JP2554514B2 - Hair cosmetics - Google Patents
Hair cosmeticsInfo
- Publication number
- JP2554514B2 JP2554514B2 JP63004351A JP435188A JP2554514B2 JP 2554514 B2 JP2554514 B2 JP 2554514B2 JP 63004351 A JP63004351 A JP 63004351A JP 435188 A JP435188 A JP 435188A JP 2554514 B2 JP2554514 B2 JP 2554514B2
- Authority
- JP
- Japan
- Prior art keywords
- cationic polymer
- hair
- cosmetic composition
- hair cosmetic
- formula
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Expired - Fee Related
Description
【発明の詳細な説明】 ［産業上の利用分野］ 本発明は毛髪に対し、優れた光沢を与え、なめらかな
感触を付与しながら、かつ良好なセット保持力を有する
毛髪化粧料に関するものである。DETAILED DESCRIPTION OF THE INVENTION [Industrial application] The present invention relates to a hair cosmetic composition which imparts excellent gloss and a smooth feel to hair and has good set-holding power. .
［従来の技術］ 従来、毛髪化粧料には毛髪に光沢やなめらかさを与え
る目的でシリコーン油、エステル油、炭化水素油などの
油分を、可溶化、乳化、溶解して用いられている。特に
シリコーン油は、表面張力が低く毛髪へのなじみに優
れ、良い光沢が得られる為、近年多用されている。[Prior Art] Conventionally, hair cosmetics have been used by solubilizing, emulsifying, and dissolving oil components such as silicone oil, ester oil, and hydrocarbon oil for the purpose of imparting gloss and smoothness to hair. In particular, silicone oil has been widely used in recent years because it has a low surface tension, is excellent in conformity to hair, and has good gloss.
また、毛髪セットの目的で高分子化合物；ポリビニー
ルピロリドン系ポリマー、酸性アクリル系ポリマーある
いはエチレンと無水マレイン酸との共重合体ポリマー等
が配合されている。Further, for the purpose of hair setting, a high molecular compound such as a polyvinylpyrrolidone-based polymer, an acidic acrylic polymer or a copolymer of ethylene and maleic anhydride is blended.
［発明が解決しようとする問題点］ しかしながら、シリコーン油に代表される油分では、
油分のもつ限界があり多量に用いたり、消費者が長いあ
いだ使用したりすると、頭髪のきしみ感が増したり脂ぎ
るといった欠点があった。更に、髪の毛や手から洗い落
とす際にも水洗いで簡単におとせるものではなかった。
又なめらかさを付与する目的でカチオン界面活性剤を多
用されているが、望ましい光沢を与えるものではなく、
多量に配合すると安全性上も好ましくないという欠点が
あった。[Problems to be Solved by the Invention] However, in oils represented by silicone oil,
When oil is used in a large amount due to the limit of oil content, or when used for a long time by consumers, it has a drawback that the squeaky feeling of the hair is increased or it becomes greasy. Furthermore, even when it is washed off from hair or hands, it cannot be easily washed off with water.
Also, a cationic surfactant is often used for the purpose of imparting smoothness, but it does not give a desired gloss,
There is a drawback in that it is not preferable from the viewpoint of safety if a large amount is blended.
一方、毛髪セットの目的で配合される上述の高分子化
合物も毛髪の固定すなわちセト力に優れるものの、光
沢、なめらかさを満足するものではなかった。On the other hand, the above-mentioned polymer compound blended for the purpose of hair setting is also excellent in fixing, ie, settling force of hair, but is not satisfactory in gloss and smoothness.
従って、本発明の目的は、上記のような欠点を解消
し、毛髪に優れた光沢を与え、なめらかな感触を付与
し、頭髪の脂じみやきしみがなく、更に髪や手からの水
洗いが簡単でかつ適度なセット力を有する毛髪化粧料を
提供することにある。Therefore, the object of the present invention is to eliminate the above-mentioned drawbacks, to impart excellent luster to hair, to impart a smooth feel, to the hair without greasiness and creaking, and to easily wash with water from the hair and hands. And to provide a hair cosmetic having an appropriate setting force.
［問題点を解決するための手段］ 本発明者等は、上記目的を達成すべく鋭意研究した結
果、特定のポリオキシアルキレン変性オルガノポリシロ
キサンとカチオン性高分子とを組み合わせて用いたなら
ば、上記目的を達成できることを見出し、この知見に基
づいて本発明を完成するに至った。[Means for Solving the Problems] As a result of intensive studies to achieve the above object, the present inventors have found that if a specific polyoxyalkylene-modified organopolysiloxane and a cationic polymer are used in combination, It has been found that the above object can be achieved, and the present invention has been completed based on this finding.
即ち、本発明は、一般式［Ａ］、［Ｂ］、［Ｃ］、
［Ｄ］で示されるポリオキシアルキレン変性オルガノポ
リシロキサンの１種又は２種以上と、カチオン性高分子
１種又は２種以上とを配合することを特徴とする毛髪化
粧料である。That is, the present invention relates to general formulas [A], [B], [C],
A hair cosmetic comprising one or more polyoxyalkylene-modified organopolysiloxanes represented by [D] and one or more cationic polymers.
（式中、Ｒは炭素数１乃至３のアルキル基、又はフェニ
ル基、Ｒ′は水素、又は炭素数１乃至６のアルキル基、
ｐは１乃至５の整数、ｍは０乃至100の整数、ｎおよび
ｘは１乃至100の整数、ｔおよびｙは０乃至50の整数で
あり、ｍ、ｎ、ｘおよびｙは平均数であり、分子中にポ
リオキシアルキレン基を40〜90重量％含有し、且つ25℃
で10〜3000センチストークスの粘度を有するように選ば
れる。） 以下、本発明の構成について、更に詳細に説明する。 (In the formula, R is an alkyl group having 1 to 3 carbon atoms, or a phenyl group, R'is hydrogen, or an alkyl group having 1 to 6 carbon atoms,
p is an integer of 1 to 5, m is an integer of 0 to 100, n and x are integers of 1 to 100, t and y are integers of 0 to 50, and m, n, x and y are average numbers. , Containing 40 to 90% by weight of polyoxyalkylene group in the molecule, and 25 ℃
Is selected to have a viscosity of 10 to 3000 centistokes. ) Hereinafter, the configuration of the present invention will be described in more detail.
本発明において用いられるポリオキシアルキレン変性
オルガノポリシロキサンは、上記の一般式［Ａ］、
［Ｂ］、［Ｃ］、［Ｄ］で示されるもので、ポリオキシ
アルキレン基を該重合体全重量に対して40〜90重量％、
好ましくは、50〜80重量％含有し、且つ25℃において10
〜3000センチストークスの粘度を有するものである。The polyoxyalkylene-modified organopolysiloxane used in the present invention has the above general formula [A],
Those represented by [B], [C] and [D], wherein the polyoxyalkylene group is 40 to 90% by weight based on the total weight of the polymer,
Preferably, the content is 50 to 80% by weight and 10 at 25 ° C.
It has a viscosity of ~ 3000 centistokes.
即ち、該重合体全重量に対するポリオキシアルキレン
基の量が40重量％未満の場合には、カチオン性高分子と
の相溶性が悪くなりその為、乾燥後のツヤが劣化し又、
髪や手についた時の水洗いも悪くなる。一方、90重量％
を越えると、なめらかさや、毛髪のセット性を落とす方
向に作用するため好ましくない。又、粘度については、
10センチストークスより低い場合は、きしみ感が増し更
にツヤの持続性が劣り、3000センチスークスを越える
と、べたつきが好ましくない。That is, when the amount of the polyoxyalkylene group relative to the total weight of the polymer is less than 40% by weight, the compatibility with the cationic polymer becomes poor, and thus the gloss after drying deteriorates,
Washing with water on your hair and hands will also be poor. On the other hand, 90% by weight
If it exceeds the range, it is not preferable because it acts in the direction of smoothness and hair settability. Also, regarding the viscosity,
When it is lower than 10 centistokes, the squeaky feeling is increased and the durability of gloss is deteriorated, and when it exceeds 3000 centistokes, stickiness is not preferable.
ポリオキシアルキレン変性オルガノポリシロキサンの
配合量は、毛髪化粧料全量中の0.1〜20重量％であり好
ましくは、0.5〜10重量％である。0.1重量％未満では、
ツヤの持続性やなめらかさが劣り、20重量％を越える
と、なめらかさや、毛髪のセット等の仕上りが劣り好ま
しくない。The amount of the polyoxyalkylene-modified organopolysiloxane compounded is 0.1 to 20% by weight, preferably 0.5 to 10% by weight, based on the total amount of the hair cosmetic composition. Below 0.1% by weight,
If the gloss and durability are inferior, and if it exceeds 20% by weight, the smoothness and the finish of hair setting are inferior, which is not preferable.
本発明で用いられるカチオン性高分子は、製品中で可
溶または、分散性の重合体であり、例えば一般式（Ｅ） （式中、R5及びR6は水素原子またはメチル基をＸはハロ
ゲン原子を表し、Ｐは150ないし6,200の整数である。） で表されるポリ（ジメチルジアリルアンモニウムハライ
ド）型カチオン性ポリマー、または一般式（Ｆ） もしくは （式中、R7及びR8は水素原子またはメチル基をＸはハロ
ゲン原子を表し、ｑ＋ｒは150ないし9000の整数であ
る。） で表されるジメチルジアリルアンモニウムハライドとア
クリルアミドの共重合体カチオン性ポリマー、または第
４級窒素含有セルロースエーテル、またはポリエチレン
グリコール、エピクロルヒドリン、プロピレンアミン及
び牛脂脂肪酸より得られるタロイルアミンの縮合生成
物、またはビニルピロリドン・ジメチルアミノエチルメ
タクリレート共重合体カチオン化物等が挙げられる。The cationic polymer used in the present invention is a polymer that is soluble or dispersible in the product and has, for example, the general formula (E). (In the formula, R 5 and R 6 are hydrogen atoms or methyl groups, X is a halogen atom, and P is an integer of 150 to 6,200.) A poly (dimethyldiallylammonium halide) type cationic polymer represented by the following formula: Or general formula (F) Or (In the formula, R 7 and R 8 are hydrogen atoms or methyl groups, X is a halogen atom, and q + r is an integer of 150 to 9000.) Copolymer of dimethyldiallylammonium halide and acrylamide Cationic Polymers, quaternary nitrogen-containing cellulose ethers, condensation products of polyethylene glycol, epichlorohydrin, propyleneamine and tallowylamine obtained from tallow fatty acid, vinylpyrrolidone / dimethylaminoethylmethacrylate copolymer cationized products and the like can be mentioned.
一般式（Ｅ）で表されるポリ（ジメチルジアリルアン
モニウムハライド）型カチオン性高分子のＸはハロゲン
でクロル、ブロム等であり、このうちクロルのものとし
ては、マーコート100（Merquat 100）という商品名で米
国メルク社（Merck ＆ Co.Inc.）から販売されているも
のなどを挙げることができる。このマーコート100は、
純分約40％の水溶液になっており、淡黄色の粘稠な液体
である。X of the poly (dimethyldiallylammonium halide) type cationic polymer represented by the general formula (E) is a halogen such as chlorine, bromine, etc. Among these, chlorine is known as Merquat 100. The products sold by Merck & Co. Inc. in the United States can be mentioned. This Marcourt 100 is
It is an approximately 40% pure aqueous solution, which is a pale yellow viscous liquid.
一般式（Ｆ）で表されるジメチルジアリルアンモニウ
ムハライドとアクリルアミドの共重合体型カチオン性ポ
リマーのＸはハロゲンでクロル、ブロム等であり、また
便宜的に一般式（Ｆ）で表現しているが、必ずしもブロ
ック型共重合体でなければならない訳ではなく、モノマ
ーの配列順序は任意で構わない。これらの例としては、
Ｘがクロルであるマーコート550（Merquat 550）［米国
メルク社（Merquar ＆ Co.Inc.）］などを挙げることが
できる。このマーコート550は、純分８％の水溶液にな
っており無色の粘稠な液体である。X in the copolymer type cationic polymer of dimethyldiallylammonium halide and acrylamide represented by the general formula (F) is halogen such as chlorine, bromine, etc., and is represented by the general formula (F) for convenience. It does not necessarily have to be a block-type copolymer, and the order of arranging the monomers may be arbitrary. Examples of these are
Mention may be made, for example, of Merquat 550 where X is chlor (Merquart & Co. Inc.). This Marquat 550 is a colorless viscous liquid which is an aqueous solution having a pure content of 8%.
ポリエチレングリコール、エピクロルヒドリン、プロ
ピレンアミン及びタロイルアミンもしくは、ココイルア
ミンの縮合生成物の例としては、ポリコートＨ（Polyqu
at H）という商品名で、西独ヘンケル社（Henkel Inter
national Co.）から販売されているものなどを挙げるこ
とができる。このポリコートＨは、純分約50％の水溶液
になっており淡黄色の粘稠な液体である。Examples of condensation products of polyethylene glycol, epichlorohydrin, propylene amine and taroyl amine or cocoyl amine include Polycoat H (Polyqu
at H) under the trade name Henkel Inter
National Co.) and so on. The polycoat H is a pale yellow viscous liquid which is an aqueous solution having a pure content of about 50%.
第４級窒素含有セルロースは、ポリマーJR−400（Pol
ymer JR−400）、ポリマーJR−125（Polymer JR−125）
ポリマーJR−30M（Polymer JR−30M）という商品名で、
米国ユニオンカーバイト社（Union Carbide Corp.）か
ら販売されているものなどである。ポリマーJRシリーズ
は白色又は、淡黄色の粉末である。The quaternary nitrogen-containing cellulose is polymer JR-400 (Pol
ymer JR-400), polymer JR-125 (Polymer JR-125)
With the trade name of Polymer JR-30M (Polymer JR-30M),
For example, those sold by Union Carbide Corp. of the United States. Polymer JR series is white or light yellow powder.
ビニルピロリドン・ジメチルアミノエチルメタクリレ
ート共重合体カチオン化物はガフコート755（Gafquat 7
55）、ガフコート734（Gafquat 734）という商品名で米
国GAF社（GAF Corp.）から販売されているものなどであ
る。Vinylpyrrolidone-dimethylaminoethylmethacrylate copolymer cationized compound is available on Gafquat 755 (Gafquat 7
55), such as those sold by the US GAF Corp. (GAF Corp.) under the trade name of Gafquat 734.
ガフコート755は純分約20％の水溶液で淡黄色の粘稠
な何液体であり、カフコート734は純分約50％のアルコ
ール溶液で淡黄色の液体である。The guff coat 755 is a pale yellow viscous liquid which is an aqueous solution of about 20% pure, and the cuff coat 734 is a pale yellow liquid which is an alcohol solution of about 50% pure.
上記カチオン性高分子は単独又は、二種以上を混合し
て配合することができるが、その適正な配合量は、本発
明の毛髪化粧料全量中の0.1〜15重量％の範囲、好まし
くは、0.2〜10％である。0.1重量％未満では、本発明の
効果が発揮されず、15％を越える配合料では、べたつき
が現れ好ましくない。The above cationic polymers can be blended alone or in a mixture of two or more, and the proper blending amount thereof is in the range of 0.1 to 15% by weight, preferably, in the total amount of the hair cosmetic composition of the present invention, 0.2 to 10%. If it is less than 0.1% by weight, the effect of the present invention is not exhibited, and if it exceeds 15%, stickiness appears and it is not preferable.
本発明の毛髪化粧料には上記の必須構成成分に加え
て、目的に応じて本発明の効果を損なわない量的、質的
範囲で、油分、水溶性高分子、分子中に２個以上の水酸
基を有する多価アルコール等の保湿剤、キレート剤、酸
化防止剤、紫外線吸収剤、界面活性剤、防腐剤、ビタミ
ン・ホルモン等の薬剤、コラーゲン・ケラチン・エラス
チン等の加水分解物、アミノ酸、ペプタイド類、天然多
糖類、粉末類、香料を配合してもよい。又、溶剤として
エタノールまたは水、エアゾールタイプのヘアスプレー
用のプロペラントガスとして種々のハロゲン化炭化水
素、LPG、ジメチルエーテル、炭酸ガス、窒素ガス等を
配合することもできる。In addition to the above-mentioned essential constituents, the hair cosmetic composition of the present invention contains, in a quantitative and qualitative range depending on the purpose, an oil component, a water-soluble polymer, and two or more in the molecule, in a quantitative and qualitative range. Moisturizers such as polyhydric alcohols having hydroxyl groups, chelating agents, antioxidants, ultraviolet absorbers, surfactants, preservatives, drugs such as vitamins and hormones, hydrolysates of collagen, keratin, elastin, etc., amino acids, peptides You may mix | blend kind, natural polysaccharides, powders, and a fragrance | flavor. Further, ethanol or water as a solvent, and various halogenated hydrocarbons, LPG, dimethyl ether, carbon dioxide gas, nitrogen gas and the like as a propellant gas for an aerosol type hair spray can be blended.
［発明の効果］ 本発明は毛髪に対し、優れた光沢を与え、なめらかな
感触を付与し、頭髪の脂じみやきしみがなく、更に髪や
手からの水洗いが簡単でかつ適度なセット力を有する毛
髪化粧料を提供するものである。[Advantages of the Invention] The present invention imparts excellent gloss to the hair, imparts a smooth feel to the hair, does not cause greasiness or squeaks on the hair, and is easy to wash with water from the hair or hands and has an appropriate setting force. The present invention provides a hair cosmetic composition.
［実施例］ 以下、実施例により本発明をさらに詳細に説明する。
本発明はこれらによって限定されるものではない。配合
量は全て重量％である。[Examples] Hereinafter, the present invention will be described in more detail with reference to Examples.
The present invention is not limited by these. All compounding amounts are weight%.
尚、効果の判定は、以下の評価法によった。 The evaluation of the effect was based on the following evaluation method.
使用性評価方法 女性パネル20名により、試料4gを実際に頭髪に直接塗
布し、各自好みのヘアスタイルにセットした後、官能に
よって評価した。Usability evaluation method Twenty female panelists actually applied 4 g of the sample directly to the hair, set the hairstyle to their liking, and evaluated it by sensory evaluation.
評価は以下の４段階評価で行なった。 The evaluation was performed according to the following four-level evaluation.
著しく良好であれば◎、良好であれば○、普通であれ
ば△、劣っていれば×と評価した。Remarkably good, ⊚, good, ◯, normal, and poor.
実施例１〜４、比較例１〜６ 表−１に示す組成の毛髪化粧料を以下の製法にて調製
した。Examples 1 to 4 and Comparative Examples 1 to 6 Hair cosmetics having the compositions shown in Table 1 were prepared by the following production method.
（製法） No.3にNo.1,2,4,5,6,を溶解した後No.7を溶解したNo.
8を添加し表−１にしめす毛髪化粧料を得た。(Manufacturing method) No. 1, 2, 4, 5, 6 was dissolved in No. 3 and then No. 7 was dissolved.
8 was added to obtain a hair cosmetic composition shown in Table 1.
なお、ポリオキシアルキレン変性オルガノポリシロキ
サンは、一般式［Ａ］で示される構造式（R:メチル基,
R′：水素,p＝３）で、ポリオキシアルキレン含有率な
らびに、粘度の条件は表−１に示した通りである。The polyoxyalkylene-modified organopolysiloxane has a structural formula (R: methyl group,
R ': hydrogen, p = 3), and the conditions of polyoxyalkylene content and viscosity are as shown in Table-1.
又、カチオン性高分子は以下の通りである。 The cationic polymer is as follows.
（注−１）…ポリマーJR−400 （米国Union Carbide社製） 白〜淡黄色粉末 （注−２）…マーコート100（米国 Merck社製） 純分 約40％水溶液 （注−３）…ポリコートＨ（西独 Henkel社製） 純分 約50％水溶液 （注−４）…ガフコート755（米国 GAF社製） 純分 約20％水溶液 表−１からわかるように、本発明の毛髪化粧料におい
ては、カチオン性高分子と特定のポリオキシアルキレン
変形オルガノポリシロキサンが共存することが必須で、
しかもポリオキシアルキレン変性オルガノポリシロキサ
ンが本発明の範囲からはずれる場合、なめらかさ、べた
つきのなさ、きしみ感のなさが著しく劣り、ツヤの持続
性、セット力、手からの洗い落としも好ましくないこと
が明らかである。(Note-1): Polymer JR-400 (manufactured by Union Carbide, USA) White to pale yellow powder (Note-2): Marcoat 100 (manufactured by Merck, USA) About 40% pure aqueous solution (Note-3): Polycoat H (West Germany Henkel) about 50% pure water solution (Note-4) ... Gaff Coat 755 (US GAF) about 20% pure water solution As can be seen from Table-1, in the hair cosmetic composition of the present invention, it is essential that the cationic polymer and the specific polyoxyalkylene-modified organopolysiloxane coexist,
Moreover, when the polyoxyalkylene-modified organopolysiloxane is out of the scope of the present invention, the smoothness, non-greasiness and squeaky feeling are remarkably inferior, and the persistence of gloss, setting power and washing off from hands are also unfavorable. Is.
実施例５ トリートメントローション 下記処方の毛髪化粧料を調製し、毛髪に直接塗布し、
洗い長さずに使用性の評価を行なった。Example 5 Treatment Lotion A hair cosmetic composition having the following formulation was prepared and directly applied to hair.
Usability was evaluated without washing length.
（１）ポリオキシアルキレン変性オルガノポリシロキサ
ン （一般式［Ａ］,Rの５％がフェニル基で残りはメチル
基,R′は水素,p＝3, ポリオキシエチレン基含有率50％， ポリオキシプロピレン基含有率20％， 粘度400CS/25℃） 2.0 （２）ガフコート755（GAF Corp.） 2.0 （３）1,3−ブチレングリコール 1.0 （４）メチルパラベン 0.1 （５）コラーゲン加水分解物 1.0 （６）ポリオキシエチレン（15モル付加） オレイルアルコールエーテル 0.5 （７）香料 適量 （８）エタノール 20.0 （９）精製水 残余 製法 （８）に（１）、（２）、（４）、（６）、（７）を
溶解し、（３）、（５）を溶解した（９）を混合しトリ
ートメントローションを得た。(1) Polyoxyalkylene-modified organopolysiloxane (general formula [A], 5% of R is a phenyl group, the rest is a methyl group, R'is hydrogen, p = 3, polyoxyethylene group content 50%, polyoxy Propylene group content 20%, viscosity 400CS / 25 ℃) 2.0 (2) Gaffcoat 755 (GAF Corp.) 2.0 (3) 1,3-butylene glycol 1.0 (4) Methylparaben 0.1 (5) Collagen hydrolyzate 1.0 (6) ) Polyoxyethylene (addition of 15 mol) oleyl alcohol ether 0.5 (7) Perfume proper amount (8) Ethanol 20.0 (9) Purified water Residual production method (8), (1), (2), (4), (6), (7) was dissolved and (3) and (5) were dissolved (9) were mixed to obtain a treatment lotion.
実施例６ ヘアムース 下記処方の毛髪化粧料を調製し、充填した。この試料
をよく振ってから手にとり、実施例５と同様に評価し
た。Example 6 Hair mousse A hair cosmetic having the following formulation was prepared and filled. This sample
Shake well, pick up, and evaluate in the same manner as in Example 5.
Was.
（１）ポリオキシアルキレン変性オルカノポリシロキサ
ン （一般式［Ｂ］,Rの１％がエチル基で残りはメチル基,
R′はブチル基,p＝3, ポリオキシエチレン基含有率45％， ポリオキシプロピレン基含有率５％， 粘度1000CS/25℃） 10.0 （２）ポリマーJR−400 （Union Carbide Corp.） 1.0 （３）ポリオキシエチレン（80モル付加） 硬化ヒマシ脂誘導体 2.0 （４）ポリオキシエチレン（80モル付加） ステアリルエーテル 0.5 （５）エタノール 20.0 （６）プロピレングリコール 5.0 （７）香料 適量 （８）精製水 残余 製法 （５）に（１）、（３）、（４）、（７）を溶解し
（８）に（２）、（６）を溶解した後混合し、その原液
90部に対し、フロン12を８部、LPG2部からなる噴射ガス
10を加えスプレー缶に充填した。(1) Polyoxyalkylene-modified orcanopolysiloxane (1% of general formula [B], R is an ethyl group and the remainder is a methyl group,
R'is butyl group, p = 3, polyoxyethylene group content 45%, polyoxypropylene group content 5%, viscosity 1000CS / 25 ℃) 10.0 (2) Polymer JR-400 (Union Carbide Corp.) 1.0 ( 3) Polyoxyethylene (80 mol addition) Hardened castor fat derivative 2.0 (4) Polyoxyethylene (80 mol addition) Stearyl ether 0.5 (5) Ethanol 20.0 (6) Propylene glycol 5.0 (7) Perfume proper amount (8) Purified water Residual method (1), (3), (4), and (7) are dissolved in (5), (2) and (6) are dissolved in (8), and then the mixture is mixed.
90 parts, 8 parts Freon 12 and 2 parts LPG
10 was added and it filled in the spray can.
実施例７ ヘアクリームオイル 下記処方の毛髪化粧料を調製し、実施例５と同様に評
価した。Example 7 Hair Cream Oil A hair cosmetic composition having the following formulation was prepared and evaluated in the same manner as in Example 5.
（１）ポリオキシアルキレン変性 オルガノポリシロキサン （一般式［Ｃ］,Rはメチル基,R′の５％がメチル基で残
りは水素,p＝1, ポリオキシエチレン基含有率75％， 粘度50CS/25℃） 18.0 （２）ポリコートＨ（Henkel Corp.） 6.0 （３）ポリオキシエチレン（40モル付加） 硬化ヒマシ油誘導体 2.0 （４）グリセリン 5.0 （５）２−ヒドロキシ−４−メトキシ ベンゾフェノン硫酸ソーダ 0.3 （６）ヒドロキシエチルセルロース （商品名；ナトロゾール250HH） 2.0 （７）エタノール 30.0 （８）オリゴペプタイド 0.5 （９）メチルパラベン 0.1 （10）香料 適量 （11）精製水 残余 製法 （４）に（６）を分散溶解し（11）に添加し溶解した
後、（７）に（１）、（３）、（９）、（10）を溶解し
たものを混合し、そのなかへ（２）、（５）、（８）を
添加しヘアクリームオイルを得た。(1) Polyoxyalkylene-modified organopolysiloxane (general formula [C], R is a methyl group, 5% of R'is a methyl group, the rest is hydrogen, p = 1, polyoxyethylene group content rate is 75%, viscosity is 50CS. / 25 ℃) 18.0 (2) Polycoat H (Henkel Corp.) 6.0 (3) Polyoxyethylene (40 mol addition) Hardened castor oil derivative 2.0 (4) Glycerin 5.0 (5) 2-Hydroxy-4-methoxy benzophenone sodium sulfate 0.3 (6) Hydroxyethyl cellulose (trade name; Natrozol 250HH) 2.0 (7) Ethanol 30.0 (8) Oligopeptide 0.5 (9) Methylparaben 0.1 (10) Perfume proper amount (11) Purified water Residual production method (4) with (6) dispersed After dissolving and adding to (11) and dissolving, mix (1), (3), (9) and (10) in (7) and mix into them (2), (5), Add (8) and add I got some comb oil.
実施例８ セットローション 下記処方の毛髪化粧料を調製し、実施例５と同様に評
価した。Example 8 Set Lotion A hair cosmetic composition having the following formulation was prepared and evaluated in the same manner as in Example 5.
（１）ポリオキシアルキレン変性 オルガノポリシロキサン （一般式［Ｄ］,Rの５％がフェニル基で残りはメチル
基,R′は水素,p＝3, ポリオキシエチレン基含有率50％， ポリオキシプロピレン基含有率25％， 粘度2500CS/25℃） 18.0 （２）マーコート100（Merck Corp.） 6.0 （３）ポリビニールピロリドン／ポリ ビニールアセテートコポリマー 1.5 （４）ポリオキシエチレン（40モル付加） 硬化ヒマシ油誘導体 2.0 （５）ジプロピレングリコール 5.0 （６）エタノール 30.0 （７）香料 適量 （８）精製水 残余 製法 （６）に（１）、（３）、（４）、（７）を溶解し
（２）、（５）を溶解した（８）を混合しセットローシ
ョンを得た。(1) Polyoxyalkylene-modified organopolysiloxane (general formula [D], 5% of R is a phenyl group, the remainder is a methyl group, R'is hydrogen, p = 3, polyoxyethylene group content 50%, polyoxy Propylene group content 25%, viscosity 2500CS / 25 ℃) 18.0 (2) Mercoat 100 (Merck Corp.) 6.0 (3) Polyvinylpyrrolidone / polyvinylacetate copolymer 1.5 (4) Polyoxyethylene (40 mol addition) Cured castor Oil derivative 2.0 (5) Dipropylene glycol 5.0 (6) Ethanol 30.0 (7) Perfume proper amount (8) Purified water Residual production method (6) dissolves (1), (3), (4) and (7) ( 2) and (8) in which (5) was dissolved were mixed to obtain a set lotion.
以上、実施例５〜８の毛髪化粧料は安定性に優れ、使
用性においても従来のものに比べ、なめらかな感触でき
しみ感がなくツヤならびにその持続に優れ、かつ良好な
セット保持力を有するものであった。As described above, the hair cosmetics of Examples 5 to 8 have excellent stability, smoother feel and less sensation in usability than conventional ones, and are excellent in gloss and lasting, and have good set holding power. It was a thing.
Claims (6)
示されるポリオキシアルキレン変性オルガノポリシロキ
サンの１種又は２種以上と、カチオン性高分子の１種又
は２種以上とを配合することを特徴とする毛髪化粧料。 （式中、Ｒは炭素数１乃至３のアルキル基、又はフェニ
ル基、Ｒ′は水素、又は炭素数１乃至６のアルキル基、
ｐは１乃至５の整数、ｍは０乃至100の整数、ｎおよび
ｘは１乃至100の整数、ｔおよびｙは０乃至50の整数で
あり、ｍ、ｎ、ｘおよびｙは平均数であり、分子中にポ
リオキシアルキレン基を40〜90重量％含有し、且つ25℃
で10〜3000センチストークスの粘度を有するように選ば
れる。）1. A polyoxyalkylene-modified organopolysiloxane represented by the general formula [A], [B], [C] or [D], or one or more thereof, and one or more of a cationic polymer. Hair cosmetics characterized by being mixed with at least one kind. (In the formula, R is an alkyl group having 1 to 3 carbon atoms, or a phenyl group, R'is hydrogen, or an alkyl group having 1 to 6 carbon atoms,
p is an integer of 1 to 5, m is an integer of 0 to 100, n and x are integers of 1 to 100, t and y are integers of 0 to 50, and m, n, x and y are average numbers. , Containing 40 to 90% by weight of polyoxyalkylene group in the molecule, and 25 ℃
Is selected to have a viscosity of 10 to 3000 centistokes. )
ロゲン原子を表し、Ｐは150ないし6,200の整数であ
る。） で表されるポリ（ジメチルジアリルアンモニウムハライ
ド）型カチオン性ポリマーである特許請求の範囲第１項
記載の毛髪化粧料。2. The cationic polymer is represented by the general formula (E): (In the formula, R 5 and R 6 represent a hydrogen atom or a methyl group, X represents a halogen atom, and P is an integer of 150 to 6,200.) A poly (dimethyldiallylammonium halide) type cationic polymer represented by the formula: The hair cosmetic composition according to claim 1, wherein
ハロゲン原子を表し、ｑ＋ｒは150ないし9,000の整数で
ある。） で表されるジメチルジアリルアンモニウムハライドとア
クリルアミドの共重合体型カチオン性ポリマーである特
許請求の範囲第１項記載の毛髪化粧料。3. The cationic polymer is represented by the general formula (F). Or (In the formula, R 7 and R 8 represent a hydrogen atom or a methyl group, X represents a halogen atom, and q + r is an integer of 150 to 9,000.) A copolymer type of dimethyldiallylammonium halide and acrylamide The hair cosmetic composition according to claim 1, which is a cationic polymer.
ロースエーテルである特許請求の範囲第１項記載の毛髪
化粧料。4. The hair cosmetic composition according to claim 1, wherein the cationic polymer is a quaternary nitrogen-containing cellulose ether.
ール、エピクロルヒドリン、プロピレンアミン及び牛脂
脂肪酸より得られるタロイルアミンの縮合生成物、又は
ポリエチレングリコール、エピクロルヒドリン、プロピ
レンアミンおよびヤシ油脂肪酸より得られるココイルア
ミンの縮合生成物である特許請求の範囲第１項記載の毛
髪化粧料。5. A cationic polymer, a condensation product of taroylamine obtained from polyethylene glycol, epichlorohydrin, propyleneamine and tallow fatty acid, or a condensation product of cocoylamine obtained from polyethylene glycol, epichlorohydrin, propyleneamine and coconut oil fatty acid. The hair cosmetic composition according to claim 1, which is a product.
メチルアミノエチルメタアクリレート共重合体カチオン
化物である特許請求の範囲第１項記載の毛髪化粧料。6. The hair cosmetic composition according to claim 1, wherein the cationic polymer is a cationized product of vinylpyrrolidone / dimethylaminoethyl methacrylate copolymer.