DE2124125C3 - Process for the production of an adhesive primer for synthetic resin putty - Google Patents
Process for the production of an adhesive primer for synthetic resin puttyInfo
- Publication number
- DE2124125C3 DE2124125C3 DE19712124125 DE2124125A DE2124125C3 DE 2124125 C3 DE2124125 C3 DE 2124125C3 DE 19712124125 DE19712124125 DE 19712124125 DE 2124125 A DE2124125 A DE 2124125A DE 2124125 C3 DE2124125 C3 DE 2124125C3
- Authority
- DE
- Germany
- Prior art keywords
- synthetic resin
- weight
- resin putty
- putty
- production
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired
Description
Die Erfindung bezieht sich auf ein Verfahren zur Herstellung einer Haftgrundierung für Kunstharzkitte an Metall- und 8etonbauwerken des Säureschutzbaues, durch Auftragen eines Gemisches aus Epoxidharz und Teer, aliphatischem Polyamin und Füllstoff.The invention relates to a method for producing an adhesive primer for synthetic resin putty on metal and concrete structures of the acid protection structure, by applying a mixture of epoxy resin and Tar, aliphatic polyamine and filler.
Kunstharzkitte mit hoher chemischer Beständigkeit werden im sogenannten Säureschutzbau zum Schutz des Untergrundes gegen chemischen Angriff verwendet. Dabei werden zur räumlichen Vermessung und Härtung der Kunstharzkitte auch saure Härter, zum Beispiel Benzolsulfonsäure, p-Toluolsulfonsäure, Amidosulfonsäure, /?-Naphthalinsulfonsäure und dergleichen zugesetzt. Durch diese Härter wird die Haftung der Kunstharzkitte auf Beton herabgesetzt. Beispielsweise be» der Ausmauerung von Behältern mit in Kunstharzkitt verlegten, keramischen Platten haben die Kunstharzkitt-Schichten erhebliche Lasten zu tragen, wobei die keramischen Platten ZLr festen Verankerung im Kunstharzkitt schwalbenschwanzförmige Vorsprünge oder Vertiefungen aufweisen. Der Kunstharzkitt muß zur Aufnahme der keramischen Platten für die Behälterauskleidung eine hinreichende Haftfestigkeit an der Behälterwandung besitzen.Synthetic resin putties with high chemical resistance are used in the so-called acid protection structure to protect the Underground used against chemical attack. This is used for spatial measurement and hardening the synthetic resin cement also acidic hardeners, for example benzenesulfonic acid, p-toluenesulfonic acid, amidosulfonic acid, /? - Naphthalenesulfonic acid and the like added. These hardeners reduce the adhesion of the synthetic resin putty to concrete. For example When lining containers with ceramic plates laid in synthetic resin putty, the synthetic resin putty has layers to bear considerable loads, with the ceramic plates ZLr firmly anchored in the Synthetic resin putty have dovetail-shaped projections or depressions. The synthetic resin putty must Adequate adhesive strength to accommodate the ceramic plates for the container lining have on the container wall.
Aus der DE-AS 12 20 542 sind Überzugsmittel zum Beschichten von ungrundierien Metallen oder anderen Werkstoffen mit Polyvinylchlorid- oder Polyvinylidenchloridüberzügen bekannt, die aus in der Hitze gelierbaren Dispersionen dieser Stoffe in Weichmachern, Stabilisatoren, Farbstoffen, Pigmenten. Epoxyharzen und Härtungsmittel bestehen, und als pastenartiges Gemisch durch Spritzen oder Tauchen aufgebracht werden. Bei einer Temperatur von 18O0C bis 185°C geliert dieses Überzugsmittel und härtet aus.From DE-AS 12 20 542 coating agents for coating unprimed metals or other materials with polyvinyl chloride or polyvinylidene chloride coatings are known, which are made from heat-gellable dispersions of these substances in plasticizers, stabilizers, dyes, pigments. Epoxy resins and curing agents exist, and are applied as a paste-like mixture by spraying or dipping. At a temperature of 18O 0 C to 185 ° C gelled this coating agent and hardens.
Unabhängig davon, daß die Metall- und Betonbauwerke des Säureschutzbaues nicht auf Temperaturen von 1800C bis 185°C erwärmt werden können, sind diese bekannten Überzugsmittel als Haftgrundierung fur das Aufbringen von Kunstharzkitten an Metall- und Betonbauwerken ungeeignet.Regardless of the metal and concrete structures of the Säureschutzbaues can not be heated to temperatures of 180 0 C to 185 ° C, these known coating compositions are not suitable as primer for the application of resin Kitten to metal and concrete structures.
Aus der DE-AS 12 23 087 sind korrosionsschützende Anstriche bekannt, die insbesondere bei Stahlkonstruktionen, Mauerwerk, Beton und dergleichen Verwendung finden. Diese Anstriche bestehen aus einem Gemisch von Epoxidharz, Teer, Füllstoff und einem aliphatischen Polyamin als Härtungsmittel. Ein solcher Korrosionsschutzanstrich härtet zwar bei Raumtemperatur aus, ist jedoch als Haftgrundierung für das Aufbringen von Kunstharzkitten an Metall- und Betonbauwerken ungeeignetFrom DE-AS 12 23 087 are anti-corrosion Paints known that are used in particular in steel structures, masonry, concrete and the like Find. These paints consist of a mixture of epoxy resin, tar, filler and an aliphatic Polyamine as a curing agent. Such an anti-corrosive paint hardens at room temperature, it is but as an adhesive primer for applying synthetic resin putty to metal and concrete structures not suitable
Der Erfindung liegt daher die Aufgabe zugrunde, ein Verfahren zur Herstellung einer Haftgrundierung gemäß dem Oberbegriff des Anspruches 1 zu schaffen, die für alle im Säureschutzbau verwendeten Kunstharzkitte eine ausreichende Haftverbindung zwischen dem Kunstharzkitt und dem Metall- oder Bfonbauwerk sicherstellt. Zur Lösung dieser Aufgabe wird bei einem Verfahren gemäß dem Oberbegriff des Patentanspuches vorgeschlagen, daß das aufzutragende Gemisch einen Anteil von 65 — 75Gew.-°/o Epoxidharz und Teer im Verhältnis von etwa 3:4. 8 — 20 Gew.-% Polyamin, 2-10 Gew.-% Füllstoff sowie zusätzlich 0,5-2,5 Gew.-% PVC-Pulver und 10-20 Gew.-% Lösungsmittelenthält. The invention is therefore based on the object of a method for producing an adhesive primer according to the preamble of claim 1 to create the synthetic resin putty for all synthetic resin putties used in acid protection structures a sufficient adhesive bond between the synthetic resin putty and the metal or telephone structure ensures. To solve this problem, in a method according to the preamble of the patent claim suggested that the mixture to be applied has a proportion of 65-75Gew.-% epoxy resin and tar in the Ratio of about 3: 4. 8-20% by weight polyamine, 2-10% by weight filler and an additional 0.5-2.5 Contains weight percent PVC powder and 10-20 weight percent solvent.
Das erfindungsgemäße Verfahren stellt sicher, daß die Kunstharzkitte sowohl für sich allein fest an den Metall- und Betonbauwerken des Säureschutzbaues haften, so daß auch keramische Platten von der Kunstharzkittschicht getragen werden können. Vor der Behälterauskleidung mit Kunstharzkitt und keramischen Spaltplatten ist das Aufbringen von Folienunterlagen oder Spachtelschichten nicht mehr erforderlich. Ein einmaliger Auftrag des erfindungsgemäßen Gemisches ist bereits ausreichend.The inventive method ensures that the synthetic resin cement both by itself firmly to the Metal and concrete structures of the acid protection structure adhere, so that ceramic plates from the Synthetic resin putty layer can be worn. In front of the container lining with synthetic resin putty and ceramic With split tiles, it is no longer necessary to apply foil underlays or filler layers. A single application of the mixture according to the invention is sufficient.
Die Erfindung wird nachfolgend anhand eines Ausführungsbeispieles näher erläutert. Dabei wurde ein Gemisch aus 35,5 Gew.-°/o Epoxidharz, 43,3 Gew.-% Teer, 15,7 Gew.-% Methylenchlorid, 13,5 Gew.-% eines aliphatischen Polyamins, 3,9 Gew.-% Talkum und 1,6 Gew.-% PVC-Pulver hergestellt. Dieses Gemisch wurde auf Beton-Prüfkörper aufgetragen. Bereits nach einmaligem Auftrag dieses Gemisches ergaben sich solche Haftfestigkeiten, daß bei Zerreißversuchen keine Ablösung der Phasengrenzfläche erfolgte, sondern die Prüfkörper zerstört wurden.The invention is explained in more detail below on the basis of an exemplary embodiment. It was a Mixture of 35.5% by weight of epoxy resin, 43.3% by weight of tar, 15.7% by weight of methylene chloride, 13.5% by weight of one aliphatic polyamine, 3.9% by weight talc and 1.6% by weight PVC powder. This mixture was applied to concrete test specimens. These resulted after just one application of this mixture Adhesion strengths that in the case of tearing tests there was no separation of the phase interface, but rather the Test specimens were destroyed.
Bei einmaligem Auftrag dieses Gemisches auf Stahl ergaben sich folgende Haftfestigkeiten:A single application of this mixture on steel resulted in the following adhesive strengths:
Phenolformaldehydharzkitt 34,2 kp/cm2 Phenol-formaldehyde resin putty 34.2 kgf / cm 2
Furanharzkitt 18,5 kp/cm2 Furan resin putty 18.5 kg / cm 2
Polyesterliarzkitt 131,0 kp/cm2 Polyester resin putty 131.0 kg / cm 2
Epoxidharzkitt 95,7 kp/cm2
Belonestrich zwischenEpoxy putty 95.7 kg / cm 2
Belone screed between
Stahlprüfkörpern 78,5 kp/cm2 Steel test pieces 78.5 kp / cm 2
Claims (1)