Investigation of the rotation speed on corrosion behavior of HP-13Cr stainless steel in the extremely aggressive oilfield environment by using the rotating cage testZhao et al., 2018
View PDF- Document ID
- 4659497506739998134
- Author
- Zhao Y
- Li X
- Zhang C
- Zhang T
- Xie J
- Zeng G
- Xu D
- Wang F
- Publication year
- Publication venue
- Corrosion Science
External Links
Snippet
The influence of rotation speed on the scale film and pitting mechanism of HP-13Cr SS in high temperature (> 180° C), high salinity (Cl− concentration> 60,000 mg/L) and high CO 2 pressure (> 4 MPa) oilfield environment was investigated using surface analysis and …
- 238000005260 corrosion 0 title abstract description 95
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| Zhao et al. | Investigation of the rotation speed on corrosion behavior of HP-13Cr stainless steel in the extremely aggressive oilfield environment by using the rotating cage test | |
| Zhang et al. | Electrochemical corrosion behavior of carbon steel under dynamic high pressure H2S/CO2 environment | |
| Asma et al. | Study on the effect of surface finish on corrosion of carbon steel in CO2 environment | |
| Aribo et al. | Erosion–corrosion behaviour of lean duplex stainless steels in 3.5% NaCl solution | |
| Zhu et al. | Study on the correlation between passive film and AC corrosion behavior of 2507 super duplex stainless steel in simulated marine environment | |
| Wei et al. | Corrosion of low alloy steel containing 0.5% chromium in supercritical CO2-saturated brine and water-saturated supercritical CO2 environments | |
| Xu et al. | Effect of Cr content on the corrosion performance of low-Cr alloy steel in a CO2 environment | |
| Tavares et al. | Effect of calcium carbonate on low carbon steel corrosion behavior in saline CO2 high pressure environments | |
| Jiang et al. | Effect of calcium ions on pitting corrosion and inhibition performance in CO2 corrosion of N80 steel | |
| Li et al. | Galvanic corrosion between N80 carbon steel and 13Cr stainless steel under supercritical CO2 conditions | |
| Lin et al. | Effect of O2 on corrosion of 3Cr steel in high temperature and high pressure CO2–O2 environment | |
| Xu et al. | Impact of surface roughness and humidity on X70 steel corrosion in supercritical CO2 mixture with SO2, H2O, and O2 | |
| Zhang et al. | The pitting to uniform corrosion evolution process promoted by large inclusions in mooring chain steels | |
| Wang et al. | Effects of flow velocity on the corrosion behaviour of super 13Cr stainless steel in ultra-HTHP CO2–H2S coexistence environment | |
| Lu et al. | Effect of temperature on the 3Cr low-alloyed steel initial corrosion behavior in CO2 solution | |
| Wang et al. | Unraveling the effect of H2S on the corrosion behavior of high strength sulfur-resistant steel in CO2/H2S/Cl− environments at ultra high temperature and high pressure | |
| Gao et al. | Corrosion behavior on carbon steel in a simulated soil solution under the interaction effect of chloride and bicarbonate ions | |
| Qi et al. | Effect of oxide scale on corrosion behavior of HP-13Cr stainless steel during well completion process | |
| Wang et al. | The role of Cr content on the corrosion resistance of carbon steel and low-Cr steels in the CO2-saturated brine | |
| Xiao et al. | Effect of elastic tensile stress on the pitting corrosion mechanism and passive film of 2205 duplex stainless steel | |
| Chen et al. | Dynamic mechanism of corrosion products formed on carbon steel in CO2 environment: Effect of silty sand | |
| Zhao et al. | Damage analysis of rotation speed on corrosion film of 3Cr steel in the CO2 environment with silty sand | |
| Zhao et al. | Early corrosion behavior of 35CrMo steel for high-strength bolt in simulated shallow and deep sea environments | |
| Yan et al. | Corrosion behaviors of SMSS 13Cr and DSS 22Cr in H2S/CO2-oil-water environment | |
| Liang et al. | Three phase corrosion of pipeline steel: Size effects of deposited solids under water droplets and an oil diffusion barrier |