WO2022230782A1 - 流量制御バルブ用シールおよび流量制御バルブ装置 - Google Patents

流量制御バルブ用シールおよび流量制御バルブ装置 Download PDF

Info

Publication number
WO2022230782A1
WO2022230782A1 PCT/JP2022/018624 JP2022018624W WO2022230782A1 WO 2022230782 A1 WO2022230782 A1 WO 2022230782A1 JP 2022018624 W JP2022018624 W JP 2022018624W WO 2022230782 A1 WO2022230782 A1 WO 2022230782A1
Authority
WO
WIPO (PCT)
Prior art keywords
seal
rotor
control valve
flow control
resin
Prior art date
Application number
PCT/JP2022/018624
Other languages
English (en)
French (fr)
Inventor
健 安田
Original Assignee
Ntn株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ntn株式会社 filed Critical Ntn株式会社
Publication of WO2022230782A1 publication Critical patent/WO2022230782A1/ja

Abstract

容易かつ安価に作製できるとともに、低リーク性、低摩擦性に優れる流量制御バルブ用シール、およびそのシールを備える流量制御バルブ装置を提供する。シール６は、導入部５を有するハウジング２と、ハウジング２内に設けられ、球状の外周面４ａとロータ開口部４ｂを有し、ハウジング２に対して回転する樹脂製のロータ４とを備えるバルブ装置１に用いられ、ロータ４の外周面４ａに摺接する環状のシールであって、軸方向の断面形状が略Ｌ字であり、該略Ｌ字をなす二辺部のうち、一方の辺部は筒状部６ａを形成し、他方の辺部は、筒状部６ａのロータ側の端部から内径側に向かって延伸しロータ４の外周面４ａに摺接するシールリップ部６ｂを形成しており、シール６の内径寸法をｄ１、ロータ開口部４ｂの内径寸法をｄ２、シールリップ部６ｂの径方向の長さをＬとしたとき、（ｄ２－ｄ１）／２＜Ｌの関係式を満たす。

Description

流量制御バルブ用シールおよび流量制御バルブ装置
　本発明は、自動車の熱効率を高めることで低燃費化を図るために、エンジンなどを冷却するための冷却水の流量および流路を調整する流量制御バルブ装置に用いられる流量制御バルブ用シール、およびそのシールを備える流量制御バルブ装置に関する。
　従来、自動車には、冷却水を循環させてエンジンなどを冷却するための循環流路が設けられている。循環流路は、例えば、ラジエータに冷却水を循環させる流路や、エアコンのヒータコアに冷却水を循環させる流路など複数の流路を有する。この循環流路内には、冷却水の流量を制御する流量制御バルブ装置が配置され、このバルブ装置によって、各流路の冷却水の流量などが調整される。
　流量制御バルブ装置として、例えば特許文献１には、流入部と流出部とを有するバルブハウジングと、弁流入部と弁流出部とを有し且つモータにて回動する球状弁と、内側に位置する円周状の主リップと該主リップと同心円で且つ外側に位置する円周状の副リップとを有するシール部材とを具備した電動ウォータバルブが開示されている。この電動ウォータバルブにおいて、シール部材の主リップの背面側で且つ水流方向上流に水流方向へ対向する受圧面が形成され、球状弁に対する押圧力が発生するとしている。また、主リップ、副リップ、球状弁に囲まれた空隙溜り部に流入した冷却水が、流入部から球状弁内に流入する水圧に抗して主リップが球状弁を押圧する力を僅かに減少させ、球状弁は僅かな力で回動可能となるとしている。
　特許文献２には、ロータの外面に当接する筒状のシール部材を用いたロータリ式バルブが開示されている。該シール部材の先端当接部は、筒状でかつロータの外周面に沿った湾曲形状にされている。さらに、この先端当接部は、先端側に向かうにつれて内側に狭まり、かつ、折り返されるように湾曲する内側湾曲部、および、先端側に向かうにつれて外側に広がり、かつ、折り返されるように湾曲する外側湾曲部の少なくともいずれかを有している。シール部材の内側湾曲部や外側湾曲部はバネとして機能し、先端当接部がロータの外周面に押し付けられる。
特開２０１６－１８８６９３号公報 特開２０１５－２１８７７５号公報
　近年、自動車の低燃費規制が厳しくなる中で、熱効率を高めることで低燃費化を図るために、エンジンなどを冷却するための冷却水の流量および流路を調整する流量制御バルブ装置の搭載が進められている。この装置に使用される環状シールには、低リーク化のほか、消費電力を低減するための低摩擦化、耐久性向上、低コスト化などが要求されている。上記のような流量制御バルブ装置の環状シールとして、特許文献１では主リップと副リップとを有する環状シールが提案されており、主リップ、副リップ、球状弁に囲まれた空隙溜り部に冷却水が溜まることにより、球状弁を僅かな力で回動可能にしている。また、特許文献２では先端当接部が湾曲した環状シールが提案されており、この湾曲部がバネとして機能し、先端当接部がロータの外周面に押し付けられるとしている。
　特許文献１および特許文献２の環状シールには、低リーク化、低摩擦化の点で、リップまたは先端当接部の寸法について検討の余地があると考えられる。特許文献１では、主リップが短いと、冷却水の圧力が作用する受圧面の面積が狭くなるため、リーク量が増加するおそれがある。一方で、主リップが長いと受圧面の面積が広くなるため、主リップのロータへの押圧力が大きくなり、高摩擦になると考えられ、また、主リップの厚さが大きいとロータへの押圧力が増加し、高摩擦になると考えられる。
　特許文献２では、先端当接部（特に内側当接部）が短いと、冷却水の圧力が作用する受圧面の面積が狭くなるため、リーク量が増加するおそれがある。一方で、先端当接部（特に内側当接部）が長いと、受圧面の面積が広くなるため、ロータへの押圧力が大きくなり、高摩擦になると考えられ、また、先端当接部の厚さが大きいとロータへの押圧力が増加し、高摩擦になると考えられる。
　また、特許文献１および特許文献２の環状シールは構造が複雑であり、樹脂成形が比較的困難である。また、複雑な構造から高コストにもなりやすい。
　本発明はこのような事情に鑑みてなされたものであり、容易かつ安価に作製できるとともに、低リーク性、低摩擦性に優れる流量制御バルブ用シール、およびそのシールを備える流量制御バルブ装置を提供することを目的とする。
　本発明の流量制御バルブ用シール（以下、単に「シール」ともいう。）は、冷却水を受け入れる導入部、及び、冷却水を送り出す吐出部を有するハウジングと、上記ハウジングの内部に設けられ、球状または円筒状の外周面と、該外周面から内周面に連通する開口部とを有し、上記ハウジングに対して回転する樹脂製のロータとを備える流量制御バルブ装置に用いられ、上記ハウジング内にて上記ロータと上記導入部または上記吐出部との間に設けられ、上記ロータの外周面に摺接する環状の樹脂製の流量制御バルブ用シールであって、上記流量制御バルブ用シールの軸方向の断面形状が略Ｌ字であり、該略Ｌ字をなす二辺部のうち、一方の辺部は筒状部を形成し、他方の辺部は、上記筒状部のロータ側の端部から内径側に向かって延伸し上記ロータの外周面に摺接するシールリップ部を形成しており、上記流量制御バルブ用シールの内径寸法をｄ１、上記開口部の内径寸法をｄ２、上記シールリップ部の径方向の長さをＬとしたとき、（ｄ２－ｄ１）／２＜Ｌの関係式を満たすことを特徴とする。
　上記シールリップ部は、上記ロータの外周面に摺接するシール面に凸状の突起を有することを特徴とする。
　上記流量制御バルブ用シールは、筒状の上記導入部または上記吐出部のロータ側の端面に装着されることを特徴とする。
　上記流量制御バルブ用シールは、射出成形可能なフッ素樹脂をベース樹脂とする樹脂組成物の射出成形体であることを特徴とする。
　上記樹脂組成物は、該樹脂組成物全体に対して非繊維状充填材を３体積％～３０体積％含み、残部が上記フッ素樹脂であり、繊維状充填材を含まないことを特徴する。
　本発明の流量制御バルブ装置（以下、単に「バルブ装置」ともいう。）は、冷却水を受け入れる導入部、及び、冷却水を送り出す吐出部を有するハウジングと、上記ハウジングの内部に設けられ、球状または円筒状の外周面と、該外周面から内周面に連通する開口部とを有し、上記ハウジングに対して回転する樹脂製のロータと、上記ハウジング内にて上記ロータと上記導入部または上記吐出部との間に設けられ、上記ロータの外周面に摺接する環状の流量制御バルブ用シールとを備える流量制御バルブ装置であって、上記流量制御バルブ用シールが、フッ素樹脂をベース樹脂とする樹脂組成物の成形体であり、上記ロータが上記流量制御バルブ用シールとはベース樹脂が異なる樹脂組成物からなる成形体であり、上記流量制御バルブ用シールの軸方向の断面形状が略Ｌ字であり、該略Ｌ字をなす二辺部のうち、一方の辺部は筒状部を形成し、他方の辺部は、上記筒状部のロータ側の端部から内径側に向かって延伸し上記ロータの外周面に摺接するシールリップ部を形成しており、上記流量制御バルブ用シールの内径寸法をｄ１、上記開口部の内径寸法をｄ２、上記シールリップ部の径方向の長さをＬとしたとき、（ｄ２－ｄ１）／２＜Ｌの関係式を満たすことを特徴とする。
　本発明の流量制御バルブ用シールは、軸方向の断面形状が略Ｌ字で比較的単純な構造であるので、射出成形などによって容易かつ安価に作製することができる。また、上記シールの略Ｌ字の二辺部は筒状部とシールリップ部をそれぞれ形成しており、シールの内径寸法をｄ１、開口部の内径をｄ２、シールリップ部の径方向の長さをＬとしたとき、（ｄ２－ｄ１）／２＜Ｌの関係式を満たす。この設計により、冷却水の圧力によって生じる荷重が、シールリップ部のロータ側の面に比べて、反ロータ側の面で大きくなる。その結果、シールリップ部がロータに押し付けられることでシール性が向上し、低リーク性に優れる。
　また、シールリップ部は、ロータの外周面に摺接するシール面に凸状の突起を有するので、シールリップ部が摩耗してもロータの外周面との接触面積が増加しにくく、回転トルクの上昇を好適に抑制できる。
　上記流量制御バルブ用シールは射出成形可能なフッ素樹脂をベース樹脂とする樹脂組成物の射出成形体であり、さらに、該樹脂組成物は非繊維状充填材を３体積％～３０体積％含み、残部がフッ素樹脂であり、繊維状充填材を含まないので、シールが接触する相手材が樹脂製のロータであっても、ロータを摩耗損傷させにくく、低摩擦性や低摩耗性に一層優れる。
　本発明の流量制御バルブ装置は、本発明の流量制御バルブ用シールを備えるので、低リーク性に優れる。さらに、流量制御バルブ用シールが、フッ素樹脂組成物からなる成形体であり、相手材であるロータが流量制御バルブ用シールとはベース樹脂の異なる樹脂組成物からなる成形体であるので、シールとロータとは異なる樹脂材同士の摺動になる。そのため、同じ樹脂材同士の摺動において懸念される高摩擦係数による摩耗増大を防止でき、低摩擦性や低摩耗性が得られる。
本発明の流量制御バルブ装置の開弁時における要部断面図である。 本発明の流量制御バルブ用シールの一例を示す断面図である。 冷却水による受圧面を示した図である。 本発明の流量制御バルブ用シールの別の例を示す断面図である。
　本発明の流量制御バルブ用シールを適用したバルブ装置の一例を図１に基づいて説明する。図１に示すように、バルブ装置１は、ハウジング２と、ハウジング２に対して回転可能に支持される回転軸３と、ハウジング２内に収納され、回転軸３と一体に回転するロータ４と、ロータ４の外周面４ａに摺接するシール６とを備える。ハウジング２には、エンジンからの冷却水を受け入れる筒状の導入部５と、ラジエータなどの各装置へ冷却水を送り出す筒状の吐出部（図示省略）が設けられている。導入部５とハウジング２の間にはＯリングなどの固定シールが設けられている。図１は、バルブ装置１の導入部側の要部断面図である。回転軸３はモータ（図示省略）に接続されている。
　シール６は、導入部５のロータ４側の端面に装着されている。より具体的には、シール６は、上記端面の内径側縁に設けられた円周溝５ａに筒状部６ａが固定されて装着されている。この場合、シール６は導入部５によって外径側から支持されている。なお、シール６は、この円周溝５ａに対して圧入されていてもよい。シール６を圧入することで、シール６と導入部５を強固に結合させることができる。
　シール６のシールリップ部６ｂがロータの外周面４ａに接触している。図１において、シール６の内径寸法をｄ１、ロータ４のロータ開口部４ｂの内径寸法をｄ２、シールリップ部６ｂの径方向の長さをＬとしたとき、（ｄ２－ｄ１）／２＜Ｌの関係式を満たしている。この関係式およびシール６の構成の詳細については後述する。
　ロータ４は、内部に中空部を有する球状の回転ロータであり、シール６と摺接する外周面４ａは、凸形球面状に形成されている。ロータ４は内外を貫通するロータ開口部４ｂを有し、シール６は中央部に貫通したシール開口部を有する。図１のバルブ装置１において、ロータ開口部４ｂの中心軸とシール６の中心軸は一致しており、ロータ開口部４ｂの形状はその中心軸に対して左右対称に形成されている。回転軸３が矢印の向きに回転し、それに伴ってロータ４も回転する。その回転によって、ロータ開口部４ｂとシール開口部が連通することで開弁状態となり、ロータ開口部４ｂとシール開口部が非連通になることで閉弁状態となる。図１の開弁状態では、黒矢印の向きに流れる冷却水が、ロータ４内へ供給される。このように、ロータ４を回動操作することで、バルブ装置１の開弁および閉弁が制御でき、それによって冷却水の流量調整や分配調整が行われる。
　ロータ４は樹脂製であり、例えば、熱可塑性樹脂をベース樹脂とした樹脂組成物の射出成形体である。熱可塑性樹脂としては、特に限定されないが、フッ素樹脂以外の熱可塑性樹脂を用いることが好ましく、例えば、ポリフェニレンサルファイド（ＰＰＳ）樹脂、ポリアミド６６（ＰＡ６６）樹脂、半芳香族ＰＡ樹脂、ポリエーテルエーテルケトン（ＰＥＥＫ）樹脂などを用いることができる。半芳香族ＰＡ樹脂としては、吸水率の小さいポリアミド９Ｔ樹脂、ポリアミド１０Ｔ樹脂が好ましい。これら樹脂の中でも、低吸水性で、耐熱性、耐アルカリ性に優れ、安価であるＰＰＳ樹脂がより好ましい。
　また、ロータ４に用いる樹脂組成物には、高強度、高弾性、高寸法精度を得るために、ガラス繊維を配合することが好ましい。ガラス繊維を配合したＰＰＳ樹脂は、高強度、高弾性に優れるため、より好ましい。ガラス繊維を配合する場合、その配合量は、樹脂組成物全体に対して１０質量％～５０質量％であり、好ましくは２０質量％～４０質量％である。ガラス繊維が所定量より多いとシールを摩耗損傷させやすくなり、少ないと充分な強度が得られにくくなる。また、この樹脂組成物には、成形収縮率の異方性をなくし、寸法精度を向上するために、ガラス繊維と、非繊維状充填材を併用してもよい。
　導入部５は樹脂製であり、例えば、熱可塑性樹脂をベース樹脂とした樹脂組成物の円筒状などの射出成形体である。熱可塑性樹脂としては、特に限定されないが、例えば、ＰＰＳ樹脂、ＰＡ６６樹脂、半芳香族ＰＡ樹脂、ＰＥＥＫ樹脂などを用いることができる。半芳香族ＰＡ樹脂としては、吸水率の小さいポリアミド９Ｔ樹脂、ポリアミド１０Ｔ樹脂が好ましい。これら樹脂の中でも、低吸水性で、耐熱性、耐アルカリ性に優れ、安価であるＰＰＳ樹脂がより好ましい。
　また、シール６は、ばねを介してロータ４に押し付けて装着してもよい。バネの付勢力を利用することで、さらに低リーク性を維持しやすくなる。具体的には、導入部５において、シール６が装着されていない側（図下側）の端面をコイルバネで押圧してもよい。もしくは、導入部５より内側に、シール６を装着するための平坦部を有する金属環を設置し、該金属環に装着されたシール６を、コイルバネを介してロータ４に押し付けてもよい。
　なお、図１は、導入部側の構成を示しているが、吐出部側も、基本的な構成は同様である。具体的には、ハウジング２内にロータ４と円筒状の吐出部（図示省略）が設けられており、該吐出部にシール６と同様の形状、材質からなるシールが装着されている。このシールのシールリップ部は、例えば凸状の突起を有し、該突起がロータ４の外周面４ａに接触している。吐出部は、ハウジング２において、導入部５から、ロータ４の回転する周方向に所定間隔離れた位置（例えば図１の導入部５と反対側の位置）に設けられる。
　次に、本発明の流量制御バルブ用シールについて、図２に基づいて説明する。図２は、該シールの軸方向断面図である。図２に示すように、シール６は環状部材であり、断面形状が略Ｌ字である。略Ｌ字をなす二辺部のうち、一方の辺部は筒状部６ａを形成し、他方の辺部は、筒状部６ａの一方側端部から内径側に向かって延伸するシールリップ部６ｂを形成している。シール６において、筒状部６ａは外径側の縁部となっている。シールリップ部６ｂは、ロータ側に配置されロータの外周面に摺接する（図１参照）。
　図２において、シールリップ部６ｂは、シール軸方向に直交した面に対して軸方向内側に傾斜して延伸している。言い換えると、シールリップ部６ｂは、Ｌ字の内角（二辺部がなす角度）が鋭角となるように延伸している。この角度は、例えば５０°～８０°である。シールリップ部６ｂがこのように傾斜して延伸することで、ロータの外周面に沿いやすく密着しやすくなる。シールリップ部６ｂのロータ側の面、つまりシール面は、図２に示すように傾斜平面（断面において直線状）であってもよく、ロータの外周面の曲面に倣った傾斜曲面（断面において円弧状）であってもよい。
　また、シールリップ部６ｂのシール面の先端側には凸状の突起６ｃが設けられている。突起６ｃは、シール全周にわたり連続して形成されている。
　図１において、シール６の内径寸法ｄ１は、シール開口部の寸法であり、具体的には、対向するシールリップ部６ｂの先端部間の距離である。また、シールリップ部６ｂの径方向の長さＬは、筒状部６ａの内周面からシールリップ部６ｂの先端部までのシール径方向における距離である。
　シール６は、流量制御バルブ装置に取り付けられた際、（ｄ２－ｄ１）／２＜Ｌの関係式を満たしている。この関係式を満たすことについて、図３を用いて説明する。図３は、図１に示すシールとロータの摺接部付近の拡大図である。流量制御バルブ装置において冷却水が流れる際には、シールリップ部６ｂに流体圧が作用する。上記関係式を満たす場合、シール６に冷却水による流体圧が作用した際には、シールリップ部６ｂの反ロータ側の受圧面Ｓ１の面積が、ロータ４側の受圧面Ｓ２の面積よりも大きくなる。そのため、シールリップ部６ｂはロータ４に容易に押し付けられるのでシール性を向上させることができる。
　また、（ｄ２－ｄ１）／２の値がＬの値に近づくほど、受圧面Ｓ１の面積と受圧面Ｓ２の面積が同程度になるため、ロータ４側への押圧力は小さくなる。この場合、ロータ４が回転する際の回転トルクは小さくなる一方、シール性はやや低下する。そのため、シール性の観点では、（ｄ２－ｄ１）／２＜Ｌ／２であることがより好ましい。
　シール６の内径寸法ｄ１とロータ開口部の内径寸法ｄ２の大小関係は特に限定されず、ｄ２＞ｄ１（図３参照）であってもよく、ｄ２＜ｄ１であってもよい。例えばｄ２＜ｄ１の場合、ロータ開口部の内周面がシールリップ部６ｂの先端部よりも径方向内側に位置することになり、ロータ４側の受圧面Ｓ２の面積がゼロになる。この場合、シール性には優れるものの、ロータ４が回転する際の回転トルクはｄ２＞ｄ１の場合よりも大きくなる。そのため、回転トルクとシール性の両立の観点から、０＜（ｄ２－ｄ１）／２＜Ｌ／２であることがさらに好ましい。
　図３に示すように、シールリップ部６ｂはシール面に凸状の突起６ｃを有している。突起６ｃを設けることで、シール６がロータ４との摺動により摩耗した際にも接触面積が増加しにくくなる。これにより、ロータ４が回転した際の回転トルクを低減することができる。突起６ｃの形状は限定されるものではないが、突起高さｈは０．１ｍｍ～２ｍｍが好ましく、０．５ｍｍ～２ｍｍがより好ましい。突起高さｈが０．１ｍｍより低いと、突起６ｃの摩耗により早期に接触面積が増加しやすく、ロータ４が回転する際の回転トルクが大きくなりやすい。また、突起６ｃの径方向の幅は、図３に示すように、リップ長さＬを超えないことが好ましい。
　シールリップ部６ｂの厚さは、突起６ｃが形成された部分を除いて０．３ｍｍ～２ｍｍであることが好ましい。０．３ｍｍ未満であると、シール６を射出成形する際にショートショットが発生しやすくなる。２ｍｍを超えるとシールリップ部６ｂの剛性が高くなり、冷却水による流体圧が作用した際に、シールリップ部６ｂがロータ４に押圧されにくくなる。なお、図３に示すように、シールリップ部６ｂにおいて、突起６ｃが形成された部分の厚さは、突起６ｃが形成されていない部分の厚さよりも大きくなっている。また、ロータ４が回転する際にシール６のシールリップ部６ｂがロータ開口部に引っ掛からないようにするため、シール開口部のエッジに面取りまたはＲ部を設けてもよい。
　また、シール６において、筒状部６ａの厚さは、シールリップ部６ｂの厚さ（突起６ｃが形成された部分を除く）よりも大きくなっていてもよい。筒状部６ａの厚さを厚くすることで、導入部または吐出部に装着された場合においてシール６を安定して固定しやすくなる。
　なお、本発明のシールは、上記図１～図３の例に限定されない。図４には本発明のシールの他の例を示す。図４のシール７は断面形状が略Ｌ字であり、略Ｌ字をなす二辺部のうち、一方の辺部は筒状部７ａを形成し、他方の辺部は、筒状部７ａから縮径するように内径側に向かって延伸するシールリップ部７ｂを形成している。図２のシール６とは異なり、図４のシール７のシールリップ部７ｂには、突起が形成されていない。図４において、シールリップ部７ｂは、略一定の厚さ（例えば０．３ｍｍ～２ｍｍ）で内径側に向かって延びている。なお、シールリップ部７ｂの厚さを、外径側から内径側にかけて連続的にまたは段階的に小さくなるように変化させてもよい。
　バルブ装置の開閉操作の際には、シールが押し付けられた状態で、ロータが回転する。シールは固定されており、シール面はロータの外周面と常に摺接することになるので、ロータの外周面に比べて摩耗が進行しやすい。また、シールは、ロータの曲面形状に密着させる必要があるため、適度な変形性が求められる。さらに、冷却水には一般的にエチレングリコールなどを主成分としたＰＨ７～１１の水溶液（不凍液）が用いられていることから、冷却水と接触するシール６には耐アルカリ性や、低吸水性も求められる。
　本発明の流量制御バルブ用シールは、樹脂組成物の成形体である。該樹脂組成物のベース樹脂は特に限定されないが、フッ素樹脂を用いることが好ましい。フッ素樹脂をベース樹脂としたフッ素樹脂組成物は、低弾性、低硬度であるため、樹脂製のロータの曲面状（球状または円筒状）の外周面に沿って変形しやすく、シールしやすい。さらに、フッ素樹脂は耐アルカリ性や、低吸水性に優れており、冷却水と接触する環境下でも樹脂の劣化を抑制できる。これにより、安価に作製できるとともに、摺接するロータの摩耗損傷が少なく、低リーク性、低摩擦性に優れる。
　フッ素樹脂は単体では摩耗しやすいが、適切な充填材を配合することで耐摩耗性を向上させることができる。上記フッ素樹脂組成物は、非繊維状充填材を含み、繊維状充填材を含まないことが好ましい。これにより、相手材である樹脂製のロータを摩耗損傷させにくく、低摩擦低摩耗特性が得られる。
　フッ素樹脂としては、テトラフルオロエチレン－パーフルオロアルキルビニルエーテル共重合体（ＰＦＡ）樹脂、テトラフルオロエチレン－ヘキサフルオロプロピレン共重合体（ＦＥＰ）樹脂、テトラフルオロエチレン－エチレン共重合体（ＥＴＦＥ）樹脂、ポリテトラフルオロエチレン（ＰＴＦＥ）樹脂などを用いることができる。これらの中でも、射出成形可能な溶融フッ素樹脂であるＰＦＡ樹脂、ＦＥＰ樹脂、ＥＴＦＥ樹脂を用いることが好ましい。これにより、シールを射出成形体として得ることができる。
　ＰＦＡ樹脂や、ＦＥＰ樹脂、ＥＴＦＥ樹脂をベースとしたフッ素樹脂組成物を成形する場合は、例えば、原材料をヘンシェルミキサー、ボールミキサー、リボンブレンダー、レディゲミキサーなどにて乾式混合し、さらに二軸押出し機などの溶融押出し機にて溶融混練し、成形用ペレットを得た後、射出成形により成形することができる。
　フッ素樹脂組成物には、冷却水中での摩擦摩耗特性を向上するために、ＰＨ７～１１のアルカリ性水溶液に耐性のある充填材を配合することが好ましい。充填材としては、炭素繊維、黒鉛、ＰＴＦＥ樹脂、無機物（マイカ、タルク、炭酸カルシウムなど）、ウィスカ（炭酸カルシウム、チタン酸カリウムなど）などが挙げられる。これら充填材の中では非繊維状充填材を用いることが好ましく、この場合、相手材となるロータへの攻撃性の点から繊維状充填材を含まないことがより好ましい。
　非繊維状充填材は、炭素繊維、ガラス繊維、ウィスカなどのアスペクト比を有する繊維状充填材以外であればよく、不定形の粒状、球状、鱗片状、板状の充填材などが挙げられる。これらの中でも異方性がない、粒状、球状の充填材が好ましい。
　非繊維状充填材としては、黒鉛を用いることが好ましい。黒鉛は冷却水中での低摩擦低摩耗特性を付与する効果がある。鱗片状、粒状、球状の黒鉛を用いることができるが、フッ素樹脂組成物の弾性率を高めない、粒状黒鉛または球状黒鉛を用いることがより好ましい。黒鉛の平均粒子径は限定されないが、３μｍ～５０μｍが好ましく、１０μｍ～３０μｍがより好ましい。５０μｍを超えると、フッ素樹脂組成物の引張伸び特性が低下する。平均粒子径は、例えば、レーザー光散乱法を利用した粒子径分布測定装置などを用いて測定することができる。上述したベース樹脂に黒鉛を配合したフッ素樹脂組成物からなるシールは、樹脂製のロータを摩耗損傷しにくく、長期で安定したシール性が得られる。また、耐アルカリ性に優れるので、劣化することなく、長期使用が可能である。
　また、フッ素樹脂組成物のベース樹脂として、溶融フッ素樹脂であるＰＦＡ樹脂や、ＦＥＰ樹脂、ＥＴＦＥ樹脂を用いる場合、充填材としてＰＴＦＥ樹脂を配合してもよい。ＰＴＦＥ樹脂の平均粒子径は、特に限定されるものではないが１０μｍ～５０μｍとすることが好ましい。
　なお、本発明の効果を阻害しない程度に、フッ素樹脂組成物に対して周知の樹脂用添加剤を配合してもよい。この添加剤としては、例えば、窒化ホウ素、二硫化モリブデン、二硫化タングステンなどの摩擦特性向上剤、炭素粉末、酸化鉄、酸化チタンなどの着色剤が挙げられる。
　本発明のシールに用いる樹脂組成物は、樹脂組成物全体に対して、上述したベース樹脂を７０体積％～９７体積％含む。樹脂組成物に充填材を配合する場合、充填材が３体積～３０体積％で残部がベース樹脂である組成物が好ましく、充填材が５体積％～２０体積％で残部がフッ素樹脂である組成物がより好ましい。充填材としては、非繊維状充填材を用いることが好ましい。充填材が３０体積％を超えると、フッ素樹脂組成物の引張伸び特性が低下するおそれがある。
　本発明の流量制御バルブ装置において、流量制御バルブ用シールは、フッ素樹脂組成物の成形体であり、ロータは、シールとは異なるベース樹脂からなる樹脂組成物の成形体であるので、シールとロータとは異なる樹脂材同士の摺動となる。そのため、同じ樹脂材同士の摺動において想定される高摩擦係数による摩耗増大を防止でき、良好な低摩擦性や低摩耗性が得られる。
　以下、実施例を挙げて本発明をさらに具体的に説明する。ただし、本発明は以下の実施例に限定されるものではない。
実施例１～実施例４、比較例１
　表２の配合割合（体積％）で配合したＥＴＦＥ樹脂組成物を用い、射出成形によって流量制御バルブ用シールを作製した。なお、シールの形状は、図２に示すシール６の形状（突起あり）と図４に示すシール７の形状（突起なし）の２種類とした。
　ＥＴＦＥ樹脂組成物に用いた原料を以下に示す。
（１）ＥＴＦＥ樹脂
　ＡＧＣ株式会社：Ｃ－８８ＡＸＭＰ
（２）黒鉛
　日本黒鉛工業株式会社：ＡＣＰ（平均粒子径：２４μｍ）
　球状のロータ（ガラス繊維４０質量％入りＰＰＳ樹脂組成物）に、上記で得た各種シールを押し付けた状態を模した試験治具を作製した。この試験治具に対し冷却水を流して、シールのリーク試験を行った。試験に用いた冷却水は、自動車のエンジン冷却水であり、その主成分はエチレングリコールである。リーク試験の条件を表１に示す。また、試験結果を表２に一括して示す。
　ロータ：φ６０（外径寸法）、表面粗さＲａ１μｍ
　シール：φ２３（外径寸法）×φ１５（内径寸法ｄ１）×２．５ｍｍ（高さ）
　　　　　シールリップ部の厚さ０．８ｍｍ（突起が形成された部分を除く）
　　　　　突起高さ０．２ｍｍ（図２のシール形状の場合）
Figure JPOXMLDOC01-appb-T000001
Figure JPOXMLDOC01-appb-T000002
　表２に示すように、（ｄ２－ｄ１）／２＜Ｌの関係式を満たす実施例１～実施例４は、冷却水のリーク量が１ｍｌ／ｍｉｎ～８ｍｌ／ｍｉｎであり、低リーク性に優れる結果であった。一方、（ｄ２－ｄ１）／２＞Ｌとなる比較例１は、冷却水のリーク量が３３ｍｌ／ｍｉｎであり、実施例に比べて劣る結果であった。
　本発明の流量制御バルブ用シールは、射出成形などによって容易かつ安価に作製できるとともに、低リーク性、低摩擦性に優れる流量制御バルブ用シール、およびそのシールを備える流量制御バルブ装置に広く利用できる。
　１　　バルブ装置
　２　　ハウジング
　３　　回転軸
　４　　ロータ
　５　　導入部
　６　　シール
　７　　シール

Claims (6)

  1. 　冷却水を受け入れる導入部、及び、冷却水を送り出す吐出部を有するハウジングと、前記ハウジングの内部に設けられ、球状または円筒状の外周面と、該外周面から内周面に連通する開口部とを有し、前記ハウジングに対して回転する樹脂製のロータとを備える流量制御バルブ装置に用いられ、
    　前記ハウジング内にて前記ロータと前記導入部または前記吐出部との間に設けられ、前記ロータの外周面に摺接する環状の樹脂製の流量制御バルブ用シールであって、
    　前記流量制御バルブ用シールの軸方向の断面形状が略Ｌ字であり、該略Ｌ字をなす二辺部のうち、一方の辺部は筒状部を形成し、他方の辺部は、前記筒状部のロータ側の端部から内径側に向かって延伸し前記ロータの外周面に摺接するシールリップ部を形成しており、
    　前記流量制御バルブ用シールの内径寸法をｄ１、前記開口部の内径寸法をｄ２、前記シールリップ部の径方向の長さをＬとしたとき、（ｄ２－ｄ１）／２＜Ｌの関係式を満たすことを特徴とする流量制御バルブ用シール。
  2. 　前記シールリップ部は、前記ロータの外周面に摺接するシール面に凸状の突起を有することを特徴とする請求項１記載の流量制御バルブ用シール。
  3. 　前記流量制御バルブ用シールは、筒状の前記導入部または前記吐出部のロータ側の端面に装着されることを特徴とする請求項１記載の流量制御バルブ用シール。
  4. 　前記流量制御バルブ用シールは、射出成形可能なフッ素樹脂をベース樹脂とする樹脂組成物の射出成形体であることを特徴とする請求項１記載の流量制御バルブ用シール。
  5. 　前記樹脂組成物は、該樹脂組成物全体に対して非繊維状充填材を３体積％～３０体積％含み、残部が前記フッ素樹脂であり、繊維状充填材を含まないことを特徴する請求項４記載の流量制御バルブ用シール。
  6. 　冷却水を受け入れる導入部、及び、冷却水を送り出す吐出部を有するハウジングと、前記ハウジングの内部に設けられ、球状または円筒状の外周面と、該外周面から内周面に連通する開口部とを有し、前記ハウジングに対して回転する樹脂製のロータと、前記ハウジング内にて前記ロータと前記導入部または前記吐出部との間に設けられ、前記ロータの外周面に摺接する環状の流量制御バルブ用シールとを備える流量制御バルブ装置であって、
    　前記流量制御バルブ用シールが、フッ素樹脂をベース樹脂とする樹脂組成物の成形体であり、前記ロータが前記流量制御バルブ用シールとはベース樹脂が異なる樹脂組成物からなる成形体であり、
    　前記流量制御バルブ用シールの軸方向の断面形状が略Ｌ字であり、該略Ｌ字をなす二辺部のうち、一方の辺部は筒状部を形成し、他方の辺部は、前記筒状部のロータ側の端部から内径側に向かって延伸し前記ロータの外周面に摺接するシールリップ部を形成しており、前記流量制御バルブ用シールの内径寸法をｄ１、前記開口部の内径寸法をｄ２、前記シールリップ部の径方向の長さをＬとしたとき、（ｄ２－ｄ１）／２＜Ｌの関係式を満たすことを特徴とする流量制御バルブ装置。
PCT/JP2022/018624 2021-04-27 2022-04-22 流量制御バルブ用シールおよび流量制御バルブ装置 WO2022230782A1 (ja)