JP4134457B2 - Photosensitive resin precursor composition - Google Patents

Photosensitive resin precursor composition Download PDF

Info

Publication number
JP4134457B2
JP4134457B2 JP28548299A JP28548299A JP4134457B2 JP 4134457 B2 JP4134457 B2 JP 4134457B2 JP 28548299 A JP28548299 A JP 28548299A JP 28548299 A JP28548299 A JP 28548299A JP 4134457 B2 JP4134457 B2 JP 4134457B2
Authority
JP
Japan
Prior art keywords
general formula
carbon atoms
organic group
mol
precursor composition
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Expired - Fee Related
Application number
JP28548299A
Other languages
Japanese (ja)
Other versions
JP2000187317A5 (en
JP2000187317A (en
Inventor
真佐夫 富川
良治 奥田
陽二 藤田
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Toray Industries Inc
Original Assignee
Toray Industries Inc
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Toray Industries Inc filed Critical Toray Industries Inc
Priority to JP28548299A priority Critical patent/JP4134457B2/en
Publication of JP2000187317A publication Critical patent/JP2000187317A/en
Publication of JP2000187317A5 publication Critical patent/JP2000187317A5/ja
Application granted granted Critical
Publication of JP4134457B2 publication Critical patent/JP4134457B2/en
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Description

【0001】
【発明の属する技術分野】
この発明は、半導体素子の表面保護膜、層間絶縁膜などに適した紫外線で露光した部分がアルカリ水溶液に溶解するポジ型の感光性ポリイミド前駆体組成物に関する。
【0002】
【従来の技術】
露光した部分が現像により溶解するポジ型の耐熱性樹脂前駆体組成物としては、ポリアミド酸にナフトキノンジアジドを添加したもの(特開昭52−13315号公報)、水酸基を有した可溶性ポリイミドにナフトキノンジアジドを添加したもの(特開昭64−60630号公報)、水酸基を有したポリアミドにナフトキノンジアジドを添加したもの(特開昭56−27140号公報)などが知られていた。
【0003】
しかしながら、通常のポリアミド酸にナフトキノンジアジドを添加したものではナフトキノンジアジドのアルカリに対する溶解阻害効果よりポリアミド酸のカルボキシル基の溶解性が高いために、ほとんどの場合希望するパターンを得ることが出来ないという問題点があった。また、水酸基を有した可溶性ポリイミド樹脂を添加したものでは、今述べたような問題点は少なくなったものの、可溶性にするために構造が限定されること、得られるポリイミド樹脂の耐溶剤性が悪い点などが問題であった。
【0004】
以上の欠点を考慮し、本発明はポリイミド前駆体に新規ナフトキノンジアジド化合物を添加することで、得られる樹脂組成物が、露光前はアルカリ現像液にほとんど溶解せず、露光すると容易にアルカリ現像液に溶解するために、現像による膜減りが少なく、かつ短時間に現像できることを見いだし、発明に至ったものである。
【0005】
【発明が解決しようとする課題】
本発明は、特定の構造を有したポリイミド前駆体に特定のナフトキノンジアジド化合物を加えることで、現像による未露光部の膜減りが少なく、かつ短時間で現像できるポジ型の耐熱性樹脂組成物を提供することにある。
【0006】
【課題を解決するための手段】
本発明は(a)一般式(1)で表される構造単位を主成分とするポリマーと、(b)一般式(2)で表される少なくとも1つのキノンジアジド化合物を含有することを特徴とする感光性樹脂前駆体組成物である。
【0007】
【化7】

Figure 0004134457
【0008】
(一般式(1)のR1は少なくとも2個以上の炭素原子を有する3価から8価の有機基を示し、R2は、少なくとも2個以上の炭素原子を有する2価から6価の有機基を示し、R3は水素、または炭素数1から10までの有機基を示す。nは10から100000までの整数、mは1から2までの整数、p、qは0から4までの整数である。pとqは同時に0になることはない。)
【0009】
【化8】
Figure 0004134457
【0010】
(一般式(2)中、1つのキノンジアジド化合物においてQの全てが水素原子になることはない。)
【0011】
【発明の実施の形態】
本発明における一般式(1)で表される構造単位を主成分とするポリマーとは、加熱あるいは適当な触媒により、イミド環、オキサゾール環、その他の環状構造を有するポリマーとなり得るものである。環構造となることで、耐熱性、耐溶剤性が飛躍的に向上する。
【0012】
上記一般式(1)は、水酸基を有したポリアミド酸を表しており、この水酸基の存在のために、アルカリ水溶液に対する溶解性が水酸基を有さないポリアミド酸よりも良好になる。特に、水酸基の中でもフェノール性の水酸基がアルカリ水溶液に対する溶解性より好ましい。また、フッ素原子を一般式(1)中に10重量%以上有することで、アルカリ水溶液で現像する際に、膜の界面に撥水性が適度に出るために、界面のしみこみなどが抑えられる。しかしながら、フッ素原子含有量が20重量%を越えると、アルカリ水溶液に対する溶解性が低下すること、熱処理により環状構造にしたポリマーの耐有機溶媒性が低下すること、発煙硝酸に対する溶解性が低下するために好ましくない。このように、フッ素原子は10重量%から20重量%含まれることが好ましい。
【0013】
上記一般式(1)中、R1(OH)p(COOR3)mは酸の構造成分を表しており、この基は芳香族環を含有し、かつ、水酸基を1個から4個有した、炭素数2以上の3価または8価の基が好ましい。
【0014】
具体的には、一般式(3)に示されるような構造のものが好ましく、この場合、R、Rは炭素数2から20より選ばれる3から4価の有機基を表している。特に得られるポリマーの耐熱性より芳香族環を含んだものが好ましく、その中でも特に好ましい構造としてトリメリット残基、トリメシン酸残基、ナフタレントリカルボン酸残基のようなものを挙げることができる。またR は炭素数3から20の3価から6価の有機基が好ましい。さらに、水酸基はアミド結合と隣り合った位置にあることが好ましい。このような例として、フッ素原子を含んだ、ビス(3−アミノ−4−ヒドロキシフェニル)ヘキサフルオロプロパン残基、ビス(3−ヒドロキシ−4−アミノフェニル)ヘキサフルオロプロパン残基、フッ素原子を含まない、ビス(3−アミノ−4−ヒドロキシフェニル)プロパン残基、ビス(3−ヒドロキシ−4−アミノフェニル)プロパン残基、3,3’−ジアミノ−4,4’−ジヒドロキシビフェニル残基、3,3’−ジアミノ−4,4’−ジヒドロキシビフェニル残基、2,4−ジアミノ−フェノール残基、2,5−ジアミノフェノール残基、1,4−ジアミノ−2,5−ジヒドロキシベンゼン残基のアミノ基が結合したものなどを挙げることができる。
【0015】
また、R7、R8は水素、あるいは炭素数1から10の有機基が良い。炭素数10以上になるとアルカリ現像液に対する溶解性が低下する。
【0016】
u、wは1であり、vは1から4までの整数を表している。vが5以上になると、得られる耐熱性樹脂膜の特性が低下する。
【0017】
一般式(3)で表される構造の中で、好ましい構造を例示すると下記に示したような構造が挙げられるが、これらに限定されない。
【0018】
【化9】
Figure 0004134457
【0019】
2(OH)q成分のqが1以上のものを使用する場合、水酸基を有していないテトラカルボン酸残基、トリカルボン酸残基も使用することもできる。このようなものの例としては、ピロメリット酸残基、ベンゾフェノンテトラカルボン酸残基、ビフェニルテトラカルボン酸残基、ジフェニルエーテルテトラカルボン酸残基、ジフェニルスルホンテトラカルボン酸残基などの芳香族テトラカルボン酸残基やそのカルボキシル基2個をメチル基やエチル基にしたジエステル化合物、ブタンテトラカルボン酸残基、シクロペンタンテトラカルボン酸残基などの脂肪族のテトラカルボン酸残基やそのカルボキシル基2個をメチル基やエチル基にしたジエステル化合物、トリメリット酸残基、トリメシン酸残基などの芳香族トリカルボン酸残基などを挙げることができる。
【0020】
また、アルカリに対する溶解性、感光性能、耐熱性を損なわない範囲で、テレフタル酸、イソフタル酸、ジフェニルエーテルジカルボン酸、ナフタレンジカルボン酸などの芳香族ジカルボン酸、アジピン酸などの脂肪族ジカルボン酸などで変性することが出来る。これらは、酸成分の50モル%以下の変性が好ましいが、さらに好ましくは30モル%以下である。
【0021】
上記一般式(1)中、R2(OH)qはジアミンの構造成分を表している。この中で、R2(OH)qの好ましい例としては、得られるポリマーの耐熱性より芳香族を有し、かつ水酸基を有するものが好ましく、具体的な例としてはフッ素原子を有した、ビス(アミノ−ヒドロキシ−フェニル)ヘキサフルオロプロパン残基、フッ素原子を有さない、ジアミノジヒドロキシピリミジン残基、ジアミノジヒドロキシピリジン残基、ヒドロキシ−ジアミノ−ピリミジン残基、ジアミノフェノール残基、ジヒドロキシベンチジン残基などの化合物や一般式(4)、(5)、(6)に示す構造のものをあげることができる。
【0022】
一般式(4)において、R、R11は炭素数2から20の3価から4価の有機基を示しており、得られるポリマーの耐熱性より芳香族環を有したものが好ましい。−R (OH)r−、−R 11 (OH)s−として、具体的には下記に示されたものを挙げることができる。
【0023】
【化10】
Figure 0004134457
【0024】
(aは1から4の整数、b、cは0から4の整数であり、b+cは1以上である。
【0025】
また、ヒドロキシシクロヘキシル基、ジヒドロキシシクロヘキシル基などの脂肪族の基も使用することができる。R10は炭素数2から30の2価の有機基を表している。得られるポリマーの耐熱性よりは芳香族を有した2価の基がよく、このような例を下記に示す。
【0026】
【化11】
Figure 0004134457
【0027】
一般式(5)において、R12、R14は炭素数2から20の2価の有機基を表している。得られるポリマーの耐熱性よりは芳香族を有した2価の基がよく、このようなものとしては上記一般式(4)のR10の具体例に例示したものと同様のものを挙げることができる。R13、炭素数3から20より選ばれる3価から6価の有機基を示しており、得られるポリマーの耐熱性より芳香族環を有したものが好ましい。−R 13 (OH)z−としては上記一般式(4)の−R (OH)r−、−R 11 (OH)s−の具体例に例示したものと同様のものを挙げることができる。
【0028】
一般式(6)においてR15は炭素数2から20の2価の有機基を表している。得られるポリマーの耐熱性よりは芳香族を有した2価の基がよく、このようなものとしては上記一般式(4)のR10の具体例に例示したものと同様のものを挙げることができる。R16 は3価から6価の有機基を示しており、得られるポリマーの耐熱性より芳香族環を有したものが好ましい。−R 16 (OH)t−としては上記一般式(4)のR、R11の具体例に例示したものと同様のものを挙げることができる。
【0029】
一般式(4)で表されるものの具体的な例を下記に示す。
【0030】
【化12】
Figure 0004134457
【0031】
一般式(5)で表されるものの具体的な例を下記に示す。
【0032】
【化13】
Figure 0004134457
【0033】
一般式(6)で表されるものの具体的な例を下記に示す。
【0034】
【化14】
Figure 0004134457
【0035】
また、R1(OH)p(COOR3)mのpが1から4のいずれかである時は、水酸基の無いジアミン成分を使用することもできる。この例を下記に示す。
【0036】
【化15】
Figure 0004134457
【0037】
一般式(1)のR3は水素、あるいは炭素数1から10の有機基を表している。得られる感光性樹脂前駆体溶液の安定性からは、R3は有機基が好ましいが、アルカリ水溶液の溶解性より見ると水素が好ましい。本発明においては、水素原子とアルキル基を混在させることができる。このR3の水素と有機基の量を制御することで、アルカリ水溶液に対する溶解速度が変化するので、この調整により適度な溶解速度を有した感光性樹脂前駆体組成物を得ることが出来る。R3は全てが水素原子、全て有機基でも良いが、より好ましい範囲は、R3の10%から90%が水素原子であることである。R3の炭素数が10を越えるとアルカリ水溶液に溶解しなくなる。
【0038】
さらに、基板との接着性を向上させるために、耐熱性を低下させない範囲で R1(OH)p(COOR3)m、R2(OH)qにシロキサン構造を有する脂肪族の基を共重合してもよい。具体的には、R1(OH)p(COOR3)mとして、下記に示したものを1から20モル%共重合したものを挙げることができる。
【0039】
【化16】
Figure 0004134457
【0040】
2(OH)q成分として、ビス(3−アミノプロピル)テトラメチルジシロキサン残基、ビス(4−アミノフェニル)オクタメチルペンタシロキサン残基、α、ω−ビス(3−アミノプロピル)パーメチルポリシロキサン残基などを1〜20モル%共重合したものなどがあげられる。
【0041】
3は、炭素数1から16までの炭化水素基を少なくとも1つ以上含有し、その他は水素原子であることが好ましい。
【0042】
本発明のポリマーは一般式(1)で表される構造単位のみからなるものであっても良いし、他の構造単位との共重合体あるいはブレンド体であっても良い。その際、一般式(1)で表される構造単位を90モル%以上含有していることが好ましい。共重合あるいはブレンドに用いられる構造単位の種類および量は最終加熱処理によって得られるポリイミド系ポリマの耐熱性を損なわない範囲で選択することが好ましい。
【0043】
本発明の感光性樹脂前駆体組成物の合成例としては、低温中でテトラカルボン酸2無水物とジアミン化合物を反応させる方法(C.E.Sroogら、Journal Polymer Science誌、PartA−3、1373(1965))、テトラカルボン酸2無水物とアルコールとによりジエステルを得、その後アミンと縮合剤の存在下で反応させる方法(特開昭61−72022号公報)、テトラカルボン酸2無水物とアルコールとによりジエステルを得、その後残りのジカルボン酸を酸クロリド化し、アミンと反応させる方法(特開昭55−30207号公報)などで合成することができる。
【0044】
本発明において、添加されるナフトキノンジアジド化合物としては、一般式(2)に示されるものである。このような構造の化合物を添加することで、現像後の未露光部の膜減りが大幅に低下し、良好なパターンを短い現像時間で得ることが出来る。一般式(2)で示される1つのキノンジアジド化合物において、Qの水素原子が増加すると一般式(2)で表される感光剤の、アルカリ現像液に対する溶解性が高まるために、一般式(1)で表されるポリマーを保護する効果が低下する。このような点から見ると、水素原子である割合は1/3以下が好ましく、さらに好ましくは1/5以下である。また、水素原子以外のものとしては、4−ナフトキノンジアジドスルホニル基、5−ナフトキノンジアジドスルホニル基を挙げることが出来る。4−ナフトキノンジアジドスルホニル基は水銀灯のi線領域に吸収を持っており、i線露光に適しており、5−ナフトキノンジアジドスルホニル基は水銀灯のg線領域まで吸収が伸びており、g線露光に適している。本発明においては、4−ナフトキノンジアジドスルホニル基、5−ナフトキノンジアジドスルホニル基のどちらも好ましく使用することが出来るが、露光する波長によって4−ナフトキノンジアジドスルホニル基、5−ナフトキノンジアジドスルホニル基を選択することが好ましい。また、同一分子中に4−ナフトキノンジアジドスルホニル基、5−ナフトキノンジアジドスルホニル基を併用して導入することもできるし、4−ナフトキノンジアジドスルホニル基を感光基として導入した感光剤と5−ナフトキノンジアジドスルホニル基を感光基として導入した感光剤を混合して使用することもできる。
【0045】
本発明における一般式(2)で表される感光剤としては、1種類の構造のものを使用してもよいし、複数の構造のものを混合して使用してもよい。
【0049】
また、必要に応じて上記、感光性樹脂前駆体組成物と基板との塗れ性を向上させる目的で界面活性剤、乳酸エチルやプロピレングリコールモノメチルエーテルアセテートなどのエステル類、エタノールなどのアルコール類、シクロヘキサノン、メチルイソブチルケトンなどのケトン類、テトラヒドロフラン、ジオキサンなどのエーテル類を混合しても良い。また、2酸化ケイ素、2酸化チタンなどの無機粒子、あるいはポリイミドの粉末などを添加することもできる。
【0050】
さらにシリコンウエハなどの下地基板との接着性を高めるために、シランカップリング剤、チタンキレート剤などを感光性樹脂前駆体組成物のワニスに0.5から10重量%添加したり、下地基板をこのような薬液で前処理したりすることもできる。
【0051】
ワニスに添加する場合、メチルメタクリロキシジメトキシシラン、3−アミノプロピルトリメトキシシラン、などのシランカップリング剤、チタンキレート剤、アルミキレート剤をワニス中のポリマーに対して0.5から10重量%添加する。
【0052】
基板を処理する場合、上記で述べたカップリング剤をイソプロパノール、エタノール、メタノール、水、テトラヒドロフラン、プロピレングリコールモノメチルエーテルアセテート、プロピレングリコールモノメチルエーテル、乳酸エチル、アジピン酸ジエチルなどの溶媒に0.5から20重量%溶解させた溶液をスピンコート、浸漬、スプレー塗布、蒸気処理などで表面処理をする。場合によっては、その後50℃から300℃までの温度をかけることで、基板と上記カップリング剤との反応を進行させる。
【0053】
次に、本発明の感光性樹脂前駆体組成物を用いて耐熱性樹脂パターンを形成する方法について説明する。
【0054】
感光性樹脂前駆体組成物を基板上に塗布する。基板としてはシリコンウエハ、セラミックス類、ガリウムヒ素などが用いられるが、これらに限定されない。塗布方法としてはスピンナを用いた回転塗布、スプレー塗布、ロールコーティングなどの方法がある。また、塗布膜厚は、塗布手法、組成物の固形分濃度、粘度などによって異なるが通常、乾燥後の膜厚が、0.1から150μmになるように塗布される。
【0055】
次に感光性樹脂前駆体組成物を塗布した基板を乾燥して、感光性樹脂前駆体組成物皮膜を得る。乾燥はオーブン、ホットプレート、赤外線などを使用し、50度から150度の範囲で1分から数時間行うのが好ましい。
【0056】
次に、この感光性樹脂前駆体組成物皮膜上に所望のパターンを有するマスクを通して化学線を照射し、露光する。露光に用いられる化学線としては紫外線、可視光線、電子線、X線などがあるが、本発明では水銀灯のi線(365nm)、h線(405nm)、g線(436nm)を用いるのが好ましい。
【0057】
耐熱性樹脂のパターンを形成するには、露光後、現像液を用いて露光部を除去することによって達成される。現像液としては、テトラメチルアンモニウムの水溶液、ジエタノールアミン、ジエチルアミノエタノール、水酸化ナトリウム、水酸化カリウム、炭酸ナトリウム、炭酸カリウム、トリエチルアミン、ジエチルアミン、メチルアミン、ジメチルアミン、酢酸ジメチルアミノエチル、ジメチルアミノエタノール、ジメチルアミノエチルメタクリレート、シクロヘキシルアミン、エチレンジアミン、ヘキサメチレンジアミンなどのアルカリ性を示す化合物の水溶液が好ましい。また場合によっては、これらのアルカリ水溶液にN−メチル−2−ピロリドン、N,N−ジメチルホルムアミド、N,N−ジメチルアセトアミド、ジメチルスルホキシド、γ−ブチロラクロン、ジメチルアクリルアミドなどの極性溶媒、メタノール、エタノール、イソプロパノールなどのアルコール類、乳酸エチル、プロピレングリコールモノメチルエーテルアセテートなどのエステル類、シクロペンタノン、シクロヘキサノン、イソブチルケトン、メチルイソブチルケトンなどのケトン類などを単独あるいは数種を組み合わせたものを添加してもよい。現像後は水にてリンス処理をする。ここでもエタノール、イソプロピルアルコ−ルなどのアルコール類、乳酸エチル、プロピレングリコールモノメチルエーテルアセテートなどのエステル類などを水に加えてリンス処理をしても良い。
【0058】
現像後、200度から500度の温度を加えて耐熱性樹脂皮膜に変換する。この加熱処理は温度を選び、段階的に昇温するか、ある温度範囲を選び連続的に昇温しながら5分から5時間実施する。一例としては、130度、200度、350度で各30分ずつ熱処理する。あるいは室温より400度まで2時間かけて直線的に昇温するなどの方法が挙げられる。
【0059】
本発明による感光性樹脂前駆体組成物により形成した耐熱性樹脂皮膜は、半導体のパッシベーション膜、半導体素子の保護膜、高密度実装用多層配線の層間絶縁膜などの用途に用いられる。
【0060】
【実施例】
以下発明をより詳細に説明するために、実施例で説明するが、本発明はこれに限定されない。
特性の測定方法
膜厚の測定
大日本スクリーン製造社製ラムダエースSTM−602を使用し、屈折率1.64で測定を行った。
【0061】
合成例1 ナフトキノンジアジド化合物(1)の合成
乾燥窒素気流下、1,1,2,2−テトラ(4−ヒドロキシフェニル)エタン19.9g(0.05モル)と4−ナフトキノンジアジドスルホニル酸クロリド47.0g(0.175モル)を1,4−ジオキサン500gに溶解させ、40℃に加熱した。ここに、1,4−ジオキサン50gと混合させたトリエチルアミン17.7g(0.175モル)を系内の温度が45度以上にならないように滴下した。滴下後40度で2時間攪拌した。副生したトリエチルアミンの塩酸塩を濾過し、ろ液を1%塩酸3lに投入させた。その後、析出した沈殿をろ過で集めた。さらに、水10lで洗浄を2度繰り返し、50℃の真空乾燥機で20時間乾燥させ、ナフトキノンジアジド化合物(1)を得た。
【0062】
【化18】
Figure 0004134457
【0063】
合成例2 ナフトキノンジアジド化合物(2)の合成
乾燥窒素気流下、1,1,2−トリ(3−メチル−4−ヒドロキシフェニル)エタン17.4g(0.05モル)と5−ナフトキノンジアジドスルホニル酸クロリド34.9g(0.13モル)を1,4−ジオキサン400gに溶解させ、40℃に加熱した。ここに、1,4−ジオキサン40gと混合させたトリエチルアミン13.1g(0.13モル)を系内の温度が45℃以上にならないように滴下した。滴下後40℃で2時間攪拌した。副生したトリエチルアミンの塩酸塩を濾過し、ろ液を1%塩酸3lに投入した。その後、析出した沈殿をろ過で集めた。この沈殿を10lの水で2回洗浄し、50℃の真空乾燥機で20時間乾燥させ、ナフトキノンジアジド化合物(2)を得た。
【0064】
【化19】
Figure 0004134457
【0065】
合成例3 ナフトキノンジアジド化合物(3)の合成
乾燥窒素気流下、1,1,2−トリ(3、5−ジメチル−4−ヒドロキシフェニル)プロパン20.2g(0.05モル)と5−ナフトキノンジアジドスルホニル酸クロリド37.6g(0.14モル)を1,4−ジオキサン400gに溶解させ、40℃に加熱した。ここに、1,4−ジオキサン40gと混合させたトリエチルアミン14.2g(0.14モル)を系内の温度が45℃以上にならないように滴下した。滴下後40℃で2時間攪拌した。副生したトリエチルアミンの塩酸塩を濾過し、ろ液を1%塩酸3lに投入した。その後、析出した沈殿をろ過で集めた。水10lでこの沈殿を2回洗浄を繰り返し、50℃の真空乾燥機で20時間乾燥させ、ナフトキノンジアジド化合物(3)を得た。
【0066】
【化20】
Figure 0004134457
【0067】
合成例4 ナフトキノンジアジド化合物(4)の合成
乾燥窒素気流下、4,4’,4’’,4’’’−(1、4−フェニレンジメチリデン)テトラキス(2、6−ジメチルフェノール)29.3g(0.05モル)と4−ナフトキノンジアジドスルホニル酸クロリド43.0g(0.16モル)を1,4−ジオキサン700gに溶解させ、40℃に加熱した。ここに、1,4−ジオキサン60gと混合させたトリエチルアミン16.2g(0.16モル)を系内の温度が45℃以上にならないように滴下した。滴下後40℃で2時間攪拌した。副生したトリエチルアミンの塩酸塩をろ過し、ろ液を1%塩酸3lに投入した。その後、析出した沈殿をろ過で集めた。この沈殿を10lの水で2回洗浄し、50℃の真空乾燥機で20時間乾燥させ、ナフトキノンジアジド化合物(4)を得た。
【0068】
【化21】
Figure 0004134457
【0069】
合成例5 ヒドロキシル基含有酸無水物の合成
乾燥窒素気流下、2,2−ビス(3−アミノ−4−ヒドロキシフェニル)ヘキサフルオロプロパン(BAHF)18.3g(0.05モル)とアリルグリシジルエーテル34.2g(0.3モル)をガンマブチロラクトン(GBL)100gに溶解させ、−15℃に冷却した。ここにGBL50gに溶解させた無水トリメリット酸クロリド22.1g(0.11モル)を反応液の温度が0℃を越えないように滴下した。滴下終了後、0℃で4時間反応させた。
【0070】
この溶液をロータリーエバポレーターで濃縮して、トルエン1lに投入して酸無水物(1)を得た。得られた物質は350℃までに明確な融点が見られなかった。
【0071】
【化22】
Figure 0004134457
【0072】
合成例6 ヒドロキシル基含有ジアミン化合物(1)の合成
BAHF18.3g(0.05モル)をアセトン100ml、プロピレンオキシド17.4g(0.3モル)に溶解させ、−15℃に冷却した。ここに4−ニトロベンゾイルクロリド20.4g(0.11モル)をアセトン100mlに溶解させた溶液を滴下した。滴下終了後、−15℃で4時間反応させ、その後室温に戻した。溶液をロータリーエバポレーターで濃縮し、得られた固体を水とアセトンで洗浄し、80℃の真空乾燥機で乾燥した。
【0073】
乾燥させた固体を25gと5%パラジウム−炭素2gを500mlのオートクレーブにメチルセロソルブ300mlとともに加えた。ここに、水素を圧力8kgf/cm2で加圧し、温度を60℃にまで上昇させて水素をこれ以上吸収しない段階まで攪拌を続けた。水素を吸収しなくなってから、10分攪拌した後、加熱を停止し、温度が30℃以下になったところで、容器の圧力を放圧し、反応を停止させた。反応終了後、溶液をろ過して、ろ液を水1lに投入して、目的物の沈殿を得た。これを50℃の真空乾燥機で20時間乾燥させた。
【0074】
【化23】
Figure 0004134457
【0075】
合成例7 ヒドロキシル基含有ジアミン(2)の合成
2−アミノ−4−ニトロフェノール30.8g(0.2モル)をアセトン200ml、プロピレンオキシド60g(0.68モル)に溶解させ、−15℃に冷却した。ここにイソフタル酸クロリド22.4g(0.11モル)をアセトン200mlに溶解させた溶液を徐々に滴下した。滴下終了後、−15℃で4時間反応させた。その後、室温に戻して生成している沈殿をろ過で集めた。
【0076】
乾燥させた沈殿30gと5%パラジウム−炭素3gを500mlのオートクレーブにメチルセロソルブ400mlとともに加えた。次いで合成例6と同様にして目的のジアミンを得た。
【0077】
【化24】
Figure 0004134457
【0078】
合成例8 ヒドロキシル基含有ジアミン(3)の合成
2−アミノ−4−ニトロフェノール15.4g(0.1モル)をアセトン80ml、プロピレンオキシド30g(0.34モル)に溶解させ、−15℃に冷却した。ここに3−ニトロベンゾイルクロリド19.5g(0.105モル)をアセトン80mlに溶解させた溶液を徐々に滴下した。滴下終了後、−15℃で4時間反応させた。その後、室温に戻して生成している沈殿をろ過で集めた。
【0079】
乾燥させた固体25gと5%パラジウム−炭素2gを用い、合成例6と同様にして目的のジアミンを得た。
【0080】
【化25】
Figure 0004134457
【0081】
比較例1
乾燥窒素気流下、4,4’−ジアミノフェニルエーテル5.01g(0.025モル)、1,3−ビス(3−アミノプロピル)テトラメチルジシロキサン1.24g(0.005モル)をN−メチル−2−ピロリドン(NMP)50gに溶解させた。ここに合成例5で得られたヒドロキシ基含有酸無水物21.4g(0.03モル)をNMP14gとともに加えて、20℃で1時間反応させ、次いで50℃で4時間反応させた。その後、N,N−ジメチルホルムアミドジメチルアセタール7.14g(0.06モル)をNMP5gで希釈した溶液を10分かけて滴下した。滴下後、50℃で3時間攪拌した。得られた溶液40.0gにナフトキノンジアジド化合物(1)2.0gを加えて感光性ポリイミド前駆体組成物のワニスAを得た。
【0082】
6インチシリコンウエハ上に、感光性ポリイミド前駆体のワニスAをプリベ−ク後の膜厚が5μmとなるように塗布し、ついでホットプレート(大日本スクリーン社製SCW−636)を用いて、120℃で3分プリベ−クすることにより、感光性ポリイミド前駆体膜を得た。ついで、露光機(ニコン社製g線ステッパーNSR−1505−G6E)に、パターンの切られたレチクルをセットし、露光量500mJ/cm2(436nmの強度)でg線露光を行った。
【0083】
現像は、大日本スクリーン製造社製SCW−636の現像装置を用い、50回転で水酸化テトラメチルアンモニウムの2.38%水溶液を10秒間噴霧した。この後、0回転で50秒間静置し、400回転で水にてリンス処理、3000回転で10秒振り切り乾燥した。
【0084】
現像後の未露光部の膜厚は4.4μmであり、現像により膜の減少は0.6μmと少なく良好であった。現像後のパターンを観察した結果、半導体用バッファーコートとして要求される3μmのパターンが解像しており、パターン形状も問題なかった。
【0085】
比較例2
乾燥窒素気流下、ヒドロキシル基含有ジアミン(1)15.1g(0.025モル)をN−メチル−2−ピロリドン(NMP)50gに溶解させた。ここに合成例5で得られたヒドロキシ基含有酸無水物17.5g(0.025モル)をピリジン30gとともに加えて、60℃で6時間反応させた。反応終了後、溶液を水2lに投入して、ポリマー固体の沈殿をろ過で集めた。ポリマー固体を80℃の真空乾燥機で20時間乾燥した。
【0086】
このようにして得たポリマーの固体10gを計り、ナフトキノンジアジド化合物(2)2g、ビニルトリメトキシシラン1gとをGBL30gに溶解させて感光性ポリイミド前駆体組成物のワニスBを得た。
【0087】
4インチシリコンウエハ上に、ワニスBを用いて比較例1と同様に感光性ポリイミド前駆体膜を得た。ついで、露光機(キャノン社製コンタクトアライナーPLA−501F)に、パターンの切られたマスクをセットし、露光量600mJ/cm(365nmの強度)で露光を行った。
【0088】
現像は、現像液として2.38%テトラメチルアンモニウムヒドロキシド水溶液を用い、0回転で60秒静置した以外は比較例1と同様に現像した。現像後の未露光部の膜厚は4.3μmであり、現像により膜の減少は0.7μmと少なく良好であった。現像後のパタ−ンを光学顕微鏡で目視した結果、10μmのラインが解像しており、パターン形状も問題なかった。
【0089】
実施例
乾燥窒素気流下、ヒドロキシル基含有ジアミン化合物(2)17.0g(0.045モル)、1,3−ビス(3−アミノプロピル)テトラメチルジシロキサン1.24g(0.005モル)をNMP50gに溶解させた。ここに3,3’,4,4’−ジフェニルエーテルテトラカルボン酸無水物12.4g(0.04モル)をNMP21gとともに加えて、20℃で1時間反応させ、次いで50℃で2時間反応させた。ここに無水マレイン酸0.98g(0.01モル)を加え、50℃で2時間攪拌後、N,N−ジメチルホルムアミドジエチルアセタール14.7g(0.1モル)をNMP5gで希釈した溶液を10分かけて滴下した。滴下後、50℃で3時間攪拌した。得られた溶液30gにナフトキノンジアジド化合物(3)1.6gを溶解させて感光性ポリイミド前駆体組成物のワニスCを得た。
【0090】
ワニスCを用いて比較例1と同様に感光性ポリイミド前駆体膜を得た。ついで、ニコン製i線ステッパーNSR−1505−i7Aを用いて、露光量400mJ/cm(365nmの強度)でi線露光を行った以外は比較例1と同様に露光した。
【0091】
現像は、0回転で40秒間静置した以外は比較例1と同様に現像した。現像後の未露光部の膜厚は4.8μmであり、現像により膜の減少は0.2μmと少なく良好であった。現像後のパターンを観察した結果、半導体用バッファーコートとして要求される3μmのパターンが解像しており、パターン形状も問題なかった。
【0092】
比較例3
乾燥窒素気流下、ヒドロキシル基含有ジアミン化合物(3)6.08g(0.025モル)と4,4’−ジアミノジフェニルエーテル4.51g(0.0225モル)と1,3−ビス(3−アミノプロピル)テトラメチルジシロキサン0.62g(0.0025モル)をNMP70gに溶解させた。合成例5で得られたヒドロキシル基含有酸無水物24.99g(0.035モル)、3,3’,4,4’−ビフェニルテトラカルボン酸2無水物4.41g(0.015モル)を室温でNMP25gとともに加え、そのまま室温で1時間、その後50℃で2時間攪拌した。ついで、グリシジルメチルエーテル17.6g(0.2モル)をNMP10gで希釈した溶液を加え、70℃で6時間攪拌した。このポリマー溶液40gにナフトキノンジアジド化合物(4)2.5gを溶解させて感光性ポリイミド前駆体組成物のワニスDを得た。
【0093】
4インチシリコンウェハー上にワニスDを用いて比較例1と同様に感光性ポリイミド前駆体膜を得た。ついで、露光量300mJ/cm(365nmの強度)で露光を行った以外は比較例2と同様に露光した。
【0094】
現像は、0.8%テトラメチルアンモニウムヒドロキシド水溶液を用い、0回転で80秒静置した以外は比較例1と同様に行った。現像後の未露光部の膜厚は4.2μmであり、現像により膜の減少は0.8μmと少なく良好であった。現像後のパタ−ンを光学顕微鏡で目視した結果、10μmのラインが解像しており、パターン形状も問題なかった。
【0095】
比較例4
比較例1と同様に合成したポリイミド前駆体溶液40gに没食子酸メチルに5−ナフトキノンジアジドスルホン酸を平均3個導入したナフトキノンジアジド化合物(東洋合成社製MG−300)2.0gを溶解させて感光性ポリイミド前駆体組成物のワニスEを得た。
【0096】
比較例1と同様にパターン加工性の評価したところ、現像による膜の減少が1.4μmあり、かつ現像時間が100秒と比較例1に比較して2倍に長くなっている。このように膜減りが大きく、現像時間が長く問題があった。
【0097】
比較例
実施例と同様に合成したポリイミド前駆体溶液30gに2,3,4,4’−テトラヒドロキシベンゾフェノンの4−ナフトキノンジアジドスルホン酸を平均3個導入したナフトキノンジアジド化合物(東洋合成社製4NT(4)−300)1.6gを溶解させて感光性ポリイミド前駆体組成物のワニスFを得た。
【0098】
実施例と同様にパターン加工性の評価したところ、現像による膜の減少が2μmあり、かつ現像時間が120秒と実施例に較べると3倍に長くなった。このように膜減りが大きく現像時間が長く、問題があった。
【0099】
【発明の効果】
本発明によれば、特定の構造を有したポリイミド前駆体に特定のナフトキノンジアジド化合物を加えることで、現像による未露光部の膜減りが少なく、かつ短時間で現像できるポジ型の耐熱性樹脂組成物を得ることができる。[0001]
BACKGROUND OF THE INVENTION
The present invention relates to a positive type photosensitive polyimide precursor composition in which a portion exposed to ultraviolet rays suitable for a surface protective film, an interlayer insulating film and the like of a semiconductor element is dissolved in an alkaline aqueous solution.
[0002]
[Prior art]
As the positive heat-resistant resin precursor composition in which the exposed portion is dissolved by development, naphthoquinone diazide is added to polyamic acid (Japanese Patent Laid-Open No. 52-13315), naphthoquinone diazide is added to a soluble polyimide having a hydroxyl group. In which naphthoquinonediazide is added to polyamide having a hydroxyl group (Japanese Patent Laid-Open No. 56-27140) is known.
[0003]
However, in the case where naphthoquinone diazide is added to normal polyamic acid, the solubility of the carboxyl group of the polyamic acid is higher than the dissolution inhibiting effect of naphthoquinone diazide on alkali, so the desired pattern cannot be obtained in most cases. There was a point. In addition, with the addition of a soluble polyimide resin having a hydroxyl group, the problems as described above are reduced, but the structure is limited to make it soluble, and the solvent resistance of the resulting polyimide resin is poor. The point was a problem.
[0004]
In consideration of the above disadvantages, the present invention is obtained by adding a novel naphthoquinonediazide compound to the polyimide precursor, so that the resulting resin composition is hardly dissolved in an alkali developer before exposure, and easily exposed to an alkali developer. Therefore, the present inventors have found that the film can be developed in a short period of time and can be developed in a short time.
[0005]
[Problems to be solved by the invention]
The present invention provides a positive heat-resistant resin composition that can be developed in a short time with little film loss in unexposed areas due to development by adding a specific naphthoquinonediazide compound to a polyimide precursor having a specific structure. It is to provide.
[0006]
[Means for Solving the Problems]
The present invention comprises (a) a polymer having a structural unit represented by general formula (1) as a main component, and (b) at least one quinonediazide compound represented by general formula (2). It is a photosensitive resin precursor composition.
[0007]
[Chemical 7]
Figure 0004134457
[0008]
(R in general formula (1)1Represents a trivalent to octavalent organic group having at least 2 carbon atoms, R2Represents a divalent to hexavalent organic group having at least 2 carbon atoms, and RThreeRepresents hydrogen or an organic group having 1 to 10 carbon atoms. n is an integer from 10 to 100,000, m is an integer from 1 to 2, and p and q are integers from 0 to 4. p and q are not 0 at the same time. )
[0009]
[Chemical 8]
Figure 0004134457
[0010]
(In general formula (2)1In one quinonediazide compound, not all of Q are hydrogen atoms. )
[0011]
DETAILED DESCRIPTION OF THE INVENTION
The polymer having the structural unit represented by the general formula (1) in the present invention as a main component can be a polymer having an imide ring, an oxazole ring, or other cyclic structure by heating or an appropriate catalyst. With the ring structure, the heat resistance and solvent resistance are dramatically improved.
[0012]
The general formula (1) represents a polyamic acid having a hydroxyl group, and the presence of the hydroxyl group makes the solubility in an alkaline aqueous solution better than that of a polyamic acid having no hydroxyl group. In particular, among the hydroxyl groups, phenolic hydroxyl groups are more preferable than solubility in an aqueous alkali solution. In addition, when the fluorine atom is contained in the general formula (1) by 10% by weight or more, water repellency appears moderately at the interface of the film when developing with an alkaline aqueous solution, so that the penetration of the interface can be suppressed. However, if the fluorine atom content exceeds 20% by weight, the solubility in an alkaline aqueous solution is reduced, the organic solvent resistance of the polymer having a cyclic structure by heat treatment is reduced, and the solubility in fuming nitric acid is reduced. It is not preferable. Thus, the fluorine atom is preferably contained in an amount of 10 to 20% by weight.
[0013]
In the general formula (1), R1(OH) p (COORThreeM) represents a structural component of an acid, and this group is preferably a trivalent or octavalent group having 2 or more carbon atoms, which contains an aromatic ring and has 1 to 4 hydroxyl groups.
[0014]
  Specifically, a structure as shown in the general formula (3) is preferable. In this case, R4, R6Represents a trivalent to tetravalent organic group selected from 2 to 20 carbon atoms. In particular, those containing an aromatic ring are preferred from the heat resistance of the polymer obtained, and among them, particularly preferred structures include trimellitic residues, trimesic acid residues, naphthalene tricarboxylic acid residues and the like. Also R5 Is charcoalA trivalent to hexavalent organic group having a prime number of 3 to 20 is preferred. Furthermore, the hydroxyl group is preferably located adjacent to the amide bond. Examples of this include bis (3-amino-4-hydroxyphenyl) hexafluoropropane residues, bis (3-hydroxy-4-aminophenyl) hexafluoropropane residues, fluorine atoms containing fluorine atoms. Bis (3-amino-4-hydroxyphenyl) propane residue, bis (3-hydroxy-4-aminophenyl) propane residue, 3,3′-diamino-4,4′-dihydroxybiphenyl residue, 3 , 3′-diamino-4,4′-dihydroxybiphenyl residue, 2,4-diamino-phenol residue, 2,5-diaminophenol residue, 1,4-diamino-2,5-dihydroxybenzene residue The thing which the amino group couple | bonded can be mentioned.
[0015]
R7, R8Is preferably hydrogen or an organic group having 1 to 10 carbon atoms. When the number of carbon atoms is 10 or more, the solubility in an alkali developer decreases.
[0016]
  u and w are1, V represents an integer from 1 to 4. When v is 5 or more, the properties of the resulting heat-resistant resin film are degraded.
[0017]
  General formula (3)Structure represented byPreferred amongConstructionFor example, the structure shown belowMadeAlthough not mentioned, it is not limited to these.
[0018]
[Chemical 9]
Figure 0004134457
[0019]
R2(OH) When q of component q is 1 or more, a tetracarboxylic acid residue or tricarboxylic acid residue having no hydroxyl group can also be used. Examples of such residues include aromatic tetracarboxylic acid residues such as pyromellitic acid residues, benzophenone tetracarboxylic acid residues, biphenyl tetracarboxylic acid residues, diphenyl ether tetracarboxylic acid residues, and diphenyl sulfone tetracarboxylic acid residues. A diester compound in which two or two carboxyl groups are converted to a methyl or ethyl group, an aliphatic tetracarboxylic acid residue such as a butanetetracarboxylic acid residue or a cyclopentanetetracarboxylic acid residue, or two of its carboxyl groups are methylated. And aromatic dicarboxylic acid residues such as trimester acid residues and trimesic acid residues.
[0020]
Moreover, it is modified with aromatic dicarboxylic acids such as terephthalic acid, isophthalic acid, diphenyl ether dicarboxylic acid, naphthalenedicarboxylic acid, and aliphatic dicarboxylic acids such as adipic acid, as long as solubility in alkali, photosensitive performance, and heat resistance are not impaired. I can do it. These are preferably modified by 50 mol% or less of the acid component, more preferably 30 mol% or less.
[0021]
In the general formula (1), R2(OH) q represents a structural component of diamine. In this, R2Preferable examples of (OH) q are those having an aromatic and hydroxyl group from the heat resistance of the resulting polymer, and specific examples include bis (amino-hydroxy-phenyl) having a fluorine atom. ) Hexafluoropropane residues, compounds having no fluorine atom, diaminodihydroxypyrimidine residues, diaminodihydroxypyridine residues, hydroxy-diamino-pyrimidine residues, diaminophenol residues, dihydroxybenzidine residues and general formulas The thing of the structure shown to (4), (5), (6) can be mention | raise | lifted.
[0022]
  In the general formula (4), R9, R11Has 2 to 20 carbon atomsOf 3It represents a tetravalent to tetravalent organic group, and those having an aromatic ring are preferred from the heat resistance of the resulting polymer.-R 9 (OH) r-, -R 11 (OH) s-Specific examples include those shown below.
[0023]
[Chemical Formula 10]
Figure 0004134457
[0024]
(A is an integer from 1 to 4, b and c are integers from 0 to 4, and b + c is 1 or more.
[0025]
In addition, aliphatic groups such as a hydroxycyclohexyl group and a dihydroxycyclohexyl group can also be used. RTenRepresents a divalent organic group having 2 to 30 carbon atoms. A divalent group having an aromatic is better than the heat resistance of the obtained polymer, and such an example is shown below.
[0026]
Embedded image
Figure 0004134457
[0027]
  In the general formula (5), R12, R14Represents a divalent organic group having 2 to 20 carbon atoms. A divalent group having an aromatic is better than the heat resistance of the obtained polymer. Examples of such a group include R in the above general formula (4).10The thing similar to what was illustrated in the specific example can be mentioned. R13Is, CharcoalA trivalent to hexavalent organic group selected from a prime number of 3 to 20 is shown, and those having an aromatic ring are preferred from the heat resistance of the resulting polymer.-R 13 (OH) z-As in the above general formula (4)-R 9 (OH) r-, -R 11 (OH) s-The thing similar to what was illustrated in the specific example can be mentioned.
[0028]
  In the general formula (6), R15Represents a divalent organic group having 2 to 20 carbon atoms. A divalent group having an aromatic is better than the heat resistance of the obtained polymer. Examples of such a group include R in the above general formula (4).10The thing similar to what was illustrated in the specific example can be mentioned. R16 Is 3It represents a hexavalent to hexavalent organic group, and those having an aromatic ring are preferred from the heat resistance of the resulting polymer.-R 16 (OH) t-As R in the above general formula (4)9, R11The thing similar to what was illustrated in the specific example can be mentioned.
[0029]
Specific examples of what is represented by the general formula (4) are shown below.
[0030]
Embedded image
Figure 0004134457
[0031]
Specific examples of what is represented by the general formula (5) are shown below.
[0032]
Embedded image
Figure 0004134457
[0033]
Specific examples of what is represented by the general formula (6) are shown below.
[0034]
Embedded image
Figure 0004134457
[0035]
R1(OH) p (COORThree) When p of m is any one of 1 to 4, a diamine component having no hydroxyl group can be used. An example of this is shown below.
[0036]
Embedded image
Figure 0004134457
[0037]
R in the general formula (1)ThreeRepresents hydrogen or an organic group having 1 to 10 carbon atoms. From the stability of the resulting photosensitive resin precursor solution, RThreeIs preferably an organic group, but hydrogen is preferred from the viewpoint of the solubility of an alkaline aqueous solution. In the present invention, a hydrogen atom and an alkyl group can be mixed. This RThreeBy controlling the amounts of hydrogen and organic groups, the dissolution rate in the aqueous alkali solution changes, and this adjustment makes it possible to obtain a photosensitive resin precursor composition having an appropriate dissolution rate. RThreeMay be all hydrogen atoms and all organic groups, but a more preferred range is RThree10% to 90% of the hydrogen atoms are hydrogen atoms. RThreeIf the number of carbons exceeds 10, it will not dissolve in the alkaline aqueous solution.
[0038]
Furthermore, in order to improve the adhesion to the substrate, R is within the range that does not decrease the heat resistance.1(OH) p (COORThree) M, R2(OH) q may be copolymerized with an aliphatic group having a siloxane structure. Specifically, R1(OH) p (COORThree) M may be one obtained by copolymerizing 1 to 20 mol% of the compounds shown below.
[0039]
Embedded image
Figure 0004134457
[0040]
R2As the (OH) q component, bis (3-aminopropyl) tetramethyldisiloxane residue, bis (4-aminophenyl) octamethylpentasiloxane residue, α, ω-bis (3-aminopropyl) permethylpolysiloxane Examples thereof include those obtained by copolymerizing 1 to 20 mol% of residues and the like.
[0041]
RThreeContains at least one hydrocarbon group having 1 to 16 carbon atoms, and the others are preferably hydrogen atoms.
[0042]
The polymer of the present invention may be composed only of the structural unit represented by the general formula (1), or may be a copolymer or blend with other structural units. In that case, it is preferable to contain 90 mol% or more of the structural unit represented by General formula (1). The type and amount of structural units used for copolymerization or blending are preferably selected within a range that does not impair the heat resistance of the polyimide polymer obtained by the final heat treatment.
[0043]
As a synthesis example of the photosensitive resin precursor composition of the present invention, a method of reacting a tetracarboxylic dianhydride and a diamine compound at a low temperature (CE Sroog et al., Journal Polymer Science, Part A-3, 1373). (1965)), a method in which a diester is obtained from tetracarboxylic dianhydride and an alcohol and then reacted in the presence of an amine and a condensing agent (Japanese Patent Laid-Open No. 61-72022), tetracarboxylic dianhydride and alcohol To obtain a diester, and then the remaining dicarboxylic acid is acid chlorided and reacted with an amine (Japanese Patent Laid-Open No. 55-30207).
[0044]
In the present invention, the naphthoquinonediazide compound to be added is represented by the general formula (2). By adding a compound having such a structure, the film loss in the unexposed area after development is greatly reduced, and a good pattern can be obtained in a short development time. In one quinonediazide compound represented by the general formula (2), when the hydrogen atom of Q increases, the solubility of the photosensitizer represented by the general formula (2) in an alkaline developer increases. The effect which protects the polymer represented by this falls. From this point of view, the ratio of hydrogen atoms is preferably 1/3 or less, and more preferably 1/5 or less. Moreover, as a thing other than a hydrogen atom, 4-naphthoquinone diazide sulfonyl group and 5-naphthoquinone diazide sulfonyl group can be mentioned. The 4-naphthoquinone diazide sulfonyl group has absorption in the i-line region of the mercury lamp and is suitable for i-line exposure, and the 5-naphthoquinone diazide sulfonyl group has absorption extended to the g-line region of the mercury lamp. Is suitable. In the present invention, both 4-naphthoquinone diazide sulfonyl group and 5-naphthoquinone diazide sulfonyl group can be preferably used, but 4-naphthoquinone diazide sulfonyl group and 5-naphthoquinone diazide sulfonyl group should be selected according to the wavelength to be exposed. Is preferred. In addition, a 4-naphthoquinone diazide sulfonyl group and a 5-naphthoquinone diazide sulfonyl group can be introduced in the same molecule together, or a photosensitizer in which a 4-naphthoquinone diazide sulfonyl group is introduced as a photosensitive group and a 5-naphthoquinone diazide sulfonyl group. It is also possible to use a mixture of a photosensitive agent introduced with a group as a photosensitive group.
[0045]
As the photosensitizer represented by the general formula (2) in the present invention, one having one type of structure may be used, or one having a plurality of structures may be mixed and used.
[0049]
If necessary, for the purpose of improving the coating properties between the photosensitive resin precursor composition and the substrate, surfactants, esters such as ethyl lactate and propylene glycol monomethyl ether acetate, alcohols such as ethanol, cyclohexanone , Ketones such as methyl isobutyl ketone, and ethers such as tetrahydrofuran and dioxane may be mixed. In addition, inorganic particles such as silicon dioxide and titanium dioxide, or polyimide powder can be added.
[0050]
Further, in order to improve the adhesion to the base substrate such as a silicon wafer, 0.5 to 10% by weight of a silane coupling agent, a titanium chelating agent, etc. is added to the varnish of the photosensitive resin precursor composition. It can also be pretreated with such a chemical.
[0051]
When added to the varnish, 0.5 to 10% by weight of a silane coupling agent such as methylmethacryloxydimethoxysilane or 3-aminopropyltrimethoxysilane, titanium chelating agent, or aluminum chelating agent is added to the polymer in the varnish. To do.
[0052]
When processing a substrate, the coupling agent described above is added to a solvent such as isopropanol, ethanol, methanol, water, tetrahydrofuran, propylene glycol monomethyl ether acetate, propylene glycol monomethyl ether, ethyl lactate, diethyl adipate, and the like in an amount of 0.5 to 20. Surface treatment is performed by spin coating, dipping, spray coating, steam treatment, etc. on the solution in which the weight% is dissolved. In some cases, the reaction between the substrate and the coupling agent is allowed to proceed by applying a temperature from 50 ° C. to 300 ° C.
[0053]
Next, a method for forming a heat resistant resin pattern using the photosensitive resin precursor composition of the present invention will be described.
[0054]
The photosensitive resin precursor composition is applied onto the substrate. A silicon wafer, ceramics, gallium arsenide, or the like is used as the substrate, but is not limited thereto. Examples of the application method include spin coating using a spinner, spray coating, and roll coating. The coating film thickness varies depending on the coating method, the solid content concentration of the composition, the viscosity, and the like, but is usually applied so that the film thickness after drying is 0.1 to 150 μm.
[0055]
Next, the substrate coated with the photosensitive resin precursor composition is dried to obtain a photosensitive resin precursor composition film. Drying is preferably performed using an oven, a hot plate, infrared rays, or the like at a range of 50 to 150 degrees for 1 minute to several hours.
[0056]
Next, the photosensitive resin precursor composition film is exposed to actinic radiation through a mask having a desired pattern. Actinic rays used for exposure include ultraviolet rays, visible rays, electron beams, and X-rays. In the present invention, it is preferable to use i-rays (365 nm), h-rays (405 nm), and g-rays (436 nm) of mercury lamps. .
[0057]
Formation of the heat-resistant resin pattern is achieved by removing the exposed portion using a developer after exposure. Developers include tetramethylammonium aqueous solution, diethanolamine, diethylaminoethanol, sodium hydroxide, potassium hydroxide, sodium carbonate, potassium carbonate, triethylamine, diethylamine, methylamine, dimethylamine, dimethylaminoethyl acetate, dimethylaminoethanol, dimethyl An aqueous solution of a compound showing alkalinity such as aminoethyl methacrylate, cyclohexylamine, ethylenediamine, hexamethylenediamine and the like is preferable. In some cases, these alkaline aqueous solutions may contain polar solvents such as N-methyl-2-pyrrolidone, N, N-dimethylformamide, N, N-dimethylacetamide, dimethylsulfoxide, γ-butyrolaclone, dimethylacrylamide, methanol, ethanol, Alcohols such as isopropanol, esters such as ethyl lactate and propylene glycol monomethyl ether acetate, ketones such as cyclopentanone, cyclohexanone, isobutyl ketone, and methyl isobutyl ketone may be added singly or in combination. Good. After development, rinse with water. Here, alcohols such as ethanol and isopropyl alcohol, and esters such as ethyl lactate and propylene glycol monomethyl ether acetate may be added to water for rinsing treatment.
[0058]
After development, a temperature of 200 ° C. to 500 ° C. is applied to convert to a heat resistant resin film. This heat treatment is carried out for 5 minutes to 5 hours by selecting the temperature and raising the temperature stepwise, or selecting a certain temperature range and continuously raising the temperature. As an example, heat treatment is performed for 30 minutes at 130 degrees, 200 degrees, and 350 degrees. Alternatively, a method such as linearly raising the temperature from room temperature to 400 degrees over 2 hours can be mentioned.
[0059]
The heat-resistant resin film formed from the photosensitive resin precursor composition according to the present invention is used for applications such as a semiconductor passivation film, a protective film for semiconductor elements, and an interlayer insulating film for multilayer wiring for high-density mounting.
[0060]
【Example】
In order to describe the present invention in more detail below, examples will be described, but the present invention is not limited thereto.
Measuring method of characteristics
Measurement of film thickness
Measurement was performed at a refractive index of 1.64 using Lambda Ace STM-602 manufactured by Dainippon Screen Mfg.
[0061]
Synthesis Example 1 Synthesis of naphthoquinonediazide compound (1)
In a dry nitrogen stream, 19.9 g (0.05 mol) of 1,1,2,2-tetra (4-hydroxyphenyl) ethane and 47.0 g (0.175 mol) of 4-naphthoquinone diazide sulfonyl chloride were added to 1, It was dissolved in 500 g of 4-dioxane and heated to 40 ° C. Here, 17.7 g (0.175 mol) of triethylamine mixed with 50 g of 1,4-dioxane was added dropwise so that the temperature in the system would not be 45 degrees or more. It stirred at 40 degree | times after dripping for 2 hours. The triethylamine hydrochloride formed as a by-product was filtered, and the filtrate was poured into 3 l of 1% hydrochloric acid. Thereafter, the deposited precipitate was collected by filtration. Further, washing with 10 l of water was repeated twice, followed by drying with a vacuum dryer at 50 ° C. for 20 hours to obtain a naphthoquinonediazide compound (1).
[0062]
Embedded image
Figure 0004134457
[0063]
Synthesis Example 2 Synthesis of naphthoquinonediazide compound (2)
Under a dry nitrogen stream, 17.4 g (0.05 mol) of 1,1,2-tri (3-methyl-4-hydroxyphenyl) ethane and 34.9 g (0.13 mol) of 5-naphthoquinone diazide sulfonyl chloride were added. It was dissolved in 400 g of 1,4-dioxane and heated to 40 ° C. Here, 13.1 g (0.13 mol) of triethylamine mixed with 40 g of 1,4-dioxane was added dropwise so that the temperature in the system would not be 45 ° C. or higher. It stirred at 40 degreeC after dripping for 2 hours. The triethylamine hydrochloride formed as a by-product was filtered, and the filtrate was poured into 3 l of 1% hydrochloric acid. Thereafter, the deposited precipitate was collected by filtration. This precipitate was washed twice with 10 l of water and dried with a vacuum dryer at 50 ° C. for 20 hours to obtain a naphthoquinonediazide compound (2).
[0064]
Embedded image
Figure 0004134457
[0065]
Synthesis Example 3 Synthesis of naphthoquinonediazide compound (3)
Under a dry nitrogen stream, 20.2 g (0.05 mol) of 1,1,2-tri (3,5-dimethyl-4-hydroxyphenyl) propane and 37.6 g (0.14 mol) of 5-naphthoquinonediazide sulfonyl chloride ) Was dissolved in 400 g of 1,4-dioxane and heated to 40 ° C. Here, 14.2 g (0.14 mol) of triethylamine mixed with 40 g of 1,4-dioxane was added dropwise so that the temperature in the system would not be 45 ° C. or higher. It stirred at 40 degreeC after dripping for 2 hours. The triethylamine hydrochloride formed as a by-product was filtered, and the filtrate was poured into 3 l of 1% hydrochloric acid. Thereafter, the deposited precipitate was collected by filtration. This precipitate was washed twice with 10 l of water and dried in a vacuum dryer at 50 ° C. for 20 hours to obtain a naphthoquinonediazide compound (3).
[0066]
Embedded image
Figure 0004134457
[0067]
Synthesis Example 4 Synthesis of naphthoquinonediazide compound (4)
Under a dry nitrogen stream, 29.3 g (0.05 mol) of 4,4 ′, 4 ″, 4 ′ ″-(1,4-phenylenedimethylidene) tetrakis (2,6-dimethylphenol) and 4-naphtho 43.0 g (0.16 mol) of quinonediazide sulfonyl chloride was dissolved in 700 g of 1,4-dioxane and heated to 40 ° C. Here, 16.2 g (0.16 mol) of triethylamine mixed with 60 g of 1,4-dioxane was added dropwise so that the temperature inside the system would not be 45 ° C. or higher. It stirred at 40 degreeC after dripping for 2 hours. The triethylamine hydrochloride formed as a by-product was filtered, and the filtrate was put into 3 l of 1% hydrochloric acid. Thereafter, the deposited precipitate was collected by filtration. This precipitate was washed twice with 10 l of water and dried with a vacuum dryer at 50 ° C. for 20 hours to obtain a naphthoquinonediazide compound (4).
[0068]
Embedded image
Figure 0004134457
[0069]
Synthesis Example 5 Synthesis of hydroxyl group-containing acid anhydride
In a dry nitrogen stream, 18.3 g (0.05 mol) of 2,2-bis (3-amino-4-hydroxyphenyl) hexafluoropropane (BAHF) and 34.2 g (0.3 mol) of allyl glycidyl ether were gamma-treated. It was dissolved in 100 g of butyrolactone (GBL) and cooled to -15 ° C. To this, 22.1 g (0.11 mol) of trimellitic anhydride chloride dissolved in 50 g of GBL was added dropwise so that the temperature of the reaction solution did not exceed 0 ° C. After completion of dropping, the reaction was carried out at 0 ° C. for 4 hours.
[0070]
This solution was concentrated by a rotary evaporator and charged into 1 l of toluene to obtain an acid anhydride (1). The material obtained did not have a clear melting point up to 350 ° C.
[0071]
Embedded image
Figure 0004134457
[0072]
Synthesis Example 6 Synthesis of hydroxyl group-containing diamine compound (1)
18.3 g (0.05 mol) of BAHF was dissolved in 100 ml of acetone and 17.4 g (0.3 mol) of propylene oxide, and cooled to -15 ° C. A solution prepared by dissolving 20.4 g (0.11 mol) of 4-nitrobenzoyl chloride in 100 ml of acetone was added dropwise thereto. After completion of dropping, the mixture was reacted at −15 ° C. for 4 hours and then returned to room temperature. The solution was concentrated with a rotary evaporator, and the obtained solid was washed with water and acetone and dried with a vacuum dryer at 80 ° C.
[0073]
25 g of the dried solid and 2 g of 5% palladium-carbon were added to a 500 ml autoclave along with 300 ml of methyl cellosolve. Here, hydrogen was pressurized at a pressure of 8 kgf / cm 2, the temperature was raised to 60 ° C., and stirring was continued until no more hydrogen was absorbed. After absorbing hydrogen, the mixture was stirred for 10 minutes, and then the heating was stopped. When the temperature became 30 ° C. or lower, the pressure in the container was released to stop the reaction. After completion of the reaction, the solution was filtered, and the filtrate was poured into 1 liter of water to obtain a target precipitate. This was dried with a vacuum dryer at 50 ° C. for 20 hours.
[0074]
Embedded image
Figure 0004134457
[0075]
Synthesis Example 7 Synthesis of hydroxyl group-containing diamine (2)
2-Amino-4-nitrophenol (30.8 g, 0.2 mol) was dissolved in acetone (200 ml) and propylene oxide (60 g, 0.68 mol), and cooled to -15 ° C. A solution prepared by dissolving 22.4 g (0.11 mol) of isophthalic acid chloride in 200 ml of acetone was gradually added dropwise thereto. After completion of dropping, the reaction was carried out at −15 ° C. for 4 hours. Thereafter, the precipitate formed by returning to room temperature was collected by filtration.
[0076]
30 g of the dried precipitate and 3 g of 5% palladium-carbon were added to a 500 ml autoclave along with 400 ml of methyl cellosolve. Subsequently, the target diamine was obtained in the same manner as in Synthesis Example 6.
[0077]
Embedded image
Figure 0004134457
[0078]
Synthesis Example 8 Synthesis of hydroxyl group-containing diamine (3)
15.4 g (0.1 mol) of 2-amino-4-nitrophenol was dissolved in 80 ml of acetone and 30 g (0.34 mol) of propylene oxide, and cooled to -15 ° C. A solution prepared by dissolving 19.5 g (0.105 mol) of 3-nitrobenzoyl chloride in 80 ml of acetone was gradually added dropwise thereto. After completion of dropping, the reaction was carried out at −15 ° C. for 4 hours. Thereafter, the precipitate formed by returning to room temperature was collected by filtration.
[0079]
Using 25 g of the dried solid and 2 g of 5% palladium-carbon, the target diamine was obtained in the same manner as in Synthesis Example 6.
[0080]
Embedded image
Figure 0004134457
[0081]
  ComparisonExample 1
  Under a dry nitrogen stream, 5.01 g (0.025 mol) of 4,4′-diaminophenyl ether and 1.24 g (0.005 mol) of 1,3-bis (3-aminopropyl) tetramethyldisiloxane were added to N—. It was dissolved in 50 g of methyl-2-pyrrolidone (NMP). To this, 21.4 g (0.03 mol) of the hydroxy group-containing acid anhydride obtained in Synthesis Example 5 was added together with 14 g of NMP, and reacted at 20 ° C. for 1 hour, and then reacted at 50 ° C. for 4 hours. Thereafter, a solution prepared by diluting 7.14 g (0.06 mol) of N, N-dimethylformamide dimethylacetal with 5 g of NMP was added dropwise over 10 minutes. After dropping, the mixture was stirred at 50 ° C. for 3 hours. The naphthoquinone diazide compound (1) 2.0g was added to 40.0g of obtained solutions, and the varnish A of the photosensitive polyimide precursor composition was obtained.
[0082]
On a 6-inch silicon wafer, a photosensitive polyimide precursor varnish A was applied so that the film thickness after pre-baking was 5 μm, and then a hot plate (SCW-636 manufactured by Dainippon Screen Co., Ltd.) was used. A photosensitive polyimide precursor film was obtained by pre-baking at 3 ° C. for 3 minutes. Next, a reticle with a cut pattern was set in the exposure machine (g-line stepper NSR-1505-G6E manufactured by Nikon Corporation), and the exposure amount was 500 mJ / cm.2The g-line exposure was performed at (intensity of 436 nm).
[0083]
Development was performed using a SCW-636 developing device manufactured by Dainippon Screen Mfg. Co., Ltd., and sprayed with a 2.38% aqueous solution of tetramethylammonium hydroxide for 10 seconds at 50 revolutions. Thereafter, the plate was allowed to stand for 50 seconds at 0 rotation, rinsed with water at 400 rotation, and shaken and dried for 10 seconds at 3000 rotation.
[0084]
The film thickness of the unexposed part after development was 4.4 μm, and the film reduction due to development was as small as 0.6 μm, which was good. As a result of observing the developed pattern, the 3 μm pattern required as a semiconductor buffer coat was resolved, and the pattern shape was satisfactory.
[0085]
  ComparisonExample 2
  Under a dry nitrogen stream, 15.1 g (0.025 mol) of hydroxyl group-containing diamine (1) was dissolved in 50 g of N-methyl-2-pyrrolidone (NMP). 17.5 g (0.025 mol) of the hydroxy group-containing acid anhydride obtained in Synthesis Example 5 was added thereto together with 30 g of pyridine, and the mixture was reacted at 60 ° C. for 6 hours. After completion of the reaction, the solution was poured into 2 liters of water, and the polymer solid precipitate was collected by filtration. The polymer solid was dried in a vacuum dryer at 80 ° C. for 20 hours.
[0086]
10 g of the polymer solid thus obtained was weighed, and 2 g of naphthoquinonediazide compound (2) and 1 g of vinyltrimethoxysilane were dissolved in 30 g of GBL to obtain varnish B of a photosensitive polyimide precursor composition.
[0087]
  Using varnish B on a 4-inch silicon waferComparisonA photosensitive polyimide precursor film was obtained in the same manner as in Example 1. Next, a mask with a pattern cut was set in an exposure machine (Canon contact aligner PLA-501F), and the exposure amount was 600 mJ / cm.2The exposure was performed at an intensity of 365 nm.
[0088]
  The development was performed except that a 2.38% tetramethylammonium hydroxide aqueous solution was used as a developing solution and the solution was allowed to stand for 60 seconds at 0 rotationComparisonDeveloped as in Example 1. The film thickness of the unexposed part after development was 4.3 μm, and the reduction in film due to development was as small as 0.7 μm, which was good. As a result of visually observing the developed pattern with an optical microscope, the 10 μm line was resolved and the pattern shape was satisfactory.
[0089]
  Example1
  Under a dry nitrogen stream, 17.0 g (0.045 mol) of hydroxyl group-containing diamine compound (2) and 1.24 g (0.005 mol) of 1,3-bis (3-aminopropyl) tetramethyldisiloxane were added to 50 g of NMP. Dissolved. To this, 12.4 g (0.04 mol) of 3,3 ′, 4,4′-diphenyl ether tetracarboxylic anhydride was added together with 21 g of NMP, and reacted at 20 ° C. for 1 hour, and then reacted at 50 ° C. for 2 hours. . To this, 0.98 g (0.01 mol) of maleic anhydride was added, stirred for 2 hours at 50 ° C., and then a solution obtained by diluting 14.7 g (0.1 mol) of N, N-dimethylformamide diethyl acetal with 5 g of NMP was added. It was added dropwise over a period of minutes. After dropping, the mixture was stirred at 50 ° C. for 3 hours. 1.6 g of naphthoquinone diazide compound (3) was dissolved in 30 g of the resulting solution to obtain a varnish C of a photosensitive polyimide precursor composition.
[0090]
  With varnish CComparisonA photosensitive polyimide precursor film was obtained in the same manner as in Example 1. Next, using a Nikon i-line stepper NSR-1505-i7A, the exposure amount was 400 mJ / cm.2Except i-line exposure at (365 nm intensity)ComparisonExposed as in Example 1.
[0091]
  The development was performed except for 40 seconds at 0 rotation.ComparisonDeveloped as in Example 1. The film thickness of the unexposed part after development was 4.8 μm, and the reduction in film due to development was as small as 0.2 μm, which was good. As a result of observing the developed pattern, the 3 μm pattern required as a semiconductor buffer coat was resolved, and the pattern shape was satisfactory.
[0092]
  Comparative Example 3
  Under a dry nitrogen stream, 6.08 g (0.025 mol) of hydroxyl group-containing diamine compound (3), 4.51 g (0.0225 mol) of 4,4′-diaminodiphenyl ether and 1,3-bis (3-aminopropyl) ) 0.62 g (0.0025 mol) of tetramethyldisiloxane was dissolved in 70 g of NMP. 24.99 g (0.035 mol) of the hydroxyl group-containing acid anhydride obtained in Synthesis Example 5 and 4.41 g (0.015 mol) of 3,3 ′, 4,4′-biphenyltetracarboxylic dianhydride were obtained. The mixture was added together with 25 g of NMP at room temperature, and stirred as it was at room temperature for 1 hour and then at 50 ° C. for 2 hours. Then, a solution obtained by diluting 17.6 g (0.2 mol) of glycidyl methyl ether with 10 g of NMP was added and stirred at 70 ° C. for 6 hours. The naphthoquinone diazide compound (4) 2.5g was dissolved in 40g of this polymer solution, and the varnish D of the photosensitive polyimide precursor composition was obtained.
[0093]
  Using varnish D on a 4 inch silicon waferComparisonA photosensitive polyimide precursor film was obtained in the same manner as in Example 1. Next, exposure 300mJ / cm2Except for exposure at (intensity of 365 nm)ComparisonExposed as in Example 2.
[0094]
  Development was performed except that 0.8% tetramethylammonium hydroxide aqueous solution was used and allowed to stand for 80 seconds at 0 rotation.ComparisonPerformed as in Example 1. The film thickness of the unexposed area after development was 4.2 μm, and the film reduction due to development was as small as 0.8 μm, which was good. As a result of visually observing the developed pattern with an optical microscope, the 10 μm line was resolved and the pattern shape was satisfactory.
[0095]
  Comparative Example 4
  ComparisonPhotosensitivity was obtained by dissolving 2.0 g of a naphthoquinone diazide compound (MG-300, manufactured by Toyo Gosei Co., Ltd.) obtained by introducing an average of three 5-naphthoquinone diazide sulfonic acids into methyl gallate into 40 g of the polyimide precursor solution synthesized in the same manner as in Example 1. The varnish E of the polyimide precursor composition was obtained.
[0096]
  ComparisonThe pattern processability was evaluated in the same manner as in Example 1. As a result, the reduction in film due to development was 1.4 μm, and the development time was 100 seconds.ComparisonCompared to Example 1, it is twice as long. Thus, there was a problem that the film thickness was large and the development time was long.
[0097]
  Comparative example5
  Example1A naphthoquinone diazide compound (4NT (4) -300 manufactured by Toyo Gosei Co., Ltd.) in which an average of three 3,4,4'-tetrahydroxybenzophenone 4-naphthoquinone diazide sulfonic acids were introduced into 30 g of the polyimide precursor solution synthesized in the same manner as above. 1.6g was dissolved and the varnish F of the photosensitive polyimide precursor composition was obtained.
[0098]
  Example1In the same manner as in Example 1, the pattern processability was evaluated. As a result, the film was reduced by 2 μm and the development time was 120 seconds.1Compared to, it is three times longer. Thus, there was a problem that the film thickness was greatly reduced and the development time was long.
[0099]
【The invention's effect】
According to the present invention, by adding a specific naphthoquinonediazide compound to a polyimide precursor having a specific structure, a positive heat-resistant resin composition that can be developed in a short time with less film loss at unexposed areas due to development. You can get things.

Claims (5)

(a)下記一般式(1)で表される構造単位を主成分とするポリマーと、(b)下記一般式(2)で表される少なくとも1つのキノンジアジド化合物を含有することを特徴とする感光性樹脂前駆体組成物。
Figure 0004134457
(一般式(1)のRは少なくとも2個以上の炭素原子を有する3価から8価の有機基を示し、Rは、少なくとも2個以上の炭素原子を有する2価から6価の有機基を示し、Rは水素、または炭素数1から10までの有機基を示す。nは10から100000までの整数、mは1から2までの整数、p、qは0から4までの整数である。pとqは同時に0になることはない。)
Figure 0004134457
(一般式(2)中、1つのキノンジアジド化合物においてQの全てが水素原子になることはない。)
A photosensitivity comprising (a) a polymer having a structural unit represented by the following general formula (1) as a main component and (b) at least one quinonediazide compound represented by the following general formula (2). Resin precursor composition.
Figure 0004134457
(R 1 in the general formula (1) represents a trivalent to octavalent organic group having at least 2 carbon atoms, and R 2 represents a divalent to hexavalent organic group having at least 2 carbon atoms. R 3 represents hydrogen or an organic group having 1 to 10 carbon atoms, n is an integer from 10 to 100,000, m is an integer from 1 to 2, p, q is an integer from 0 to 4 (P and q cannot be 0 at the same time.)
Figure 0004134457
(In general formula (2) , not all of Q's in one quinonediazide compound are hydrogen atoms.)
一般式(1)のR(COOR)m(OH)pが、下記一般式(3)で表されることを特徴とする請求項1記載の感光性樹脂前駆体組成物。
Figure 0004134457
(一般式(3)のR、Rは炭素数2から20より選ばれる3価から4価の有機基を示し、Rは炭素数3から20より選ばれる3価から6価の有機基を示し、R、Rは水素および/または炭素数1から10までの有機基を示す。u、wは1であり、vは1から4までの整数である。)
The photosensitive resin precursor composition according to claim 1, wherein R 1 (COOR 3 ) m (OH) p in the general formula (1) is represented by the following general formula (3).
Figure 0004134457
(R 4 and R 6 in the general formula (3) represent a trivalent to tetravalent organic group selected from 2 to 20 carbon atoms, and R 5 represents a trivalent to hexavalent organic group selected from 3 to 20 carbon atoms. And R 7 and R 8 represent hydrogen and / or an organic group having 1 to 10 carbon atoms, u and w are 1 and v is an integer from 1 to 4.
一般式(1)のR(OH)qが、下記一般式(4)で表されることを特徴とする請求項1記載の感光性樹脂前駆体組成物。
Figure 0004134457
(一般式(4)のR、R11は炭素数2から20より選ばれる3価から4価の有機基を示し、R10は炭素数2から30よりなる2価の有機基を示す。r、sは1あるいは2の整数である。)
The photosensitive resin precursor composition according to claim 1, wherein R 2 (OH) q in the general formula (1) is represented by the following general formula (4).
Figure 0004134457
(R 9, R 11 in the general formula (4) represents a tetravalent organic group trivalent that Ru is selected from 2 to 20 carbon atoms, R 10 represents a divalent organic group composed of 2 to 30 carbon atoms R and s are integers of 1 or 2.)
一般式(1)のR(OH)qが、下記一般式(5)で表されることを特徴とする請求項1記載の感光性樹脂前駆体組成物。
Figure 0004134457
(一般式(5)のR12、R14は炭素数2から20より選ばれる2価の有機基を示し、R13は、炭素数3から20より選ばれる3価から6価の有機基を示す。zは1から4までの整数である。)
The photosensitive resin precursor composition according to claim 1, wherein R 2 (OH) q in the general formula (1) is represented by the following general formula (5).
Figure 0004134457
(R 12, R 14 in the general formula (5) represents a divalent organic group selected from 2 to 20 carbon atoms, R 13 is a hexavalent organic group trivalent from 3 carbon atoms Ru selected from 20 Z is an integer from 1 to 4.)
一般式(1)のR(OH)qが、一般式(6)で表されることを特徴とする請求項1記載の感光性樹脂前駆体組成物。
Figure 0004134457
(一般式(6)のR15は炭素数2から20より選ばれる2価の有機基を示し、R16は、炭素数3から20より選ばれる3価から6価の有機基を示す。tは1から4までの整数である。)
The photosensitive resin precursor composition according to claim 1, wherein R 2 (OH) q in the general formula (1) is represented by the general formula (6).
Figure 0004134457
(R 15 in the general formula (6) represents a divalent organic group selected from 2 to 20 carbon atoms, R 16 represents a hexavalent organic group trivalent from 3 carbon atoms Ru selected from 20. t is an integer from 1 to 4.)
JP28548299A 1998-10-13 1999-10-06 Photosensitive resin precursor composition Expired - Fee Related JP4134457B2 (en)