JP7383375B2 - Optical glass and optical elements - Google Patents

Optical glass and optical elements Download PDF

Info

Publication number
JP7383375B2
JP7383375B2 JP2018189911A JP2018189911A JP7383375B2 JP 7383375 B2 JP7383375 B2 JP 7383375B2 JP 2018189911 A JP2018189911 A JP 2018189911A JP 2018189911 A JP2018189911 A JP 2018189911A JP 7383375 B2 JP7383375 B2 JP 7383375B2
Authority
JP
Japan
Prior art keywords
content
cao
glass
mass ratio
total content
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
JP2018189911A
Other languages
Japanese (ja)
Other versions
JP2019112292A (en
Inventor
昂浩 庄司
将士 金子
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Hoya Corp
Original Assignee
Hoya Corp
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Hoya Corp filed Critical Hoya Corp
Priority to CN201811480139.5A priority Critical patent/CN109956666B/en
Publication of JP2019112292A publication Critical patent/JP2019112292A/en
Application granted granted Critical
Publication of JP7383375B2 publication Critical patent/JP7383375B2/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Description

本発明は、光学ガラスおよび光学素子に関する。 TECHNICAL FIELD The present invention relates to optical glasses and optical elements.

特許文献1には、屈折率ndが1.79以上、アッベ数νdが27以上の光学ガラスが開示されている。特許文献1に記載されている光学ガラスは、再加熱試験においてガラス内部が失透しないことを特徴としている。そして、特許文献1に記載のガラスは、上記の光学特性を得るため、Laなどの希土類酸化物成分を含有している。 Patent Document 1 discloses an optical glass having a refractive index nd of 1.79 or more and an Abbe number νd of 27 or more. The optical glass described in Patent Document 1 is characterized in that the inside of the glass does not devitrify in a reheating test. The glass described in Patent Document 1 contains a rare earth oxide component such as La 2 O 3 in order to obtain the above optical properties.

特開2006-219365号公報Japanese Patent Application Publication No. 2006-219365

ところで、希土類酸化物は他のガラス成分と比べ、原料の価格が変動しやすくまた供給量が限られているため、ガラスの安定を安定供給する観点から、その使用量を削減することが望ましい。
さらに、希土類酸化物成分は他のガラス成分と比べ、ガラスの比重を高める作用があり、ガラスの低比重化には好ましい成分とは言えない。
オートフォーカス方式の光学系に搭載する光学素子には、オートフォーカス機能を駆動する際の消費電力を低減するために軽量化が求められている。ガラスの比重を低減することができれば、レンズ等の光学素子の重量を減少できる。
By the way, compared to other glass components, raw material prices of rare earth oxides tend to fluctuate and supplies are limited, so it is desirable to reduce the amount used from the viewpoint of stably supplying glass.
Furthermore, the rare earth oxide component has the effect of increasing the specific gravity of glass compared to other glass components, and cannot be said to be a preferred component for lowering the specific gravity of glass.
Optical elements installed in autofocus optical systems are required to be lightweight in order to reduce power consumption when driving the autofocus function. If the specific gravity of glass can be reduced, the weight of optical elements such as lenses can be reduced.

そこで、本発明は、所望の光学恒数を有し、安定供給が可能であって、比較的比重が小さい光学ガラス、ならびに前記光学ガラスからなる光学素子を提供することを目的とする。 SUMMARY OF THE INVENTION Therefore, an object of the present invention is to provide an optical glass that has desired optical constants, can be stably supplied, and has a relatively low specific gravity, as well as an optical element made of the optical glass.

本発明の要旨は以下のとおりである。
(1)屈折率ndが1.69~1.87、アッベ数νdが24~36であって、
SiOの含有量が10~50質量%であり、
TiOの含有量が40質量%以下であり、
Nbの含有量が5~60質量%であり、
BaOの含有量が10質量%以下であり、
La、Y、Gd、YbおよびLuの合計含有量が13.5質量%以下であり、
NbおよびTiOの合計含有量に対するNbの含有量の質量比[Nb/(Nb+TiO)]が0.6以下であり、
LiO、NaOおよびKOからなる群から選択される1以上のガラス成分を含み、
MgO、CaO、SrOおよびBaOのからなる群から選択される1以上のガラス成分を含み、
MgO、CaO、SrOおよびBaOの合計含有量R’Oに対するCaOの含有量の質量比(CaO/R’O)と、LiO、NaOおよびKOの合計含有量ROに対するNaOの含有量の質量比(NaO/RO)との合計[(CaO/R’O)+(NaO/RO)]が1.1より大きく、
上記合計含有量R’Oに対するMgOおよびCaOの合計含有量の質量比[(MgO+CaO)/R’O]が0.44~1.0である、光学ガラス。
The gist of the present invention is as follows.
(1) The refractive index nd is 1.69 to 1.87, the Abbe number νd is 24 to 36,
The content of SiO 2 is 10 to 50% by mass,
The content of TiO 2 is 40% by mass or less,
The content of Nb 2 O 5 is 5 to 60% by mass,
The content of BaO is 10% by mass or less,
The total content of La 2 O 3 , Y 2 O 3 , Gd 2 O 3 , Yb 2 O 3 and Lu 2 O 3 is 13.5% by mass or less,
The mass ratio of the content of Nb 2 O 5 to the total content of Nb 2 O 5 and TiO 2 [Nb 2 O 5 /(Nb 2 O 5 +TiO 2 )] is 0.6 or less,
Containing one or more glass components selected from the group consisting of Li 2 O, Na 2 O and K 2 O,
Containing one or more glass components selected from the group consisting of MgO, CaO, SrO and BaO,
Mass ratio of CaO content to total content R'O of MgO, CaO, SrO and BaO (CaO/R'O) and total content R2O of Li 2 O, Na 2 O and K 2 O The sum of the content of Na 2 O and the mass ratio (Na 2 O/R 2 O) [(CaO/R'O) + (Na 2 O/R 2 O)] is greater than 1.1,
An optical glass having a mass ratio [(MgO+CaO)/R'O] of the total content of MgO and CaO to the total content R'O of 0.44 to 1.0.

(2)屈折率ndが1.69~1.87、アッベ数νdが24~36であって、
SiOの含有量が10~50質量%であり、
TiOの含有量が40質量%以下であり、
Nbの含有量が5~60質量%であり、
BaOの含有量が10質量%以下であり、
La、Y、Gd、YbおよびLuの合計含有量が13.5質量%以下であり、
NbおよびTiOの合計含有量に対するNbの含有量の質量比[Nb/(Nb+TiO)]が0.6以下であり、
LiO、NaOおよびKOの合計含有量ROおよびMgO、CaO、SrOおよびBaOの合計含有量R’Oの合計含有量に対するNaOの含有量の質量比[NaO/(RO+R’O)]が0より大きく、
上記合計含有量ROおよび上記合計含有量R’Oの合計含有量に対するCaOの含有量の質量比[CaO/(RO+R’O)]が0.1以上であり、
上記合計含有量R’Oに対するMgOおよびCaOの合計含有量の質量比[(MgO+CaO)/R’O]が0.44~1.0である、光学ガラス。
(2) the refractive index nd is 1.69 to 1.87 and the Abbe number νd is 24 to 36,
The content of SiO 2 is 10 to 50% by mass,
The content of TiO 2 is 40% by mass or less,
The content of Nb 2 O 5 is 5 to 60% by mass,
The content of BaO is 10% by mass or less,
The total content of La 2 O 3 , Y 2 O 3 , Gd 2 O 3 , Yb 2 O 3 and Lu 2 O 3 is 13.5% by mass or less,
The mass ratio of the content of Nb 2 O 5 to the total content of Nb 2 O 5 and TiO 2 [Nb 2 O 5 /(Nb 2 O 5 +TiO 2 )] is 0.6 or less,
Total content of Li 2 O, Na 2 O and K 2 O Total content of R 2 O and MgO, CaO, SrO and BaO Mass ratio of the content of Na 2 O to the total content of R'O [Na 2 O/(R 2 O+R'O)] is greater than 0,
The mass ratio [CaO/(R 2 O + R'O)] of the content of CaO to the total content of the total content R 2 O and the total content R'O is 0.1 or more,
An optical glass having a mass ratio [(MgO+CaO)/R'O] of the total content of MgO and CaO to the total content R'O of 0.44 to 1.0.

(3)屈折率ndが1.69~1.87、アッベ数νdが24~36であって、
SiOの含有量が10~50質量%であり、
TiOの含有量が40質量%以下であり、
Nbの含有量が5~60質量%であり、
BaOの含有量が10質量%以下であり、
La、Y、Gd、YbおよびLuの合計含有量が13.5質量%以下であり、
NbおよびTiOの合計含有量が30質量%以上であり、
NbおよびTiOの合計含有量に対するNbの含有量の質量比[Nb/(Nb+TiO)]が0.7以下であり、
LiO、NaOおよびKOの合計含有量ROおよびMgO、CaO、SrOおよびBaOの合計含有量R’Oの合計含有量に対する上記合計含有量R’Oの質量比[R’O/(RO+R’O)]が0.7~1.0であり、
上記合計含有量R’Oに対するMgOおよびCaOの合計含有量の質量比[(MgO+CaO)/R’O]が0.26~1.0である、光学ガラス。
(3) the refractive index nd is 1.69 to 1.87, the Abbe number νd is 24 to 36,
The content of SiO 2 is 10 to 50% by mass,
The content of TiO 2 is 40% by mass or less,
The content of Nb 2 O 5 is 5 to 60% by mass,
The content of BaO is 10% by mass or less,
The total content of La 2 O 3 , Y 2 O 3 , Gd 2 O 3 , Yb 2 O 3 and Lu 2 O 3 is 13.5% by mass or less,
The total content of Nb 2 O 5 and TiO 2 is 30% by mass or more,
The mass ratio of the content of Nb 2 O 5 to the total content of Nb 2 O 5 and TiO 2 [Nb 2 O 5 /(Nb 2 O 5 +TiO 2 )] is 0.7 or less,
The mass ratio [ R 'O/(R 2 O + R'O)] is 0.7 to 1.0,
An optical glass having a mass ratio [(MgO+CaO)/R'O] of the total content of MgO and CaO to the total content R'O of 0.26 to 1.0.

(4)屈折率ndが1.69~1.87、アッベ数νdが24~36であって、
SiOの含有量が10~50質量%であり、
TiOの含有量が40質量%以下であり、
Nbの含有量が5~60質量%であり、
の含有量が5質量%以下であり、
BaOの含有量が10質量%以下であり、
La、Y、Gd、YbおよびLuの合計含有量が13.5質量%以下であり、
NbおよびTiOの合計含有量に対するNbの含有量の質量比[Nb/(Nb+TiO)]が0.5以下であり、
LiO、NaOおよびKOの合計含有量ROおよびMgO、CaO、SrOおよびBaOの合計含有量R’Oの合計含有量に対する上記合計含有量R’Oの質量比[R’O/(RO+R’O)]が0.71~1.0であり、
上記合計含有量R’Oに対するMgOおよびCaOの合計含有量の質量比[(MgO+CaO)/R’O]が0.26~1.0である、光学ガラス。
(4) the refractive index nd is 1.69 to 1.87, the Abbe number νd is 24 to 36,
The content of SiO 2 is 10 to 50% by mass,
The content of TiO 2 is 40% by mass or less,
The content of Nb 2 O 5 is 5 to 60% by mass,
The content of B 2 O 3 is 5% by mass or less,
The content of BaO is 10% by mass or less,
The total content of La 2 O 3 , Y 2 O 3 , Gd 2 O 3 , Yb 2 O 3 and Lu 2 O 3 is 13.5% by mass or less,
The mass ratio of the content of Nb 2 O 5 to the total content of Nb 2 O 5 and TiO 2 [Nb 2 O 5 /(Nb 2 O 5 +TiO 2 )] is 0.5 or less,
The mass ratio [ R 'O/(R 2 O + R'O)] is 0.71 to 1.0,
An optical glass having a mass ratio [(MgO+CaO)/R'O] of the total content of MgO and CaO to the total content R'O of 0.26 to 1.0.

(5)上記(1)~(4)のいずれかに記載の光学ガラスからなる光学素子。 (5) An optical element made of the optical glass according to any one of (1) to (4) above.

本発明によれば、所望の光学恒数を有し、比較的比重が小さい光学ガラス、ならびに前記光学ガラスからなる光学素子を提供できる。 According to the present invention, it is possible to provide an optical glass having desired optical constants and a relatively low specific gravity, and an optical element made of the optical glass.

以下、本発明の実施形態について説明する。なお、本発明および本明細書において、光学ガラスのガラス組成は、特記しない限り、酸化物基準で表示する。ここで「酸化物基準のガラス組成」とは、ガラス原料が熔融時にすべて分解されて光学ガラス中で酸化物として存在するものとして換算することにより得られるガラス組成をいい、各ガラス成分の表記は慣習にならい、SiO、TiOなどを記載する。ガラス成分の含有量および合計含有量は、特記しない限り質量基準であり、「%」は「質量%」を意味する。 Embodiments of the present invention will be described below. In the present invention and this specification, the glass composition of optical glass is expressed on an oxide basis unless otherwise specified. Here, "oxide-based glass composition" refers to the glass composition obtained by converting the glass raw materials as if they were all decomposed during melting and existing as oxides in the optical glass, and the notation of each glass component is Following customary practice, SiO 2 , TiO 2 , etc. are listed. The content of the glass component and the total content are based on mass unless otherwise specified, and "%" means "% by mass".

ガラス成分の含有量は、公知の方法、例えば、誘導結合プラズマ発光分光分析法(ICP-AES)、誘導結合プラズマ質量分析法(ICP-MS)等の方法で定量することができる。また、本明細書および本発明において、構成成分の含有量が0%とは、この構成成分を実質的に含まないことを意味し、該成分が不可避的不純物レベルで含まれることを許容する。 The content of the glass component can be determined by a known method, for example, inductively coupled plasma optical emission spectroscopy (ICP-AES), inductively coupled plasma mass spectrometry (ICP-MS), or the like. Furthermore, in this specification and the present invention, the content of a component of 0% means that the component is not substantially contained, and the component is allowed to be contained at an unavoidable impurity level.

また、本明細書では、屈折率は、特記しない限り、ヘリウムのd線(波長587.56nm)における屈折率ndをいう。 Furthermore, in this specification, unless otherwise specified, the refractive index refers to the refractive index nd at the d-line (wavelength 587.56 nm) of helium.

アッベ数νdは、分散に関する性質を表す値として用いられるものであり、下式で表される。ここで、nFは青色水素のF線(波長486.13nm)における屈折率、nCは赤色水素のC線(656.27nm)における屈折率である。
νd=(nd-1)/(nF-nC)
The Abbe number νd is used as a value representing properties related to dispersion, and is expressed by the following formula. Here, nF is the refractive index of blue hydrogen at the F line (wavelength 486.13 nm), and nC is the refractive index of red hydrogen at the C line (656.27 nm).
νd=(nd-1)/(nF-nC)

部分分散比Pg,Fは、g線、F線、c線における各屈折率ng、nF、nCを用いて次のように表される。
Pg,F=(ng-nF)/(nF-nC)
横軸をアッベ数νd、縦軸を部分分散比Pg,Fとする平面において、ノーマルラインは下式により表される。
Pg,F(0)=0.6483-(0.0018×νd)
さらに、ノーマルラインからの部分分散比Pg,Fの偏差ΔPg,Fは次のように表される。
ΔPg,F=Pg,F-Pg,F(0)
The partial dispersion ratios Pg and F are expressed as follows using the refractive indices ng, nF, and nC at the g-line, F-line, and c-line.
Pg,F=(ng-nF)/(nF-nC)
In a plane where the horizontal axis is the Abbe number νd and the vertical axis is the partial dispersion ratio Pg,F, the normal line is expressed by the following formula.
Pg,F(0)=0.6483-(0.0018×νd)
Furthermore, the deviation ΔPg,F of the partial dispersion ratio Pg,F from the normal line is expressed as follows.
ΔPg, F=Pg, F-Pg, F(0)

以下に、本発明の光学ガラスを、第1実施形態、第2実施形態、第3実施形態および第4実施形態として説明する。なお、第2、第3、第4実施形態における各ガラス成分の作用、効果は、第1実施形態における各ガラス成分の作用、効果と同様である。したがって、第2、第3、第4実施形態において、第1実施形態に関する説明と重複する事項については適宜省略する。 The optical glass of the present invention will be described below as a first embodiment, a second embodiment, a third embodiment, and a fourth embodiment. Note that the actions and effects of each glass component in the second, third, and fourth embodiments are the same as the actions and effects of each glass component in the first embodiment. Therefore, in the second, third, and fourth embodiments, matters that overlap with the description regarding the first embodiment will be omitted as appropriate.

第1実施形態
第1実施形態に係る光学ガラスは、
屈折率ndが1.69~1.87、アッベ数νdが24~36であって、
SiOの含有量が10~50質量%であり、
TiOの含有量が40質量%以下であり、
Nbの含有量が5~60質量%であり、
BaOの含有量が10質量%以下であり、
La、Y、Gd、YbおよびLuの合計含有量が13.5質量%以下であり、
NbおよびTiOの合計含有量に対するNbの含有量の質量比[Nb/(Nb+TiO)]が0.6以下であり、
LiO、NaOおよびKOからなる群から選択される1以上のガラス成分を含み、
MgO、CaO、SrOおよびBaOのからなる群から選択される1以上のガラス成分を含み、
MgO、CaO、SrOおよびBaOの合計含有量R’Oに対するCaOの含有量の質量比(CaO/R’O)と、LiO、NaOおよびKOの合計含有量ROに対するNaOの含有量の質量比(NaO/RO)との合計[(CaO/R’O)+(NaO/RO)]が1.1より大きく、
上記合計含有量R’Oに対するMgOおよびCaOの合計含有量の質量比[(MgO+CaO)/R’O]が0.44~1.0である。
First Embodiment The optical glass according to the first embodiment is
The refractive index nd is 1.69 to 1.87, the Abbe number νd is 24 to 36,
The content of SiO 2 is 10 to 50% by mass,
The content of TiO 2 is 40% by mass or less,
The content of Nb 2 O 5 is 5 to 60% by mass,
The content of BaO is 10% by mass or less,
The total content of La 2 O 3 , Y 2 O 3 , Gd 2 O 3 , Yb 2 O 3 and Lu 2 O 3 is 13.5% by mass or less,
The mass ratio of the content of Nb 2 O 5 to the total content of Nb 2 O 5 and TiO 2 [Nb 2 O 5 /(Nb 2 O 5 +TiO 2 )] is 0.6 or less,
Containing one or more glass components selected from the group consisting of Li 2 O, Na 2 O and K 2 O,
Containing one or more glass components selected from the group consisting of MgO, CaO, SrO and BaO,
Mass ratio of CaO content to total content R'O of MgO, CaO, SrO and BaO (CaO/R'O) and total content R2O of Li 2 O, Na 2 O and K 2 O The sum of the content of Na 2 O and the mass ratio (Na 2 O/R 2 O) [(CaO/R'O) + (Na 2 O/R 2 O)] is greater than 1.1,
The mass ratio of the total content of MgO and CaO to the above-mentioned total content R'O [(MgO+CaO)/R'O] is 0.44 to 1.0.

第1実施形態に係る光学ガラスにおいて、SiOの含有量は10~50%である。SiOの含有量の下限は、好ましくは12%であり、さらには15%、17%、20%の順により好ましい。また、SiOの含有量の上限は、好ましくは45%であり、さらには40%、37%、35%の順により好ましい。
SiOの含有量が少なすぎると、熱的安定性が低下するおそれがある。また、SiOの含有量が多すぎると、屈折率が低下するおそれがある。SiOの含有量を上記範囲とすることで、熱的安定性に優れる光学ガラスが得られる。
In the optical glass according to the first embodiment, the content of SiO 2 is 10 to 50%. The lower limit of the SiO 2 content is preferably 12%, and more preferably 15%, 17%, and 20% in this order. Further, the upper limit of the content of SiO 2 is preferably 45%, and more preferably 40%, 37%, and 35% in that order.
If the content of SiO 2 is too low, thermal stability may decrease. Furthermore, if the content of SiO 2 is too large, the refractive index may decrease. By setting the content of SiO 2 within the above range, an optical glass with excellent thermal stability can be obtained.

第1実施形態に係る光学ガラスにおいて、TiOの含有量は40%以下である。TiOの含有量の上限は、好ましくは35%であり、さらには30%、28%、25%の順により好ましい。TiOの含有量の下限は、好ましくは0%であり、さらには5%、8%、10%の順により好ましい。TiOの含有量は0%でもよい。
TiOの含有量が多すぎると、部分分散比Pg,Fが増加するおそれがある。また、TiOの含有量が少なすぎると、所望の光学恒数が得られないおそれがある。TiOの含有量を上記範囲とすることで、比重を低減し、またガラスの原料コストの増加を抑制できる。
In the optical glass according to the first embodiment, the content of TiO 2 is 40% or less. The upper limit of the TiO 2 content is preferably 35%, and more preferably 30%, 28%, and 25% in that order. The lower limit of the content of TiO 2 is preferably 0%, and more preferably 5%, 8%, and 10% in that order. The content of TiO 2 may be 0%.
If the content of TiO 2 is too large, the partial dispersion ratio Pg, F may increase. Moreover, if the content of TiO 2 is too small, there is a possibility that desired optical constants may not be obtained. By setting the content of TiO 2 within the above range, specific gravity can be reduced and an increase in glass raw material cost can be suppressed.

第1実施形態に係る光学ガラスにおいて、Nbの含有量は5~60%である。Nbの含有量の下限は、好ましくは7%であり、さらには8%、9%、10%の順により好ましい。また、Nbの含有量の上限は、好ましくは45%であり、さらには40%、35%、30%の順により好ましい。
Nbの含有量が少なすぎると、所望の屈折率nd、アッベ数νdおよび部分分散比Pg,Fが得られないおそれがある。また、Nbの含有量が多すぎると、熱的安定性が低下し、また高分散化するおそれがある。Nbの含有量を上記範囲とすることで、部分分散比Pg,Fを低減し、またガラスの原料コストの増加を抑制できる。
In the optical glass according to the first embodiment, the content of Nb 2 O 5 is 5 to 60%. The lower limit of the content of Nb 2 O 5 is preferably 7%, and more preferably 8%, 9%, and 10% in that order. Further, the upper limit of the content of Nb 2 O 5 is preferably 45%, and more preferably 40%, 35%, and 30% in that order.
If the content of Nb 2 O 5 is too small, there is a possibility that the desired refractive index nd, Abbe number νd, and partial dispersion ratios Pg and F cannot be obtained. Moreover, if the content of Nb 2 O 5 is too large, thermal stability may decrease and there is a risk of high dispersion. By setting the content of Nb 2 O 5 within the above range, it is possible to reduce the partial dispersion ratios Pg and F and to suppress an increase in the cost of raw materials for glass.

第1実施形態に係る光学ガラスにおいて、BaOの含有量は10%以下である。BaOの含有量の上限は、好ましくは9%であり、さらには8%、7%の順により好ましい。BaOの含有量の下限は、好ましくは0%であり、さらには1%、2%、3%、3.5%の順により好ましい。BaOの含有量は0%でもよい。
BaOの含有量が多すぎると、比重が増大するおそれがある。BaOの含有量が少なすぎると、熱的安定性が低下するおそれがある。BaOの含有量を上記範囲とすることで熱的安定性に優れる光学ガラスが得られる。
In the optical glass according to the first embodiment, the BaO content is 10% or less. The upper limit of the BaO content is preferably 9%, more preferably 8% and then 7%. The lower limit of the BaO content is preferably 0%, and more preferably 1%, 2%, 3%, and 3.5% in this order. The content of BaO may be 0%.
If the BaO content is too high, the specific gravity may increase. If the content of BaO is too low, thermal stability may decrease. By setting the BaO content within the above range, an optical glass with excellent thermal stability can be obtained.

第1実施形態に係る光学ガラスにおいて、La、Y、Gd、YbおよびLuの合計含有量[La+Y+Gd+Yb+Lu]は13.5%以下である。合計含有量[La+Y+Gd+Yb+Lu]の上限は、好ましくは12%であり、さらには11%、10%、9%の順により好ましい。また、合計含有量[La+Y+Gd+Yb+Lu]の下限は、好ましくは0%であり、さらには0.5%、1%、1.5%の順により好ましい。
合計含有量[La+Y+Gd+Yb+Lu]が大きすぎると、比重が増大するおそれがある。また、合計含有量[La+Y+Gd+Yb+Lu]が小さすぎると、所望の光学恒数が得られないおそれがある。合計含有量[La+Y+Gd+Yb+Lu]を上記範囲とすることで、所望の光学恒数を有する光学ガラスが得られる。
In the optical glass according to the first embodiment, the total content of La 2 O 3 , Y 2 O 3 , Gd 2 O 3 , Yb 2 O 3 and Lu 2 O 3 [La 2 O 3 +Y 2 O 3 +Gd 2 O 3 +Yb 2 O 3 +Lu 2 O 3 ] is 13.5% or less. The upper limit of the total content [La 2 O 3 + Y 2 O 3 + Gd 2 O 3 + Yb 2 O 3 + Lu 2 O 3 ] is preferably 12%, and more preferably in the order of 11%, 10%, and 9%. . Further, the lower limit of the total content [La 2 O 3 +Y 2 O 3 +Gd 2 O 3 +Yb 2 O 3 +Lu 2 O 3 ] is preferably 0%, more preferably 0.5%, 1%, 1. The order of 5% is more preferable.
If the total content [La 2 O 3 +Y 2 O 3 +Gd 2 O 3 +Yb 2 O 3 +Lu 2 O 3 ] is too large, the specific gravity may increase. Moreover, if the total content [La 2 O 3 +Y 2 O 3 +Gd 2 O 3 +Yb 2 O 3 +Lu 2 O 3 ] is too small, there is a possibility that desired optical constants cannot be obtained. By setting the total content [La 2 O 3 +Y 2 O 3 +Gd 2 O 3 +Yb 2 O 3 +Lu 2 O 3 ] within the above range, an optical glass having desired optical constants can be obtained.

第1実施形態に係る光学ガラスにおいて、NbおよびTiOの合計含有量に対するNbの含有量の質量比[Nb/(Nb+TiO)]は0.6以下である。質量比[Nb/(Nb+TiO)]上限は、好ましくは0.60であり、さらには0.55、0.52、0.50の順により好ましい。また、質量比[Nb/(Nb+TiO)]は、好ましくは0より大きく、その下限は0.10、0.20、0.30の順により好ましい。
質量比[Nb/(Nb+TiO)]が大きすぎると、比重が増大するおそれがある。質量比[Nb/(Nb+TiO)]が小さすぎると、部分分散比Pg,Fが増加するおそれがある。質量比[Nb/(Nb+TiO)]を上記範囲とすることで、比重を低減し、またガラスの原料コストの増加を抑制できる。
In the optical glass according to the first embodiment, the mass ratio of the content of Nb 2 O 5 to the total content of Nb 2 O 5 and TiO 2 [Nb 2 O 5 /(Nb 2 O 5 +TiO 2 )] is 0. 6 or less. The upper limit of the mass ratio [Nb 2 O 5 /(Nb 2 O 5 +TiO 2 )] is preferably 0.60, and more preferably in the order of 0.55, 0.52, and 0.50. Further, the mass ratio [Nb 2 O 5 /(Nb 2 O 5 +TiO 2 )] is preferably larger than 0, and its lower limit is preferably in the order of 0.10, 0.20, and 0.30.
If the mass ratio [Nb 2 O 5 /(Nb 2 O 5 +TiO 2 )] is too large, the specific gravity may increase. If the mass ratio [Nb 2 O 5 /(Nb 2 O 5 +TiO 2 )] is too small, the partial dispersion ratios Pg, F may increase. By setting the mass ratio [Nb 2 O 5 /(Nb 2 O 5 +TiO 2 )] within the above range, specific gravity can be reduced and an increase in glass raw material cost can be suppressed.

第1実施形態に係る光学ガラスは、LiO、NaOおよびKOからなる群から選択される1以上のガラス成分を含み、好ましくはNaOを含み、より好ましくはNaOおよびKOを含む。
光学ガラスが、LiO、NaOおよびKOからなる群から選択される1以上のガラス成分を含むことで、ガラスの熔解性を高めることができる。
The optical glass according to the first embodiment contains one or more glass components selected from the group consisting of Li 2 O, Na 2 O and K 2 O, preferably contains Na 2 O, and more preferably contains Na 2 O. and K 2 O.
When the optical glass contains one or more glass components selected from the group consisting of Li 2 O, Na 2 O and K 2 O, the solubility of the glass can be improved.

第1実施形態に係る光学ガラスは、MgO、CaO、SrOおよびBaOのからなる群から選択される1以上のガラス成分を含み、好ましくはCaOを含み、より好ましくはCaOおよびBaOを含む。
光学ガラスが、MgO、CaO、SrOおよびBaOのからなる群から選択される1以上のガラス成分を含むことで、屈折率ndの低下を抑制できる。
The optical glass according to the first embodiment contains one or more glass components selected from the group consisting of MgO, CaO, SrO, and BaO, preferably contains CaO, and more preferably contains CaO and BaO.
When the optical glass contains one or more glass components selected from the group consisting of MgO, CaO, SrO, and BaO, a decrease in the refractive index nd can be suppressed.

第1実施形態に係る光学ガラスにおいて、MgO、CaO、SrOおよびBaOの合計含有量R’Oに対するCaOの含有量の質量比(CaO/R’O)と、LiO、NaOおよびKOの合計含有量ROに対するNaOの含有量の質量比(NaO/RO)との合計[(CaO/R’O)+(NaO/RO)]は1.1より大きい。[(CaO/R’O)+(NaO/RO)]の下限は、好ましくは1.2であり、さらには1.3、1.35、1.4の順により好ましい。[(CaO/R’O)+(NaO/RO)]の上限は、好ましくは1.9であり、さらには1.85、1.8の順により好ましい。
[(CaO/R’O)+(NaO/RO)]が小さすぎると、比重が低下し、所望の光学恒数が得られないおそれがある。[(CaO/R’O)+(NaO/RO)]を上記範囲とすることで、低比重で所望の光学恒数を有する光学ガラスが得られる。
In the optical glass according to the first embodiment, the mass ratio of the content of CaO to the total content R'O of MgO, CaO, SrO , and BaO (CaO/R'O), and the mass ratio of the content of CaO to the total content R'O of Li 2 O, Na 2 O, and The sum of the mass ratio of the Na 2 O content to the total K 2 O content R 2 O (Na 2 O/R 2 O) [(CaO/R'O) + (Na 2 O/R 2 O) ] is greater than 1.1. The lower limit of [(CaO/R'O)+(Na 2 O/R 2 O)] is preferably 1.2, and more preferably 1.3, 1.35, and 1.4 in that order. The upper limit of [(CaO/R'O)+(Na 2 O/R 2 O)] is preferably 1.9, and more preferably 1.85 and 1.8 in that order.
If [(CaO/R'O)+(Na 2 O/R 2 O)] is too small, the specific gravity may decrease and desired optical constants may not be obtained. By setting [(CaO/R'O)+(Na 2 O/R 2 O)] within the above range, an optical glass having a low specific gravity and desired optical constants can be obtained.

第1実施形態に係る光学ガラスにおいて、MgO、CaO、SrOおよびBaOの合計含有量R’Oに対するMgOおよびCaOの合計含有量の質量比[(MgO+CaO)/R’O]は0.44~1.0である。質量比[(MgO+CaO)/R’O]の下限は、好ましくは0.5であり、さらには0.55、0.6の順により好ましい。また、質量比[(MgO+CaO)/R’O]の上限は、好ましくは0.9であり、さらには0.85、0.8、0.78の順により好ましい。
質量比[(MgO+CaO)/R’O]が小さすぎると、比重が増大するおそれがある。質量比[(MgO+CaO)/R’O]が大きすぎると、熱的安定性が低下するおそれがある。質量比[(MgO+CaO)/R’O]を上記範囲とすることで、比重が低減された光学ガラスを得ることができる。
In the optical glass according to the first embodiment, the mass ratio [(MgO+CaO)/R'O] of the total content of MgO and CaO to the total content R'O of MgO, CaO, SrO , and BaO is 0.44 to 1. .0. The lower limit of the mass ratio [(MgO+CaO)/R'O] is preferably 0.5, and more preferably 0.55 and 0.6 in that order. Further, the upper limit of the mass ratio [(MgO+CaO)/R'O] is preferably 0.9, and more preferably 0.85, 0.8, and 0.78 in this order.
If the mass ratio [(MgO+CaO)/R'O] is too small, the specific gravity may increase. If the mass ratio [(MgO+CaO)/R'O] is too large, thermal stability may decrease. By setting the mass ratio [(MgO+CaO)/R'O] within the above range, an optical glass with reduced specific gravity can be obtained.

次に、第1実施形態に係る光学ガラスにおける、ガラス成分の含有量および比率の好ましい態様を以下に詳述する。 Next, preferred aspects of the contents and ratios of glass components in the optical glass according to the first embodiment will be described in detail below.

第1実施形態に係る光学ガラスにおいて、LiO、NaOおよびKOの合計含有量ROおよびMgO、CaO、SrOおよびBaOの合計含有量R’Oの合計含有量に対するNaOの含有量の質量比[NaO/(RO+R’O)]は、好ましくは0より大きく、その下限は、0.1、0.13、0.15の順により好ましい。質量比[NaO/(RO+R’O)]の上限は、好ましくは0.8であり、さらには0.7、0.6、0.5の順により好ましい。
質量比[NaO/(RO+R’O)]が小さすぎると、ガラスの熔解性が低下するおそれがある。質量比[NaO/(RO+R’O)]が大きすぎると、熱的安定性が低下するおそれがある。
In the optical glass according to the first embodiment, the total content R2O of Li2O , Na2O and K2O and the total content R'O of MgO, CaO, SrO and BaO, Na2 The mass ratio of O content [Na 2 O/(R 2 O+R'O)] is preferably larger than 0, and its lower limit is more preferably in the order of 0.1, 0.13, and 0.15. The upper limit of the mass ratio [Na 2 O/(R 2 O+R'O)] is preferably 0.8, and more preferably in the order of 0.7, 0.6, and 0.5.
If the mass ratio [Na 2 O/(R 2 O+R'O)] is too small, the solubility of the glass may decrease. If the mass ratio [Na 2 O/(R 2 O+R'O)] is too large, thermal stability may decrease.

第1実施形態に係る光学ガラスにおいて、上記合計含有量ROおよび上記合計含有量R’Oの合計含有量に対するCaOの含有量の質量比[CaO/(RO+R’O)]は、好ましくは0.1以上であり、その下限は0.15、0.18、0.2の順により好ましい。質量比[CaO/(RO+R’O)]の上限は、好ましくは0.95であり、さらには0.90、0.87、0.85の順により好ましい。
質量比[CaO/(RO+R’O)]が小さすぎると、屈折率が低下し、比重が増加するおそれがある。質量比[CaO/(RO+R’O)]が大きすぎると、熱的安定性が低下するおそれがある。
In the optical glass according to the first embodiment, the mass ratio of the CaO content to the total content of the total content R 2 O and the total content R'O [CaO/(R 2 O+R'O)] is Preferably it is 0.1 or more, and the lower limit is more preferably in the order of 0.15, 0.18, and 0.2. The upper limit of the mass ratio [CaO/(R 2 O+R'O)] is preferably 0.95, and more preferably in the order of 0.90, 0.87, and 0.85.
If the mass ratio [CaO/(R 2 O+R'O)] is too small, the refractive index may decrease and the specific gravity may increase. If the mass ratio [CaO/(R 2 O+R'O)] is too large, thermal stability may decrease.

第1実施形態に係る光学ガラスにおいて、NbおよびTiOの合計含有量[Nb+TiO]の下限は、好ましくは5%であり、さらには10%、15%、20%、22%の順により好ましい。また、合計含有量[Nb+TiO]の上限は、好ましくは60%であり、さらには50%、45%、40%の順により好ましい。
合計含有量[Nb+TiO]を上記範囲とすることで、所望の光学恒数を有する光学ガラスが得られる。
In the optical glass according to the first embodiment, the lower limit of the total content of Nb 2 O 5 and TiO 2 [Nb 2 O 5 +TiO 2 ] is preferably 5%, and more preferably 10%, 15%, and 20%. , 22% are more preferred. Further, the upper limit of the total content [Nb 2 O 5 +TiO 2 ] is preferably 60%, and more preferably 50%, 45%, and 40% in that order.
By setting the total content [Nb 2 O 5 +TiO 2 ] within the above range, an optical glass having desired optical constants can be obtained.

第1実施形態に係る光学ガラスにおいて、MgO、CaO、SrOおよびBaOの合計含有量R’OとLiO、NaOおよびKOの合計含有量ROとの合計含有量に対する合計含有量R’Oの質量比[R’O/(R’O+RO)]の下限は、好ましくは0.50、さらには0.55、0.60、0.65の順により好ましい。また、質量比[R’O/(R’O+RO)]の上限は、好ましくは0.99、さらには0.98、0.97の順により好ましい。
質量比[R’O/(R’O+RO)]が小さすぎると、屈折率ndが低下するおそれがある。質量比[R’O/(R’O+RO)]が大きすぎると、熱的安定性が低下するおそれがある。質量比[R’O/(R’O+RO)]を上記範囲とすることで、高屈折率の光学ガラスを得ることができる。
In the optical glass according to the first embodiment, the sum of the total content R'O of MgO, CaO, SrO and BaO and the total content R 2 O of Li 2 O, Na 2 O and K 2 O The lower limit of the mass ratio [R'O/(R'O+R 2 O)] of the content R'O is preferably 0.50, and more preferably in the order of 0.55, 0.60, and 0.65. Further, the upper limit of the mass ratio [R'O/(R'O+R 2 O)] is preferably 0.99, and more preferably 0.98 and 0.97 in that order.
If the mass ratio [R'O/(R'O+R 2 O)] is too small, the refractive index nd may decrease. If the mass ratio [R'O/(R'O+R 2 O)] is too large, thermal stability may decrease. By setting the mass ratio [R'O/(R'O+R 2 O)] within the above range, an optical glass with a high refractive index can be obtained.

第1実施形態に係る光学ガラスにおいて、Bの含有量の上限は、好ましくは5%であり、さらには4.5%、4.2%、4%の順により好ましい。また、Bの含有量の下限は、好ましくは0%であり、さらには0.5%、0.7%、1%の順により好ましい。Bの含有量は0%であってもよい。
の含有量が多すぎると屈折率ndが低下するおそれがある。Bの含有量を上記範囲とすることで、ガラスの熱的安定性を改善できる。
In the optical glass according to the first embodiment, the upper limit of the content of B 2 O 3 is preferably 5%, and more preferably 4.5%, 4.2%, and 4% in that order. Further, the lower limit of the content of B 2 O 3 is preferably 0%, and more preferably 0.5%, 0.7%, and 1% in that order. The content of B 2 O 3 may be 0%.
If the content of B 2 O 3 is too large, the refractive index nd may decrease. By setting the content of B 2 O 3 within the above range, the thermal stability of the glass can be improved.

第1実施形態に係る光学ガラスにおける、上記以外のガラス成分の含有量および比率の好ましい態様を以下に詳述する。 Preferred aspects of the contents and ratios of glass components other than the above in the optical glass according to the first embodiment will be described in detail below.

第1実施形態に係る光学ガラスにおいて、Pの含有量の上限は、好ましくは5%であり、さらには4.5%、4%、3.5%の順により好ましい。また、Pの含有量の下限は、好ましくは0%であり、さらには0.5%、1%、1.5%の順により好ましい。Pの含有量は0%であってもよい。Pの含有量を上記範囲とすることで、部分分散比Pg,Fの増加を抑制し、ガラスの熱的安定性を保持できる。 In the optical glass according to the first embodiment, the upper limit of the content of P 2 O 5 is preferably 5%, and more preferably 4.5%, 4%, and 3.5% in that order. Further, the lower limit of the content of P 2 O 5 is preferably 0%, and more preferably 0.5%, 1%, and 1.5% in that order. The content of P 2 O 5 may be 0%. By setting the content of P 2 O 5 within the above range, it is possible to suppress an increase in the partial dispersion ratio Pg, F and maintain the thermal stability of the glass.

第1実施形態に係るガラスにおいて、Alの含有量の上限は、好ましくは3%であり、さらには2%、1.5%、1%の順により好ましい。Alの含有量は0%であってもよい。Alの含有量を上記範囲とすることで、ガラスの耐失透性および熱的安定性を保持できる。 In the glass according to the first embodiment, the upper limit of the content of Al 2 O 3 is preferably 3%, and more preferably 2%, 1.5%, and 1% in that order. The content of Al 2 O 3 may be 0%. By setting the content of Al 2 O 3 within the above range, the devitrification resistance and thermal stability of the glass can be maintained.

第1実施形態に係るガラスにおいて、ZrOの含有量の下限は、好ましくは3%であり、さらには4%、5%、6%の順により好ましい。また、ZrOの含有量の上限は、好ましくは15%であり、さらには13%、11%、10%の順により好ましい。ZrOの含有量を上記範囲とすることで、所望の光学恒数を実現し、また部分分散比Pg,Fを低減できる。 In the glass according to the first embodiment, the lower limit of the ZrO 2 content is preferably 3%, and more preferably 4%, 5%, and 6% in that order. Further, the upper limit of the content of ZrO 2 is preferably 15%, and more preferably 13%, 11%, and 10% in that order. By setting the content of ZrO 2 within the above range, desired optical constants can be achieved and the partial dispersion ratios Pg and F can be reduced.

第1実施形態に係るガラスにおいて、WOの含有量の上限は、好ましくは5%であり、さらには3%、1%、0%の順により好ましい。WOの含有量を上記範囲とすることで、透過率を高めることができ、また、部分分散比Pg,Fおよび比重を低減できる。 In the glass according to the first embodiment, the upper limit of the content of WO 3 is preferably 5%, and more preferably 3%, 1%, and 0% in this order. By setting the content of WO 3 within the above range, the transmittance can be increased, and the partial dispersion ratios Pg, F and specific gravity can be reduced.

第1実施形態において、Biの含有量の上限は、好ましくは5%であり、さらには3%、1%、0%の順により好ましい。Biの含有量を上記範囲とすることで、ガラスの熱的安定性を改善し、また、部分分散比Pg,Fおよび比重を低減できる。 In the first embodiment, the upper limit of the content of Bi 2 O 3 is preferably 5%, and more preferably 3%, 1%, and 0% in that order. By setting the content of Bi 2 O 3 within the above range, the thermal stability of the glass can be improved, and the partial dispersion ratios Pg, F and specific gravity can be reduced.

第1実施形態に係るガラスにおいて、LiOの含有量の上限は、好ましくは10%であり、さらには8%、6%、5%の順により好ましい。LiOの含有量は少ない方が好ましく、その下限は好ましくは0%である。 In the glass according to the first embodiment, the upper limit of the Li 2 O content is preferably 10%, and more preferably 8%, 6%, and 5% in that order. It is preferable that the content of Li 2 O is small, and the lower limit thereof is preferably 0%.

第1実施形態に係るガラスにおいて、NaOの含有量の上限は、好ましくは15%であり、さらには12%、10%、8%の順により好ましい。NaOの含有量の下限は、好ましくは1%であり、さらには2%、3%、4%の順により好ましい。 In the glass according to the first embodiment, the upper limit of the Na 2 O content is preferably 15%, and more preferably 12%, 10%, and 8% in that order. The lower limit of the Na 2 O content is preferably 1%, and more preferably 2%, 3%, and 4% in that order.

第1実施形態に係るガラスにおいて、KOの含有量の上限は、好ましくは15%であり、さらには12%、10%、8%の順により好ましい。KOの含有量の下限は、好ましくは0.05%であり、さらには0.1%、0.15%の順により好ましい。 In the glass according to the first embodiment, the upper limit of the K 2 O content is preferably 15%, and more preferably 12%, 10%, and 8% in that order. The lower limit of the content of K 2 O is preferably 0.05%, more preferably 0.1% and then 0.15%.

LiO、NaOおよびKOは、部分分散比Pg,Fを低減する成分であり、液相温度を下げ、ガラスの熱的安定性を改善する働きを有するが、これらの含有量が多くなると、化学的耐久性、耐候性が低下する。そのため、LiO、NaOおよびKOの各含有量は、それぞれ上記範囲であることが好ましい。 Li 2 O, Na 2 O and K 2 O are components that reduce the partial dispersion ratio Pg,F, and have the function of lowering the liquidus temperature and improving the thermal stability of the glass, but their content When the amount increases, chemical durability and weather resistance decrease. Therefore, each content of Li 2 O, Na 2 O and K 2 O is preferably within the above range.

第1実施形態に係る光学ガラスにおいて、LiO、NaOおよびKOの合計含有量ROの下限は、好ましくは1.05%であり、さらには1.5%、2%、2.5%の順により好ましい。また、合計含有量ROの上限は、好ましくは15%であり、さらには13%、11%、10%の順により好ましい。合計含有量ROを上記範囲とすることで、ガラスの比重を低減し、またガラスの熱的安定性を維持できる。 In the optical glass according to the first embodiment, the lower limit of the total content R 2 O of Li 2 O, Na 2 O and K 2 O is preferably 1.05%, more preferably 1.5% and 2%. , 2.5% are more preferred. Further, the upper limit of the total content R 2 O is preferably 15%, and more preferably 13%, 11%, and 10% in that order. By setting the total content R 2 O within the above range, the specific gravity of the glass can be reduced and the thermal stability of the glass can be maintained.

第1実施形態に係るガラスにおいて、CsOの含有量の上限は、好ましくは10%であり、さらには5%、3%、1%の順により好ましい。CsOの含有量の下限は、好ましくは0%である。 In the glass according to the first embodiment, the upper limit of the Cs 2 O content is preferably 10%, and more preferably 5%, 3%, and 1% in that order. The lower limit of the Cs 2 O content is preferably 0%.

CsOは、ガラスの熱的安定性を改善する働きを有するが、これらの含有量が多くなると、化学的耐久性、耐候性が低下する。そのため、CsOの各含有量は、上記範囲であることが好ましい。 Cs 2 O has the function of improving the thermal stability of glass, but when its content increases, chemical durability and weather resistance decrease. Therefore, each content of Cs 2 O is preferably within the above range.

第1実施形態に係るガラスにおいて、MgOの含有量の上限は、好ましくは25%であり、さらには23%、21%、20%の順により好ましい。また、MgOの含有量の下限は、好ましくは0%である。 In the glass according to the first embodiment, the upper limit of the MgO content is preferably 25%, and more preferably 23%, 21%, and 20% in this order. Further, the lower limit of the MgO content is preferably 0%.

第1実施形態に係るガラスにおいて、CaOの含有量の上限は、好ましくは25%であり、さらには23%、21%、20%の順により好ましい。また、CaOの含有量の下限は、好ましくは0%である。 In the glass according to the first embodiment, the upper limit of the CaO content is preferably 25%, and more preferably 23%, 21%, and 20% in this order. Further, the lower limit of the CaO content is preferably 0%.

第1実施形態に係るガラスにおいて、SrOの含有量の上限は、好ましくは20%であり、さらには10%、5%、3%の順により好ましい。また、SrOの含有量の下限は、好ましくは0%である。 In the glass according to the first embodiment, the upper limit of the SrO content is preferably 20%, and more preferably 10%, 5%, and 3% in that order. Further, the lower limit of the SrO content is preferably 0%.

MgO、CaO、SrO、BaOは、いずれもガラスの熱的安定性および耐失透性を改善させる働きを有し、屈折率を高め所望の恒数を達成しやすくするガラス成分である。しかし、これらガラス成分の含有量が多くなると、比重が増加し、高分散性が損なわれ、また、ガラスの熱的安定性および耐失透性が低下する。そのため、これらガラス成分の各含有量は、それぞれ上記範囲であることが好ましい。 MgO, CaO, SrO, and BaO all have the function of improving the thermal stability and devitrification resistance of glass, and are glass components that increase the refractive index and make it easier to achieve a desired constant. However, when the content of these glass components increases, the specific gravity increases, high dispersibility is impaired, and the thermal stability and devitrification resistance of the glass decrease. Therefore, the content of each of these glass components is preferably within the above range.

第1実施形態に係るガラスにおいて、MgOおよびCaOの合計含有量[MgO+CaO]の下限は、好ましくは0%であり、さらには5%、8%、10%の順により好ましい。また、合計含有量[MgO+CaO]の上限は、好ましくは30%であり、さらには28%、25%、22%の順により好ましい。比重増大および熱的安定性の低下を抑制する観点から、合計含有量[MgO+CaO]は上記範囲であることが好ましい。 In the glass according to the first embodiment, the lower limit of the total content of MgO and CaO [MgO+CaO] is preferably 0%, and more preferably 5%, 8%, and 10% in that order. Further, the upper limit of the total content [MgO+CaO] is preferably 30%, and more preferably 28%, 25%, and 22% in that order. From the viewpoint of suppressing an increase in specific gravity and a decrease in thermal stability, the total content [MgO+CaO] is preferably within the above range.

第1実施形態に係るガラスにおいて、MgO、CaO、SrOおよびBaOの合計含有量R’Oの上限は、好ましくは30%であり、さらには28%、25%、22%の順により好ましい。また、合計含有量R’Oの下限は、好ましくは0%であり、さらには5%、8%、10%の順により好ましい。合計含有量R’Oは0%であってもよい。合計含有量R’Oを上記範囲とすることで、比重の増加を抑制し、所望の屈折率を達成し、また高分散化を妨げることなく熱的安定性を維持できる。 In the glass according to the first embodiment, the upper limit of the total content R'O of MgO, CaO, SrO, and BaO is preferably 30%, and more preferably 28%, 25%, and 22% in that order. Further, the lower limit of the total content R'O is preferably 0%, and more preferably 5%, 8%, and 10% in that order. The total content R'O may be 0%. By setting the total content R'O within the above range, an increase in specific gravity can be suppressed, a desired refractive index can be achieved, and thermal stability can be maintained without hindering high dispersion.

第1実施形態に係るガラスにおいて、ZnOの含有量の上限は、好ましくは20%であり、さらには10%、5%、3%の順により好ましい。また、ZnOの含有量の下限は、好ましくは0%である。 In the glass according to the first embodiment, the upper limit of the ZnO content is preferably 20%, and more preferably 10%, 5%, and 3% in that order. Further, the lower limit of the ZnO content is preferably 0%.

ZnOは、ガラスの熱的安定性を改善する働きを有するガラス成分である。しかし、ZnOの含有量が多すぎると比重が上昇する。そのため、ガラスの熱的安定性を改善し、所望の光学恒数を維持する観点から、ZnOの含有量は上記範囲であることが好ましい。 ZnO is a glass component that functions to improve the thermal stability of glass. However, if the ZnO content is too large, the specific gravity will increase. Therefore, from the viewpoint of improving the thermal stability of the glass and maintaining desired optical constants, the content of ZnO is preferably within the above range.

第1実施形態に係る光学ガラスにおいて、Laの含有量の上限は、好ましくは15%であり、さらには14.5%、14%、13.5%の順により好ましい。また、Laの含有量の下限は、好ましくは0%であり、さらには1%、1.5%、2%の順により好ましい。Laの含有量は0%であってもよい。Laの含有量を上記範囲とすることで、所望の光学恒数を実現し、比重の増大を抑えることができ、また部分分散比Pg,Fを低減できる。 In the optical glass according to the first embodiment, the upper limit of the content of La 2 O 3 is preferably 15%, and more preferably 14.5%, 14%, and 13.5% in that order. Further, the lower limit of the content of La 2 O 3 is preferably 0%, and more preferably 1%, 1.5%, and 2% in that order. The content of La 2 O 3 may be 0%. By setting the content of La 2 O 3 within the above range, desired optical constants can be achieved, increase in specific gravity can be suppressed, and partial dispersion ratios Pg and F can be reduced.

第1実施形態に係るガラスにおいて、Yの含有量の上限は、好ましくは20%であり、さらには10%、5%、3%の順により好ましい。また、Yの含有量の下限は、好ましくは0%である。 In the glass according to the first embodiment, the upper limit of the content of Y 2 O 3 is preferably 20%, and more preferably 10%, 5%, and 3% in that order. Moreover, the lower limit of the content of Y 2 O 3 is preferably 0%.

の含有量が多くなり過ぎるとガラスの熱的安定性が低下し、製造中にガラスが失透しやすくなる。したがって、ガラスの熱的安定性の低下を抑制する観点から、Yの含有量は上記範囲であることが好ましい。 If the content of Y 2 O 3 becomes too large, the thermal stability of the glass will decrease, and the glass will be more likely to devitrify during production. Therefore, from the viewpoint of suppressing a decrease in the thermal stability of the glass, the content of Y 2 O 3 is preferably within the above range.

第1実施形態に係るガラスにおいて、Taの含有量の上限は、好ましくは20%であり、さらには10%、5%、3%の順により好ましい。また、Taの含有量の下限は、好ましくは0%である。 In the glass according to the first embodiment, the upper limit of the content of Ta 2 O 5 is preferably 20%, and more preferably 10%, 5%, and 3% in that order. Moreover, the lower limit of the content of Ta 2 O 5 is preferably 0%.

Taは、ガラスの熱的安定性を改善する働きを有するガラス成分であり、部分分散比Pg,Fを低下させる成分である。一方、Taの含有量が多くなると、ガラスの熱的安定性が低下し、ガラスを熔融するときに、ガラス原料の熔け残りが生じやすくなる。また、比重が上昇する。そのため、Taの含有量は上記範囲であることが好ましい。 Ta 2 O 5 is a glass component that has the function of improving the thermal stability of glass, and is a component that reduces the partial dispersion ratio Pg,F. On the other hand, when the content of Ta 2 O 5 increases, the thermal stability of the glass decreases, and unmelted glass raw materials tend to remain when melting the glass. Also, the specific gravity increases. Therefore, the content of Ta 2 O 5 is preferably within the above range.

第1実施形態に係るガラスにおいて、Scの含有量は、好ましくは2%以下である。また、Scの含有量の下限は、好ましくは0%である。 In the glass according to the first embodiment, the content of Sc 2 O 3 is preferably 2% or less. Further, the lower limit of the content of Sc 2 O 3 is preferably 0%.

第1実施形態に係るガラスにおいて、HfOの含有量は、好ましくは2%以下である。また、HfOの含有量の下限は、好ましくは0%である。 In the glass according to the first embodiment, the content of HfO 2 is preferably 2% or less. Further, the lower limit of the content of HfO 2 is preferably 0%.

Sc、HfOは、ガラスの高分散性を高める働きを有するが、高価な成分である。そのため、Sc、HfOの各含有量は上記範囲であることが好ましい。 Sc 2 O 3 and HfO 2 have the function of increasing the high dispersibility of glass, but are expensive components. Therefore, it is preferable that each content of Sc 2 O 3 and HfO 2 is within the above range.

第1実施形態に係るガラスにおいて、Luの含有量は、好ましくは2%以下である。また、Luの含有量の下限は、好ましくは0%である。 In the glass according to the first embodiment, the content of Lu 2 O 3 is preferably 2% or less. Further, the lower limit of the content of Lu 2 O 3 is preferably 0%.

Luは、ガラスの高分散性を高める働きを有するが、分子量が大きいことから、ガラスの比重を増加させるガラス成分でもある。そのため、Luの含有量は上記範囲であることが好ましい。 Lu 2 O 3 has the function of increasing the high dispersibility of glass, but since it has a large molecular weight, it is also a glass component that increases the specific gravity of glass. Therefore, the content of Lu 2 O 3 is preferably within the above range.

第1実施形態に係るガラスにおいて、GeOの含有量は、好ましくは2%以下である。また、GeOの含有量の下限は、好ましくは0%である。 In the glass according to the first embodiment, the GeO 2 content is preferably 2% or less. Further, the lower limit of the content of GeO 2 is preferably 0%.

GeOは、ガラスの高分散性を高める働きを有するが、一般的に使用されるガラス成分の中で、突出して高価な成分である。したがって、ガラスの製造コストの増加を抑制する観点から、GeOの含有量は上記範囲であることが好ましい。 GeO 2 has the function of increasing the high dispersibility of glass, but is by far the most expensive component among commonly used glass components. Therefore, from the viewpoint of suppressing an increase in the manufacturing cost of glass, the content of GeO 2 is preferably within the above range.

第1実施形態に係るガラスにおいて、Gdの含有量は、好ましくは2%以下である。また、Gdの含有量の下限は、好ましくは0%である。 In the glass according to the first embodiment, the content of Gd 2 O 3 is preferably 2% or less. Moreover, the lower limit of the content of Gd 2 O 3 is preferably 0%.

Gdの含有量が多くなり過ぎるとガラスの熱的安定性が低下する。また、Gdの含有量が多くなり過ぎるとガラスの比重が増大する。したがって、ガラスの熱的安定性を良好に維持しつつ、比重の増大を抑制する観点から、Gdの含有量は上記範囲であることが好ましい。 If the content of Gd 2 O 3 becomes too large, the thermal stability of the glass will decrease. Moreover, when the content of Gd 2 O 3 becomes too large, the specific gravity of the glass increases. Therefore, from the viewpoint of suppressing an increase in specific gravity while maintaining good thermal stability of the glass, the content of Gd 2 O 3 is preferably within the above range.

第1実施形態に係るガラスにおいて、Ybの含有量は、好ましくは2%以下である。また、Ybの含有量の下限は、好ましくは0%である。 In the glass according to the first embodiment, the content of Yb 2 O 3 is preferably 2% or less. Further, the lower limit of the content of Yb 2 O 3 is preferably 0%.

Ybは、La、Gd、Yと比べて分子量が大きいため、ガラスの比重を増大させる。ガラスの比重が増大すると、光学素子の質量が増大する。例えば、質量の大きいレンズをオートフォーカス式の撮像レンズに組み込むと、オートフォーカス時にレンズの駆動に要する電力が増大し、電池の消耗が激しくなる。したがって、Ybの含有量を低減させて、ガラスの比重の増大を抑えることが望ましい。 Since Yb 2 O 3 has a larger molecular weight than La 2 O 3 , Gd 2 O 3 , and Y 2 O 3 , it increases the specific gravity of the glass. As the specific gravity of the glass increases, the mass of the optical element increases. For example, if a lens with a large mass is incorporated into an autofocus type imaging lens, the power required to drive the lens during autofocus increases, resulting in rapid battery consumption. Therefore, it is desirable to reduce the content of Yb 2 O 3 to suppress an increase in the specific gravity of the glass.

また、Ybの含有量が多すぎるとガラスの熱的安定性が低下する。ガラスの熱的安定性の低下を防ぎ、比重の増大を抑制する観点から、Ybの含有量は上記範囲であることが好ましい。 Moreover, if the content of Yb 2 O 3 is too large, the thermal stability of the glass will decrease. From the viewpoint of preventing a decrease in the thermal stability of the glass and suppressing an increase in specific gravity, the content of Yb 2 O 3 is preferably within the above range.

第1実施形態に係るガラスは、主として上述のガラス成分、すなわち、必須成分としてSiOおよびNb、任意成分としてTiO、BaO、B、P、Al、ZrO、WO、Bi、LiO、NaO、KO、CsO、MgO、CaO、SrO、ZnO、La、Y、Ta、Sc、HfO、Lu、GeO、GdおよびYbで構成されていることが好ましく、上述のガラス成分の合計含有量は、95%よりも多くすることが好ましく、98%よりも多くすることがより好ましく、99%よりも多くすることがさらに好ましく、99.5%よりも多くすることが一層好ましい。 The glass according to the first embodiment mainly contains the above-mentioned glass components, that is, SiO 2 and Nb 2 O 5 as essential components, and TiO 2 , BaO, B 2 O 3 , P 2 O 5 , and Al 2 O 3 as optional components. , ZrO 2 , WO 3 , Bi 2 O 3 , Li 2 O, Na 2 O, K 2 O, Cs 2 O, MgO, CaO, SrO, ZnO, La 2 O 3 , Y 2 O 3 , Ta 2 O 5 , Sc 2 O 3 , HfO 2 , Lu 2 O 3 , GeO 2 , Gd 2 O 3 and Yb 2 O 3 , the total content of the above-mentioned glass components being more than 95%. It is preferably greater than 98%, even more preferably greater than 99%, and even more preferably greater than 99.5%.

なお、本実施形態に係るガラスは、基本的に上記ガラス成分により構成されることが好ましいが、本発明の作用効果を妨げない範囲において、その他の成分を含有することも可能である。また、本発明において、不可避的不純物の含有を排除するものではない。 Although it is preferable that the glass according to the present embodiment is basically composed of the above-mentioned glass components, it is also possible to contain other components within a range that does not impede the effects of the present invention. Furthermore, the present invention does not exclude the inclusion of unavoidable impurities.

(その他の成分)
上記成分の他に、上記光学ガラスは、清澄剤としてSb、CeO等を少量含有することもできる。清澄剤の総量(外割添加量)は0%以上、1%未満とすることが好ましく、0%以上0.5%以下とすることがより好ましい。
(Other ingredients)
In addition to the above components, the optical glass may also contain a small amount of Sb 2 O 3 , CeO 2 , etc. as a clarifying agent. The total amount of the clarifier (external addition amount) is preferably 0% or more and less than 1%, more preferably 0% or more and 0.5% or less.

外割添加量とは、清澄剤を除く全ガラス成分の合計含有量を100%としたときの清澄剤の添加量を重量百分率で表したものである。 The external addition amount is the addition amount of the fining agent expressed as a weight percentage when the total content of all glass components excluding the fining agent is 100%.

Pb、Cd、As、Th等は、環境負荷が懸念される成分である。そのため、それぞれPbO、CdO、ThOの含有量は、いずれも0~0.1%であることが好ましく、0~0.05%であることがより好ましく、0~0.01%であることが一層好ましく、PbO、CdO、ThOを実質的に含まないことが特に好ましい。 Pb, Cd, As, Th, etc. are components that are concerned about their environmental impact. Therefore, the content of PbO, CdO, and ThO 2 is preferably 0 to 0.1%, more preferably 0 to 0.05%, and 0 to 0.01%. is more preferable, and it is particularly preferable that PbO, CdO, and ThO 2 are substantially not contained.

Asの含有量は、0~0.1%であることが好ましく、0~0.05%であることがより好ましく、0~0.01%であることが一層好ましく、Asを実質的に含まないことが特に好ましい。 The content of As 2 O 3 is preferably 0 to 0.1%, more preferably 0 to 0.05%, and even more preferably 0 to 0.01%. It is particularly preferable that 3 is not substantially contained.

更に、上記光学ガラスは、可視領域の広い範囲にわたり高い透過率が得られる。こうした特長を活かすには、着色性の元素を含まないことが好ましい。着色性の元素としては、Cu、Co、Ni、Fe、Cr、Eu、Nd、Er、V等を例示することができる。いずれの元素とも、100質量ppm未満であることが好ましく、0~80質量ppmであることがより好ましく、0~50質量ppm以下であることが更に好ましく、実質的に含まれないことが特に好ましい。 Furthermore, the above-mentioned optical glass can provide high transmittance over a wide visible range. In order to take advantage of these features, it is preferable not to contain any coloring elements. Examples of coloring elements include Cu, Co, Ni, Fe, Cr, Eu, Nd, Er, and V. The content of any element is preferably less than 100 mass ppm, more preferably 0 to 80 mass ppm, even more preferably 0 to 50 mass ppm or less, and particularly preferably substantially absent. .

また、Ga、Te、Tb等は、導入が不要な成分であり、高価な成分でもある。そのため、質量%表示によるGa、TeO、TbOの含有量の範囲は、いずれも、それぞれ0~0.1%であることが好ましく、0~0.05%であることがより好ましく、0~0.01%であることが更に好ましく、0~0.005%であることが一層好ましく、0~0.001%であることがより一層好ましく、実質的に含まれないことが特に好ましい。 Further, Ga, Te, Tb, etc. are components that do not need to be introduced and are also expensive components. Therefore, the content range of Ga 2 O 3 , TeO 2 , and TbO 2 expressed in mass % is preferably 0 to 0.1%, more preferably 0 to 0.05%. It is preferably 0 to 0.01%, even more preferably 0 to 0.005%, even more preferably 0 to 0.001%, and substantially not contained. Particularly preferred.

(ガラス特性)
<屈折率nd>
第1実施形態に係る光学ガラスにおいて、屈折率ndは1.69~1.87である。屈折率ndは、1.70~1.865、または1.75~1.860とすることもできる。屈折率ndは、SiO、TiO、Nb等の含有量を調整することで制御できる。
(Glass characteristics)
<Refractive index nd>
In the optical glass according to the first embodiment, the refractive index nd is 1.69 to 1.87. The refractive index nd can also be between 1.70 and 1.865, or between 1.75 and 1.860. The refractive index nd can be controlled by adjusting the content of SiO 2 , TiO 2 , Nb 2 O 5 and the like.

<アッベ数νd>
第1実施形態に係る光学ガラスにおいて、アッベ数νdは24~36である。アッベ数νdは、25~35、または26~34とすることもできる。アッベ数νdは、SiO、TiO、Nb等の含有量を調整することで制御できる。
<Abbe number νd>
In the optical glass according to the first embodiment, the Abbe number νd is 24 to 36. The Abbe number νd can also be set to 25 to 35 or 26 to 34. The Abbe number νd can be controlled by adjusting the content of SiO 2 , TiO 2 , Nb 2 O 5 and the like.

<ガラスの比重>
第1実施形態に係る光学ガラスの比重は、好ましくは3.95以下であり、さらには3.80以下、3.70以下、3.67以下、3.65以下の順により好ましい。比重は小さいほど好ましく、その下限は好ましくは2.60である。比重は、SiO、B、LiO、NaO、KO、MgO、CaO、SrO、BaO、ZrO、La、Gd、Nb、TiOの含有量を調整することで制御できる。
<Specific gravity of glass>
The specific gravity of the optical glass according to the first embodiment is preferably 3.95 or less, and more preferably in the order of 3.80 or less, 3.70 or less, 3.67 or less, and 3.65 or less. The lower the specific gravity, the more preferable it is, and the lower limit thereof is preferably 2.60. The specific gravity is SiO 2 , B 2 O 3 , Li 2 O, Na 2 O, K 2 O, MgO, CaO, SrO, BaO, ZrO 2 , La 2 O 3 , Gd 2 O 3 , Nb 2 O 5 , TiO It can be controlled by adjusting the content of 2 .

<部分分散比Pg,F>
第1実施形態に係る光学ガラスの部分分散比Pg,Fの上限は、好ましく0.6095であり、さらには0.6050、0.6030、0.6025、0.6020の順により好ましい。また、部分分散比Pg,Fは小さいほど好ましく、その下限は好ましく0.5800である。部分分散比Pg,Fを上記範囲とすることで、高次の色収差補正に好適な光学ガラスが得られる。
<Partial dispersion ratio Pg, F>
The upper limit of the partial dispersion ratio Pg,F of the optical glass according to the first embodiment is preferably 0.6095, and more preferably in the order of 0.6050, 0.6030, 0.6025, and 0.6020. Further, the smaller the partial dispersion ratio Pg, F is, the more preferable it is, and its lower limit is preferably 0.5800. By setting the partial dispersion ratios Pg and F within the above range, an optical glass suitable for correcting high-order chromatic aberration can be obtained.

また、第1実施形態に係る光学ガラスの部分分散比Pg,Fの偏差ΔPg,Fの上限は、好ましく0.0150であり、さらには0.0100、0.0070、0.0065の順により好ましい。また、偏差ΔPg,Fは小さいほど好ましく、その下限は好ましく-0.0050である。 Further, the upper limit of the deviation ΔPg,F of the partial dispersion ratio Pg,F of the optical glass according to the first embodiment is preferably 0.0150, and more preferably in the order of 0.0100, 0.0070, and 0.0065. . Further, the smaller the deviation ΔPg,F, the better, and its lower limit is preferably -0.0050.

<ガラス転移温度Tg>
第1実施形態に係る光学ガラスのガラス転移温度Tgの上限は、好ましくは740℃であり、さらには700℃、690℃、685℃、680℃の順により好ましい。また、ガラス転移温度Tgの下限は、好ましくは430℃であり、さらには460℃、490℃、520℃の順により好ましい。ガラス転移温度Tgは、LiO、NaO、KO等の含有量を調整することにより制御できる。
<Glass transition temperature Tg>
The upper limit of the glass transition temperature Tg of the optical glass according to the first embodiment is preferably 740°C, and more preferably in the order of 700°C, 690°C, 685°C, and 680°C. Further, the lower limit of the glass transition temperature Tg is preferably 430°C, and more preferably 460°C, 490°C, and 520°C in this order. The glass transition temperature Tg can be controlled by adjusting the content of Li 2 O, Na 2 O, K 2 O, etc.

<ガラスの光線透過性>
第1実施形態に係る光学ガラスの光線透過性は、着色度λ80、λ70およびλ5により評価できる。
厚さ10.0mm±0.1mmのガラス試料について波長200~700nmの範囲で分光透過率を測定し、外部透過率が80%となる波長をλ80、外部透過率が70%となる波長をλ70、外部透過率が5%となる波長をλ5とする。
<Light transmittance of glass>
The light transmittance of the optical glass according to the first embodiment can be evaluated by the degree of coloration λ80, λ70, and λ5.
The spectral transmittance of a glass sample with a thickness of 10.0 mm ± 0.1 mm is measured in the wavelength range of 200 to 700 nm, and the wavelength at which the external transmittance is 80% is λ80, and the wavelength at which the external transmittance is 70% is λ70. , the wavelength at which the external transmittance is 5% is λ5.

第1実施形態に係る光学ガラスのλ80は、好ましくは520nm以下であり、より好ましくは500nm以下であり、さらに好ましくは475nm以下であり、一層好ましくは455nm以下である。また、λ70は、好ましくは500nm以下であり、より好ましくは480nm以下であり、さらに好ましくは465nm以下であり、一層好ましくは450nm以下である。さらに、λ5は、好ましくは390nm以下であり、より好ましくは380nm以下であり、さらに好ましくは370nm以下である。 λ80 of the optical glass according to the first embodiment is preferably 520 nm or less, more preferably 500 nm or less, still more preferably 475 nm or less, and still more preferably 455 nm or less. Further, λ70 is preferably 500 nm or less, more preferably 480 nm or less, still more preferably 465 nm or less, and still more preferably 450 nm or less. Furthermore, λ5 is preferably 390 nm or less, more preferably 380 nm or less, and even more preferably 370 nm or less.

(光学ガラスの製造)
第1実施形態に係る光学ガラスは、上記所定の組成となるようにガラス原料を調合し、調合したガラス原料により公知のガラス製造方法に従って作製すればよい。例えば、複数種の化合物を調合し、十分混合してバッチ原料とし、バッチ原料を石英坩堝や白金坩堝中に入れて粗熔解(ラフメルト)する。粗熔解によって得られた熔融物を急冷、粉砕してカレットを作製する。さらにカレットを白金坩堝中に入れて加熱、再熔融(リメルト)して熔融ガラスとし、さらに清澄、均質化した後に熔融ガラスを成形し、徐冷して光学ガラスを得る。熔融ガラスの成形、徐冷には、公知の方法を適用すればよい。
(manufacture of optical glass)
The optical glass according to the first embodiment may be produced by blending glass raw materials to have the above-mentioned predetermined composition, and using the blended glass raw materials according to a known glass manufacturing method. For example, a plurality of compounds are prepared and sufficiently mixed to form a batch raw material, and the batch raw material is put into a quartz crucible or a platinum crucible and roughly melted (rough melted). The molten material obtained by rough melting is rapidly cooled and pulverized to produce cullet. Further, the cullet is placed in a platinum crucible, heated and remelted to obtain molten glass, and after further clarification and homogenization, the molten glass is shaped and slowly cooled to obtain optical glass. A known method may be applied to forming and slowly cooling the molten glass.

なお、ガラス中に所望のガラス成分を所望の含有量となるように導入することができれば、バッチ原料を調合するときに使用する化合物は特に限定されないが、このような化合物として、酸化物、炭酸塩、硝酸塩、水酸化物、フッ化物等が挙げられる。 Note that the compounds used when preparing the batch raw materials are not particularly limited as long as the desired glass components can be introduced into the glass at the desired content, but examples of such compounds include oxides, carbonates, etc. Examples include salts, nitrates, hydroxides, fluorides, and the like.

(光学素子等の製造)
第1実施形態に係る光学ガラスを使用して光学素子を作製するには、公知の方法を適用すればよい。例えば、上記光学ガラスの製造において、熔融ガラスを鋳型に流し込んで板状に成形し、本発明に係る光学ガラスからなるガラス素材を作製する。得られたガラス素材を適宜、切断、研削、研磨し、プレス成形に適した大きさ、形状のカットピースを作製する。カットピースを加熱、軟化して、公知の方法でプレス成形(リヒートプレス)し、光学素子の形状に近似する光学素子ブランクを作製する。光学素子ブランクをアニールし、公知の方法で研削、研磨して光学素子を作製する。
(Manufacture of optical elements, etc.)
In order to produce an optical element using the optical glass according to the first embodiment, a known method may be applied. For example, in the production of the optical glass described above, molten glass is poured into a mold and formed into a plate shape to produce a glass material made of the optical glass according to the present invention. The obtained glass material is appropriately cut, ground, and polished to produce cut pieces of a size and shape suitable for press molding. The cut piece is heated and softened, and then press-molded (reheat-pressed) by a known method to produce an optical element blank that approximates the shape of the optical element. An optical element blank is annealed, ground and polished by a known method to produce an optical element.

作製した光学素子の光学機能面には使用目的に応じて、反射防止膜、全反射膜などをコーティングしてもよい。 The optically functional surface of the manufactured optical element may be coated with an antireflection film, a total reflection film, etc. depending on the purpose of use.

本発明の一態様によれば、上記光学ガラスからなる光学素子を提供することができる。光学素子の種類としては、球面レンズ、非球面レンズ等のレンズ、プリズム、回折格子等を例示することができる。レンズの形状としては、両凸レンズ、平凸レンズ、両凹レンズ、平凹レンズ、凸メニスカスレンズ、凹メニスカスレンズ等の諸形状を例示することができる。光学素子は、上記光学ガラスからなるガラス成形体を加工する工程を含む方法により製造することができる。加工としては、切断、切削、粗研削、精研削、研磨等を例示することができる。こうした加工を行う際、上記ガラスを使用することにより、破損を軽減することができ、高品質の光学素子を安定して供給することができる。 According to one aspect of the present invention, an optical element made of the optical glass described above can be provided. Examples of the types of optical elements include lenses such as spherical lenses and aspheric lenses, prisms, and diffraction gratings. Examples of the shape of the lens include various shapes such as a biconvex lens, a plano-convex lens, a biconcave lens, a plano-concave lens, a convex meniscus lens, and a concave meniscus lens. The optical element can be manufactured by a method including a process of processing a glass molded body made of the optical glass. Examples of processing include cutting, cutting, rough grinding, fine grinding, and polishing. By using the above-mentioned glass during such processing, breakage can be reduced and high-quality optical elements can be stably supplied.

第2実施形態
第2実施形態に係る光学ガラスは、
屈折率ndが1.69~1.87、アッベ数νdが24~36であって、
SiOの含有量が10~50質量%であり、
TiOの含有量が40質量%以下であり、
Nbの含有量が5~60質量%であり、
BaOの含有量が10質量%以下であり、
La、Y、Gd、YbおよびLuの合計含有量が13.5質量%以下であり、
NbおよびTiOの合計含有量に対するNbの含有量の質量比[Nb/(Nb+TiO)]が0.6以下であり、
LiO、NaOおよびKOの合計含有量ROおよびMgO、CaO、SrOおよびBaOの合計含有量R’Oの合計含有量に対するNaOの含有量の質量比[NaO/(RO+R’O)]が0より大きく、
上記合計含有量ROおよび上記合計含有量R’Oの合計含有量に対するCaOの含有量の質量比[CaO/(RO+R’O)]が0.1以上であり、
上記合計含有量R’Oに対するMgOおよびCaOの合計含有量の質量比[(MgO+CaO)/R’O]が0.44~1.0である。
Second Embodiment The optical glass according to the second embodiment is
The refractive index nd is 1.69 to 1.87, the Abbe number νd is 24 to 36,
The content of SiO 2 is 10 to 50% by mass,
The content of TiO 2 is 40% by mass or less,
The content of Nb 2 O 5 is 5 to 60% by mass,
The content of BaO is 10% by mass or less,
The total content of La 2 O 3 , Y 2 O 3 , Gd 2 O 3 , Yb 2 O 3 and Lu 2 O 3 is 13.5% by mass or less,
The mass ratio of the content of Nb 2 O 5 to the total content of Nb 2 O 5 and TiO 2 [Nb 2 O 5 /(Nb 2 O 5 +TiO 2 )] is 0.6 or less,
Total content of Li 2 O, Na 2 O and K 2 O Total content of R 2 O and MgO, CaO, SrO and BaO Mass ratio of the content of Na 2 O to the total content of R'O [Na 2 O/(R 2 O+R'O)] is greater than 0,
The mass ratio [CaO/(R 2 O + R'O)] of the content of CaO to the total content of the total content R 2 O and the total content R'O is 0.1 or more,
The mass ratio of the total content of MgO and CaO to the above-mentioned total content R'O [(MgO+CaO)/R'O] is 0.44 to 1.0.

第2実施形態に係る光学ガラスにおいて、SiOの含有量は10~50%である。SiOの含有量の下限は、好ましくは12%であり、さらには15%、17%、20%の順により好ましい。また、SiOの含有量の上限は、好ましくは45%であり、さらには40%、37%、35%の順により好ましい。 In the optical glass according to the second embodiment, the content of SiO 2 is 10 to 50%. The lower limit of the SiO 2 content is preferably 12%, and more preferably 15%, 17%, and 20% in this order. Further, the upper limit of the content of SiO 2 is preferably 45%, and more preferably 40%, 37%, and 35% in that order.

第2実施形態に係る光学ガラスにおいて、TiOの含有量は40%以下である。TiOの含有量の上限は、好ましくは35%であり、さらには30%、28%、25%の順により好ましい。TiOの含有量の下限は、好ましくは0%であり、さらには5%、8%、10%の順により好ましい。TiOの含有量は0%でもよい。 In the optical glass according to the second embodiment, the content of TiO 2 is 40% or less. The upper limit of the TiO 2 content is preferably 35%, and more preferably 30%, 28%, and 25% in that order. The lower limit of the content of TiO 2 is preferably 0%, and more preferably 5%, 8%, and 10% in that order. The content of TiO 2 may be 0%.

第2実施形態に係る光学ガラスにおいて、Nbの含有量は5~60%である。Nbの含有量の下限は、好ましくは7%であり、さらには8%、9%、10%の順により好ましい。また、Nbの含有量の上限は、好ましくは45%であり、さらには40%、35%、30%の順により好ましい。 In the optical glass according to the second embodiment, the content of Nb 2 O 5 is 5 to 60%. The lower limit of the content of Nb 2 O 5 is preferably 7%, and more preferably 8%, 9%, and 10% in that order. Further, the upper limit of the content of Nb 2 O 5 is preferably 45%, and more preferably 40%, 35%, and 30% in that order.

第2実施形態に係る光学ガラスにおいて、BaOの含有量は10%以下である。BaOの含有量の上限は、好ましくは9%であり、さらには8%、7%の順により好ましい。BaOの含有量の下限は、好ましくは0%であり、さらには1%、2%、3%、3.5%の順により好ましい。BaOの含有量は0%でもよい。 In the optical glass according to the second embodiment, the BaO content is 10% or less. The upper limit of the BaO content is preferably 9%, more preferably 8% and then 7%. The lower limit of the BaO content is preferably 0%, and more preferably 1%, 2%, 3%, and 3.5% in this order. The content of BaO may be 0%.

第2実施形態に係る光学ガラスにおいて、La、Y、Gd、YbおよびLuの合計含有量[La+Y+Gd+Yb+Lu]は13.5%以下である。合計含有量[La+Y+Gd+Yb+Lu]の上限は、好ましくは12%であり、さらには11%、10%、9%の順により好ましい。また、合計含有量[La+Y+Gd+Yb+Lu]の下限は、好ましくは0%であり、さらには0.5%、1%、1.5%の順により好ましい。 In the optical glass according to the second embodiment, the total content of La 2 O 3 , Y 2 O 3 , Gd 2 O 3 , Yb 2 O 3 and Lu 2 O 3 [La 2 O 3 +Y 2 O 3 +Gd 2 O 3 +Yb 2 O 3 +Lu 2 O 3 ] is 13.5% or less. The upper limit of the total content [La 2 O 3 + Y 2 O 3 + Gd 2 O 3 + Yb 2 O 3 + Lu 2 O 3 ] is preferably 12%, and more preferably in the order of 11%, 10%, and 9%. . Further, the lower limit of the total content [La 2 O 3 +Y 2 O 3 +Gd 2 O 3 +Yb 2 O 3 +Lu 2 O 3 ] is preferably 0%, more preferably 0.5%, 1%, 1. The order of 5% is more preferable.

第2実施形態に係る光学ガラスにおいて、NbおよびTiOの合計含有量に対するNbの含有量の質量比[Nb/(Nb+TiO)]は0.6以下である。質量比[Nb/(Nb+TiO)]上限は、好ましくは0.60であり、さらには0.55、0.52、0.50の順により好ましい。また、質量比[Nb/(Nb+TiO)]は、好ましくは0より大きく、その下限は0.10、0.20、0.30の順により好ましい。 In the optical glass according to the second embodiment, the mass ratio of the content of Nb 2 O 5 to the total content of Nb 2 O 5 and TiO 2 [Nb 2 O 5 /(Nb 2 O 5 +TiO 2 )] is 0. 6 or less. The upper limit of the mass ratio [Nb 2 O 5 /(Nb 2 O 5 +TiO 2 )] is preferably 0.60, and more preferably in the order of 0.55, 0.52, and 0.50. Further, the mass ratio [Nb 2 O 5 /(Nb 2 O 5 +TiO 2 )] is preferably larger than 0, and its lower limit is preferably in the order of 0.10, 0.20, and 0.30.

第2実施形態に係る光学ガラスにおいて、LiO、NaOおよびKOの合計含有量ROおよびMgO、CaO、SrOおよびBaOの合計含有量R’Oの合計含有量に対するNaOの含有量の質量比[NaO/(RO+R’O)]は、0より大きい。く、質量比[NaO/(RO+R’O)]の下限は、好ましくは0.1であり、さらには0.13、0.15の順により好ましい。質量比[NaO/(RO+R’O)]の上限は、好ましくは0.8であり、さらには0.7、0.6、0.5の順により好ましい。
質量比[NaO/(RO+R’O)]が小さすぎると、ガラスの熔解性が低下するおそれがある。質量比[NaO/(RO+R’O)]が大きすぎると、熱的安定性が低下するおそれがある。
In the optical glass according to the second embodiment, the total content R2O of Li2O , Na2O and K2O and the total content R'O of MgO, CaO, SrO and BaO, Na2 The mass ratio of O content [Na 2 O/(R 2 O+R'O)] is greater than 0. The lower limit of the mass ratio [Na 2 O/(R 2 O+R'O)] is preferably 0.1, and more preferably 0.13 and 0.15. The upper limit of the mass ratio [Na 2 O/(R 2 O+R'O)] is preferably 0.8, and more preferably in the order of 0.7, 0.6, and 0.5.
If the mass ratio [Na 2 O/(R 2 O+R'O)] is too small, the solubility of the glass may decrease. If the mass ratio [Na 2 O/(R 2 O+R'O)] is too large, thermal stability may decrease.

第2実施形態に係る光学ガラスにおいて、上記合計含有量ROおよび上記合計含有量R’Oの合計含有量に対するCaOの含有量の質量比[CaO/(RO+R’O)]は、0.1以上である。質量比[CaO/(RO+R’O)]の下限は、好ましくは0.15であり、さらには0.18、0.2の順により好ましい。質量比[CaO/(RO+R’O)]の上限は、好ましくは0.95であり、さらには0.90、0.87、0.85の順により好ましい。
質量比[CaO/(RO+R’O)]が小さすぎると、屈折率が低下し、比重が増加するおそれがある。質量比[CaO/(RO+R’O)]が大きすぎると、熱的安定性が低下するおそれがある。
In the optical glass according to the second embodiment, the mass ratio of the CaO content to the total content of the total content R 2 O and the total content R′O [CaO/(R 2 O+R′O)] is It is 0.1 or more. The lower limit of the mass ratio [CaO/(R 2 O+R'O)] is preferably 0.15, and more preferably 0.18 and 0.2 in that order. The upper limit of the mass ratio [CaO/(R 2 O+R'O)] is preferably 0.95, and more preferably in the order of 0.90, 0.87, and 0.85.
If the mass ratio [CaO/(R 2 O+R'O)] is too small, the refractive index may decrease and the specific gravity may increase. If the mass ratio [CaO/(R 2 O+R'O)] is too large, thermal stability may decrease.

第2実施形態に係る光学ガラスにおいて、MgO、CaO、SrOおよびBaOの合計含有量R’Oに対するMgOおよびCaOの合計含有量の質量比[(MgO+CaO)/R’O]は0.44~1.0である。質量比[(MgO+CaO)/R’O]の下限は、好ましくは0.5であり、さらには0.55、0.6の順により好ましい。また、質量比[(MgO+CaO)/R’O]の上限は、好ましくは0.9であり、さらには0.85、0.8、0.78の順により好ましい。 In the optical glass according to the second embodiment, the mass ratio [(MgO+CaO)/R'O] of the total content of MgO and CaO to the total content R'O of MgO, CaO, SrO , and BaO is 0.44 to 1. .0. The lower limit of the mass ratio [(MgO+CaO)/R'O] is preferably 0.5, and more preferably 0.55 and 0.6 in that order. Further, the upper limit of the mass ratio [(MgO+CaO)/R'O] is preferably 0.9, and more preferably 0.85, 0.8, and 0.78 in this order.

次に、第2実施形態に係る光学ガラスにおける、ガラス成分の含有量および比率の好ましい態様を以下に詳述する。 Next, preferred aspects of the contents and ratios of glass components in the optical glass according to the second embodiment will be described in detail below.

第2実施形態に係る光学ガラスは、好ましくは、LiO、NaOおよびKOからなる群から選択される1以上のガラス成分を含み、より好ましくはNaOを含み、さらに好ましくはLiO、NaOおよびKOを含む。
光学ガラスが、LiO、NaOおよびKOからなる群から選択される1以上のガラス成分を含むことで、ガラスの溶解性を高めることができる。
The optical glass according to the second embodiment preferably contains one or more glass components selected from the group consisting of Li 2 O, Na 2 O and K 2 O, more preferably Na 2 O, and still more preferably includes Li 2 O, Na 2 O and K 2 O.
When the optical glass contains one or more glass components selected from the group consisting of Li 2 O, Na 2 O and K 2 O, the solubility of the glass can be improved.

第2実施形態に係る光学ガラスは、好ましくは、MgO、CaO、SrOおよびBaOのからなる群から選択される1以上のガラス成分を含み、より好ましくはCaOを含み、さらに好ましくはCaOおよびBaOを含む。
光学ガラスが、MgO、CaO、SrOおよびBaOのからなる群から選択される1以上のガラス成分を含むことで、屈折率ndの低下を抑制できる。
The optical glass according to the second embodiment preferably contains one or more glass components selected from the group consisting of MgO, CaO, SrO, and BaO, more preferably contains CaO, and still more preferably contains CaO and BaO. include.
When the optical glass contains one or more glass components selected from the group consisting of MgO, CaO, SrO, and BaO, a decrease in the refractive index nd can be suppressed.

第2実施形態に係る光学ガラスにおいて、MgO、CaO、SrOおよびBaOの合計含有量R’Oに対するCaOの含有量の質量比(CaO/R’O)と、LiO、NaOおよびKOの合計含有量ROに対するNaOの含有量の質量比(NaO/RO)との合計[(CaO/R’O)+(NaO/RO)]は、好ましくは1.1より大きく、その下限は、1.2、1.3、1.35、1.4の順により好ましい。[(CaO/R’O)+(NaO/RO)]の上限は、好ましくは1.9であり、さらには1.85、1.8の順により好ましい。 In the optical glass according to the second embodiment, the mass ratio of the content of CaO to the total content R'O of MgO, CaO, SrO , and BaO (CaO/R'O), and the mass ratio of the content of CaO to the total content R'O of Li 2 O, Na 2 O, and K The sum of the mass ratio of the Na 2 O content to the total 2 O content R 2 O (Na 2 O/R 2 O) [(CaO/R'O) + (Na 2 O/R 2 O)] is preferably larger than 1.1, and its lower limit is preferably in the order of 1.2, 1.3, 1.35, and 1.4. The upper limit of [(CaO/R'O)+(Na 2 O/R 2 O)] is preferably 1.9, and more preferably 1.85 and 1.8 in that order.

第2実施形態に係る光学ガラスにおいて、MgO、CaO、SrOおよびBaOの合計含有量R’OとLiO、NaOおよびKOの合計含有量ROとの合計含有量に対する合計含有量R’Oの質量比[R’O/(R’O+RO)]の下限は、好ましくは0.50、さらには0.55、0.60、0.65の順により好ましい。また、質量比[R’O/(R’O+RO)]の上限は、好ましくは0.99、さらには0.98、0.97の順により好ましい。 In the optical glass according to the second embodiment, the sum of the total content R'O of MgO, CaO, SrO and BaO and the total content R 2 O of Li 2 O, Na 2 O and K 2 O The lower limit of the mass ratio [R'O/(R'O+R 2 O)] of the content R'O is preferably 0.50, and more preferably in the order of 0.55, 0.60, and 0.65. Further, the upper limit of the mass ratio [R'O/(R'O+R 2 O)] is preferably 0.99, and more preferably 0.98 and 0.97 in that order.

第2実施形態に係る光学ガラスにおいて、NbおよびTiOの合計含有量[Nb+TiO]の下限は、好ましくは5%であり、さらには20%、22%、24%、25%の順により好ましい。また、合計含有量[Nb+TiO]の上限は、好ましくは60%であり、さらには50%、45%、40%の順により好ましい。 In the optical glass according to the second embodiment, the lower limit of the total content of Nb 2 O 5 and TiO 2 [Nb 2 O 5 +TiO 2 ] is preferably 5%, and more preferably 20%, 22%, and 24%. , 25% are more preferred. Further, the upper limit of the total content [Nb 2 O 5 +TiO 2 ] is preferably 60%, and more preferably 50%, 45%, and 40% in that order.

第2実施形態に係る光学ガラスにおいて、Bの含有量の上限は、好ましくは5%であり、さらには4.5%、4.2%、4%の順により好ましい。また、Bの含有量の下限は、好ましくは0%であり、さらには0.5%、0.7%、1%の順により好ましい。Bの含有量は0%であってもよい。 In the optical glass according to the second embodiment, the upper limit of the content of B 2 O 3 is preferably 5%, and more preferably 4.5%, 4.2%, and 4% in that order. Further, the lower limit of the content of B 2 O 3 is preferably 0%, and more preferably 0.5%, 0.7%, and 1% in that order. The content of B 2 O 3 may be 0%.

第2実施形態に係る光学ガラスにおいて、上記以外のガラス成分の含有量および比率については、第1実施形態と同様とすることができる。また、第2実施形態におけるガラス特性、光学ガラスの製造および光学素子等の製造についても、第1実施形態と同様とすることができる。 In the optical glass according to the second embodiment, the contents and ratios of glass components other than those described above can be the same as in the first embodiment. Further, the glass properties, the production of optical glass, the production of optical elements, etc. in the second embodiment can be the same as in the first embodiment.

第3実施形態
第3実施形態に係る光学ガラスは、
屈折率ndが1.69~1.87、アッベ数νdが24~36であって、
SiOの含有量が10~50質量%であり、
TiOの含有量が40質量%以下であり、
Nbの含有量が5~60質量%であり、
BaOの含有量が10質量%以下であり、
La、Y、Gd、YbおよびLuの合計含有量が13.5質量%以下であり、
NbおよびTiOの合計含有量が30質量%以上であり、
NbおよびTiOの合計含有量に対するNbの含有量の質量比[Nb/(Nb+TiO)]が0.7以下であり、
LiO、NaOおよびKOの合計含有量ROおよびMgO、CaO、SrOおよびBaOの合計含有量R’Oの合計含有量に対する上記合計含有量R’Oの質量比[R’O/(RO+R’O)]が0.7~1.0であり、
上記合計含有量R’Oに対するMgOおよびCaOの合計含有量の質量比[(MgO+CaO)/R’O]が0.26~1.0である。
Third Embodiment The optical glass according to the third embodiment is
The refractive index nd is 1.69 to 1.87, the Abbe number νd is 24 to 36,
The content of SiO 2 is 10 to 50% by mass,
The content of TiO 2 is 40% by mass or less,
The content of Nb 2 O 5 is 5 to 60% by mass,
The content of BaO is 10% by mass or less,
The total content of La 2 O 3 , Y 2 O 3 , Gd 2 O 3 , Yb 2 O 3 and Lu 2 O 3 is 13.5% by mass or less,
The total content of Nb 2 O 5 and TiO 2 is 30% by mass or more,
The mass ratio of the content of Nb 2 O 5 to the total content of Nb 2 O 5 and TiO 2 [Nb 2 O 5 /(Nb 2 O 5 +TiO 2 )] is 0.7 or less,
The mass ratio [ R 'O/(R 2 O + R'O)] is 0.7 to 1.0,
The mass ratio of the total content of MgO and CaO to the total content R'O [(MgO+CaO)/R'O] is 0.26 to 1.0.

第3実施形態に係る光学ガラスにおいて、SiOの含有量は10~50%である。SiOの含有量の下限は、好ましくは12%であり、さらには15%、17%、20%の順により好ましい。また、SiOの含有量の上限は、好ましくは45%であり、さらには40%、37%、35%の順により好ましい。 In the optical glass according to the third embodiment, the content of SiO 2 is 10 to 50%. The lower limit of the SiO 2 content is preferably 12%, and more preferably 15%, 17%, and 20% in that order. Further, the upper limit of the content of SiO 2 is preferably 45%, and more preferably 40%, 37%, and 35% in that order.

第3実施形態に係る光学ガラスにおいて、TiOの含有量は40%以下である。TiOの含有量の上限は、好ましくは35%であり、さらには30%、28%、25%の順により好ましい。TiOの含有量の下限は、好ましくは0%であり、さらには5%、8%、10%の順により好ましい。TiOの含有量は0%でもよい。 In the optical glass according to the third embodiment, the content of TiO 2 is 40% or less. The upper limit of the TiO 2 content is preferably 35%, and more preferably 30%, 28%, and 25% in that order. The lower limit of the content of TiO 2 is preferably 0%, and more preferably 5%, 8%, and 10% in that order. The content of TiO 2 may be 0%.

第3実施形態に係る光学ガラスにおいて、Nbの含有量は5~60%である。Nbの含有量の下限は、好ましくは7%であり、さらには8%、9%、10%の順により好ましい。また、Nbの含有量の上限は、好ましくは45%であり、さらには40%、35%、30%の順により好ましい。 In the optical glass according to the third embodiment, the content of Nb 2 O 5 is 5 to 60%. The lower limit of the content of Nb 2 O 5 is preferably 7%, and more preferably 8%, 9%, and 10% in that order. Further, the upper limit of the content of Nb 2 O 5 is preferably 45%, and more preferably 40%, 35%, and 30% in that order.

第3実施形態に係る光学ガラスにおいて、BaOの含有量は10%以下である。BaOの含有量の上限は、好ましくは9%であり、さらには8%、7%の順により好ましい。BaOの含有量の下限は、好ましくは0%であり、さらには1%、2%、3%、3.5%の順により好ましい。BaOの含有量は0%でもよい。 In the optical glass according to the third embodiment, the BaO content is 10% or less. The upper limit of the BaO content is preferably 9%, more preferably 8% and then 7%. The lower limit of the BaO content is preferably 0%, and more preferably 1%, 2%, 3%, and 3.5% in that order. The content of BaO may be 0%.

第3実施形態に係る光学ガラスにおいて、La、Y、Gd、YbおよびLuの合計含有量[La+Y+Gd+Yb+Lu]は13.5%以下である。合計含有量[La+Y+Gd+Yb+Lu]の上限は、好ましくは12%であり、さらには11%、10%、9%の順により好ましい。また、合計含有量[La+Y+Gd+Yb+Lu]の下限は、好ましくは0%であり、さらには0.5%、1%、1.5%の順により好ましい。 In the optical glass according to the third embodiment, the total content of La 2 O 3 , Y 2 O 3 , Gd 2 O 3 , Yb 2 O 3 and Lu 2 O 3 [La 2 O 3 +Y 2 O 3 +Gd 2 O 3 +Yb 2 O 3 +Lu 2 O 3 ] is 13.5% or less. The upper limit of the total content [La 2 O 3 + Y 2 O 3 + Gd 2 O 3 + Yb 2 O 3 + Lu 2 O 3 ] is preferably 12%, and more preferably in the order of 11%, 10%, and 9%. . Further, the lower limit of the total content [La 2 O 3 +Y 2 O 3 +Gd 2 O 3 +Yb 2 O 3 +Lu 2 O 3 ] is preferably 0%, more preferably 0.5%, 1%, 1. The order of 5% is more preferable.

第3実施形態に係る光学ガラスにおいて、NbおよびTiOの合計含有量[Nb+TiO]は30%以上である。合計含有量[Nb+TiO]の下限は、好ましくは30.05%であり、さらには30.1%、30.15%、30.2%の順により好ましい。また、合計含有量[Nb+TiO]の上限は、好ましくは60%であり、さらには50%、45%、40%の順により好ましい。
合計含有量[Nb+TiO]を上記範囲とすることで、所望の光学恒数を有する光学ガラスが得られる。
In the optical glass according to the third embodiment, the total content of Nb 2 O 5 and TiO 2 [Nb 2 O 5 +TiO 2 ] is 30% or more. The lower limit of the total content [Nb 2 O 5 +TiO 2 ] is preferably 30.05%, and more preferably in the order of 30.1%, 30.15%, and 30.2%. Further, the upper limit of the total content [Nb 2 O 5 +TiO 2 ] is preferably 60%, and more preferably 50%, 45%, and 40% in that order.
By setting the total content [Nb 2 O 5 +TiO 2 ] within the above range, an optical glass having desired optical constants can be obtained.

第3実施形態に係る光学ガラスにおいて、NbおよびTiOの合計含有量に対するNbの含有量の質量比[Nb/(Nb+TiO)]は0.7以下である。質量比[Nb/(Nb+TiO)]上限は、好ましくは0.70、であり、さらには0.65、0.60、0.55、0.50の順により好ましい。また、質量比[Nb/(Nb+TiO)]は、好ましくは0より大きく、その下限は0.10、0.20、0.30の順により好ましい。 In the optical glass according to the third embodiment, the mass ratio of the content of Nb 2 O 5 to the total content of Nb 2 O 5 and TiO 2 [Nb 2 O 5 /(Nb 2 O 5 +TiO 2 )] is 0. 7 or less. The upper limit of the mass ratio [Nb 2 O 5 /(Nb 2 O 5 +TiO 2 )] is preferably 0.70, and more preferably in the order of 0.65, 0.60, 0.55, and 0.50. . Further, the mass ratio [Nb 2 O 5 /(Nb 2 O 5 +TiO 2 )] is preferably larger than 0, and its lower limit is preferably in the order of 0.10, 0.20, and 0.30.

第3実施形態に係る光学ガラスにおいて、MgO、CaO、SrOおよびBaOの合計含有量R’OとLiO、NaOおよびKOの合計含有量ROとの合計含有量に対する合計含有量R’Oの質量比[R’O/(R’O+RO)]は0.7~1.0である。質量比[R’O/(R’O+RO)]の下限は、好ましくは0.71、さらには0.72、0.73、0.74の順により好ましい。また、質量比[R’O/(R’O+RO)]の上限は、好ましくは0.99、さらには0.98、0.97の順により好ましい。
質量比[R’O/(R’O+RO)]が小さすぎると、屈折率ndが低下するおそれがある。質量比[R’O/(R’O+RO)]が大きすぎると、熱的安定性および熔解性が低下し、低分散化し、また比重が上昇するおそれがある。質量比[R’O/(R’O+RO)]を上記範囲とすることで、高屈折率の光学ガラスを得ることができる。
In the optical glass according to the third embodiment, the sum of the total content R'O of MgO, CaO, SrO and BaO and the total content R 2 O of Li 2 O, Na 2 O and K 2 O The mass ratio of the content R'O [R'O/(R'O+R 2 O)] is 0.7 to 1.0. The lower limit of the mass ratio [R'O/(R'O+R 2 O)] is preferably 0.71, and more preferably in the order of 0.72, 0.73, and 0.74. Further, the upper limit of the mass ratio [R'O/(R'O+R 2 O)] is preferably 0.99, and more preferably 0.98 and 0.97 in that order.
If the mass ratio [R'O/(R'O+R 2 O)] is too small, the refractive index nd may decrease. If the mass ratio [R'O/(R'O+R 2 O)] is too large, the thermal stability and solubility may decrease, the dispersion may become low, and the specific gravity may increase. By setting the mass ratio [R'O/(R'O+R 2 O)] within the above range, an optical glass with a high refractive index can be obtained.

第3実施形態に係る光学ガラスにおいて、MgO、CaO、SrOおよびBaOの合計含有量R’Oに対するMgOおよびCaOの合計含有量の質量比[(MgO+CaO)/R’O]は0.26~1.0である。質量比[(MgO+CaO)/R’O]の下限は、好ましくは0.35であり、さらには0.4、0.45、0.5の順により好ましい。また、質量比[(MgO+CaO)/R’O]の上限は、好ましくは0.98であり、さらには0.96、0.94、0.92の順により好ましい。
質量比[(MgO+CaO)/R’O]が小さすぎると、比重が増大するおそれがある。質量比[(MgO+CaO)/R’O]が大きすぎると、熱的安定性が低下するおそれがある。質量比[(MgO+CaO)/R’O]を上記範囲とすることで、比重が低減された光学ガラスを得ることができる。
In the optical glass according to the third embodiment, the mass ratio [(MgO+CaO)/R'O] of the total content of MgO and CaO to the total content R'O of MgO, CaO, SrO , and BaO is 0.26 to 1. .0. The lower limit of the mass ratio [(MgO+CaO)/R'O] is preferably 0.35, and more preferably in the order of 0.4, 0.45, and 0.5. Further, the upper limit of the mass ratio [(MgO+CaO)/R'O] is preferably 0.98, and more preferably in the order of 0.96, 0.94, and 0.92.
If the mass ratio [(MgO+CaO)/R'O] is too small, the specific gravity may increase. If the mass ratio [(MgO+CaO)/R'O] is too large, thermal stability may decrease. By setting the mass ratio [(MgO+CaO)/R'O] within the above range, an optical glass with reduced specific gravity can be obtained.

次に、第3実施形態に係る光学ガラスにおける、ガラス成分の含有量および比率の好ましい態様を以下に詳述する。 Next, preferred aspects of the contents and ratios of glass components in the optical glass according to the third embodiment will be described in detail below.

第3実施形態に係る光学ガラスは、好ましくは、LiO、NaOおよびKOからなる群から選択される1以上のガラス成分を含み、より好ましくはNaOを含み、さらに好ましくはLiO、NaOおよびKOを含む。
光学ガラスが、LiO、NaOおよびKOからなる群から選択される1以上のガラス成分を含むことで、ガラスの溶解性を高めることができる。
The optical glass according to the third embodiment preferably contains one or more glass components selected from the group consisting of Li 2 O, Na 2 O and K 2 O, more preferably Na 2 O, and still more preferably includes Li 2 O, Na 2 O and K 2 O.
When the optical glass contains one or more glass components selected from the group consisting of Li 2 O, Na 2 O and K 2 O, the solubility of the glass can be improved.

第3実施形態に係る光学ガラスは、好ましくは、MgO、CaO、SrOおよびBaOのからなる群から選択される1以上のガラス成分を含み、より好ましくはCaOを含み、さらに好ましくはCaOおよびBaOを含む。
光学ガラスが、MgO、CaO、SrOおよびBaOのからなる群から選択される1以上のガラス成分を含むことで、屈折率ndの低下を抑制できる。
The optical glass according to the third embodiment preferably contains one or more glass components selected from the group consisting of MgO, CaO, SrO, and BaO, more preferably contains CaO, and still more preferably contains CaO and BaO. include.
When the optical glass contains one or more glass components selected from the group consisting of MgO, CaO, SrO, and BaO, a decrease in the refractive index nd can be suppressed.

第3実施形態に係る光学ガラスにおいて、MgO、CaO、SrOおよびBaOの合計含有量R’Oに対するCaOの含有量の質量比(CaO/R’O)と、LiO、NaOおよびKOの合計含有量ROに対するNaOの含有量の質量比(NaO/RO)との合計[(CaO/R’O)+(NaO/RO)]は、好ましくは1.1より大きく、その下限は1.2、1.3、1.35、1.4の順により好ましい。[(CaO/R’O)+(NaO/RO)]の上限は、好ましくは1.9であり、さらには1.85、1.8の順により好ましい。 In the optical glass according to the third embodiment, the mass ratio of the content of CaO to the total content R'O of MgO, CaO, SrO , and BaO (CaO/R'O), and the mass ratio of the content of CaO to the total content R'O of Li 2 O, Na 2 O, and K The sum of the mass ratio of the Na 2 O content to the total 2 O content R 2 O (Na 2 O/R 2 O) [(CaO/R'O) + (Na 2 O/R 2 O)] is preferably larger than 1.1, and its lower limit is preferably in the order of 1.2, 1.3, 1.35, and 1.4. The upper limit of [(CaO/R'O)+(Na 2 O/R 2 O)] is preferably 1.9, and more preferably 1.85 and 1.8 in that order.

第3実施形態に係る光学ガラスにおいて、LiO、NaOおよびKOの合計含有量ROおよびMgO、CaO、SrOおよびBaOの合計含有量R’Oの合計含有量に対するNaOの含有量の質量比[NaO/(RO+R’O)]は、好ましくは0より大きく、その下限は、0.1、0.13、0.15の順により好ましい。質量比[NaO/(RO+R’O)]の上限は、好ましくは0.8であり、さらには0.7、0.6、0.5の順により好ましい。 In the optical glass according to the third embodiment, the total content R2O of Li2O , Na2O and K2O and the total content R'O of MgO, CaO, SrO and BaO, Na2 The mass ratio of O content [Na 2 O/(R 2 O+R'O)] is preferably larger than 0, and its lower limit is more preferably in the order of 0.1, 0.13, and 0.15. The upper limit of the mass ratio [Na 2 O/(R 2 O+R'O)] is preferably 0.8, and more preferably in the order of 0.7, 0.6, and 0.5.

第3実施形態に係る光学ガラスにおいて、上記合計含有量ROおよび上記合計含有量R’Oの合計含有量に対するCaOの含有量の質量比[CaO/(RO+R’O)]は、好ましくは0.1以上であり、その下限は0.15、0.18、0.2の順により好ましい。質量比[CaO/(RO+R’O)]の上限は、好ましくは0.95であり、さらには0.90、0.87、0.85の順により好ましい。 In the optical glass according to the third embodiment, the mass ratio of the CaO content to the total content of the total content R 2 O and the total content R′O [CaO/(R 2 O+R′O)] is Preferably it is 0.1 or more, and the lower limit is more preferably in the order of 0.15, 0.18, and 0.2. The upper limit of the mass ratio [CaO/(R 2 O+R'O)] is preferably 0.95, and more preferably in the order of 0.90, 0.87, and 0.85.

第3実施形態に係る光学ガラスにおいて、Bの含有量の上限は、好ましくは5%であり、さらには4.5%、4.2%、4%の順により好ましい。また、Bの含有量の下限は、好ましくは0%であり、さらには0.5%、0.7%、1%の順により好ましい。Bの含有量は0%であってもよい。 In the optical glass according to the third embodiment, the upper limit of the content of B 2 O 3 is preferably 5%, and more preferably 4.5%, 4.2%, and 4% in that order. Further, the lower limit of the content of B 2 O 3 is preferably 0%, and more preferably 0.5%, 0.7%, and 1% in that order. The content of B 2 O 3 may be 0%.

第3実施形態に係る光学ガラスにおいて、上記以外のガラス成分の含有量および比率については、第1実施形態と同様とすることができる。 In the optical glass according to the third embodiment, the contents and ratios of glass components other than those described above can be the same as in the first embodiment.

したがって、第3実施形態に係る光学ガラスは、
屈折率ndが1.69~1.87、
アッベ数νdが24~36であって、
SiOの含有量が10~50%であり、
TiOの含有量が40%以下であり、
Nbの含有量が5~60%であり、
BaOの含有量が10%以下であり、
La、Y、Gd、YbおよびLuの合計含有量が13.5%以下であり、
NbおよびTiOの合計含有量が30%以上であり、
NbおよびTiOの合計含有量に対するNbの含有量の質量比[Nb/(Nb+TiO)]が0.7以下であり、
LiO、NaOおよびKOの合計含有量ROおよびMgO、CaO、SrOおよびBaOの合計含有量R’Oの合計含有量に対する上記合計含有量R’Oの質量比[R’O/(RO+R’O)]が0.7~1.0であり、
上記合計含有量R’Oに対するMgOおよびCaOの合計含有量の質量比[(MgO+CaO)/R’O]が0.26~1.0であ
LiO、NaOおよびKOの合計含有量ROおよびMgO、CaO、SrOおよびBaOの合計含有量R’Oの合計含有量に対するNaOの含有量の質量比[NaO/(RO+R’O)]が0.1以上であってもよい。
Therefore, the optical glass according to the third embodiment is
refractive index nd is 1.69 to 1.87,
Abbe number νd is 24 to 36,
The content of SiO 2 is 10 to 50%,
The content of TiO 2 is 40% or less,
The content of Nb 2 O 5 is 5 to 60%,
The content of BaO is 10% or less,
The total content of La 2 O 3 , Y 2 O 3 , Gd 2 O 3 , Yb 2 O 3 and Lu 2 O 3 is 13.5% or less,
The total content of Nb 2 O 5 and TiO 2 is 30% or more,
The mass ratio of the content of Nb 2 O 5 to the total content of Nb 2 O 5 and TiO 2 [Nb 2 O 5 /(Nb 2 O 5 +TiO 2 )] is 0.7 or less,
The mass ratio [ R 'O/(R 2 O + R'O)] is 0.7 to 1.0,
The mass ratio [(MgO+CaO)/R'O] of the total content of MgO and CaO to the total content R'O is 0.26 to 1.0,
Total content of Li 2 O, Na 2 O and K 2 O Total content of R 2 O and MgO, CaO, SrO and BaO Mass ratio of the content of Na 2 O to the total content of R'O [Na 2 O/(R 2 O+R'O)] may be 0.1 or more.

また、第3実施形態に係る光学ガラスは、
屈折率ndが1.69~1.87、
アッベ数νdが24~36であって、
SiOの含有量が10~50%であり、
TiOの含有量が40%以下であり、
Nbの含有量が5~60%であり、
BaOの含有量が3.5%以上10%以下であり、
La、Y、Gd、YbおよびLuの合計含有量が13.5%以下であり、
NbおよびTiOの合計含有量が30%以上であり、
NbおよびTiOの合計含有量に対するNbの含有量の質量比[Nb/(Nb+TiO)]が0.60以下であり、
LiO、NaOおよびKOの合計含有量ROおよびMgO、CaO、SrOおよびBaOの合計含有量R’Oの合計含有量に対する上記合計含有量R’Oの質量比[R’O/(RO+R’O)]が0.7~0.97であり、
上記合計含有量R’Oに対するMgOおよびCaOの合計含有量の質量比[(MgO+CaO)/R’O]が0.26~1.0であってもよい。
Moreover, the optical glass according to the third embodiment is
refractive index nd is 1.69 to 1.87,
Abbe number νd is 24 to 36,
The content of SiO 2 is 10 to 50%,
The content of TiO 2 is 40% or less,
The content of Nb 2 O 5 is 5 to 60%,
The content of BaO is 3.5% or more and 10% or less,
The total content of La 2 O 3 , Y 2 O 3 , Gd 2 O 3 , Yb 2 O 3 and Lu 2 O 3 is 13.5% or less,
The total content of Nb 2 O 5 and TiO 2 is 30% or more,
The mass ratio of the content of Nb 2 O 5 to the total content of Nb 2 O 5 and TiO 2 [Nb 2 O 5 /(Nb 2 O 5 +TiO 2 )] is 0.60 or less,
The mass ratio [ R 'O/(R 2 O + R'O)] is 0.7 to 0.97,
The mass ratio of the total content of MgO and CaO to the total content R'O [(MgO+CaO)/R'O] may be 0.26 to 1.0.

第3実施形態におけるガラス特性、光学ガラスの製造および光学素子等の製造についても、第1実施形態と同様とすることができる。 Glass properties, production of optical glass, production of optical elements, etc. in the third embodiment can be the same as in the first embodiment.

第4実施形態
第4実施形態に係る光学ガラスは、
屈折率ndが1.69~1.87、アッベ数νdが24~36であって、
SiOの含有量が10~50質量%であり、
TiOの含有量が40質量%以下であり、
Nbの含有量が5~60質量%であり、
の含有量が5質量%以下であり、
BaOの含有量が10質量%以下であり、
La、Y、Gd、YbおよびLuの合計含有量が13.5質量%以下であり、
NbおよびTiOの合計含有量に対するNbの含有量の質量比[Nb/(Nb+TiO)]が0.5以下であり、
LiO、NaOおよびKOの合計含有量ROおよびMgO、CaO、SrOおよびBaOの合計含有量R’Oの合計含有量に対する上記合計含有量R’Oの質量比[R’O/(RO+R’O)]が0.71~1.0であり、
上記合計含有量R’Oに対するMgOおよびCaOの合計含有量の質量比[(MgO+CaO)/R’O]が0.26~1.0である。
Fourth Embodiment The optical glass according to the fourth embodiment is
The refractive index nd is 1.69 to 1.87, the Abbe number νd is 24 to 36,
The content of SiO 2 is 10 to 50% by mass,
The content of TiO 2 is 40% by mass or less,
The content of Nb 2 O 5 is 5 to 60% by mass,
The content of B 2 O 3 is 5% by mass or less,
The content of BaO is 10% by mass or less,
The total content of La 2 O 3 , Y 2 O 3 , Gd 2 O 3 , Yb 2 O 3 and Lu 2 O 3 is 13.5% by mass or less,
The mass ratio of the content of Nb 2 O 5 to the total content of Nb 2 O 5 and TiO 2 [Nb 2 O 5 /(Nb 2 O 5 +TiO 2 )] is 0.5 or less,
The mass ratio [ R 'O/(R 2 O + R'O)] is 0.71 to 1.0,
The mass ratio of the total content of MgO and CaO to the total content R'O [(MgO+CaO)/R'O] is 0.26 to 1.0.

第4実施形態に係る光学ガラスにおいて、SiOの含有量は10~50%である。SiOの含有量の下限は、好ましくは12%であり、さらには15%、17%、20%の順により好ましい。また、SiOの含有量の上限は、好ましくは45%であり、さらには40%、37%、35%の順により好ましい。 In the optical glass according to the fourth embodiment, the content of SiO 2 is 10 to 50%. The lower limit of the SiO 2 content is preferably 12%, and more preferably 15%, 17%, and 20% in that order. Further, the upper limit of the content of SiO 2 is preferably 45%, and more preferably 40%, 37%, and 35% in that order.

第4実施形態に係る光学ガラスにおいて、TiOの含有量は40%以下である。TiOの含有量の上限は、好ましくは35%であり、さらには30%、28%、25%の順により好ましい。TiOの含有量の下限は、好ましくは0%であり、さらには5%、8%、10%の順により好ましい。TiOの含有量は0%でもよい。 In the optical glass according to the fourth embodiment, the content of TiO 2 is 40% or less. The upper limit of the TiO 2 content is preferably 35%, and more preferably 30%, 28%, and 25% in that order. The lower limit of the content of TiO 2 is preferably 0%, and more preferably 5%, 8%, and 10% in that order. The content of TiO 2 may be 0%.

第4実施形態に係る光学ガラスにおいて、Nbの含有量は5~60%である。Nbの含有量の下限は、好ましくは7%であり、さらには8%、9%、10%の順により好ましい。また、Nbの含有量の上限は、好ましくは45%であり、さらには40%、35%、30%の順により好ましい。 In the optical glass according to the fourth embodiment, the content of Nb 2 O 5 is 5 to 60%. The lower limit of the content of Nb 2 O 5 is preferably 7%, and more preferably 8%, 9%, and 10% in that order. Further, the upper limit of the content of Nb 2 O 5 is preferably 45%, and more preferably 40%, 35%, and 30% in that order.

第4実施形態に係る光学ガラスにおいて、Bの含有量は5%以下である。Bの含有量の上限は、好ましくは4.5%であり、さらには4.2%、4%の順により好ましい。また、Bの含有量の下限は、好ましくは0%であり、さらには0.5%、0.7%、1%の順により好ましい。Bの含有量は0%であってもよい。
の含有量が多すぎると屈折率ndが低下するおそれがある。Bの含有量を上記範囲とすることで、ガラスの熱的安定性を改善できる。
In the optical glass according to the fourth embodiment, the content of B 2 O 3 is 5% or less. The upper limit of the content of B 2 O 3 is preferably 4.5%, and more preferably 4.2% and then 4%. Further, the lower limit of the content of B 2 O 3 is preferably 0%, and more preferably 0.5%, 0.7%, and 1% in that order. The content of B 2 O 3 may be 0%.
If the content of B 2 O 3 is too large, the refractive index nd may decrease. By setting the content of B 2 O 3 within the above range, the thermal stability of the glass can be improved.

第4実施形態に係る光学ガラスにおいて、BaOの含有量は10%以下である。BaOの含有量の上限は、好ましくは9%であり、さらには8%、7%の順により好ましい。BaOの含有量の下限は、好ましくは0%であり、さらには1%、2%、3%、3.5%の順により好ましい。BaOの含有量は0%でもよい。 In the optical glass according to the fourth embodiment, the BaO content is 10% or less. The upper limit of the BaO content is preferably 9%, more preferably 8% and then 7%. The lower limit of the BaO content is preferably 0%, and more preferably 1%, 2%, 3%, and 3.5% in this order. The content of BaO may be 0%.

第4実施形態に係る光学ガラスにおいて、La、Y、Gd、YbおよびLuの合計含有量[La+Y+Gd+Yb+Lu]は13.5%以下である。合計含有量[La+Y+Gd+Yb+Lu]の上限は、好ましくは12%であり、さらには11%、10%、9%の順により好ましい。また、合計含有量[La+Y+Gd+Yb+Lu]の下限は、好ましくは0%であり、さらには0.5%、1%、1.5%の順により好ましい。 In the optical glass according to the fourth embodiment, the total content of La 2 O 3 , Y 2 O 3 , Gd 2 O 3 , Yb 2 O 3 and Lu 2 O 3 [La 2 O 3 +Y 2 O 3 +Gd 2 O 3 +Yb 2 O 3 +Lu 2 O 3 ] is 13.5% or less. The upper limit of the total content [La 2 O 3 + Y 2 O 3 + Gd 2 O 3 + Yb 2 O 3 + Lu 2 O 3 ] is preferably 12%, and more preferably in the order of 11%, 10%, and 9%. . Further, the lower limit of the total content [La 2 O 3 +Y 2 O 3 +Gd 2 O 3 +Yb 2 O 3 +Lu 2 O 3 ] is preferably 0%, more preferably 0.5%, 1%, 1. The order of 5% is more preferable.

第4実施形態に係る光学ガラスにおいて、NbおよびTiOの合計含有量に対するNbの含有量の質量比[Nb/(Nb+TiO)]は0.5以下である。質量比[Nb/(Nb+TiO)]上限は、好ましくは0.50、であり、さらには0.48、0.47、0.46、0.45、0.44の順により好ましい。また、質量比[Nb/(Nb+TiO)]は、好ましくは0より大きく、その下限は0.10、0.20、0.30の順により好ましい。
質量比[Nb/(Nb+TiO)]が大きすぎると、比重が増大するおそれがある。質量比[Nb/(Nb+TiO)]が小さすぎると、部分分散比Pg,Fが増加するおそれがある。質量比[Nb/(Nb+TiO)]を上記範囲とすることで、比重を低減し、またガラスの原料コストの増加を抑制できる。
In the optical glass according to the fourth embodiment, the mass ratio of the content of Nb 2 O 5 to the total content of Nb 2 O 5 and TiO 2 [Nb 2 O 5 /(Nb 2 O 5 +TiO 2 ) ] is 0. 5 or less. The upper limit of the mass ratio [Nb 2 O 5 /(Nb 2 O 5 +TiO 2 )] is preferably 0.50, and more preferably 0.48, 0.47, 0.46, 0.45, 0.44. This order is more preferable. Further, the mass ratio [Nb 2 O 5 /(Nb 2 O 5 +TiO 2 )] is preferably larger than 0, and its lower limit is preferably in the order of 0.10, 0.20, and 0.30.
If the mass ratio [Nb 2 O 5 /(Nb 2 O 5 +TiO 2 )] is too large, the specific gravity may increase. If the mass ratio [Nb 2 O 5 /(Nb 2 O 5 +TiO 2 )] is too small, the partial dispersion ratios Pg, F may increase. By setting the mass ratio [Nb 2 O 5 /(Nb 2 O 5 +TiO 2 )] within the above range, specific gravity can be reduced and an increase in glass raw material cost can be suppressed.

第4実施形態に係る光学ガラスにおいて、MgO、CaO、SrOおよびBaOの合計含有量R’OとLiO、NaOおよびKOの合計含有量ROとの合計含有量に対する合計含有量R’Oの質量比[R’O/(R’O+RO)]は0.71~1.0である。質量比[R’O/(R’O+RO)]の下限は、好ましくは0.72、さらには0.73、0.74の順により好ましい。また、質量比[R’O/(R’O+RO)]の上限は、好ましくは0.99、さらには0.98、0.97の順により好ましい。
質量比[R’O/(R’O+RO)]が小さすぎると、屈折率ndが低下するおそれがある。質量比[R’O/(R’O+RO)]が大きすぎると、熱的安定性および熔解性が低下し、低分散化し、また比重が上昇するおそれがある。質量比[R’O/(R’O+RO)]を上記範囲とすることで、高屈折率の光学ガラスを得ることができる。
In the optical glass according to the fourth embodiment, the sum of the total content R'O of MgO, CaO, SrO , and BaO and the total content R 2 O of Li 2 O, Na 2 O, and K 2 O The mass ratio of the content R'O [R'O/(R'O+R 2 O)] is 0.71 to 1.0. The lower limit of the mass ratio [R'O/(R'O+R 2 O)] is preferably 0.72, more preferably 0.73 and 0.74 in that order. Further, the upper limit of the mass ratio [R'O/(R'O+R 2 O)] is preferably 0.99, and more preferably 0.98 and 0.97 in that order.
If the mass ratio [R'O/(R'O+R 2 O)] is too small, the refractive index nd may decrease. If the mass ratio [R'O/(R'O+R 2 O)] is too large, the thermal stability and solubility may decrease, the dispersion may become low, and the specific gravity may increase. By setting the mass ratio [R'O/(R'O+R 2 O)] within the above range, an optical glass with a high refractive index can be obtained.

第4実施形態に係る光学ガラスにおいて、MgO、CaO、SrOおよびBaOの合計含有量R’Oに対するMgOおよびCaOの合計含有量の質量比[(MgO+CaO)/R’O]は0.26~1.0である。質量比[(MgO+CaO)/R’O]の下限は、好ましくは0.35であり、さらには0.4、0.45、0.5の順により好ましい。また、質量比[(MgO+CaO)/R’O]の上限は、好ましくは0.98であり、さらには0.96、0.94、0.92の順により好ましい。 In the optical glass according to the fourth embodiment, the mass ratio [(MgO+CaO)/R'O] of the total content of MgO and CaO to the total content R'O of MgO, CaO, SrO , and BaO is 0.26 to 1. .0. The lower limit of the mass ratio [(MgO+CaO)/R'O] is preferably 0.35, and more preferably in the order of 0.4, 0.45, and 0.5. Further, the upper limit of the mass ratio [(MgO+CaO)/R'O] is preferably 0.98, and more preferably in the order of 0.96, 0.94, and 0.92.

次に、第4実施形態に係る光学ガラスにおける、ガラス成分の含有量および比率の好ましい態様を以下に詳述する。 Next, preferred aspects of the contents and ratios of glass components in the optical glass according to the fourth embodiment will be described in detail below.

第4実施形態に係る光学ガラスは、好ましくは、LiO、NaOおよびKOからなる群から選択される1以上のガラス成分を含み、より好ましくはNaOを含み、さらに好ましくはLiO、NaOおよびKOを含む。
光学ガラスが、LiO、NaOおよびKOからなる群から選択される1以上のガラス成分を含むことで、ガラスの溶解性を高めることができる。
The optical glass according to the fourth embodiment preferably contains one or more glass components selected from the group consisting of Li 2 O, Na 2 O and K 2 O, more preferably Na 2 O, and still more preferably includes Li 2 O, Na 2 O and K 2 O.
When the optical glass contains one or more glass components selected from the group consisting of Li 2 O, Na 2 O and K 2 O, the solubility of the glass can be improved.

第4実施形態に係る光学ガラスは、好ましくは、MgO、CaO、SrOおよびBaOのからなる群から選択される1以上のガラス成分を含み、より好ましくはCaOを含み、さらに好ましくはCaOおよびBaOを含む。
光学ガラスが、MgO、CaO、SrOおよびBaOのからなる群から選択される1以上のガラス成分を含むことで、屈折率ndの低下を抑制できる。
The optical glass according to the fourth embodiment preferably contains one or more glass components selected from the group consisting of MgO, CaO, SrO, and BaO, more preferably contains CaO, and still more preferably contains CaO and BaO. include.
When the optical glass contains one or more glass components selected from the group consisting of MgO, CaO, SrO, and BaO, a decrease in the refractive index nd can be suppressed.

第4実施形態に係る光学ガラスにおいて、MgO、CaO、SrOおよびBaOの合計含有量R’Oに対するCaOの含有量の質量比(CaO/R’O)と、LiO、NaOおよびKOの合計含有量ROに対するNaOの含有量の質量比(NaO/RO)との合計[(CaO/R’O)+(NaO/RO)]は、好ましくは1.1より大きく、その下限は、1.2、1.3、1.35、1.4の順により好ましい。[(CaO/R’O)+(NaO/RO)]の上限は、好ましくは1.9であり、さらには1.85、1.8の順により好ましい。 In the optical glass according to the fourth embodiment, the mass ratio of the content of CaO to the total content R'O of MgO, CaO, SrO , and BaO (CaO/R'O), and the mass ratio of the content of CaO to the total content R'O of Li 2 O, Na 2 O, and K The sum of the mass ratio of the Na 2 O content to the total 2 O content R 2 O (Na 2 O/R 2 O) [(CaO/R'O) + (Na 2 O/R 2 O)] is preferably larger than 1.1, and its lower limit is preferably in the order of 1.2, 1.3, 1.35, and 1.4. The upper limit of [(CaO/R'O)+(Na 2 O/R 2 O)] is preferably 1.9, and more preferably 1.85 and 1.8 in that order.

第4実施形態に係る光学ガラスにおいて、LiO、NaOおよびKOの合計含有量ROおよびMgO、CaO、SrOおよびBaOの合計含有量R’Oの合計含有量に対するNaOの含有量の質量比[NaO/(RO+R’O)]は、好ましくは0より大きく、その下限は、0.1、0.13、0.15の順により好ましい。質量比[NaO/(RO+R’O)]の上限は、好ましくは0.8であり、さらには0.7、0.6、0.5の順により好ましい。 In the optical glass according to the fourth embodiment, the total content R2O of Li2O , Na2O and K2O and the total content R'O of MgO, CaO, SrO and BaO, Na2 The mass ratio of O content [Na 2 O/(R 2 O+R'O)] is preferably larger than 0, and its lower limit is more preferably in the order of 0.1, 0.13, and 0.15. The upper limit of the mass ratio [Na 2 O/(R 2 O+R'O)] is preferably 0.8, and more preferably in the order of 0.7, 0.6, and 0.5.

第4実施形態に係る光学ガラスにおいて、上記合計含有量ROおよび上記合計含有量R’Oの合計含有量に対するCaOの含有量の質量比[CaO/(RO+R’O)]は、好ましくは0.1以上であり、その下限は0.15、0.18、0.2の順により好ましい。質量比[CaO/(RO+R’O)]の上限は、好ましくは0.95であり、さらには0.90、0.87、0.85の順により好ましい。 In the optical glass according to the fourth embodiment, the mass ratio of the CaO content to the total content of the total content R 2 O and the total content R'O [CaO/(R 2 O+R'O)] is Preferably it is 0.1 or more, and the lower limit is more preferably in the order of 0.15, 0.18, and 0.2. The upper limit of the mass ratio [CaO/(R 2 O+R'O)] is preferably 0.95, and more preferably in the order of 0.90, 0.87, and 0.85.

第4実施形態に係る光学ガラスにおいて、NbおよびTiOの合計含有量[Nb+TiO]の下限は、好ましくは5%であり、さらには20%、22%、24%、25%の順により好ましい。また、合計含有量[Nb+TiO]の上限は、好ましくは60%であり、さらには50%、45%、40%の順により好ましい。 In the optical glass according to the fourth embodiment, the lower limit of the total content of Nb 2 O 5 and TiO 2 [Nb 2 O 5 +TiO 2 ] is preferably 5%, and more preferably 20%, 22%, and 24%. , 25% are more preferred. Further, the upper limit of the total content [Nb 2 O 5 +TiO 2 ] is preferably 60%, and more preferably 50%, 45%, and 40% in that order.

第4実施形態に係る光学ガラスにおいて、上記以外のガラス成分の含有量および比率については、第1実施形態と同様とすることができる。 In the optical glass according to the fourth embodiment, the contents and ratios of glass components other than those described above can be the same as in the first embodiment.

したがって、第4実施形態に係る光学ガラスは、
屈折率ndが1.69~1.87、
アッベ数νdが24~36であって、
SiOの含有量が10~50%であり、
TiOの含有量が40%以下であり、
Nbの含有量が5~60%であり、
の含有量が5%以下であり、
BaOの含有量が10%以下であり、
La、Y、Gd、YbおよびLuの合計含有量が13.5%以下であり、
NbおよびTiOの合計含有量に対するNbの含有量の質量比[Nb/(Nb+TiO)]が0.5以下であり、
LiO、NaOおよびKOの合計含有量ROおよびMgO、CaO、SrOおよびBaOの合計含有量R’Oの合計含有量に対する上記合計含有量R’Oの質量比[R’O/(RO+R’O)]が0.71~1.0であり、
上記合計含有量R’Oに対するMgOおよびCaOの合計含有量の質量比[(MgO+CaO)/R’O]が0.26~1.0であり、
LiO、NaOおよびKOの合計含有量ROおよびMgO、CaO、SrOおよびBaOの合計含有量R’Oの合計含有量に対するNaOの含有量の質量比[NaO/(RO+R’O)]が0.1以上であってもよい。
Therefore, the optical glass according to the fourth embodiment is
refractive index nd is 1.69 to 1.87,
Abbe number νd is 24 to 36,
The content of SiO 2 is 10 to 50%,
The content of TiO 2 is 40% or less,
The content of Nb 2 O 5 is 5 to 60%,
The content of B 2 O 3 is 5% or less,
The content of BaO is 10% or less,
The total content of La 2 O 3 , Y 2 O 3 , Gd 2 O 3 , Yb 2 O 3 and Lu 2 O 3 is 13.5% or less,
The mass ratio of the content of Nb 2 O 5 to the total content of Nb 2 O 5 and TiO 2 [Nb 2 O 5 /(Nb 2 O 5 +TiO 2 )] is 0.5 or less,
The mass ratio [ R 'O/(R 2 O + R'O)] is 0.71 to 1.0,
The mass ratio [(MgO+CaO)/R'O] of the total content of MgO and CaO to the total content R'O is 0.26 to 1.0,
Total content of Li 2 O, Na 2 O and K 2 O Total content of R 2 O and MgO, CaO, SrO and BaO Mass ratio of the content of Na 2 O to the total content of R'O [Na 2 O/(R 2 O+R'O)] may be 0.1 or more.

また、第4実施形態におけるガラス特性、光学ガラスの製造および光学素子等の製造についても、第1実施形態と同様とすることができる。 Further, the glass properties, the production of optical glass, the production of optical elements, etc. in the fourth embodiment can be the same as in the first embodiment.

以下に、本発明を実施例により更に詳細に説明する。ただし、本発明は実施例に示す態様に限定されるものではない。 EXAMPLES Below, the present invention will be explained in more detail with reference to Examples. However, the present invention is not limited to the embodiments shown in the examples.

(実施例1)
表1-1~1-10および表2-1~2-10に示すガラス組成を有するガラスサンプルを以下の手順で作製し、各種評価を行った。
(Example 1)
Glass samples having glass compositions shown in Tables 1-1 to 1-10 and Tables 2-1 to 2-10 were prepared according to the following procedure, and various evaluations were performed.

[光学ガラスの製造]
まず、ガラスの構成成分に対応する酸化物、水酸化物、炭酸塩、および硝酸塩を原材料として準備し、得られる光学ガラスのガラス組成が、表1-1~1-10に示す各組成となるように上記原材料を秤量、調合して、原材料を十分に混合した。こうして得られた調合原料(バッチ原料)を、白金坩堝に投入し、1350℃~1450℃で2~5時間加熱して熔融ガラスとし、攪拌して均質化を図り、清澄してから、熔融ガラスを適当な温度に予熱した金型に鋳込んだ。鋳込んだガラスを、ガラス転移温度TgからTgより100℃低い温度の間で30分間熱処理し、炉内で室温まで放冷することにより、ガラスサンプルを得た。
[Manufacture of optical glass]
First, oxides, hydroxides, carbonates, and nitrates corresponding to the constituent components of the glass are prepared as raw materials, and the glass composition of the resulting optical glass is as shown in Tables 1-1 to 1-10. The above raw materials were weighed and prepared, and the raw materials were thoroughly mixed. The blended raw materials (batch raw materials) obtained in this way are put into a platinum crucible, heated at 1350°C to 1450°C for 2 to 5 hours to form molten glass, stirred to homogenize, clarified, and then molten glass. was cast into a mold preheated to an appropriate temperature. A glass sample was obtained by heat-treating the cast glass at a temperature between the glass transition temperature Tg and a temperature 100° C. lower than Tg for 30 minutes, and allowing it to cool to room temperature in a furnace.

[ガラス成分組成の確認]
得られたガラスサンプルについて、誘導結合プラズマ発光分光分析法(ICP-AES)で各ガラス成分の含有量を測定し、表1-1~1-10に示す各組成のとおりであることを確認した。
[Confirmation of glass component composition]
Regarding the obtained glass sample, the content of each glass component was measured by inductively coupled plasma emission spectroscopy (ICP-AES), and it was confirmed that the composition was as shown in Tables 1-1 to 1-10. .

[光学特性の測定]
得られたガラスサンプルを、さらにガラス転移温度Tg付近で約30分から約2時間アニール処理した後、炉内で降温速度-30℃/時間で室温まで冷却してアニールサンプルを得た。得られたアニールサンプルについて、屈折率nd、ng、nFおよびnC、アッベ数νd、部分分散比Pg,F、比重、ガラス転移温度Tg、λ80、λ70およびλ5を測定した。結果を表3-1~3-10に示す。
(i)屈折率nd、ng、nF、nCおよびアッベ数νd
上記アニールサンプルについて、JIS規格 JIS B 7071-1の屈折率測定法により、屈折率nd、ng、nF、nCを測定し、下式に基づきアッベ数νdを算出した。
νd=(nd-1)/(nF-nC)
[Measurement of optical properties]
The obtained glass sample was further annealed at around the glass transition temperature Tg for about 30 minutes to about 2 hours, and then cooled to room temperature in a furnace at a cooling rate of -30° C./hour to obtain an annealed sample. For the obtained annealed sample, the refractive index nd, ng, nF and nC, Abbe's number νd, partial dispersion ratio Pg, F, specific gravity, glass transition temperature Tg, λ80, λ70 and λ5 were measured. The results are shown in Tables 3-1 to 3-10.
(i) Refractive index nd, ng, nF, nC and Abbe number νd
For the annealed sample, the refractive indexes nd, ng, nF, and nC were measured by the refractive index measurement method of JIS standard JIS B 7071-1, and the Abbe number νd was calculated based on the following formula.
νd=(nd-1)/(nF-nC)

(ii)部分分散比Pg,F
g線、F線、c線における各屈折率ng、nF、nCを用いて、下記式に基づき部分分散比Pg,Fを算出した。
Pg,F=(ng-nF)/(nF-nC)
(ii) Partial dispersion ratio Pg,F
Partial dispersion ratios Pg and F were calculated based on the following formula using the refractive indexes ng, nF, and nC at the g-line, F-line, and c-line.
Pg,F=(ng-nF)/(nF-nC)

(iii)部分分散比Pg,Fの偏差ΔPg,F
部分分散比Pg,Fおよびアッベ数νdを用いて、下記式に基づき算出した。
ΔPg,F=Pg,F+(0.0018×νd)-0.6483
(iii) Deviation ΔPg,F of partial dispersion ratio Pg,F
It was calculated based on the following formula using the partial dispersion ratio Pg, F and the Abbe number νd.
ΔPg,F=Pg,F+(0.0018×νd)-0.6483

(iv)比重
比重は、アルキメデス法により測定した。
(iv) Specific gravity Specific gravity was measured by the Archimedes method.

(v)ガラス転移温度Tg
ガラス転移温度Tgは、NETZSCH JAPAN社製の示差走査熱量分析装置(DSC3300SA)を使用し、昇温速度10℃/分にて測定した。
(v) Glass transition temperature Tg
The glass transition temperature Tg was measured using a differential scanning calorimeter (DSC3300SA) manufactured by NETZSCH JAPAN at a heating rate of 10° C./min.

(vi)λ80、λ70、λ5
上記アニールサンプルを、厚さ10mmで、互いに平行かつ光学研磨された平面を有するように加工し、波長280nmから700nmまでの波長域における分光透過率を測定した。光学研磨された一方の平面に垂直に入射する光線の強度を強度Aとし、他方の平面から出射する光線の強度を強度Bとして、分光透過率B/Aを算出した。分光透過率が80%になる波長をλ80とし、分光透過率B/Aを算出した。分光透過率が70%になる波長をλ70とし、分光透過率が5%になる波長をλ5とした。なお、分光透過率には試料表面における光線の反射損失も含まれる。
(vi) λ80, λ70, λ5
The annealed sample was processed to have a thickness of 10 mm, parallel to each other and optically polished planes, and the spectral transmittance in the wavelength range from 280 nm to 700 nm was measured. The spectral transmittance B/A was calculated by setting the intensity of the light beam perpendicularly incident on one optically polished plane as intensity A, and the intensity of the light beam emerging from the other plane as intensity B. The wavelength at which the spectral transmittance was 80% was defined as λ80, and the spectral transmittance B/A was calculated. The wavelength at which the spectral transmittance was 70% was defined as λ70, and the wavelength at which the spectral transmittance was 5% was defined as λ5. Note that the spectral transmittance also includes reflection loss of light rays on the sample surface.

Figure 0007383375000001
Figure 0007383375000001

Figure 0007383375000002
Figure 0007383375000002

Figure 0007383375000003
Figure 0007383375000003

Figure 0007383375000004
Figure 0007383375000004

Figure 0007383375000005
Figure 0007383375000005

Figure 0007383375000006
Figure 0007383375000006

Figure 0007383375000007
Figure 0007383375000007

Figure 0007383375000008
Figure 0007383375000008

Figure 0007383375000009
Figure 0007383375000009

Figure 0007383375000010
Figure 0007383375000010

Figure 0007383375000011
Figure 0007383375000011

Figure 0007383375000012
Figure 0007383375000012

Figure 0007383375000013
Figure 0007383375000013

Figure 0007383375000014
Figure 0007383375000014

Figure 0007383375000015
Figure 0007383375000015

Figure 0007383375000016
Figure 0007383375000016

Figure 0007383375000017
Figure 0007383375000017

Figure 0007383375000018
Figure 0007383375000018

Figure 0007383375000019
Figure 0007383375000019

Figure 0007383375000020
Figure 0007383375000020

Figure 0007383375000021
Figure 0007383375000021

Figure 0007383375000022
Figure 0007383375000022

Figure 0007383375000023
Figure 0007383375000023

Figure 0007383375000024
Figure 0007383375000024

Figure 0007383375000025
Figure 0007383375000025

Figure 0007383375000026
Figure 0007383375000026

Figure 0007383375000027
Figure 0007383375000027

Figure 0007383375000028
Figure 0007383375000028

Figure 0007383375000029
Figure 0007383375000029

Figure 0007383375000030
Figure 0007383375000030

(実施例2)
実施例1において作製した各光学ガラスを用いて、公知の方法により、レンズブランクを作製し、レンズブランクを研磨等の公知方法により加工して各種レンズを作製した。
作製した光学レンズは、両凸レンズ、両凹レンズ、平凸レンズ、平凹レンズ、凹メニスカスレンズ、凸メニスカスレンズ等の各種レンズである。
各種レンズは、他種の光学ガラスからなるレンズと組合せることにより、二次の色収差を良好に補正することができた。
(Example 2)
Using each optical glass produced in Example 1, a lens blank was produced by a known method, and the lens blank was processed by a known method such as polishing to produce various lenses.
The produced optical lenses are various lenses such as a biconvex lens, a biconcave lens, a plano-convex lens, a plano-concave lens, a concave meniscus lens, and a convex meniscus lens.
By combining various lenses with lenses made of other types of optical glass, secondary chromatic aberrations could be corrected well.

また、ガラスが低比重であるため、各レンズとも同等の光学特性、大きさを有するレンズよりも重量が小さく、各種撮像機器、特に省エネ可能という理由等によりオートフォーカス式の撮像機器用として好適である。同様にして、実施例1で作製した各種光学ガラスを用いてプリズムを作製した。 In addition, because the glass has a low specific gravity, each lens weighs less than lenses with the same optical characteristics and size, making it suitable for use in various imaging devices, especially autofocus imaging devices due to its energy saving potential. be. Similarly, prisms were produced using the various optical glasses produced in Example 1.

今回開示された実施の形態はすべての点で例示であって制限的なものではないと考えられるべきである。本発明の範囲は上記した説明ではなくて特許請求の範囲によって示され、特許請求の範囲と均等の意味および範囲内でのすべての変更が含まれることが意図される。 The embodiments disclosed this time should be considered to be illustrative in all respects and not restrictive. The scope of the present invention is indicated by the claims rather than the above description, and it is intended that all changes within the meaning and range equivalent to the claims are included.

例えば、上記に例示されたガラス組成に対し、明細書に記載の組成調整を行うことにより、本発明の一態様にかかる光学ガラスを作製することができる。
また、明細書に例示または好ましい範囲として記載した事項の2つ以上を任意に組み合わせることは、もちろん可能である。
For example, the optical glass according to one embodiment of the present invention can be produced by adjusting the composition described in the specification with respect to the glass composition exemplified above.
Furthermore, it is of course possible to arbitrarily combine two or more of the items described as examples or preferred ranges in the specification.

Claims (3)

屈折率ndが1.69~1.87、アッベ数νdが24~36であって、
SiO2の含有量が10~50質量%であり、
TiO2の含有量が13.68~21.74質量%であり、
Nb25の含有量が8.25~21.11質量%であり、
BaOの含有量が10質量%以下であり、
GeO2の含有量が2質量%以下であり、
Ta25の含有量が3質量%以下であり、
La23、Y23、Gd23、Yb23およびLu23の合計含有量が13.5質量%以下であり、
Nb25およびTiO2の合計含有量に対するNb25の含有量の質量比[Nb25/(Nb25+TiO2)]が0.6以下であり、
Li2O、Na2OおよびK2Oからなる群から選択される1以上のガラス成分を含み、
MgO、CaO、SrOおよびBaOのからなる群から選択される1以上のガラス成分を含み、
MgO、CaO、SrOおよびBaOの合計含有量R’Oに対するCaOの含有量の質量比(CaO/R’O)と、Li2O、Na2OおよびK2Oの合計含有量R2Oに対するNa2Oの含有量の質量比(Na2O/R2O)との合計[(CaO/R’O)+(Na2O/R2O)]が1.2以上であり、
上記合計含有量R2Oおよび上記合計含有量R’Oの合計含有量に対するCaOの含有量の質量比[CaO/(R2O+R’O)]が0.303以上であり、
上記合計含有量R’Oに対するMgOおよびCaOの合計含有量の質量比[(MgO+CaO)/R’O]が0.44~1.0である、光学ガラス。
The refractive index nd is 1.69 to 1.87, the Abbe number νd is 24 to 36,
The content of SiO 2 is 10 to 50% by mass,
The content of TiO 2 is 13.68 to 21.74 % by mass,
The content of Nb 2 O 5 is 8.25 to 21.11 % by mass,
The content of BaO is 10% by mass or less,
The content of GeO 2 is 2% by mass or less,
The content of Ta 2 O 5 is 3% by mass or less,
The total content of La 2 O 3 , Y 2 O 3 , Gd 2 O 3 , Yb 2 O 3 and Lu 2 O 3 is 13.5% by mass or less,
The mass ratio of the content of Nb 2 O 5 to the total content of Nb 2 O 5 and TiO 2 [Nb 2 O 5 /(Nb 2 O 5 +TiO 2 )] is 0.6 or less,
Containing one or more glass components selected from the group consisting of Li 2 O, Na 2 O and K 2 O,
Containing one or more glass components selected from the group consisting of MgO, CaO, SrO and BaO,
Mass ratio of CaO content to total content R'O of MgO, CaO, SrO and BaO (CaO/R'O) and total content R2O of Li 2 O, Na 2 O and K 2 O The sum of the content of Na 2 O and the mass ratio (Na 2 O/R 2 O) [(CaO/R'O) + (Na 2 O/R 2 O)] is 1.2 or more,
The mass ratio [CaO/(R 2 O + R'O)] of the CaO content to the total content of the total content R 2 O and the total content R'O is 0.303 or more,
An optical glass having a mass ratio [(MgO+CaO)/R'O] of the total content of MgO and CaO to the total content R'O of 0.44 to 1.0.
屈折率ndが1.69~1.87、アッベ数νdが24~36であって、
SiO2の含有量が10~50質量%であり、
TiO2の含有量が13.68~21.74質量%であり、
Nb25の含有量が8.25~21.11質量%であり、
BaOの含有量が10質量%以下であり、
GeO2の含有量が2質量%以下であり、
Ta25の含有量が3質量%以下であり、
La23、Y23、Gd23、Yb23およびLu23の合計含有量が13.5質量%以下であり、
Nb25およびTiO2の合計含有量に対するNb25の含有量の質量比[Nb25/(Nb25+TiO2)]が0.6以下であり、
Li2O、Na2OおよびK2Oの合計含有量R2OおよびMgO、CaO、SrOおよびBaOの合計含有量R’Oの合計含有量に対するNa2Oの含有量の質量比[Na2O/(R2O+R’O)]が0より大きく、
上記合計含有量R2Oおよび上記合計含有量R’Oの合計含有量に対するCaOの含有量の質量比[CaO/(R2O+R’O)]が0.303以上であり、
上記合計含有量R’Oに対するMgOおよびCaOの合計含有量の質量比[(MgO+CaO)/R’O]が0.44~1.0である、光学ガラス。
The refractive index nd is 1.69 to 1.87, the Abbe number νd is 24 to 36,
The content of SiO 2 is 10 to 50% by mass,
The content of TiO 2 is 13.68 to 21.74 % by mass,
The content of Nb 2 O 5 is 8.25 to 21.11 % by mass,
The content of BaO is 10% by mass or less,
The content of GeO 2 is 2% by mass or less,
The content of Ta 2 O 5 is 3% by mass or less,
The total content of La 2 O 3 , Y 2 O 3 , Gd 2 O 3 , Yb 2 O 3 and Lu 2 O 3 is 13.5% by mass or less,
The mass ratio of the content of Nb 2 O 5 to the total content of Nb 2 O 5 and TiO 2 [Nb 2 O 5 /(Nb 2 O 5 +TiO 2 )] is 0.6 or less,
Total content of Li 2 O, Na 2 O and K 2 O Total content of R 2 O and MgO, CaO, SrO and BaO Mass ratio of the content of Na 2 O to the total content of R'O [Na 2 O/(R 2 O+R'O)] is greater than 0,
The mass ratio [CaO/(R 2 O + R'O)] of the CaO content to the total content of the total content R 2 O and the total content R'O is 0.303 or more,
An optical glass having a mass ratio [(MgO+CaO)/R'O] of the total content of MgO and CaO to the total content R'O of 0.44 to 1.0.
請求項1または2に記載の光学ガラスからなる光学素子。
An optical element comprising the optical glass according to claim 1 or 2.
JP2018189911A 2017-12-22 2018-10-05 Optical glass and optical elements Active JP7383375B2 (en)