JP5061473B2 - Nitride semiconductor devices - Google Patents

Description

  The present invention relates to a semiconductor device using a nitride-based semiconductor, such as a Schottky barrier diode, a pn junction diode, a pin junction diode, and a vertical transistor.

  Patent Document 1 describes a semiconductor element that can stabilize the operation of the element. In this semiconductor element, the n-type GaN substrate has a region where dislocations are concentrated on at least a part of the back surface. Each nitride-based semiconductor layer is formed on the surface of the n-type GaN substrate. The insulating film is formed on a region where dislocations are concentrated. The n-side electrode is formed so as to be in contact with the region on the back surface of the n-type GaN substrate other than the region where dislocations are concentrated.

  In the GaN-based semiconductor laser device of Patent Document 2, the p-side electrode and the n-side electrode are provided on the laminated structure side. The semiconductor laser device uses a GaN single crystal substrate instead of a sapphire substrate, and directly forms a stacked structure of GaN-based compound semiconductor layers on the GaN single crystal substrate without providing a GaN-ELO structure layer. . The GaN single crystal substrate has a continuous band-shaped core part having a width of 10 micrometers, and the distance between the core part and the core part is about 400 micrometers. The laser stripe, the pad metal of the p-side electrode, and the n-side electrode are provided in a laminated structure on a region other than the core portion of the GaN single crystal substrate. The horizontal distance between the side edge portion of the pad metal and the outer peripheral edge of the core portion is 95 micrometers, and the horizontal distance between the n-side electrode and the outer peripheral edge of the core portion is also 95 micrometers. According to the GaN-based semiconductor light emitting device, the current leakage can be reduced while being formed on the GaN single crystal substrate.

The nitride-based compound semiconductor element of Patent Document 3 uses a semiconductor substrate having periodic high-density defect regions. In the GaN-based semiconductor laser device, the stacked structure of the n-type GaN layer, the n-type AlGaN cladding layer, the active layer, the Mg-doped p-type GaN optical waveguide layer, the p-type AlGaN cladding layer, and the p-type GaN contact layer is an n-type GaN substrate. It is provided above. A through hole having a diameter of 50 micrometers is provided in the core portion of the high-density defect region of the GaN substrate, and is buried with a high resistance layer, for example, a SiO ₂ layer or a SiN _X layer. The n-side electrode is provided so as to be positioned between the through holes, and the p-side electrode is provided on the n-side electrode. Since the high resistance layer becomes the current blocking layer, the region where the current is injected is limited to the region sandwiched between the high resistance layers. The active region of the GaN-based semiconductor laser device is a region sandwiched between the extension lines of the high resistance layer in the active layer.

  In the nitride-based semiconductor laser device of Patent Document 4, an n-type AlGaN cladding layer, an n-type GaN first light guide layer, an InGaN active layer, a p-type InGaN layer, a second light guide layer, a p-type AlGaN cladding layer, and p The laminated structure having the type GaN contact layer is provided on the n-type GaN substrate. The upper layer portion of the p-type cladding layer and the p-type contact layer are formed as a ridge stripe portion extending in a ridge stripe shape in one direction. Both sides of the ridge stripe portion are covered with an insulating film, and the ridge stripe portion is located between the high-density defect regions. The p-side electrode extends along the ridge stripe portion between the high-density defect regions. The n-side electrode is formed as an electrode layer in which a part of the n-side electrode is cut out from an electrode layer provided on almost the entire back surface of the GaN substrate so as not to contact the high-density defect region. According to this, the generation of leakage current can be suppressed by using a semiconductor substrate that periodically has a high-density defect region in a low-density defect region.

  In the nitride semiconductor laser element of Patent Document 5, the stacked structure of the group III nitride semiconductor and the electrodes provided on the upper surface of the stacked structure and the lower surface of the substrate are arranged as follows. The laser light waveguide region is provided at a position off the dislocation concentration region penetrating the substrate in the vertical direction. The electrodes provided on the upper surface of the laminated structure and the lower surface of the substrate are provided at positions dislocated from above and below the dislocation concentration region. This nitride semiconductor laser device has excellent operating characteristics and a long laser oscillation life.

  The light-emitting element structure or element structure of Patent Document 6 is provided on a nitride-based III-V group compound semiconductor substrate 1. In the nitride-based III-V group compound semiconductor substrate, a plurality of second dislocation densities having a second average dislocation density higher than the first average dislocation density in the first region made of a crystal having the first average dislocation density. The areas are regularly arranged. When manufacturing these semiconductor light emitting devices or semiconductor devices, element regions are defined on the nitride-based III-V compound semiconductor substrate so that the second regions are not substantially included, or light emitting regions or active regions are formed. So that the second region is not substantially included. As a result, a semiconductor light-emitting element having good characteristics such as light emission characteristics and high reliability and a long life and a semiconductor element having good characteristics and high reliability and a long life are realized.

  In Patent Document 7, using a nitride semiconductor substrate in which low dislocation density regions and high dislocation density regions are alternately present in a short period, a nitride semiconductor light emitting diode (LED) having a large area including a plurality of both regions is included. ) Form a chip. The current is concentrated in the low dislocation density region by the current barrier layer provided under the p-electrode. The current barrier layer is formed of AlGaN or the like that is in Schottky junction with the p electrode. According to this nitride semiconductor light emitting diode, while using a substrate in which low dislocation density regions and high dislocation density regions exist alternately like an ELOG growth substrate, a sufficient light emission area can be obtained, and quantum efficiency and linearity can be obtained. Excellent.

The GaN-based field effect transistor of Patent Document 8 has a stacked structure in which a plurality of GaN epitaxial crystal layers are stacked. A gate electrode and a source electrode (operation electrode) are arranged on the surface of the laminated structure, and a drain electrode is arranged on the back surface. In the stacked structure of this GaN-based field effect transistor, the electric field concentration region during operation has a lower dislocation density than other regions. According to this GaN-based field effect transistor, since the GaN crystal in the region where the electric field concentrates during operation is of high quality, excellent breakdown voltage is exhibited.
JP 2004-260152 A Japanese Patent Laid-Open No. 2004-23050 JP 2003-229623 A JP 2003-229638 A JP 2003-273470 A JP 2003-124572 A JP 2002-33512 A JP 2001-230410 A

  Patent Documents 1 to 7 describe semiconductor optical devices such as semiconductor lasers. The structure of the semiconductor optical device is different from that of a power semiconductor device such as a Schottky barrier diode, a pn junction diode, a pin junction diode, or a vertical transistor. The operation of the semiconductor optical device is different from the operation of these power semiconductor devices.

  There is a GaN substrate called a random core substrate in which high defect density regions (core portions) are randomly distributed and the defect density is not controlled. When a semiconductor multilayer structure is formed on this GaN substrate, dislocations in the GaN substrate become threading dislocations and are taken over by the semiconductor multilayer structure. For this reason, the position of the high defect density region of the semiconductor multilayer structure is also random. When an electron transit element such as a pn junction diode, a pin diode, or a MIS field effect transistor is formed on this region, threading dislocations become a leakage current path. Leakage current causes deterioration and variation in device performance, and affects long-term reliability of the device. In particular, in a high power vertical device, electrons travel in the vertical direction when the electronic device is on. A high reverse bias is applied to threading dislocations when the electronic device is off. Due to this reverse bias, electric field concentration occurs in the core portion having a low resistance. This electric field concentration causes an increase in loss and breakdown voltage failure, such as a large reverse leakage current flowing from the front electrode to the back electrode, causing breakdown breakdown.

  In order to avoid this, a GaN substrate in which the position of the core part is controlled can be used. A semiconductor layer can be grown on the GaN substrate to form a semiconductor layer with a controlled core position on the GaN substrate. In addition, a semiconductor layer in which the position of the core portion is controlled can be formed over a different substrate such as a silicon substrate. On these substrates, electronic devices can be selectively created in each of the low defect density regions. In the substrate, the low defect density region and the core portion are arranged as follows. For example, the low defect density region is surrounded by several core portions around it. Alternatively, the low defect density region is sandwiched between the core portions.

  However, since the low defect density region is not a single-connected region, the use of this GaN substrate is not only a limitation in the device layout design, but also makes it difficult to produce a large-area device. For example, in a stripe core substrate in which the core portion extends in a stripe shape, an element can be formed in each of the low dislocation regions of the stripe core substrate, but it is difficult to dispose the element across the core portion. An electric traveling element with high current and high output cannot be realized.

  The present invention has been made in view of such circumstances, and a Schottky barrier diode, a pn junction diode having a structure capable of reducing the influence of the arrangement of the core portion having a high threading dislocation density and increasing the element area, An object of the present invention is to provide a semiconductor device using a pin junction diode, a vertical transistor, and a nitride semiconductor.

According to one aspect of the present invention, a semiconductor device using a nitride-based semiconductor is a Schottky barrier diode, which includes (a) a conductive substrate having a front surface and a back surface, and (b) a first threading dislocation density. A first region having a small threading dislocation density; a second region having a threading dislocation density greater than the first threading dislocation density; and a third region having a threading dislocation density smaller than the first threading dislocation density. A first conductivity type gallium nitride based semiconductor layer provided on the surface of the conductive substrate; and (c) the first and third gallium nitride based semiconductor layers of the first conductivity type gallium nitride based semiconductor layer. First and second electrodes each forming a Schottky junction in the region; and (d) provided on the first conductivity type gallium nitride based semiconductor layer and the first and second electrodes. 2 electric (E) a protective insulating film having first and second openings respectively located on the protective insulating film; and (e) provided on the protective insulating film and passing through the first and second openings to the first and second electrodes. A wiring conductor to be connected; (f) a first insulating layer provided between the second region of the first conductivity type gallium nitride based semiconductor layer and the protective insulating film; and (g) the conductive material. A second electrode layer provided on the back surface of the conductive substrate, wherein the second region of the first conductivity type gallium nitride based semiconductor region includes the first region and the third region. It is provided in between. The first region of the first conductivity type gallium nitride based semiconductor layer is provided for a first element, and the third region of the first conductivity type gallium nitride based semiconductor layer is for a second device. The semiconductor device is a Schottky barrier diode including the first and second elements.

  According to the Schottky barrier diode, the first element of the Schottky barrier diode is provided in the first region of the first conductivity type gallium nitride semiconductor layer, and the first element of the first conductivity type gallium nitride semiconductor layer is provided. In the region 3, a second element of a Schottky barrier diode is provided. The first and second elements include first and second electrodes that form Schottky junctions in the first and third regions, respectively, and the first and second electrodes do not extend over the insulating layer. The protective insulating film protects the edges of the first and second electrodes and the surface of the first conductivity type gallium nitride based semiconductor layer. The first and second electrodes are connected to each other through a wiring conductor. Although the second region is provided between the first region and the third region, the first insulating layer is provided between the second region and the wiring conductor. The second region of the first gallium nitride based semiconductor layer is not electrically connected. Even when a reverse bias is applied to the Schottky barrier diode, a high electric field is not directly applied to the second region of the first-conductivity-type gallium nitride based semiconductor layer, which is caused by the electric field in the second region. A decrease in dielectric breakdown voltage can be suppressed.

According to another aspect of the present invention, the semiconductor device using a nitride-based semiconductor is a pn junction diode, which includes (a) a conductive substrate having a front surface and a back surface, and (b) a first through-hole. A first region having a threading dislocation density smaller than the dislocation density; a second region having a threading dislocation density larger than the first threading dislocation density; and a first region having a threading dislocation density smaller than the first threading dislocation density. A first conductivity type gallium nitride based semiconductor layer provided on the surface of the conductive substrate, and (c) a first threading dislocation density lower than a second threading dislocation density. A second region having a threading dislocation density larger than the second threading dislocation density, and a third region having a threading dislocation density smaller than the second threading dislocation density, 1 conductivity type gallium nitride A second conductivity type gallium nitride based semiconductor layer provided on the semiconductor layer, and (d) first and third regions forming ohmic junctions in the first and third regions of the second conductivity type gallium nitride based semiconductor layer, respectively. First and second electrodes are provided on the second electrode, the second conductivity type gallium nitride based semiconductor layer, and the first and second electrodes, respectively, and located on the first and second electrodes, respectively. (E) a wiring conductor provided on the protective insulating film and connected to the first and second electrodes through the first and second openings; (f) A first insulating layer provided between the second region of the first conductivity type gallium nitride based semiconductor layer and the protective insulating film; and (g) provided on the back surface of the conductive substrate. and a second electrode layer, the first conductivity type The gallium phosphide-based semiconductor layer and the second conductivity type gallium nitride-based semiconductor layer form a pn junction structure, and the first region of the second conductivity-type gallium nitride-based semiconductor layer is the first conductivity type. The second region of the second conductivity type gallium nitride semiconductor layer is provided on the first region of the gallium nitride semiconductor layer, and the second region of the second conductivity type gallium nitride semiconductor layer is the second region of the first conductivity type gallium nitride semiconductor layer. The third region of the second conductivity type gallium nitride based semiconductor layer is provided on the third region of the first conductivity type gallium nitride based semiconductor layer. The first regions of the first conductivity type gallium nitride semiconductor layer and the second conductivity type gallium nitride semiconductor layer are provided for a first element, and the first conductivity type gallium nitride semiconductor layer and the The third region of the second conductivity type gallium nitride based semiconductor layer is provided for the second element, and the semiconductor device is a pn junction diode including the first and second elements.

  According to the pn junction diode, the first element of the pn junction diode is provided in the first region of the gallium nitride based semiconductor layer of the first conductivity type and the second conductivity type. A second element of a pn junction diode is provided in the third region of the second conductivity type gallium nitride based semiconductor layer. The first and second elements include first and second electrodes that form ohmic junctions in the first and third regions, respectively, and the first and second electrodes do not extend over the insulating layer. The protective insulating film protects the edges of the first and second electrodes and the surface of the first conductivity type gallium nitride based semiconductor layer. The first and second electrodes are connected to each other through a wiring conductor. Although the second region is provided between the first region and the third region, the first insulating layer is provided between the second region and the wiring conductor. The second region of the first gallium nitride based semiconductor layer is not electrically connected. Even when a reverse bias is applied to the pn junction diode, a high electric field is not directly applied to the second region of the first-conductivity-type gallium nitride-based semiconductor layer, which is caused by the electric field in the second region. A decrease in dielectric breakdown voltage can be suppressed.

According to another aspect of the present invention, a semiconductor device using a nitride-based semiconductor is a pin junction diode, the semiconductor device comprising: (a) a conductive substrate having a front surface and a back surface; and (b) a first penetration. A first region having a threading dislocation density smaller than the dislocation density; a second region having a threading dislocation density larger than the first threading dislocation density; and a first region having a threading dislocation density smaller than the first threading dislocation density. A first conductivity type gallium nitride based semiconductor layer provided on the surface of the conductive substrate, and (c) a first threading dislocation density lower than a second threading dislocation density. A second region having a threading dislocation density larger than the second threading dislocation density, and a third region having a threading dislocation density smaller than the second threading dislocation density, 1 conductivity type gallium nitride A second conductivity type gallium nitride based semiconductor layer provided on the semiconductor layer, (d) a first region having a threading dislocation density lower than the third threading dislocation density, and the third threading dislocation density. A second region having a high threading dislocation density; and a third region having a threading dislocation density smaller than the third threading dislocation density; and the first conductivity type gallium nitride based semiconductor layer and the second region An i-type gallium nitride-based semiconductor layer provided between the conductive-type gallium nitride-based semiconductor layer; and (e) an ohmic junction in each of the first and third regions of the second-conductivity-type gallium nitride-based semiconductor layer. First and second electrodes formed; and (f) provided on the second conductivity type gallium nitride based semiconductor layer and the first and second electrodes, respectively, on the first and second electrodes. Located first and (G) a wiring conductor provided on the protective insulating film and connected to the first and second electrodes through the first and second openings; and (h) ) A first insulating layer provided between the second region of the second conductivity type gallium nitride based semiconductor layer and the protective insulating film; and (i) provided on the back surface of the conductive substrate. And the first conductive gallium nitride semiconductor layer, the i-type gallium nitride semiconductor layer, and the second conductive gallium nitride semiconductor layer constitute a pin junction structure, The first region of the i-type gallium nitride semiconductor layer includes the first region of the first conductivity type gallium nitride semiconductor layer and the first region of the second conductivity type gallium nitride semiconductor layer. I-type gallium nitride provided between The second region of the semiconductor-based semiconductor layer is provided between the second region of the first-conductivity-type gallium nitride-based semiconductor layer and the second region of the second-conductivity-type gallium nitride-based semiconductor layer. The third region of the i-type gallium nitride semiconductor layer includes the third region of the first conductivity type gallium nitride semiconductor layer and the third region of the second conductivity type gallium nitride semiconductor layer. 3 region. The first regions of the first conductivity type gallium nitride based semiconductor layer, the i type gallium nitride based semiconductor layer, and the second conductivity type gallium nitride based semiconductor layer are provided for a first element, and The third region of the conductive gallium nitride based semiconductor layer, the i-type gallium nitride based semiconductor layer, and the second conductive gallium nitride based semiconductor layer is provided for a second element, and the semiconductor device includes: A pin junction diode including a first element and a second element.

  According to this pin junction diode, the first element of the pin junction diode is provided in the first region of the gallium nitride based semiconductor layer of the first conductivity type, i-type and second conductivity type. The second element of the pin junction diode is provided in the third region of the gallium nitride based semiconductor layer of the type, i-type, and second conductivity type. The first and second elements include first and second electrodes that form ohmic junctions in the first and third regions, and the first and second electrodes do not extend over the insulating layer. The protective insulating film protects the edges of the first and second electrodes and the surface of the first conductivity type gallium nitride based semiconductor layer. The first and second electrodes are connected to each other through a wiring conductor. Although the second region is provided between the first region and the third region, the first insulating layer is provided between the second region and the wiring conductor. The second region of the first gallium nitride based semiconductor layer is not electrically connected. Even when a reverse bias is applied to the pin junction diode, a high electric field is not directly applied to the second region of the first-conductivity-type gallium nitride based semiconductor layer, which is caused by the electric field in the second region. A decrease in dielectric breakdown voltage can be suppressed.

According to another aspect of the present invention, a semiconductor device using a nitride-based semiconductor is a vertical transistor, the semiconductor device comprising: (a) a conductive substrate having a front surface and a back surface; and (b) a first through hole. A first region having a threading dislocation density smaller than the dislocation density; a second region having a threading dislocation density larger than the first threading dislocation density; and a first region having a threading dislocation density smaller than the first threading dislocation density. A first conductivity type gallium nitride semiconductor layer provided on the surface of the conductive substrate, and (c) first and second layers made of the first conductivity type gallium nitride semiconductor. And (d) a second conductive type gallium nitride based semiconductor, and provided between the first conductive region and the first conductive region of the first conductive type gallium nitride based semiconductor layer. A first well region formed, ( 2) a second well region made of a second conductivity type gallium nitride semiconductor and provided between the third region and the second conductivity region of the first conductivity type gallium nitride semiconductor layer; (F) a first gate insulating layer provided on the first region and the first well region of the first conductivity type gallium nitride based semiconductor layer; and (g) the first conductivity type gallium nitride. A second gate insulating layer provided on the third region and the second well region of the semiconductor layer; and (h) a first gate electrode provided on the first gate insulating layer. (I) a second gate electrode provided on the second gate insulating layer; and (j) first and second electrodes forming ohmic junctions with the first and second conductive regions, respectively. (K) the first conductivity type gallium nitride based semiconductor layer, the first And a first protective insulating film provided on the first and second electrodes and having first and second openings located on the first and second electrodes, respectively. (M) a first wiring conductor provided on the protective insulating film and connected to the first and second electrodes through the first and second openings; and (n) the first conductivity. A first insulating layer provided between the second region of the gallium nitride based semiconductor layer and the protective insulating film; and (p) on the first protective insulating film and the first wiring conductor. A second protective insulating film provided; and (q) first and second openings of the second protective insulating film and the first protective insulating film provided on the second protective insulating film. The first gate electrode and the second gate electrode through the third and fourth openings of the film A second wiring conductor connecting the electrodes to each other ; and (r) a second electrode layer provided on the back surface of the conductive substrate , wherein the first conductive type gallium nitride based semiconductor layer The second region is provided between the first region and the third region. The first region of the first conductivity type gallium nitride based semiconductor layer is provided for a first element, and the third region of the first conductivity type gallium nitride based semiconductor layer is for a second device. The semiconductor device is a vertical transistor including the first and second elements.

  According to another aspect of the present invention, a semiconductor device using a nitride-based semiconductor is a vertical transistor, which includes (a) a conductive substrate having a front surface and a back surface, and (b) a first through-hole. A first region having a threading dislocation density smaller than the dislocation density; a second region having a threading dislocation density larger than the first threading dislocation density; and a first region having a threading dislocation density smaller than the first threading dislocation density. A first conductivity type gallium nitride semiconductor layer provided on the surface of the conductive substrate, and (c) first and second layers made of the first conductivity type gallium nitride semiconductor. And (d) a second conductive type gallium nitride based semiconductor, and provided between the first conductive region and the first conductive region of the first conductive type gallium nitride based semiconductor layer. A first well region formed, ( 2) a second well region made of a second conductivity type gallium nitride semiconductor and provided between the third region and the second conductivity region of the first conductivity type gallium nitride semiconductor layer; (F) a first gate insulating layer provided on the first region and the first well region of the first conductivity type gallium nitride based semiconductor layer; and (g) the first conductivity type gallium nitride. A second gate insulating layer provided on the third region and the second well region of the semiconductor layer; and (h) a first gate electrode provided on the first gate insulating layer. (I) a second gate electrode provided on the second gate insulating layer; and (j) first and second electrodes forming ohmic junctions with the first and second conductive regions, respectively. (K) the first conductivity type gallium nitride based semiconductor layer, the first First protective insulation having first and second openings provided on the first and second gate electrodes, respectively, and located on the first and second gate electrodes, respectively. (M) a first wiring conductor provided on the protective insulating film and connected to the first and second gate electrodes through the first and second openings; and (n) the first A first insulating layer provided between the second region of the one-conductivity-type gallium nitride based semiconductor layer and the protective insulating film; and (p) the first protective insulating film and the first wiring conductor. A second protective insulating film provided thereon; (q) provided on the second protective insulating film; the first and second openings of the second protective insulating film; and the first The first electrode and the second electrode are passed through the third and fourth openings of the protective insulating film. A second wiring conductor connecting the electrodes to each other, and the second region of the first conductivity type gallium nitride based semiconductor layer is provided between the first region and the third region. ing.

  According to this vertical transistor, the first element of the vertical transistor is provided in the first region of the first conductivity type gallium nitride semiconductor layer, and the first transistor of the first conductivity type gallium nitride semiconductor layer is provided. In the region 3, the second element of the vertical transistor is provided. The first and second elements include first and second electrodes that form ohmic junctions in the first and third regions, respectively, and the first and second electrodes do not extend over the insulating layer. The protective insulating film protects the edges of the first and second electrodes and the surface of the first conductivity type gallium nitride based semiconductor layer. The first and second electrodes are connected to each other through a wiring conductor. Although the second region is provided between the first region and the third region, the first insulating layer is provided between the second region and the wiring conductor. The second region of the first gallium nitride based semiconductor layer is not electrically connected. Even when a reverse bias is applied to the vertical transistor, a high electric field is not directly applied to the second region of the first-conductivity-type gallium nitride-based semiconductor layer, which is caused by the electric field in the second region. A decrease in dielectric breakdown voltage can be suppressed. According to this structure, a MOS transistor and a MIS transistor are provided.

According to another aspect of the present invention, a semiconductor device using a nitride-based semiconductor includes (a) a conductive substrate having a front surface and a back surface, and (b) a first threading dislocation density lower than the first threading dislocation density. 1 region, a second region having a threading dislocation density larger than the first threading dislocation density, and a third region having a threading dislocation density smaller than the first threading dislocation density, A first conductive type gallium nitride based semiconductor layer provided on the surface of the conductive substrate; and (c) electrically connected to the first and third regions of the first conductive type gallium nitride based semiconductor layer, respectively. And (d) provided on the first conductive type gallium nitride based semiconductor layer and the first and second electrodes, and on the first and second electrodes. First and second openings located respectively And (e) a wiring conductor provided on the protective insulating region and connected to the first and second electrodes through the first and second openings, and (f) the first A first insulating layer provided between the second region of the conductive gallium nitride based semiconductor layer and the protective insulating region; and the second region of the first conductive gallium nitride based semiconductor layer. Is provided between the first region and the third region.

  According to this nitride semiconductor device, the first element of the semiconductor device is provided in the first region of the gallium nitride semiconductor layer, and the semiconductor is provided in the third region of the gallium nitride semiconductor layer. A second element of the device is provided. The first and second elements may include first and second electrodes electrically connected to the first and third regions, respectively, and the first and second electrodes may extend over the insulating layer. Absent. The protective insulating film protects the edges of the first and second electrodes and the surface of the first conductivity type gallium nitride based semiconductor layer. The first and second electrodes are connected to each other through a wiring conductor. Although the second region is provided between the first region and the third region, the first insulating layer is provided between the second region and the wiring conductor. The second region of the first gallium nitride based semiconductor layer is not electrically connected. Even when a reverse bias is applied to the semiconductor device, a high electric field is not directly applied to the second region of the first-conductivity-type gallium nitride based semiconductor layer, so that the insulation caused by the electric field in the second region A decrease in breakdown voltage can be suppressed.

According to another aspect of the present invention, a semiconductor device using a nitride-based semiconductor is a vertical insulated gate bipolar transistor, and the semiconductor device is made of (a) a surface made of a semiconductor material different from that of a gallium nitride-based semiconductor, and A semiconductor substrate having a back surface; (b) a first region having a threading dislocation density lower than the first threading dislocation density; a second region having a threading dislocation density greater than the first threading dislocation density; And a third region having a threading dislocation density lower than the first threading dislocation density, and provided on the surface of the conductive substrate, and (c) a first First and second conductive regions made of a conductive type gallium nitride based semiconductor; and (d) the first conductive type gallium nitride based semiconductor layer made of a second conductive type gallium nitride based semiconductor. A first well region provided between the first conductive region and the first conductive region; and (e) a second conductive type gallium nitride based semiconductor, the first conductive type gallium nitride based semiconductor layer A second well region provided between the third region and the second conductive region; (f) the first region of the first conductivity type gallium nitride based semiconductor layer; A first gate insulating layer provided on the well region; and (g) a first gate insulating layer provided on the third region and the second well region of the first conductivity type gallium nitride based semiconductor layer. Two gate insulating layers; (h) a first gate electrode provided on the first gate insulating layer; and (i) a second gate electrode provided on the second gate insulating layer; (J) ohmic junctions are formed in the first and second conductive regions, respectively. (K) provided on the first conductive type gallium nitride based semiconductor layer, the first and second gate electrodes, and the first and second electrodes, and A first protective insulating film having first and second openings located on the first and second electrodes, respectively; (m) provided on the first protective insulating film; A first wiring conductor connected to the first and second electrodes through the opening, (n) the second region of the first conductivity type gallium nitride based semiconductor layer, and the first protective insulating film (P) a second protective insulating film provided on the first protective insulating film and the first wiring conductor; and (q) the second insulating layer provided between A first opening and a second opening of the second protective insulating film; A second wiring conductor for connecting the first gate electrode and the second gate electrode through the third and fourth openings of the first protective insulating film; and (r) different from the gallium nitride based semiconductor. A mask made of a material and provided between the first and third regions of the first conductivity type gallium nitride based semiconductor layer and the semiconductor substrate; and (s) the back surface of the conductive substrate. And a second electrode layer provided on the semiconductor substrate, wherein the semiconductor substrate has a second conductivity type. The first region of the first conductivity type gallium nitride based semiconductor layer is provided for a first element, and the third region of the first conductivity type gallium nitride based semiconductor layer is for a second device. The semiconductor device is a vertical insulated gate bipolar transistor including the first and second elements.

  According to another aspect of the present invention, a semiconductor device using a nitride-based semiconductor is a vertical insulated gate bipolar transistor, and the semiconductor device is made of (a) a surface made of a semiconductor material different from that of a gallium nitride-based semiconductor, and A semiconductor substrate having a back surface; (b) a first region having a threading dislocation density lower than the first threading dislocation density; a second region having a threading dislocation density greater than the first threading dislocation density; And a third region having a threading dislocation density lower than the first threading dislocation density, and provided on the surface of the conductive substrate, and (c) a first First and second conductive regions made of a conductive type gallium nitride based semiconductor; and (d) the first conductive type gallium nitride based semiconductor layer made of a second conductive type gallium nitride based semiconductor. A first well region provided between the first conductive region and the first conductive region; and (e) a second conductive type gallium nitride based semiconductor, the first conductive type gallium nitride based semiconductor layer A second well region provided between the third region and the second conductive region; (f) the first region of the first conductivity type gallium nitride based semiconductor layer; A first gate insulating layer provided on the well region; and (g) a first gate insulating layer provided on the third region and the second well region of the first conductivity type gallium nitride based semiconductor layer. Two gate insulating layers; (h) a first gate electrode provided on the first gate insulating layer; and (i) a second gate electrode provided on the second gate insulating layer; (J) ohmic junctions are formed in the first and second conductive regions, respectively. (K) provided on the first conductive type gallium nitride based semiconductor layer, the first and second gate electrodes, and the first and second electrodes, and A first protective insulating film having first and second openings positioned on the first and second gate electrodes, respectively; (m) provided on the first protective insulating film; A first wiring conductor connected to the first and second gate electrodes through two openings, and (n) the second region of the first conductivity type gallium nitride semiconductor layer and the protective insulating film A first insulating layer provided therebetween; (p) a second protective insulating film provided on the first protective insulating film and the first wiring conductor; and (q) the second protection. First and second openings of the second protective insulating film provided on the insulating film And a second wiring conductor for connecting the first electrode and the second electrode to each other through the third and fourth openings of the first protective insulating film, and (r) a material different from the gallium nitride based semiconductor And a mask provided between each of the first and third regions of the first conductivity type gallium nitride based semiconductor layer and the semiconductor substrate, wherein the semiconductor substrate has a second conductivity type. Have.

  According to this insulated gate bipolar transistor, the first element of the semiconductor device is provided in the first region of the gallium nitride based semiconductor layer, and the third region of the semiconductor device is provided in the third region of the gallium nitride based semiconductor layer. Two elements are provided. The first and second elements may include first and second electrodes electrically connected to the first and third regions, respectively, and the first and second electrodes may extend over the insulating layer. Absent. The protective insulating film protects the edges of the first and second electrodes and the surface of the first conductivity type gallium nitride based semiconductor layer. The first and second electrodes are connected to each other through a wiring conductor. Although the second region is provided between the first region and the third region, the first insulating layer is provided between the second region and the wiring conductor. The second region of the first gallium nitride based semiconductor layer is not electrically connected. Even when a reverse bias is applied to the semiconductor device, a high electric field is not directly applied to the second region of the first-conductivity-type gallium nitride based semiconductor layer, so that the insulation caused by the electric field in the second region A decrease in breakdown voltage can be suppressed. In addition, since the mask is provided over the conductive substrate, the threading dislocation density in the first and third regions of the gallium nitride based semiconductor layer can be reduced.

  The semiconductor device using the nitride semiconductor according to the present invention further includes a second electrode layer provided on the back surface of the conductive substrate, and the conductive substrate has a threading dislocation smaller than a predetermined threading dislocation density. Gallium nitride including a first region having a density, a second region having a threading dislocation density larger than the predetermined threading dislocation density, and a third region having a threading dislocation density smaller than the predetermined threading dislocation density And the first region of the first conductivity type gallium nitride based semiconductor layer is provided on the first region of the gallium nitride based semiconductor support base, and The second region of the conductivity type gallium nitride based semiconductor layer is provided on the second region of the gallium nitride based semiconductor support base, and the third region of the first conductivity type gallium nitride based semiconductor layer is provided. region The second electrode layer is provided on the third region of the gallium nitride based semiconductor support substrate, and the second electrode layer is in ohmic contact with the first and third regions on the back surface of the gallium nitride based semiconductor support substrate. Is made. According to this semiconductor device, since the gallium nitride based semiconductor support base is used, a gallium nitride based semiconductor layer having a good crystal quality is grown thereon.

  The semiconductor device using a nitride semiconductor according to the present invention further includes a second insulating layer provided between the second region and the second electrode layer of the gallium nitride semiconductor support base. According to this semiconductor device, since the second insulating layer is provided between the second region of the gallium nitride based semiconductor support base and the second electrode layer, the second electrode layer is composed of the gallium nitride based base material. It is not directly connected to the second region of the semiconductor support substrate. Even when a large voltage is applied to the semiconductor device, a high electric field is not directly applied to the second region of the gallium nitride based semiconductor support base, so that the breakdown voltage generated due to the electric field in the second region can be reduced. Reduction can be suppressed.

  In the semiconductor device using the nitride semiconductor according to the present invention, the gallium nitride based semiconductor support base is made of gallium nitride. According to this vertical transistor, a decrease in dielectric breakdown voltage can be suppressed using a gallium nitride supporting base having excellent crystal quality.

  The vertical transistor according to the present invention includes a material different from a gallium nitride based semiconductor as a constituent element, and the first and third regions of the first conductive type gallium nitride based semiconductor layer and the conductive substrate Each of the conductive substrates is made of a semiconductor material different from that of the gallium nitride semiconductor. According to this semiconductor device, a gallium nitride based semiconductor layer is grown on a conductive substrate made of a semiconductor material while controlling dislocations using a mask. A Schottky diode, a pn junction diode, a pin junction diode, a MOS transistor, and a MIS transistor are also provided.

  The above and other objects, features, and advantages of the present invention will become more readily apparent from the following detailed description of preferred embodiments of the present invention, which proceeds with reference to the accompanying drawings.

  As described above, according to the present invention, the influence of the arrangement of the core portion having a high threading dislocation density can be reduced and the device area can be increased, and the Schottky barrier diode, the pn junction diode, the pin junction diode, the vertical A nitride semiconductor device using a type transistor and a nitride semiconductor is provided.

  The knowledge of the present invention can be easily understood by considering the following detailed description with reference to the accompanying drawings shown as examples. Subsequently, embodiments of the semiconductor device according to the present invention (for example, a Schottky barrier diode, a pn junction diode, a pin junction diode, and a vertical transistor) will be described with reference to the accompanying drawings. Where possible, the same parts are denoted by the same reference numerals.

(First embodiment)
FIG. 1 is a drawing showing a Schottky barrier diode of a semiconductor device according to an embodiment of the present invention. The Schottky barrier diode 11 includes a conductive substrate 13, a first conductivity type gallium nitride semiconductor layer 15, a first electrode 17 a, a second electrode 17 b, a protective insulating film 18, and a first insulating layer 19. A wiring conductor 20 and an electrode layer 21. The conductive substrate 13 has a front surface 13a and a back surface 13b. The first conductivity type gallium nitride based semiconductor layer 15 is provided on the surface 13 a of the conductive substrate 13. The first conductivity type gallium nitride based semiconductor layer 15 includes a first region 15a, a second region 15b, and a third region 15c. The first region 15a has a first threading dislocation density _{D 1} is smaller than the threading dislocation density _{D 11.} Second region 15b (referred to as "core" in the following examples) has a first threading dislocation density D ₁ greater than the threading dislocation density D _12. The third region 15c has a first threading dislocation density _{D 1} is smaller than the threading dislocation density _{D 13.} The first electrode 17 a forms a Schottky junction with the first region 15 a of the first conductivity type gallium nitride based semiconductor layer 15. The second electrode 17 b forms a Schottky junction with the third region 15 c of the first conductivity type gallium nitride based semiconductor layer 15. The protective insulating film 18 is provided on the first conductivity type gallium nitride based semiconductor layer 15 and the first and second electrodes 17a and 17b, and is located on the first and second electrodes 17a and 17b, respectively. Has first and second openings. The protective insulating film 18 covers the edges of the first and second electrodes 17a and 17b. The first insulating layer 19 is provided between the second region 15 b of the first conductivity type gallium nitride based semiconductor layer 15 and the protective insulating film 18. The wiring conductor 20 is provided on the protective insulating film 18 and connected to the first and second electrodes 17 a and 17 b through the first and second openings of the protective insulating film 18. The electrode layer 21 is provided on the back surface 13 b of the conductive substrate 13. The second region 15b of the gallium nitride based semiconductor layer 15 is provided between the first region 15a and the third region 15c.

  According to the Schottky barrier diode 11, the first element SBD1 of the Schottky barrier diode 11 is provided in the first region 15a of the first conductivity type gallium nitride semiconductor layer 15, and the first conductivity type gallium nitride is provided. In the third region 15c of the system semiconductor layer 15, the second element SBD2 of the Schottky barrier diode 11 is provided. The first element SBD1 includes a first electrode 17a that forms a Schottky junction in the first region 15a, and the second element SBD2 includes a second electrode 17b that forms a Schottky junction in the third region 15c. . The first and second electrodes 17 a and 17 b do not extend over the insulating layer 19. The protective insulating film 18 protects the edges of the first and second electrodes 17 a and 17 b and the surface of the first conductivity type gallium nitride based semiconductor layer 15. The first and second electrodes 17 a and 17 b are connected to each other through the wiring conductor 20. Although the second region 15b is provided between the first region 15a and the third region 15c, the first insulating layer 19 and the protective insulating film 18 are formed of the second region 15b, the wiring conductor 20, and the like. Therefore, the wiring conductor 20 is not electrically connected to the second region 15 b of the first gallium nitride based semiconductor layer 15. Even when a reverse bias is applied to the Schottky barrier diode 11, a high electric field is not directly applied to the second region 15b of the first conductivity type gallium nitride based semiconductor layer 15, so that the electric field in the second region 15b is not applied to the second region 15b. It is possible to suppress a decrease in dielectric breakdown voltage caused by the cause.

Examples of the material of the gallium nitride based semiconductor layer 15 include GaN, AlGaN, InGaN, and InAlGaN. In addition, the first threading dislocation density D ₁ is, for example, 1 × 10 ⁸ cm ⁻² , and the threading dislocation density D ₁₁ , D ₁₃ is, for example, 1 × 10 ⁸ cm ⁻² or less. For example, D ₁₂ is larger than 1 × 10 ⁸ cm ⁻² . As a material of the first insulating layer 19, for example, nitride, oxide, fluoride, SOG, or the like can be used alone or as a multilayer film. Examples of the nitride include silicon nitride such as SiN _X. Examples of the oxide include SiO ₂ , ZnO, TiO ₂ , Ta ₂ O ₅ , Al ₂ O ₃ , Ga ₂ O ₃ , ZrO ₂ , PbO, HfO ₂ , CeO ₂ , Y ₂ O ₃ , Cr ₂ O ₃ , Bi ₂ O ₃ , In ₂ O ₃ , Nd ₂ O ₃ , Sb ₂ O _{3 and the} like can be given. Examples of the fluoride include magnesium fluoride such as MgF ₂ , AlF ₃ , CeF ₂ , CaF ₂ , NdF ₃ , PbF ₂ , BaF ₂ , and SrF ₂ .

  In the Schottky barrier diode 11, each of the second regions 15b of the first conductivity type gallium nitride based semiconductor layer 15 extends in the X direction. Each of the first region 15a and the third region 15c also extends in the X direction. The first, second, and third regions 15a, 15b, and 15c are arranged in the Y direction. Each of the first, second, and third regions 15a, 15b, 15c extends in the Z-axis direction from one surface of the first conductivity type gallium nitride based semiconductor layer 15 to the opposite surface. The second region 15b separates the other from one of the first region 15a and the third region 15c. The first insulating layer 19 covers the second region 15b.

  In the Schottky barrier diode 11, a groove 15 d provided in accordance with the second region 15 b is provided on the surface of the first conductivity type gallium nitride based semiconductor layer 15. The groove 15d extends in the X-axis direction. Since the first insulating layer 19 is provided in the groove 15d, and the insulating layer can be thickened without impairing the flatness of the element, the first insulating layer 19 can be easily held by the high electric field insulating layer.

In a preferred example of the Schottky barrier diode 11, the conductive substrate 13 can be made of a group III nitride such as a gallium nitride semiconductor or AlN. Examples of the gallium nitride semiconductor include GaN, AlGaN, InGaN, and AlInGaN. . Preferably, the conductive substrate 13 includes a gallium nitride based semiconductor support base 23. The gallium nitride based semiconductor support base 23 includes a first region 23a, a second region 23b, and a third region 23c. In the gallium nitride-based semiconductor supporting base 23, the first area 23a has a first threading dislocation density _{D 2} smaller than the threading dislocation density _{D 21.} The second region 23b has a first threading dislocation density _{D 2} is greater than the threading dislocation density _{D 22.} The third region 23c has a first threading dislocation density _{D 2} smaller than the threading dislocation density _{D 23.} The second threading dislocation density D ₂ is, for example, 1 × 10 ⁸ cm ⁻² , and the threading dislocation density D ₂₁ , D ₂₃ is, for example, 1 × 10 ⁸ cm ⁻² or less, and the threading dislocation density D _22. For example, it is larger than 1 × 10 ⁸ cm ⁻² .

  The first region 15 a of the gallium nitride based semiconductor layer 15 is provided on the first region 23 a of the gallium nitride based semiconductor support base 23. The second region 15 b of the gallium nitride based semiconductor layer 15 is provided on the second region 23 b of the gallium nitride based semiconductor support base 23. The third region 15 c of the gallium nitride based semiconductor layer 15 is provided on the third region 23 c of the gallium nitride based semiconductor support base 23. If the gallium nitride based semiconductor layer 15 is epitaxially grown on the gallium nitride based semiconductor support base 23, the above structure can be obtained.

  In the Schottky barrier diode 11, each of the second regions 23b of the gallium nitride based semiconductor support base 23 extends in the X direction. Each of the first region 23a and the third region 23c extends in the X direction. The first, second and third regions 23a, 23b and 23c are arranged in the Y direction. Each of the first, second, and third regions 23a, 23b, and 23c extends from one surface of the support base 23 to the other surface facing the Z-axis direction. The second region 23b separates the other from one of the first region 23a and the third region 23c.

  The second electrode layer 21 forms an ohmic junction with the first and third regions 23 a and 23 c on the back surface 23 d of the gallium nitride based semiconductor support base 23.

  According to the Schottky barrier diode 11, since the conductive substrate 13 includes the gallium nitride based semiconductor support base 23, the threading dislocation density in the first and third regions 15a and 15c of the gallium nitride based semiconductor layer 15 can be reduced.

Example 1
An epitaxial film structure (n-type GaN semiconductor layer) for a Schottky barrier diode is formed on a conductive n-type GaN substrate having a striped core by MOVPE. The n-type GaN semiconductor layer has a core portion that inherits the core on the surface of the n-type GaN substrate. The core portion is etched to a predetermined depth by reactive ion etching, and an SiN film is buried in the etched portion to form a current barrier portion. Thereby, element isolation is formed. An n-type Schottky electrode as an anode electrode is integrally formed in the low defect density region of the n-type GaN semiconductor layer by an electron beam evaporation method and a lift-off method. Further, a protective insulating film such as a SiN film or a SiO ₂ film is formed so as to cover the anode electrode, the current barrier portion, and the n-type GaN semiconductor layer exposed therebetween. Next, a part of the protective insulating film on the anode electrode is etched with buffered hydrofluoric acid or the like by a photolithography technique to expose a part of the anode electrode. Finally, a wiring conductor that short-circuits the exposed anode electrodes, for example, Al, is integrally formed by vapor deposition. An n-type ohmic electrode as a cathode electrode common to each element is formed on the entire back surface of the substrate by vapor deposition.

  FIG. 2A is a diagram showing a modification of the Schottky barrier diode according to the present embodiment. FIG. 2A is a cross-sectional view of the Schottky barrier diode 11a, and shows a cross section corresponding to the line I-I shown in FIG. The Schottky barrier diode 11 a further includes a second insulating layer 25 provided between the second region 23 b of the gallium nitride based semiconductor support base 23 and the second electrode layer 21. Examples of the material of the second insulating layer 25 include silicon nitride.

  According to this Schottky barrier diode 11a, since the second insulating layer 25 is provided between the second region 23b of the gallium nitride based semiconductor support base 23 and the second electrode layer 21, the second electrode The layer 21 is not directly connected to the second region 23 b of the gallium nitride based semiconductor support base 23. Even when a reverse bias is applied to the Schottky barrier diode 11a, a high electric field is not directly applied to the second region 23b of the gallium nitride based semiconductor support base 23, which is caused by the electric field in the second region 23b. A reduction in the dielectric breakdown voltage that occurs can be suppressed.

  In the Schottky barrier diode 11a, a groove 23e provided in accordance with the second region 23b is provided on the back surface of the gallium nitride based semiconductor support base 23. Since the second insulating layer 25 is provided in the groove 23e, and the insulating layer can be thickened without impairing the flatness of the element, the second insulating layer 25 can be easily held by the high electric field insulating layer. The groove 23e extends in the X-axis direction. The depth of the groove 23e is, for example, 0.01 μm to 10 μm, preferably 0.1 μm to 1 μm.

In an example of the Schottky barrier diode 11a,
Support base 23: n-type gallium nitride first conductivity type gallium nitride semiconductor layer 15: n-type gallium nitride electrode 17a, 17b: Schottky electrode, Ni (80 nm) / Au (30 nm)
Protective insulating film 18: SiO ₂ , thickness 1000 nm
First insulating layer 19: silicon nitride, thickness 1000 nm
Wiring conductor 20: Al
Second electrode layer 21: ohmic electrode,
Ti (20 nm) / Al (100 nm) / Ti (20 nm) / Au (200 nm)
Second insulating layer 25: silicon nitride, thickness 1000 nm
It is. As described above, when the gallium nitride based semiconductor support base 23 is made of gallium nitride, a decrease in dielectric breakdown voltage can be suppressed by using a GaN support base having excellent crystal quality. The first region 23a and the third region 23c of the gallium nitride based semiconductor support base 23 are preferably single crystals, and the second region 23b is preferably single crystal. Furthermore, the crystal axes of the first region 23a and the third region 23c of the gallium nitride based semiconductor support base 23 can be opposite to the crystal axes of the second region 23b. When the first conductivity type gallium nitride based semiconductor layer 15 is made of gallium nitride, the first region 15a and the third region 15c of the gallium nitride based semiconductor layer 15 are single crystals, and the second region 15b is It is preferably a single crystal. Further, the crystal axes of the first region 15a and the third region 15c of the gallium nitride based semiconductor layer 15 may be opposite to the crystal axis of the second region 15b. For example, the surface of the first region 15a and the third region 15c is one of the Ga surface and the N surface, and the surface of the second region 15b is the other of the Ga surface and the N surface.

(Example 2)
In the diode of Example 1, before forming the cathode electrode on the back surface, the core portion on the back surface is formed with a recess having a predetermined depth by reactive ion etching, and the SiO ₂ film for the current barrier portion is embedded. Form. After this, a cathode electrode common to each element is formed on the entire back surface by vapor deposition.

FIG. 2B is a drawing showing another modification of the Schottky barrier diode according to the present embodiment. FIG. 2B is a cross-sectional view of the Schottky barrier diode 11b, and shows a cross section corresponding to the line I-I shown in FIG. In the Schottky barrier diode 11b, the conductive substrate 13 can be a support base 27 made of a semiconductor material different from the gallium nitride based semiconductor. The support base 27 is made of a semiconductor having the same first conductivity type as that of the gallium nitride based semiconductor layer 15 and includes, for example, Si, SiC, GaAs and the like. In addition to the support base 27, the Schottky barrier diode 11b includes a first conductivity type gallium nitride semiconductor layer 35, first and second electrodes 37a and 37b, a first insulating layer 39, and a second electrode layer. 31, and further includes a protective insulating film 18 and a wiring conductor 20. The Schottky barrier diode 11 b further includes a mask 33 provided between the first and third regions 35 a and 35 c of the gallium nitride based semiconductor layer 35 and the support base 27. According to the Schottky barrier diode 11b, the gallium nitride based semiconductor layer 35 is grown on the semiconductor support base 27 while controlling dislocations using the mask 33. The gallium nitride based semiconductor layer 35 includes a first region 35a, a second region 35b, and a third region 35c. The first region 35a has a first threading dislocation density _{D 1} is smaller than the threading dislocation density _{D 11.} The second region 35b has a first threading dislocation density _{D 1} greater than the threading dislocation density _{D 12.} The third region 35c has a first threading dislocation density _{D 1} is smaller than the threading dislocation density _{D 13.} The gallium nitride based semiconductor layer 35 is provided on the surface 27 a of the support base 27. The first and second electrodes 37a and 37b form Schottky junctions with the first region 35a and the third region 35c of the first gallium nitride based semiconductor layer 35, respectively. The first insulating layer 39 is provided between the second region 35 b of the gallium nitride based semiconductor layer 35 and the protective insulating film 18. The protective insulating film 18 covers the edges of the first and second electrodes 37a and 37b. The second electrode layer 31 is provided on the back surface 27 b of the support base 27. The second region 35b of the gallium nitride based semiconductor layer 35 is provided between the first region 35a and the third region 35c.

An example of the Schottky barrier diode 11b is
Protective insulating film 18: SiO ₂ , thickness 1000 nm
Wiring conductor 20: Al
Support base 27: n-type silicon first conductivity type gallium nitride semiconductor layer 35: n-type gallium nitride electrode 37a, 37b: Schottky electrode, Pt (25 nm) / Au (300 nm)
First insulating layer 39: silicon nitride mask 33: SiO ₂
Second electrode layer 31: Ohmic electrode Ti (20 nm) / Al (100 nm) / Ti (20 nm) / Au (200 nm)
It is. Thus, when the conductive substrate 13 is made of n-type silicon, the mask 33 extends in the X-axis direction and is arranged in the Y direction. If the gallium nitride based semiconductor layer 35 is epitaxially grown on the semiconductor support base 27, the above structure can be obtained. The width W of the mask 33 is, for example, not less than 5 μm and not more than 500 μm. The interval D between the masks 33 is, for example, 1 μm or more and 100 μm or less.

(Second Embodiment)
FIG. 3 is a drawing showing a pn junction diode of the semiconductor device according to the embodiment of the present invention. The pn junction diode 41 includes a conductive substrate 13, a first conductivity type gallium nitride semiconductor layer 15, a protective insulating film 18, a first insulating layer 19, a wiring conductor 20, and a second electrode layer 21. , A second conductivity type gallium nitride based semiconductor layer 43, and first and second electrodes 45a, 45b. The second conductivity type gallium nitride based semiconductor layer 43 includes a first region 43a, a second region 43b, and a third region 43c. The first region 43a has a second threading dislocation density _{D 3} smaller than the threading dislocation density _{D 31.} The second region 43b has a second threading dislocation density _{D 3} greater than the threading dislocation density _{D 32.} The third region 43c has a second threading dislocation density _{D 3} smaller than the threading dislocation density _{D 33.} The second conductivity type gallium nitride based semiconductor layer 43 is provided on the first conductivity type gallium nitride based semiconductor layer 15.
The first electrode 45 a forms an ohmic junction with the first region 43 a of the second conductivity type gallium nitride based semiconductor layer 43. The second electrode 45 b forms an ohmic junction with the third region 43 c of the second conductivity type gallium nitride based semiconductor layer 43. The protective insulating film 18 is provided on the second conductivity type gallium nitride based semiconductor layer 43 and the first and second electrodes 45a and 45b, and is located on the first and second electrodes 45a and 45b, respectively. Has first and second openings. The protective insulating film 18 covers the edges of the first and second electrodes 45a and 45b. The first insulating layer 19 is provided between the second region 43 b of the second conductivity type gallium nitride based semiconductor layer 43 and the protective insulating film 18. The wiring conductor 20 is provided on the protective insulating film 18 and connected to the first and second electrodes 45 a and 45 b through the first and second openings of the protective insulating film 18. The second electrode layer 21 is provided on the back surface 13 b of the conductive substrate 13.

  The first conductivity type gallium nitride based semiconductor layer 15 and the second conductivity type gallium nitride based semiconductor layer 43 constitute a pn junction structure J1. The first region 43 a of the second conductivity type gallium nitride based semiconductor layer 43 is provided on the first region 15 a of the first conductivity type gallium nitride based semiconductor layer 15. The second region 43 b of the second conductivity type gallium nitride based semiconductor layer 43 is provided on the second region 15 b of the first conductivity type gallium nitride based semiconductor layer 15. The third region 43 c of the second conductivity type gallium nitride based semiconductor layer 43 is provided on the third region 15 c of the first conductivity type gallium nitride based semiconductor layer 15. The second region 43b of the gallium nitride based semiconductor layer 43 is provided between the first region 43a and the third region 43c.

  According to the pn junction diode 41, the first regions 15a and 43a of the gallium nitride based semiconductor layers 15 and 43 are provided with the first element PND1 of the pn junction diode. A third element 15c, 43c of 43 is provided with a second element PND2 of a pn junction diode. The first element PND1 includes a first electrode 45a that forms an ohmic junction with the first region 43a of the second conductivity type gallium nitride based semiconductor layer 43, and the second element PND2 includes a second conductivity type gallium nitride. The second region 45 c of the system semiconductor layer 43 includes a second electrode 45 b that forms an ohmic junction. The first and second electrodes 45 a and 45 b do not extend over the insulating layer 19. The protective insulating film 18 protects the edges of the first and second electrodes 45 a and 45 b and the surface of the second conductivity type gallium nitride based semiconductor layer 43. The first and second electrodes 45 a and 45 b are connected to each other through the wiring conductor 20. Although the second region 43b of the gallium nitride based semiconductor layer 43 is provided between the first region 43a and the third region 43c, the first insulating layer 19 and the protective insulating film 18 are composed of the gallium nitride based semiconductor. Since it is provided between the second region 43 b of the layer 43 and the wiring conductor 20, the wiring conductor 20 is not electrically connected to the second region 43 b of the gallium nitride based semiconductor layer 43. Even when a reverse bias is applied to the pn junction diode 41, a high electric field is not directly applied to the second region 43b of the gallium nitride based semiconductor layer 43, so that the breakdown voltage due to the electric field in the second region 43b is reduced. Reduction can be suppressed.

Examples of the material of the gallium nitride based semiconductor layer 43 include GaN, AlGaN, InGaN, and AlInGaN. As the second threading dislocation density _{D 3,} for example, 1 × a ¹⁰ 8 ^{cm -2,} the threading dislocation density _{D 31, D 33,} for example, ^{1 × 10 2 cm -2 ~1 ×} 10 8 cm - ^2, as the threading dislocation density _{D 32,} for example, at most 1 × ¹⁰ 8 ^cm greater than ^-2 1 × ¹⁰ 12 ^{cm -2} or less.

  In the pn junction diode 41, each of the second regions 43b of the second conductivity type gallium nitride based semiconductor layer 43 extends in the X direction. Each of the first region 43a and the third region 43c extends in the X direction. The first, second, and third regions 43a, 43b, and 43c are arranged in the Y direction. Each of the first, second, and third regions 43a, 43b, and 43c extends from one surface of the second conductivity type gallium nitride based semiconductor layer 43 to the other surface facing in the Z-axis direction. The second region 43b separates the other from one of the first region 43a and the third region 43c. The first insulating layer 19 covers the second region 43b.

  In the pn junction diode 41, a groove 43 d provided in accordance with the second region 43 b is provided on the surface of the second conductivity type gallium nitride based semiconductor layer 43. The groove 43d extends in the X-axis direction. Since the first insulating layer 19 is provided in the groove 43d, and the insulating layer can be thickened without impairing the flatness of the element, the first insulating layer 19 can be easily held by the high electric field insulating layer. In the pn junction diode 41, the conductive substrate 13 made of the same material as that of the Schottky barrier diode 11 can be used.

(Example 3)
An epitaxial film structure having an n-type GaN semiconductor layer and a p-type GaN semiconductor layer is formed on the n-type GaN substrate for Example 1 by the MOVPE method. The n-type and p-type GaN semiconductor layers have a core portion that takes over the core of the substrate. The core portion of the p-type GaN surface is etched to a predetermined depth by reactive ion etching, and a SiN film is embedded in the etching region to form a current barrier portion for element isolation. In the low defect density region, a p-type ohmic electrode as an anode electrode is formed by an electron beam evaporation method and a lift-off method. Further, a protective insulating film such as a SiN film or a SiO ₂ film is formed so as to cover the anode electrode, the current barrier portion, and the p-type GaN semiconductor layer exposed therebetween. Next, a part of the protective insulating film on the anode electrode is etched with buffered hydrofluoric acid or the like by a photolithography technique to expose a part of the anode electrode. Finally, a wiring conductor that short-circuits the exposed anode electrodes, for example, Al, is integrally formed by vapor deposition. An n-type ohmic electrode as a cathode electrode common to each element is formed on the entire back surface of the substrate by vapor deposition.

  FIG. 4A is a diagram showing a modification of the pn junction diode according to the present embodiment. 4A is a cross-sectional view of the pn junction diode 41a and shows a cross section corresponding to the II-II line shown in FIG. The pn junction diode 41 a further includes a second insulating layer 25 provided between the second region 23 b of the gallium nitride based semiconductor support base 23 and the second electrode layer 21. As the material of the second insulating layer 25, for example, nitride, oxide, fluoride, SOG, or the like can be used as a single body or a multilayer film, as in the first embodiment. According to the pn junction diode 41a, since the second insulating layer 25 is provided between the second region 23b of the gallium nitride based semiconductor support base 23 and the second electrode layer 21, the second electrode The layer 21 is not directly connected to the second region 23 b of the gallium nitride based semiconductor support base 23. Even when a reverse bias is applied to the pn junction diode 41a, a high electric field is not directly applied to the second region 23b of the gallium nitride based semiconductor support base 23, which is caused by the electric field in the second region 23b. A reduction in the dielectric breakdown voltage that occurs can be suppressed.

  In the pn junction diode 41, a groove 23e provided in accordance with the second region 23b is provided on the back surface of the gallium nitride based semiconductor support base 23. Since the second insulating layer 25 is provided in the groove 23e, and the insulating layer can be thickened without impairing the flatness of the element, the second insulating layer 25 can be easily held by the high electric field insulating layer. The groove 23e extends in the X-axis direction.

An example of a pn junction diode 41a is shown below:
Protective insulating film 18: SiO ₂ , thickness 1000 nm
Wiring conductor 20: Al
Support base 23: n-type gallium nitride first conductivity type gallium nitride semiconductor layer 15: n-type gallium nitride second conductivity type gallium nitride semiconductor layer 43: p-type gallium nitride junction J1; homojunction electrodes 45a, 45b: ohmic electrodes , Ni (5 nm) / Au (100 nm)
First insulating layer 19: silicon nitride, thickness 1000 nm
Second electrode layer 21: Ohmic electrode Ti (20 nm) / Al (100 nm) / Ti (20 nm) / Au (200 nm)
Second insulating layer 25: silicon nitride, thickness 1000 nm

Example 4
In the diode of Example 3, before forming the cathode electrode on the back surface, a recess having a predetermined depth is formed in the core portion on the back surface by reactive ion etching, and an SiO ₂ film for the current barrier portion is embedded. Form. After this, a cathode electrode common to each element is formed on the entire back surface by vapor deposition.

  FIG. 4B is a drawing showing another modification of the pn junction diode according to the present embodiment. FIG. 4B is a cross-sectional view of the pn junction diode 41b, and shows a cross section corresponding to the II-II line shown in FIG. In the pn junction diode 41b, the conductive substrate 13 can be a support base 27 made of a first conductivity type semiconductor material different from a gallium nitride based semiconductor. In addition to the support base 27, the pn junction diode 41b includes a first conductivity type gallium nitride semiconductor layer 35, a second conductivity type gallium nitride semiconductor layer 47, first and second electrodes 49a and 49b, 1 insulating layer 39, second electrode layer 31, and mask 33, and further includes protective insulating film 18 and wiring conductor 20. The protective insulating film 18 covers the edges of the first and second electrodes 49a and 49b.

According to the pn junction diode 41b, the gallium nitride based semiconductor layers 35 and 43 are grown on the support base 27 made of a semiconductor material while controlling dislocations using the mask 33. The second conductivity type gallium nitride based semiconductor layer 47 includes a first region 47a, a second region 47b, and a third region 47c. The first region 47a has a second threading dislocation density _{D 4} is smaller than the threading dislocation density _{D 41.} The second region 47b has a second threading dislocation density _{D 4} is greater than the threading dislocation density _{D 42.} The third region 47c has a second threading dislocation density _{D 4} is smaller than the threading dislocation density _{D 43.} The second conductivity type gallium nitride based semiconductor layer 47 is provided on the surface 27 a of the semiconductor support base 27. The first and second electrodes 45a and 45b form ohmic junctions with the first region 47a and the third region 47c of the second conductivity type gallium nitride based semiconductor layer 47, respectively. The first insulating layer 39 is provided between the second region 47 b of the second conductivity type gallium nitride based semiconductor layer 47 and the protective insulating film 18. The second region 47b of the gallium nitride based semiconductor region 47 is provided between the first region 47a and the third region 47c.

(Third embodiment)
FIG. 5 is a drawing showing a pin junction diode of a semiconductor device according to an embodiment of the present invention. The pin junction diode 51 includes a conductive substrate 13, a first conductive type gallium nitride based semiconductor layer 15, a protective insulating film 18, a first insulating layer 19, a wiring conductor 20, a second electrode layer 21, and the like. A second conductivity type gallium nitride based semiconductor layer 43, first and second electrodes 45a and 45b, and an i-type gallium nitride based semiconductor layer 53. The gallium nitride based semiconductor layer 53 includes a first region 53a, a second region 53b, and a third region 53c. The first region 53a has a third threading dislocation density _{D 5} is smaller than the threading dislocation density _{D 51.} The second region 53b has a third threading dislocation density _{D 5} is greater than the threading dislocation density _{D 52.} The third region 53c has a third threading dislocation density _{D 5} is smaller than the threading dislocation density _{D 53.} The i-type gallium nitride semiconductor layer 53 is provided between the first conductive gallium nitride semiconductor layer 15 and the second conductive gallium nitride semiconductor layer 43. The first conductivity type gallium nitride based semiconductor layer 15, the i type gallium nitride based semiconductor layer 53, and the second conductivity type gallium nitride based semiconductor layer 43 form a pin junction structure J2.

  The first electrode 45 a forms an ohmic junction with the first region 43 a of the second conductivity type gallium nitride based semiconductor layer 43. The second electrode 45 b forms an ohmic junction with the third region 43 c of the second conductivity type gallium nitride based semiconductor layer 43. The protective insulating film 18 is provided on the second conductivity type gallium nitride based semiconductor layer 43 and the first and second electrodes 45a and 45b, and is located on the first and second electrodes 45a and 45b, respectively. Has first and second openings. The first insulating layer 19 is provided between the second region 43 b of the second conductivity type gallium nitride based semiconductor layer 43 and the protective insulating film 18. The wiring conductor 20 is provided on the protective insulating film 18 and connected to the first and second electrodes 45 a and 45 b through the first and second openings of the protective insulating film 18. The second electrode layer 21 is provided on the back surface 13 b of the conductive substrate 13.

  The first region 53 a of the i-type gallium nitride based semiconductor layer 53 includes a first region 15 a of the first conductivity type gallium nitride based semiconductor layer 15 and a first region 43 a of the second conductivity type gallium nitride based semiconductor layer 43. It is provided in between. The second region 53 b of the i-type gallium nitride semiconductor layer 53 includes a second region 15 b of the first conductivity type gallium nitride semiconductor layer 15 and a second region 43 b of the second conductivity type gallium nitride semiconductor layer 43. It is provided between. The third region 53 c of the i-type gallium nitride semiconductor layer 53 includes a third region 15 c of the first conductivity type gallium nitride semiconductor layer 15 and a third region 43 c of the second conductivity type gallium nitride semiconductor layer 43. It is provided between.

  According to the pin junction diode 51, the first region 15a, 43a, 53a of the gallium nitride based semiconductor layers 15, 43, 53 is provided with the first element PIND1 of the pin junction diode, and the gallium nitride series. In the third regions 15c, 43c, 53c of the semiconductor layers 15, 43, 53, a second element PIND2 of a pin junction diode is provided. The first element PIND1 includes a first electrode 45a that forms an ohmic junction with the first region 43a of the second conductivity type gallium nitride based semiconductor layer 43, and the second element PIND2 includes a second conductivity type gallium nitride. The second region 45 c of the system semiconductor layer 43 includes a second electrode 45 b that forms an ohmic junction. The first and second electrodes 45 a and 45 b do not extend over the insulating layer 19. The protective insulating film 18 protects the edges of the first and second electrodes 45 a and 45 b and the surface of the second conductivity type gallium nitride based semiconductor layer 43. The first and second electrodes 45 a and 45 b are connected to each other through the wiring conductor 20. Although the second region 43b of the second conductivity type gallium nitride based semiconductor layer 43 is provided between the first region 43a and the third region 43c, the first insulating layer 19 is the second region 43b. And the wiring conductor 20, the wiring conductor 20 is not electrically connected to the second region 43 b of the gallium nitride based semiconductor layer 43. Even when a reverse bias is applied to the pin junction diode 51, a high electric field is not directly applied to the second regions 15b, 43b, 53b of the gallium nitride based semiconductor layers 15, 43, 53. A decrease in dielectric breakdown voltage caused by the electric field in 15b, 43b, and 53b can be suppressed.

  In the pin junction diode 51, each of the second regions 53b of the i-type gallium nitride based semiconductor layer 53 extends in the X direction. Each of the first region 53a and the third region 53c extends in the X direction. The first, second and third regions 53a, 53b, 53c are arranged in the Y direction. Each of the first, second, and third regions 53a, 53b, 53c extends from one surface of the i-type gallium nitride based semiconductor layer 53 to the other surface facing the Z-axis direction. The second region 53b separates the other from one of the first region 53a and the third region 53c.

(Example 5)
An epitaxial film structure having an n-type GaN semiconductor layer, a high-resistance GaN layer, and a p-type GaN semiconductor layer is formed on the n-type GaN substrate for Example 1 by the MOVPE method. The p-type GaN semiconductor and the high-resistance GaN have a core portion that takes over the core of the substrate. A concave portion having a predetermined depth is formed in the core portion by reactive ion etching, and an SiN film is embedded in the etching region to form a current barrier portion for element isolation. In the low defect density region, a p-type ohmic electrode as an anode electrode is formed by an electron beam evaporation method and a lift-off method. Further, a protective insulating film such as a SiN film or a SiO ₂ film is formed so as to cover the anode electrode, the current barrier portion, and the p-type GaN semiconductor layer exposed therebetween. Next, a part of the protective insulating film on the anode electrode is etched with buffered hydrofluoric acid or the like by a photolithography technique to expose a part of the anode electrode. Finally, a wiring conductor that short-circuits the exposed anode electrodes, for example, Al, is integrally formed by vapor deposition. An n-type ohmic electrode as a cathode electrode common to each element is formed on the entire back surface of the substrate by vapor deposition.

  Similarly to the pn junction diode 41a, the pin junction diode 51 can also have an insulating layer on the back surface of the substrate. Similarly to the pn junction diode 41b, the pin junction diode 51 can include a substrate made of a different material.

(Fourth embodiment)
FIG. 6 is a drawing showing a vertical transistor according to the present embodiment. Examples of the vertical transistor include a MIS transistor and a MOS transistor. The vertical transistor 61 includes a conductive substrate 13, a second electrode layer 21, a first conductive gallium nitride based semiconductor layer 63, a first conductive region 65a, a second conductive region 65b, First well region 67a, second well region 67b, first and second gate insulating layers 69a and 69b, first and second gate electrodes 71a and 71b, and first and second electrodes 73a, 73b, a first insulating layer 75, a first protective insulating film 68, a first wiring conductor 70, a second protective insulating film 72, and a second wiring Conductor 74. The first conductivity type gallium nitride based semiconductor layer 63 is provided on the surface 13a of the conductive substrate 13, and includes a first region 63a, a second region 63b, and a third region 63c. The first region 63a has a first threading dislocation density _{D 6} smaller dislocation density _{D 61.} The second region 63b has a first threading dislocation density _{D 6} greater than the threading dislocation density _{D 62.} The third region 63c has a first threading dislocation density _{D 6} smaller dislocation density _{D 63.}
The first and second conductive regions 65a and 65b are made of a first conductivity type gallium nitride based semiconductor. The first well region 67a is made of a second conductivity type gallium nitride based semiconductor, and between the first region 63a and the first conductive region 65a of the first conductivity type gallium nitride based semiconductor layer 63. Is provided. The second well region 67b is made of a second conductivity type gallium nitride based semiconductor, and between the third region 63c and the second conductive region 65b of the first conductivity type gallium nitride based semiconductor layer 63. Is provided.

  The first gate insulating layer 69a is provided on the first region 63a and the first well region 67a of the first conductivity type gallium nitride based semiconductor layer 63. The second gate insulating layer 69b is provided on the third region 63c and the second well region 67b of the first conductivity type gallium nitride based semiconductor layer 63. The first gate electrode 71a is located on the first gate insulating layer 69a. The first gate electrode 71a is provided to control the channel CH1 of the vertical transistor, and the surface conductivity of the well region 67a is modulated according to the voltage of the gate electrode 71a. The second gate electrode 71b is located on the second gate insulating layer 69b. The second gate electrode 71b is provided to control the channel CH2 of the vertical transistor, and the surface conductivity of the well region 67b is modulated according to the voltage of the gate electrode 71b. The first and second electrodes 73a and 73b are provided on the first and second conductive regions 65a and 65b, respectively, and the first and second gate electrodes 71a and 71b are first conductive. The gallium nitride based semiconductor layer 63 is provided. The first and second electrodes 73a and 73b form ohmic junctions with the first and second conductive regions 65a and 65b, and respond to modulation according to the voltage of the gate electrodes 71a and 71b. Carriers flowing to the vertical transistor are supplied and function as a source electrode.

  The first protective insulating film 68 includes first and second well regions 67a and 67b, a first conductivity type gallium nitride based semiconductor layer 63, first and second gate electrodes 71a and 71b, and first and second well regions 67a and 67b. The first and second openings are provided on the electrodes 73a and 73b and located on the first and second electrodes 73a and 73b, respectively. The first protective insulating film 68 covers the edges of the first and second electrodes 73a and 73b. The first wiring conductor 70 is provided on the first protective insulating film 68 and is connected to the first and second electrodes 73a and 73b through the first and second openings. The second protective insulating film 72 is provided on the first protective insulating film 68 and the first wiring conductor 70. The second wiring conductor 74 is provided on the second protective insulating film 72. The second wiring conductor 74 is connected to the first gate electrode 71a through the first and second openings of the second protective insulating film 72 and the third and fourth openings of the first protective insulating film 68. The second gate electrode 71b is connected to each other. The first insulating layer 75 is provided between the second region 63 b of the first conductivity type gallium nitride based semiconductor layer 63 and the first protective insulating film 68.

  According to the vertical transistor 61, the first region 63a of the gallium nitride based semiconductor layer 63 is provided for the first element TRA1 of the vertical transistor 61, and the third region 63a of the gallium nitride based semiconductor layer 63 is provided. The region 63c is provided for the second element TRA2 of the vertical transistor 61. The first element TRA1 includes a first electrode 73a that forms an ohmic junction with the first region 63a. The second element TRA2 includes a second electrode 73b that forms an ohmic junction with the third region 63c. The first and second electrodes 73a and 73b do not extend over the insulating layer 75. The first protective insulating film 68 protects the edges of the first and second electrodes 73a and 73b and the surfaces of the gallium nitride based semiconductor regions 63, 67a and 67b. The first and second electrodes 73 a and 73 b are connected to each other through the first wiring conductor 70. Although the second region 63b of the gallium nitride based semiconductor layer 63 is provided between the first region 63a and the third region 63c, the first insulating layer 75 is formed between the second region 63b and the first region 63b. Since the wiring conductor 70 is provided between the protective insulating film 68 and the protective insulating film 68, the wiring conductor 70 is not connected to the second region 63 b of the gallium nitride based semiconductor layer 63. Even when a reverse bias is applied to the vertical transistor 61, a high electric field is not directly applied to the second region 63 b of the gallium nitride based semiconductor layer 63, which is caused by the electric field in the second region 63 b. A decrease in dielectric breakdown voltage can be suppressed.

  In the above embodiment, the first and second electrodes 73a and 73b are connected to each other using the first wiring conductor 70, and the first gate electrode 71a and the second electrode are connected to each other using the second wiring conductor 74. Are connected to each other. However, the first gate electrode 71a and the second gate electrode 71b are connected to each other using the first wiring conductor 70, and the first and second electrodes 73a and 73b are connected to each other using the second wiring conductor 74. May be connected to each other.

  Similar to the embodiment already described, in the vertical transistor 61, the conductive substrate 13 can be made of a group III nitride such as GaN or AlN. Preferably, the conductive substrate 13 includes a gallium nitride based semiconductor support base 23. According to the vertical transistor 61, since the conductive substrate 13 includes the gallium nitride based semiconductor support base 23, the threading dislocation density in the first and third regions 63a and 63c of the gallium nitride based semiconductor layer 63 can be reduced.

  Similarly to the embodiment already described, in the vertical transistor 61, a groove 63d is provided on the surface of the first conductivity type gallium nitride based semiconductor layer 63 in accordance with the position of the second region 63b. Yes. The groove 63d extends in the X-axis direction. Since the first insulating layer 75 is provided in the groove 63d, and the insulating layer can be thickened without impairing the flatness of the element, the first insulating layer 75 can be easily held by the high electric field insulating layer.

  FIG. 7A illustrates a modification of the vertical transistor according to this embodiment. FIG. 7A is a cross-sectional view of the vertical transistor 61a, and shows a cross section corresponding to the line III-III shown in FIG. The vertical transistor 61 a can further include a second insulating layer 25 provided between the second region 23 b of the gallium nitride based semiconductor support base 23 and the second electrode layer 21. According to the vertical transistor 61a, since the second insulating layer 25 is provided between the second region 23b of the gallium nitride based semiconductor support base 23 and the second electrode layer 21, the second electrode The layer 21 is not directly connected to the second region 23 b of the gallium nitride based semiconductor support base 23. Even when a reverse bias is applied to the vertical transistor 61a, a high electric field is not directly applied to the second region 23b of the gallium nitride based semiconductor support base 23. Therefore, this is caused by the electric field in the second region 23b. A reduction in the dielectric breakdown voltage that occurs can be suppressed.

(Example 6)
An epitaxial film structure having an n-type GaN semiconductor layer, a p-type well GaN region, and an n-type GaN semiconductor region is formed on the n-type GaN substrate for Example 1 by the MOVPE method. The surface of the n-type GaN semiconductor layer has a core portion that takes over the core of the substrate. A concave portion having a predetermined depth is formed in the core portion by reactive ion etching, and a current barrier portion for element isolation is formed by embedding an SiN film in the etching region. Further, after forming a Ga ₂ O ₃ film for forming an inversion layer on a low defect density region different from the core region, a source electrode and a gate electrode common to each element are formed by an electron beam evaporation method and a lift-off method. Next, a first protective insulating film, for example, a SiN film, a SiO ₂ film, or the like having a window for extracting the source electrode wiring is formed. The window is etched by buffered hydrofluoric acid or the like by a photolithography technique to expose a part of the source electrode. Thereafter, a first wiring conductor, for example, Al is integrally formed by vapor deposition so that the source electrodes are short-circuited. Subsequently, a second protective insulating film, for example, a SiN film, a SiO ₂ film, or the like having a window for taking out the gate electrode wiring is formed. The window is etched by buffered hydrofluoric acid or the like by photolithography technique to expose a part of the gate electrode. A second wiring conductor such as Al is integrally formed by vapor deposition so that the gate electrodes are short-circuited. A drain electrode common to each element is formed on the entire back surface of the substrate by vapor deposition. Thereby, a MOS transistor is provided.
(Example 7)
Similar to Example 6, an epitaxial film structure and a current barrier portion are formed. After forming a SiN film for forming an inversion layer in the low defect density region, a source electrode and a gate electrode common to each element and a drain electrode common to each element are formed. Thereby, a MIS transistor is provided.

An example of the vertical transistor 61a is shown below:
Support base 23: n-type gallium nitride first conductivity type gallium nitride based semiconductor layer 63: n-type gallium nitride conductive region 65a, 65b: n-type gallium nitride well region 67a, 67b: p-type gallium nitride first gate electrode 71a 71b: Ni, Pt, polysilicon, Al, Ti, W, Ir, transition metal silicide gate insulating layers 69a, 69b: Ga ₂ O ₃ , SiN, MgO, SiO ₂ , Sc ₂ O ₃ , Gd ₂ O ₃
First insulating layer 75: silicon nitride electrodes 73a, 73b: ohmic electrode Ti (20 nm) / Al (100 nm) / Ti (20 nm) / Au (200 nm)
Second electrode layer 21: Ohmic electrode Ti (20 nm) / Al (100 nm) / Ti (20 nm) / Au (200 nm)
First protective insulating film 68: SiO ₂ (500 nm)
First wiring conductor 70: Al
Second protective insulating film 72: SiO ₂ (500 nm)
Second wiring conductor 74: Al

(Example 8)
In the transistor of Example 6 or 7, before forming the drain electrode on the back surface, a recess having a predetermined depth is formed in the core portion on the back surface by reactive ion etching, and the SiO ₂ film for the current barrier portion Embedded. Thereafter, a drain electrode common to each element is formed on the entire back surface by vapor deposition.

  FIG. 7B is a drawing showing another modification of the vertical transistor according to the present exemplary embodiment. FIG. 7B is a cross-sectional view of the vertical transistor 61b and shows a cross section corresponding to the line III-III shown in FIG. In the vertical transistor 61b, the conductive substrate 13 can be the support base 27 made of the first conductive type semiconductor different from the gallium nitride based semiconductor, as in the embodiment already described. The vertical transistor 61b includes the first conductive type gallium nitride based semiconductor layer 35, the first conductive region 65a, the second conductive region 65b, the first and second wells in addition to the support base 27. Regions 67a and 67b, first and second gate insulating layers 69a and 69b, first and second gate electrodes 71a and 71b, first and second electrodes 73a and 73b, and a first insulating layer 75, the second electrode layer 31, and the mask 33, and further includes a first protective insulating film 68, a first wiring conductor 70, a second protective insulating film 72, and a second wiring conductor. 74.

(Fifth embodiment)
FIG. 8 is a view showing a vertical transistor according to the present embodiment. Examples of the vertical transistor include an IGBT transistor. The IGBT transistor 81 includes a first conductive type gallium nitride based semiconductor layer 77, a first conductive region 65a, a second conductive region 65b, a first well region 67a, and a second well region 67b. The first gate insulating layer 69a, the second gate insulating layer 69b, the first gate electrode 71a, the second gate electrode 71b, the first and second electrodes 73a and 73b, and the second A conductive semiconductor support base 83, a second electrode layer 31, a mask 33, a first protective insulating film 68, a first wiring conductor 70, and a second protective insulating film 72 and a second wiring conductor 74. The first conductivity type gallium nitride semiconductor layer 77 corresponds to the first conductivity type gallium nitride semiconductor layer 35 described in the first embodiment, and similarly, the first region 77a and the second region Region 77b and a third region 77c. The first region 77a has a first threading dislocation density _{D 7} smaller dislocation density _{D 71.} The second region 67b has a first threading dislocation density _{D 7} is greater than the threading dislocation density _{D 72.} The third region 67c has a first threading dislocation density _{D 7} smaller dislocation density _{D 73.} In the IGBT transistor 81, for example, p-type Si, p-type SiC, p-type GaAs or the like can be used as the second conductive type semiconductor support base 83.

  In the above embodiment, the first and second electrodes 73a and 73b are connected to each other using the first wiring conductor 70, and the first gate electrode 71a and the second electrode are connected to each other using the second wiring conductor 74. Are connected to each other. However, the first gate electrode 71a and the second gate electrode 71b are connected to each other using the first wiring conductor 70, and the first and second electrodes 73a and 73b are connected to each other using the second wiring conductor 74. May be connected to each other.

An example of an IGBT transistor 81 is shown below:
Support base 83: p-type silicon first conductivity type gallium nitride semiconductor layer 77: n-type gallium nitride conductive region 65a, 65b: n-type gallium nitride well region 67a, 67b: p-type gallium nitride first gate electrode 71a, 71b: Ni, Pt, polysilicon, Al, Ti, W, Ir, transition metal silicide gate insulating layer 69a, 69b: Ga ₂ O ₃ , SiN, MgO, SiO ₂ , Sc ₂ O ₃ , Gd ₂ O ₃
First insulating layer 75: silicon nitride, thickness 1000 nm
Electrodes 73a and 73b: Ohmic electrodes, Al, transition metal silicide, Cu
The second electrode layer 31: ohmic electrode first protective insulating film 68: SiO ₂ (thickness 500 nm)
First wiring conductor 70: Al
Second protective insulating film 72: SiO ₂ (thickness 500 nm)
Second wiring conductor 74: Al

(Sixth embodiment)
A method for manufacturing a semiconductor device having two terminals will be described with reference to FIGS. As shown in FIG. 9, an n-type gallium nitride substrate 91 is prepared. The n-type gallium nitride substrate 91 includes a first region 91a and a second region 91b. The first region 91a and the second region 91b extend in the X-axis direction, and the first region 91a and the second region 91b are alternately arranged. Each of the first regions 91a is made of a gallium nitride single crystal, and each of the second regions 91b is made of a gallium nitride single crystal. The threading dislocation density D _A1 of the first region 91a is smaller than the threading dislocation density D _B1 of the second region 91b, and the threading dislocation density D _A1 of the first region 91a is a sufficiently good value for forming a semiconductor element. It is. Therefore, the first region 91a is called a low defect density region, and the second region 91b is called a high defect density region. For example, the C axis of the gallium nitride single crystal in the first region 91a is opposite to the C axis of the gallium nitride single crystal in the second region 91b.

  An n-type gallium nitride semiconductor film 93 is formed on the surface 91 d of the n-type gallium nitride substrate 91. This formation is performed using, for example, a metal organic chemical vapor deposition method. The n-type gallium nitride semiconductor film 93 is deposited, for example, on the first region 93a deposited on the first region 91a of the n-type gallium nitride substrate 91 and on the second region 93b of the n-type gallium nitride substrate 91. Second region 93b. The first region 93a and the second region 93b extend in the X-axis direction along the first region 91a and the second region 91b, respectively, and are alternately arranged in the Y-axis direction. The n-type gallium nitride semiconductor film 93 is, for example, 1 μm to 50 μm, preferably about 5 μm.

  Next, a groove 93 c is formed in the n-type gallium nitride semiconductor film 93. The grooves 93c extend in the X-axis direction along the second region 93b, and are alternately arranged in the Y-axis direction. The depth of the groove 93c of the n-type gallium nitride semiconductor film 93 is, for example, 0.01 μm to 10 μm, preferably 1 μm or less. The groove 93c is formed by, for example, photolithography and etching.

  As shown in FIG. 10, a silicon nitride film 95 is formed so as to cover the second region 93b. The silicon nitride film 95 extends in the X-axis direction along the second region 93b and the groove 93c, and is arranged on the n-type gallium nitride semiconductor film 93 in accordance with the arrangement of the second region 93b. The silicon nitride film 95 is obtained, for example, by depositing a SiN film by a vapor deposition method and then forming a pattern on the SiN film using a photolithography method. The film thickness of the SiN film is, for example, 0.01 μm to 10 μm, preferably 1 μm or less. When the silicon nitride film 95 is formed in the trench 93, a step generated by providing the silicon nitride film 95 can be reduced, and an electric field caused by an electrode provided in the vicinity of the step can be prevented from being locally increased. .

  If a p-type gallium nitride semiconductor film is grown prior to the nitride film growth for the silicon nitride film 95, a method for manufacturing a pn diode is provided. Further, if an i-type gallium nitride semiconductor film and a p-type gallium nitride semiconductor film are grown sequentially for the silicon nitride film 95 prior to the nitride film growth, a method for manufacturing a pin diode is provided.

  As shown in FIG. 11, a Schottky electrode 97 is formed on the first region 93 a of the n-type gallium nitride semiconductor film 93. The Schottky electrodes 97 extend in stripes along the first regions 93 a, and the Schottky electrodes 97 and the silicon nitride films 95 are alternately arranged on the n-type gallium nitride semiconductor film 93. Each of the Schottky electrodes 97 is separated from the silicon nitride film 95 without contacting the silicon nitride film 95. Each Schottky electrode 97 is formed in each of the gallium nitride regions 91a and 93a delimited by the second regions 91b and 93b. Through these steps, elements Diode1 and Diode2 are formed in each of the gallium nitride regions 91a and 93a separated by the second regions 91b and 93b.

  As shown in FIG. 12, a protective insulating film 96 is formed on the n-type gallium nitride semiconductor film 93, the Schottky electrode 97, and the silicon nitride film 95. The protective insulating film 96 has openings 96a, 96b, 96c, and 96d provided on the Schottky electrode 97, respectively. A Schottky electrode 97 is exposed in the openings 96a to 96d. The protective insulating film 96 is obtained, for example, by depositing a SiN film by a vapor deposition method and then forming a pattern on the SiN film using a photolithography method. The film thickness of the protective insulating film 96 is, for example, 0.01 μm to 10 μm. Preferably, it is 1 μm or less.

  As shown in FIG. 13, a wiring conductor 98 is formed on the protective insulating film 96. The wiring conductor 98 is electrically connected to the Schottky electrode 97 through the openings 96a, 96b, 96c, and 96d. An ohmic electrode 99 is formed on the back surface 91e of the n-type gallium nitride substrate 91. In addition, an alloying process is performed as needed. By these steps, the elements Diode1 and Diode2 formed in each of the gallium nitride regions 91a and 93a separated by the second regions 91b and 93b are connected. These elements Diode 1 and Diode 2 are connected in parallel by a wiring conductor 98 that goes over the insulating film 95 and the protective insulating film 96. Since the elements Diode1 and Diode2 are not directly formed on the high defect density region, the breakdown voltage is less likely to decrease due to the high defect density. Further, since the elements Diode 1 and Diode 2 are directly connected via the Schottky electrode 97, there is an advantage that a conductive material different from the material used for the Schottky electrode can be used as the wiring conductor. In order to operate as a high-power, low-loss device, the wiring conductor that short-circuits each diode needs to have a low resistance, but a low-resistance material such as Al, Cu, or Au is thickened and connected in parallel. As a result, the resistance can be reduced. At this time, these wiring conductors do not need to function as Schottky electrodes.

  As described above, according to the embodiment of the present invention, there is provided a method for manufacturing a diode having a structure capable of reducing the influence of the arrangement of the core portion having a high threading dislocation density and increasing the element area. .

(Seventh embodiment)
A method for manufacturing a semiconductor device having three terminals will be described with reference to FIGS. As shown in FIG. 14, an n-type gallium nitride substrate 101 is prepared. The n-type gallium nitride substrate 101 includes a first region 101a and a second region 101b. The first region 101a and the second region 101b extend in the X-axis direction, and the first region 101a and the second region 101b are alternately arranged. Each of the first regions 101a is made of a gallium nitride single crystal, and each of the second regions 101b is made of a gallium nitride single crystal. The threading dislocation density D _A2 of the first region 101a is lower than the threading dislocation density D _B2 of the second region 101b, and the threading dislocation density D _A2 of the first region 101a is a sufficiently good value for forming a semiconductor element. It is. Therefore, the first region 101a is called a low defect density region, and the second region 101b is called a high defect density region. For example, the C axis of the gallium nitride single crystal in the first region 101a is opposite to the C axis of the gallium nitride single crystal in the second region 101b.

  An n-type gallium nitride semiconductor film 103 is formed on the surface 101 d of the n-type gallium nitride substrate 101. This formation is performed using, for example, a metal organic chemical vapor deposition method. The n-type gallium nitride semiconductor film 103 is deposited, for example, on the first region 103 a deposited on the first region 101 a of the n-type gallium nitride substrate 101 and on the second region 101 b of the n-type gallium nitride substrate 101. And a second region 103b. The first region 103a and the second region 103b extend in the X-axis direction along the first region 101a and the second region 101b, respectively, and are alternately arranged in the Y-axis direction.

  As shown in FIG. 15, a groove 103 c is formed in the n-type gallium nitride semiconductor film 103. The grooves 103c extend in the X-axis direction along the second region 103b, and are alternately arranged in the Y-axis direction. The depth of the groove 103c of the n-type gallium nitride semiconductor film 103 is, for example, 0.01 μm to 10 μm, preferably 1 μm or less. The groove 103c is formed by, for example, photolithography and etching.

  Next, a silicon nitride film 105 is formed in the groove 103c so as to cover the second region 103b. The silicon nitride film 105 extends in the X-axis direction along the second region 103b, and is arranged on the n-type gallium nitride semiconductor film 103 in accordance with the arrangement of the second region 103b. The silicon nitride film 105 is obtained, for example, by depositing a SiN film by a vapor deposition method and then forming a pattern on the SiN film using a photolithography method. The thickness of the SiN film is, for example, 0.01 μm to 10 μm, preferably 1 μm or less.

  As shown in FIG. 16, a well region 107 is formed in the surface layer of the n-type gallium nitride semiconductor film 103. The well region 107 is formed, for example, by forming a recess in the first region 103a of the n-type gallium nitride semiconductor film 103 and depositing a p-type gallium nitride semiconductor in the recess. The concave portion is formed by, for example, forming an insulating film mask using photolithography and etching using the insulating film mask. The p-type gallium nitride based semiconductor is grown by selective growth by metal organic vapor phase epitaxy using an insulating film mask. By this selective growth, a well region 107 is formed in the recess. The well region 107 extends along the second region 103b. Between the two well regions 107, the first region 103a of the gallium nitride semiconductor film 103 is located. The depth of the well region 107 is, for example, about 0.5 μm to 5 μm.

  As shown in FIG. 17, an n-type gallium nitride semiconductor region 109 is formed in the surface layer of the well region 107. The n-type gallium nitride semiconductor region 109 is formed, for example, by forming a recess in the well region 107 and depositing an n-type gallium nitride based semiconductor in the recess. The recess is formed by, for example, forming an insulating film mask using photolithography and etching using the insulating film mask. Further, the n-type gallium nitride based semiconductor is grown by selective growth by metal organic vapor phase epitaxy using an insulating film mask. By this selective growth, an n-type gallium nitride semiconductor region 109 is formed in the recess. The n-type gallium nitride semiconductor region 109 extends along the second region 103b. Each of the n-type gallium nitride semiconductor regions 109 is separated from the first region 103a of the gallium nitride semiconductor film 103 by the well region 107, and the conductivity of the well region 107 is modulated, so that the n-type gallium nitride is modulated. The semiconductor region 109 is electrically connected to the first region 103 a of the gallium nitride semiconductor film 103. The depth of the n-type gallium nitride semiconductor region 109 is, for example, about 0.1 μm to 1 μm.

As shown in FIG. 18, a gate insulating film 111 is formed. As the gate insulating film 111, for example, gallium oxide, SiO ₂ , SiN, MgO, or the like can be used. After an insulating film for the gate insulating film 111 is deposited by, for example, a vapor deposition method, the gate insulating film 111 is formed by patterning the insulating film. By the patterning, the gate insulating film 111 is located on the well region 107, on the first region 103 a of the n-type gallium nitride semiconductor film 103 between the well regions 107, and on the n-type gallium nitride semiconductor region 109.

  As shown in FIG. 19, the current electrode 113 a is formed on the n-type gallium nitride semiconductor region 109. The electrode 113a is manufactured by depositing a conductive film using, for example, an electron beam evaporation method and a lift-off method, and then forming a pattern using a photolithography method. The electrode 113a is formed on the n-type gallium nitride semiconductor region 109, and makes an ohmic contact with the n-type gallium nitride semiconductor region 109 without contacting the gallium nitride semiconductor film 103 by performing an alloying process as necessary. . The electrode 113 a is formed on the well region 107 and makes electrical contact with the well region 107. The electrode 113 a is formed for each n-type gallium nitride semiconductor region 109 separated by the well region 107, and is separated from the insulating film 105 without overcoming the insulating film 105.

  As shown in FIG. 20, the gate electrode 115 is formed on the gate insulating film 111. The gate electrode 115 is formed on the well region 107 and the first region 103a of the n-type gallium nitride semiconductor film 103 between the well regions 107 so that the conductivity of the surface of the well region 107 can be modulated. Located on region 109.

  As shown in FIG. 21, a first protective insulating film 110 is formed. The first protective insulating film 110 has openings 110a, 110b, 110c, and 110d located on the electrode 113a. The openings 110a to 110d are obtained, for example, by depositing an insulating film by a vapor deposition method and then forming a pattern on the insulating film using a photolithography method and an etching technique. The film thickness of the first protective insulating film 110 is, for example, 0.01 μm to 10 μm. Preferably, it is 1 μm or less.

  As shown in FIG. 22, the first wiring conductor 112 is formed on the first protective insulating film 110. The first wiring conductor 112 connects the electrodes 113a to each other through the openings 110a, 110b, 110c, and 110d of the first protective insulating film 110. The first wiring conductor 112 is not formed on the gate electrode for the upper layer wiring. The first wiring conductor 112 connects the electrodes 113a in parallel.

  As shown in FIG. 23, a second protective insulating film 114 is formed on the first protective insulating film 110 and the first wiring conductor 112. The second protective insulating film 114 has openings 114 a and 114 b located on the gate electrode 111. The first protective insulating film 110 also has openings 110e and 110f located on the gate electrode 111. These openings 110e, 110f, 114a, and 114b are obtained by depositing an insulating film by, for example, a vapor deposition method and then forming a pattern on the insulating film by using a photolithography method and an etching technique. The film thickness of the second protective insulating film 114 is, for example, 0.01 μm to 10 μm. Preferably, it is 1 μm or less.

  As shown in FIG. 24, the second wiring conductor 116 is formed on the second protective insulating film 114. The second wiring conductor 116 connects the gate electrodes 111 to each other through the openings 114a, 114b, 110e, and 110f of the protective insulating films 110 and 114. Further, a conductive film 113b is formed on the back surface by vapor deposition or sputtering, and alloying is performed as necessary.

  Thus, the main process of manufacturing the vertical transistor has been described. If necessary, in place of the n-type gallium nitride substrate 101, a semiconductor substrate different from the gallium nitride based semiconductor is prepared, and after forming a mask on the main surface of the substrate, the n-type nitridation is performed on the substrate and the mask. A gallium semiconductor film can be deposited. This n-type gallium nitride semiconductor film corresponds to the n-type gallium nitride semiconductor film 103. The semiconductor substrate may have p-type conductivity.

  As a modification of the above manufacturing method, the first wiring conductor 112 is formed so as to connect the gate electrodes 111 to each other, and the second wiring conductor 116 is formed so as to connect the electrodes 113 to each other. Good. For this purpose, the opening of the first wiring conductor 112 is formed in accordance with the position of the gate electrode 111. The openings of the first wiring conductor 112 and the second wiring conductor 116 are formed in accordance with the position of the electrode 113.

  As described above, according to the embodiment of the present invention, it is possible to reduce the influence of the arrangement of the core portion having a high threading dislocation density, and to increase the element area. A method is provided for making a vertical transistor, such as an insulated gate bipolar transistor.

  While the principles of the invention have been illustrated and described in the preferred embodiments, it will be appreciated by those skilled in the art that the invention can be modified in arrangement and detail without departing from such principles. The present invention is not limited to the specific configuration disclosed in the present embodiment. For example, the individual film formation methods and etching methods described in the embodiments are examples, and the present invention is not limited to specific examples. We therefore claim all modifications and changes that come within the scope and spirit of the following claims.

FIG. 1 is a drawing showing a Schottky barrier diode of a semiconductor device according to an embodiment of the present invention. FIG. 2A is a diagram showing a modification of the Schottky barrier diode. FIG. 2B is a drawing showing another modification of the Schottky barrier diode. FIG. 3 is a drawing showing a pn junction diode of the semiconductor device according to the embodiment of the present invention. FIG. 4A is a diagram showing a modification of the pn junction diode. FIG. 4B is a drawing showing another modification of the pn junction diode. FIG. 5 is a drawing showing a pin junction diode of a semiconductor device according to an embodiment of the present invention. FIG. 6 is a drawing showing a vertical transistor according to the present embodiment. FIG. 7A illustrates a modification of the vertical transistor according to this embodiment. FIG. 7B is a drawing showing another modification of the vertical transistor according to the present exemplary embodiment. FIG. 8 is a view showing a vertical transistor according to the present embodiment. FIG. 9 is a drawing showing a step of forming a groove in a current barrier portion from epitaxial growth in a method of manufacturing a semiconductor device having two terminals. FIG. 10 is a drawing showing an insulating film growth step in the method for manufacturing the semiconductor device. FIG. 11 is a drawing showing an electrode forming step in the method for manufacturing the semiconductor device. FIG. 12 is a drawing showing a protective insulating film forming step in the method for manufacturing the semiconductor device. FIG. 13 is a drawing showing a wiring electrode forming step in the method for manufacturing the semiconductor device. FIG. 14 is a drawing showing an n-type semiconductor region forming step in a method for manufacturing a semiconductor device having three terminals. FIG. 15 is a drawing showing an insulating film growth step in the method for manufacturing the semiconductor device. FIG. 16 is a drawing showing a well region forming step in the method of manufacturing the semiconductor device. FIG. 17 is a drawing showing an n-type semiconductor region growth step in the method for manufacturing the semiconductor device. FIG. 18 is a drawing showing a gate insulating film growth step in the method for manufacturing the semiconductor device. FIG. 19 is a drawing showing an n-type semiconductor region electrode forming step in the method for manufacturing the semiconductor device. FIG. 20 is a drawing showing a gate electrode formation step in the method for manufacturing the semiconductor device. FIG. 21 is a drawing showing a first protective insulating film forming step in the method for manufacturing the semiconductor device. FIG. 22 is a drawing showing a first wiring electrode forming step in the method for manufacturing the semiconductor device. FIG. 23 is a drawing showing a second protective insulating film forming step in the method for manufacturing the semiconductor device. FIG. 24 is a drawing showing a second wiring electrode forming step and a back electrode forming step in the method for manufacturing the semiconductor device.

Explanation of symbols

DESCRIPTION OF SYMBOLS 11, 11a, 11b ... Schottky barrier diode, 13 ... Conductive substrate, 15 ... 1st conductivity type gallium nitride semiconductor layer, 15a, 15b, 15c ... Area | region of 1st conductivity type gallium nitride semiconductor layer, 17a, 17b ... Electrode, 18 ... protective insulating film, 19 ... first insulating layer, 20 ... wiring conductor, 21 ... second electrode layer, 23 ... gallium nitride based semiconductor support base, 23e ... groove, 25 ... second insulating layer, 27 ... Support base, 31 ... Second electrode layer, 33 ... Mask, 35 ... First conductivity type gallium nitride based semiconductor layer, 37a, 37b ... Electrode, 39 ... First insulating layer, 41, 41a, 41b ... pn Junction diode, 43 ... second conductivity type gallium nitride based semiconductor layer, 45a, 45b ... first electrode, 47 ... second conductivity type gallium nitride based semiconductor layer, 49a, 49b ... first electrode, 51 ... pin junction die 53, i-type gallium nitride based semiconductor layer, 61, 61a, 61b ... vertical transistor, 63 ... first conductive type gallium nitride based semiconductor layer, 65a ... first conductive region, 65b ... second conductive 67a ... first well region, 67b ... second well region, 68 ... first protective insulating film, 69a ... first gate insulating layer, 69b ... second gate insulating layer, 70 ... first Wiring conductor, 71a ... first gate electrode, 71b ... second gate electrode, 72 ... second protective insulating film, 73a, 73b ... electrode, 74 ... second wiring conductor, 75 ... first insulating layer , 77... First conductivity type gallium nitride based semiconductor layer, 81... IGBT transistor, 83... Second conductivity type semiconductor support base, D ₁ , D ₁₁ , D ₁₂ , D ₁₃ ... threading dislocation density, D ₂ , D ₂₁ , _D 22, _{D 23 ...} threading dislocation density _{D 3, D 31, D 32} , D 33 ... threading dislocation _{density, D 4, D 41, D} 42, D 43 ... threading dislocation _{density, D 5, D 51, D} 52, D 53 ... threading dislocation density, _{D 6} , D ₆₁ , D ₆₂ , D ₆₃ ... threading dislocation density, D ₇ , D ₇₁ , D ₇₂ , D ₇₃ ... threading dislocation density, J2 ... pin junction structure, J1 ... pn junction structure, SBD1, SBD2 ... Schottky junction diode Element, PND1, PND2 ... pn junction diode element, PIND1, PIND2 ... pin junction diode element, TRAN1, TRAN2 ... vertical transistor, IGBT1, IGBT2 ... vertical insulated gate bipolar transistor

Claims (10)

A semiconductor device using a nitride-based semiconductor,
A conductive substrate having a front surface and a back surface;
A first region having a threading dislocation density smaller than the first threading dislocation density; a second region having a threading dislocation density larger than the first threading dislocation density; and a threading dislocation smaller than the first threading dislocation density. A third region having a density, and a first conductivity type gallium nitride based semiconductor layer provided on the surface of the conductive substrate;
First and second electrodes forming Schottky junctions in the first and third regions of the first conductivity type gallium nitride based semiconductor layer,
Protective insulation provided on the first conductivity type gallium nitride based semiconductor layer and the first and second electrodes and having first and second openings respectively located on the first and second electrodes A membrane,
A wiring conductor provided on the protective insulating film and connected to the first and second electrodes through the first and second openings;
A first insulating layer provided between the second region of the first conductivity type gallium nitride based semiconductor layer and the protective insulating film;
A second electrode layer provided on the back surface of the conductive substrate;
With
A groove is provided on the surface of the first conductivity type gallium nitride based semiconductor layer in accordance with the position of the second region of the first conductivity type gallium nitride based semiconductor layer, and the first insulating layer is formed of the groove. Provided in
The protective insulating film and the first insulating layer are provided between the wiring conductor and the second region of the first conductivity type gallium nitride based semiconductor layer,
The first region of the first conductivity type gallium nitride based semiconductor layer is provided for a first element, and the third region of the first conductivity type gallium nitride based semiconductor layer is for a second device. Provided in
The second region of the first conductivity type gallium nitride based semiconductor layer is provided between the first region and the third region;
The semiconductor device is a Schottky barrier diode including the first and second elements. A semiconductor device using a nitride-based semiconductor,
A conductive substrate having a front surface and a back surface;
A first region having a threading dislocation density smaller than the first threading dislocation density; a second region having a threading dislocation density larger than the first threading dislocation density; and a threading dislocation smaller than the first threading dislocation density. A third region having a density, and a first conductivity type gallium nitride based semiconductor layer provided on the surface of the conductive substrate;
A first region having a threading dislocation density smaller than a second threading dislocation density; a second region having a threading dislocation density larger than the second threading dislocation density; and a threading dislocation smaller than the second threading dislocation density. A second region having a density, and a second conductivity type gallium nitride based semiconductor layer provided on the first conductivity type gallium nitride based semiconductor layer,
First and second electrodes forming ohmic junctions in the first and third regions of the second conductivity type gallium nitride based semiconductor layer,
Protective insulation provided on the second-conductivity-type gallium nitride based semiconductor layer and the first and second electrodes and having first and second openings respectively located on the first and second electrodes A membrane,
A wiring conductor provided on the protective insulating film and connected to the first and second electrodes through the first and second openings;
A first insulating layer provided between the second region of the first conductivity type gallium nitride based semiconductor layer and the protective insulating film;
A second electrode layer provided on the back surface of the conductive substrate;
With
A groove is provided on the surface of the second conductivity type gallium nitride based semiconductor layer in accordance with the position of the second region of the second conductivity type gallium nitride based semiconductor layer, and the first insulating layer is formed of the groove. Provided in
The protective insulating film and the first insulating layer are provided between the wiring conductor and the second region of the second conductivity type gallium nitride semiconductor layer,
The first regions of the first conductivity type gallium nitride semiconductor layer and the second conductivity type gallium nitride semiconductor layer are provided for a first element, and the first conductivity type gallium nitride semiconductor layer and the The third region of the second conductivity type gallium nitride based semiconductor layer is provided for the second element;
The first conductivity type gallium nitride based semiconductor layer and the second conductivity type gallium nitride based semiconductor layer constitute a pn junction structure,
The first region of the second conductivity type gallium nitride based semiconductor layer is provided on the first region of the first conductivity type gallium nitride based semiconductor layer;
The second region of the second conductivity type gallium nitride based semiconductor layer is provided on the second region of the first conductivity type gallium nitride based semiconductor layer,
The third region of the second conductivity type gallium nitride based semiconductor layer is provided on the third region of the first conductivity type gallium nitride based semiconductor layer;
The semiconductor device is a pn junction diode including the first and second elements. A semiconductor device using a nitride-based semiconductor,
A conductive substrate having a front surface and a back surface;
A first region having a threading dislocation density smaller than the first threading dislocation density; a second region having a threading dislocation density larger than the first threading dislocation density; and a threading dislocation smaller than the first threading dislocation density. A third region having a density, and a first conductivity type gallium nitride based semiconductor layer provided on the surface of the conductive substrate;
A first region having a threading dislocation density smaller than a second threading dislocation density; a second region having a threading dislocation density larger than the second threading dislocation density; and a threading dislocation smaller than the second threading dislocation density. A second region having a density, and a second conductivity type gallium nitride based semiconductor layer provided on the first conductivity type gallium nitride based semiconductor layer,
A first region having a threading dislocation density smaller than a third threading dislocation density; a second region having a threading dislocation density larger than the third threading dislocation density; and a threading dislocation smaller than the third threading dislocation density. A third region having a density, and an i-type gallium nitride semiconductor layer provided between the first conductivity type gallium nitride semiconductor layer and the second conductivity type gallium nitride semiconductor layer;
First and second electrodes forming ohmic junctions in the first and third regions of the second conductivity type gallium nitride based semiconductor layer,
Protective insulation provided on the second-conductivity-type gallium nitride based semiconductor layer and the first and second electrodes and having first and second openings respectively located on the first and second electrodes A membrane,
A wiring conductor provided on the protective insulating film and connected to the first and second electrodes through the first and second openings;
A first insulating layer provided between the second region of the second conductivity type gallium nitride based semiconductor layer and the protective insulating film;
A second electrode layer provided on the back surface of the conductive substrate;
With
A groove is provided on the surface of the second conductivity type gallium nitride based semiconductor layer in accordance with the position of the second region of the second conductivity type gallium nitride based semiconductor layer, and the first insulating layer is formed of the groove. Provided in
The protective insulating film and the first insulating layer are provided between the wiring conductor and the second region of the second conductivity type gallium nitride semiconductor layer,
The first regions of the first conductivity type gallium nitride based semiconductor layer, the i type gallium nitride based semiconductor layer, and the second conductivity type gallium nitride based semiconductor layer are provided for a first element, and The third region of the conductive gallium nitride based semiconductor layer, the i-type gallium nitride based semiconductor layer, and the second conductive gallium nitride based semiconductor layer is provided for a second element;
The first conductivity type gallium nitride based semiconductor layer, the i type gallium nitride based semiconductor layer and the second conductivity type gallium nitride based semiconductor layer constitute a pin junction structure,
The first region of the i-type gallium nitride semiconductor layer includes the first region of the first conductivity type gallium nitride semiconductor layer and the first region of the second conductivity type gallium nitride semiconductor layer. It is provided between
The second region of the i-type gallium nitride semiconductor layer includes the second region of the first conductivity type gallium nitride semiconductor layer and the second region of the second conductivity type gallium nitride semiconductor layer. It is provided between
The third region of the i-type gallium nitride semiconductor layer includes the third region of the first conductivity type gallium nitride semiconductor layer and the third region of the second conductivity type gallium nitride semiconductor layer. It is provided between
The semiconductor device is a pin junction diode including the first and second elements. A semiconductor device using a nitride-based semiconductor,
A conductive substrate having a front surface and a back surface;
A first region having a threading dislocation density smaller than the first threading dislocation density; a second region having a threading dislocation density larger than the first threading dislocation density; and a threading dislocation smaller than the first threading dislocation density. A third region having a density, and a first conductivity type gallium nitride based semiconductor layer provided on the surface of the conductive substrate;
First and second conductive regions made of a first conductivity type gallium nitride based semiconductor;
A first well region made of a second conductivity type gallium nitride semiconductor and provided between the first region and the first conductivity region of the first conductivity type gallium nitride semiconductor layer;
A second well region made of a second conductivity type gallium nitride semiconductor and provided between the third region and the second conductivity region of the first conductivity type gallium nitride semiconductor layer;
A first gate insulating layer provided on the first region and the first well region of the first conductivity type gallium nitride based semiconductor layer;
A second gate insulating layer provided on the third region and the second well region of the first conductivity type gallium nitride based semiconductor layer;
A first gate electrode provided on the first gate insulating layer;
A second gate electrode provided on the second gate insulating layer;
First and second electrodes forming ohmic junctions in the first and second conductive regions, respectively;
The first conductivity type gallium nitride based semiconductor layer, the first and second gate electrodes, and the first and second electrodes are provided on the first and second electrodes, respectively. A first protective insulating film having first and second openings;
A first wiring conductor provided on the first protective insulating film and connected to the first and second electrodes through the first and second openings;
A first insulating layer provided between the second region of the first conductivity type gallium nitride based semiconductor layer and the first protective insulating film;
A second protective insulating film provided on the first protective insulating film and the first wiring conductor;
The first protective insulating film is provided on the second protective insulating film, and the first and second openings of the second protective insulating film and the third and fourth openings of the first protective insulating film are used. A second wiring conductor connecting the gate electrode and the second gate electrode to each other;
A second electrode layer provided on the back surface of the conductive substrate;
With
A groove is provided on the surface of the first conductivity type gallium nitride based semiconductor layer in accordance with the position of the second region of the first conductivity type gallium nitride based semiconductor layer, and the first insulating layer is formed of the groove. Provided in
The first protective insulating film and the first insulating layer are provided between the first wiring conductor and the second region of the first conductivity type gallium nitride based semiconductor layer,
The first region of the first conductivity type gallium nitride based semiconductor layer is provided for a first element, and the third region of the first conductivity type gallium nitride based semiconductor layer is for a second device. Provided in
The second region of the first conductivity type gallium nitride based semiconductor layer is provided between the first region and the third region;
The semiconductor device is a vertical transistor including the first and second elements. A semiconductor device using a nitride semiconductor,
A conductive substrate made of a semiconductor material different from a gallium nitride based semiconductor and having a front surface and a back surface;
A first region having a threading dislocation density smaller than the first threading dislocation density; a second region having a threading dislocation density larger than the first threading dislocation density; and a threading dislocation smaller than the first threading dislocation density. A first conductivity type gallium nitride based semiconductor layer provided on the surface of the conductive substrate and including a third region having a density;
First and second conductive regions made of a first conductivity type gallium nitride based semiconductor;
A first well region made of a second conductivity type gallium nitride semiconductor and provided between the first region and the first conductivity region of the first conductivity type gallium nitride semiconductor layer;
A second well region made of a second conductivity type gallium nitride semiconductor and provided between the third region and the second conductivity region of the first conductivity type gallium nitride semiconductor layer;
A first gate insulating layer provided on the first region and the first well region of the first conductivity type gallium nitride based semiconductor layer;
A second gate insulating layer provided on the third region and the second well region of the first conductivity type gallium nitride based semiconductor layer;
A first gate electrode provided on the first gate insulating layer;
A second gate electrode provided on the second gate insulating layer;
First and second electrodes forming ohmic junctions in the first and second conductive regions, respectively;
The first conductivity type gallium nitride based semiconductor layer, the first and second gate electrodes, and the first and second electrodes are provided on the first and second electrodes, respectively. A first protective insulating film having first and second openings;
A first wiring conductor provided on the first protective insulating film and connected to the first and second electrodes through the first and second openings;
A first insulating layer provided between the second region of the first conductivity type gallium nitride based semiconductor layer and the first protective insulating film;
A second protective insulating film provided on the first protective insulating film and the first wiring conductor;
The first protective insulating film is provided on the second protective insulating film, and the first and second openings of the second protective insulating film and the third and fourth openings of the first protective insulating film are used. A second wiring conductor connecting the gate electrode and the second gate electrode to each other;
A mask made of a material different from that of the gallium nitride based semiconductor and provided between the first and third regions of the first conductivity type gallium nitride based semiconductor layer and the conductive substrate ,
A second electrode layer provided on the back surface of the conductive substrate;
With
A groove is provided on the surface of the first conductivity type gallium nitride based semiconductor layer in accordance with the position of the second region of the first conductivity type gallium nitride based semiconductor layer, and the first insulating layer is formed of the groove. Provided in
The first protective insulating film and the first insulating layer are provided between the first wiring conductor and the second region of the first conductivity type gallium nitride based semiconductor layer,
The first region of the first conductivity type gallium nitride based semiconductor layer is provided for a first element, and the third region of the first conductivity type gallium nitride based semiconductor layer is for a second device. Provided in
The semiconductor device according to claim 1, wherein the conductive substrate has a second conductivity type, and the semiconductor device is a vertical insulated gate bipolar transistor including the first and second elements. The first to third regions of the first conductivity type gallium nitride based semiconductor layer extend in a first direction;
6. The first to third regions of the first conductivity type gallium nitride based semiconductor layer are arranged in a second direction intersecting the first direction. A semiconductor device according to any one of the above. The conductive substrate includes a first region having a threading dislocation density smaller than a predetermined threading dislocation density, a second region having a threading dislocation density larger than the predetermined threading dislocation density, and the predetermined threading dislocation density. A gallium nitride based semiconductor support substrate including a third region having a low threading dislocation density;
The first region of the first conductivity type gallium nitride based semiconductor layer is provided on the first region of the gallium nitride based semiconductor support base;
The second region of the first conductivity type gallium nitride based semiconductor layer is provided on the second region of the gallium nitride based semiconductor support base;
The third region of the first conductivity type gallium nitride based semiconductor layer is provided on the third region of the gallium nitride based semiconductor support base;
The said 2nd electrode layer forms ohmic junction in the said 1st and 3rd area | region in the back surface of the said gallium nitride semiconductor support base | substrate, The Claim 1 characterized by the above-mentioned. The semiconductor device described.   The semiconductor device according to claim 7, further comprising a second insulating layer provided between the second region of the gallium nitride based semiconductor support base and the second electrode layer. .   9. The semiconductor device according to claim 7, wherein the gallium nitride based semiconductor support base is made of gallium nitride. Further comprising a mask made of a material different from that of the gallium nitride based semiconductor and provided between the first and third regions of the first conductivity type gallium nitride based semiconductor layer and the conductive substrate,
The semiconductor device according to claim 1, wherein the conductive substrate is made of a semiconductor material different from a gallium nitride based semiconductor.