熱膨脹期間移動，有利的是在環上放置一個重物，例如，等於殼體中部10的重物。當皮帶移動進入爐子時，該重物也使組件穩定。特別是，這種重量的存在使部件，尤其是鈦環，冷卻得更慢。藉由限制熱膨脹係數的影響，使組件承受的應力較小。還觀察到，在冷卻期間在5級鈦環上放置這樣的重物給予該環抗氧化的一些保護。
在離開爐子時，將硬焊的部件有利地放置在石墨架上以避免熱衝擊，並且附加的重量(也等於殼體中部的重量的數量級)用於在進行更快速的冷卻操作期間牢固地保持環在殼體中部。
這種底切凹槽的存在對於確保組件的黏附是必不可少的，因為否則，硬焊黏附到鈦，但是不能適當地黏附到陶瓷。如果沒有藉由凹槽4內部的硬焊材料5的重量執行錨固功能，則由於兩種材料的冷卻速度不同，當零件冷卻時，環會上升。這證實必須保持足夠緩慢的冷卻以最大程度地減小由熱膨脹施加的應力。還應注意，由於在鈦和氧化鋯基陶瓷之間形成薄界面層的硬焊材料，該環也趨於上升。
由於底切凹槽4，因為硬焊材料產生將兩個部件保持在一起的金屬支撐，該底切用作環的機械錨。
因此，可以在陶瓷殼體中部上硬焊5級鈦環，並在抗拔性測試中給出良好的結果。
方法的改進還涉及優化部件的尺寸，特別是減小鈦環的橫截面，其橫截面約為0.75mm至1.00mm的等級。
本發明還關於一種手錶1000，其包括藉由根據本發明的方法製作的至少一個結構和/或外部元件100。
簡而言之，本發明以一種用於可控氣氛硬焊的方法提供了一種用於5級鈦部件和氧化鋯基陶瓷部件之間的耐用、高品質的組件。它與其他技術的不同之處在於，在組裝步驟中以硬焊膏的形式添加了材料。此外，與常規技術相比，本發明確保組件具有更好的機械和熱性能。
在該方法中，硬焊膏與5級鈦熔化，這使得可以形成鈦部件的金屬延伸，但不與陶瓷反應。因此，所有的機械和熱阻性能都由硬焊及其在陶瓷部件中形成的凹槽內的錨固品質決定。
1:第一軸承表面 2:第二軸承表面 3:接合區域 4:第一凹槽 5:硬焊材料 6:頸部 7:第二凹槽 8:底部 10:第一陶瓷部件 11:第一基本表面 12:第二基本表面 13:交叉線 20:第二金屬合金部件 21:基本表面 22:基本表面 23:第二交叉線 100:結構和/或外部時計元件 1000:手錶
藉由參考圖式閱讀以下詳細描述，本發明的其他特徵和優點將變得明顯，其中： -[圖1]表示第一未處理部件的示意性平面圖，該第一未處理部件在此由氧化鋯基的陶瓷殼體中部形成。 -[圖2]示出了在徑向平面中的圖1的殼體中部的細節的示意性剖視圖，在第一軸承表面上用於容納第二部件，其在這裡是環。 -[圖3]以類似於圖2的方式表示了根據本發明的這種殼體中部的佈置，具有第一凹槽在其厚度中從第一軸承表面被設定後退。 -[圖4]以類似於圖3的方式示出了沉積在該凹槽中的硬焊。 -[圖5]以與圖2類似的方式表示第二部件，該第二部件在此由鈦合金環構成，尤其是5級鈦合金構成，並且包括第二軸承表面，該第二軸承表面被佈置為以與殼體中部的第一個支撐面至少部分互補地協作於接合區域中。 -[圖6]以與圖5類似的方式表示第二部件的變型製備，具有第二凹槽在其厚度中從第二軸承表面被設定後退。 -[圖7]以與圖4類似的方式表示該環在插入方向上的這種殼體中部上的插入，以形成準備好放入爐中的組件。 -[圖8]以類似於圖7的方式表示在硬焊操作之後在可控氣氛爐中，特別是在氬氣氣氛下進行的該組件。 -[圖9]以與圖1類似的方式表示這種殼體中部具有在角部附近的四個凹槽。 -[圖10]以類似於圖3的方式表示第一凹槽，該第一凹槽具有尖峰輪廓，相對於插入方向傾斜，並且也相對於形成殼體中部的第一軸承表面的基本表面傾斜，例如，雷射加工。 -[圖11]以與圖9類似的方式表示一旦硬焊材料沉積在凹槽中的情況下的殼體中部，並且在第一軸承表面上形成波形圖案。 -[圖12]以類似於圖10的方式表示第一凹槽，該第一凹槽具有圓形輪廓，相對於插入方向垂直，並且相對於形成殼體中部的第一軸承表面的基本表面之一傾斜，例如，在對底切進行機械加工之後。 -[圖13]以類似於圖10的方式表示具有輪廓的第一凹槽，其中頸部比凹槽的底部窄。 -[圖14]是表示包括根據本發明的方法製作的至少一個結構和/或外部元件的手錶的方塊圖。
1:第一軸承表面
2:第二軸承表面
3:接合區域
4:第一凹槽
5:硬焊材料
10:第一陶瓷部件
20:第二金屬合金部件
100:結構和/或外部時計元件
DI:插入方向

Claims (21)

  1. 一種用於硬焊第一陶瓷部件(10)和第二金屬合金部件(20)以製造結構和/或外部時計元件(100)的方法，其特徵在於，氧化鋯基的陶瓷被選擇用於該第一部件(10)，並且鈦合金被選擇用於該第二部件(20)，並且其中至少一個第一凹槽(4)被製造在該第一部件(10)內，在與該第二部件(20)的第二軸承表面(2)的接合區域(3)中相對於第一軸承表面(1)被設定後退，硬焊材料(5)被沉積在該第一軸承表面(1)上以及每個凹槽(4)內，該第二表面(2)被定位成與該第一表面(1)對準以形成組件，並且該組件在比該硬焊材料(5)的熔化溫度更高的溫度下在受控氣氛中被加熱，以形成在該接合區域(3)中該第二部件(20)到該第一部件(10)的該硬焊，並且進一步的特徵在於至少一個該第二軸承表面(2)在第二部件(20)中以正割於位於該接合區域(3)中的至少第二交叉線(23)上之至少兩個基本表面(21、22)製造。
  2. 根據請求項1之硬焊方法，其中該硬焊在包含在該第一部件(10)中的至少一個第一軸承表面(1)與包括在該第二部件(20)中的至少一個第二軸承表面(2)之間的至少一個接合區域(3)中進行，其至少部分地與該第一軸承表面(1)互補，並且其中該第一部件(10)和/或該第二部件(20)分別被佈置，是藉由使至少一個錐形鑽孔或狹縫或凹槽類型的第一凹槽(4)從其該第一軸承表面(1)和/或其該第二軸承表面(2)被設定後退，和/或分別使形成接收器的第二凹槽(7)從該第一軸承表面(1)和/或該第二軸承表面(2)被設定後退，該接收器被佈置成允許硬焊材料(5)穿透深入該第一部件(10)內，並促進在該第一部件(10)和/或該第二部件(20)內的該硬焊材料(5)的機械黏合，其中選擇至少與該鈦合金相容的該硬焊材料(5)，其中該第一部件(10)和/或該第二部件(20)是藉由將硬焊材料(5)沉積在該第一軸承表面(1)上以及從該第一軸承表面(1)被設定後退的每個該第一凹槽(4)內和/或分別在該第二軸承表面(2)上和從該第二軸承表面(2)被設定後退的每個該第二凹槽(7)內而製備，並且其中該第二部件(20)的該第二表面(2)被定位成與該第一部件(10)的該第一表面(1)對準以形成組件，並且該組件在受控氣氛中將被加熱到該硬焊材料(5)的該熔化溫度的溫度以上，以形成在該接合區域(3)中該第二部件(20)和該第一部件(10)之間的該硬焊。
  3. 根據請求項1之硬焊方法，其中該第一部件(10)藉由使該錐形鑽孔或狹縫或凹槽型的至少一個第一凹槽(4)從其該第一軸承表面(1)被設定後退而被佈置，該第一凹槽(4)形成接收器並從該第一軸承表面(1)被設定後退，該接收器被佈置成允許硬焊材料(5)穿透深入該第一部件(10)內，並促進該硬焊材料(5)在該第一部件(10)內的機械黏合，其中選擇至少與該鈦合金相容的該硬焊材料(5)，其中該第一部件(10)是藉由將硬焊材料(5)沉積在該第一軸承表面(1)上和在從該第一軸承表面(1)被設定後退的每個該凹槽(4)內而製備，其中該第二部件(20)的該第二表面(2)被位於與因此製備的該第一部件(10)的該第一表面(1)對準，以形成組件，並且其中該組件在受控的氣氛中被加熱到該硬焊材料(5)的熔化溫度以上的溫度，以形成在該接合區域中在該第二組件(20)和該第一組件(10)之間的該硬焊(3)。
  4. 根據請求項1至3中任一項之方法，其中該第一部件(10)的至少該第一軸承表面(1)被製造成具有至少兩個第一基本表面(11、12)，該至少兩個第一基本表面(11、12)正割在至少一個第一交叉線(13)上，並且至少一個該第一凹槽(4)被製造在該第一交叉線(13)上。
  5. 根據請求項2之方法，其中至少一個該第二凹槽(7)被製造在該第二交叉線(23)上。
  6. 根據請求項1之方法，其中在該硬焊操作期間，該組件被機械地保持緊壓在該接合區域(3)的附近。
  7. 根據請求項1之方法，其中該硬焊材料(5)以硬焊膏的形式被選擇，該硬焊材料(5)在壓力下被插入至少在每個該第一凹槽(4)中，並從該第一表面(1)被設定後退。
  8. 根據請求項1之方法，其中至少一個該第一凹槽(4)被製造在靠近該第一表面(1)具有頸部(6)，其中該頸部(6)的橫截面小於該第一凹槽(4)面向該第一表面(1)的底部(8)的橫截面，以在該硬焊操作之後形成將該第二部件(20)機械地保持至該第一部件(10)的鍵。
  9. 根據請求項1之方法，其中該第二部件(20)的單個插入方向(DI)被確定以用於其與該第一部件(10)的該對準，並且其中至少一個該第一凹槽(4)被製造傾斜或垂直於該插入方向(DI)。
  10. 根據請求項1之方法，其中該第二部件(20)的單個插入方向(DI)被確定以用於其與該第一部件(10)的該對準，並且其中該第一表面(1)和該第二表面(2)被製造有徑向間隙(JR)在它們之間，在該沉積硬焊材料(5)之前的該自由狀態下，其徑向間隙(JR)被包含在0.010 mm至0.040 mm之間的半徑處，垂直於該插入方向(DI)。
  11. 根據請求項10之方法，其中在該沉積硬焊材料(5)之前的該自由狀態下，該第一表面(1)和該第二表面(2)被製造有徑向間隙(JR)在它們之間，其徑向間隙(JR)被包含在0.015mm至0.025mm之間的半徑處，垂直於該插入方向(DI)。
  12. 根據請求項1之方法，其中選擇適合於在鋼上硬焊碳化鎢的硬焊材料作為該硬焊材料(5)。
  13. 根據請求項1之方法，其中該硬焊材料(5)被選擇為包括銅、錳和鎳，並且無鎘，具有超細的晶粒尺寸，並且包括用於在受控氣氛爐中的溫度在1000℃至1100℃之間硬焊的黏合劑。
  14. 根據請求項1之方法，其中至少一個該第一凹槽(4)在該第一陶瓷部件(10)的製造期間被製造。
  15. 根據請求項1之方法，其中至少一個該第一凹槽(4)被使用雷射完全加工或精加工。
  16. 根據請求項1之方法，其中至少一個該第一凹槽(4)被使用工具或砂輪完全地加工或機械地精加工。
  17. 根據請求項1之方法，其中複數個不連續的第一凹槽(4)在該接合區域(3)中被形成。
  18. 根據請求項1之方法，其中選擇該鈦合金等級5的鈦，根據ASTM F136的％的含量，其包括從0.00到0.08 C、從0.0到0.3 Fe、從0.0000到0.0125 H、從0.00至0.05 N、從0.0至0.2 O、從5.50至6.75 Al、從3.5至4.5 V、從0.0至0.1 OE(每個其他元素)，從0.0至0.4 TO(所有其他元素)，其餘為鈦。
  19. 根據請求項1之方法，其中氧化鋯基的陶瓷被選擇以含有： -單獨或組合地選自氧化釔、氧化鎂和氧化鈣的氧化物的群組之至少一個穩定劑； -旨在產生玻璃相，並單獨或組合地選自氧化矽、氧化鋁、氧化鋰和氧化釔的群組之至少一種元素； -用作顏料的氧化物粉末； -和形成剩餘物至100重量％之氧化鋯粉末。
  20. 根據請求項19之方法，其中該氧化鋯基的陶瓷被選擇以含有： -3至20重量％的至少一個穩定劑，其單獨或組合地選自包含氧化釔、氧化鎂和氧化鈣的氧化物的群組； -0.1至5重量％的旨在產生玻璃相的至少一個元件，其單獨或組合地選自包含氧化矽、氧化鋁、氧化鋰和氧化釔的群組； -1至10重量％的用作顏料的氧化物粉末； -和形成剩餘物至100重量％之氧化鋯粉末。
  21. 一種手錶，包含藉由根據請求項1之方法製作的至少一個結構元件和/或外部元件。
TW108140066A 2018-12-14 2019-11-05 用於針對鐘錶或珠寶硬焊鈦合金零件與氧化鋯基的陶瓷零件之方法 TWI710543B (zh)