JP2013071336A - Heat sealing packaging material - Google Patents

Abstract

PROBLEM TO BE SOLVED: To provide a laminated body and a packaging material excellent in heat resistance and adherence while having water repellency and non-bonding characteristics.SOLUTION: In this heat sealing packaging material, a heat seal layer (b) is laminated on a base material layer (a), and a particle-containing layer (e) which is a mixing layer of crenellated ball-shaped micron grains (c) having 1-50 μm of a primary grain size and hydrophobic particles having 5 nm to 1 μm of a primary grain size and thermoplastic resin (d) is installed on a face of the heat seal layer (b) which is not adjacent to the base material layer (a).

Description

  The present invention relates to a packaging material used for packaging foods, beverages, pharmaceuticals, cosmetics, chemicals, and other daily necessities, and industrial articles, particularly a packaging material excellent in non-adhesiveness of contents. Specifically, container lid materials such as yogurt, jelly, pudding, syrup, retort food packaging materials such as porridge, pasta sauce, soup, liquids such as chemicals and pharmaceuticals, semi-solids, gel-like substances, etc. By adding anti-adhesive performance to the thermal adhesive layers of plastic materials for storage such as cosmetics, seasonings, syrups, and face-washing creams, it is possible to reduce the remaining amount of contents, take out and ease of use. The present invention relates to a heat-sealable packaging material that can be improved.

  There are a wide variety of packaging materials around us. Its contents are diverse, such as food, beverages, pharmaceuticals, cosmetics, chemicals, and other daily necessities such as yogurt, liquid detergent, shampoo, toothpaste, curry roux, pasta sauce, seasoning, syrup, facial cream, etc. In industrial goods, the properties of the contents range widely, including solids, gels, liquids, and viscous materials.

A packaging material for packaging these contents is required to have storability, light shielding properties, thermal adhesiveness, heat resistance, durability, and the like.
However, even if the packaging material satisfies these characteristics, there is a problem that the contents adhere to the packaging material. This problem makes it difficult to use up all of the contents, resulting in waste. In addition, it takes time and effort to squeeze out and collect the contents that remain attached, and the contents are scattered to the surroundings at that time, and the work efficiency is reduced by dirtying hands and clothes. Let For this reason, in addition to the said item required in packaging material, it is desirable to have the property (non-adhesiveness) to which the content does not adhere easily.

On the other hand, as a packaging material for suppressing adhesion, a lid material (Patent Document 1) in which hydrophobic oxide fine particles are laminated in a three-dimensional network structure on a seal layer has been proposed. In addition, as a material using a wax, a packaging material (Patent Document 2) forming a coating film containing a wax, solid fine particles, a surfactant and a dispersion medium (Patent Document 2) or dispersed in the wax. A heat-sealing lid material for packaging containers having anti-adhesive properties comprising a filler (Patent Document 3), and further a lid material comprising a wax and an ethylene-unsaturated ester polymer as components and comprising a hot melt adhesive In addition, a content adhesion preventing lid material (Patent Document 4) to which wet silica particles are adhered has been proposed.
However, lid materials such as those mentioned above are particularly vulnerable to heat, and the anti-adhesion performance is lost due to heating, and the wear resistance and adhesion are also weak. There is concern that you may lose.
Furthermore, other additives are used, and there is room for further improvement in promoting practical application of those where the adhesion prevention effect is reduced unless the amount used is strictly controlled. Moreover, the range which exhibits the performance is limited, and the effect with respect to the content containing fat is weak.

Japanese Patent No. 4348401 JP 2010-254377 A JP 2009-73523 A Japanese Patent No. 4668352

Film wrapping materials are used in various situations because of their durability, flexibility in shape, flexibility, and operability. However, there was a splash of liquid when opening the packaging container, and a pour residue after pouring the contents, and there was an unpleasant operability during use and disposal.
It is an object of the present invention to improve the water-repellent effect with the object of reducing discomfort caused by splashing and pouring of liquid when the contents are poured out. Furthermore, it aims at providing the packaging material which has favorable non-adhesion performance, while being excellent in heat resistance and adhesiveness rather than the conventional thing. In addition, by reducing the amount of pour residue, it is possible to reduce waste and effectively use products, and to support ecological living.

  In the present invention, in order to solve the above-mentioned problems, first, the invention of claim 1 has at least a base material, a heat seal layer, and a fine particle-containing layer, and the fine particle-containing layer has a primary particle diameter of 1 μm or more. A heat-sealable packaging material comprising at least a part of 50 μm gold plain sugar type micron particles and hydrophobic fine particles having a primary particle size of 5 nm to 1 μm.

  The invention relating to claim 2 is characterized in that the gold flat sugar type micron particle has a methyl group, an alkyl group, a fluorinated alkyl group, a methacryl group, an epoxy group, an amino group, a carboxyl group, a sulfonic acid on at least a part of the material surface. The heat-sealable packaging material according to claim 1, which is an inorganic oxide having any functional group of a hydroxyl group.

  The invention relating to claim 3 is characterized in that the gold flat sugar type micron particle has a methyl group, an alkyl group, a fluorinated alkyl group, a methacryl group, an epoxy group, an amino group, a carboxyl group, a sulfonic acid on at least a part of the material surface. The heat-sealing packaging material according to claim 1, wherein the heat-sealing packaging material is an organic substance having any functional group of a hydroxyl group.

  The invention according to claim 4 is the functional group in which the surface of the material is processed with any of methyl group, amino group, epoxy group, tetramethoxysilane, imidazole group, or silane coupling agent. The heat-sealable packaging material according to claim 1, wherein the heat-sealing packaging material is a silicone to which is added.

  The invention according to claim 5 is characterized in that the surface of the hydrophobic fine particles is subjected to a hydrophobic treatment of any one of dimethylsilyl, trimethylsilyl, dimethylpolysiloxane, dimethylsiloxane, aminoalkylsilyl, alkylsilyl, and methacrylsilyl. The heat-sealable packaging material according to any one of claims 1 to 4.

  The invention according to claim 6 is characterized in that the octopus area of the gold-peeled micron particles is 10% or more of the entire surface area when viewed from above in the coat layer. The heat-sealing packaging material according to any one of the above.

  In the invention according to claim 7, the fine particle-containing layer includes acrylic, EVA, polyester, polyolefin, silicone, polyester silicone, fluorosilicone, silane, silylated urethane acrylic, poval, eval, amorphous silica, urethane, vinyl chloride. The heat-sealable packaging material according to any one of claims 1 to 6, comprising a thermoplastic resin of any one of polyamide, nitrified cotton, sol-gel, SBR, acrylic silicone, alkyl oligomer, and medium. It is.

According to the packaging material of the present invention, the fine particle-containing layer contains gold flat sugar-type micron particles having a primary particle size of 1 to 50 μm and hydrophobic fine particles having a primary particle size of 5 nm to 1 μm, so that good heat A packaging material that exhibits excellent non-adhesiveness while maintaining adhesiveness can be obtained. That is, high non-adhesiveness can be obtained without impeding the thermal adhesiveness practically without being restricted by the type and thickness of the heat seal layer.

  The apparent surface area with respect to the particle size is increased by using confetti type particles in the fine particle-containing layer. In addition, by using confetti type particles, it has countless small protrusions around the core particle of 1 to 50 μm, and further mixed with hydrophobic fine particles of 5 nm to 1 μm around it, so it is micron order By taking a more complicated fractal structure in which there are protrusions of a smaller order around the particle and nanoparticles are present on the surface thereof, a non-adhesion effect superior to the conventional one can be obtained. Furthermore, since the particles can be caught by the protrusions, the effect of improving the adhesion to the thermal adhesive layer can be obtained.

  An anti-adhesion layer with excellent heat resistance and adhesion (heat seal layer) by applying the structural effects obtained by the micron-order irregularities of the heat seal layer in the prior art to the gold flat sugar type particles used in the fine particle-containing layer And a fine particle-containing layer).

  As described above, according to the packaging material of the present invention, it is a simple manufacturing method in which a water repellent coating agent in which gold flat sugar particles and hydrophobic fine particles are dispersed in a solvent and a thermoplastic resin is applied and dried on a heat seal layer, It is possible to produce a packaging material that is superior in non-adhesiveness, heat resistance, and wear resistance as compared with the prior art. Furthermore, it can be used for various applications regardless of the form of the packaging material.

It is a schematic diagram of the packaging material in connection with this invention.

  The packaging material of the present invention has at least a base material, a heat seal layer, and a fine particle-containing layer, and the fine particle-containing layer includes a confetti type micron particle having a primary particle size of 1 μm to 50 μm, and a primary particle size of 5 nm. To 1 μm of hydrophobic fine particles.

  FIG. 1 shows a schematic diagram of a cross-sectional structure of the packaging material of the present invention. The heat seal layer (b) is laminated on the base material layer (a), and the primary particle diameter is 1 μm to 50 μm on the surface of the heat seal layer (b) not adjacent to the base material layer (a). And a fine particle-containing layer (e), which is a mixed layer of micronized particles (c) of the confetti type and hydrophobic fine particles (d) having a primary particle size of 5 nm to 1 μm.

For the base material layer (a), for example, a known material such as paper, a synthetic material, or a laminated material can be used. Specifically, polyester resins such as polyethylene terephthalate resin (PET), polyethylene naphthalate resin (PEN), polybutylene terephthalate resin (PBT), polyolefin resins such as polyethylene resin (PE), polypropylene resin (PP), Polyamide resin (PA) such as nylon-6, nylon-66, polycarbonate resin (PC), polyacrylonitrile resin (PAN), polyimide resin (PI), polyvinyl alcohol resin (PVA), polyvinylidene chloride resin (PVDC), ethylene -Stretched or unstretched film such as vinyl alcohol copolymer resin (EVOH), nylon-6 / metaxylylenediamine nylon 6 coextruded film, polypropylene / ethylene-vinyl alcohol copolymer coextruded film Which one can be suitably used.
Alternatively, a composite film obtained by laminating these two or more films may be used. Metal foil such as aluminum foil and paper can be used alone or in a laminated manner.
In addition, the thickness of the base material layer is usually appropriately selected within the range of 3 μm to 150 μm in consideration of workability. In addition, each layer made of a known material may be laminated at an arbitrary position. Examples thereof include a printing layer, a printing protective layer (so-called overprint layer), a colored layer, an adhesive layer, an adhesion reinforcing layer, a primer coat layer, an anchor coat layer, an anti-slip agent layer, a lubricant layer, and an antifogging agent layer.

As the heat sealing layer (b), a known material can be used. For example, PE, PP, EVA, styrene rubber, SBR, acrylic, polyester, heat-meltable fluororesin, and the like of the sealant film. More specifically, low density polyethylene resin (LDPE), medium density polyethylene resin (MDPE), high density polyethylene resin (HDPE), linear low density polyethylene resin (L-LDPE), polypropylene resin (PP), ethylene -Propylene copolymer (EP), ethylene-α olefin copolymer, ethylene-acrylic acid copolymer (EAA), ethylene-methacrylic acid copolymer (EMAA), ethylene-methyl acrylate copolymer (EMA) , Ethylene-ethyl acrylate copolymer (EEA), ethylene-methyl methacrylate copolymer (EMMA), ionomer resin, ethylene-vinyl acetate copolymer (EVA), or a film of these resins Film, or acrylic, polyester, ethylene, EVA, vinyl acetate , Lacquer type adhesives such as modified olefins, synthetic rubbers, vinyls, EAAs, urethanes, imines, etc. The main components are ethylene vinyl acetates, polyolefins, polyamides, synthetic rubbers, acrylics, polyurethanes An adhesive such as a hot-melt adhesive can be used.
Although the thickness of these heat seal layers is not particularly limited, it is usually preferably about 1 μm to 150 μm from the viewpoint of sealing performance, productivity, cost, and the like.

The gold flat sugar type micron particle (c) refers to a particle having a plurality of protrusions smaller than the particle diameter on a spherical particle.
The apparent surface area with respect to the particle size is increased by using confetti type particles in the fine particle-containing layer. When the primary particle size is 1 μm to 50 μm, it is mixed with hydrophobic fine particles having a primary particle size of 5 nm to 1 μm, thereby taking a fractal structure in which nanoparticles are adhered around micron-order particles, and a more excellent non-particle size. An adhesion effect can be obtained. Furthermore, since the particles can be caught due to the protrusions, the effect of improving the adhesion to the heat seal layer can be obtained as compared with the case of using spherical micron particles.
The surface of the material of the confetti type micron particles (c) may be subjected to surface treatment if necessary, but the material is not particularly limited. For example, the functional group on the surface includes a silanol group, an alkoxy group, a hydroxyl group, a methyl group, an amino group, an epoxy group, a tetramethoxysilane, an imidazole group, or a surface treated with a silane coupling agent.
Examples of the material of the confetti type micron particles (c) include inorganic oxides such as silicon oxide, zinc oxide, indium oxide, magnesium oxide, aluminum oxide, titanium oxide, zirconium oxide, and iron oxide. Examples of organic substances include polystyrene, polylactic acid, acrylic, chitosan, dextran, albumin, agarose, and polyethyleneimine.
If the primary particle size of the confetti type particles (c) is less than 1 μm, the portion embedded in the fine particle-containing layer (e) increases, and the structure effect of the microscopic irregularities cannot be obtained, so that the water repellency is lowered. In addition, if the primary particle size of the confetti type particles (c) is more than 50 μm, the contact area of the confetti particles in the fine particle-containing layer (e) is lowered, so that it is easy to fall off, which is not preferable as a cover material. .
The shape of the confetti type particle (c) is preferably such that the surface area of the small protrusion is 15% or more with respect to the surface area of the micron particle. For example, the surface of micron particles having a primary particle diameter of 20 μm has about 60 small protrusions having a particle diameter of 2 μm. If the surface area of the small protrusions is less than 15% of the surface area of the micron particles, the adhesion with the fine particle-containing layer (e) is not significantly different from the case of using spherical micron particles, which is good. Adhesion cannot be obtained.

As the hydrophobic fine particles (d), those obtained by subjecting the surfaces of fine particles of metal or inorganic compound to a water repellent treatment can be preferably used. For example, silicon oxide, zinc oxide, indium oxide, magnesium oxide, aluminum oxide, titanium oxide, zirconium oxide, etc. whose surface has been subjected to trimethylsilyl treatment can be mentioned.
The hydrophobic fine particles are not particularly limited as long as they have hydrophobicity, and may be those that have been hydrophobized by surface treatment. Examples thereof include those having dimethylsilyl, trimethylsilyl, dimethylpolysiloxane, dimethylsiloxane, aminoalkylsilyl, alkylsilyl, and methacrylsilyl. In particular, hydrophobic silica fine particles having a trimethylsilyl group on the surface are preferable in that better non-adhesiveness can be obtained.

  In the fine particle-containing layer (e), a thermoplastic resin component is used in order to improve the adhesion with the thermal adhesive layer (b). The thermoplastic resin is not particularly limited as long as it improves adhesion, and for example, polyester resin, EVA resin, SBR resin, polyolefin, acrylic resin, silicone resin, and the like can be used.

  As a method for applying the fine particle-containing layer (e), known methods such as roll coating, gravure coating, bar coating, doctor blade coating, kiss reverse coating, die coating, dip coating, spray coating, and brush coating can be employed.

  The solvent of the coating solution for the fine particle-containing layer (e) is not particularly limited. For example, alcohol (ethanol, IPA, methanol), cyclohexane, toluene, acetone, propylene glycol, hexylene glycol, butyl diglycol, pentamethylene glycol, normal Aqueous solvents or organic solvents such as pentane, normal hexane, hexyl alcohol and the like can be appropriately selected. At this time, a dispersant, a colorant, an anti-settling agent, a viscosity modifier and the like can be used in combination.

  It is necessary for the octopus sugar type micron particles to have an occupation area of 10% or more of the entire surface area when viewed from above in the coat layer. When the occupied area is less than that, the contents (for example, yogurt) enter the gaps between the irregularities, and excellent non-adhesiveness cannot be obtained.

  Hereinafter, the features of the present invention will be described more specifically with reference to examples. However, the scope of the present invention is not limited to the examples.

Example 1
A 1 g / m ² polyester anchor coat is applied to the corona-treated surface of a PET film (25 μm) substrate by gravure printing, and 3 g of a lacquer type adhesive mainly composed of polyacrylate is applied thereon. / M ^{2 was} applied to form a heat seal layer. Hydrophobic silica fine particles (Nippon Aerosil; R812S primary particle size 7 nm) dispersed in an ethanol solution and silica particles (primary particle size) having a part of a confetti-type methyl group dispersed in an ethanol solution on the heat seal layer. 20 μm), and acrylic resin as a thermoplastic resin is applied at a dry weight of 0.4 g / m ² , 0.2 g / m ² and 0.9 g / m ^2, and dried at 80 ° C. for 1 minute. A sample of heat-sealable packaging material was obtained.

Example 2
A sample of heat-sealable packaging material was prepared in the same procedure as in Example 1. However, the confetti type particles used were silica particles having a part of methyl group (primary particle size 30 μm).

Example 3
A sample of heat-sealable packaging material was prepared in the same procedure as in Example 1. However, the confetti type particles used were silica particles having a part of methyl group (primary particle size of 40 μm).

Example 4
A sample of heat-sealable packaging material was prepared in the same procedure as in Example 1. However, the gold flat sugar type particles used were acrylic particles (primary particle size 20 μm) having a part of methyl groups.

Example 5
A sample of heat-sealable packaging material was prepared in the same procedure as in Example 1. However, the gold flat type particles used were silicone particles having a part of methyl group (primary particle size 20 μm).

Example 6
A sample of heat-sealable packaging material was prepared in the same procedure as in Example 1. However, the formulation was adjusted so that the occupied area of micron particles was 50%, and coating was performed.

Example 7
A sample of heat-sealable packaging material was prepared in the same procedure as in Example 1. However, the formulation was adjusted so that the area occupied by the micron particles was 90%.

Example 8
A sample of heat-sealable packaging material was prepared in the same procedure as in Example 1. However, hydrophobic fine particles whose surface functional groups were dimethyl groups were used.

Example 9
A sample of heat-sealable packaging material was prepared in the same procedure as in Example 1. However, hydrophobic fine particles whose surface functional groups were alkyl groups were used.

Example 10
A sample of heat-sealable packaging material was prepared in the same procedure as in Example 1. However, the primary particle diameter of hydrophobic fine particles was 50 nm.

Example 11
A sample of heat-sealable packaging material was prepared in the same procedure as in Example 1. However, a hydrophobic fine particle having a primary particle diameter of 90 nm was used.

Example 12
A sample of heat-sealable packaging material was prepared in the same procedure as in Example 1. However, the material of the used thermoplastic resin was EVA.

<< Comparative Example 1 >>
A sample of heat-sealable packaging material was prepared in the same procedure as in Example 1. However, the gold flat sugar type particles used were those having a primary particle size of 0.5 μm of silica particles partially having methyl groups.

<< Comparative Example 2 >>
A sample of heat-sealable packaging material was prepared in the same procedure as in Example 1. However, the gold flat sugar particles used were those having a primary particle size of 80 μm of silica particles having a part of methyl groups.

<< Comparative Example 3 >>
A sample of heat-sealable packaging material was prepared in the same procedure as in Example 1. However, spherical micron particles were used.

<< Comparative Example 4 >>
A sample of heat-sealable packaging material was prepared in the same procedure as in Example 1. However, coating was performed so that the occupation area of micron particles was 1%.

<< Comparative Example 5 >>
A sample of heat-sealable packaging material was prepared in the same procedure as in Example 1. However, hydrophobic fine particles having a primary particle size of 3 μm were used.

<< Comparative Example 6 >>
A sample of a heat-sealable packaging material was produced in the same procedure as in Example 1 without using a thermoplastic resin.

Using the above heat-sealable packaging material, the fallability and adhesion of the tap water and yogurt as the contents to the heat-seal layer were evaluated. The evaluation method is as follows.
<Evaluation>
The roll-off property was prepared by fixing the sample-containing layer side of each manufactured sample as a test surface, and fixing this surface on a horizontal flat table as an upper surface. The tap water or yoghurt was dropped from a close distance there, the flat table was tilted from the horizontal, and the dropability was evaluated by the angle at which the droplets fell (falling angle). The falling angle of 20 degrees or less was marked with ◎, the rolling angle of more than 20 degrees with 80 degrees or less was marked with ◯, the adhesion remaining on the test surface was Δ, and the adhesion was marked with X. The results are shown in Table 1.
Regarding adhesion, the cellophane tape was peeled off after being applied to the test surface, and water repellency was observed on the surface, thereby confirming whether the surface of the fine particle-containing layer was not taken up by the cellophane tape. A sample having water repellency on the surface after the cellophane tape was peeled off was marked with ◯, and a sample with a small amount of water attached was marked with Δ. The results are shown in Table 1.
Evaluation results

From the results of Table 1, it can be seen that the films of the present invention shown in Examples 1 to 12 exhibit high non-adhesiveness as well as having adhesiveness.
However, as can be seen from the results of Comparative Examples 1 and 2, when the primary particle size of the micron particles is smaller than the range of Claim 1, excellent non-adhesiveness cannot be obtained. If it exceeds, adhesion cannot be obtained.
As can be seen from the results of Comparative Example 3, when the shape of the micron particles is spherical, the adhesion is lowered. From this, it can be said that the adhesiveness of the coating film is improved because the micron particles are confetti type.
As can be seen from the results of Comparative Examples 4 and 5, when the primary particle size of the hydrophobic fine particles used exceeds the range of claim 1 or the occupied area of micron particles is outside the range of claim 6, the surface becomes complicated. Insufficient non-adhesiveness cannot be obtained due to lack of.
As can be seen from the result of Comparative Example 6, as described in claim 7, adhesion cannot be obtained unless a thermoplastic resin is used.

  Thus, the packaging material film using the heat-sealable packaging material of the present invention has high water-repellency and yogurt-repellency in addition to high adhesion to the heat-seal layer, and after taking out due to adhesion of contents The remaining amount of the resin is reduced, and the take-out property can be improved.

  The packaging material of the present invention is effective for various uses such as lids, pillow bags, gusset bags, self-standing bags, three-side seal bags, four-side seal bags, etc., refill containers, molded containers, packaging sheets, tubes, etc. Can be used.

(A) ... base material (b) ... heat sealing layer (c) ... gold-peeled micron particles (d) ... hydrophobic fine particles and thermoplastic resin layer (e) ... fine particle-containing layer

Claims (7)

  It has at least a base material, a heat seal layer, and a fine particle-containing layer. In the fine particle-containing layer, a plain particle type micron particle having a primary particle size of 1 μm to 50 μm and hydrophobic fine particles having a primary particle size of 5 nm to 1 μm are contained. A heat-sealing packaging material characterized in that it is contained at least in part.   The gold plain sugar type micron particle has at least part of the material surface with a functional group of any of methyl group, alkyl group, fluorinated alkyl group, methacryl group, epoxy group, amino group, carboxyl group, sulfonic acid and hydroxyl group. The heat-sealing packaging material according to claim 1, wherein the heat-sealing packaging material is an inorganic oxide containing   The gold plain sugar type micron particle has at least part of the material surface with a functional group of any of methyl group, alkyl group, fluorinated alkyl group, methacryl group, epoxy group, amino group, carboxyl group, sulfonic acid and hydroxyl group. The heat-sealing packaging material according to claim 1, wherein the heat-sealing packaging material is an organic substance having   The gold plain sugar type micron particle is made of silicone having a functional surface treated with any of methyl group, amino group, epoxy group, tetramethoxysilane, imidazole group, or silane coupling agent. The heat-sealable packaging material according to claim 1, characterized in that   The surface of the hydrophobic fine particles is subjected to a hydrophobic treatment of any one of dimethylsilyl, trimethylsilyl, dimethylpolysiloxane, dimethylsiloxane, aminoalkylsilyl, alkylsilyl, and methacrylsilyl. The heat-sealing packaging material according to any one of the above.   The occupying area when viewed from the top of the coating layer of the gold-peeled micron particles is an occupying ratio of 10% or more of the entire surface area. 6. Heat-sealing packaging material.   The fine particle-containing layer includes acrylic, EVA, polyester, polyolefin, silicone, polyester silicone, fluorine silicone, silane, silylated urethane acrylic, poval, eval, amorphous silica, urethane, vinyl chloride, polyamide, nitrified cotton, sol gel, The heat-sealing packaging material according to any one of claims 1 to 6, comprising a thermoplastic resin of any one of SBR, acrylic silicone, alkyl oligomer, and medium.