Failure analysis of cracking in the welded joints of hydrogen reformer outlet pigtail tubesLi et al., 2022
- Document ID
- 8860803500580074399
- Author
- Li G
- Cai Q
- Lu X
- Zhu X
- Xu S
- Publication year
- Publication venue
- Engineering Failure Analysis
External Links
Snippet
Cracking failure of Incoloy 800H welded joints used for about eight months occurred in hydrogen reformer outlet pigtail tubes. Visual inspection, microscopic examination, chemical composition and microhardness testing were performed to find out the failure mechanism …
- 210000001503 Joints 0 title abstract description 48
Classifications
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/40—Ferrous alloys, e.g. steel alloys containing chromium with nickel
- C22C38/46—Ferrous alloys, e.g. steel alloys containing chromium with nickel with vanadium
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C19/00—Alloys based on nickel or cobalt
- C22C19/03—Alloys based on nickel or cobalt based on nickel
- C22C19/05—Alloys based on nickel or cobalt based on nickel with chromium
- C22C19/051—Alloys based on nickel or cobalt based on nickel with chromium and Mo or W
- C22C19/055—Alloys based on nickel or cobalt based on nickel with chromium and Mo or W with the maximum Cr content being at least 20% but less than 30%
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C19/00—Alloys based on nickel or cobalt
- C22C19/03—Alloys based on nickel or cobalt based on nickel
- C22C19/05—Alloys based on nickel or cobalt based on nickel with chromium
- C22C19/058—Alloys based on nickel or cobalt based on nickel with chromium without Mo and W
-
- C—CHEMISTRY; METALLURGY
- C22—METALLURGY; FERROUS OR NON-FERROUS ALLOYS; TREATMENT OF ALLOYS OR NON-FERROUS METALS
- C22C—ALLOYS
- C22C38/00—Ferrous alloys, e.g. steel alloys
- C22C38/18—Ferrous alloys, e.g. steel alloys containing chromium
- C22C38/22—Ferrous alloys, e.g. steel alloys containing chromium with molybdenum or tungsten
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING OR OTHER TREATMENTS
- C21D9/00—Heat treatment, e.g. annealing, hardening, quenching, tempering, adapted for particular articles; Furnaces therefor
- C21D9/50—Heat treatment, e.g. annealing, hardening, quenching, tempering, adapted for particular articles; Furnaces therefor for welded joints
-
- C—CHEMISTRY; METALLURGY
- C21—METALLURGY OF IRON
- C21D—MODIFYING THE PHYSICAL STRUCTURE OF FERROUS METALS; GENERAL DEVICES FOR HEAT TREATMENT OF FERROUS OR NON-FERROUS METALS OR ALLOYS; MAKING METAL MALLEABLE BY DECARBURISATION, TEMPERING OR OTHER TREATMENTS
- C21D9/00—Heat treatment, e.g. annealing, hardening, quenching, tempering, adapted for particular articles; Furnaces therefor
- C21D9/08—Heat treatment, e.g. annealing, hardening, quenching, tempering, adapted for particular articles; Furnaces therefor for tubular bodies or pipes
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| Pandey et al. | Effect of groove design and post-weld heat treatment on microstructure and mechanical properties of P91 steel weld | |
| Swaminathan et al. | Failure analysis and remaining life assessment of service exposed primary reformer heater tubes | |
| Ghalambaz et al. | A case study on failure of AISI 347H stabilized stainless steel pipe in a petrochemical plant | |
| Alvino et al. | Damage characterization in two reformer heater tubes after nearly 10 years of service at different operative and maintenance conditions | |
| Pramanick et al. | Failure investigation of super heater tubes of coal fired power plant | |
| Guan et al. | Analysis of failed ethylene cracking tubes | |
| Kim et al. | Corrosion and creep behavior of a Ni-base alloy in supercritical-carbon dioxide environment at 650 C | |
| Attarian et al. | Microstructural and failure analysis of welded primary reformer furnace tube made of HP-Nb micro alloyed heat resistant steel | |
| Pourmohammad et al. | Failure investigation on a radiant tube in an ethylene cracking unit | |
| Reihani et al. | Failure analysis and weld ability improvement of 35% Cr–45% Ni heat resistant alloy | |
| Kolluri et al. | Characterization of high temperature tensile and creep–fatigue properties of Alloy 800H for intermediate heat exchanger components of (V) HTRs | |
| Han et al. | Material degradation and embrittlement evaluation of ethylene cracking furnace tubes after long term service | |
| Guan et al. | Cracks and precipitate phases in 321 stainless steel weld of flue gas pipe | |
| Bhaumik et al. | Failure of reformer tube of an ammonia plant | |
| Li et al. | Failure analysis of cracking in the welded joints of hydrogen reformer outlet pigtail tubes | |
| Xiao et al. | Failure analysis of convection section tube in an ethylene cracking furnace due to metal dusting | |
| Li et al. | Characterization and formation mechanism of ultra-fine ferrite grains in dissimilar metal weld between austenitic stainless steel and low alloy ferritic steel | |
| Subramanian | Dissimilar metal weld failure of steam piping in a hydrogen unit of petroleum refinery | |
| Fuyang et al. | Feasibility assessment of local repairment for reformer furnace tubes in service exposure | |
| Guan et al. | Analysis of failed electron beam welds in ethylene cracking tubes | |
| Taghipour et al. | High temperature corrosion and metal dusting failure of deflector rods in a petrochemical cracking unit | |
| Guo et al. | Effects of W and Ce micro addition in filler metal on microstructure and creep strength of Cr35Ni45NbM alloy weld joint | |
| Shi et al. | Failure analysis of high-temperature reformer tube of Incoloy 800H in synthetic ammonia installation | |
| Tabuchi et al. | Long-term creep strength and fracture of Gr. 91 steel welds | |
| Guo et al. | Microstructural characterization and mechanical behavior of Cr25Ni35NbM alloy dissimilar weld joint for application in a hydrogen reformer furnace |