WO2024106156A1 - 積層体 - Google Patents

積層体 Download PDF

Info

Publication number
WO2024106156A1
WO2024106156A1 PCT/JP2023/038599 JP2023038599W WO2024106156A1 WO 2024106156 A1 WO2024106156 A1 WO 2024106156A1 JP 2023038599 W JP2023038599 W JP 2023038599W WO 2024106156 A1 WO2024106156 A1 WO 2024106156A1
Authority
WO
WIPO (PCT)
Prior art keywords
weight
adherend
acrylate
film
meth
Prior art date
Application number
PCT/JP2023/038599
Other languages
English (en)
French (fr)
Inventor
和也 浦上
圭太 小川
尚樹 橋本
貴之 足立
Original Assignee
日東電工株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 日東電工株式会社 filed Critical 日東電工株式会社
Publication of WO2024106156A1 publication Critical patent/WO2024106156A1/ja

Abstract

外力による変形による変形跡が残りにくく、被着体からの表面保護フィルムの初期剥離力が適度であり、被着体からの表面保護フィルムの剥離力の経時変化が小さい、表面保護フィルムと被着体を含む積層体を提供する。　本発明の実施形態による積層体は、表面保護フィルムと被着体を含む積層体であって、該表面保護フィルムは、基材と粘着剤層を有し、該粘着剤層と該被着体が直接積層されてなり、該被着体の該表面保護フィルム側の表面の水接触角が８５°以上であり、該被着体の該表面保護フィルム側の表面の算術平均表面粗さＲａが０．６μｍ以下であり、（ｉ）該粘着剤層のクリープリカバリー値が９６％以上である、および（ｉｉ）該表面保護フィルムのせん断弾性係数Ｇが３９．０Ｎ／５０ｍｍ3以下である、から選ばれる少なくとも１種である。

Description

積層体
　本発明は、積層体に関する。
　光学部材の表面には、表面保護や耐衝撃性付与等を目的として、表面保護フィルムが設けられる。表面保護フィルムとしては、代表的には、デバイスの組み立て、加工、輸送等の使用前の状態において一時的に仮着され、デバイスの使用前に再剥離されるもの（工程材として用いられるもの）、デバイスの使用時にもデバイス表面に貼着したままの状態で使用されるもの（永久接着を目的としたもの）がある（例えば、特許文献１参照）。
　工程材として用いられる表面保護フィルムおよび永久接着を目的とした表面保護フィルムは、いずれも、フィルム基材の主面に粘着剤層を備え、この粘着剤層を介して、保護対象である被着体の表面に貼り合わせられる（例えば、特許文献２参照）。
　光学部材などを被着体とし、この被着体に表面保護フィルムの粘着剤層が貼り合わせられた積層構造を有する積層体は、従来、次のような問題がある。
　上記のような積層体の取り扱い時の外力による変形により変形跡が残ってしまうと、不良品となってしまうおそれがあり、歩留まりが低下してしまうおそれがある。
　上記のような積層体において、被着体からの表面保護フィルムの初期剥離力が低すぎると、被着体からの表面保護フィルムの浮きが生じるおそれや、被着体の表面保護フィルムと反対側に設けられたはく離ライナー（すなわち、はく離ライナー／被着体／表面保護フィルムの積層構成における該はく離ライナー）をはく離する際に、被着体とはく離ライナーの界面でのはく離よりも表面保護フィルムと被着体の界面でのはく離が起こってしまうというはく離不良（意図しない箇所のはく離）が生じるおそれがある。
　上記のような積層体において、被着体からの表面保護フィルムの初期剥離力が高すぎると、被着体から表面保護フィルムを剥離できなくなるおそれがある。
　上記のような積層体において、被着体からの表面保護フィルムの剥離力が経時で大きく上昇すると、被着体から表面保護フィルムを剥離できなくなるおそれがある。
特許第３５１８６７７号公報 特許第６２４９６１７号公報
　本発明の課題は、外力による変形による変形跡が残りにくく、被着体からの表面保護フィルムの初期剥離力が適度であり、被着体からの表面保護フィルムの剥離力の経時変化が小さい、表面保護フィルムと被着体を含む積層体を提供することにある。
　［１］本発明の一つの実施形態による積層体は、表面保護フィルムと被着体を含む積層体であって、該表面保護フィルムは、基材と粘着剤層を有し、該粘着剤層と該被着体が直接積層されてなり、該被着体の該表面保護フィルム側の表面の水接触角が８５°以上であり、該被着体の該表面保護フィルム側の表面の算術平均表面粗さＲａが０．６μｍ以下であり、該粘着剤層のクリープリカバリー値が９６％以上である。
　［２］本発明の別の一つの実施形態による積層体は、表面保護フィルムと被着体を含む積層体であって、該表面保護フィルムは、基材と粘着剤層を有し、該粘着剤層と該被着体が直接積層されてなり、該被着体の該表面保護フィルム側の表面の水接触角が８５°以上であり、該被着体の該表面保護フィルム側の表面の算術平均表面粗さＲａが０．６μｍ以下であり、該表面保護フィルムのせん断弾性係数Ｇが３９．０Ｎ／５０ｍｍ3以下である。
　［３］上記［１］または［２］に記載の積層体において、上記水接触角が８５°～１０５°であってもよい。
　［４］上記［１］から［３］までのいずれかに記載の積層体において、上記算術平均表面粗さＲａが０．１μｍ以下であってもよい。
　［５］上記［１］、［３］、または［４］に記載の積層体において、上記クリープリカバリー値が９９％以上であってもよい。
　［６］上記［２］から［４］までのいずれかに記載の積層体において、上記せん断弾性係数Ｇが３０．０Ｎ／５０ｍｍ3以下であってもよい。
　本発明によれば、外力による変形による変形跡が残りにくく、被着体からの表面保護フィルムの初期剥離力が適度であり、被着体からの表面保護フィルムの剥離力の経時変化が小さい、表面保護フィルムと被着体を含む積層体を提供することができる。
本発明の積層体の一つの実施形態を示す概略断面図である。 積層体の変形を評価する方法を説明する概略説明図である。
　本明細書中で「重量」との表現がある場合は、重さを示すＳＩ系単位として慣用されている「質量」と読み替えてもよい。
　本明細書中で「（メタ）アクリル」との表現がある場合は、「アクリルおよび／またはメタクリル」を意味し、「（メタ）アクリレート」との表現がある場合は、「アクリレートおよび／またはメタクリレート」を意味し、「（メタ）アリル」との表現がある場合は、「アリルおよび／またはメタリル」を意味し、「（メタ）アクロレイン」との表現がある場合は、「アクロレインおよび／またはメタクロレイン」を意味する。
　本発明の実施形態による積層体は、表面保護フィルムと被着体を含む。表面保護フィルムは、基材と粘着剤層を有する。
　本発明の実施形態による積層体においては、粘着剤層と被着体が直接積層されてなる。
　図１は、本発明の積層体の一つの実施形態であり、積層体１０００は、表面保護フィルム１００と被着体２００を含み、該表面保護フィルム１００は、基材１０と粘着剤層２０を有する。粘着剤層２０と被着体２００は直接積層されている。
　本発明の実施形態による積層体は、表面保護フィルムと被着体を含んでいれば、本発明の効果を損なわない範囲で、任意の適切な他の層を含んでいてもよい。このような他の層としては、例えば、ガラス、ディスプレイ、撮像装置、レンズ、（ハーフ）ミラーが挙げられる。
　本発明の実施形態による積層体の総厚みは、被着体の種類や含み得る他の層の種類によって適宜設定し得る。代表的には、本発明の実施形態による積層体の総厚みは、好ましくは１０μｍ～１０００μｍであり、より好ましくは２５μｍ～８００μｍであり、さらに好ましくは４０μｍ～６００μｍであり、特に好ましくは５０μｍ～５００μｍである。
　本発明の実施形態による積層体においては、被着体の表面保護フィルム側（表面保護フィルムが積層されている側）の表面の水接触角が、好ましくは８５°以上であり、より好ましくは８５°～１１０°であり、さらに好ましくは８５°～１０５°であり、さらに好ましくは９０°～１００°であり、特に好ましくは９５°～１００°であり、最も好ましくは９５°～９９°である。上記水接触角が上記範囲内にあれば、本発明の効果がより発現し得る。上記水接触角が上記範囲を外れて小さすぎると、表面保護フィルムが被着体に過度に密着しやすくなり、例えば、被着体からの表面保護フィルムの初期剥離力が高くなって、被着体から表面保護フィルムを剥離できなくなるおそれがあり、被着体からの表面保護フィルムの剥離力が経時で大きく上昇しすぎて、被着体から表面保護フィルムを剥離できなくなるおそれがある。上記水接触角が上記範囲を外れて大きすぎると、表面保護フィルムが被着体に過度に密着しにくくなり、例えば、被着体からの表面保護フィルムの初期剥離力が低すぎることとなり、被着体からの表面保護フィルムの浮きが生じるおそれや、被着体の表面保護フィルムと反対側に設けられたはく離ライナー（すなわち、はく離ライナー／被着体／表面保護フィルムの積層構成における該はく離ライナー）をはく離する際に、被着体とはく離ライナーの界面でのはく離よりも表面保護フィルムと被着体の界面でのはく離が起こってしまうというはく離不良（意図しない箇所のはく離）が生じるおそれがある。
　本発明の実施形態による積層体においては、被着体の表面保護フィルム側（表面保護フィルムが積層されている側）の表面の算術平均表面粗さＲａが、好ましくは０．６μｍ以下であり、より好ましくは０．３５μｍ以下であり、さらに好ましくは０．２μｍ以下であり、特に好ましくは０．１μｍ以下であり、最も好ましくは０．０８μｍ以下である。上記算術平均表面粗さＲａの下限値は小さければ小さいほどよく、好ましくは０μｍ以上である。上記算術平均表面粗さＲａが上記範囲内にあれば、本発明の効果がより発現し得る。上記算術平均表面粗さＲａが上記範囲を外れて大きすぎると、例えば、表面保護フィルムが有する粘着剤層の厚みが大きい場合、被着体からの表面保護フィルムの剥離力が経時で大きく上昇しすぎて、被着体から表面保護フィルムを剥離できなくなるおそれがある。
　本発明の実施形態による積層体においては、表面保護フィルムが有する粘着剤層のクリープリカバリー値が、好ましくは９６％以上であり、より好ましくは９７％以上であり、さらに好ましくは９８％以上であり、特に好ましくは９９％以上である。上記クリープリカバリー値が上記範囲内にあれば、本発明の効果がより発現し得る。上記クリープリカバリー値が上記範囲を外れて小さすぎると、外力による変形による変形跡が残りやすくなるおそれがある。
　本発明の実施形態による積層体においては、表面保護フィルムのせん断弾性係数Ｇが、好ましくは３９．０Ｎ／５０ｍｍ3以下であり、より好ましくは２７．０Ｎ／５０ｍｍ3～３９．０Ｎ／５０ｍｍ3であり、さらに好ましくは２７．５Ｎ／５０ｍｍ3～３８．５Ｎ／５０ｍｍ3であり、特に好ましくは２８．０Ｎ／５０ｍｍ3～３８．０Ｎ／５０ｍｍ3である。上記せん断弾性係数Ｇが上記範囲内にあれば、本発明の効果がより発現し得る。上記せん断弾性係数Ｇが上記範囲を外れてると、外力による変形による変形跡が残りやすくなるおそれがある。
　本発明の実施形態による積層体においては、表面保護フィルムが有する粘着剤層の厚みが、好ましくは１μｍ以上であり、より好ましくは５μｍ以上であり、さらに好ましくは１０μｍ以上であり、特に好ましくは１５μｍ以上であり、最も好ましくは１８μｍ以上である。上記粘着剤層の厚みの上限値は、好ましくは１５０μｍ以下であり、より好ましくは１００μｍ以下であり、さらに好ましくは８０μｍ以下であり、特に好ましくは５０μｍ以下であり、最も好ましくは３０μｍ以下である。上記粘着剤層の厚みが上記範囲内にあれば、本発明の効果がより発現し得る。上記粘着剤層の厚みが上記範囲を外れて小さすぎると、外力による変形による変形跡が残りやすくなるおそれがある。上記粘着剤層の厚みが上記範囲を外れて大きすぎると、被着体が光学部材である場合など、薄型デバイスへの適用ができなくなるおそれがある。
≪≪１．表面保護フィルム≫≫
　表面保護フィルムは、基材と粘着剤層を有する。表面保護フィルムの一つの実施形態は、基材と粘着剤層とからなる（例えば、図１に示すように、表面保護フィルム１００が、基材１０と粘着剤層２０とからなる）。
　表面保護フィルムは、本発明の効果を損なわない範囲で、基材と粘着剤層以外の任意の適切な他の層を有していてもよい。
　このような他の層としては、例えば、易接着層、易滑層、ブロッキング防止層、帯電防止層、反射防止層、オリゴマー防止層、粘着剤層の基材と反対側の表面に設けるはく離ライナーが挙げられる。
　表面保護フィルムの構成要素（基材、粘着剤層、必要に応じて他の層など）は、本発明の効果を損なわない範囲で、任意の適切な添加剤を含んでいてもよい。このような添加剤としては、例えば、酸化防止剤、紫外線吸収剤、光安定剤、造核剤、充填剤、顔料、界面活性剤、帯電防止剤が挙げられる。
　粘着剤層の基材と反対側には、被着体と積層するまでの間、保護等のために、必要に応じて、はく離ライナーが設けられていてもよい。
　はく離ライナーとしては、例えば、紙やプラスチックフィルム等の基材（ライナー基材）の表面がシリコーン処理されたはく離ライナー、紙やプラスチックフィルム等の基材（ライナー基材）の表面がポリオレフィン系樹脂によりラミネートされたはく離ライナーなどが挙げられる。ライナー基材としてのプラスチックフィルムとしては、例えば、ポリエチレンフィルム、ポリプロピレンフィルム、ポリブテンフィルム、ポリブタジエンフィルム、ポリメチルペンテンフィルム、ポリ塩化ビニルフィルム、塩化ビニル共重合体フィルム、ポリエチレンテレフタレートフィルム、ポリブチレンテレフタレートフィルム、ポリウレタンフィルム、エチレン－酢酸ビニル共重合体フィルムなどが挙げられる。
　はく離ライナーの厚みは、好ましくは１μｍ～５００μｍであり、より好ましくは３μｍ～４５０μｍであり、さらに好ましくは５μｍ～４００μｍであり、特に好ましくは１０μｍ～３００μｍである。
≪１－１．基材≫
　基材は、１層からなる基材であってもよいし、２層以上の積層構造からなる基材であってもよい。
　基材の厚みは、本発明の効果を損なわない範囲で、任意の適切な厚みを採用し得る。本発明の効果をより発現させ得る点で、基材の厚みは、好ましくは５μｍ～１０００μｍであり、より好ましくは１０μｍ～８００μｍであり、さらに好ましくは２０μｍ～６００μｍであり、特に好ましくは３０μｍ～４００μｍである。
　基材の材料としては、本発明の効果を損なわない範囲で、任意の適切な材料を採用し得る。本発明の効果をより発現させ得る点で、このような材料としては、好ましくは、プラスチックが挙げられる。
　プラスチックとしては、本発明の効果を損なわない範囲で、任意の適切なプラスチックを採用し得る。本発明の効果をより発現させ得る点で、このようなプラスチックとしては、好ましくは、熱可塑性樹脂が挙げられる。
　熱可塑性樹脂としては、例えば、ポリエステル、アクリル系樹脂、ウレタン系樹脂、ポリカーボネート、トリアセチルセルロース（ＴＡＣ）、ポリオレフィン（オレフィン単独重合体、オレフィンと他のモノマーの共重合体）、ポリアミド（ナイロン）、全芳香族ポリアミド（アラミド）、ポリイミド（ＰＩ）、ポリ塩化ビニル（ＰＶＣ）、ポリ酢酸ビニル、環状オレフィン系ポリマーが挙げられる。
　熱可塑性樹脂としては、本発明の効果をより発現させ得る点で、ポリエステルが好ましい。ポリエステルとしては、例えば、ポリエチレンテレフタレート（ＰＥＴ）、ポリエチレンナフタレート（ＰＥＮ）、ポリブチレンテレフタレート（ＰＢＴ）が挙げられ、本発明の効果をより発現させ得る点で、ポリエチレンテレフタレート（ＰＥＴ）が好ましい。
≪１－２．粘着剤層≫
　粘着剤層は、１層からなる粘着剤層であってもよいし、２層以上の積層構造からなる粘着剤層であってもよい。
　粘着剤層の厚みは、前述した通りである。
　粘着剤層を構成する粘着剤は、好ましくは、アクリル系粘着剤、ウレタン系粘着剤、および、シリコーン系粘着剤からなる群から選ばれる少なくとも１種である。
　粘着剤層は、より好ましくは、アクリル系粘着剤から構成される。
　アクリル系粘着剤は、アクリル系粘着剤組成物から形成される。
　アクリル系粘着剤は、このように、アクリル系粘着剤組成物から形成されるものとして規定し得る。これは、アクリル系粘着剤は、アクリル系粘着剤組成物が、加熱や紫外線照射などによって架橋反応などを起こすことにより、アクリル系粘着剤となるため、アクリル系粘着剤をその構造により直接特定することが不可能であり、また、およそ実際的でないという事情（「不可能・非実際的事情」）が存在するため、「アクリル系粘着剤組成物から形成されるもの」との規定により、アクリル系粘着剤を「物」として妥当に特定したものである。
　粘着剤層は、任意の適切な方法によって形成し得る。このような方法としては、例えば、粘着剤層を構成する粘着剤を形成する粘着剤組成物を任意の適切な基材上に塗布し、必要に応じて加熱や乾燥を行い、必要に応じて硬化させて、該基材上において粘着剤層を形成する方法、粘着剤層を構成する粘着剤を形成する粘着剤組成物を任意の適切なはく離ライナーなどのフィルム上に塗布し、必要に応じて加熱や乾燥を行い、必要に応じて硬化させて、該フィルム上において粘着剤層を形成し、該粘着剤層上に任意の適切な基材を貼り合わせて転写することにより、該基材上において粘着剤層を形成する方法、が挙げられる。
　アクリル系粘着剤組成物を塗布する手段としては、本発明の効果を損なわない範囲で、任意の適切な手段を採用し得る。このような塗布の手段としては、例えば、ロールコート法、グラビアロールコート法、リバースロールコート法、キスロールコート法、ディップロールコート法、バーコート法、ロールブラッシュコート法、スプレーコート法、ナイフコート法、エアーナイフコート法、コンマコート法、ダイレクトコート法、ダイコート法が挙げられる。
　アクリル系粘着剤組成物の加熱や乾燥は、本発明の効果を損なわない範囲で、任意の適切な手段を採用し得る。このような加熱や乾燥の手段としては、例えば、６０℃～１８０℃に加熱することや、例えば、室温程度の温度で、エージング処理を行うことが挙げられる。
　アクリル系粘着剤組成物の硬化は、本発明の効果を損なわない範囲で、任意の適切な手段を採用し得る。このような硬化の手段としては、例えば、熱、紫外線照射、レーザー線照射、α線照射、β線照射、γ線照射、Ｘ線照射、電子線照射が挙げられる。
　アクリル系粘着剤組成物は、本発明の効果をより発現させ得る点で、好ましくは、アクリル系ポリマーを含む。
＜１－２－ａ．アクリル系ポリマー＞
　アクリル系ポリマーは、アクリル系粘着剤の分野においていわゆるベースポリマーと称され得るものである。アクリル系ポリマーは、１種のみであってもよいし、２種以上であってもよい。
　すなわち、粘着剤層の好ましい実施形態は、アクリル系粘着剤組成物から形成されるアクリル系粘着剤から構成され、該アクリル系粘着剤組成物はアクリル系ポリマーをベースポリマーとして含む実施形態である。
　アクリル系粘着剤組成物中のアクリル系ポリマーの含有割合は、固形分換算で、好ましくは６０重量％～９９．９重量％であり、より好ましくは６５重量％～９９．９重量％であり、さらに好ましくは７０重量％～９９．９重量％であり、特に好ましくは７５重量％～９９．９重量％であり、最も好ましくは８０重量％～９９．９重量％である。
　アクリル系ポリマーとしては、本発明の効果を損なわない範囲で、任意の適切なアクリル系ポリマーを採用し得る。
　アクリル系ポリマーの重量平均分子量は、本発明の効果をより発現させ得る点で、好ましくは３０万～２００万であり、より好ましくは３５万～１５０万であり、さらに好ましくは４０万～１００万であり、特に好ましくは５０万～１００万である。上記重量平均分子量が低すぎると、低分子量成分が多く含まれる傾向があり、低分子量成分の塑性変形が起こり得るため、外力による変形による変形跡が残りやすくなるおそれがある。
　アクリル系ポリマーの好ましい実施形態は、重合開始剤を用いた溶液重合で調製したアクリル系ポリマーである。重合開始剤を用いた重合の方法としては、例えば、従来公知の方法など、本発明の効果を損なわない範囲で、任意の適切な方法を採用し得る。
　アクリル系ポリマーは、モノマー成分（Ｍ）を重合して得られるものである。ここでいうモノマー成分（Ｍ）には、アクリル系粘着剤組成物中に含み得る後述する架橋剤は包含されない。アクリル系ポリマーを重合により得る際には、モノマー成分（Ｍ）、重合開始剤以外に、本発明の効果を損なわない範囲で、任意の適切な添加剤を用いてもよい。
　アクリル系ポリマーは、このように、モノマー成分（Ｍ）を重合して得られるものとして規定し得る。これは、アクリル系ポリマーは、モノマー成分（Ｍ）が重合反応を起こすことによりアクリル系ポリマーとなり、アクリル系ポリマーをその構造により直接特定することが不可能であり、また、およそ実際的でないという事情（「不可能・非実際的事情」）が存在するため、「モノマー成分（Ｍ）を重合して得られるもの」との規定により、アクリル系ポリマーを「物」として妥当に特定したものである。
　アクリル系ポリマーは、本発明の効果をより発現させ得る点で、そのガラス転移温度Ｔｇが、好ましくは０℃以下であり、より好ましくは－１０℃以下であり、さらに好ましくは－１５℃以下であり、特に好ましくは－２０℃以下であり、最も好ましくは－２５℃以下である。上記ガラス転移温度Ｔｇの下限値は、好ましくは－１００℃以上であり、より好ましくは－９０℃以上であり、さらに好ましくは－８０℃以上である。アクリル系ポリマーのガラス転移温度Ｔｇを上記の特定の範囲内に調整することにより、本発明の効果をより発現させ得る。
　ここで、アクリル系ポリマーのガラス転移温度Ｔｇとは、アクリル系ポリマーを構成する各モノマーの単独重合体（ホモポリマー）のガラス転移温度Ｔｇおよび該モノマーの重量分率（重量基準の共重合割合）に基づいて、フォックス（Ｆｏｘ）の式から求められる値をいう。Ｆｏｘの式とは、以下に示すように、共重合体のガラス転移温度Ｔｇと、該共重合体を構成するモノマーのそれぞれを単独重合したホモポリマーのガラス転移温度Ｔｇｉとの関係式である。
１／Ｔｇ＝Σ（Ｗｉ／Ｔｇｉ）
　上記Ｆｏｘの式において、Ｔｇは共重合体のガラス転移温度（単位：Ｋ）、Ｗｉは該共重合体におけるモノマーｉの重量分率（重量基準の共重合割合）、Ｔｇｉはモノマーｉのホモポリマーのガラス転移温度（単位：Ｋ）を表す。ホモポリマーのガラス転移温度Ｔｇとしては、公知資料に記載の値を採用するものとする。
　ホモポリマーのガラス転移温度Ｔｇとして、例えば、具体的には以下の値を用い得る。
ｎ－ブチルアクリレート（ＢＡ）のホモポリマー：－５５℃
ラウリルアクリレート（ＬＡ）のホモポリマー：－２３℃
２－エチルヘキシルアクリレート（２ＥＨＡ）のホモポリマー：－７０℃
メタクリル酸メチル（ＭＭＡ）のホモポリマー：１０５℃
２－ヒドロキシエチルアクリレート（ＨＥＡ）のホモポリマー：－１５℃
４－ヒドロキシブチルアクリレート（４ＨＢＡ）のホモポリマー：－４０℃
Ｎ－ビニル－２－ピロリドン（ＮＶＰ）のホモポリマー：８０℃
酢酸ビニル（ＶＡｃ）のホモポリマー：３０℃
アクリル酸（ＡＡ）のホモポリマー：１０６℃
　上記で例示した以外のホモポリマーのガラス転移温度Ｔｇについては、「Ｐｏｌｙｍｅｒ　Ｈａｎｄｂｏｏｋ」（第３版、Ｊｏｈｎ　Ｗｉｌｅｙ　＆　Ｓｏｎｓ，Ｉｎｃ．，１９８９）に記載の数値を用いることができる。上記「Ｐｏｌｙｍｅｒ　Ｈａｎｄｂｏｏｋ」に複数の数値が記載されている場合は、ｃｏｎｖｅｎｔｉｏｎａｌの値を採用する。上記「Ｐｏｌｙｍｅｒ　Ｈａｎｄｂｏｏｋ」に記載のないモノマーについては、モノマー製造企業のカタログ値を採用する。上記「Ｐｏｌｙｍｅｒ　Ｈａｎｄｂｏｏｋ」に記載がなく、モノマー製造企業のカタログ値も提供されていないモノマーのホモポリマーのガラス転移温度Ｔｇとしては、特開２００７－５１２７１号公報に記載の測定方法により得られる値を用いるものとする。
　モノマー成分（Ｍ）は、好ましくは、アルキル（メタ）アクリレート（ａ）と極性基含有モノマー（ｂ）を含む。アルキル（メタ）アクリレート（ａ）は、１種のみであってもよいし、２種以上であってもよい。極性基含有モノマー（ｂ）は、１種のみであってもよいし、２種以上であってもよい。
　なお、アルキル（メタ）アクリレート（ａ）のエステル部分のアルキル基（以下、単に「エステル部分のアルキル基」と称することがある。）には、水酸基を含むアルキル基および水酸基以外の極性基を含むアルキル基は含まない。したがって、アルキル（メタ）アクリレート（ａ）は、極性基含有モノマー（ｂ）と明確に区別される。
　モノマー成分（Ｍ）中のアルキル（メタ）アクリレート（ａ）の含有割合は、本発明の効果をより発現させ得る点で、好ましくは４０重量％～９９．９９９重量％である。
　モノマー成分（Ｍ）が含む極性基含有モノマー（ｂ）が、後述するように、水酸基含有モノマー（ｂ１）を含み水酸基以外の極性基を有するモノマー（ｂ２）を含まない実施形態である場合は、特に、モノマー成分（Ｍ）中のアルキル（メタ）アクリレート（ａ）の含有割合は、本発明の効果をより発現させ得る点で、より好ましくは６０重量％～９９．９９９重量％であり、さらに好ましくは８０重量％～９９．９９重量％であり、さらに好ましくは８５重量％～９９．９重量％であり、特に好ましくは９０重量％～９９．５重量％であり、最も好ましくは９５重量％～９９重量％である。
　モノマー成分（Ｍ）が含む極性基含有モノマー（ｂ）が、後述するように、水酸基含有モノマー（ｂ１）を含まず水酸基以外の極性基を有するモノマー（ｂ２）を含む実施形態である場合は、特に、モノマー成分（Ｍ）中のアルキル（メタ）アクリレート（ａ）の含有割合は、本発明の効果をより発現させ得る点で、より好ましくは４３重量％～９０重量％であり、さらに好ましくは４６重量％～８０重量％であり、特に好ましくは４８重量％～７０重量％であり、最も好ましくは５０重量％～６０重量％である。
　アルキル（メタ）アクリレート（ａ）において、エステル部分のアルキル基は、本発明の効果をより発現させ得る点で、好ましくは、炭素数１～２０のアルキル基であり、より好ましくは、炭素数１～１８のアルキル基であり、さらに好ましくは、炭素数１～１６のアルキル基であり、特に好ましくは、炭素数１～１４のアルキル基であり、最も好ましくは、炭素数１～１２のアルキル基である。
　エステル部分のアルキル基は、本発明の効果をより発現させ得る点で、好ましくは、鎖状アルキル基である。ここで鎖状とは、直鎖状および分岐鎖状を包含する意味である。
　アルキル（メタ）アクリレート（ａ）としては、例えば、メチル（メタ）アクリレート、エチル（メタ）アクリレート、プロピル（メタ）アクリレート、イソプロピル（メタ）アクリレート、ｎ－ブチル（メタ）アクリレート、イソブチル（メタ）アクリレート、ｓ－ブチル（メタ）アクリレート、ペンチル（メタ）アクリレート、イソペンチル（メタ）アクリレート、ヘキシル（メタ）アクリレート、ヘプチル（メタ）アクリレート、２－エチルヘキシル（メタ）アクリレート、オクチル（メタ）アクリレート、イソオクチル（メタ）アクリレート、ノニル（メタ）アクリレート、イソノニル（メタ）アクリレート、デシル（メタ）アクリレート、イソデシル（メタ）アクリレート、ウンデシル（メタ）アクリレート、ラウリル（メタ）アクリレート、トリデシル（メタ）アクリレート、テトラデシル（メタ）アクリレート、ペンタデシル（メタ）アクリレート、ヘキサデシル（メタ）アクリレート、ヘプタデシル（メタ）アクリレート、オクタデシル（メタ）アクリレート、イソステアリル（メタ）アクリレート、ノナデシル（メタ）アクリレート、エイコシル（メタ）アクリレート、シクロペンチル（メタ）アクリレート、シクロヘキシル（メタ）アクリレート、イソボルニル（メタ）アクリレートが挙げられる。
　本発明の効果をより発現させ得る点で、アルキル（メタ）アクリレート（ａ）は、その単独重合体（ホモポリマー）のガラス転移温度Ｔｇが－８０℃～－６０℃の範囲内にあるアルキル（メタ）アクリレート（ａ１）を含むことが好ましい。このようなアルキル（メタ）アクリレート（ａ１）としては、例えば、２－エチルヘキシルアクリレート（２ＥＨＡ）（その単独重合体（ホモポリマー）のガラス転移温度Ｔｇ＝－７０℃）が挙げられる。
　アルキル（メタ）アクリレート（ａ１）の単独重合体（ホモポリマー）のガラス転移温度Ｔｇとして、例えば、具体的には以下の値を用い得る。
ｎ－ブチルアクリレート（ＢＡ）のホモポリマー：－５５℃
ラウリルアクリレート（ＬＡ）のホモポリマー：－２３℃
２－エチルヘキシルアクリレート（２ＥＨＡ）のホモポリマー：－７０℃
　上記で例示した以外のホモポリマーのガラス転移温度Ｔｇについては、「Ｐｏｌｙｍｅｒ　Ｈａｎｄｂｏｏｋ」（第３版、Ｊｏｈｎ　Ｗｉｌｅｙ　＆　Ｓｏｎｓ，Ｉｎｃ．，１９８９）に記載の数値を用いることができる。上記「Ｐｏｌｙｍｅｒ　Ｈａｎｄｂｏｏｋ」に複数の数値が記載されている場合は、ｃｏｎｖｅｎｔｉｏｎａｌの値を採用する。上記「Ｐｏｌｙｍｅｒ　Ｈａｎｄｂｏｏｋ」に記載のないモノマーについては、モノマー製造企業のカタログ値を採用する。上記「Ｐｏｌｙｍｅｒ　Ｈａｎｄｂｏｏｋ」に記載がなく、モノマー製造企業のカタログ値も提供されていないモノマーのホモポリマーのガラス転移温度Ｔｇとしては、特開２００７－５１２７１号公報に記載の測定方法により得られる値を用いるものとする。
　アルキル（メタ）アクリレート（ａ）全量中のアルキル（メタ）アクリレート（ａ１）の含有割合は、本発明の効果をより発現させ得る点で、好ましくは５０重量％～１００重量％であり、より好ましくは７０重量％～１００重量％であり、さらに好ましくは８０重量％～１００重量％であり、特に好ましくは９０重量％～１００重量％であり、最も好ましくは９５重量％～１００重量％である。
　その単独重合体（ホモポリマー）のガラス転移温度Ｔｇが－８０℃～－６０℃の範囲内にあるアルキル（メタ）アクリレート（ａ１）は、本発明の効果を発現させ得る側面においてアクリル系ポリマーの粘着特性等に影響を及ぼし得る。アルキル（メタ）アクリレート（ａ）が、その単独重合体（ホモポリマー）のガラス転移温度Ｔｇが－８０℃～－６０℃の範囲内にあるアルキル（メタ）アクリレート（ａ１）を、好ましくは上記の含有割合で含むことにより、本発明の効果がより発現し得る。
　アルキル（メタ）アクリレート（ａ）は、アルキル（メタ）アクリレート（ａ１）以外のアルキル（メタ）アクリレートを含んでいてもよい。アルキル（メタ）アクリレート（ａ）全量中のアルキル（メタ）アクリレート（ａ１）以外のアルキル（メタ）アクリレートの含有割合は、本発明の効果をより発現させ得る点で、好ましくは０重量％～５０重量％であり、より好ましくは０重量％～３０重量％であり、さらに好ましくは０重量％～２０重量％であり、特に好ましくは０重量％～１０重量％であり、最も好ましくは０重量％～５重量％である。
　モノマー成分（Ｍ）中の極性基含有モノマー（ｂ）の含有割合は、本発明の効果をより発現させ得る点で、好ましくは１重量％～６０重量％であり、より好ましくは５重量％～６０重量％であり、さらに好ましくは１０重量％～６０重量％であり、特に好ましくは１５重量％～６０重量％であり、最も好ましくは２０重量％～６０重量％である。
　極性基含有モノマー（ｂ）としては、極性基を有するモノマーであれば、本発明の効果を損なわない範囲で、任意の適切なモノマーを採用し得る。このような極性基含有モノマー（ｂ）としては、水酸基含有モノマー（ｂ１）を含む実施形態（Ｉ）、水酸基含有モノマー（ｂ１）を含まない実施形態（ＩＩ）が挙げられる。なお、ここにいう「水酸基」には、カルボキシル基（－ＣＯＯＨ）が有する－ＯＨ基は含まない。
　極性基含有モノマー（ｂ）としては、アクリル系ポリマーのガラス転移温度Ｔｇを前述した好ましい範囲に調整できる範囲で、上記の実施形態の中から適宜選択すればよい。
　水酸基含有モノマー（ｂ１）は、１種のみであってもよいし、２種以上であってもよい。水酸基以外の極性基を有するモノマー（ｂ２）は、１種のみであってもよいし、２種以上であってもよい。
　水酸基含有モノマー（ｂ１）としては、例えば、２－ヒドロキシエチル（メタ）アクリレート、２－ヒドロキシプロピル（メタ）アクリレート、３－ヒドロキシプロピル（メタ）アクリレート、２－ヒドロキシブチル（メタ）アクリレート、４－ヒドロキシブチル（メタ）アクリレート等のヒドロキシアルキル（メタ）アクリレート；ポリプロピレングリコールモノ（メタ）アクリレート；Ｎ－ヒドロキシエチル（メタ）アクリルアミド；が挙げられる。
　本発明の効果をより発現させ得る点で、水酸基含有モノマー（ｂ１）は、その単独重合体（ホモポリマー）のガラス転移温度Ｔｇが、好ましくは－６０℃～－１０℃であり、より好ましくは－５５℃～－１０℃であり、さらに好ましくは－４５℃～－１０℃であり、特に好ましくは－３５℃～－１０℃であり、最も好ましくは－２５℃～－１０℃である。水酸基含有モノマー（ｂ１）の単独重合体（ホモポリマー）のガラス転移温度Ｔｇは、アクリル系ポリマーの粘着特性等に影響を及ぼし得る。モノマー成分（Ｍ）中に含み得る水酸基含有モノマー（ｂ１）として、その単独重合体（ホモポリマー）のガラス転移温度Ｔｇが上記範囲内にある水酸基含有モノマーを採用することにより、本発明の効果をより発現させ得る。
　水酸基含有モノマー（ｂ１）の単独重合体（ホモポリマー）のガラス転移温度Ｔｇについては、アルキル（メタ）アクリレート（ａ１）の単独重合体（ホモポリマー）のガラス転移温度Ｔｇについての説明を援用し得る。
　本発明の効果をより一層発現させ得る点で、水酸基含有モノマー（ｂ１）としては、好ましくは、２－ヒドロキシエチル（メタ）アクリレート、２－ヒドロキシプロピル（メタ）アクリレート、３－ヒドロキシプロピル（メタ）アクリレート、２－ヒドロキシブチル（メタ）アクリレート、４－ヒドロキシブチル（メタ）アクリレート等のヒドロキシアルキル（メタ）アクリレートが挙げられ、より好ましくは、ヒドロキシアルキル基のアルキル基部分が炭素数２～４の直鎖状アルキル基であるヒドロキシアルキル（メタ）アクリレートが挙げられ、さらに好ましくは、２－ヒドロキシエチルアクリレート（ＨＥＡ）（その単独重合体（ホモポリマー）のガラス転移温度Ｔｇ＝－１５℃）、４－ヒドロキシブチルアクリレート（４ＨＢＡ）（その単独重合体（ホモポリマー）のガラス転移温度Ｔｇ＝－４０℃）が挙げられ、特に好ましくは、２－ヒドロキシエチルアクリレート（ＨＥＡ）（その単独重合体（ホモポリマー）のガラス転移温度Ｔｇ＝－１５℃）である。
　極性基含有モノマー（ｂ）が、水酸基含有モノマー（ｂ１）を必須に含む実施形態（Ｉ）である場合、極性基含有モノマー（ｂ）中の水酸基含有モノマー（ｂ１）の含有割合は、本発明の効果をより発現させ得る点で、好ましくは１重量％～１００重量％であり、より好ましくは１０重量％～１００重量％であり、さらに好ましくは５０重量％～１００重量％であり、さらに好ましくは７０重量％～１００重量％であり、特に好ましくは９０重量％～１００重量％であり、最も好ましくは９５重量％～１００重量％である。
　水酸基含有モノマー（ｂ１）を必須に含む実施形態（Ｉ）においては、極性基含有モノマー（ｂ）は、水酸基以外の極性基を有するモノマー（ｂ２）を含んでいてもよい。この場合、極性基含有モノマー（ｂ）中の水酸基以外の極性基を有するモノマー（ｂ２）の含有割合は、本発明の効果をより発現させ得る点で、好ましくは０重量％～９９重量％であり、より好ましくは０重量％～９０重量％であり、さらに好ましくは０重量％～５０重量％であり、さらに好ましくは０重量％～３０重量％であり、特に好ましくは０重量％～１０重量％であり、最も好ましくは０重量％～５重量％である。
　極性基含有モノマー（ｂ）が、水酸基含有モノマー（ｂ１）を必須に含む実施形態（Ｉ）である場合、モノマー成分（Ｍ）中の水酸基含有モノマー（ｂ１）の含有割合は、本発明の効果をより発現させ得る点で、好ましくは０．００１重量％～４０重量％であり、より好ましくは０．０１重量％～２０重量％であり、さらに好ましくは０．１重量％～１５重量％であり、特に好ましくは０．５重量％～１０重量％であり、最も好ましくは１重量％～５重量％である。
　水酸基以外の極性基を有するモノマー（ｂ２）としては、例えば、カルボキシル基含有モノマー、スルホン酸基含有モノマー、リン酸基含有モノマー、シアノ基含有モノマー、酸無水物基含有モノマー、ビニルエステル類、複素環含有ビニル系モノマー、芳香族ビニル化合物、アミド基含有モノマー、イミド基含有モノマー、アミノ基含有モノマー、エポキシ基含有モノマー、イソシアネート基含有モノマー、芳香族炭化水素基を有する（メタ）アクリル酸エステル、芳香族ビニル化合物、オレフィン類やジエン類、ビニルエーテル類、（メタ）アクリロイルモルホリン、ビニルエーテル類、ハロゲン基含有モノマーが挙げられる。
　カルボキシ基含有モノマーとしては、例えば、アクリル酸（ＡＡ）、メタクリル酸（ＭＡＡ）、カルボキシエチル（メタ）アクリレート、カルボキシペンチル（メタ）アクリレート、イタコン酸、マレイン酸、フマル酸、クロトン酸、イソクロトン酸が挙げられる。
　スルホン酸基含有モノマーとしては、例えば、ビニルスルホン酸ナトリウムが挙げられる。
　リン酸基含有モノマーとしては、例えば、２－ヒドロキシエチルアクリロイルフォスフェートが挙げられる。
　シアノ基含有モノマーとしては、例えば、アクリロニトリル、メタクリロニトリルが挙げられる。
　酸無水物基含有モノマーとしては、例えば、無水マレイン酸、無水イタコン酸が挙げられる。
　ビニルエステル類としては、例えば、酢酸ビニル（ＶＡｃ）、プロピオン酸ビニル、ラウリン酸ビニルが挙げられる。
　複素環含有ビニル系モノマーとしては、例えば、Ｎ－ビニル－２－ピロリドン、（メタ）アクリロイルモルホリン、Ｎ－ビニルピペリドン、Ｎ－ビニルピペラジン、Ｎ－ビニルピロール、Ｎ－ビニルイミダゾール、ビニルピリジン、ビニルピリミジン、ビニルオキサゾールが挙げられる。
　芳香族ビニル化合物としては、例えば、スチレン、ビニルトルエンが挙げられる。
　アミド基含有モノマーとしては、例えば、（メタ）アクリルアミド、Ｎ，Ｎ－ジメチル（メタ）アクリルアミド、Ｎ－メチロール（メタ）アクリルアミド、Ｎ－メトキシメチル（メタ）アクリルアミド、Ｎ－ブトキシメチル（メタ）アクリルアミド、Ｎ－ヒドロキシエチル（メタ）アクリルアミドが挙げられる。
　イミド基含有モノマーとしては、例えば、シクロヘキシルマレイミド、イソプロピルマレイミドが挙げられる。
　アミノ基含有モノマーとしては、例えば、（メタ）アクリル酸アミノエチル、（メタ）アクリル酸ジメチルアミノエチル、（メタ）アクリル酸ｔ－ブチルアミノエチルが挙げられる。
　エポキシ基含有モノマーとしては、例えば、（メタ）アクリル酸グリシジル、（メタ）アクリル酸メチルグリシジルが挙げられる。
　イソシアネート基含有モノマーとしては、例えば、２－メタクリロイルオキシエチルイソシアネートが挙げられる。
　芳香族炭化水素基を有する（メタ）アクリル酸エステルとしては、例えば、フェニル（メタ）アクリレート、フェノキシエチル（メタ）アクリレート、ベンジル（メタ）アクリレートが挙げられる。
　芳香族ビニル化合物としては、例えば、スチレン、ビニルトルエンが挙げられる。
　オレフィン類やジエン類としては、例えば、エチレン、ブタジエン、イソプレン、イソブチレンが挙げられる。
　ビニルエーテル類としては、例えば、ビニルアルキルエーテルが挙げられる。
　ハロゲン基含有モノマーとしては、例えば、塩化ビニルが挙げられる。
　本発明の効果をより発現させ得る点で、水酸基以外の極性基を有するモノマー（ｂ２）は、その単独重合体（ホモポリマー）のガラス転移温度Ｔｇが、好ましくは０℃～１３０℃であり、より好ましくは１０℃～１２０℃であり、さらに好ましくは２０℃～１１０℃である。
　水酸基以外の極性基を有するモノマー（ｂ２）の単独重合体（ホモポリマー）のガラス転移温度Ｔｇについては、アルキル（メタ）アクリレート（ａ１）の単独重合体（ホモポリマー）のガラス転移温度Ｔｇについての説明を援用し得る。
　水酸基以外の極性基を有するモノマー（ｂ２）の一つの実施形態は、その単独重合体（ホモポリマー）のガラス転移温度Ｔｇが０℃～６０℃の水酸基以外の極性基を有するモノマー（ｂ２－１）とその単独重合体（ホモポリマー）のガラス転移温度Ｔｇが７０℃～１３０℃の水酸基以外の極性基を有するモノマー（ｂ２－２）とを含む。この実施形態においては、水酸基以外の極性基を有するモノマー（ｂ２）中の水酸基以外の極性基を有するモノマー（ｂ２－１）の含有割合は、本発明の効果をより発現させ得る点で、好ましくは５０重量％～９９重量％であり、より好ましくは７０重量％～９９重量％であり、さらに好ましくは８０重量％～９９重量％であり、特に好ましくは９０重量％～９９重量％である。この実施形態においては、水酸基以外の極性基を有するモノマー（ｂ２）中の水酸基以外の極性基を有するモノマー（ｂ２－２）の含有割合は、本発明の効果をより発現させ得る点で、好ましくは１重量％～５０重量％であり、より好ましくは１重量％～３０重量％であり、さらに好ましくは１重量％～２０重量％であり、特に好ましくは１重量％～１０重量％である。この実施形態においては、水酸基以外の極性基を有するモノマー（ｂ２）中の水酸基以外の極性基を有するモノマー（ｂ２－１）と水酸基以外の極性基を有するモノマー（ｂ２－２）との合計の含有割合は、好ましくは６０重量％～１００重量％であり、より好ましくは８０重量％～１００重量％であり、さらに好ましくは９０重量％～１００重量％であり、特に好ましくは９５重量％～１００重量％であり、最も好ましくは９８重量％～１００重量％である。
　その単独重合体（ホモポリマー）のガラス転移温度Ｔｇが０℃～６０℃の水酸基以外の極性基を有するモノマー（ｂ２－１）の該ガラス転移温度Ｔｇは、好ましくは１０℃～５０℃であり、より好ましくは２０℃～４０℃である。このような水酸基以外の極性基を有するモノマー（ｂ２－１）としては、例えば、酢酸ビニル（ＶＡｃ）（その単独重合体（ホモポリマー）のガラス転移温度Ｔｇ＝３０℃）が挙げられる。
　その単独重合体（ホモポリマー）のガラス転移温度Ｔｇが７０℃～１３０℃の水酸基以外の極性基を有するモノマー（ｂ２－２）の該ガラス転移温度Ｔｇは、好ましくは８０℃～１２０℃であり、より好ましくは９０℃～１１０℃である。このような水酸基以外の極性基を有するモノマー（ｂ２－２）としては、例えば、アクリル酸（ＡＡ）（その単独重合体（ホモポリマー）のガラス転移温度Ｔｇ＝１０６℃）が挙げられる。
　極性基含有モノマー（ｂ）が、水酸基含有モノマー（ｂ１）を含まない実施形態（ＩＩ）である場合、すなわち、水酸基以外の極性基を有するモノマー（ｂ２）を必須に含む場合、モノマー成分（Ｍ）中の水酸基以外の極性基を有するモノマー（ｂ２）の含有割合は、本発明の効果をより発現させ得る点で、好ましくは１０重量％～５７重量％であり、より好ましくは２０重量％～５４重量％であり、さらに好ましくは３０重量％～５２重量％であり、特に好ましくは４０重量％～５０重量％である。
　一つの実施形態としては、モノマー成分（Ｍ）は、好ましくは、アルキル（メタ）アクリレート（ａ）と極性基含有モノマー（ｂ）を含み、該モノマー成分（Ｍ）中の該アルキル（メタ）アクリレート（ａ）の含有割合が４３重量％～９０重量％であり、該アルキル（メタ）アクリレート（ａ）が、その単独重合体（ホモポリマー）のガラス転移温度Ｔｇが－８０℃～－６０℃の範囲内にあるアルキル（メタ）アクリレート（ａ１）であり、該極性基含有モノマー（ｂ）が水酸基含有モノマー（ｂ１）を含まず、水酸基以外の極性基を有するモノマー（ｂ２）を必須に含み、該水酸基含有モノマー（ｂ２）は、その単独重合体（ホモポリマー）のガラス転移温度Ｔｇが０℃～１３０℃の範囲内にあり、該モノマー成分（Ｍ）中の該極性基含有モノマー（ｂ２）の含有割合が１０重量％～５７重量％である。
　本発明の効果を一層発現させ得る一つの実施形態としては、
（ｉ）モノマー成分（Ｍ）は、好ましくは、アルキル（メタ）アクリレート（ａ）と極性基含有モノマー（ｂ）を含み、
（ｉｉ）モノマー成分（Ｍ）中のアルキル（メタ）アクリレート（ａ）の含有割合が、好ましくは６０重量％～９９．９９９重量％であり、より好ましくは８０重量％～９９．９９重量％であり、さらに好ましくは８５重量％～９９．９重量％であり、特に好ましくは９０重量％～９９．５重量％であり、最も好ましくは９５重量％～９９重量％であり、
（ｉｉｉ）アルキル（メタ）アクリレート（ａ）が、好ましくは、その単独重合体（ホモポリマー）のガラス転移温度Ｔｇが－８０℃～－６０℃の範囲内にあるアルキル（メタ）アクリレート（ａ１）を必須に含み、
（ｉｖ）アルキル（メタ）アクリレート（ａ）全量中のアルキル（メタ）アクリレート（ａ１）の含有割合が、好ましくは５０重量％～１００重量％であり、より好ましくは７０重量％～１００重量％であり、さらに好ましくは８０重量％～１００重量％であり、特に好ましくは９０重量％～１００重量％であり、最も好ましくは９５重量％～１００重量％であり、
（ｖ）モノマー成分（Ｍ）中の極性基含有モノマー（ｂ）の含有割合が、好ましくは０．００１重量％～４０重量％であり、より好ましくは０．０１重量％～２０重量％であり、さらに好ましくは０．１重量％～１５重量％であり、特に好ましくは０．５重量％～１０重量％であり、最も好ましくは１重量％～５重量％であり、
（ｖｉ）極性基含有モノマー（ｂ）が、好ましくは、水酸基含有モノマー（ｂ１）を必須に含み、
（ｖｉｉ）水酸基含有モノマー（ｂ１）は、、好ましくは、その単独重合体（ホモポリマー）のガラス転移温度Ｔｇが－６０℃～－１０℃の範囲内にあり、
（ｖｉｉｉ）極性基含有モノマー（ｂ）中の水酸基含有モノマー（ｂ１）の含有割合が、好ましくは１重量％～１００重量％であり、より好ましくは１０重量％～１００重量％であり、さらに好ましくは５０重量％～１００重量％であり、さらに好ましくは７０重量％～１００重量％であり、特に好ましくは９０重量％～１００重量％であり、最も好ましくは９５重量％～１００重量％であり、
（ｉｘ）モノマー成分（Ｍ）中の極性基含有モノマー（ｂ１）の含有割合が、好ましくは０．００１重量％～４０重量％であり、より好ましくは０．０１重量％～２０重量％であり、さらに好ましくは０．１重量％～１５重量％であり、特に好ましくは０．５重量％～１０重量％であり、最も好ましくは１重量％～５重量％である。
　モノマー成分（Ｍ）は、アルキル（メタ）アクリレート（ａ）と極性基含有モノマー（ｂ）のいずれにも該当しないその他のモノマー（ｃ）を含んでいてもよい。その他のモノマー（ｃ）は、例えば、アクリル系ポリマーのガラス転移温度Ｔｇの調整、粘着性能の調整等の目的で使用することができる。その他のモノマーは、１種のみであってもよいし、２種以上であってもよい。
　モノマー成分（Ｍ）中のその他モノマー（ｃ）の含有割合は、好ましくは２０重量％以下であり、より好ましくは１０重量％以下であり、さらに好ましくは５重量％以下であり、特に好ましくは３重量％以下であり、最も好ましくは１重量％以下である。
　アクリル系ポリマーは、モノマー成分（Ｍ）を重合して得られるものである。アクリル系ポリマーの好ましい実施形態は、重合開始剤を用いた溶液重合で調製したアクリル系ポリマーである。
　重合開始剤は、重合反応の種類に応じて、任意の適切な重合開始剤を採用し得る。重合開始剤は、１種のみであってもよいし、２種以上であってもよい。
　重合開始剤としては、代表的には、熱重合開始剤が挙げられる。
　熱重合開始剤は、好ましくは、アクリル系ポリマーを溶液重合によって得る際に採用され得る。このような熱重合開始剤としては、例えば、２，２’－アゾビスイソブチロニトリル（ＡＩＢＮ）、２，２’－アゾビス－２－メチルブチロニトリル、２，２’－アゾビス（２－メチルプロピオン酸）ジメチル、４，４’－アゾビス－４－シアノバレリアン酸、アゾビスイソバレロニトリル、２，２’－アゾビス（２－アミジノプロパン）ジヒドロクロライド、２，２’－アゾビス［２－（５－メチル－２－イミダゾリン－２－イル）プロパン］ジヒドロクロライド、２，２’－アゾビス（２－メチルプロピオンアミジン）二硫酸塩、２，２’－アゾビス（Ｎ，Ｎ’－ジメチレンイソブチルアミジン）、２，２’－アゾビス［Ｎ－（２－カルボキシエチル）－２－メチルプロピオンアミジン］ハイドレート（ＶＡ－０５７、和光純薬工業（株）製）などのアゾ系開始剤；過硫酸カリウム、過硫酸アンモニウムなどの過硫酸塩、ジ（２－エチルヘキシル）パーオキシジカーボネート、ジ（４－ｔ－ブチルシクロヘキシル）パーオキシジカーボネート、ジ－ｓｅｃ－ブチルパーオキシジカーボネート、ｔ－ブチルパーオキシネオデカノエート、ｔ－ヘキシルパーオキシピバレート、ｔ－ブチルパーオキシピバレート、ジラウロイルパーオキシド、ジ－ｎ－オクタノイルパーオキシド、１，１，３，３－テトラメチルブチルパーオキシ－２－エチルヘキサノエート、ジ（４－メチルベンゾイル）パーオキシド、ジベンゾイルパーオキシド、ｔ－ブチルパーオキシイソブチレート、１，１－ジ（ｔ－ヘキシルパーオキシ）シクロヘキサン、ｔ－ブチルハイドロパーオキシド、過酸化水素などの過酸化物系開始剤；過硫酸塩と亜硫酸水素ナトリウムの組み合わせ、過酸化物とアスコルビン酸ナトリウムの組み合わせなどの過酸化物と還元剤とを組み合わせたレドックス系開始剤；フェニル置換エタン等の置換エタン系開始剤；芳香族カルボニル化合物；が挙げられる。
　熱重合開始剤の使用量は、本発明の効果を損なわない範囲で、任意の適切な使用量に設定され得る。熱重合開始剤の使用量は、本発明の効果をより発現させ得る点で、モノマー成分（Ｍ）１００重量部に対して、好ましくは０．００１重量部～１０重量部であり、より好ましくは０．００５重量部～５重量部であり、さらに好ましくは０．００７重量部～３重量部であり、特に好ましくは０．０１重量部～１重量部である。
　アクリル系ポリマーを溶液重合によって得る際に用いる溶剤としては、本発明の効果を損なわない範囲で、任意の適切な溶剤を採用し得る。
＜１－２－ｂ．架橋剤＞
　アクリル系粘着剤組成物は、架橋剤を含んでいてもよい。架橋剤を用いることにより、アクリル系粘着剤の凝集力を向上でき、本発明の効果をより発現させ得る。架橋剤は、１種のみであってもよいし、２種以上であってもよい。
　架橋剤としては、例えば、イソシアネート系架橋剤、エポキシ系架橋剤、シリコーン系架橋剤、オキサゾリン系架橋剤、アジリジン系架橋剤、シラン系架橋剤、アルキルエーテル化メラミン系架橋剤、金属キレート系架橋剤、過酸化物等の架橋剤が挙げられ、本発明の効果をより発現させ得る点で、好ましくは、イソシアネート系架橋剤、エポキシ系架橋剤、および、過酸化物からなる群から選ばれる少なくとも１種（ｃ成分）である。
　イソシアネート系架橋剤は、イソシアネート基（イソシアネート基をブロック剤または数量体化等により一時的に保護したイソシアネート再生型極性基を含む）を１分子中に２つ以上有する化合物を用いることができる。イソシアネート系架橋剤としては、例えば、トリレンジイソシアネート、キシレンジイソシアネート等の芳香族イソシアネート；イソホロンジイソシアネート等の脂環族イソシアネート；ヘキサメチレンジイソシアネート等の脂肪族イソシアネート；が挙げられる。
　イソシアネート系架橋剤としては、例えば、ブチレンジイソシアネート、ヘキサメチレンジイソシアネート等の低級脂肪族ポリイソシアネート類；シクロペンチレンジイソシアネート、シクロヘキシレンジイソシアネート、イソホロンジイソシアネート等の脂環族イソシアネート類；２，４－トリレンジイソシアネート、４，４’－ジフェニルメタンジイソシアネート、キシリレンジイソシアネート、ポリメチレンポリフェニルイソシアネート等の芳香族ジイソシアネート類；トリメチロールプロパン／トリレンジイソシアネート３量体付加物（例えば、東ソー社製、商品名コロネートＬ）、トリメチロールプロパン／ヘキサメチレンジイソシアネート３量体付加物（例えば、東ソー社製、商品名：コロネートＨＬ）、ヘキサメチレンジイソシアネートのイソシアヌレート体（例えば、東ソー社製、商品名：コロネートＨＸ）等のイソシアネート付加物；キシリレンジイソシアネートのトリメチロールプロパン付加物（例えば、三井化学社製、商品名：タケネートＤ１１０Ｎ）、キシリレンジイソシアネートのトリメチロールプロパン付加物（例えば、三井化学社製、商品名：タケネートＤ１２０Ｎ）、イソホロンジイソシアネートのトリメチロールプロパン付加物（例えば、三井化学社製、商品名：タケネートＤ１４０Ｎ）、ヘキサメチレンジイソシアネートのトリメチロールプロパン付加物（例えば、三井化学社製、商品名：タケネートＤ１６０Ｎ）；ポリエーテルポリイソシアネート、ポリエステルポリイソシアネート、ならびにこれらと各種のポリオールとの付加物；イソシアヌレート結合、ビューレット結合、アロファネート結合等で多官能化したポリイソシアネート；が挙げられる。これらの中でも、変形性と凝集力とをバランスよく両立し得る点で、好ましくは、芳香族イソシアネート、脂環式イソシアネートである。
　エポキシ系架橋剤としては、エポキシ基を１分子中に２つ以上有する多官能エポキシ化合物を用いることができる。エポキシ系架橋剤としては、例えば、Ｎ，Ｎ，Ｎ’，Ｎ’－テトラグリシジル－ｍ－キシレンジアミン、ジグリシジルアニリン、１，３－ビス（Ｎ，Ｎ－ジグリシジルアミノメチル）シクロヘキサン、１，６－ヘキサンジオールジグリシジルエーテル、ネオペンチルグリコールジグリシジルエーテル、エチレングリコールジグリシジルエーテル、プロピレングリコールジグリシジルエーテル、ポリエチレングリコールジグリシジルエーテル、ポリプロピレングリコールジグリシジルエーテル、ソルビトールポリグリシジルエーテル、グリセロールポリグリシジルエーテル、ペンタエリスリトールポリグリシジルエーテル、ポリグリセロールポリグリシジルエーテル、ソルビタンポリグリシジルエーテル、トリメチロールプロパンポリグリシジルエーテル、アジピン酸ジグリシジルエステル、ｏ－フタル酸ジグリシジルエステル、トリグリシジル－トリス（２－ヒドロキシエチル）イソシアヌレート、レゾルシンジグリシジルエーテル、ビスフェノール－Ｓ－ジグリシジルエーテル、分子内にエポキシ基を２つ以上有するエポキシ系樹脂が挙げられる。エポキシ系架橋剤の市販品としては、例えば、三菱ガス化学社製の商品名「テトラッドＣ」、「テトラッドＸ」が挙げられる。
　過酸化物としては、例えば、ジベンゾイルパーオキシド、ジクミルパーオキサイド、ジ－ｔ－ブチルパーオキサイド、ジ－ｔ－ブチルパーオキシ－３，３，５－トリメチルシクロヘキサン、ｔ－ブチルヒドロパーオキサイド、ｔ－ブチルクミルパーオキサイド、２，５－ジメチル－２，５－ジ（ｔ－ブチルパーオキシン）ヘキシン－３、２，５－ジメチル－２，５－ジ（ベンゾイルパーオキシ）ヘキサン、２，５－ジメチル－２，５－モノ（ｔ－ブチルパーオキシ）－ヘキサン、α，α'－ビス（ｔ－ブチルパーオキシ－ｍ－イソプロピル）ベンゼン、ジ（２－エチルヘキシル）パーオキシジカーボネート、ジ（４－ｔ－ブチルシクロヘキシル）パーオキシジカーボネート、ジ－ｓｅｃ－ブチルパーオキシジカーボネート、ｔ－ブチルパーオキシネオデカノエート、ｔ－ヘキシルパーオキシピバレート、ｔ－ブチルパーオキシピバレート、ジラウロイルパーオキシド、ジ－ｎ－オクタノイルパーオキシド、１，１，３，３－テトラメチルブチルパーオキシ－２－エチルヘキサノエート、ジ（４－メチルベンゾイル）パーオキシド、ｔ－ブチルパーオキシイソブチレート、１，１－ジ（ｔ－ヘキシルパーオキシ）シクロヘキサン、１，１－ジ（ｔ－ブチルパーオキシ）シクロヘキサン、ｔ－ブチルパーオキシ－２－エチルへキシルカーボネート、ｔ－アミルパーオキシイソプロピルカーボネート、３，５，５－トリメチルヘキサノイルパーオキサイド、ｔ－ブチルパーオキシ－２－ヘキサノエートレート、ｔ－ブチルパーオキシピバレート、ｔ－へキシルパーオキシピバレートが挙げられる。過酸化物の市販品としては、例えば、日本油脂株式会社製の商品名「ナイパーＢＭＴ」シリーズ、「ナイパーＢＷ」シリーズが挙げられる。
　アクリル系粘着剤組成物中の架橋剤の含有量は、本発明の効果を損なわない範囲で、任意の適切な含有量を採用し得る。このような含有量としては、例えば、本発明の効果をより発現させ得る点で、アクリル系ポリマーの固形分（１００重量部）に対して、好ましくは０．０５重量部～２０重量部であり、より好ましくは０．１重量部～１８重量部であり、さらに好ましくは０．５重量部～１５重量部であり、特に好ましくは０．５重量部～１０重量部である。
＜１－２－ｃ．多官能アルコール＞
　アクリル系粘着剤組成物は、多官能アルコールを含んでいてもよい。多官能アルコールを用いることにより、アクリル系粘着剤に適度なやわらかさを付与し得る。多官能アルコールは、１種のみであってもよいし、２種以上であってもよい。
　多官能アルコールの官能基数としては、本発明の効果がより発現し得る点で、好ましくは２以上であり、より好ましくは３～６であり、さらに好ましくは３～５であり、特に好ましくは３～４であり、最も好ましくは３である。
　多官能アルコールとしては、例えば、ポリエーテルポリオール、ポリエステルポリオールなどが挙げられる。
　ポリエーテルポリオールとしては、例えば、ポリプロピレングリコール（２官能）、ビスフェノールＡにプロピレンオキシドを付加させたジオール（２官能）、グリセリンにプロピレンオキシドを付加させたトリオール（３官能）、トリメチロールプロパンにプロピレンオキシドを付加させたトリオール（３官能）、エチレンジアミンの活性水素にプロピレンオキシドを付加させたテトラオール（４官能）、ソルビトールまたはシュークローズにプロピレンオキシドを付加させたポリオール（多官能）、グリセリンにプロピレンオキシドとエチレンオキシドを付加させたトリオールであってエチレンオキシドで末端がブロックされているトリオール（３官能）、エチレンジアミンの活性水素にプロピレンオキシドとエチレンオキシドを付加させたテトラオールであってエチレンオキシドで末端がブロックされているテトラオール（４官能）、ポリプロピレンポリエチレングリコールであってエチレンオキシドで末端がブロックされているポリプロピレンポリエチレングリコール（２官能）、ビスフェノールＡにプロピレンオキシドとエチレンオキシドを付加させたジオールであってエチレンオキシドで末端がブロックされているジオール（２官能）、トリメチロールプロパンにエチレンオキシドを付加させたトリオール（３官能）、ポリプロピレンポリエチレングリコールであってエチレンオキシドとプロピレンオキシドがランダムに付加したポリプロピレンポリエチレングリコール（２官能）、グリセリンにプロピレンオキシドとエチレンオキシドを付加させたトリオールであってエチレンオキシドとプロピレンオキシドがランダムに付加したトリオール（３官能）、難燃ポリオール（２官能）などが挙げられる。
　ポリエーテルポリオールの市販品としては、例えば、株式会社ＡＤＥＫＡのアデカポリオール（例えば、Ｐシリーズ、ＢＰＸシリーズ、Ｇシリーズ、Ｔシリーズ、ＥＤＰシリーズ、ＳＰシリーズ、ＳＣシリーズ、Ｒシリーズ、ＲＤシリーズ、ＡＭシリーズ、ＢＭシリーズ、ＣＭシリーズ、ＥＭシリーズ、ＧＭシリーズ、ＰＲシリーズ、ＧＲシリーズ、難燃ポリオールなど）、三洋化成工業株式会社のポリオール（例えば、サンニックスＧＰシリーズ、サンニックスＰＰシリーズ、サンニックスＴＰ－４００シリーズ、サンニックスＳＰ－７５０シリーズ、サンニックスＰＬ－２１００・ＰＰシリーズ、サンエスターシリーズ、プライムポールシリーズ、ニューポールシリーズ、メルポールシリーズ、ＰＥＧシリーズ、マクロゴールシリーズなど）などが挙げられる。
　ポリエーテルポリオールとしては、本発明の効果がより発現し得る点で、好ましくは、グリセリンにプロピレンオキシドを付加させたトリオール（３官能）、トリメチロールプロパンにプロピレンオキシドを付加させたトリオール（３官能）、グリセリンにプロピレンオキシドとエチレンオキシドを付加させたトリオールであってエチレンオキシドで末端がブロックされているトリオール（３官能）、トリメチロールプロパンにエチレンオキシドを付加させたトリオール（３官能）、グリセリンにプロピレンオキシドとエチレンオキシドを付加させたトリオールであってエチレンオキシドとプロピレンオキシドがランダムに付加したトリオール（３官能）であり、より好ましくは、グリセリンにプロピレンオキシドを付加させたトリオール（３官能）、グリセリンにプロピレンオキシドとエチレンオキシドを付加させたトリオールであってエチレンオキシドで末端がブロックされているトリオール（３官能）、グリセリンにプロピレンオキシドとエチレンオキシドを付加させたトリオールであってエチレンオキシドとプロピレンオキシドがランダムに付加したトリオール（３官能）であり、さらに好ましくは、グリセリンにプロピレンオキシドを付加させたトリオール（３官能）である。
　ポリエステルポリオールとしては、例えば、酸成分とグリコール成分とを反応させて得られるポリエステルポリオールが挙げられる。酸成分としては、例えば、テレフタル酸、アジピン酸、アゼライン酸、セバチン酸、無水フタル酸、イソフタル酸、トリメリット酸などが挙げられる。グリコール成分としては、例えば、エチレングリコール、プロピレングリコール、ジエチレングリコール、ブチレングリコール、１，６－ヘキサングリコール、３－メチル－１，５－ペンタンジオール、３，３’－ジメチロールヘプタン、ポリオキシエチレングリコール、ポリオキシプロピレングリコール、１，４－ブタンジオール、ネオペンチルグリコール、ブチルエチルペンタンジオール、ポリオール成分としてグリセリン、トリメチロールプロパン、ペンタエリスリトールなどが挙げられる。ポリエステルポリオール（ａ１）としては、その他に、ポリカプロラクトン、ポリ（β－メチル－γ－バレロラクトン）、ポリバレロラクトン等のラクトン類を開環重合して得られるポリエステルポリオールなども挙げられる。
　ポリエステルポリオールの市販品としては、例えば、株式会社ＡＤＥＫＡのアデカニューエース（例えば、Ｆ１８－６２、Ｆ７－６７、Ｙ９－１０、Ｙ４－５、Ｙ５２－１３、Ｙ５２－２１、Ｖ１４－９０、ＹＧ－１０８、Ｆ１２１２－２９、＃５０、Ｙ６５－５５、ＹＴ－１０１、ＹＴ－６５１、ＮＳ－２４００など）などが挙げられる。
　多官能アルコールの数平均分子量は、本発明の効果がより発現し得る点で、好ましくは５０～１００００であり、より好ましくは６０～５０００である。
　アクリル系粘着剤組成物中の多官能アルコールの含有量は、本発明の効果を損なわない範囲で、任意の適切な含有量を採用し得る。このような含有量としては、例えば、本発明の効果をより発現させ得る点で、アクリル系ポリマーの固形分（１００重量部）に対して、好ましくは０．０００１重量部～２０重量部であり、より好ましくは０．００１重量部～１５重量部であり、さらに好ましくは０．０１重量部～１０重量部であり、特に好ましくは０．１重量部～５重量部である。
＜１－２－ｄ．他の成分＞
　アクリル系粘着剤組成物は、本発明の効果を損なわない範囲で、任意の適切な他の成分を含有し得る。このような他の成分としては、例えば、アクリル系ポリマー以外のポリマー成分、架橋促進剤、架橋触媒、シランカップリング剤、粘着付与樹脂（ロジン誘導体、ポリテルペン樹脂、石油樹脂、油溶性フェノールなど）、老化防止剤、無機充填剤、有機充填剤、金属粉、着色剤（顔料や染料など）、箔状物、紫外線吸収剤、酸化防止剤、光安定剤、造核剤、連鎖移動剤、可塑剤、軟化剤、界面活性剤、帯電防止剤、導電剤、安定剤、表面潤滑剤、レベリング剤、腐食防止剤、耐熱安定剤、重合禁止剤、滑剤、溶剤、触媒などが挙げられる。
≪≪２．被着体≫≫
　被着体は、表面保護フィルムが積層される側の表面の水接触角および算術平均表面粗さＲａが前述の好ましい範囲にある被着体であれば、本発明の効果を損なわない範囲で、任意の適切な被着体を採用し得る。
　被着体の表面保護フィルム側（表面保護フィルムが積層されている側）の表面の水接触角は、前述したように、好ましくは８５°以上であり、より好ましくは８５°～１１０°であり、さらに好ましくは８５°～１０５°であり、特に好ましくは９０°～１００°であり、最も好ましくは９１°～１００°である。上記水接触角が上記範囲内にあれば、本発明の効果がより発現し得る。上記水接触角が上記範囲を外れて小さすぎると、表面保護フィルムが被着体に過度に密着しやすくなり、例えば、被着体からの表面保護フィルムの初期剥離力が高くなって、被着体から表面保護フィルムを剥離できなくなるおそれがあり、被着体からの表面保護フィルムの剥離力が経時で大きく上昇しすぎて、被着体から表面保護フィルムを剥離できなくなるおそれがある。上記水接触角が上記範囲を外れて大きすぎると、表面保護フィルムが被着体に過度に密着しにくくなり、例えば、被着体からの表面保護フィルムの初期剥離力が低すぎることとなり、被着体からの表面保護フィルムの浮きが生じるおそれや、表面保護フィルムに最表面に設けられ得るはく離ライナーをはく離する際のはく離不良が生じるおそれがある。
　被着体の表面保護フィルム側（表面保護フィルムが積層されている側）の表面の算術平均表面粗さＲａは、前述したように、好ましくは０．６μｍ以下であり、より好ましくは０．３５μｍ以下であり、さらに好ましくは０．２μ以下であり、特に好ましくは０．１μｍ以下であり、最も好ましくは０．０８μｍ以下である。上記算術平均表面粗さＲａの下限値は小さければ小さいほどよく、好ましくは０μｍ以上である。上記算術平均表面粗さＲａが上記範囲内にあれば、本発明の効果がより発現し得る。上記算術平均表面粗さＲａが上記範囲を外れて大きすぎると、例えば、表面保護フィルムが有する粘着剤層の厚みが大きい場合、被着体からの表面保護フィルムの剥離力が経時で大きく上昇しすぎて、被着体から表面保護フィルムを剥離できなくなるおそれがある。
　被着体は、代表的には、光学部材である。光学部材としては、本発明の効果を損なわない範囲で、任意の適切な光学部材を採用し得る。このような光学部材としては、例えば、任意の適切な基材上に任意の適切な層を有する部材が挙げられる。具体的な光学部材としては、例えば、偏光板、位相差板、ディスプレイ、撮像装置、レンズ、（ハーフ）ミラーなどが挙げられる。
　なお、被着体としては、表面保護フィルムを積層する側の表面の水接触角と表面保護フィルムを積層する側の表面の算術平均表面粗さＲａが前述した好ましい範囲に入るような被着体を選択すればよく、その表面の材料については任意の適切な材料を採用し得る。しかしながら、本発明の効果をより発現させ得る点で、このような材料としては、代表的には、樹脂が挙げられ、被着体としては、好ましくは、任意の適切な樹脂層を有する部材が挙げられる。
　被着体の厚みは、その種類によって、任意の適切な厚みを採用し得る。代表的には、被着体の厚みは、好ましくは５μｍ～９５０μｍであり、より好ましくは２０μｍ～７５０μｍであり、さらに好ましくは３０μｍ～５５０μｍであり、特に好ましくは４０μｍ～４５０μｍである。
　以下、実施例により本発明を具体的に説明するが、本発明はこれら実施例になんら限定されるものではない。なお、実施例等における、試験および評価方法は以下のとおりである。なお、「部」と記載されている場合は、特記事項がない限り「重量部」を意味し、「％」と記載されている場合は、特記事項がない限り「重量％」を意味する。
＜水接触角の測定＞
　被着体の表面保護フィルム側（表面保護フィルムが積層されている側）の表面に水２μLを滴下し、滴下０．５秒後の水接触角［°］を求めた。水接触角の測定は、市販の接触角測定装置を用いて、ＪＩＳ　Ｒ　３２５７：１９９９に準拠して測定した（液滴法）。具体的には、下記の条件で測定した。測定は５回行い、その平均値を採用した（ｎ＝５）。
［水接触角測定条件］
測定装置：接触角測定器　ＤｒｏｐＭａｓｔｅｒ　ＤＭ７００（協和界面科学社製）
測定雰囲気：２３℃、５０％ＲＨ
測定液体：蒸留水
測定時間：着滴５００ｍｓ後
＜算術平均表面粗さＲａの測定＞
　被着体の表面保護フィルム側（表面保護フィルムが積層されている側）の表面の、算術平均表面粗さＲａを測定した。具体的には、下記の条件で測定した。
［算術平均表面粗さＲａの測定条件］
測定装置：高精度微細形状測定機　ＳＵＲＦＣＯＲＤＥＲ　ＥＴ４０００Ａ（小坂研究所社製）
検出部の触針：先端曲率半径０．５μｍ、頂角６０度、材質ダイヤモンド
基準長さ（粗さ曲線のカットオフ値λｃ）：０．８ｍｍ
評価長さ（基準長さ）：１２ｍｍ
触針の送り速さ：１ｍｍ／ｓ
縦倍率：２００００倍
横倍率：１０倍
＜変形の評価＞
　図２に示すように、上面に、縦２５ｍｍ、横２５ｍｍ、深さ１ｍｍのサイズの凹部が形成された試験板２０００の上面に、実施例、比較例で得られた積層体（表面保護フィルム付被着体）を縦６０ｍｍ、横６０ｍｍに切り取った試験片）１０００を載置した。この状態で、半径Ｒ＝８ｍｍの棒３０００を、積層体１０００の上面（表面保護フィルム側）から試験板２０００の凹部中央部の底面に向かって１ｍｍ押し込み、この状態を１．０秒間保持してから棒を積層体１０００から離したとき、積層体１０００に押し跡が残るか否かを確認した。
（評価）
なし（〇）：押し跡が残らない。
あり（×）：押し跡が残る。
＜初期剥離力（Ａ）＞
　実施例、比較例で得られた積層体（表面保護フィルム付被着体）について、製造後、温度２３℃、相対湿度５０％の環境に３０分間静置した後、同環境下で、剥離角度１８０°、引張速度３００ｍｍ／分でピール試験を行って１８０°剥離力を測定し、これを初期剥離力とした。
　なお、本発明の実施形態の積層体においては、本発明の効果をより発現し得る点で、この初期剥離力（Ａ）は、好ましくは０．０２５Ｎ／２５ｍｍ以上０．１００Ｎ／２５ｍｍ未満であり、より好ましくは０．０３０Ｎ／２５ｍｍ以上０．０９０Ｎ／２５ｍｍ未満であり、さらに好ましくは０．０３５Ｎ／２５ｍｍ以上０．０８５Ｎ／２５ｍｍ未満であり、さらに好ましくは０．０４０Ｎ／２５ｍｍ以上０．０８５Ｎ／２５ｍｍ未満であり、さらに好ましくは０．０４０Ｎ／２５ｍｍ以上０．０８０Ｎ／２５ｍｍ未満であり、特に好ましくは０．０４０Ｎ／２５ｍｍ以上０．０７５Ｎ／２５ｍｍ未満であり、最も好ましくは０．０４０Ｎ／２５ｍｍ以上０．０７０Ｎ／２５ｍｍ未満である。
　評価基準は下記の通りとした。
（評価基準）
◎：０．０４０Ｎ／２５ｍｍ以上０．０８５Ｎ／２５ｍｍ未満
〇：０．０３０Ｎ／２５ｍｍ以上０．０４０Ｎ／２５ｍｍ未満または０．０８５Ｎ／２５ｍｍ以上０．０９０Ｎ／２５ｍｍ未満
△：０．０２５Ｎ／２５ｍｍ以上０．０３０Ｎ／２５ｍｍ未満または０．０９０Ｎ／２５ｍｍ以上０．１００Ｎ／２５ｍｍ未満
×：０．０２５Ｎ／２５ｍｍ未満または０．１００Ｎ／２５ｍｍ以上
＜６０℃×７２時間保管後の剥離力（Ｂ）＞
　実施例、比較例で得られた積層体（表面保護フィルム付被着体）について、製造後、温度６０℃の環境に７２時間保管し、その後、温度２３℃、相対湿度５０％の環境に３０分間静置した後、同環境下で、剥離角度１８０°、引張速度３００ｍｍ／分でピール試験を行って１８０°剥離力を測定し、これを６０℃×７２時間保管後の剥離力とした。
　なお、本発明の実施形態の積層体においては、本発明の効果をより発現し得る点で、この６０℃×７２時間保管後の剥離力（Ｂ）は、好ましくは０．０３０Ｎ／２５ｍｍ以上０．１１５Ｎ／２５ｍｍ未満であり、より好ましくは０．０４０Ｎ／２５ｍｍ以上０．１０５Ｎ／２５ｍｍ未満であり、さらに好ましくは０．０４０Ｎ／２５ｍｍ以上０．１００Ｎ／２５ｍｍ未満であり、さらに好ましくは０．０４５Ｎ／２５ｍｍ以上０．０９５Ｎ／２５ｍｍ未満であり、さらに好ましくは０．０５０Ｎ／２５ｍｍ以上０．０９５Ｎ／２５ｍｍ未満であり、特に好ましくは０．０５５Ｎ／２５ｍｍ以上０．０９５Ｎ／２５ｍｍ未満であり、最も好ましくは０．０５５Ｎ／２５ｍｍ以上０．０９２Ｎ／２５ｍｍ未満である。
　評価基準は下記の通りとした。
（評価基準）
◎：０．０５５Ｎ／２５ｍｍ以上０．０９５Ｎ／２５ｍｍ未満
〇：０．０４０Ｎ／２５ｍｍ以上０．０５５Ｎ／２５ｍｍ未満または０．０９５Ｎ／２５ｍｍ以上０．１００Ｎ／２５ｍｍ未満
△：０．０３０Ｎ／２５ｍｍ以上０．０４０Ｎ／２５ｍｍ未満または０．１００Ｎ／２５ｍｍ以上０．１１５Ｎ／２５ｍｍ未満
×：０．０３０Ｎ／２５ｍｍ未満または０．１１５Ｎ／２５ｍｍ以上
＜剥離力変化（Ｂ）－（Ａ）＞
　本発明の実施形態の積層体においては、本発明の効果をより発現し得る点で、この剥離力変化（Ｂ）－（Ａ）は、小さければ小さいほど好ましく、好ましくは０．０４５Ｎ／２５ｍｍ未満であり、より好ましくは０．０４２Ｎ／２５ｍｍ未満であり、さらに好ましくは０．０４０Ｎ／２５ｍｍ未満であり、さらに好ましくは０．０３７Ｎ／２５ｍｍ未満であり、さらに好ましくは０．０３５Ｎ／２５ｍｍ未満であり、特に好ましくは０．０３２Ｎ／２５ｍｍ未満であり、最も好ましくは０．０３０Ｎ／２５ｍｍ未満である。
　評価基準は下記の通りとした。
（評価基準）
◎：０．０３５Ｎ／２５ｍｍ未満
〇：０．０３５Ｎ／２５ｍｍ以上０．０４２Ｎ／２５ｍｍ未満
△：０．０４２Ｎ／２５ｍｍ以上０．０４５Ｎ／２５ｍｍ未満
×：０．０４５Ｎ／２５ｍｍ以上
＜粘着剤層のクリープリカバリー値＞
　積層体から粘着剤層のみを取り出し、積層して約１ｍｍの厚みとし、これをφ８ｍｍに打ち抜き、円柱状のペレットを作製して測定用サンプルとした。
　動的粘弾性測定装置（ＴＡ　Ｉｎｓｔｒｕｍｅｎｔｓ社製、ＤＨＲ２）を用い、得られた測定サンプルをφ８ｍｍパラレルプレートの治具に固定した。２５℃において、５ＫＰａの変形応力を加えて３００秒間保持した後の変形歪み（％）をＡ値、さらに変形応力を０にして３００秒間保持した後の変形歪み（％）をＢ値とし、［｛（Ａ値－Ｂ値）／Ａ値｝×１００］で算出される値をクリープリカバリー値とした。
＜せん断弾性係数＞
　実施例、比較例で得られた積層体に用いられている表面保護フィルムを５ｍｍ（ＴＤ）×５０ｍｍ（ＭＤ）に切り出し、アクリル板（三菱ケミカル製、商品名「アクリライトＬ」）を被着体として、該表面保護フィルムの粘着剤層を接地面積５ｍｍ×１０ｍｍとなるようにして貼り合わせた。その後、温度２３℃、相対湿度５０％の環境に３０分間静置した後、同環境下で、精密万能試験機（島津製作所社製、ＡＵＴＯＧＲＡＰＨ　ＡＧ－Ｘ　ｐｌｕｓ）を用いて、せん断方向に、引張速度０．０６ｍｍ／ｍｉｎでせん断応力を測定し、せん断ひずみ（横軸）－せん断応力（縦軸）曲線を得た。
　せん断弾性係数Ｇは、せん断ひずみ０．０５ｍｍから０．２ｍｍまでの傾きとして、下記式より算出した。
　Ｇ＝τ／γ＝（τ0.2－τ0.05）／（０．２－０．０５）
τ：せん断応力［Ｎ／５０ｍｍ2］
γ：せん断ひずみ［ｍｍ］
τ0.2：せん断ひずみ０．２ｍｍにおけるせん断応力［Ｎ／５０ｍｍ2］
τ0.05：せん断ひずみ０．０５ｍｍにおけるせん断応力［Ｎ／５０ｍｍ2］
［製造例１］：アクリル系ポリマー（１）の製造
　温度計、攪拌機、冷却器および窒素ガス導入管を備える反応容器内に、モノマー成分として、２－エチルヘキシルアクリレート（２ＥＨＡ）：９６．２重量部、２－ヒドロキシエチルアクリレート（ＨＥＡ）：３．８重量部、ならびに、重合開始剤として２，２’－アゾビスイソブチロニトリル（ＡＩＢＮ）：０．２重量部を、酢酸エチル：１５０重量部とともに仕込み、２３℃で緩やかに攪拌しながら窒素ガスを導入して窒素置換を行った。その後、液温を６５℃付近に保って６時間重合反応を行い、アクリル系ポリマー（１）の溶液（濃度４０重量％）を製造した。アクリル系ポリマー（１）の重量平均分子量は５４万であった。
　また、アクリル系ポリマー（１）のＴｇは、ＦＯＸの式により算出すると、（－７０℃×０．９６２）＋（－１５℃×０．０３８）＝（－６７．３４℃）＋（－０．５７℃）＝－６７．９１℃であった。
［製造例２］：アクリル系ポリマー（２）の製造
　温度計、攪拌機、冷却器および窒素ガス導入管を備える反応容器内に、モノマー成分として、２－エチルヘキシルアクリレート（２ＥＨＡ）：１００．０重量部、酢酸ビニル（ＶＡｃ）：８０重量部、アクリル酸（ＡＡ）：５．０重量部、ならびに、重合開始剤としてベンゾイルパーオキサイド（ＢＰＯ、日油（株）製「ナイパー（登録商標）ＢＷ」）：０．３重量部を、トルエン：２６３重量部とともに仕込み、２３℃で緩やかに攪拌しながら窒素ガスを導入して窒素置換を行った。その後、液温を６３℃付近に保って６時間重合反応を行った。その後、容器内容物の温度を８０℃に昇温して３．５時間熟成し、アクリル系ポリマー（２）の溶液（濃度４０重量％）を製造した。アクリル系ポリマー（２）の重量平均分子量は６５万であった。
　また、アクリル系ポリマー（２）のＴｇは、ＦＯＸの式により算出すると、（－７０℃×０．５４１）＋（３０℃×０．４３２）＋（１０６℃×０．０２７）＝（－３７．８７℃）＋（１２．９６℃）＋（２．８６℃）＝－２２．０５℃であった。
［製造例３］：アクリル系ポリマー（３）の製造
　６時間重合反応を行った後、熟成を行わなかった以外は、製造例２と同様に行い、アクリル系ポリマー（３）の溶液（濃度４０重量％）を製造した。アクリル系ポリマー（３）の重量平均分子量は８１万であった。
［製造例４］：アクリル系ポリマー（４）の製造
　熟成時間を３．５時間から２時間に変更した以外は、製造例２と同様に行い、アクリル系ポリマー（４）の溶液（濃度４０重量％）を製造した。アクリル系ポリマー（４）の重量平均分子量は７１万であった。
［製造例５］：アクリル系ポリマー（５）の製造
　熟成時間を３．５時間から７時間に変更した以外は、製造例２と同様に行い、アクリル系ポリマー（５）の溶液（濃度４０重量％）を製造した。アクリル系ポリマー（５）の重量平均分子量は４６万であった。
［製造例６］：アクリル系粘着剤組成物（１）の製造
　製造例１で得られたアクリル系ポリマー（１）の溶液の固形分１００重量部に対して、添加剤としてサンニックスＰＰ－３０００（三洋化成工業社製）を固形分換算で０．５重量部加え、架橋剤としてタケネートＤ－１０１Ｅ（三井化学社製）を固形分換算で３．０重量部を加えて、全体の固形分が２９重量％となるようにトルエンで希釈し、ディスパーで攪拌し、アクリル系粘着剤組成物（１）を製造した。
［製造例７］：アクリル系粘着剤組成物（２）の製造
　製造例２で得られたアクリル系ポリマー（２）の溶液の固形分１００重量部に対して、架橋剤としてＴＥＴＲＡＤ－Ｃ（三菱瓦斯化学社製）を固形分換算で４．０重量部を加えて、全体の固形分が２２重量％となるようにメチルエチルケトンで希釈し、ディスパーで攪拌し、アクリル系粘着剤組成物（２）を製造した。
［製造例８］：アクリル系粘着剤組成物（３）の製造
　製造例３で得られたアクリル系ポリマー（３）の溶液の固形分１００重量部に対して、架橋剤としてＴＥＴＲＡＤ－Ｃ（三菱瓦斯化学社製）を固形分換算で４．０重量部を加えて、全体の固形分が２２重量％となるようにメチルエチルケトンで希釈し、ディスパーで攪拌し、アクリル系粘着剤組成物（３）を製造した。
［製造例９］：アクリル系粘着剤組成物（４）の製造
　製造例４で得られたアクリル系ポリマー（４）の溶液の固形分１００重量部に対して、架橋剤としてＴＥＴＲＡＤ－Ｃ（三菱瓦斯化学社製）を固形分換算で４．０重量部を加えて、全体の固形分が２２重量％となるようにメチルエチルケトンで希釈し、ディスパーで攪拌し、アクリル系粘着剤組成物（４）を製造した。
［製造例１０］：アクリル系粘着剤組成物（５）の製造
　製造例５で得られたアクリル系ポリマー（５）の溶液の固形分１００重量部に対して、架橋剤としてＴＥＴＲＡＤ－Ｃ（三菱瓦斯化学社製）を固形分換算で４．０重量部を加えて、全体の固形分が２２重量％となるようにメチルエチルケトンで希釈し、ディスパーで攪拌し、アクリル系粘着剤組成物（５）を製造した。
［製造例１１］：表面保護フィルム（１）の製造
　二軸延伸ポリエステルフィルム（三菱ケミカル製「Ｔ１００Ｃ３８」、厚み３８μｍ）のコロナ面に、製造例６で得られたアクリル系粘着剤組成物（１）を塗布し、１３０℃で２分間加熱して、厚み２１μｍの粘着剤層を形成した。粘着剤層の表面に、はく離ライナー（片面がシリコーン離型処理された厚み２５μｍのポリエステルフィルム）の離型処理面を貼り合わせ、はく離ライナー付きの表面保護フィルム（１）を製造した。
［製造例１２］：表面保護フィルム（２）の製造
　二軸延伸ポリエステルフィルム（三菱ケミカル製「Ｔ１００Ｃ３８」、厚み３８μｍ）のコロナ面に、製造例７で得られたアクリル系粘着剤組成物（２）を塗布し、１３０℃で２分間加熱して、厚み２１μｍの粘着剤層を形成した。粘着剤層の表面に、はく離ライナー（片面がシリコーン離型処理された厚み２５μｍのポリエステルフィルム）の離型処理面を貼り合わせ、はく離ライナー付きの表面保護フィルム（２）を製造した。
［製造例１３］：表面保護フィルム（３）の製造
　二軸延伸ポリエステルフィルム（三菱ケミカル製「Ｔ１００Ｃ３８」、厚み３８μｍ）のコロナ面に、製造例８で得られたアクリル系粘着剤組成物（３）を塗布し、１３０℃で２分間加熱して、厚み１０μｍの粘着剤層を形成した。粘着剤層の表面に、はく離ライナー（片面がシリコーン離型処理された厚み２５μｍのポリエステルフィルム）の離型処理面を貼り合わせ、はく離ライナー付きの表面保護フィルム（３）を製造した。
［製造例１４］：表面保護フィルム（４）の製造
　二軸延伸ポリエステルフィルム（三菱ケミカル製「Ｔ１００Ｃ３８」、厚み３８μｍ）のコロナ面に、製造例９で得られたアクリル系粘着剤組成物（４）を塗布し、１３０℃で２分間加熱して、厚み１０μｍの粘着剤層を形成した。粘着剤層の表面に、はく離ライナー（片面がシリコーン離型処理された厚み２５μｍのポリエステルフィルム）の離型処理面を貼り合わせ、はく離ライナー付きの表面保護フィルム（４）を製造した。
［製造例１５］：表面保護フィルム（５）の製造
　二軸延伸ポリエステルフィルム（三菱ケミカル製「Ｔ１００Ｃ３８」、厚み３８μｍ）のコロナ面に、製造例１０で得られたアクリル系粘着剤組成物（５）を塗布し、１３０℃で２分間加熱して、厚み１０μｍの粘着剤層を形成した。粘着剤層の表面に、はく離ライナー（片面がシリコーン離型処理された厚み２５μｍのポリエステルフィルム）の離型処理面を貼り合わせ、はく離ライナー付きの表面保護フィルム（５）を製造した。
［製造例１６］：塗工液（１）の製造
　紫外線硬化型ウレタンアクリレート樹脂（新中村化学社製、商品名「ＵＡ５３Ｈ－８０ＭＢ」、固形分８０％）：５０重量部、および、ペンタエリスリトールトリアクリレートを主成分とする多官能アクリレート（大阪有機化学工業社製、商品名「ビスコート＃３００」、固形分１００％）：５０重量部を準備した。これらの樹脂と、これらの樹脂の合計の樹脂固形分１００重量部あたり、粒子としてアクリルとスチレンの共重合粒子（積水化成品工業社製、商品名「テクポリマーＳＳＸ１０５５ＱＸＥ」）を０．５重量部、増粘剤として有機粘土である合成スメクタイト（クニミネ工業社製、商品名「スメクトンＳＡＮ」）を１．５重量部、光重合開始剤（ＢＡＳＦ社製、商品名「ＯＭＮＩＲＡＤ９０７」）を５重量部、レベリング剤（ＤＩＣ社製、商品名「ＧＲＡＮＤＩＣ　ＰＣ４１００」、固形分１０％）を０．１重量部混合した。この混合物を固形分濃度が４０％となるように、トルエン／シクロペンタノン混合溶媒（７０／３０）で希釈して、塗工液（１）を製造した。
［製造例１７］：塗工液（２）の製造
　製造例１６において、レベリング剤（ＤＩＣ社製、商品名「ＧＲＡＮＤＩＣ　ＰＣ４１００」、固形分１０％）を信越化学工業社製の商品名「ＫＹ－１２０３」（固形分２０％）に変更した以外は、製造例１６と同様に行い、塗工液（２）を製造した。
［製造例１８］：塗工液（３）の製造
　製造例１６において、アクリルとスチレンの共重合粒子（積水化成品工業社製、商品名「テクポリマーＳＳＸ１０５５ＱＸＥ」）の使用量を０．５重量部から３．０重量部に変更した以外は、製造例１６と同様に行い、塗工液（３）を製造した。
［製造例１９］：塗工液（４）の製造
　製造例１６において、レベリング剤（ＤＩＣ社製、商品名「ＧＲＡＮＤＩＣ　ＰＣ４１００」、固形分１０％）の使用量を０．１重量部から０．０１重量部に変更した以外は、製造例１６と同様に行い、塗工液（４）を製造した。
［製造例２０］：塗工液（５）の製造
　製造例１６において、レベリング剤（ＤＩＣ社製、商品名「ＧＲＡＮＤＩＣ　ＰＣ４１００」、固形分１０％）の使用量を０．１重量部から０．０５重量部に変更した以外は、製造例１６と同様に行い、塗工液（５）を製造した。
［製造例２１］：塗工液（６）の製造
　製造例１６において、レベリング剤（ＤＩＣ社製、商品名「ＧＲＡＮＤＩＣ　ＰＣ４１００」、固形分１０％）の使用量を０．１重量部から０．１５重量部に変更した以外は、製造例１６と同様に行い、塗工液（６）を製造した。
［製造例２２］：被着体（１）の製造
　基材として、二軸延伸ポリエステルフィルム（三菱ケミカル社製、商品名「Ｔ１００Ｃ＃３８」）を準備した。
　基材のコロナ面に、製造例１６で製造した塗工液（１）を、ワイヤーバーを用いて塗工し、未乾燥の塗膜を形成した。そして、この未乾燥の塗膜が形成された基材を、１００℃で１分間加熱することにより、未乾燥の塗膜を乾燥させた。その後、高圧水銀ランプにて積算光量３００ｍＪ／ｃｍ2の紫外線を照射し、塗膜を硬化処理して、塗膜厚み５μｍの被着体（１）を製造した。
［製造例２３］：被着体（２）の製造
　基材として、二軸延伸ポリエステルフィルム（三菱ケミカル社製、商品名「Ｔ１００Ｃ＃３８」）を準備した。
　基材のコロナ面に、製造例１７で製造した塗工液（２）を、ワイヤーバーを用いて塗工し、未乾燥の塗膜を形成した。そして、この未乾燥の塗膜が形成された基材を、１００℃で１分間加熱することにより、未乾燥の塗膜を乾燥させた。その後、高圧水銀ランプにて積算光量３００ｍＪ／ｃｍ2の紫外線を照射し、塗膜を硬化処理して、塗膜厚み５μｍの被着体（２）を製造した。
［製造例２４］：被着体（３）の製造
　基材として、二軸延伸ポリエステルフィルム（三菱ケミカル社製、商品名「Ｔ１００Ｃ＃３８」）を準備した。
　基材のコロナ面に、製造例１６で製造した塗工液（１）を、ワイヤーバーを用いて塗工し、未乾燥の塗膜を形成した。そして、この未乾燥の塗膜が形成された基材を、１００℃で１分間加熱することにより、未乾燥の塗膜を乾燥させた。その後、高圧水銀ランプにて積算光量３００ｍＪ／ｃｍ2の紫外線を照射し、塗膜を硬化処理して、塗膜厚み３μｍの被着体（３）を製造した。
［製造例２５］：被着体（４）の製造
　基材として、二軸延伸ポリエステルフィルム（三菱ケミカル社製、商品名「Ｔ１００Ｃ＃３８」）を準備した。
　基材のコロナ面に、製造例１８で製造した塗工液（３）を、ワイヤーバーを用いて塗工し、未乾燥の塗膜を形成した。そして、この未乾燥の塗膜が形成された基材を、１００℃で１分間加熱することにより、未乾燥の塗膜を乾燥させた。その後、高圧水銀ランプにて積算光量３００ｍＪ／ｃｍ2の紫外線を照射し、塗膜を硬化処理して、塗膜層厚み３μｍの被着体（４）を製造した。
［製造例２６］：被着体（５）の製造
　基材として、二軸延伸ポリエステルフィルム（三菱ケミカル社製、商品名「Ｔ１００Ｃ＃３８」）を準備した。
　基材のコロナ面に、製造例１９で製造した塗工液（４）を、ワイヤーバーを用いて塗工し、未乾燥の塗膜を形成した。そして、この未乾燥の塗膜が形成された基材を、１００℃で１分間加熱することにより、未乾燥の塗膜を乾燥させた。その後、高圧水銀ランプにて積算光量３００ｍＪ／ｃｍ2の紫外線を照射し、塗膜を硬化処理して、塗膜層厚み５μｍの被着体（５）を製造した。
［製造例２７］：被着体（６）の製造
　基材として、二軸延伸ポリエステルフィルム（三菱ケミカル社製、商品名「Ｔ１００Ｃ＃３８」）を準備した。
　基材のコロナ面に、製造例２０で製造した塗工液（５）を、ワイヤーバーを用いて塗工し、未乾燥の塗膜を形成した。そして、この未乾燥の塗膜が形成された基材を、１００℃で１分間加熱することにより、未乾燥の塗膜を乾燥させた。その後、高圧水銀ランプにて積算光量３００ｍＪ／ｃｍ2の紫外線を照射し、塗膜を硬化処理して、塗膜層厚み５μｍの被着体（６）を得た。
［製造例２８］：被着体（７）の製造
　基材として、二軸延伸ポリエステルフィルム（三菱ケミカル社製、商品名「Ｔ１００Ｃ＃３８」）を準備した。
　基材のコロナ面に、製造例２１で製造した塗工液（６）を、ワイヤーバーを用いて塗工し、未乾燥の塗膜を形成した。そして、この未乾燥の塗膜が形成された基材を、１００℃で１分間加熱することにより、未乾燥の塗膜を乾燥させた。その後、高圧水銀ランプにて積算光量３００ｍＪ／ｃｍ2の紫外線を照射し、塗膜を硬化処理して、塗膜層厚み５μｍの被着体（７）を得た。
［製造例２９］：被着体（８）の製造
　基材として、二軸延伸ポリエステルフィルム（三菱ケミカル社製、商品名「Ｔ１００Ｃ＃３８」）を準備した。
　基材のコロナ面に、製造例１６で製造した塗工液（１）を、ワイヤーバーを用いて塗工し、未乾燥の塗膜を形成した。そして、この未乾燥の塗膜が形成された基材を、１００℃で１分間加熱することにより、未乾燥の塗膜を乾燥させた。その後、高圧水銀ランプにて積算光量３００ｍＪ／ｃｍ2の紫外線を照射し、塗膜を硬化処理して、塗膜層厚み４．５μｍの被着体（８）を製造した。
［実施例１］：積層体（１）の製造
　はく離ライナー付きの表面保護フィルム（１）を幅２５ｍｍ、長さ１００ｍｍのサイズに切り出し、はく離ライナーを剥離後に、幅７０ｍｍ、長さ１００ｍｍのサイズに切り出した被着体（１）に、圧力０．２５ＭＰａ、送り速度０．３ｍ／分でロール圧着し、積層体（１）を得た。
　結果を表１に示した。
［実施例２］：積層体（２）の製造
　はく離ライナー付きの表面保護フィルム（２）を幅２５ｍｍ、長さ１００ｍｍのサイズに切り出し、はく離ライナーを剥離後に、幅７０ｍｍ、長さ１００ｍｍのサイズに切り出した被着体（１）に、圧力０．２５ＭＰａ、送り速度０．３ｍ／分でロール圧着し、積層体（２）を得た。
　結果を表１に示した。
［実施例３］：積層体（３）の製造
　はく離ライナー付きの表面保護フィルム（３）を幅２５ｍｍ、長さ１００ｍｍのサイズに切り出し、はく離ライナーを剥離後に、幅７０ｍｍ、長さ１００ｍｍのサイズに切り出した被着体（１）に、圧力０．２５ＭＰａ、送り速度０．３ｍ／分でロール圧着し、積層体（３）を得た。
　結果を表１に示した。
［実施例４］：積層体（４）の製造
　はく離ライナー付きの表面保護フィルム（４）を幅２５ｍｍ、長さ１００ｍｍのサイズに切り出し、はく離ライナーを剥離後に、幅７０ｍｍ、長さ１００ｍｍのサイズに切り出した被着体（１）に、圧力０．２５ＭＰａ、送り速度０．３ｍ／分でロール圧着し、積層体（４）を得た。
　結果を表１に示した。
［実施例５］：積層体（５）の製造
　はく離ライナー付きの表面保護フィルム（１）を幅２５ｍｍ、長さ１００ｍｍのサイズに切り出し、はく離ライナーを剥離後に、幅７０ｍｍ、長さ１００ｍｍのサイズに切り出した被着体（２）に、圧力０．２５ＭＰａ、送り速度０．３ｍ／分でロール圧着し、積層体（５）を得た。
　結果を表１に示した。
［実施例６］：積層体（６）の製造
　はく離ライナー付きの表面保護フィルム（４）を幅２５ｍｍ、長さ１００ｍｍのサイズに切り出し、はく離ライナーを剥離後に、幅７０ｍｍ、長さ１００ｍｍのサイズに切り出した被着体（２）に、圧力０．２５ＭＰａ、送り速度０．３ｍ／分でロール圧着し、積層体（６）を得た。
　結果を表１に示した。
［実施例７］：積層体（７）の製造
　はく離ライナー付きの表面保護フィルム（１）を幅２５ｍｍ、長さ１００ｍｍのサイズに切り出し、はく離ライナーを剥離後に、幅７０ｍｍ、長さ１００ｍｍのサイズに切り出した被着体（３）に、圧力０．２５ＭＰａ、送り速度０．３ｍ／分でロール圧着し、積層体（７）を得た。
　結果を表１に示した。
［実施例８］：積層体（８）の製造
　はく離ライナー付きの表面保護フィルム（４）を幅２５ｍｍ、長さ１００ｍｍのサイズに切り出し、はく離ライナーを剥離後に、幅７０ｍｍ、長さ１００ｍｍのサイズに切り出した被着体（３）に、圧力０．２５ＭＰａ、送り速度０．３ｍ／分でロール圧着し、積層体（８）を得た。
　結果を表１に示した。
［実施例９］：積層体（９）の製造
　はく離ライナー付きの表面保護フィルム（１）を幅２５ｍｍ、長さ１００ｍｍのサイズに切り出し、はく離ライナーを剥離後に、幅７０ｍｍ、長さ１００ｍｍのサイズに切り出した被着体（６）に、圧力０．２５ＭＰａ、送り速度０．３ｍ／分でロール圧着し、積層体（９）を得た。
　結果を表１に示した。
［実施例１０］：積層体（１０）の製造
　はく離ライナー付きの表面保護フィルム（１）を幅２５ｍｍ、長さ１００ｍｍのサイズに切り出し、はく離ライナーを剥離後に、幅７０ｍｍ、長さ１００ｍｍのサイズに切り出した被着体（７）に、圧力０．２５ＭＰａ、送り速度０．３ｍ／分でロール圧着し、積層体（１０）を得た。
　結果を表１に示した。
［実施例１１］：積層体（１１）の製造
　はく離ライナー付きの表面保護フィルム（１）を幅２５ｍｍ、長さ１００ｍｍのサイズに切り出し、はく離ライナーを剥離後に、幅７０ｍｍ、長さ１００ｍｍのサイズに切り出した被着体（８）に、圧力０．２５ＭＰａ、送り速度０．３ｍ／分でロール圧着し、積層体（１１）を得た。
　結果を表１に示した。
［比較例１］：積層体（Ｃ１）の製造
　はく離ライナー付きの表面保護フィルム（５）を幅２５ｍｍ、長さ１００ｍｍのサイズに切り出し、はく離ライナーを剥離後に、幅７０ｍｍ、長さ１００ｍｍのサイズに切り出した被着体（１）に、圧力０．２５ＭＰａ、送り速度０．３ｍ／分でロール圧着し、積層体（Ｃ１）を得た。
　結果を表１に示した。
［比較例２］：積層体（Ｃ２）の製造
　はく離ライナー付きの表面保護フィルム（１）を幅２５ｍｍ、長さ１００ｍｍのサイズに切り出し、はく離ライナーを剥離後に、幅７０ｍｍ、長さ１００ｍｍのサイズに切り出した被着体（４）に、圧力０．２５ＭＰａ、送り速度０．３ｍ／分でロール圧着し、積層体（Ｃ２）を得た。
　結果を表１に示した。
［比較例３］：積層体（Ｃ３）の製造
　はく離ライナー付きの表面保護フィルム（１）を幅２５ｍｍ、長さ１００ｍｍのサイズに切り出し、はく離ライナーを剥離後に、幅７０ｍｍ、長さ１００ｍｍのサイズに切り出した被着体（５）に、圧力０．２５ＭＰａ、送り速度０．３ｍ／分でロール圧着し、積層体（Ｃ３）を得た。
　結果を表１に示した。
Figure JPOXMLDOC01-appb-T000001
　本発明の積層体は、任意の適切な用途に用い得る。好ましくは、本発明の積層体は、光学部材や電子部材の分野において好ましく用いられる。

Claims (6)

  1. 　表面保護フィルムと被着体を含む積層体であって、
    　該表面保護フィルムは、基材と粘着剤層を有し、
    　該粘着剤層と該被着体が直接積層されてなり、
    　該被着体の該表面保護フィルム側の表面の水接触角が８５°以上であり、
    　該被着体の該表面保護フィルム側の表面の算術平均表面粗さＲａが０．６μｍ以下であり、
    　該粘着剤層のクリープリカバリー値が９６％以上である、
    　積層体。
  2. 　表面保護フィルムと被着体を含む積層体であって、
    　該表面保護フィルムは、基材と粘着剤層を有し、
    　該粘着剤層と該被着体が直接積層されてなり、
    　該被着体の該表面保護フィルム側の表面の水接触角が８５°以上であり、
    　該被着体の該表面保護フィルム側の表面の算術平均表面粗さＲａが０．６μｍ以下であり、
    　該表面保護フィルムのせん断弾性係数Ｇが３９．０Ｎ／５０ｍｍ3以下である、
    　積層体。
  3. 　前記水接触角が８５°～１０５°である、請求項１または２に記載の積層体。
  4. 　前記算術平均表面粗さＲａが０．１μｍ以下である、請求項１または２に記載の積層体。
  5. 　前記クリープリカバリー値が９９％以上である、請求項１に記載の積層体。
  6. 　前記せん断弾性係数Ｇが３０．０Ｎ／５０ｍｍ3以下である、請求項２に記載の積層体。
PCT/JP2023/038599 2022-11-16 2023-10-25 積層体 WO2024106156A1 (ja)