RU2496744C1 - Crude mixture for making porcelain - Google Patents
Crude mixture for making porcelain Download PDFInfo
- Publication number
- RU2496744C1 RU2496744C1 RU2012121113/03A RU2012121113A RU2496744C1 RU 2496744 C1 RU2496744 C1 RU 2496744C1 RU 2012121113/03 A RU2012121113/03 A RU 2012121113/03A RU 2012121113 A RU2012121113 A RU 2012121113A RU 2496744 C1 RU2496744 C1 RU 2496744C1
- Authority
- RU
- Russia
- Prior art keywords
- crude mixture
- porcelain
- quartz
- kaolin
- feldspar
- Prior art date
Abstract
Description
Изобретение относится к области технологии силикатов, в частности, к составам сырьевых смесей для изготовления фарфоровых предметов декоративно-художественного и хозяйственно-бытового назначения.The invention relates to the field of technology of silicates, in particular, to compositions of raw mixtures for the manufacture of porcelain for decorative, artistic and household purposes.
Известна сырьевая смесь для изготовления фарфора следующего состава, мас, %: глинистые материалы (каолин) 20,0-45,0; полевой шпаг 8,0-22,0, кварц 9,0-20,0; костяная зола 20,0-60,0 [1].Known raw mix for the manufacture of porcelain of the following composition, wt.%: Clay materials (kaolin) 20.0-45.0; field sword 8.0-22.0, quartz 9.0-20.0; bone ash 20.0-60.0 [1].
Задачей изобретения является повышение морозостойкости изделий, полученных из сырьевой смеси.The objective of the invention is to increase the frost resistance of products obtained from a raw mix.
Технический результат достигается тем, что сырьевая смесь для изготовления фарфора, содержащая каолин, полевой шпат, кварц, костяную золу, дополнительно включает циркон при следующем соотношении компонентов, мас.%; каолин 28,0-32,0; полевой шпат 24,0-26,0; кварц 24,0-26,0; костяная зола 13,0-15,0; циркон 5,0-7,0.The technical result is achieved in that the raw mixture for the manufacture of porcelain, containing kaolin, feldspar, quartz, bone ash, further includes zircon in the following ratio of components, wt.%; kaolin 28.0-32.0; feldspar 24.0-26.0; quartz 24.0-26.0; bone ash 13.0-15.0; zircon 5.0-7.0.
В таблице приведены составы сырьевой смеси для изготовления фарфора.The table shows the composition of the raw mix for the manufacture of porcelain.
Для приготовления сырьевой смеси рекомендуется использовать каолин Просяновекого месторождения, полевой шпат и кварц Чупинского месторождения [2].To prepare the raw mix, it is recommended to use kaolin of the Prosyanovek deposit, feldspar and quartz of the Chupinsky deposit [2].
Компоненты дозируют в требуемых количествах. В шаровую мельницу загружают полевой шпат, кварц, циркон, волластонит, заливают воду и проводят измельчение компонентов в течение 6-8 часов. Затем в мельницу добавляют каолин, костяную золу и измельчают еще в течение 2-3 часов. Степень измельчения готового шликера должна соответствовать остатку не более 2% на сите 0056. Обезвоживание суспензии до получения коржей с влажностью 20-25% производят на фильтрах-прессах периодического действия (в качестве фильтровальных полотен могут быть использованы ткани из синтетического волокна). Обезвоженную массу проминают в вакуум-прессах после чего ей дают вылежаться в массохранилище в условиях повышенной влажности не менее 10 сут.The components are dosed in the required amounts. Feldspar, quartz, zircon, wollastonite are loaded into a ball mill, water is poured and components are ground for 6-8 hours. Then, kaolin, bone ash are added to the mill and crushed for another 2-3 hours. The degree of grinding of the finished slurry should correspond to a residue of no more than 2% on sieve 0056. Dehydration of the suspension to obtain cake layers with a moisture content of 20-25% is carried out on batch filter presses (synthetic fiber fabrics can be used as filter sheets). The dehydrated mass is washed in a vacuum press, after which it is allowed to mature in the mass storage in conditions of high humidity for at least 10 days.
Из полученной фарфоровой массы пластическим способом формуют изделия, которые сушат при температуре до влажности не более 6% и при температуре 1280°С проводят первый обжиг. Поверхность изделий декорируют керамическими красками, наносят слой прозрачной глазури и при температуре 1160°С проводят второй обжит.From the obtained porcelain mass, plastic products are molded that are dried at a temperature of not more than 6% humidity and carry out the first firing at a temperature of 1280 ° C. The surface of the products is decorated with ceramic paints, a layer of transparent glaze is applied, and at a temperature of 1160 ° C a second habitat is carried out.
Источники информацииInformation sources
1. Мороз И.И. Фарфор, фаянс, майолика. - Киев: Технша, 1975. - С.290.1. Frost II Porcelain, faience, majolica. - Kiev: Technsha, 1975. - P.290.
2. Справочник мастера-фарфориста /И.М. Бердичевский и др. - М.: Легпромбытиздат, 1992. - С.41, 48, 52.2. Reference master porcelain / I.M. Berdichevsky et al. - M.: Legprombytizdat, 1992 .-- P.41, 48, 52.
Claims (1)