JP6586019B2 - An apparatus for producing a nonwoven fabric or woven fabric containing nanofibers. - Google Patents

An apparatus for producing a nonwoven fabric or woven fabric containing nanofibers. Download PDF

Info

Publication number
JP6586019B2
JP6586019B2 JP2016003177A JP2016003177A JP6586019B2 JP 6586019 B2 JP6586019 B2 JP 6586019B2 JP 2016003177 A JP2016003177 A JP 2016003177A JP 2016003177 A JP2016003177 A JP 2016003177A JP 6586019 B2 JP6586019 B2 JP 6586019B2
Authority
JP
Japan
Prior art keywords
conductor
nanofiber
raw material
material solution
woven fabric
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Active
Application number
JP2016003177A
Other languages
Japanese (ja)
Other versions
JP2017125265A (en
Inventor
信裕 梅原
信裕 梅原
辰也 鈴木
辰也 鈴木
Original Assignee
株式会社エアード
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 株式会社エアード filed Critical 株式会社エアード
Priority to JP2016003177A priority Critical patent/JP6586019B2/en
Publication of JP2017125265A publication Critical patent/JP2017125265A/en
Application granted granted Critical
Publication of JP6586019B2 publication Critical patent/JP6586019B2/en
Active legal-status Critical Current
Anticipated expiration legal-status Critical

Description

本願は、ナノ繊維が含有された不織布又は織布の製造装置に関し、詳しくは、ワイヤ状の導電体を走行させつつ、この導電体に間隔を設けて、ナノ繊維原料溶液の液滴を塗付し、これをプラス電極として、接地電極の間に高電圧を印加し、不織布又は織布を走行させるナノ繊維を含有した不織布又は織布の製造装置に関する。 The present application relates to an apparatus for manufacturing a nonwoven fabric or a woven fabric containing nanofibers. Specifically, while running a wire-like conductor, the conductor is spaced to apply a nanofiber raw material solution droplet. The present invention also relates to a non-woven fabric or woven fabric manufacturing apparatus containing nanofibers that use this as a positive electrode and apply a high voltage between ground electrodes to run the non-woven fabric or woven fabric.

粉塵、ハウスダスト、浮遊粒子状物質や花粉等の微小な有害粒子を除去し得るだけでなく、空気中に浮遊する各種細菌、ウイルス等を取り除くために、不織布又は織布の層に、ナノ繊維層を重ねて二層状態のものが開示されている。 In addition to removing fine harmful particles such as dust, house dust, suspended particulate matter and pollen, in order to remove various bacteria, viruses, etc. floating in the air, nanofibers in the nonwoven fabric or woven fabric layer Two layers are disclosed with the layers being stacked.

ナノ繊維の製造装置として、一般的には、エレクトロスピニング法を用いて、一方の電極をシリンジとし、アースされたコレクタを設け、これらの間に高電圧を印加して、シリンジから押出された溶液が電荷を帯び,細かな繊維となってコレクタに向かってナノ繊維が放出され、開口部から放出されたナノ繊維をコレクタで捕集する方法が用いられている。 As an apparatus for producing nanofibers, generally, an electrospinning method is used. One electrode is a syringe, a grounded collector is provided, a high voltage is applied between them, and a solution extruded from the syringe. Is charged, becomes a fine fiber, nanofibers are released toward the collector, and the nanofibers released from the openings are collected by the collector.

この方法においては、問題点として(1)シリンジ開口部が、乾燥してナノ繊維原料が固化して汚染される。(2)コレクタにナノ繊維が付着する。このため、シリンジから押出された溶液に、必要な電荷を与えることができず、常に、ノズル開口部の清掃するとともに、コレクタに集積されたナノ繊維を取り除き、コレクタの清掃をしなければならない。実験室規模の装置などでは容易に少量のナノ繊維を作ることができるが、これを常用化するためには大量生産が可能でなければならない。このため前記の問題点が解決されなければならない。 In this method, as problems, (1) the syringe opening is dried and the nanofiber raw material is solidified and contaminated. (2) Nanofibers adhere to the collector. For this reason, a necessary charge cannot be given to the solution extruded from the syringe, and the nozzle opening must always be cleaned, and the nanofibers accumulated in the collector must be removed to clean the collector. A small-scale nanofiber can be easily produced in a laboratory scale apparatus or the like, but mass production must be possible in order to make this a regular use. For this reason, the above-mentioned problems must be solved.

これらの問題点を解決する方法として、下記特許文献1にアース電極として金属球を用いて、シリンジ開口部からこの金属球に向けて放出されるナノ繊維の方向を、高速気流を用いて変えて、別途設けたナノファイバー捕集部に向けて飛散させて、捕集部の捕集面で捕集する。この捕集面は、ドラム状又は板状でありナノ繊維は捕集面上に積層される。この捕集面に、不織布又は織布を用いることにより、二層構造の繊維が製造できる。しかし、この二層構造のナノ繊維層は、はがれやすく、取り扱いが容易でない。 As a method for solving these problems, in Patent Document 1 below, a metal sphere is used as a ground electrode, and the direction of nanofibers emitted from the syringe opening toward the metal sphere is changed using a high-speed air flow. Then, it is scattered toward the separately provided nanofiber collecting part and collected on the collecting surface of the collecting part. The collection surface is in the form of a drum or a plate, and the nanofibers are laminated on the collection surface. By using a nonwoven fabric or a woven fabric for the collecting surface, a fiber having a two-layer structure can be produced. However, this nanofiber layer having a two-layer structure is easy to peel off and is not easy to handle.

また、下記特許文献2には、シリンジ開口部とコレクタ間に高電圧を印加して、このコレクタの上にロールされた不織布を設け、この不織布を一定方向に走行させて、不織布上にナノ繊維の層を設けている。この方法においては、不織布を貫通して、コレクタまで達するナノ繊維の一部が存在して、徐々にコレクタがナノ繊維で汚染され、ナノ繊維原料溶液に十分な電荷を与えることができず、コレクタ表面の清掃を頻繁に行う必要がある。上述のように、シリンジ開口部も汚染されるため、常に清掃を余儀なくされる(本願の図11を参照)。 Further, in Patent Document 2 below, a high voltage is applied between the syringe opening and the collector, a nonwoven fabric rolled on the collector is provided, the nonwoven fabric is run in a certain direction, and nanofibers are formed on the nonwoven fabric. The layer is provided. In this method, there is a part of the nanofibers that penetrate the nonwoven fabric and reach the collector, and the collector is gradually contaminated with nanofibers, so that the nanofiber raw material solution cannot be charged sufficiently, and the collector It is necessary to clean the surface frequently. As described above, since the syringe opening is also contaminated, cleaning is always required (see FIG. 11 of the present application).

本願発明はこれらの問題点を解決し、従来技術のエレクトロスピニング法で使用されるシリンジを用いることなく、ナノ繊維原料溶液の液滴を塗付した走行する導電体をプラス電極として使用する。この装置で作られた製品は、ナノ繊維が不織布等の中に入っているため、ナノ繊維が剥がれおちることが無く、取り扱いが容易であり、通気抵抗が小さく、且つ濾過効果も優れる。 The present invention solves these problems, and uses a traveling conductor coated with droplets of a nanofiber raw material solution as a positive electrode without using a syringe used in a conventional electrospinning method. Since the nanofiber is contained in a nonwoven fabric or the like, the product made by this apparatus is easy to handle, has a low airflow resistance, and has an excellent filtration effect.

特開2011−127234JP2011-127234A 特開2014−166299JP 2014-166299 A

高電圧で印加されたプラス電極及び接地電極を、ナノ繊維原料溶液又はナノ繊維で汚染させることなく、連続して不織布又は織布にナノ繊維を含有させる装置を提供する。本願装置により製造されたナノ繊維を含有する不織布又は織布は、マスク及びフィルター等に利用される。 There is provided an apparatus for continuously incorporating a nanofiber into a nonwoven fabric or a woven fabric without contaminating the positive electrode and the ground electrode applied with a high voltage with the nanofiber raw material solution or the nanofiber. Nonwoven fabrics or woven fabrics containing nanofibers produced by the device of the present application are used for masks and filters.

本願発明は、従来技術のエレクトロスピニング法を用いてナノ繊維を製造する装置において、プラス電極に使用されていたシリンジに代えて、走行するワイヤ状の導電体をプラス電極とする。この導電体は、金属、カーボンが使用される。走行速度は、導電体の種類、ナノ繊維原料溶液の種類、濃度、粘度により適宜選択できる。「ワイヤ状」とは、針金のごとく細くて長い形状をいい、断面が円形に限らず、矩形、多角形等も含む。 The present invention uses a traveling wire-like conductor as a positive electrode in place of the syringe used for the positive electrode in an apparatus for producing nanofibers using a conventional electrospinning method. This conductor is made of metal or carbon. The traveling speed can be appropriately selected depending on the type of conductor, the type, concentration, and viscosity of the nanofiber raw material solution. The “wire shape” means a thin and long shape like a wire, and the cross section is not limited to a circle, but also includes a rectangle, a polygon, and the like.

上記金属は、エレクトロスピニング法で通常使用される金属を使用できる。好ましくは、金又は金で被覆されたワイヤ状の導電体を使用する。金又は、金で被覆された導電体を使用した場合、図3に示すようなナノ繊維原料溶液を含浸させたスポンジにワイヤ状の導電体を貫通させることにより、図4及び図5に示すよう間隔を設けて液滴を形成・塗付できる。このため、ナノ繊維原料溶液の液滴に安定した電荷を帯電させることができる。
本願明細書に記載の「スポンジ」とは、内部に細かな孔が無数に空いた多孔質の柔らかい物質をいう。液体に浸すと孔内の空気と置換される形で液体を吸い取り、また外部からの力で容易に放出する特性を有するものの総称をいい、フェルト等も含む。
The said metal can use the metal normally used by the electrospinning method. Preferably, gold or a wire-like conductor covered with gold is used. When gold or a conductor coated with gold is used, a wire-like conductor is penetrated through a sponge impregnated with a nanofiber raw material solution as shown in FIG. Drops can be formed and applied at intervals. For this reason, a stable charge can be charged to the droplets of the nanofiber raw material solution.
The “sponge” described in the present specification refers to a porous soft substance having innumerable fine pores inside. It is a generic term for materials that absorb the liquid in a form that replaces the air in the holes when immersed in the liquid, and that can be easily released by external force, including felt.

本願発明に使用される「カーボン」とは、カーボンファイバー又は導電性カーボンブラックをいう。このカーボン又は、このカーボンで被覆されたものも、金又は、金で被覆された導電体と同様な効果を有する。 “Carbon” used in the present invention refers to carbon fiber or conductive carbon black. This carbon or the one coated with carbon has the same effect as gold or a conductor coated with gold.

定量点滴塗付装置を用いて、間隔を設けて、ナノ繊維原料溶液の液滴を導電体に一定量を塗付させることもできる。塗付されるナノ繊維原料溶液の液滴の量は、ナノ繊原料溶液の、濃度、粘度、導電値、印加電圧等により適宜選択される。 It is also possible to apply a fixed amount of droplets of the nanofiber raw material solution to the conductor by using a fixed-quantity drip coating apparatus at intervals. The amount of droplets of the nanofiber raw material solution to be applied is appropriately selected according to the concentration, viscosity, conductivity value, applied voltage, etc. of the nanofiber raw material solution.

走行する導電体は、ロールされたワイヤ状の金属等をロールから繰出し、他方で、このワイヤを巻取ることで達成される。または、図2に示すように、空間に矩形状に導電体を架線して、一定方向に回転させることによっても達成される。このワイヤ状の導電体は、繰り返して使用することもできる。また、廃棄して、新たな導電体を用いることもできる。 The running conductor is achieved by feeding a rolled wire-like metal or the like from the roll and winding the wire on the other hand. Alternatively, as shown in FIG. 2, this can also be achieved by placing a conductor in a rectangular shape in the space and rotating it in a certain direction. This wire-like conductor can be used repeatedly. It can also be discarded and a new conductor can be used.

また、上述のワイヤ状の導電体と平行に指向性電極を設けることにより、導電体から噴射されるナノ繊維の流れを、接地電極側の一定方向に誘導して、ナノ繊維の不織布への含有効率を上げることができる。 In addition, by providing a directional electrode in parallel with the wire-shaped conductor described above, the flow of nanofibers ejected from the conductor is induced in a certain direction on the ground electrode side, and the nanofibers are contained in the nonwoven fabric. Efficiency can be increased.

導電性のない樹脂テープに、導電体を帯状に印刷して使用することもできる。テープに導電体を印刷するというときは、導電体を蒸着すること、導電性フィラーを樹脂等と混練して印刷することも含む。導電性の無い樹脂テープの素材は、通常使用されるポリエチレンテレフタレート、ポリエチレンナフタレート、ポリアミド等の素材が使用できる。 It is also possible to use a conductor printed on a non-conductive resin tape in a strip shape. When the conductor is printed on the tape, the process includes vapor-depositing the conductor and kneading and printing the conductive filler with a resin or the like. As the material of the resin tape having no electrical conductivity, materials such as polyethylene terephthalate, polyethylene naphthalate and polyamide which are usually used can be used.

印刷される導電体の材質は、金属、カーボンを用いる。金属については、通常エレクトロスピニング法においてプラス極に用いられる金属を使用できる。好ましくは金を用いる。金を用いることにより上述のワイヤ状の導電体と同様な効果が得られる。上記樹脂テープには、複数の帯状の導電体を印刷することもできる。 Metal or carbon is used as the material of the printed conductor. As for the metal, a metal that is usually used as a positive electrode in the electrospinning method can be used. Preferably gold is used. By using gold, the same effect as that of the above-described wire-like conductor can be obtained. A plurality of strip-shaped conductors can be printed on the resin tape.

この導電体の表面に、一定間隔で突起部を設けることが好ましく、この突起物に上述の定量点滴塗付装置を用いて、ナノ繊維原料溶液を付着させる。この突起部を設けたときは、突起部から安定したナノ繊維のジェット流が接地電極に向かって噴射される。 Protrusions are preferably provided on the surface of the conductor at regular intervals, and the nanofiber raw material solution is attached to the protrusions using the above-described quantitative drip coating apparatus. When this protrusion is provided, a stable nanofiber jet flow is ejected from the protrusion toward the ground electrode.

上述のプラス電極と、接地電極の間に、不織布又は織布を配設して両極間に高電圧を印加する。高電圧とは、従来技術のエレクトロスピニング法で用いられる数kV〜数10kVの直流高電圧をいい、本願発明においては、通常15KV〜35KVを用いる。
印加する高電圧は、ナノ繊維原料の種類、濃度、導電値、プラス電極に使用される導電体の種類により異なる。
A non-woven fabric or a woven fabric is disposed between the positive electrode and the ground electrode, and a high voltage is applied between both electrodes. The high voltage refers to a DC high voltage of several kV to several tens of kV used in the conventional electrospinning method. In the present invention, normally 15 KV to 35 KV is used.
The high voltage to be applied varies depending on the type, concentration, conductivity value, and type of conductor used for the plus electrode.

この不織布及び織布は、連続的にナノ繊維を含有させるために、走行させる。走行速度は、所望のナノ繊維目付量により変更する。不織布及び織布の種類は限定されない。 The nonwoven fabric and the woven fabric are run to continuously contain nanofibers. The running speed is changed depending on the desired nanofiber weight per unit area. The kind of nonwoven fabric and woven fabric is not limited.

接地電極については、通常エレクトロスピニング法において用いられる金属又はカーボンを使用できる。これらの材質からなるワイヤ、テープ、板、メッシュ網等を使用する。ナノ繊維は上述の不織布また織布に捕集されて、不織布又は織布に含有される。印加電圧によっては、ナノ繊維の一部がこの不織布又は織布の貫通孔を通過して、接地電極に到達して、接地電極を汚染することがある。 For the ground electrode, a metal or carbon usually used in the electrospinning method can be used. Wires, tapes, plates, mesh nets, etc. made of these materials are used. Nanofibers are collected in the above-mentioned nonwoven fabric or woven fabric and contained in the nonwoven fabric or woven fabric. Depending on the applied voltage, a part of the nanofiber may pass through the through-hole of the nonwoven fabric or woven fabric, reach the ground electrode, and contaminate the ground electrode.

この場合、接地電極は一定時間ごとに取り換えるか、または清掃する必要がある。好ましくは、接地電極はロール状にして、走行させて常に新しく汚染の無い表面を曝すことが好ましい。 In this case, the ground electrode needs to be replaced or cleaned at regular intervals. Preferably, the ground electrode is rolled and run to always expose a new and clean surface.

本願発明に係る製造装置は、連続して且つ安定して工業的規模で、ナノ繊維を含有した不織布又は織布の製造することができる。このため、安価なナノ繊維を含有した不織布又は織布の供給が可能である。 The production apparatus according to the present invention can produce a nonwoven fabric or a woven fabric containing nanofibers continuously and stably on an industrial scale. For this reason, it is possible to supply a non-woven fabric or a woven fabric containing inexpensive nanofibers.

本願発明で製造された、ナノ繊維を含有する不織布又は織布は、ナノ繊維が剥がれ落ちることが無く、取扱いが容易であり、マスクの原料、フィルター等に好適に使用される。また、スポーツウェア等に使用するときは、体内から発生する発汗蒸気は、この素材を通して排出されるが、雨滴等は、この素材を通して、侵入することはなく、快適な着心地を得ることができる。 The non-woven fabric or woven fabric containing nanofibers produced in the present invention is easy to handle because the nanofibers are not peeled off, and is suitably used for mask raw materials, filters and the like. In addition, when used for sportswear, sweat vapor generated from the body is discharged through this material, but raindrops and the like do not enter through this material, and a comfortable comfort can be obtained. .

本願装置によれば、走行する導電体にナノ繊維原料溶液の液滴を間隔を設けて付着させる。この液滴のすべては、速やかにナノ繊維となって接地電極に向かって噴射され、導電体が汚染されることが無い。このため、連続して安定且つ、一定の電荷をナノ繊維原料溶液の液滴に帯電させることが可能であり、ナノ繊維含有不織布又は織布の工業的規模で製造が可能である。本願装置で製造されるナノ繊維含有不織布又は織布は、ナノ繊維が剥がれおちることが無く、取扱いが容易であり、空気の通過抵抗も小さく、浮遊粒子状物質等の微小な有害粒子の除去効果が大きい。 According to the apparatus of the present application, the droplets of the nanofiber raw material solution are attached to the traveling conductor with a gap. All of these droplets quickly become nanofibers and are ejected toward the ground electrode, so that the conductor is not contaminated. For this reason, it is possible to charge the droplets of the nanofiber raw material solution with a stable and constant charge, and it is possible to produce nanofiber-containing nonwoven fabrics or woven fabrics on an industrial scale. Nanofiber-containing non-woven fabric or woven fabric produced by the device of the present application is easy to handle, with no nanofiber peeling off, low air passage resistance, and removal effect of minute harmful particles such as suspended particulate matter Is big.

また、図4に示すように、ワイヤ状の導電体が金又は金で被覆されたもので構成されているときは、走行する導電体に、ナノ繊維原料溶液の液滴を確実に、安定して塗付できる。この液滴は比較的に定間隔で塗付され且つ、塗付された液滴の形状は一定であり、この液滴からは、安定したナノ繊維が噴射され、均一にナノ繊維が含有した不織布又は織布が得られる。また、印加電圧は22KV〜28KVで安定したナノ繊維が生成され、ナノ繊維径は、60nm〜180nmと小さくすることができる。 In addition, as shown in FIG. 4, when the wire-shaped conductor is composed of gold or gold coated, the droplets of the nanofiber raw material solution are reliably and stably applied to the traveling conductor. Can be applied. The droplets are applied at relatively regular intervals, and the shape of the applied droplets is constant. From these droplets, stable nanofibers are ejected, and the nonwoven fabric contains nanofibers uniformly. Or a woven fabric is obtained. In addition, a stable nanofiber is generated at an applied voltage of 22 KV to 28 KV, and the nanofiber diameter can be reduced to 60 nm to 180 nm.

更に、ワイヤ状の導電体がカーボン又はカーボンで被覆されているもので構成されるときも、導電体が金又は金で被覆されたもので構成されているときと、同等の効果が得られ、安定したナノ繊維が噴射され、均一にナノ繊維が含有した不織布又は織布が得られる。 Furthermore, when the wire-like conductor is composed of carbon or carbon-coated one, the same effect can be obtained as when the conductor is composed of gold or gold-coated one, Stable nanofibers are sprayed to obtain a nonwoven fabric or woven fabric containing nanofibers uniformly.

ナノ繊維原料溶液の塗付装置40が、図3に示すようにナノ繊維原料溶液を含浸させたスポンジ41に、導電体を貫通させて、構成されているときは、簡易、安価にナノ繊維原料溶液の塗付装置が作成できる。 When the nanofiber raw material application device 40 is configured by passing a conductor through a sponge 41 impregnated with a nanofiber raw material solution as shown in FIG. 3, the nanofiber raw material is simply and inexpensively configured. Solution applicator can be created.

更にまた、ナノ繊維原料溶液を、定量点滴塗付装置でナノ繊維原料溶液の液滴を導電体に塗付したときは、確実に一定間隔、一定量、安定した一定形状の液滴が塗付でき、この液滴からは安定したナノ繊維が接地電極に向かって、噴射される。 Furthermore, when a nanofiber raw material solution is applied to a conductor using a quantitative drip coater, it is surely applied at a constant interval, a constant amount, and a stable and constant shape. From this droplet, stable nanofibers are ejected toward the ground electrode.

本願他の発明のナノ繊維を含有した不織布又は織布の製造装置における、導電性の無いテープに導電体を印刷して走行させる場合は、帯状に複数の導電体を並列して印刷可能であり、また導電体が軽量になり、取扱いが容易となる。装置全体をコンパクトにできる。 In the manufacturing apparatus for nonwoven fabrics or woven fabrics containing nanofibers of other inventions of the present application, when a conductor is printed on a non-conductive tape and traveled, a plurality of conductors can be printed in parallel in a strip shape. In addition, the conductor becomes light and easy to handle. The entire device can be made compact.

この印刷された導電体に凸部を一定間隔に配設し、この凸部の上端部にナノ繊維原料溶液を定量点滴塗付装置を用いて、ナノ繊維原料溶液を塗付させると、安定したナノ繊維が噴射される。 Protruding portions are arranged at regular intervals on the printed conductor, and the nanofiber raw material solution is applied to the upper end portion of the protruding portions by using a quantitative drip coating apparatus. Nanofibers are jetted.

導電体を固定して、ナノ繊維原料溶液塗付装置を走行させて、導電体にナノ繊維原料溶液を塗付するときも、上述した導電体を走行させたときと同等の効果が得られ、且つ、装置自体がコンパクトになる。 When the conductor is fixed and the nanofiber raw material solution coating device is run to apply the nanofiber raw material solution to the conductor, the same effect as when the above-described conductor is run is obtained. In addition, the device itself becomes compact.

本願発明1に係るナノ繊維含有不織布又は織布の製造装置の基本構成図である。BRIEF DESCRIPTION OF THE DRAWINGS It is a basic block diagram of the manufacturing apparatus of the nanofiber containing nonwoven fabric or woven fabric which concerns on this invention 1. 本願発明1に係る走行する導電体の他の態様の説明図である。It is explanatory drawing of the other aspect of the conductor which drive | works based on this invention. 本願発明1に係るスポンジを用いたナノ繊維原料溶液の塗付装置の例を示す説明図である。It is explanatory drawing which shows the example of the application apparatus of the nanofiber raw material solution using the sponge which concerns on this invention. 導電体に金のワイヤを使用したときのナノ繊維原料溶液の液滴付着状態を示す図である。It is a figure which shows the droplet adhesion state of a nanofiber raw material solution when using a gold wire for a conductor. ステンレスのワイヤを使用したときのナノ繊維原料溶液の液滴付着状態を示す図である。It is a figure which shows the droplet adhesion state of a nanofiber raw material solution when using a stainless steel wire. 指向性電極を設置したときの説明図である。It is explanatory drawing when a directional electrode is installed. 本願発明2のナノ繊維含有不織布又は織布の製造装置に係るテープに導電体を印刷した状態示す説明図である。It is explanatory drawing which shows the state which printed the conductor on the tape which concerns on the manufacturing apparatus of the nanofiber containing nonwoven fabric or woven fabric of this invention. 印刷された導電体にナノ繊維原料溶液を塗付した説明図である。It is explanatory drawing which applied the nanofiber raw material solution to the printed conductor. 本願発明3のナノ繊維含有不織布又は織布の製造装置の基本的構成を示す説明図である。It is explanatory drawing which shows the basic composition of the manufacturing apparatus of the nanofiber containing nonwoven fabric of this-application invention 3, or a woven fabric. ナノ繊維繊維を含有した不織布の切断断面の図である。It is a figure of the cut section of the nonwoven fabric containing nanofiber fiber. 従来技術の不織布にナノ繊維層を積層させる装置の要部図である。It is a principal part figure of the apparatus which laminates | stacks a nanofiber layer on the nonwoven fabric of a prior art.

本願発明を実施するための形態を図に基づいて詳細に説明する。これらの図において共通の部材には共通の符号(番号)を付している。また、図から明らかに判断できる部材には符号をつけていない。これらの図は本願発明を説明するために模式的に描いたものであり本願発明はこれらの図に限定されない。 A mode for carrying out the present invention will be described in detail with reference to the drawings. In these drawings, common members (numbers) are given common members. In addition, members that can be clearly judged from the figure are not labeled. These drawings are schematically drawn for explaining the present invention, and the present invention is not limited to these drawings.

本願発明は、従来技術のエレクトロスピニング法に用いるシリンジに代えて、走行するワイヤ状の導電体にナノ繊維原料溶液の液滴を塗付してナノ繊維を発生させ、不織布又は織布(以下これらを「不織布等30」ともいう。)にナノ繊維を含有させる。従来技術によると、不織布等30にナノ繊維を積層したものが開示されているが、不織布等30にナノ繊維を積層した場合には、ナノ繊維が不織布等30から剥がれやすく、取扱いが困難であった。本願発明は、ナノ繊維を含有した不織布等30の製造装置であって、本願発明に係る装置により、製造された製品はナノ繊維が剥がれおちることが無く、取扱いが容易であり、空気の通過抵抗も小さく、マスク生地、濾過布等に好適に利用できる。 In the present invention, instead of the syringe used in the electrospinning method of the prior art, nanofibers are generated by applying droplets of a nanofiber raw material solution to a traveling wire-like conductor, and a nonwoven fabric or a woven fabric (hereinafter referred to as these) Is also referred to as “nonwoven fabric 30”). According to the prior art, nanofibers laminated on non-woven fabric 30 are disclosed. However, when nanofibers are laminated on non-woven fabric 30, nanofibers are easily peeled off from non-woven fabric 30 and handling is difficult. It was. The present invention is an apparatus for manufacturing a nonwoven fabric 30 containing nanofibers, etc., and the device manufactured by the apparatus according to the present invention is such that the nanofiber does not peel off, is easy to handle, and has an air passage resistance. And can be suitably used for mask fabrics, filter cloths and the like.

また、本願発明は印加電圧のプラス電極側にシリンジを使用しないため、シリンジ開口部においてナノ繊維原料溶液42が、乾燥・固化して汚染されることがない。本願発明に係る装置1は、プラスに印加されるワイヤ状の導電体10が、走行し、常に汚染の無い新しい表面に高電圧が印加される。このため、プラス電極が汚染されることが無く、ナノ繊維原料溶液42の液滴44に安定した電荷を帯電させることができ、ナノ繊維は継続して、安定して生成される。上述したように、ワイヤ状とは、針金のごとく細くて長い形状をいい、断面が円形に限らず、矩形、多角形等も含む。 In addition, since the present invention does not use a syringe on the positive electrode side of the applied voltage, the nanofiber raw material solution 42 is not dried and solidified at the syringe opening. In the device 1 according to the present invention, the wire-like conductor 10 applied to the plus travels and a high voltage is always applied to a new surface free from contamination. For this reason, the positive electrode is not contaminated, the droplet 44 of the nanofiber raw material solution 42 can be charged with a stable charge, and the nanofiber is continuously generated stably. As described above, the wire shape means a thin and long shape like a wire, and the cross section is not limited to a circle but includes a rectangle, a polygon, and the like.

本願発明1には、ワイヤ状の導電体10を複数本並列に配設することができる。シリンジを使用することなく、この導電体10を使用して、これに液滴44を塗付するのであるから、平面上に高密度に液滴44を分布させることができ、ナノ繊維50を大量に工業的規模で製造可能である. In the present invention 1, a plurality of wire-like conductors 10 can be arranged in parallel. Since the conductor 10 is used without using a syringe and the droplets 44 are applied to the conductor 10, the droplets 44 can be distributed with high density on a flat surface, and a large amount of nanofibers 50 can be distributed. It can be manufactured on an industrial scale.

更にまた、従来技術においては、継続して使用したときに、プラス電極であるシリンジも、接地電極側にもナノ繊維で徐々に汚染され、安定したナノ繊維を生成できなくなる。このため、常に、シリンジと接地電極を清掃する必要があった。本願においては、プラス電極となる導電体10は、汚染されることなく、清掃する必要はない。特別な高電圧(例えば50KV以上)を印加しない限り、接地電圧側もほとんど汚染されることはない。大電圧を印加する必要があるときは、接地電極を走行させて清掃作業を省くことができる。 Furthermore, in the prior art, when continuously used, the syringe that is a positive electrode is also gradually contaminated with nanofibers on the ground electrode side, and stable nanofibers cannot be generated. For this reason, it was necessary to always clean the syringe and the ground electrode. In the present application, the conductor 10 serving as the positive electrode is not contaminated and does not need to be cleaned. Unless a special high voltage (for example, 50 KV or more) is applied, the ground voltage side is hardly contaminated. When it is necessary to apply a large voltage, the ground electrode can be run to save the cleaning work.

図1は、本願発明1に係るナノ繊維含有不織布又は織布の製造装置の基本構成図である。本願発明1は、ワイヤ状の導電体10を走行させ、上記導電体10をプラス電極側とする。導電体10は、腐食が少なく導電率が高いものを使用する。例えば、金、銀、銅、ステンレス、カーボン等が挙げられる。これらのものは、いづれも本願発明1の導電体10として使用可能である。 FIG. 1 is a basic configuration diagram of an apparatus for producing a nanofiber-containing nonwoven fabric or woven fabric according to Invention 1 of the present application. In the present invention 1, a wire-like conductor 10 is run, and the conductor 10 is on the positive electrode side. The conductor 10 has a low corrosion and a high conductivity. For example, gold, silver, copper, stainless steel, carbon, etc. are mentioned. Any of these can be used as the conductor 10 of the present invention 1.

これらの金属のうちで、金が好ましく使用できる。プラス電極として用いる導電体10と接地電極20の間には高電圧が印加され、この導電体10には、ナノ繊維原料溶液42が塗付されるため、電極にわずかの化学変化があっても、ナノ繊維50の生成に大きな影響を及ぼす。上述の材質中で銅、銀、ステンレスが比較的反応性に富むこととは対照的に、金は標準酸化・還元電位に基づくイオン化傾向が、全金属中で最も小さく反応性が低い。 Of these metals, gold can be preferably used. A high voltage is applied between the conductor 10 used as the positive electrode and the ground electrode 20, and the nanofiber raw material solution 42 is applied to the conductor 10, so even if there is a slight chemical change in the electrode. This greatly affects the production of the nanofiber 50. In contrast to copper, silver, and stainless steel, which are relatively reactive among the above materials, gold has the lowest ionization tendency based on the standard oxidation / reduction potential among all metals and has low reactivity.

導電体10が金で被覆されているものも特に好ましく用いられる。金で被覆とは、メッキ、蒸着、金フィラーを樹脂等と混練してスラリー状にして塗布することも含む。金で被覆したもの、特に金メッキは、安価であり、金そのものを使用したときと同等の効果を発揮する。
又、カーボンは化学反応性がほとんどなく、金と同等の効果を発揮する。
Particularly preferably, the conductor 10 is coated with gold. Covering with gold includes plating, vapor deposition, and kneading a gold filler with a resin or the like to form a slurry. Those coated with gold, especially gold plating, are inexpensive and exhibit the same effects as when gold itself is used.
Carbon has almost no chemical reactivity and exhibits the same effect as gold.

カーボンからなるワイヤー状の導電体10は、カーボンファイバーを撚って得られる糸をそのまま使用することができる。また、得られる糸が細すぎる場合は、複数の糸を撚り合わせて所望の線径のワイヤー状の導電体10を得ることができる。カーボンファイバー及びカーボンファイバーから得られる糸は、市販されているため、容易に入手できる。
また、カーボンで被覆したものは、カーボンファイバー及び/又は導電性カーボンブラックのフィラーを合成樹脂等を母材としてスラリー状にして金属又は樹脂に塗付して得られる。カーボンで被覆したときは、上記カーボンそのものを使用したときよりも安価であり、カーボンと同等の効果を発揮する。
For the wire-like conductor 10 made of carbon, a yarn obtained by twisting carbon fiber can be used as it is. Moreover, when the obtained yarn is too thin, a plurality of yarns can be twisted together to obtain the wire-like conductor 10 having a desired wire diameter. Since the carbon fiber and the yarn obtained from the carbon fiber are commercially available, they can be easily obtained.
Further, the carbon-coated one can be obtained by applying a filler of carbon fiber and / or conductive carbon black to a metal or resin in a slurry form using a synthetic resin or the like as a base material. When coated with carbon, it is less expensive than when the carbon itself is used, and exhibits the same effect as carbon.

上述の導電体10は、図1に示すように走行させる。巻かれた導電体10の繰出し器11を一方に配設し、他方に巻取り器12を配設して巻き取る。
図2に示すように、一本の導電体で閉鎖回路を架設して、導電体移動装置13でワイヤ状導電体10を走行させることもできる。この、導電体10は、使い捨てにすることもでき、必要に応じて、清掃して再利用もできる。このワイヤ状導電体10は、複数を並列に配設して、ナノ繊維50の生成量を増すことができる。また、他の態様としては、ワイヤ状の導電体10を、エアアクチュエータ、電磁アクチュエータ、逆転モーター等を使用して、往復動させることもできる。
The above-described conductor 10 is run as shown in FIG. The winding device 11 of the wound conductor 10 is disposed on one side, and the winder 12 is disposed on the other side and wound.
As shown in FIG. 2, a closed circuit can be constructed with a single conductor, and the wire-like conductor 10 can be run by the conductor moving device 13. The conductor 10 can be disposable, and can be cleaned and reused as necessary. A plurality of the wire-like conductors 10 can be arranged in parallel to increase the production amount of the nanofibers 50. As another aspect, the wire-like conductor 10 can be reciprocated using an air actuator, an electromagnetic actuator, a reverse rotation motor, or the like.

このワイヤ状の導電体10の直径(導電体の断面が多角形である場合は、対角線)は、印加電圧、ナノ繊維原料溶液42の種類、ナノ繊維50の目付量、導電体10の種類により、任意に選択できる。通常は0.5mm〜0.1mmが用いられる。0.5mm以上であるときは、印加電圧を大きくする必要があるうえに、ワイヤ状の導電体10に塗付されたナノ繊維原料溶液42からナノ繊維50が安定して噴射しない。また、0.1mm以下であるときは、導電体10が破損する恐れがある。好ましくは0.4mm〜0.15mmの導電体10を用いる。この範囲であれば、印加電圧を大きくする必要が無く安全であり、導電体10の強度も十分である。 The diameter of the wire-like conductor 10 (or a diagonal line when the conductor has a polygonal cross section) depends on the applied voltage, the type of the nanofiber raw material solution 42, the basis weight of the nanofiber 50, and the type of the conductor 10. Can be selected arbitrarily. Usually, 0.5 mm to 0.1 mm is used. When it is 0.5 mm or more, it is necessary to increase the applied voltage, and the nanofibers 50 are not stably ejected from the nanofiber raw material solution 42 applied to the wire-like conductor 10. Moreover, when it is 0.1 mm or less, the conductor 10 may be damaged. Preferably, the conductor 10 having a thickness of 0.4 mm to 0.15 mm is used. Within this range, the applied voltage need not be increased and is safe, and the strength of the conductor 10 is sufficient.

図3は、本願発明1に係るスポンジ41を用いたナノ繊維原料溶液42の塗付装置40の例を示す説明図である。上述したように、スポンジ41とは内部に細かな孔が無数に空いた多孔質の柔らかい物質であり、フェルト等を含む物質の総称をいう。ナノ繊維原料溶液42に浸すと孔内の空気と置換される形でナノ繊維原料溶液42を吸い取り、スポンジ41全体の細孔を満たす。 FIG. 3 is an explanatory view showing an example of a coating apparatus 40 for applying the nanofiber raw material solution 42 using the sponge 41 according to the first aspect of the present invention. As described above, the sponge 41 is a porous soft substance having countless fine pores inside, and is a generic name for substances including felt and the like. When immersed in the nanofiber raw material solution 42, the nanofiber raw material solution 42 is sucked in such a manner that the air in the pores is replaced and fills the pores of the entire sponge 41.

タンク43にナノ繊維原料溶液42を入れて、スポンジ41を浸漬してナノ繊維原料溶液42を含浸させる。液位計46を用いて、ナノ繊維原料溶液が使用により減少したときは、ナノ繊維原料溶液補充タンク47から、電磁バルブを開閉して、タンク43の水位を一定に保つ。このナノ繊維原料溶液42を含んだスポンジ41にワイヤ状の導電体10を貫通させて、走行させる。タンク43の減少を目視して、手動でバルブを操作して、ナノ繊維原料溶液42を補充することもできる。 The nanofiber raw material solution 42 is placed in the tank 43, and the sponge 41 is immersed to impregnate the nanofiber raw material solution 42. When the nanofiber raw material solution is reduced by using the liquid level meter 46, the electromagnetic valve is opened and closed from the nanofiber raw material solution replenishing tank 47 to keep the water level in the tank 43 constant. The wire-like conductor 10 is penetrated through the sponge 41 containing the nanofiber raw material solution 42, and is run. By visually observing the decrease of the tank 43, the valve can be manually operated to replenish the nanofiber raw material solution.

塗付装置40を固定して、ナノ繊維原料溶液42を含浸させたスポンジ41に、ワイヤ状の導電部材10を貫通させて、走行させると、この導電部材10にナノ繊維原料溶液42が塗付され、時間の経過(通常は数秒内)とともに、図4、図5に示すように、一定の間隔で液滴44が形成される。
上述の導電体10のスポンジ41内の走行速度は、状導電体10の種類及び線径、ナノ繊維原料溶液の種類、濃度、粘度、抵抗値等により異なるが、走行速度にあまり関係なく図4、図5に示すような液滴が導電体に形成される。通常は、毎秒3cm〜9cmで走行させる。この走行速度であれば、導電体10に連続してナノ繊維原料溶液の液滴が形成される。更に具体的には、導電体10に塗付された液滴44が、ナノ繊維50となって、良好に消滅する速度とすることができる。
When the coating device 40 is fixed and the wire-like conductive member 10 is passed through the sponge 41 impregnated with the nanofiber raw material solution 42 and is run, the nanofiber raw material solution 42 is applied to the conductive member 10. As time passes (usually within a few seconds), droplets 44 are formed at regular intervals as shown in FIGS.
The traveling speed of the conductor 10 in the sponge 41 varies depending on the type and wire diameter of the conductor 10, the kind of nanofiber raw material solution, the concentration, the viscosity, the resistance value, etc. A droplet as shown in FIG. 5 is formed on the conductor. Usually, it runs at 3 to 9 cm per second. At this traveling speed, droplets of the nanofiber raw material solution are formed continuously on the conductor 10. More specifically, the droplet 44 applied to the conductor 10 becomes the nanofiber 50, and the speed at which the droplet 44 disappears can be achieved.

液滴の付着状態は導電体10の材質により、大きく異なる。
図4は、金メッキ製のワイヤ状の導電体10aを使用したときのナノ繊維原料溶液42の液滴付着状態を示す図である。この線径は0.3mmであり、線径を0.45mm、0.23mmにしても、同様に良好な形状であり、液滴44の間隔Xが一定であるのがが認められる。
The adhesion state of the droplets varies greatly depending on the material of the conductor 10.
FIG. 4 is a diagram showing a droplet adhesion state of the nanofiber raw material solution 42 when the wire-like conductor 10a made of gold plating is used. This wire diameter is 0.3 mm. Even when the wire diameters are 0.45 mm and 0.23 mm, the shape is similarly good, and it is recognized that the interval X between the droplets 44 is constant.

図5は、ステンレス製のワイヤ状の導電体10bを使用したときのナノ繊維原料溶液42の液滴44の付着状態を示す図である。この線径は0.3mmであり、液滴44の大きさが一定しない。また、液滴44の間隔Yも一定しない。線径を0.45mm、0.23mmにしても、同様に良好な形状の液滴が得られなく、間隔Yも一定しない。 FIG. 5 is a diagram showing the state of adhesion of the droplets 44 of the nanofiber raw material solution 42 when the stainless steel wire-like conductor 10b is used. This wire diameter is 0.3 mm, and the size of the droplet 44 is not constant. Further, the interval Y between the droplets 44 is not constant. Even if the wire diameters are 0.45 mm and 0.23 mm, similarly good droplets cannot be obtained, and the interval Y is not constant.

この状態で、プラス電極と接地電極に25KVの電圧を印加したとき金及び金で被覆された金メッキ製のワイヤ状の導電体10aからは、安定して、連続的にナノ繊維50の噴射が目視され、生成された不織布を、顕微鏡で観察すると図10に示すように不織布の中にナノ繊維50が均一に含有されていることが認められる。 In this state, when a voltage of 25 KV is applied to the plus electrode and the ground electrode, the nanofibers 50 are stably and continuously ejected from the gold-plated wire-shaped conductor 10a coated with gold and gold. When the produced nonwoven fabric is observed with a microscope, it is recognized that the nanofibers 50 are uniformly contained in the nonwoven fabric as shown in FIG.

一方、ステンレス製のワイヤ10bの線径及び走行速度を代えて、種々試みても、金メッキ製のワイヤ状の導電体10bより優れた、安定した一定の液滴の形状、安定した液滴の間隔は観察できない。また、液滴の付着したステンレス製のワイヤ状の導電体10bと接地電極の間に、30KVを印加したときでも、連続して安定したナノ繊維50の噴射が目視されず、生成された不織布を、顕微鏡で観察すると不織布の中にナノ繊維50が金メッキ製のワイヤ状の導電体10aで試みたときほど均一に含有されていないことが認められる。 On the other hand, even if various attempts are made by changing the wire diameter and traveling speed of the stainless steel wire 10b, the shape of the stable and constant droplets and the stable interval between the droplets are superior to those of the wire-like conductor 10b made of gold plating. Cannot be observed. In addition, even when 30 KV is applied between the wire-like conductor 10b made of stainless steel to which the droplets are attached and the ground electrode, the continuous injection of the nanofibers 50 is not visually observed, and the produced nonwoven fabric is When observed with a microscope, it is recognized that the nanofibers 50 are not contained in the nonwoven fabric as uniformly as the gold-plated wire-shaped conductor 10a.

ナノ繊維原料溶液の塗付装置40は、定量点滴塗布装置(図示せず)を使用することが好ましい。定量点滴塗布装置は、導電体10の材質、直径、ナノ繊維原料溶液に関係なく、常に一定量の液滴を、所望の間隔で塗付できる。この定量点滴塗布装置は、導電体10と塗付部が接触しないものを使用する。この定量点滴塗布装置は例えば、「非接触式ジェットディスペンサー」として普及しているので、市販のものを容易に入手できる。 The nanofiber raw material solution coating apparatus 40 preferably uses a quantitative drip coating apparatus (not shown). Regardless of the material, diameter, and nanofiber raw material solution of the conductor 10, the fixed-quantity drip coating apparatus can always apply a certain amount of droplets at a desired interval. This fixed-quantity drip coating device uses a device in which the conductor 10 and the coating part do not contact each other. For example, since this quantitative drip application device is widely used as a “non-contact type jet dispenser”, a commercially available one can be easily obtained.

導電体10と接地電極20の間に印加される高電圧は、特に限定されない。従来技術のエレクトロスピニング法で印加される電圧が用いられる。導電体10の種類及び直径、ナノ繊維原料溶液の種類、濃度、粘度、導電値等により異なるが、本願発明で使用される印加電圧は、通常15KV〜35KVである。
接地電極20は、上述した導電体10に使用した材質が、そのまま適用できる。この接地電極20は、導電体10に高電圧を印加したとき、ナノ繊維50が織布等30を一部が貫通するため、徐々にナノ繊維50により汚染される場合があり、このため、接地電極20は清掃をする必要が生じる。この場合は、接地電極20は、ロールした金属等又は網状の金属等を図1及び図2に示すように走行させることが好ましい。
The high voltage applied between the conductor 10 and the ground electrode 20 is not particularly limited. A voltage applied by a conventional electrospinning method is used. The applied voltage used in the present invention is usually 15 KV to 35 KV, although it varies depending on the type and diameter of the conductor 10, the type of nanofiber raw material solution, concentration, viscosity, conductivity value, and the like.
The material used for the conductor 10 described above can be applied to the ground electrode 20 as it is. When a high voltage is applied to the conductor 10, the ground electrode 20 may be gradually contaminated by the nanofiber 50 because the nanofiber 50 partially penetrates the woven fabric 30 or the like. The electrode 20 needs to be cleaned. In this case, it is preferable that the ground electrode 20 travels a rolled metal or the like or a net-like metal or the like as shown in FIGS.

不織布等30の材質は、特に限定されない。ロール状の不織布等30を図1、図2、図9に示すように導電体10と接地電極20の間を走行させる。走行速度は、ナノ繊維50の所望の目付量により選択する。ナノ繊維50は、ワイヤ状の導電体10に塗付されたナノ繊維原料溶液42の液滴44から、接地電極20に向かって噴射されて不織布等30に含有・捕集される。捕集効率を上げるために、通常はナノ繊維安定化ダクト60を設けて、ナノ繊維50の噴射される方向を遊動して捕集効率を向上させる。 The material of the nonwoven fabric 30 is not particularly limited. A roll-shaped nonwoven fabric 30 or the like is run between the conductor 10 and the ground electrode 20 as shown in FIGS. The traveling speed is selected according to the desired basis weight of the nanofiber 50. The nanofibers 50 are ejected from the droplets 44 of the nanofiber raw material solution 42 applied to the wire-like conductor 10 toward the ground electrode 20 and are contained and collected in the nonwoven fabric 30 or the like. In order to increase the collection efficiency, normally, a nanofiber stabilization duct 60 is provided, and the collection efficiency is improved by moving in the direction in which the nanofibers 50 are jetted.

上述のナノ繊維原料溶液の材質は特に限定されない。エレクトロスピニング法で従来使用されているものは、使用可能である。例えば、ポリマーとしてポリウレタン、ポリビニルアルコール、ポリアミド、ポリフッ化ビニリデン等が挙げられる。
溶媒としてはポリウレタンにはジメチルホルムアミド、メチルエチルケトン等が挙げられる。他のポリマーには、水、蟻酸、、ジメチルアセトアミド、メチルエチルケトン、アセトン等が挙げられる。ポリマーと溶媒の比率は、導電体10、ポリマーの種類、印加電圧、所望するナノ繊維の径等により、調整される。これらのナノ繊維原料溶液の導電率の調整に例えば硫酸銅等を添加することができる。
導電体が、金、金で被覆されたもの、カーボン又はカーボンで被覆されたものを使用するときは、ポリマーと溶媒の比率を考慮することなく常に安定したナノ繊維50が生成される。
The material of the nanofiber raw material solution described above is not particularly limited. Any conventionally used electrospinning method can be used. Examples of the polymer include polyurethane, polyvinyl alcohol, polyamide, and polyvinylidene fluoride.
Examples of the solvent include dimethylformamide, methyl ethyl ketone and the like as polyurethane. Other polymers include water, formic acid, dimethylacetamide, methyl ethyl ketone, acetone and the like. The ratio of the polymer to the solvent is adjusted by the conductor 10, the type of polymer, the applied voltage, the desired nanofiber diameter, and the like. For example, copper sulfate can be added to adjust the conductivity of these nanofiber raw material solutions.
When the conductor is gold, gold-coated, carbon or carbon-coated, stable nanofibers 50 are always generated without considering the ratio of polymer to solvent.

図6は、指向性電極70を設けた場合の説明図である。指向性とは、ナノ繊維50の噴射を一定方向(接地電極方向)に、誘導する性質等をいう。導電体10に高電圧を印加すると、ナノ繊維50の多くは、接地電極20に向かって噴射されるが、ナノ繊維50の一部は、電気的に低電圧のあらゆる物体にひきつけられる。このため、指向性電極70を設けて、ナノ繊維50の捕集効率を高める。 FIG. 6 is an explanatory diagram when the directional electrode 70 is provided. The directivity refers to the property of inducing the injection of the nanofibers 50 in a certain direction (ground electrode direction). When a high voltage is applied to the conductor 10, most of the nanofibers 50 are ejected toward the ground electrode 20, but a part of the nanofibers 50 is attracted to any electrically low voltage object. For this reason, the directional electrode 70 is provided and the collection efficiency of the nanofiber 50 is improved.

図6(1)は、従来技術における、ナノ繊維50に指向性を付与する方法であり、送風機80、及びナノ繊維安定化ダクト60を設けてナノ繊維50の捕集効率を高める一例である。
図6(2)は、本願発明1において指向性電極70及び指向性電極70aを設置したときの説明図である。指向性電極70は、ワイヤ導電体10を基点にして、接地電極20と対称の方向に、ワイヤ状の導電体10と平行にして架線する。この接地電極の材質は、ワイヤ状の導電体10の材質がそのまま適用できる。この印加電圧は、導電体10に印加する電圧と同じ程度とする。上述の図2における一本の導電体で閉鎖回路を架設した場合も指向性電極の形態の例となる。
FIG. 6 (1) is a method for imparting directivity to the nanofiber 50 in the prior art, and is an example in which the fan 80 and the nanofiber stabilizing duct 60 are provided to increase the collection efficiency of the nanofiber 50.
FIG. 6B is an explanatory diagram when the directional electrode 70 and the directional electrode 70a are installed in the first aspect of the present invention. The directional electrode 70 is wired in parallel to the wire-like conductor 10 in a direction symmetrical to the ground electrode 20 with the wire conductor 10 as a base point. As the material of the ground electrode, the material of the wire-like conductor 10 can be applied as it is. This applied voltage is set to the same level as the voltage applied to the conductor 10. The case where the closed circuit is constructed with the single conductor in FIG. 2 is also an example of the form of the directional electrode.

他の本願発明2は、導電体210を導電性の無いテープ250に沿って、帯状に印刷して、この導電体をプラス電極に使用する。
図7は、テープに導電体を印刷した状態示す説明図である。
図7(1)は、テープに導電体を印刷した平面図である。
図7(2)は、側面図である。
図7(3)は、図7(1)に係るA−A断面図である。
In another invention of the present invention 2, the conductor 210 is printed in a strip shape along the non-conductive tape 250, and this conductor is used as a plus electrode.
FIG. 7 is an explanatory diagram showing a state in which a conductor is printed on a tape.
FIG. 7A is a plan view of a conductor printed on a tape.
FIG. 7B is a side view.
FIG. 7 (3) is a cross-sectional view taken along line AA in FIG. 7 (1).

テープ250の材質は、導電性のないテープであれば、特に制限はない。通常使用される樹脂製テープであるポリエステル系の樹脂テープ、例えばポリエチレンテレフタレート等が挙げられる。テープ250に、並列して複数の導電体210を印刷することもできる。 The material of the tape 250 is not particularly limited as long as it is a non-conductive tape. A polyester resin tape that is a commonly used resin tape, such as polyethylene terephthalate, may be mentioned. A plurality of conductors 210 may be printed on the tape 250 in parallel.

このテープに印刷される導電体210を構成する材質は、上述した発明1に用いられた導電体である、例えば金、銀、銅、カーボン、等が挙げられる。印刷方法は特に限定されない。これらの導電体のフィラーを樹脂等で混練して従来技術に基づいてペースト状にして印刷することができる。蒸着印刷が可能でである導電体は、蒸着印刷することもできる。 Examples of the material constituting the conductor 210 printed on the tape include the conductors used in the above-described invention 1, such as gold, silver, copper, and carbon. The printing method is not particularly limited. These conductor fillers can be kneaded with a resin or the like to be printed in a paste form based on the conventional technique. A conductor that can be vapor-deposited can also be vapor-deposited.

この印刷された導電体210の幅Tは、導電体210の材質、ナノ繊維原料溶液の材質、濃度、印加電圧等によりことなるが、通常は2mm〜0.20mm、好ましくは1.5mm〜0.20mmである。2mmを超えるとナノ繊維50の噴射が劣り、0.20mm以下であると印刷が困難となる。 The width T of the printed conductor 210 varies depending on the material of the conductor 210, the material of the nanofiber raw material solution, the concentration, the applied voltage, and the like, but is usually 2 mm to 0.20 mm, preferably 1.5 mm to 0. 20 mm. If it exceeds 2 mm, the nanofiber 50 is poorly jetted, and if it is 0.20 mm or less, printing becomes difficult.

図8は、導電体210に液滴を塗付した状態を表す。
図8(1)は、上述の導電体210の印刷を平面にした場合の側面図を示す。
図8(2)は、上述の導電体210に突起部211を設けた場合の側面図を示す。
他の本願発明2は、導電体210には、ナノ繊維原料溶液を上述のした発明1で使用した定量点滴塗布装置を用いて、塗付する。
FIG. 8 shows a state where droplets are applied to the conductor 210.
FIG. 8A shows a side view when the above-described conductor 210 is printed on a plane.
FIG. 8B shows a side view in the case where the protrusion 211 is provided on the conductor 210 described above.
In another invention 2 of the present application, the nanofiber raw material solution is applied to the conductor 210 using the quantitative drip coating apparatus used in the invention 1 described above.

この突起部211の上に、ナノ繊維原料溶液42を定量点滴塗付装置で塗付した場合は、図8(1)に示した導電体10を平面帯状に印刷して、ナノ繊維原料溶液42を塗付した場合よりも、ナノ繊維50の噴射が良好となる。 When the nanofiber raw material solution 42 is applied onto the protrusion 211 with a quantitative drip application device, the conductor 10 shown in FIG. The nanofibers 50 can be sprayed better than when applied.

本願発明2においては、上述のテープ250上に導電体210を印刷して、この導電体210に定量点滴塗付装置を用いて、ナノ繊維原料溶液42を塗付することを除いて上述の本願発明1の構成がそのまま、適用される。 In the second aspect of the present invention, the conductor 210 is printed on the tape 250 described above, and the nanofiber raw material solution 42 is applied to the conductor 210 using a quantitative drip coater. The configuration of the invention 1 is applied as it is.

他の本願発明3は、導電体10を固定して設け、この導電体10をプラス電極側とし、導電体10に、ナノ繊維原料溶液42の塗付装置40を往復動させて、間隔を設けてナノ繊維原料溶液42の液滴44を塗付し、導電体10と接地電極20との間に不織布等30を走行させ、不織布等30にナノ繊維を含有させる製造装置である。 In another invention 3 of the present application, the conductor 10 is fixedly provided, the conductor 10 is set as the positive electrode side, and the coating device 40 of the nanofiber raw material solution 42 is reciprocated on the conductor 10 to provide an interval. Then, a droplet 44 of the nanofiber raw material solution 42 is applied, the nonwoven fabric 30 is run between the conductor 10 and the ground electrode 20, and the nonwoven fabric 30 contains the nanofiber.

図9は、本願発明3のナノ繊維含有不織布又は織布の製造装置3の基本的構成を示す説明図である。図3に示す上述のナノ繊維原料溶液42の塗付装置40のスポンジ41に導電体10を貫通させ、導電体10の両端を固定具311で固定する。このナノ繊維原料溶液42の塗付装置40をコンベア300のベルト301に固定し、更に、ガイド302をガイド固定具303で固定して、ナノ繊維原料溶液42の塗付装置40の走行を安定化する。 FIG. 9 is an explanatory diagram showing a basic configuration of the nanofiber-containing nonwoven fabric or woven fabric manufacturing apparatus 3 according to the third aspect of the present invention. The conductor 10 is passed through the sponge 41 of the coating device 40 for the nanofiber raw material solution 42 shown in FIG. 3, and both ends of the conductor 10 are fixed with a fixture 311. The nanofiber raw material solution 42 application device 40 is fixed to the belt 301 of the conveyor 300, and the guide 302 is fixed by the guide fixture 303 to stabilize the traveling of the nanofiber raw material solution 42 application device 40. To do.

コンベア301をモーターMで、ナノ繊維原料溶液の塗付装置40を往復動させる。モーターMにサーボモーターを使用して、往復動及び走行速度をコントロールすることができる。また、通常のモーターを使用して、ガイド302又は導電体10にリミットスイッチを設けて、正逆回転させて、往復走行させることもできる。また、エアーア式クチュエーター、油圧式アクチュエーター、電磁式アクチュエーター等を使用してナノ繊維原料溶液42の塗付装置40を往復動走行をさせることもできる。
導電体10を固定して、ナノ繊維原料溶液42の塗付装置40を走行させる以外の構成は、上述の、本願発明1のものが、そのまま適用できる。
The conveyor 301 is reciprocated by the motor M with the nanofiber raw material solution coating apparatus 40. A servo motor can be used for the motor M to control reciprocation and traveling speed. In addition, using a normal motor, a limit switch may be provided on the guide 302 or the conductor 10, and the reciprocating motion may be performed by rotating forward and backward. Further, the nanofiber raw material solution application device 40 can be reciprocated using an air actuator, a hydraulic actuator, an electromagnetic actuator, or the like.
For the configuration other than fixing the conductor 10 and running the coating device 40 of the nanofiber raw material solution 42, the above-described configuration of the present invention 1 can be applied as it is.

図10は、ナノ繊維を含有した不織布の切断断面を1000倍で撮影した図面代用写真である。具体的には金メッキを施したワイヤ状の直径0.3mmの導電体10に、スポンジを用いた塗付装置を用いて、ポリウレタン溶液の液滴44を塗付して、25KVの電圧を印加したときの図面代用写真である。不織布30を構成する不織布ファイバー30aの間にナノ繊維50が蜘蛛の巣状態に存在することが確認される。このナノ繊維の線径は60nm〜180nmと推定される。 FIG. 10 is a drawing-substituting photograph in which a cut section of a nonwoven fabric containing nanofibers was photographed at a magnification of 1000 times. Specifically, a droplet of polyurethane solution 44 was applied to a wire-like conductor 10 having a diameter of 0.3 mm that was plated with gold using a sponge application device, and a voltage of 25 KV was applied. It is a photograph substituted for drawing. It is confirmed that the nanofiber 50 exists in the state of the spider web between the nonwoven fabric fibers 30a constituting the nonwoven fabric 30. The wire diameter of the nanofiber is estimated to be 60 nm to 180 nm.

図11は、従来技術のシリンジ49を使用したエレクトロスピニング法を用いて、不織布に、ナノ繊維層を積層させる装置の要部拡大断面図である。 FIG. 11 is an enlarged cross-sectional view of a main part of an apparatus for laminating a nanofiber layer on a nonwoven fabric using an electrospinning method using a syringe 49 of the prior art.

1 本願発明のナノ繊維を含有した不織布又は織布の製造装置
3 本願他の発明であるナノ繊維を含有した不織布又は織布の製造装置
10 導電体
10a 金メッキ製のワイヤ状の導電体
10b ステンレス製のワイヤ状の導電体
11 繰出し器
12 巻取り器
13 導電体移動装置
20 接地電極
30 不織布又は織布(不織布等)
30a 不織布構成ファイバー
40 塗付装置
41 スポンジ
42 ナノ繊維原料溶液
43 タンク
44 液滴
45 電磁バルブ
46 液位計
49 シリンジ
50 ナノ繊維
60 ナノ繊維安定化ダクト
70 指向性電極
80 送風機
210 導電体
211 凸部
250 テープ
300 コンベア
301 ベルト
302 ガイド
303 ガイド固定具
311 導電体固定具
M モータ
X 液滴の間隔
Y 液滴の間隔
DESCRIPTION OF SYMBOLS 1 Manufacturing apparatus of the nonwoven fabric or woven fabric containing the nanofiber of this invention 3 Manufacturing apparatus 10 of the nonwoven fabric or woven fabric containing the nanofiber which is another invention of this application 10 Conductor 10a Wire-shaped conductor 10b made of gold plating Made of stainless steel Wire-shaped conductor 11 Feeder 12 Winder 13 Conductor moving device 20 Ground electrode 30 Nonwoven fabric or woven fabric (nonwoven fabric, etc.)
30a Non-woven fabric fiber 40 Application device 41 Sponge 42 Nanofiber raw material solution 43 Tank 44 Droplet 45 Electromagnetic valve 46 Level gauge 49 Syringe 50 Nanofiber 60 Nanofiber stabilization duct 70 Directional electrode 80 Blower 210 Conductor 211 Convex 250 Tape 300 Conveyor 301 Belt 302 Guide 303 Guide fixture 311 Conductor fixture M Motor X Droplet interval Y Droplet interval

Claims (4)

ワイヤ状の導電体を走行させ、上記導電体をプラス電極側として、
上記導電体は、金からなる導電体、カーボンからなる導電体、金を被覆した導電体
びカーボンを被覆した導電体、の群から選ばれるいずれか1種からなり、
上記導電体の直径は0.5mm〜0.1mmであり、
上記導電体にナノ繊維原料溶液の塗付装置を用いて、間隔を設けて上記ナノ繊維原
料溶液の液滴を塗付し、
上記導電体と接地電極との間に不織布又は織布を走行させ、
上記導電体と上記接地電極の間に高電圧を印加して、
上記不織布又は上記織布にナノ繊維を含有させることを特徴とするナノ繊維を含
有した不織布又は織布の製造装置。
Run a wire-like conductor, the conductor as a positive electrode side,
The conductor is a conductor made of gold, a conductor made of carbon, or a conductor coated with gold.
And one selected from the group of conductors coated with carbon,
The conductor has a diameter of 0.5 mm to 0.1 mm,
Using the nanofiber raw material solution application device to the conductor , the nanofiber raw material solution droplets are applied at intervals,
Run a nonwoven fabric or woven fabric between the conductor and the ground electrode,
Applying a high voltage between the conductor and the ground electrode,
An apparatus for producing a nonwoven fabric or woven fabric containing nanofibers, wherein the nonwoven fabric or woven fabric contains nanofibers.
上記ナノ繊維原料溶液の上記塗付装置は、上記ナノ繊維原料溶液を含浸させたスポ
ンジに、上記導電体を貫通させてなる請求項1に記載のナノ繊維を含有した不織布
又は織布の製造装置。
2. The nanofiber-containing non-woven fabric or woven fabric according to claim 1 , wherein the nanofiber raw material solution coating apparatus is a sponge impregnated with the nanofiber raw material solution, and the conductor is passed through the sponge. apparatus.
導電体を導電性の無いテープに印刷して走行させ、上記導電体をプラス電極側とし、
上記導電体にナノ繊維原料溶液を定量点滴塗付装置を用いて、間隔を設けて上記ナ
ノ繊維原料溶液の液滴を上記テープに印刷された上記導電体に塗付し、
上記導電体と接地電極との間に不織布又は織布を走行させ、
上記導電体と上記接地電極の間に高電圧を印加して、
上記不織布又は上記織布にナノ繊維を含有させることを特徴とするナノ繊維を含
有した不織布又は織布の製造装置。
Print the conductor on non-conductive tape and run it, the conductor is the positive electrode side,
The nanofiber raw material solution is applied to the conductor using a quantitative drip coater, and droplets of the nanofiber raw material solution are applied to the conductor printed on the tape at intervals.
Run a nonwoven fabric or woven fabric between the conductor and the ground electrode,
Applying a high voltage between the conductor and the ground electrode,
An apparatus for producing a nonwoven fabric or woven fabric containing nanofibers, wherein the nonwoven fabric or woven fabric contains nanofibers.
ワイヤー状の導電体を固定して設け、上記導電体をプラス電極側とし、
上記導電体に、ナノ繊維原料溶液の塗付装置を往復動させて、間隔を設けて上記ナ
ノ繊維原料溶液の液滴を塗付し、
上記導電体と接地電極との間に不織布又は織布を走行させ、
上記導電体と上記接地電極の間に高電圧を印加して、
上記不織布又は上記織布にナノ繊維を含有させることを特徴とするナノ繊維を含
有した不織布又は織布の製造装置。
A wire-like conductor is fixed and provided, and the conductor is on the positive electrode side,
The nanofiber raw material solution applicator is reciprocated on the conductor to apply droplets of the nanofiber raw material solution at intervals.
Run a nonwoven fabric or woven fabric between the conductor and the ground electrode,
Applying a high voltage between the conductor and the ground electrode,
An apparatus for producing a nonwoven fabric or woven fabric containing nanofibers, wherein the nonwoven fabric or woven fabric contains nanofibers.
JP2016003177A 2016-01-12 2016-01-12 An apparatus for producing a nonwoven fabric or woven fabric containing nanofibers. Active JP6586019B2 (en)