JP2020139150A - プライマー塗膜用組成物、プライマー塗膜用組成物セット及びプライマー塗膜 - Google Patents
プライマー塗膜用組成物、プライマー塗膜用組成物セット及びプライマー塗膜 Download PDFInfo
- Publication number
- JP2020139150A JP2020139150A JP2020027367A JP2020027367A JP2020139150A JP 2020139150 A JP2020139150 A JP 2020139150A JP 2020027367 A JP2020027367 A JP 2020027367A JP 2020027367 A JP2020027367 A JP 2020027367A JP 2020139150 A JP2020139150 A JP 2020139150A
- Authority
- JP
- Japan
- Prior art keywords
- coating film
- primer coating
- composition
- modified product
- diisocyanate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
(式中、nは正の整数を表す。)
装置:TOSOH HCL−8320(東ソー(株)製)
カラム:TSKgel G4000H+G2500H(7.5mmI.D×30cm)(東ソー(株)製)
検出器:RI
溶離液:THF
注入量:100μL
流速:1.0mL/分
測定温度:40℃
サンプル濃度:0.3wt/vol%
(芳香族ポリイソシアネート又はその変性物)
A−1:4,4’−ジフェニルメタンジイソシアネート(製品名:ミリオネートMT、東ソー(株)製(以下同様))
A−2:4,4−ジフェニルメタンジイソシアネート(45質量%)及び2,4’−ジフェニルメタンジイソシアネート(55質量%)の混合物(製品名:ミリオネートNM)
A−3:ジフェニルメタンジイソシアネートのカルボジイミド変性物を含む組成物(製品名:ミリオネートMTL)
A−4:ジフェニルメタンジイソシアネートをポリオールにより一部反応させ得られた変性物(製品名:コロネート1050)
A−5:ジフェニルメタンジイソシアネートをポリオールにより一部反応させ得られた変性物(製品名:コロネート1057)
B−1、B−2、B−3、B−4:ヘキサメチレンジイソシアネートのイソシアヌレート体(それぞれ、製品名:コロネートHX、コロネートHXR、コロネートHXLV、コロネートHK)
B−5:ヘキサメチレンジイソシアネートのアロファネート体及びヘキサメチレンジイソシアネートのイソシアヌレート体(HDIトリマー)の混合物(製品名:コロネート2760)
B−6:ヘキサメチレンジイソシアネートのアロファネート体(製品名:コロネート2770)
(可塑剤)
C−1:アジピン酸イソノニル(製品名:DINA、田岡化学工業(株)製)
D−1:ジオール型ポリプロピレングリコール(Mn=400、製品名:アクトコールD−400、三井化学SKCポリウレタン(株)製)
D−2:トリオール型ポリプロピレングリコール(Mn=400、製品名:アクトコールT−400、三井化学SKCポリウレタン(株)製)
D−3:ジオール型ポリプロピレングリコール(Mn=1500、製品名:アクトコールD−1500、三井化学SKCポリウレタン(株)製)
D−4:トリオール型ポリプロピレングリコール(Mn=1500、製品名:アクトコールT−1500、三井化学SKCポリウレタン(株)製)
D−5:ヒマシ油(製品名:マルトクA、伊藤製油(株)製)
実施例及び比較例においては、表1〜3に示す組成に基づき原料を混合して、下記に示す方法により、プライマー塗膜用組成物を得た。
まず、四つ口フラスコに所定の芳香族ポリイソシアネート又はその変性物と、脂肪族ジイソシアネートの変性物、及び可塑剤を仕込み、窒素ガス雰囲気下で、撹拌しながら10〜30℃で30分間混合させて各主剤を得た。
調製したプライマー塗膜用組成物について、下記の方法により−10℃における低温貯蔵性を評価した。容量30mLのサンプル瓶へ主剤を20g封入し、温湿度試験槽(商品名「HIFLEX NEO FX―411N」、楠本化成(株))を用いて、−10℃とした環境下で貯蔵し、目視にて結晶が観察されるまでの日数を評価した。結果を表1〜3に示す。観察期間は最大で90日とし、90日間結晶化しなかった(液状を保った)場合は、表において「90日」と示す。30日以上結晶化しない場合に、低温貯蔵安定性に優れているといえる。
上述した実施例に係るプライマー塗膜用組成物を主剤として、この主剤と、表4〜6に示す硬化剤とを混合して、混合物を得た。混合物の組成を表4〜6に示す。
主剤と硬化剤とを混合した後、混合物の23℃での粘度が4000mPa・sに達するまでの時間(分)をそれぞれ測定した。表4〜6において、主剤の種類として「1−1」と記載しているものは、上述した実施例1−1の主剤を用いたことを意味し、他の実施例においても同様である。また、「比1−3」は、「比較例1−3」の主剤を用いたことを意味する。
23℃、湿度50%の空気循環型環境試験室内において、上述した主剤と硬化剤と、ポルトランドセメント粉(商品名「ポルトランドセメント」、太平洋セメント(株))とを、表7〜10に記載の混合比(質量比)で混合して、混合物を下地(コンクリート板)に0.2kg/m2塗布し、1日後の状態により発泡の有無を評価した。評価基準としては、目視観察により、発泡がなかったものをA、泡が発生したものをBとした。表7〜10において、主剤及び硬化剤の種類として「2−1」と記載しているものは、上述した実施例2−1の主剤及び硬化剤の組み合わせであることを意味し、他の実施例においても同様である。また、「比2−1」又は「比2−2」は、「比較例2−1」又は「比較例2−2」の主剤及び硬化剤の組み合わせであることを意味する。
23℃、湿度50%の空気循環型環境試験室内において、上述した主剤と、硬化剤と、ポルトランドセメント粉(商品名「ポルトランドセメント」、太平洋セメント(株))とを、表7〜10に記載の混合比(質量比)で混合して、混合物を下地(コンクリート板)に塗布した試験片を作製した。上塗り材(商品名「HCエコプルーフET」、保土谷建材(株))を幅3cmの帯状とした不織布に含浸させて、これを混合物の塗布の翌日に試験片に重ねた。同様の方法にて、混合物の塗布から2日後に上塗り材を含浸させた不織布を重ねたもの、及び3日後に上塗り材を含浸させた不織布を重ねたもののそれぞれについて、1週間養生した。養生後、万能材料試験機(商品名「オートグラフAGS−X 10N−10KN」、島津製作所(株))を用いて、JIS K6854−2を参考に、帯状の不織布を180°方向へ引張り、試験片の剥離状態から接着性を評価した。評価基準としては、材料破壊が生じたものをA、材料破壊と界面剥離が混在したものをB、界面剥離が生じたものをCとした。表中、実施例3−19〜3−24については、混合物塗布の翌日に混合物が硬化しなかったため、混合物塗布の2日後より評価した。
23℃、湿度50%の空気循環型環境試験室内において、上述した主剤と硬化剤と、ポルトランドセメント粉(商品名「ポルトランドセメント」、太平洋セメント(株))とを、表7〜10に記載の混合比(質量比)で混合して、混合物を下地(コンクリート板)に0.2kg/m2塗布した。混合物の塗布から16時間後に、塗布後の混合物を指で触れることにより乾燥の程度を評価した。評価基準としては、タックが全くないもの(上塗り材の施工が可能)をA、若干のタックがあるもの(上塗り材の施工は可能)をB、タックがあるもの(上塗り材の施工が困難)をCとした。
Claims (8)
- 芳香族ポリイソシアネート又はその変性物と、脂肪族ジイソシアネートの変性物と、を含有する、プライマー塗膜用組成物。
- 前記芳香族ポリイソシアネート又はその変性物は、4,4’−ジフェニルメタンジイソシアネート、2,4’−ジフェニルメタンジイソシアネート、ジフェニルメタンジイソシアネートのカルボジイミド変性物、ジフェニルメタンジイソシアネートのポリオール変性物、及びポリメチレンポリフェニルポリイソシアネートからなる群より選ばれる少なくとも1種である、請求項1に記載のプライマー塗膜用組成物。
- 前記脂肪族ジイソシアネートの変性物は、ヘキサメチレンジイソシアネートの変性物である、請求項1又は2に記載のプライマー塗膜用組成物。
- 前記脂肪族ジイソシアネートの変性物の含有量が、前記プライマー塗膜用組成物全量基準で、80質量%未満である、請求項1〜3のいずれか一項に記載のプライマー塗膜用組成物。
- 前記芳香族ポリイソシアネート又はその変性物の含有量が、前記芳香族ポリイソシアネート又はその変性物、及び前記脂肪族ジイソシアネートの変性物の含有量の合計を基準として、20質量%より大きい、請求項1〜4のいずれか一項に記載のプライマー塗膜用組成物。
- 請求項1〜5のいずれか一項に記載のプライマー塗膜用組成物からなる主剤と、硬化剤と、を備える、プライマー塗膜用組成物セット。
- 前記硬化剤はヒドロキシ化合物を含有する、請求項6に記載のプライマー塗膜用組成物セット。
- 請求項6又は7に記載のプライマー塗膜用組成物セットにおける前記主剤及び前記硬化剤を含有する混合物の硬化物を含む、プライマー塗膜。