Xiao et al., 2023 - Google Patents
Failure analysis of convection section tube in an ethylene cracking furnace due to metal dustingXiao et al., 2023
- Document ID
- 5774804886153257805
- Author
- Xiao S
- Wang J
- Huang C
- Tian L
- Su W
- Publication year
- Publication venue
- Engineering Failure Analysis
External Links
Snippet
To study the failure in the convection section tubes of an ethylene cracking furnace, macroscopic inspections, chemical composition analysis, metallographic microscopy, hardness testing, Scanning Electron Microscopy (SEM) and Energy Dispersive …
Classifications
-
- C—CHEMISTRY; METALLURGY
- C10—PETROLEUM, GAS OR COKE INDUSTRIES; TECHNICAL GASES CONTAINING CARBON MONOXIDE; FUELS; LUBRICANTS; PEAT
- C10G—CRACKING HYDROCARBON OILS; PRODUCTION OF LIQUID HYDROCARBON MIXTURES, e.g. BY DESTRUCTIVE HYDROGENATION, OLIGOMERISATION, POLYMERISATION; RECOVERY OF HYDROCARBON OILS FROM OIL-SHALE, OIL-SAND, OR GASES; REFINING MIXTURES MAINLY CONSISTING OF HYDROCARBONS; REFORMING OF NAPHTHA; MINERAL WAXES
- C10G9/00—Thermal non-catalytic cracking, in the absence of hydrogen, of hydrocarbon oils
- C10G9/14—Thermal non-catalytic cracking, in the absence of hydrogen, of hydrocarbon oils in pipes or coils with or without auxiliary means, e.g. digesters, soaking drums, expansion means
- C10G9/18—Apparatus
- C10G9/20—Tube furnaces
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
- C22C38/46—Ferrous alloys, e.g. steel alloys containing chromium with nickel with vanadium
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C19/00—Alloys based on nickel or cobalt
- C22C19/03—Alloys based on nickel or cobalt based on nickel
- C22C19/05—Alloys based on nickel or cobalt based on nickel with chromium
- C22C19/051—Alloys based on nickel or cobalt based on nickel with chromium and Mo or W
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/22—Ferrous alloys, e.g. steel alloys containing chromium with molybdenum or tungsten
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING OR OTHER TREATMENTS
- C21D9/00—Heat treatment, e.g. annealing, hardening, quenching, tempering, adapted for particular articles; Furnaces therefor
- C21D9/50—Heat treatment, e.g. annealing, hardening, quenching, tempering, adapted for particular articles; Furnaces therefor for welded joints
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| Alvino et al. | Damage characterization in two reformer heater tubes after nearly 10 years of service at different operative and maintenance conditions | |
| Khodamorad et al. | Analysis of ethylene cracking furnace tubes | |
| Ul-Hamid et al. | Failure analysis of furnace radiant tubes exposed to excessive temperature | |
| Swaminathan et al. | Sensitization induced stress corrosion failure of AISI 347 stainless steel fractionator furnace tubes | |
| Pourmohammad et al. | Failure investigation on a radiant tube in an ethylene cracking unit | |
| Movahedi-Rad et al. | Failure analysis of superheater tube | |
| Attarian et al. | Microstructural and failure analysis of welded primary reformer furnace tube made of HP-Nb micro alloyed heat resistant steel | |
| Bahrami et al. | Failure of AISI 304H stainless steel elbows in a heat exchanger | |
| Firouzeh et al. | Failure assessment of ASTM A213-T12 superheater boiler tubes in a natural gas liquid plant | |
| Han et al. | Material degradation and embrittlement evaluation of ethylene cracking furnace tubes after long term service | |
| Tari et al. | Failure analysis of ethylene cracking tube | |
| Zhu et al. | High temperature corrosion and microstructure deterioration of KHR35H radiant tubes in continuous annealing furnace | |
| Mobaraki et al. | Effect of cracking feedstock on carburization mechanism of cracking furnace tubes | |
| Bhaumik et al. | Failure of reformer tube of an ammonia plant | |
| Zangeneh et al. | Fitness-for-service assessment and failure analysis of AISI 304 demineralized-water (DM) pipeline weld crack | |
| Mahalli et al. | Investigation of intergranular stress corrosion cracking in a failed 347H stainless steel furnace tube | |
| Liu et al. | Failure analysis of sulphidation-oxidation corrosion of Incoloy 800HT superheater tube | |
| Xiao et al. | Failure analysis of convection section tube in an ethylene cracking furnace due to metal dusting | |
| Shayegani et al. | Failure analysis of reactor heater tubes SS347H in ISOMAX unit | |
| Taghipour et al. | High temperature corrosion and metal dusting failure of deflector rods in a petrochemical cracking unit | |
| Shalaby et al. | Failure of 321 stainless steel heater tube in heavy crude oil | |
| Mohtadi-Bonab et al. | Rupture analysis of 12Cr1MoV super-heater tubes in power plants | |
| Azevedo et al. | Cracking of 2.25 Cr–1.0 Mo steel tube/stationary tube-sheet weldment of a heat-exchanger | |
| Kaewkumsai et al. | High temperature failure of natural gas feed burner pipe | |
| Poorhaydari | Failure of a hydrogenerator reactor inlet piping by high-temperature hydrogen attack |