Three phase corrosion of pipeline steel: Size effects of deposited solids under water droplets and an oil diffusion barrierLiang et al., 2021
View HTML- Document ID
- 6774068903544371627
- Author
- Liang H
- Schaller R
- Asselin E
- Publication year
- Publication venue
- Journal of Pipeline Science and Engineering
External Links
Snippet
Existing studies have examined either under deposit corrosion in bulk solutions or underoil droplet corrosion without deposits. Yet, neither of these scenarios represents the conditions existing within a diluted bitumen pipeline where underoil droplet corrosion occurs in tandem …
- 238000005260 corrosion 0 title abstract description 251
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| Zhu et al. | Study on the correlation between passive film and AC corrosion behavior of 2507 super duplex stainless steel in simulated marine environment | |
| Song et al. | Effects of chloride ions on corrosion of ductile iron and carbon steel in soil environments | |
| Zhao et al. | Investigation of the rotation speed on corrosion behavior of HP-13Cr stainless steel in the extremely aggressive oilfield environment by using the rotating cage test | |
| Javidi et al. | Failure analysis of a wet gas pipeline due to localised CO2 corrosion | |
| Liang et al. | Three phase corrosion of pipeline steel: Size effects of deposited solids under water droplets and an oil diffusion barrier | |
| Stack et al. | Mapping erosion–corrosion of carbon steel in oil–water solutions: Effects of velocity and applied potential | |
| Zhu et al. | Effect of AC on stress corrosion cracking behavior and mechanism of X80 pipeline steel in carbonate/bicarbonate solution | |
| Liu et al. | Electrochemical state conversion model for occurrence of pitting corrosion on a cathodically polarized carbon steel in a near-neutral pH solution | |
| Xiong et al. | The study of under deposit corrosion of carbon steel in the flowback water during shale gas production | |
| Benamor et al. | Effect of temperature and fluid speed on the corrosion behavior of carbon steel pipeline in Qatari oilfield produced water | |
| Yahaya et al. | Effects of clay and moisture content on soil-corrosion dynamic | |
| Pedersen et al. | CO2 corrosion inhibitor performance in the presence of solids: test method development | |
| Zeng et al. | Annular corrosion risk analysis of gas injection in CO2 flooding and development of oil-based annulus protection fluid | |
| Chen et al. | Failure analysis of corrosion products formed during CO2 pre-corrosion of X70 and 3Cr steels: Effect of oxygen contamination | |
| Chen et al. | Influence of CO2 partial pressure and flow rate on the corrosion behavior of N80 steel in 3.5% NaCl | |
| Chen et al. | Dynamic mechanism of corrosion products formed on carbon steel in CO2 environment: Effect of silty sand | |
| Li et al. | Role of microstructure heterogeneity on hydrogen-assisted fracture toughness degradation of X80 weld metal in H2S-saturated solution | |
| Ma et al. | A synergistic experimental and computational study on CO2 corrosion of X65 carbon steel under dispersed droplets within oil/water mixtures | |
| Burkle | Understanding the formation of protective FeCO3 on to carbon steel pipelines during CO2 corrosion | |
| Ye et al. | Corrosion behavior of carbon steel in crude oil–water–gas multiphase environments with CO2 and H2S | |
| He et al. | Unraveling short-term O2 contamination on under deposit corrosion of X65 pipeline steel in CO2 saturated solution | |
| Sun et al. | Laboratory study of sour localized/pitting corrosion | |
| Barker | Erosion-corrosion of carbon steel pipework on an offshore oil and gas facility | |
| Ren et al. | Coupling effect of hydrostatic pressure and erosion on corrosion behavior of X70 steel in simulated seawater | |
| Jasim | Evaluation the effect of velocity and temperature on the corrosion rate of crude oil pipeline in the presence of CO2/H2S dissolved gases |