JP2008238697A - Manufacturing method of cellulose acylate film - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To manufacture a cellulose acylate film with high Re and high Rth without optical fluctuation and in which the direction of a phase delay axis is constant in a width direction at high speed. <P>SOLUTION: A dope is cast on a drum and cooled and solidified and peeled as a film 62. The film 62 is conveyed to a clip tank 65 and both the ends thereof is gripped by clips. The film 62 is held at a constant temperature T1 not lower than 180°C and not higher than 250°C in a first heating portion 111 of the clip tank 65. Then the film is heated and held at a constant temperature T2 not lower than 130°C (T1-10°C) in a second heating section 2. The temperature of the film 62 is set to be the temperature higher than T2 and lower than T1 while enlarging the width of the same in a third heating section 113. Then the gripping by the clips is released after heating the film 62 to a temperature 10°C or more lower than the T3. <P>COPYRIGHT: (C)2009,JPO&INPIT

Description

  The present invention relates to a method for producing a cellulose acylate film, and more particularly to a method for producing a cellulose acylate film used for a high-brightness liquid crystal display or the like.

  The required performance for liquid crystal displays has been increasing in recent years, and the required performance is only increasing for a plurality of polymer films constituting the liquid crystal display. The retardation film used in the liquid crystal display is required to have transparency and appropriate moisture permeability, and a cellulose acylate film can satisfy these requirements most. In recent years, the brightness of liquid crystal displays has become higher and the screen has become larger, and this has led to more stringent demands on retardation films for the uniformity of optical properties in the width direction. It is becoming.

The non-uniformity of the optical characteristics in the width direction of the retardation film mainly includes non-uniformity in the direction of the slow axis and optical unevenness. When the retardation film is manufactured continuously, that is, in a long length, generally, the slow axis is symmetric with respect to the center in the width direction of the retardation film. That is, the direction of the slow axis is not a constant direction in the width direction. Conventionally, in order to eliminate optical unevenness, a method of making the film flatter by making the thickness more uniform and smoothing the surface has been proposed (see, for example, Patent Document 1).
JP 2001-277267 A

  However, with the conventional brightness of the liquid crystal display, the optical unevenness can be suppressed to some extent by improving the uniformity and smoothness of the film thickness, but when the brightness is increased, the optical unevenness is confirmed. become. This is considered to be a phenomenon based on the fact that the retardation values such as the in-plane retardation Re and the thickness direction retardation Rth are not uniform even if the uniformity and smoothness of the thickness are improved. However, it is difficult in the prior art to produce a film so that Re and Rth in the width direction are constant, and it is more difficult if the slow axis is constant in the width direction. These problems are particularly remarkable when a retardation film having a high Re and Rth is produced. In addition, the market for liquid crystal displays is growing rapidly, and the expansion of polymer film production facilities cannot keep up with the increase in demand. Therefore, there is a problem that a method of increasing production using existing facilities is required.

  Accordingly, in view of the above problems, the present invention provides a method for producing a cellulose acylate film having a high Re and Rth, a uniform slow axis direction in the width direction and no optical unevenness at a higher speed than conventional. With the goal.

  In order to solve the above-mentioned problems, the present invention provides a casting in which a dope containing a cellulose acylate and a solvent flows out from a casting die on a traveling support to form a casting film and is peeled off as a wet film. And a tenter step of drying the wet film while applying tension in the width direction with a tenter that grips both side ends of the wet film with a gripping means to form a cellulose acylate film. In the tenter step, the wet film gripped by the gripping means is heated to maintain a constant temperature T1 in a range higher than 180 ° C. and lower than 250 ° C., and after the first step, the wet film is heated. A second step of maintaining a constant temperature T2 in the range of 130 ° C. to (T1-10) ° C., and after this second step, the width of the wet film is doubled. A third step of heating the wet film to a temperature T3 that is higher than T2 and lower than T1 while enlarging inward, and after this third step, hold the wet film at a temperature that is 10 ° C. lower than T3 And a grip releasing step for releasing the grip by the means.

  In the above manufacturing method, the solvent residual ratio of the cast film at the time of peeling is set in the range of 150 wt% or more and 320 wt% or less, and the solvent residual ratio of the wet film is 0.1 wt% or more and 10 wt% before the tenter process. It is preferable to set it as the range of weight% or less.

  A cellulose acylate film having a high Re and Rth, a uniform slow axis in the width direction and no optical unevenness can be produced at a higher speed than in the prior art.

  Hereinafter, embodiments of the present invention will be described in detail. However, the present invention is not limited to the embodiments described here.

Among the cellulose acylates, the ratio of esterifying the hydroxyl group of cellulose with carboxylic acid, that is, the substitution degree of acyl group (hereinafter referred to as acyl substitution degree) satisfies all the conditions of the following formulas (I) to (III) What is satisfied is more preferable. In (I) to (III), A and B are both acyl group substitution degrees, the acyl group in A is an acetyl group, and the acyl group in B has 3 to 22 carbon atoms.
2.5 ≦ A + B ≦ 3.0 (I)
0 ≦ A ≦ 3.0 (II)
0 ≦ B ≦ 2.9 (III)

  Glucose units constituting cellulose and having β-1,4 bonds have free hydroxyl groups at the 2nd, 3rd and 6th positions. Cellulose acylate is a polymer in which some or all of these hydroxyl groups are esterified, and the hydrogen of the hydroxyl groups is substituted with an acyl group having 2 or more carbon atoms. In addition, since the degree of substitution is 1 when esterification of one hydroxyl group in the glucose unit is 100%, in the case of cellulose acylate, the hydroxyl groups at the 2nd, 3rd and 6th positions are each 100% ester. The degree of substitution is 3.

  Here, the substitution degree of the acyl group at the 2-position of the glucose unit is DS2, the substitution degree of the acyl group at the 3-position is DS3, and the substitution degree of the acyl group at the 6-position is DS6. The total acyl group substitution degree determined by DS2 + DS3 + DS6 is preferably 2.00 to 3.00, more preferably 2.22 to 2.90, and even more preferably 2.40 to 2.88. . DS6 / (DS2 + DS3 + DS6) is preferably 0.32 or more, more preferably 0.322 or more, and further preferably 0.324 to 0.340.

  There may be only one kind of acyl group, or two or more kinds. When there are two or more acyl groups, it is preferable that one of them is an acetyl group. DSA + DSB, where DSA is the sum of the substitution degrees of the hydrogens of the hydroxyl groups at the 2nd, 3rd and 6th positions with the acetyl group, and DSB is the sum of the substitution degrees other than the acetyl groups at the 2nd, 3rd and 6th positions The value of is preferably 2.2 to 2.86, particularly preferably 2.40 to 2.80. DSB is preferably 1.50 or more, and particularly preferably 1.7 or more. Further, it is preferable that 28% or more of the DSB is a substituent at the 6-position hydroxyl group, more preferably 30% or more, still more preferably 31% or more, and particularly preferably 32% or more is a substituent at the 6-position hydroxyl group. Preferably there is. The 6-position DSA + DSB value of cellulose acylate is preferably 0.75 or more, more preferably 0.80 or more, and particularly preferably 0.85 or more. By using the cellulose acylate as described above, a dope having a preferable solubility and a dope having a low viscosity and a good filterability can be produced. In particular, when a non-chlorine organic solvent is used, the above cellulose acylate is preferable.

  The acyl group having 2 or more carbon atoms may be an aliphatic group or an aryl group, and is not particularly limited. For example, there are cellulose alkylcarbonyl ester, alkenylcarbonyl ester, aromatic carbonyl ester, aromatic alkylcarbonyl ester, etc., and these may each further have a substituted group. Propionyl group, butanoyl group, pentanoyl group, hexanoyl group, octanoyl group, decanoyl group, dodecanoyl group, tridecanoyl group, tetradecanoyl group, hexadecanoyl group, octadecanoyl group, iso-butanoyl group, t-butanoyl group, cyclohexane Examples thereof include a carbonyl group, an oleoyl group, a benzoyl group, a naphthylcarbonyl group, and a cinnamoyl group. Among these, a propionyl group, a butanoyl group, a dodecanoyl group, an octadecanoyl group, a t-butanoyl group, an oleoyl group, a benzoyl group, a naphthylcarbonyl group, a cinnamoyl group, and the like are more preferable, and a propionyl group and a butanoyl group are particularly preferable.

  It is preferable that 90% by weight or more of the cellulose acylate used as the dope material is particles having a particle diameter of 0.1 mm to 4 mm.

  The details of cellulose acylate are described in paragraphs [0140] to [0195] of JP-A-2005-104148, and these descriptions can also be applied to the present invention.

  The same applies to additives such as solvents and plasticizers, deterioration inhibitors, ultraviolet absorbers, optical anisotropy control agents, dyes, matting agents, release agents, etc., paragraph [0196] of JP-A-2005-104148. To [0516] paragraphs, and these descriptions can also be applied to the present invention. As the plasticizer, known triphenyl phosphate (TPP), biphenyl diphenyl phosphate (BDT) and the like can be used particularly preferably.

  Solvents for producing the dope include aromatic hydrocarbons (for example, benzene, toluene, etc.), halogenated hydrocarbons (for example, dichloromethane, chlorobenzene, etc.), alcohols (for example, methanol, ethanol, n-propanol, n-). Examples include butanol, diethylene glycol, etc., ketones (eg, acetone, methyl ethyl ketone, etc.), esters (eg, methyl acetate, ethyl acetate, propyl acetate, etc.) and ethers (eg, tetrahydrofuran, methyl cellosolve, etc.). Here, the dope is a polymer solution or dispersion obtained by dissolving a polymer in a solvent or dispersing in a dispersion medium.

  As the solvent for TAC, among these solvents, halogenated hydrocarbons having 1 to 7 carbon atoms are preferable, and dichloromethane is most preferable. And from the viewpoint of properties such as the solubility of TAC, the peelability of the cast film from the support, the mechanical strength of the film, and the optical properties of the film, one or several kinds of alcohols having 1 to 5 carbon atoms are selected. It is preferable to use it mixed with dichloromethane. At this time, the content of the alcohol is preferably 2% by weight to 25% by weight and more preferably 5% by weight to 20% by weight with respect to the whole solvent. Preferable specific examples of the alcohol include methanol, ethanol, n-propanol, isopropanol, n-butanol, etc. Among them, methanol, ethanol, n-butanol, or a mixture thereof is preferably used.

  For the purpose of minimizing the influence on the environment, the dope may be manufactured without using dichloromethane. As the solvent in this case, an ether having 4 to 12 carbon atoms, a ketone having 3 to 12 carbon atoms, and an ester having 3 to 12 carbon atoms are preferable, and these may be appropriately mixed and used. These ethers, ketones and esters may have a cyclic structure. A compound having two or more functional groups of ether, ketone and ester (that is, —O—, —CO— and —COO—) can also be used as the solvent. The solvent may have another functional group such as an alcoholic hydroxyl group in the chemical structure.

[Dope production method]
FIG. 1 shows a dope manufacturing facility. However, the present invention is not limited to the dope manufacturing apparatus and method shown here. The dope manufacturing facility 10 includes a solvent tank 11 for storing a solvent, a hopper 12 for supplying cellulose acylate, an additive tank 15 for storing an additive, a solvent, cellulose acylate, and an additive. A mixing tank 17 to be mixed liquid 16, a heating device 18 for heating the mixed liquid 16, a temperature regulator 21 for adjusting the temperature of the heated mixed liquid 16, and a temperature regulator. A filtration device 22 for filtering the mixed liquid 16 from the filter 21; a flash device 26 for adjusting the concentration of the dope 24 from the filtration device 22; and a filtration device 27 for filtering the concentration-adjusted dope 24. . The dope manufacturing facility 10 further includes a recovery device 28 for recovering the solvent and a regeneration device 29 for regenerating the recovered solvent. The dope manufacturing facility 10 is connected to the solution casting facility 40 via the stock tank 32. In addition, although the valves 36-38 for adjusting the amount of liquid feeding and the pumps 41 and 42 for liquid feeding are provided in dope manufacturing equipment 10, about the position where these are arranged, and increase / decrease in the number of pumps suitably Be changed.

  The dope 24 is manufactured by the following method by the dope manufacturing facility 10. By opening the valve 37, the solvent is sent from the solvent tank 11 to the mixing tank 17. Next, cellulose acylate is fed into the mixing tank 17 from the hopper 12. At this time, the cellulose acylate may be continuously sent to the mixing tank 17 by a sending unit that continuously measures and delivers, or the mixing tank 17 by a sending unit that measures and sends a predetermined amount. May be sent intermittently. In addition, the required amount of the additive solution is sent from the additive tank 15 to the mixing tank 17 by opening and closing the valve 36.

  In addition to the method of sending the additive as a solution, for example, when the additive is liquid at room temperature, the additive can be fed into the mixing tank 17 in the liquid state. Further, when the additive is solid, a method of feeding into the mixing tank 17 using a hopper or the like is also possible. When a plurality of types of additives are added, a solution in which a plurality of types of additives are dissolved can be placed in the additive tank 15. Alternatively, it is also possible to use a plurality of additive tanks and put a solution in which the additive is dissolved in each of them and send them to the mixing tank 17 through independent pipes.

  In the above description, the order of putting in the mixing tank 17 is the solvent, cellulose acylate, and additive, but is not limited to this order. The additive is not necessarily limited to mixing with the cellulose acylate and the solvent in the mixing tank 17, and may be mixed in a later step with a mixture of the cellulose acylate and the solvent by an in-line mixing method or the like.

  The mixing tank 17 includes a jacket 46 that covers the outer surface of the mixing tank 17 and is supplied with a heat transfer medium between the mixing tank 17, a first stirrer 48 that is rotated by a motor 47, and a second stirrer 52 that is rotated by a motor 51. It is preferable that it is attached. The temperature of the mixing tank 17 is adjusted by a heat transfer medium flowing into the inside of the jacket 46, and a preferable temperature range is −10 ° C. to 55 ° C. By appropriately selecting and using the types of the first stirrer 48 and the second stirrer 52, the mixed liquid 16 in which the cellulose acylate is swollen with the solvent is obtained. The first stirrer 48 preferably has an anchor blade, and the second stirrer 52 is preferably a dissolver type eccentric stirrer.

  Next, the liquid mixture 16 is sent to the heating device 18 by the pump 41. The heating device 18 is preferably a jacketed tube having a tube main body (not shown) and a jacket for passing a heat transfer medium between the tube main body, and further pressurizing the mixed liquid 16. It is preferable to have a part (not shown). By using such a heating device 18, the solid content in the mixed solution 16 can be effectively and efficiently dissolved under heating conditions or pressure heating conditions. Hereinafter, such a method of dissolving a solid component in a solvent by heating is referred to as a heating dissolution method. In the heating dissolution method, it is preferable to heat the mixed solution 16 so as to be 0 ° C to 97 ° C.

  Note that the solid component may be dissolved in a solvent by a cooling dissolution method instead of the heating dissolution method. The cooling dissolution method is a method of proceeding dissolution while cooling the mixed solution 16 so that the temperature of the mixed solution 16 is maintained or lower. In the cooling dissolution method, the mixed solution 16 is preferably cooled to a temperature of −100 ° C. to −10 ° C. The cellulose acylate can be sufficiently dissolved in the solvent by the heating dissolution method or the cooling dissolution method as described above.

  After the mixed liquid 16 is brought to about room temperature by the temperature controller 21, it is filtered by a filtration device 22 to remove foreign matters such as impurities and aggregates to obtain a dope 24. The filter used for the filtration device 22 preferably has an average pore diameter of 100 μm or less. The filtration flow rate is 50 liters / hr. The above is preferable.

  The dope 24 after filtration is sent to the stock tank 32 by the valve 38 and once stored, and then used for the production of a film.

  By the way, as described above, the method in which the solid component is once swollen and then dissolved to form a solution increases the time required for the dope production as the concentration of the cellulose acylate in the solution increases. May be problematic in terms. In such a case, it is preferable to once make a dope having a concentration lower than the target concentration and then carry out a concentration step to achieve the target concentration. For example, the dope 24 filtered by the filtering device 22 can be sent to the flash device 26 by the valve 38, and the dope 24 can be concentrated by evaporating a part of the solvent of the dope 24. The concentrated dope 24 is extracted from the flash device 26 by the pump 42 and sent to the filtration device 27. The temperature of the dope 24 during filtration is preferably 0 ° C to 200 ° C. The dope 24 from which foreign matter has been removed by the filtration device 27 is sent to the stock tank 32 and once stored, and then used for film production. In addition, since the concentrated dope 24 may contain bubbles, it is preferable to carry out a bubble removal process before sending it to the filtration device 27. As the bubble removal method, for example, various known methods such as an ultrasonic irradiation method for irradiating the dope 24 with ultrasonic waves are applied.

  Further, the solvent gas generated by the flash evaporation in the flash device 26 is condensed by the recovery device 28 having a condenser (not shown) and recovered as a liquid. The recovered solvent is regenerated and reused as a solvent for dope production by the regenerator 29. Such collection and recycling have advantages in terms of manufacturing costs and are effective in preventing adverse effects on the human body and the environment because they are implemented in a closed system.

  By the above manufacturing method, the dope 24 having a cellulose acylate concentration of 5 wt% to 40 wt% can be manufactured. The cellulose acylate concentration is more preferably in the range of 15% by weight to 30% by weight, and further preferably in the range of 17% by weight to 25% by weight. The concentration of the additive is preferably in the range of 1% by weight to 20% by weight with respect to the entire solid content.

  In addition, about the raw material in the solution casting method which obtains a TAC film, a raw material, the additive dissolution method, the filtration method, the defoaming, and the addition method, [0517] Paragraph [0616] Paragraph of JP, 2005-104148, A In detail, these descriptions can also be applied to the present invention.

[Film production equipment and method]
FIG. 2 is a schematic view showing the solution casting apparatus 40. However, the present invention is not limited to the solution casting apparatus 40. In the solution casting apparatus 40, a filtration device 61 that removes foreign matters from the dope 24 sent from the stock tank 32, and a dope 24 that has been filtered by the filtration device 61 are cast to produce a cellulose acylate film (hereinafter, referred to as “film formation device”). A casting chamber 63, which is simply referred to as a film) 62, a pin tenter 64 which holds both side ends of the film 62 with a plurality of pins and transports the film 62, and both side ends of the film 62 are used as gripping means. A clip tenter 65 that heats the film 62 while being gripped by the clip, a cutting device 67 that cuts off both end portions of the film 62, and a drying chamber that dries while transporting the film 62 over a plurality of rollers 68. 69, a cooling chamber 71 for cooling the film 62, a static elimination device 72 for reducing the charge amount of the film 62, and an energy at the side end. A knurling roller pair 73 to perform a boss machining, is provided with a winding-up chamber 76 for winding the film 62.

  An agitator 78 that is rotated by a motor 77 is attached to the stock tank 32, and the dope 24 is agitated by the rotation of the agitator 78. The dope 24 in the stock tank 32 is sent to the filtration device 61 by the pump 80.

  The casting chamber 63 includes a casting die 81 that flows out of the dope 24 and a casting drum 82 as a support on which the dope 24 is cast on the peripheral surface.

  The width of the casting die 81 is not particularly limited, but is preferably about 1.1 to 2.0 times the width of the film 62 as the final product. Further, it is preferable that a temperature controller (not shown) for controlling the temperature of the casting die 81 is attached to the casting die 81 so that the temperature of the dope 24 during film formation is maintained at a predetermined temperature. Further, the casting die 81 is provided with a plurality of thickness adjusting bolts (heat bolts) for adjusting the slit gap of the casting die 81 at predetermined intervals in order to adjust the thickness of the beads when flowing out. It is preferable that the heat bolt is controlled by an automatic thickness adjusting mechanism. The heat bolt is controlled according to the amount of pump 81 (preferably a high-precision gear pump) by a preset program, and a slit clearance profile is set. In order to precisely control the feed amount of the dope 24, the pump 80 is preferably a high precision gear pump. Further, the solution casting apparatus 40 is provided with a thickness measuring machine such as an infrared thickness gauge, and feedback control to an automatic thickness adjusting mechanism is performed based on an adjustment program based on the thickness profile of the film 62 and a detection result by the thickness measuring machine. May be performed. It is preferable to use a casting die 81 that can adjust the slit interval of the tip lip to be ± 50 μm or less so that the difference in thickness at any two positions excluding both side ends of the film 62 as a product is within 1 μm.

  In order to prevent the dope 24 from locally drying and solidifying at the lip tip of the casting die 81, it is preferable to attach a liquid supply device (not shown) for supplying liquid to the lip tip in the vicinity of the lip tip. The position where the liquid is supplied is preferably a peripheral portion of a three-phase contact line formed by both end portions of the casting bead, both end portions of the lip tip and the outside air. The flow rate of the supplied liquid is preferably 0.1 mL / min to 1.0 mL / min for each side. The liquid in this case is a liquid that dissolves in the dope 24 or a liquid that dissolves the solidified dope 24, and may have the same formulation as the solvent of the dope 24. Thereby, it is possible to prevent foreign matters, for example, solid components deposited from the dope 24 and those mixed in the casting bead from the outside from being mixed in the casting film 24a. In addition, as a pump which supplies a solvent, it is preferable to use a pulsation rate of 5% or less.

  The drum 82 below the casting die 81 is rotated by driving means (not shown). The width of the peripheral surface of the drum 82 is not particularly limited, but is preferably in the range of 1.1 to 2.0 times the casting width of the dope 24.

  The drum 82 is provided with a heat transfer medium circulation device 87 that supplies a heat transfer medium to the inside of the drum 82 to control the surface temperature of the drum. A heat transfer medium flow path (not shown) is formed inside the drum 82, and the heat transfer medium maintained at a predetermined temperature passes through the flow path, so that the drum 82 The temperature of the peripheral surface is held at a predetermined value. The surface temperature of the drum 82 is appropriately set according to the type of solvent, the type of solid component, the concentration of the dope 24, and the like.

Instead of the drum 82, a rotating roller (not shown) and a band (not shown) supported and conveyed by the rotating roller can be used, and this band can be used as a support for casting. The drum 82 is preferably capable of rotating with high accuracy so that the rotational speed unevenness is within 0.2% of the predetermined rotational speed. The rotating drum preferably has an average surface roughness of 0.01 μm or less, and preferably has a surface subjected to chrome plating or the like. Thereby, sufficient hardness and durability can be improved. The drum 82 preferably has surface defects suppressed to a minimum. Specifically, there is no pinhole of 30 μm or more, and the number of pinholes of 10 μm or more and less than 30 μm is 1 / m ² or less, and the number of pinholes of less than 10 μm is preferably ² / m ² or less.

  A decompression chamber 90 is provided in the vicinity of the casting die 81. The decompression chamber 90 sucks and decompresses air in the upstream area of the casting bead formed from the casting die 81 to the drum 82 in the rotation direction of the drum 82.

  The casting chamber 63 is provided with a temperature control device 97 for keeping the internal temperature at a predetermined value, and a condenser (condenser) 98 for condensing and recovering the solvent evaporated from the dope 24 and the casting film 24a. It is done. A recovery device 99 for recovering the condensed and liquefied solvent is provided outside the casting chamber 63.

  An air blower (not shown) may be provided in the crossing portion 101 extending from the casting chamber 63 to the pin tenter 64. It is preferable that an ear clip device (not shown) is provided between the pin tenter 64 and the clip tenter 65. This edge-cutting device cuts and removes both end portions of the film 62 held by pins in the pin tenter 64. Thereby, the grip of the clip tenter 65 by the clip can be more reliably performed. The ear clip device 67 on the downstream side of the clip tenter 65 is provided with a crusher 103 for finely cutting the side edge scraps of the cut film 62.

  An adsorption / recovery device 106 for adsorbing and recovering the solvent gas generated by evaporation from the film 62 is attached to the drying chamber 69. A cooling chamber 71 is provided downstream of the drying chamber 69, and a humidity control chamber (not shown) for adjusting the water content of the film 62 is further provided between the drying chamber 69 and the cooling chamber 71. Good. The static eliminator 72 is a so-called forced static eliminator such as a static eliminator, and adjusts the charged voltage of the film 62 to be within a predetermined range. The position of the static eliminating device 72 is not limited to the downstream side of the cooling chamber 71. The knurling imparting roller pair 73 imparts knurling to both end portions of the film 62 by embossing. Inside the take-up chamber 76, a take-up roll 107 for taking up the film 62 and a press roller 108 for controlling the tension during the take-up are provided.

  Next, an example of a method for producing the film 62 using the solution casting apparatus 40 will be described below. The dope 24 is sent to the stock tank 32 and is always made uniform by the rotation of the stirrer 78 therein. Thereby, precipitation of solid content and aggregation are suppressed until it uses for casting. Various additives can be appropriately mixed in the dope 24 even during the stirring. And the foreign material of a size more than a predetermined particle size and a gel-like foreign material are removed by filtration with the filtration apparatus 61. FIG.

  The dope 24 after being filtered is cast from the casting die 81 to the drum 82. It is preferable that the temperature of the dope 24 at the time of casting is constant in the range of 30 to 35 ° C., and the surface temperature of the drum 82 is constant in the range of −10 to 10 ° C. The temperature of the casting chamber 63 is preferably set to 10 ° C. to 30 ° C. by the temperature control device 97. The solvent evaporated in the casting chamber 63 is recovered by the recovery device 99 and then regenerated and reused as a solvent for dope production.

  A casting bead is formed from the casting die 81 to the drum 82, and a casting film 24 a is formed on the drum 82. In order to stabilize the state of the casting bead, the upstream area of the bead is controlled by the decompression chamber 90 so as to have a predetermined pressure value. The pressure in the upstream area with respect to the bead is preferably 2000 Pa to 10 Pa lower than the downstream area. It is preferable to attach a jacket (not shown) to the decompression chamber 90 so that the internal temperature is maintained at a predetermined temperature. This temperature is preferably equal to or higher than the condensation point of the dope solvent. In order to keep the casting bead in a desired shape, it is preferable to attach a suction device (not shown) to the edge portion of the casting die 81 to suck both sides of the bead. This suction air volume is 1 L / min. ~ 100 L / min. It is preferable that it is the range of these.

  The stripping can be performed as long as the casting film 24a has sufficient hardness for conveyance, regardless of the solvent residual ratio of the casting film 24a. However, it is preferable to peel off the casting film 24a from the drum 82 when the solvent residual ratio is as high as possible, specifically when the solvent residual ratio is in the range of 150 wt% to 320 wt%. This is because, when the content is higher than 320% by weight, it is practically difficult to remove. On the other hand, if the film is peeled off after being less than 150% by weight, the time that the casting film 24a has to be dried by blowing dry air or the like becomes long, so that the surface of the casting film 24a becomes rough. Sometimes. As described above, the casting film 24a is peeled off while the solvent residual ratio is high, whereby the cellulose acylate molecule orientation control by the clip tenter 65 can be performed more effectively. The solvent residual ratio is a value based on the dry amount. Specifically, when the weight of the solvent is x and the weight of the casting film 24a is y, {x / (y−x)} × 100 This is the desired value.

  In order to peel off the casting film 24a while the solvent residual ratio is as high as possible, it is preferable that the casting film 24a is cooled by the drum 82 to be gelled and solidified. When the casting film 24a has self-supporting property, it is peeled off from the drum 82 while being supported by the peeling roller 109. When the production speed is set to 50 m / min or higher, it is preferable to rapidly perform cooling so that the solvent can be removed even if the solvent residual rate is 250% or more. In consideration of production efficiency, if the exposed surface of the casting film 24a is sufficiently solidified by cooling, measures such as flowing dry air in the vicinity of the casting film 24a can be taken to improve the conveyance stability after peeling. It can be improved further.

  The wet film, that is, the film 62 containing the solvent is sent to the pin tenter 64. Both ends of the film 62 sent to the pin tenter 64 are held by pins, and are conveyed by the travel of the pins. The film 62 is dried by the drying air from the air duct 74 provided in the tenter 64 while being transported.

  The film 62 is preferably dried with a pin tenter 64 until the solvent residual ratio becomes 0.1 wt% or more and 10 wt% or less. When the solvent residual ratio is in the range of 150 wt% or more and 320 wt% or less, the cast film 24 a is peeled off and dried with the pin tenter 64 until the solvent residual ratio is within the above range, whereby the cellulose acylate molecules in the clip tenter 65 are obtained. Is more effectively controlled. That is, the effect of controlling the direction of the slow axis, the effect of increasing Re and Rth, and the effect of improving optical unevenness in the later-described steps in the clip tenter 65 are enhanced. However, in the present invention, the drying with the pin tenter 64 may not be performed until the solvent residual ratio falls within the above range. That is, the film 62 having a solvent residual ratio higher than 10% by weight may be fed into the clip tenter 65.

  In the clip tenter 65, the side end portion of the film 62 is held by a clip. Then, the film 62 is heated by the dry air discharged from the air duct 75 of the clip tenter 65 while being transported. Even when the pin tenter 64 is used, that is, when the solvent residual ratio of the film 62 is very small, or when the pin tenter 64 is not used, that is, when the solvent residual ratio of the film 62 remains large, the clip tenter 65 Can be carried out. Therefore, the film once wound after passing through the ear clip device 67 and the drying chamber 69 after the pin tenter 64 without using the clip tenter 65 may be heated by the clip tenter 65 to perform the steps described later. However, the most preferable solvent residual ratio is 0.1 wt% or more and 10 wt% or less at the start of heating in the clip tenter 65. If it is less than 0.1% by weight, the energy required for stretching in the clip tenter 64 becomes large, which may increase the cost significantly. If it is more than 10% by weight, the effect of improving optical unevenness is small. It is because it may become.

  The film 62 that has come out of the clip tenter 65 is cut and removed at both ends by an ear-cutting device 67. The separated both ends are sent to the crusher 103 by a cutter blower (not shown). By the crusher 103, the elongated side end portion is made fine to form a chip. Since this chip is reused for dope manufacturing, the raw material can be effectively used. In addition, although it can also abbreviate | omit about the cutting process of this both-sides edge part, it is preferable to carry out in any one from the said casting process to the process of winding up the said film.

  On the other hand, the film 62 from which both end portions have been cut and removed is sent to the drying chamber 69 and further dried. In the drying chamber 69, the film 62 is conveyed while being wound around a roller 68. Although the internal temperature of the drying chamber 69 is not specifically limited, It is preferable to set it as 50-160 degreeC. The drying chamber 69 is more preferably divided into a plurality of sections in the film transport direction in order to change the blowing temperature. In addition, if a preliminary drying chamber (not shown) is provided between the ear opener 67 and the drying chamber 69 to preliminarily dry the film 62, the film temperature is prevented from rising sharply in the drying chamber 69. The shape change of the film 62 in the chamber 69 can be suppressed. The solvent gas generated by evaporation in the drying chamber 69 is adsorbed and recovered by the adsorption recovery device 106. The air from which the solvent component has been removed is sent again as drying air into the drying chamber 69.

  The film 62 is cooled to approximately room temperature in the cooling chamber 71. In the case where a humidity control chamber is provided between the drying chamber 69 and the cooling chamber 71, it is preferable to blow air adjusted to a desired humidity and temperature onto the film 62 in the humidity control chamber. Thereby, it is possible to suppress the occurrence of curling of the film 62 and winding failure when winding.

  In the solution casting method, various processes such as a drying process and a side edge cutting and removing process are performed until the film peeled off from the support is wound up. In each of these processes or between each process, the film is mainly supported or conveyed by a roller. These rollers include a driving roller and a non-driving roller, and the non-driving roller is mainly used for determining a film conveyance path and improving conveyance stability.

  The neutralizing device 72 sets the charged voltage while the film 62 is being conveyed to a predetermined value. The charged voltage after neutralization is preferably -3 kV to +3 kV. Further, the film 62 is preferably imparted with knurling by a knurling roller pair 73. In addition, it is preferable that the height of the unevenness | corrugation of the knurled location is 1 micrometer-200 micrometers.

  The film 62 is taken up by a take-up roll 107 in the take-up chamber 76. It is preferable to wind the film while applying a desired tension to the film 62 by the press roller. It is more preferable to gradually change the tension from the start to the end of winding, thereby preventing excessive winding in the film roll. The length of the film to be wound is preferably 100 m or more. The width of the film 62 to be wound is preferably 600 mm or more, and preferably 1400 to 2500 mm. However, the present invention is applied even when the width is larger than 2500 mm. The present invention is also applied to the production of a thin film having a thickness of 15 μm to 100 μm.

  In the present invention, when casting the dope 24, a method in which two or more kinds of dopes are simultaneously laminated co-cast or sequentially laminated co-cast may be used. When performing simultaneous lamination and co-casting, a casting die to which a feed block is attached may be used, or a multi-manifold casting die may be used. It is preferable that the thickness of any one of the two layers exposed on the surface of the multilayer film formed by co-casting is 0.5% to 30% of the thickness of the entire film. Further, in the case of simultaneous lamination co-casting, the concentration of each dope is set in advance so that when the dope is cast from the die slit to the support, the high-viscosity dope is wrapped and cast by the low-viscosity dope. It is preferable to adjust. In the case of simultaneous lamination and co-casting, the bead formed from the die slit to the support is in contact with the outside world, that is, the exposed dope has a larger proportion of the poor solvent than the internal dope. It is preferable.

  From casting die, vacuum chamber, support structure, co-casting, peeling method, stretching, drying conditions for each process, handling method, curl, winding method after flatness correction, solvent recovery method, film recovery method The details are described in paragraphs [0617] to [0889] of JP-A-2005-104148. These descriptions can be applied to the present invention.

  FIG. 3 is an explanatory diagram of the film 62 in the clip tenter 65. The arrow lines X1 and X2 are the width direction of the film 62, and the arrow line Y is the transport direction of the film 62. In the tenter 65, a position where the holding of the film 62 by the clip is started is a first position P1, and a position where the holding is released is a second position P2. The tenter 64 has an inlet slightly upstream from the first position P1 and an outlet slightly downstream from the second position, but is not shown in FIG.

  The clip tenter 65 includes, in this order, first to third heating units 111 to 113 that heat the film 62 and a temperature lowering unit 115 that lowers the temperature of the film 62 along the transport direction Y. A blower duct 75 (see FIG. 2) is provided above the film conveyance path from the first heating unit 111 to the temperature lowering unit 115. The blower duct extends in the width direction X1 and X2 direction, and dry air is emitted. A plurality of slits are formed side by side in the film transport path direction. Moreover, the inside of the air duct is divided into a plurality in the film conveyance direction, and air having different temperatures is sent from the air blower connected to the air duct to each section. Thereby, the temperature of the air taken out from a slit is changed for every division. By adjusting the temperature of the air, the temperature of the film 62 is changed and the drying of the film 62 is advanced.

  The upstream end of the first heating unit 111 is the first position P1, and the downstream end is the third position P3. In the 1st heating part 111, the temperature of a film is raised and it is made the range higher than 180 degreeC and 250 degrees C or less. When the temperature is raised, it is preferable to maintain a constant temperature for a predetermined time. This temperature is T1. By this heat treatment in the first heating unit 111, high Re and Rth, for example, Re of 35 to 80 nm and Rth of 100 to 300 can be expressed in the film 62. In the first heating unit 111, it is preferable to keep the width of the film as the width L1 at the first position P1.

  The upstream end of the second heating unit 112 is the same as the downstream end P3 of the first heating unit 111, and the downstream end of the second heating unit 112 is a fourth position P4. The film whose temperature is maintained at T1 by the first heating unit is sent to the second heating unit 112 and heated so that the temperature falls below T1. And if it falls in the range of 130 degreeC or more and (T1-10) degreeC or less, it is preferable to keep constant at the temperature for predetermined time. When this temperature is T2, 130 ° C. ≦ T2 ≦ (T1-10) ° C. is established. By the heat treatment in the second heating unit 112, the slow axis direction becomes equal in the width directions X1 and X2 without reducing Re and Rth. In the second heating unit 112, it is preferable to maintain the width of the film 62 with the width L1 at the first position P2.

  The upstream end of the third heating unit 113 is the same as the fourth position, which is the downstream end of the second heating unit 112, and the downstream end of the third heating unit 113 is a fifth position P5. And in the 3rd heating part 113, the film 62 is heated and it is made temperature higher than T2. However, it is preferable to set the temperature lower than T1 and maintain this temperature for a certain period of time. That is, when the maximum temperature of the film 62 in the third heating unit 113 is T3, it is preferable that the condition of T2 <T3 <T1 is satisfied.

  Assuming that the width when the film 62 enters the clip tenter 65 is the first width L1, in the third step, the width of the film 62 is increased while maintaining the temperature rising process from T2 to T3 and the temperature of T3. In the following description, increasing the width is referred to as “widening”. The widening is performed by applying tension to the film 62 by moving the clip in the width direction X1, X2. The tension is preferably applied to the film 62 symmetrically with respect to the center of the film 62 in the width direction. This is because the molecular orientation is uniformly controlled in the width direction of the film 62. The widening is preferably performed so that the first width L1 is within 2 times, that is, the widening ratio is larger than 100% and smaller than 200%. Here, when the width after widening is the second width L2, the widening rate is a value obtained by {(L2−L1) / L1} × 100. In FIG. 4, reference sign KL represents the position of the most central portion in the width direction of the film 62 among the holding target parts of the film 62 held by the clip, and the first width, the second widths L1 and L2 are any Is also the distance between the holding target lines KL on both sides.

  In the present embodiment, the position where the widening is started is the fourth position P4 which is the upstream end of the third heating unit 113, but may be on the downstream side of the fourth position P4. Further, the position at which the widening is finished is not limited to the fifth position P5 that is the downstream end of the third heating unit, and may be upstream of the fifth position P5. The temperature dependency of Re can be reduced by the heat treatment and the widening process in the third heating unit 113. In addition, it is possible to reduce the temperature dependence of Re without reducing Re and Rth and without impairing the uniformity of the slow axis in the width directions X1 and X2.

  The upstream end of the temperature lowering unit 115 is the same as the fifth position, which is the downstream end of the third heating unit 113, and the downstream end is the second position P2. In the temperature lowering unit 115, the temperature of the film 62 is lowered so that the temperature of the film 62 when releasing the grip becomes 10 ° C. or more lower than T3. The temperature of the film 62 may be positively lowered by setting the temperature of the air from the air duct to about room temperature, and when the conveyance path of the temperature lowering portion 115 can be lengthened, the temperature from the air duct is equal to or higher than room temperature and is 10 from T3. The temperature of the film 62 may be gradually lowered by lowering the temperature by at least ° C. By the temperature lowering process in the temperature lowering section 115, Re, Rth are not lowered, and uniformity in the width direction X1, X2 of the slow axis is not impaired, and further, reduction in temperature dependence of Re is not impaired. Rth width direction X1 and X2 can be made constant, and optical unevenness is eliminated.

  In the temperature lowering portion 115, it is preferable to maintain the width L2 of the film 62 at the fifth position P5. Thereby, the optical unevenness can be more effectively eliminated.

  As described above, by the heating, cooling, and widening processes by the first to third heating units 111 to 113 and the temperature lowering unit 115, Re and Rth are increased, the temperature dependence of Re is lowered, and the slow axis is changed. Optical nonuniformity is eliminated by making the same direction in the width directions X1 and X2. This effect is particularly high when a retardation control agent having a higher Re and Rth than that of cellulose acylate is added to the dope to produce a high Re and Rth film. In addition, when the heating, cooling, and widening processes by the clip tenter 65 are performed on a film formed by melt film formation, a film having the same optical characteristics can be obtained. It can be applied to control optical properties of films for optical applications.

[Performance / Measurement method]
(Curl degree / thickness)
The performance of the wound cellulose acylate film and the measuring method thereof are described in paragraphs [0112] to [0139] of JP-A-2005-104148. These can also be applied to the present invention.

(Use)
The cellulose acylate film is particularly useful as a polarizing plate protective film. A cellulose acylate film is bonded to a polarizer to form a polarizing plate, and a liquid crystal display device usually has a structure in which a liquid crystal layer is sandwiched between two polarizing plates. However, the arrangement of the liquid crystal layer and the polarizing plate is not limited, and various known arrangements can be employed. Japanese Patent Application Laid-Open No. 2005-104148 describes in detail TN type, STN type, VA type, OCB type, reflection type, and other examples of liquid crystal display devices, and this also applies to the present invention. Can do. In addition, the publication discloses a cellulose acylate film provided with an optically anisotropic layer, a cellulose acylate film provided with antireflection and antiglare functions, and a biaxial cellulose acylate film provided with appropriate optical performance. There is also a description of using this as an optical compensation film. These can also be used as a polarizing plate protective film. These descriptions can be applied to the present invention. Details are described in paragraphs [1088] to [1265] of JP-A-2005-104148.

  The obtained film can be used as a polarizing plate protective film. Furthermore, it can also be used as an optical compensation film for improving the viewing angle dependency of a liquid crystal display device for television applications. Therefore, it is used not only for the conventional TN mode but also for the IPS mode, OCB mode, VA mode, and the like. Moreover, you may comprise a polarizing plate using the said film for polarizing plate protective films.

A dope 24 having the following formulation was prepared by the dope manufacturing facility 10.
100 parts by weight of cellulose triacetate (substitution degree 2.94, viscosity average polymerization degree 305.6%, dichloromethane solution 6% by mass
Viscosity of 350 mPa · s)
Dichloromethane (first component of solvent) 390 parts by weight Methanol (second component of solvent) 60 parts by weight Plasticizer 12 parts by weight Retardation increasing agent 2 parts by weight Wavelength dispersion adjusting agent shown in Chemical formula 1.8 parts by weight Citric acid ester mixture (Citric acid, monoethyl ester, diethyl ester, triethyl ester mixture) 0.006 parts by weight Fine particles (silicon dioxide (average particle size 15 nm), Mohs hardness about 7) 0.05 parts by weight

A plurality of films were produced by the solution casting apparatus 40 using the dope. Each manufacturing condition is shown in Table 1. The present invention corresponds to Experiments 1 to 3, and comparative experiments for the present invention were performed as Comparative Experiments 1 to 4. In Table 1, each item number represents the following.
Item No. 1 ... Film production speed (unit: m / min)
Item number 2 ... thickness of the film 62 to be manufactured (unit: μm)
Item No. 3 ... Residual rate of solvent when stripped (unit: wt%)
Item No. 4 ... Solvent residual ratio of the film 62 at the first position P1 (unit: wt%)
Item number 5 ... Maximum temperature T1 of the film 62 in the first heating unit 111 (unit: ° C)
Item number 6 ... Minimum temperature T2 of the film 62 in the second heating section 112 (unit: ° C)
Item number 7 ... Maximum temperature T3 of the film 62 in the third heating unit 113 (unit: ° C)
Item number 8 ... Temperature T4 (unit: ° C) of the film 62 at the second position P2.
Item number 9 ... Widening rate (unit:%)
Item number 10 ... Re (unit: nm)
Item number 11... Rth (unit: nm)
Item number 12: Slow axis shift in the film width direction (so-called axis shift)
(Unit: °)
Item number 13: Optical unevenness was visually evaluated. Evaluation is based on the following criteria.
A: Not confirmed at all
○: Slightly confirmed, but practically good level
×: Same level as before and practical for high-brightness displays
There is no level

  In Experiments 1 to 3, the heights of Re and Rth, the low variation of the slow axis, and the low level of optical unevenness were satisfied. On the other hand, in Comparative Experiment 1, Re was too low for the retardation film. In Comparative Experiments 2 and 3, the optical unevenness was not at an acceptable level. In Comparative Experiment 4, the variation of the slow axis was too large. From the above examples, it can be seen that the present invention can produce a cellulose acylate film having a high Re and Rth, a uniform slow axis direction in the width direction and no optical unevenness, at a higher speed than conventional.

It is the schematic of dope manufacturing equipment. It is the schematic of the solution casting apparatus which implemented this invention. It is explanatory drawing of the widening and heat processing of the film in a clip tenter.

Explanation of symbols

62 film 65 clip tenter

Claims (2)

A casting process in which a dope containing cellulose acylate and a solvent flows out from a casting die on a traveling support to form a casting film and peels off as a wet film, and grips both side ends of the wet film. In a method for producing a cellulose acylate film, comprising a tenter step of drying the wet film while applying tension in the width direction with a tenter gripped by means to form a cellulose acylate film,
The tenter process includes
A first step of heating the wet film gripped by the gripping means to maintain a constant temperature T1 in a range of higher than 180 ° C. and lower than or equal to 250 ° C .;
After the first step, the second step of heating the wet film and maintaining the constant temperature T2 in the range of 130 ° C. or higher and (T1-10) ° C. or lower;
After the second step, a third step of heating the wet film to a temperature T3 higher than T2 and lower than T1 while increasing the width of the wet film within 2 times;
A grip release step of releasing the grip by the grip means by lowering the temperature of the wet film by 10 ° C. or more than T3 after the third step;
A method for producing a cellulose acylate film, comprising: The solvent residual ratio of the cast film at the time of stripping is in the range of 150 wt% to 320 wt%,
2. The method for producing a cellulose acylate film according to claim 1, wherein a solvent residual ratio of the wet film is in a range of 0.1 wt% to 10 wt% before the tenter step.

Images