Bhaumik et al., 2002 - Google Patents

Failure of reformer tube of an ammonia plant

Bhaumik et al., 2002

View PDF
Document ID
12995423583363037211
Author
Bhaumik S
Rangaraju R
Parameswara M
Bhaskaran T
Venkataswamy M
Raghuram A
Krishnan R
Publication year
Publication venue
Engineering failure analysis

External Links

Snippet

The present article describes the failure of a primary reformer tube in an ammonia plant. The failure took place at the stub end of the reformer tube where a SS 321 flange was joined to a HK 40 catalyst tube by welding. Detailed metallurgical examinations indicated that the …
Continue reading at www.academia.edu (PDF) (other versions)

Classifications

    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C19/00—Alloys based on nickel or cobalt
    • C22C19/03—Alloys based on nickel or cobalt based on nickel
    • C22C19/05—Alloys based on nickel or cobalt based on nickel with chromium
    • C22C19/051—Alloys based on nickel or cobalt based on nickel with chromium and Mo or W
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
    • C22C38/46—Ferrous alloys, e.g. steel alloys containing chromium with nickel with vanadium
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C19/00—Alloys based on nickel or cobalt
    • C22C19/03—Alloys based on nickel or cobalt based on nickel
    • C22C19/05—Alloys based on nickel or cobalt based on nickel with chromium
    • C22C19/058—Alloys based on nickel or cobalt based on nickel with chromium without Mo and W
    • C—CHEMISTRY; METALLURGY
    • C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
    • C22C—ALLOYS
    • C22C38/00—Ferrous alloys, e.g. steel alloys
    • C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
    • C22C38/22—Ferrous alloys, e.g. steel alloys containing chromium with molybdenum or tungsten

Similar Documents

Publication Publication Date Title
Bhaumik et al. Failure of reformer tube of an ammonia plant
Parnian Failure analysis of austenitic stainless steel tubes in a gas fired steam heater
Otegui et al. Failure analysis of tube–tubesheet welds in cracked gas heat exchangers
Khalifeh et al. Stress corrosion cracking of a circulation water heater tubesheet
Bahrami et al. Failure of AISI 304H stainless steel elbows in a heat exchanger
Mohammadi Zahrani Premature failure of grade-316Ti stainless steel tubing in a boiler feed-water heat exchanger in a steel complex
Subramanian Dissimilar metal weld failure of steam piping in a hydrogen unit of petroleum refinery
Antunes et al. Effect of weld metal chemistry on stress corrosion cracking behavior of AISI 444 ferritic stainless steel weldments in boiling chloride solution
Shayegani et al. Failure analysis of reactor heater tubes SS347H in ISOMAX unit
Shi et al. Failure analysis of high-temperature reformer tube of Incoloy 800H in synthetic ammonia installation
Benac et al. High-temperature stress relaxation cracking and stress rupture observed in a coke gasifier failure
Shoemaker et al. Fabricating nickel alloys to avoid stress relaxation cracking
Baumert et al. Materials experience in methanol reforming units
Xiao et al. Failure analysis of convection section tube in an ethylene cracking furnace due to metal dusting
Hussain et al. Evaluation of Stress Relaxation Cracking on 800HT Pigtails of the Steam Reformer
Li et al. Failure analysis of cracking in the welded joints of hydrogen reformer outlet pigtail tubes
Das et al. Fatigue failure of a fillet welded nozzle joint
Pantazopoulos et al. Progressive failures of components in chemical process industry: Case history investigation and root-cause analysis
Jelani et al. Failure analysis of a furnace tube support
Ghosal Failure analysis of reactor effluent air cooler (REAC) in hydrocracker unit
Toppo et al. Studies on the Influence of Sodium Hydroxide Concentration on the Stress Corrosion Cracking Behavior of Modified 9Cr-1Mo (P91) Steel Weldment
Shalaby Failure investigation of a convection line elbow
Kaewkumsai et al. Reheat cracking failure of a welded alloy 803 outlet pigtail tube used in a steam hydrocarbon reforming furnace
Kucora et al. ETHYLENE PYROLYSIS FURNACE TUBE DAMAGE INSPECTION.
Maltry Case Study on Sensitization of Sensitization-Resistant Stainless Steels in Welded Joints