Qi et al., 2021 - Google Patents
Effect of oxide scale on corrosion behavior of HP-13Cr stainless steel during well completion processQi et al., 2021
View PDF- Document ID
- 2235296972681368085
- Author
- Qi W
- Wang J
- Li X
- Cui Y
- Zhao Y
- Xie J
- Zeng G
- Gao Q
- Zhang T
- Wang F
- Publication year
- Publication venue
- Journal of Materials Science & Technology
External Links
Snippet
The well completion process in oil and gas industry, aiming to build effective exploitation, is divided into acidizing and formation water production process. Oxide scale (OS) formed on the inner wall of the HP-13Cr stainless steel tubes during the hot extrusion process changes …
- 229910001220 stainless steel 0 title abstract description 168
Classifications
-
- G—PHYSICS
- G01—MEASURING; TESTING
- G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
- G01N2203/00—Investigating strength properties of solid materials by application of mechanical stress
- G01N2203/0058—Kind of property studied
- G01N2203/006—Crack, flaws, fracture or rupture
- G01N2203/0062—Crack or flaws
-
- G—PHYSICS
- G01—MEASURING; TESTING
- G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
- G01N17/00—Investigating resistance of materials to the weather, to corrosion, or to light
- G01N17/04—Corrosion probes
- G01N17/043—Coupons
- G01N17/046—Means for supporting or introducing coupons
-
- G—PHYSICS
- G01—MEASURING; TESTING
- G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
- G01N2203/00—Investigating strength properties of solid materials by application of mechanical stress
- G01N2203/02—Details not specific for a particular testing method
- G01N2203/025—Geometry of the test
-
- G—PHYSICS
- G01—MEASURING; TESTING
- G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
- G01N27/00—Investigating or analysing materials by the use of electric, electro-chemical, or magnetic means
- G01N27/72—Investigating or analysing materials by the use of electric, electro-chemical, or magnetic means by investigating magnetic variables
- G01N27/82—Investigating or analysing materials by the use of electric, electro-chemical, or magnetic means by investigating magnetic variables for investigating the presence of flaws
-
- G—PHYSICS
- G01—MEASURING; TESTING
- G01N—INVESTIGATING OR ANALYSING MATERIALS BY DETERMINING THEIR CHEMICAL OR PHYSICAL PROPERTIES
- G01N17/00—Investigating resistance of materials to the weather, to corrosion, or to light
- G01N17/006—Investigating resistance of materials to the weather, to corrosion, or to light of metals
Similar Documents
| Publication | Publication Date | Title |
|---|---|---|
| Qi et al. | Effect of oxide scale on corrosion behavior of HP-13Cr stainless steel during well completion process | |
| Zhao et al. | Investigation of the rotation speed on corrosion behavior of HP-13Cr stainless steel in the extremely aggressive oilfield environment by using the rotating cage test | |
| Yaro et al. | Effect of CO2 corrosion behavior of mild steel in oilfield produced water | |
| Song et al. | Mechanism of crack initiation and early growth of high strength steels in very high cycle fatigue regime | |
| Wang et al. | Experimental and theoretical studies of chitosan derivatives as green corrosion inhibitor for oil and gas well acid acidizing | |
| Zhen-yu et al. | Research on the construction of gradient nanostructure and anti-tribocorrosion behavior of aluminum alloy surface | |
| Mollapour et al. | Experimental and numerical analysis of Pitting Corrosion in CUSTOM 450 Stainless Steel | |
| Zhang et al. | The stress corrosion cracking behavior of N80 carbon steel under a crevice in an acidic solution containing different concentrations of NaCl | |
| Luo et al. | Stress corrosion cracking behavior and mechanism of super 13Cr stainless steel in simulated O2/CO2 containing 3.5 wt% NaCl solution | |
| Li et al. | Synergistic effect between cavitation erosion and corrosion for friction stir processed NiAl bronze in artificial seawater | |
| Hua et al. | Revealing fretting corrosion synergistic mechanism of 316 stainless steel in liquid lead-bismuth eutectic (LBE) | |
| Liu et al. | Investigation on leakage cause of oil pipeline in the west oilfield of China | |
| Zhang et al. | Corrosion and stress corrosion cracking behavior of X70 pipeline steel in a CO 2-containing solution | |
| Sun et al. | Numerical study on stress corrosion of X70 pipeline with the combined action of pits by sulfate-reducing bacteria and constant load | |
| Zhang et al. | Corrosion form transition of mooring chain in simulated deep-sea environments: Remarkable roles of dissolved oxygen and hydrostatic pressure | |
| Zhao et al. | Effect of the flow velocity on the corrosion behavior of UNS S41426 stainless steel in the extremely aggressive oilfield environment for the Tarim area | |
| Zhang et al. | Effects of chloride on electrochemical and stress corrosion cracking behavior of 9Cr ferritic–martensitic steel | |
| Liu et al. | Synergetic effect of corrosion and ultrasonic cavitation erosion on leaded brass | |
| Fu et al. | Corrosion mechanism and fatigue behavior of 2A70-T6 aluminum alloy under alternating corrosion and fatigue | |
| Tan et al. | Corrosion behavior of X80 pipeline steel local defect pits under static liquid film | |
| Zhou et al. | Effect of plastic deformation and texture on corrosion of cold-rolled AA6061 in NaCl neutral solution | |
| Paolinelli et al. | Mechanical integrity of corrosion product films on rotating cylinder specimens | |
| Pal et al. | Corrosion pit to crack transition behavior of 304 stainless steel in a chloride solution | |
| Xie et al. | Effect of low-temperature environment on stress corrosion cracking behavior of X80 pipeline steel in simulated alkaline soil solution | |
| Meena et al. | Flow-Assisted Corrosion of API 5L X56 Steel: Effect of Flow Velocity and Dissolved Oxygen |