HU222256B1 - Szóda/mész/szilikát típusú üvegkompozíciók és alkalmazásuk - Google Patents

Szóda/mész/szilikát típusú üvegkompozíciók és alkalmazásuk Download PDF

Info

Publication number
HU222256B1
HU222256B1 HU9601623A HU9601623A HU222256B1 HU 222256 B1 HU222256 B1 HU 222256B1 HU 9601623 A HU9601623 A HU 9601623A HU 9601623 A HU9601623 A HU 9601623A HU 222256 B1 HU222256 B1 HU 222256B1
Authority
HU
Hungary
Prior art keywords
weight
glass
zro
mgo
sio
Prior art date
Application number
HU9601623A
Other languages
English (en)
Other versions
HU9601623D0 (en
HUT76865A (en
Inventor
Didier Jousse
Stéphanie Koch
Francoise Rifqi
Original Assignee
Saint-Gobain Vitrage S.A.
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Priority claimed from FR9412209A external-priority patent/FR2725713B1/fr
Priority claimed from FR9414352A external-priority patent/FR2727399B1/fr
Application filed by Saint-Gobain Vitrage S.A. filed Critical Saint-Gobain Vitrage S.A.
Publication of HU9601623D0 publication Critical patent/HU9601623D0/hu
Publication of HUT76865A publication Critical patent/HUT76865A/hu
Publication of HU222256B1 publication Critical patent/HU222256B1/hu

Abstract

A találmány szerinti üvegkompozíció szubsztrátumok vagy termikusanstabil lemezek előállítására vonatkozik. A kompozíció a tömeg%-banmegadott következő alkotórészeket tartalmazza: SiO2 45–68 Al2O30–20 ZrO2 0–20 B2O3 0–10 Na2O 2–12 K2O3,5–9 CaO 1–13 MgO 0–8, ahol a SiO2, Al2O3 és ZrO2összmennyisége legfeljebb 70 tömeg%, az Al2O3 és ZrO2 összmennyiségelegalább 2 tö- meg%, a Na2O és K2O összmennyisége legalább 8 tömeg%,ahol a kompozíció BaO-ot és/vagy SrO-ot is tartal- mazhat olyanmennyiségben, amelyre érvényes a 11% ? MgO+CaO+BaO+SrO ? 30%összefüggés, továbbá a kompozícióra jellemző folyáspont legalább 530°C, és a lineáris hőtágulási együttható (?25– 300 °C) értéke 80×10–7/°C és 95×10–7/ °C között van. A fenti kompozíció felhasználhatóemissziós ernyők szubsztrátumainak vagy tűzálló üvegezésnek azelőállítására. ŕ

Claims (16)

  1. SZABADALMI IGÉNYPONTOK
    1. Üvegkompozíció szubsztrátumok vagy termikusán stabil lemezek előállítására, amely a tömeg%-ban megadott kővetkező alkotórészeket tartalmazza:
    SiO2 45-68 A12O3 0-20 30 Zro2 0-20 B2O3 0-10 Na2O 2-12 K2O 3,5-9 CaO 1-13 35 MgO 0-8,
    ahol a SiO2, A12O3 és ZrO2 összmennyisége legfeljebb 70 tömeg%, az Á12O3 és ZrO2 összmennyisége legalább 2 tömeg%, a Na2O és K2O összmennyisége legalább 8 tömeg%, és ahol a kompozíció BaO-ot és/vagy 40 SrO-ot is tartalmazhat olyan mennyiségben, amelyre érvényes a
    11% < MgO+CaO+BaO+SrO < 30% összefüggés, továbbá a kompozícióra jellemző folyáspont legalább 530 °C, és a lineáris hőtágulási együttha- 45 tó (a-25-300 °c) értéke 80 χ 10~7/ °C és 95 χ 10~7/ °C között van.
  2. 2. Az 1. igénypont szerinti üvegkompozíció, amely a tömeg%-ban megadott következő alkotórészeket tar-
    talmazza: 50 SiO2 45-68 A12O3 2-20 ZrO2 0-20 B2O3 0,5-4 Na2O 4-11 55 k2o 3,5-7 CaO 1-13 MgO 1-8, ahol a SiO2, A12O3 és ZrO2 összmennyisége legfeljebb 70 tömeg%, a Na2O és K2O összmennyisége legalább 60
    8 tömeg%, és ahol a kompozíció BaO-ot és/vagy SrO-ot is tartalmazhat olyan mennyiségben, amelyre érvényes a
    11% < MgO+CaO+BaO+SrO < 24% összefüggés, továbbá a kompozícióra jellemző folyáspont legalább 530 °C, és a lineáris hőtágulási együttható (a25_3oo °c) értéke 80 χ 10-7/ °C és 95 χ 10~7/ °C között van.
  3. 3. Az 1. vagy 2. igénypont szerinti üvegkompozíció, amelyben az A12O3 és ZrO2 összmennyisége legalább 5 tömeg%.
  4. 4. Az 1-3. igénypontok bármelyike szerinti üvegkompozíció, amelyben a SiO2 mennyisége 45-59 tömeg%.
  5. 5. Az 1-4. igénypontok bármelyike szerinti üvegkompozíció, amely a tömeg%-ban megadott következő alkotórészeket tartalmazza:
    SiO2 45-59 A12O3 5-18 ZrO2 0-17 B2O3 0,5-4 Na2O 4-10 K2O 3,5-7 CaO 1-12 MgO 1-7,
    ahol az alkálifém-oxidok összmennyisége legalább 10 tömeg%, és ahol a kompozíció BaO-ot és/vagy SrOot is tartalmazhat olyan mennyiségben, amelyre érvényes a
    14% < MgO+CaO+BaO+SrO < 22% összefüggés, továbbá a kompozícióra jellemző folyáspont legalább 550 °C, és a lineáris hőtágulási együttható (a25_300 °c) értéke 85 χ 10~7/ °C és 95 χ 10 7/ °C között van.
  6. 6. Az 1. igénypont szerinti üvegkompozíció, amely a tömeg%-ban megadott következő alkotórészeket tartalmazza:
    HU 222 256 Bl
    SiO2 45-63 ZrO2 6,5-20 ai2o3 0-18 Na2O 4-12 K2O 3,5-7 CaO 1-13 MgO 1-8,
    ahol a SiO2, A12O3 és ZrO2 összmennyisége legfeljebb 70 tömeg%, a Na2O és K2O összmennyisége legalább 8 tömeg%, és ahol a kompozíció BaO-ot és/vagy SrO-ot is tartalmazhat olyan mennyiségben, amelyre érvényes a
    11% < MgO+CaO+BaO+SrO < 24% összefüggés, továbbá a kompozícióra jellemző folyáspont legalább 530 °C, és a lineáris hőtágulási együttható (a25_3OO =c) értéke 80 χ 10~7/ °C és 95 χ 10~7/ °C között van.
  7. 7. A 6. igénypont szerinti üvegkompozíció, amelyben az A12O3 és ZrO2 összmennyisége legalább 8 tömeg%.
  8. 8. A 6. vagy 7. igénypont szerinti üvegkompozíció, amely 8-15 tömeg% ZrO2-ot tartalmaz.
  9. 9. A 6-8. igénypontok bármelyike szerinti üvegkompozíció, amely 45-59 tömeg% SiO2-ot tartalmaz.
  10. 10. A 6-9. igénypontok bármelyike szerinti üvegkompozíció, amely a tömeg%-ban megadott következő alkotórészeket tartalmazza:
    SiO2 45-59 ZrO2 8-15 A12O3 0-10 Na2O 4-10 K2O 3,5-7
    CaO 1-12
    MgO 1-7, ahol a Na2O és K2O összmennyisége legalább 10 tömeg%, a kompozíció BaO-ot és/vagy SrO-ot is tartalmazhat olyan mennyiségben, amelyre érvényes a
    14% < MgO+CaO+BaO+SrO < 22% összefüggés, továbbá a kompozícióra jellemző folyáspont legalább 550 °C, és a lineáris hőtágulási együttható (a25_300 oC) értéke 85 χ 10~7/ °C és 95 χ 10~7/ °C között van.
  11. 11. Az 1 -10. igénypontok bármelyike szerinti üvegkompozíció, amelyben az A12O3 és ZrO2 összmennyisége 8-22 tömeg%.
  12. 12. Az 1 -11. igénypontok bármelyike szerinti üvegkompozíció, amelynek viszkozitása az 1630 °C-ig, előnyösen az 1590 °C-ig teqedő hőmérsékleteken kielégíti a logr|=l,6 összefüggést.
  13. 13. Az 1-12. igénypontok bármelyike szerinti üvegkompozíció, amelynek viszkozitása az 1220 °C-ig, előnyösen az 1170 °C-ig terjedő hőmérsékleteken kielégíti a logq=3,5 összefüggést.
  14. 14. A 13. igénypont szerinti üvegkompozíció, amelynek likvidusz-hőmérséklete legfeljebb a logq=3,5 összefüggés által meghatározott hőmérsékletet éri el.
  15. 15. Az 1-4. igénypontok bármelyike szerinti üvegkompozíciók alkalmazása emissziós ernyők szubsztrátumának előállítására fémolvadékon üveg úsztatásával előállított üvegszalagból vágott üveglemezből.
  16. 16. Az 1-14. igénypontok bármelyike szerinti üvegkompozíciók alkalmazása tűzálló üvegezés előállítására fémolvadékon üveg úsztatásával előállított üvegszalagból vágott üvegtáblából vagy üveglemezből.
HU9601623A 1994-10-13 1995-10-13 Szóda/mész/szilikát típusú üvegkompozíciók és alkalmazásuk HU222256B1 (hu)