RU2145928C1

RU2145928C1 - Method for mosaic or ornamental facing of surface with natural stone tile material

Info

Publication number: RU2145928C1
Application number: RU98116947A
Authority: RU
Inventors: В.Ж. Закарян
Original assignee: Закарян Вануш Жоржикович
Priority date: 1998-08-28
Filing date: 1998-08-28
Publication date: 2000-02-27

Abstract

FIELD: construction industry. SUBSTANCE: method involves using tiles produced by sawing of cobblestone as material for making pieces of patterns or ornament. EFFECT: increased efficiency by improved quality of facing. 2 cl

Description

Изобретение относится к области строительно-отделочных работ, преимущественно к мозаичной облицовке стен, полов и т.п. помещений и зданий, в частности мозаичной облицовке поверхностей плитами из камня типа гранит. The invention relates to the field of construction and finishing works, mainly to mosaic facing of walls, floors, etc. rooms and buildings, in particular mosaic facing of surfaces with slabs of stone such as granite.

Известна облицовка полов, стен, ступеней и площадок лестниц и т.п. плитами из мрамора, гранита, базальта и других видов природного камня, получаемыми распиловкой блоков-заготовок, выпиливаемых непосредственно из массивов горных пород, с приданием плитам гладкой матовой, шлифованной, полированной и другой поверхности путем распиловки плит на облицовочные элементы определенной формы и размера, нанесения их на предварительно подготовленную поверхность на подстилочно-удерживающий слой, например, цемента, заделки швов и чистовой поверхностной обработки [1]. Использование плит из различного материала разного цвета позволяет исключить однородность облицованной поверхности за счет вкраплений плиток различного материала в виде окантовок, полос и т.п. Lining of floors, walls, steps and platforms of stairs, etc. is known. slabs made of marble, granite, basalt and other types of natural stone obtained by sawing blocks of workpieces sawed directly from rock masses, giving the slabs a smooth matte, polished, polished and other surface by sawing the slabs on the facing elements of a certain shape and size, applying them on a pre-prepared surface on a litter-holding layer, for example, cement, grouting and finishing surface treatment [1]. The use of plates of various materials of different colors eliminates the uniformity of the lined surface due to interspersed tiles of various materials in the form of edging, stripes, etc.

Недостатками известного способа являются:
- трудоемкость и высокие затраты на получение плит из заготовок, выпиливаемых из массива горного природного камня;
- низкие возможности в плане реализации дизайнерско-художественного замысла;
- непригодность для выполнения рисунка, орнамента и т.п., необходимых для мозаичной облицовки поверхности.The disadvantages of this method are:
- the complexity and high costs of obtaining plates from billets cut from an array of mountain natural stone;
- low opportunities in terms of the implementation of the design and art design;
- unsuitability for drawing, ornament, etc., necessary for mosaic surface coating.

Известен способ изготовления мозаичных изделий, при котором блоки различного материала распиливают на плиты разного цвета, которые укладывают в пакеты, из которых выпиливают повторяющиеся основные и вспомогательные элементы рисунка или орнамента, полученные элементы укладывают на смазанную подложку, совмещают плоские элементы разного цвета в общий рисунок, наносят промежуточный фон или отсутствующие элементы, пластины нагревают до 350^oC, заливают швы висмутом и производят чистовую обработку поверхности [2]. Способ позволяет ускорить процесс подготовки элементов рисунка.A known method of manufacturing mosaic products, in which blocks of various materials are sawn into plates of different colors, which are laid in bags, from which the repeating main and auxiliary elements of a pattern or ornament are sawed, the resulting elements are laid on a greased substrate, combine flat elements of different colors into a common pattern, apply an intermediate background or missing elements, the plates are heated to 350 ^o C, fill the seams with bismuth and finish the surface [2]. The method allows to accelerate the process of preparing the elements of the picture.

Недостатками известного способа являются:
- непригодность способа для мозаичной облицовки поверхностей типа стен, пола и т.п. Способ предназначен для изготовления изделий типа мозаичных плит для витражей и т.п.;
- трудоемкость и высокие затраты процесса получения плиточного материала из заготовок горного природного камня;
- сложность и ограниченные возможности подбора различных по цвету, структуре и природному узору материалов, необходимых для получения качественного мозаичного изделия.The disadvantages of this method are:
- unsuitability of the method for mosaic facing surfaces such as walls, floors, etc. The method is intended for the manufacture of products such as mosaic tiles for stained glass, etc .;
- the complexity and high costs of the process of obtaining tile material from blanks of mountain natural stone;
- the complexity and limited ability to select materials of different colors, structures and natural patterns that are necessary to obtain a high-quality mosaic product.

Известен способ изготовления мозаичных плит из отходов мрамора, гранита и других природных материалов, включающий выполнение из отходов отдельных элементов мозаики, набор мозаичной плиты по определенному орнаменту, укладку скомплектованной плиты в металлическую форму, обжим плиты, нанесение на лицевую поверхность в местах швов клея с последующей полимеризацией и чистовой обработкой [3]. A known method for the manufacture of mosaic tiles from waste marble, granite and other natural materials, including the execution of the waste of individual mosaic elements, a set of mosaic tiles according to a specific ornament, laying the completed plate in a metal mold, crimping the plate, drawing on the front surface at the joints of glue with subsequent polymerization and finishing [3].

Использование отходов природного камня для формирования плит уменьшает затраты на материал. Using natural stone waste to form slabs reduces material costs.

Недостатками известного способа являются:
- непригодность для прямой мозаичной облицовки поверхности;
- трудоемкость процесса подбора и вырезки элементов мозаики;
- ограниченные возможности подбора цветовых оттенков, естественного узора и структуры камня, связанные с использованием отходов плит, полученных из одних и тех же монолитных горных пород.The disadvantages of this method are:
- unsuitability for direct mosaic facing;
- the complexity of the process of selecting and cutting mosaic elements;
- limited selection of color shades, natural pattern and stone structure associated with the use of waste plates obtained from the same monolithic rocks.

Известен наиболее близкий к заявляемому техническому решению, выбранный в качестве ближайшего аналога способ наборно-мозаичной и декоративной облицовки поверхностей, в частности пола и стен помещений, боем плиток разного цвета природного камня типа мрамора, гранита и т.п., а также смальты, керамической плитки и т.п. [4]. При этом по рисунку художника подбирают, выпиливают и обрабатывают с лицевой стороны составные элементы мозаичной облицовки. Снятый с оригинала на кальку рисунок, орнамент и т.п. наносят на предварительно наложенный на поверхность слой гипсового вяжущего. При этом по контурам рисунка на кальке шилом накалывают отверстия, по которым рисунок припорашивают порошком угля или сухого пигмента. После этого гипс удаляют и элементы мозаичной облицовки по имеющемуся контурному рисунку наносят на облицуемую поверхность с помощью цементного раствора или специальной мастики. Полученное мозаичное изображение подвергают дополнительной поверхностной обработке, а швы окрашивают. Known closest to the claimed technical solution, selected as the closest analogue, the method of typesetting-mosaic and decorative cladding of surfaces, in particular floors and walls of rooms, by fighting tiles of different colors of natural stone such as marble, granite, etc., as well as smalt, ceramic tiles, etc. [4]. Moreover, according to the artist’s drawing, the components of the mosaic cladding are selected, sawn and processed from the front. Drawing, ornament, etc. taken from the original on tracing paper applied to a layer of gypsum binder previously applied to the surface. At the same time, holes are pierced along the contours of the drawing on tracing paper with an awl, through which the pattern is numbed with coal powder or dry pigment. After this, the gypsum is removed and the elements of the mosaic cladding are applied to the surface to be coated using the existing contour drawing using cement mortar or special mastic. The resulting mosaic image is subjected to additional surface treatment, and the seams are stained.

Недостатками известного способа являются:
- трудоемкость процесса подбора, вырезки и обработки элементов мозаики;
- недостаточно высокие художественно-эстетические качества мозаичной облицовки, связанные с ограниченными возможностями подбора требуемых цветовых оттенков, естественного узора и кристаллической структуры природных камней, полученных из одних и тех же монолитных горных пород;
- достаточно высокие затраты на материалы, несмотря на частичное использование боя плит.The disadvantages of this method are:
- the complexity of the process of selection, cutting and processing of mosaic elements;
- insufficiently high artistic and aesthetic qualities of mosaic cladding, associated with limited possibilities of selecting the required color shades, natural pattern and crystal structure of natural stones obtained from the same monolithic rocks;
- fairly high costs for materials, despite the partial use of battle plates.

Задачей изобретения является повышение художественно-эстетических показателей мозаичной облицовки, снижение трудоемкости изготовления элементов мозаичного рисунка или орнамента и снижение издержек на облицовочный материал. The objective of the invention is to increase the artistic and aesthetic indicators of mosaic cladding, reducing the complexity of manufacturing elements of a mosaic pattern or ornament, and reducing the cost of facing material.

Поставленная задача решается за счет того, что при использовании признаков, характеризующих известный способ мозаичной или декоративной облицовки поверхности плиточным материалом из природного камня, включающего распиловку заготовок камня на отдельные плиты, обработку лицевой поверхности плит, подбор и выполнение из плит элементов мозаики или декора, по форме, размеру, кристаллической структуре и т.п. соответствующих элементам предварительно выполненного мозаичного рисунка, нанесение контуров элементов рисунка на предварительно подготовленную облицовываемую поверхность, наложение и закрепление элементов мозаики на облицовываемой поверхности с помощью подстилочно-удерживающего материала и чистовую обработку поверхности, в соответствии с изобретением в качестве материала для элементов рисунка или орнамента используют плиты, получаемые распиловкой камня-булыжника. The problem is solved due to the fact that when using the signs characterizing the known method of mosaic or decorative facing of the surface with natural stone tile material, including sawing stone blanks into individual plates, processing the front surface of the plates, selecting and performing mosaic or decor elements from the plates, shape, size, crystal structure, etc. corresponding to the elements of the pre-completed mosaic pattern, drawing the contours of the elements of the pattern on the pre-prepared facing surface, applying and fixing the mosaic elements on the surface to be coated using the litter-holding material and finishing the surface, in accordance with the invention, plates are used as the material for the drawing or ornament elements obtained by sawing up cobblestone.

Предпочтительный вариант способа мозаичной или декоративной облицовки поверхности предполагает формирование рисунка или орнамента из плиток камня-булыжника разного размера с сохранением их контурной формы и использование свободного пространства между элементами рисунка или орнамента в качестве общего фона. Камни-булыжники при их распиловке на плитки с последующей шлифовкой и полировкой дают материал для облицовки поверхности, имеющий самые различные цветовые оттенки, различный оригинальный и выразительный природный узор на полированной поверхности, несвойственный плитам из монолитного горного камня, а также красивую кристаллическую структуру, что позволяет без использования дополнительных природных материалов формировать оригинальный мозаичный рисунок с многообразием цветов и цветовых оттенков. The preferred variant of the method of mosaic or decorative surface cladding involves the formation of a pattern or ornament from tiles of cobblestone of different sizes while maintaining their contour shape and using the free space between the elements of the pattern or ornament as a general background. Cobble stones, when sawn into tiles, followed by grinding and polishing, give the material for surface cladding, which has a variety of color shades, various original and expressive natural patterns on the polished surface, unusual for slabs of monolithic mountain stone, as well as a beautiful crystalline structure, which allows without using additional natural materials to form an original mosaic pattern with a variety of colors and color shades.

Распиловка камней-булыжников позволяет получать плитки различного размера оригинальной овальной формы, что дает возможность комплектовать рисунок или орнамент без резки плиток на фигурные элементы. При этом появляющееся свободное пространство может быть использовано для выполнения общего фона, создающего контраст с элементами рисунка или орнамента и повышающего выразительность композиции в целом. Sawing of cobblestone stones allows you to get tiles of various sizes of the original oval shape, which makes it possible to complete a picture or ornament without cutting tiles into curly elements. In this case, the emerging free space can be used to perform a general background that creates a contrast with the elements of a picture or ornament and increases the expressiveness of the composition as a whole.

Полученные при распиловке камней-булыжников плитки имеют конусообразно расходящиеся боковые стороны, что позволяет формировать рисунок или орнамент как с широкой, так и узкой лицевой поверхностью плиток. При формировании рисунка с узкой лицевой поверхностью может быть получено оригинальное рельефное изображение с тонким слоем образующего фон материала, что расширяет дизайнерско-художественные возможности выполнения облицовки. The tiles obtained during sawing of cobblestone stones have conically diverging sides, which allows you to form a pattern or ornament with both a wide and narrow front surface of the tiles. When forming a pattern with a narrow front surface, an original embossed image with a thin layer of the material forming the background can be obtained, which expands the design and artistic capabilities of the cladding.

Камень-булыжник практически не имеет стоимости, т.к. лишь засоряет сельхозугодья и культурно-осваиваемые площади, что до минимума снижает затраты на облицовочные работы. Cobblestone has almost no value, because it only clogs farmland and cultivated areas, which minimizes the cost of facing work.

Более подробно заявляемый способ мозаичной или декоративной облицовки поверхности рассматривается на примере его выполнения. In more detail, the claimed method of mosaic or decorative surface lining is considered on the example of its implementation.

В соответствии с заявляемым техническим решением камни-булыжники различного размера распиливают с помощью известных технических средств, например многодискового камнераспиловочного станка СМР-017, на плитки определенной толщины, которые с помощью известных средств подвергают с лицевой стороны шлифованию, полированию, обработке ультразвуком т.п. с получением требуемой гладкой глянцевой или матовой поверхности с проявившимся природным узором. Из полученных плиток различного размера, цвета, цветового оттенка, а также с различными узорами и кристаллической структурой по предварительно подготовленному рисунку на специальном столе формируют мозаичный рисунок или орнамент. На выровненную облицуемую поверхность с помощью кальки наносят рисунок или орнамент. Формирующие мозаичный рисунок плитки с помощью подстилочно-удерживающего материала, в частности цементно-песочного раствора, наносят на облицуемую поверхность по предварительно нанесенному рисунку. После нанесения мозаичного рисунка или орнамента имеющиеся между мозаичными элементами свободные пространства заделывают образующим фон материалом, в частности раствором смешанной с цементом крошки, полученной при распиловке. После затвердевания раствора мозаичную или декоративную облицовку с помощью известных средств подвергают чистовой обработке. In accordance with the claimed technical solution, cobblestones of various sizes are cut using known technical means, for example, a multi-disk stone sawing machine СМР-017, onto tiles of a certain thickness, which are subjected to grinding, polishing, and ultrasonic processing from the front side using known methods. with obtaining the required smooth glossy or matte surface with a natural pattern. From the obtained tiles of various sizes, colors, shades of color, as well as with various patterns and crystal structure according to a previously prepared drawing, a mosaic pattern or ornament is formed on a special table. A pattern or ornament is applied to the leveled surface to be coated with tracing paper. The tiles forming the mosaic pattern with the help of a litter-holding material, in particular cement-sand mortar, are applied to the surface to be coated according to the previously applied pattern. After applying the mosaic pattern or ornament, the available spaces between the mosaic elements are covered with the material forming the background, in particular with a solution of crumbs mixed with cement obtained during sawing. After the solution has solidified, the mosaic or decorative lining is finished using known means.

Полученная описанным способом мозаичная или декоративная облицовка отличается высокими художественно-эстетическими показателями, имеет по сравнению с облицовкой плитками горного камня большое разнообразие цветовых оттенков и оригинальные, четко проступающие природные узоры на плитках. The mosaic or decorative lining obtained in the described way is distinguished by high artistic and aesthetic indicators, has a wide variety of color shades and original, clearly visible natural patterns on the tiles compared to the lining of mountain stone tiles.

Заявляемое техническое решение полностью решает задачу, стоящую перед изобретением. The claimed technical solution completely solves the problem facing the invention.

Заявляемое техническое решение с характеризующими его отличительными признаками на настоящее время в Российской Федерации и за границей не известно и отвечает требованиям критерия "новизна". The claimed technical solution with its distinguishing features currently in the Russian Federation and abroad is not known and meets the requirements of the criterion of "novelty."

Заявляемое техническое решение является оригинальным, не вытекает очевидным образом из существующего уровня техники, дает неожиданный эффект и отвечает требованиям критерия "изобретательский уровень". The claimed technical solution is original, does not follow obviously from the existing level of technology, gives an unexpected effect and meets the criteria of the "inventive step".

Заявляемый способ мозаичной или декоративной облицовки поверхности может быть реализован промышленным способом для облицовки стен, полов и т.п. с использованием известных технических средств, материалов и технологий и отвечает требованиям критерия "промышленная применимость". The inventive method of mosaic or decorative surface lining can be implemented industrially for wall, floor, etc. using well-known technical means, materials and technologies and meets the requirements of the criterion of "industrial applicability".

Библиографические данные
[1] В. И. Малин и др. Наружная и внутренняя облицовка зданий природным камнем. М.: Высшая школа, 1991, с. 32-39.Bibliographic data
[1] V. I. Malin et al. External and internal cladding of buildings with natural stone. M .: Higher school, 1991, p. 32-39.

[2] Патент РФ N 2019422, МПК: B 44 C 1/28, публ. 15.09.94. Бюлл. N 17. [2] RF Patent N 2019422, IPC: B 44 C 1/28, publ. 09/15/94. Bull. N 17.

[3] А.с. СССР N 697356, МКИ: B 44 C 1/28, публ. 1979. Бюлл. N 42. [3] A.S. USSR N 697356, MKI: B 44 C 1/28, publ. 1979. Bull. N 42.

[4] Справочник молодого облицовщика, плиточника и мозаичника. М.: Высшая школа, 1988, с. 170-171. [4] Handbook of the young tiler, tiler and mosaic. M .: Higher school, 1988, p. 170-171.

Claims

1. The method of mosaic or decorative surface lining with natural stone tile material, including sawing stone blanks into finishing plates, processing the front surface of the plates, selecting and making mosaic or decor elements from the plates in shape, size, color, crystal structure and the corresponding elements previously made mosaic drawing, drawing the contours of drawing elements on a previously prepared facing surface, applying and fixing mosaic elements on the facing surface with the help of litter-retaining material and surface finishing, characterized in that as the material for the elements of the pattern or ornament use the plates obtained by sawing stone cobblestones.

2. The method of mosaic or decorative surface lining according to claim 1, characterized in that the pattern or ornament is formed from cobblestone tiles of different sizes while maintaining their contour shape, and the free space between the elements of the pattern or ornament is used as a general background.