JP2006272588A - Reflection preventing film and image display - Google Patents

Abstract

<P>PROBLEM TO BE SOLVED: To provide a reflection preventing film which is low in surface reflectance, has glare shielding properties, suppresses the glaring of an image plane, and has a neutral color tone, and also to provide an image display with the film incorporated. <P>SOLUTION: In the reflection preventing film, at least two layers of a layer A having a thickness of at least 0.3 μm and an index of refraction of 1.62 or below, and a layer B whose index of refraction is lower than that of the layer A and 1.42 or below are laminated at a position where the layer A is closer to a substrate film than the layer B. The haze of the reflection preventing film is 1.6-30.0%, and the surface reflection spectrum in a wavelength range of 400-700 nm satisfies the following three conditions: (1) the minimum reflectance is 0.6-2.0%, (2) the maximum reflectance is 3.5% or below, and (3) the difference between the maximum reflectance and the minimum reflectance is 2.5% or below. <P>COPYRIGHT: (C)2007,JPO&INPIT

Description

  The present invention relates to an antireflection film having a low surface reflectance, an antiglare property, suppressing a glare phenomenon on a screen and having a neutral color, and an image display device using the same. More specifically, the present invention relates to an antireflection film used on the display display surface, the surface of the deflecting plate, and the like. The present invention also relates to an image display device incorporating an antireflection film.

  In display devices such as televisions and personal computer monitors, external light such as sunlight and fluorescent lamps is reflected and reflected on the surface, which makes it difficult to see the displayed image. In order to solve this problem, a method has been employed in which irregularities are provided on the surface to diffuse externally reflected light, or thin films having a high refractive index and a low refractive index are alternately laminated to prevent light reflection.

  However, the method of irregularly reflecting external light is insufficient in terms of improving the visibility of the image because the image on the display looks blurred.

As a method for improving this, a method of providing a hard coat layer, a high refractive index layer, and a low refractive index layer from the lower layer side on the surface of the organic film has been proposed. (Patent Document 1)
However, in this method, if the refractive index difference between the high refractive index layer and the low refractive index layer is large, the reflectance is relatively higher in the visible light region in the low wavelength region or in the high wavelength region than in the vicinity of the lowest reflectance. Is tinged with blue or red, and there is a problem in the purity of the color tone. In addition, since the high refractive index layer contains a large amount of conductive metal oxide fine particles and the film thickness is thin, the haze as an anti-reflection film is increased and the clearness of the image is deteriorated. In addition to the problem that the hardness and chemical resistance are lowered, the cost is increased due to the large number of layers.

In addition, a method of sequentially laminating porous silica and a polysiloxane polymer on the antiglare hard coat layer has been proposed. (Patent Document 2)
However, with this method, the anti-glare hard coat layer increases haze, suppresses glare on the display surface, and has an effect of preventing illumination light such as a fluorescent lamp from being reflected on the screen (having antiglare properties). When used as an antireflection film for a display device, there is a problem that visibility of an image is impaired. In addition, if the refractive index of the polysiloxane polymer is not sufficiently low, it is difficult to suppress reflection in the entire visible light region, and the reflectance increases in the low or high wavelength region of the visible light region. There arises a problem that the color of light is not neutral.
JP 2001-350001 A JP 2003-139908 A

  In view of the background art, the present invention provides an antireflection film having a low surface reflectance, an antiglare property, suppressing glare on the screen, and having a neutral color, and an image display device incorporating the antireflection film. Is.

The present invention employs the following means in order to solve such problems. That is, the antireflection film of the present invention has an A layer having a film thickness of 0.3 μm or more and a refractive index of 1.62 or less on at least one surface of the base film, and a refractive index lower than that of the A layer, and The antireflection film in which at least two of the B layers of 1.42 or less are laminated at a position where the A layer is closer to the base film than the B layer, and the haze of the antireflection film is 1.6. The surface reflection spectrum at a wavelength of 400 to 700 nm of the antireflection film, which is ˜30.0% and defined in the text, satisfies all the following three conditions.
(1) The minimum reflectance is 0.3% or more and 2.0% or less,
(2) The maximum reflectance is 3.5% or less,
(3) The difference between the maximum reflectance and the minimum reflectance is 2.5% or less.

  The image display device of the present invention is characterized in that the antireflection film is adhered to the image display surface or the surface of the front plate.

  According to the present invention, it is possible to easily provide an antireflection film having a low surface reflectance, an antiglare property, a screen glare and a neutral color. It is suitably used as an antireflection film applied to the front surface of a flat screen TV or the front surface of a liquid crystal television.

  The present invention is an A layer that satisfies the above-mentioned problems, that is, an antireflection film that has a low surface reflectance, an antiglare property, suppresses glare on the screen, and is neutral in color. The B layer is formed by laminating at a position where the A layer is closer to the base film than the B layer, and the haze of the antireflection film satisfies a specific condition by the A layer and the B layer. When satisfying and satisfying specific conditions for the minimum reflectance and the maximum reflectance, it was found that such problems can be solved at once.

  The haze of the antireflection film here is in the range of 1.6 to 30% in order to obtain a good screen. That is, when the haze exceeds the upper limit of the above range, the display screen is whitish, the light transmittance is lowered, the visibility of the screen is inferior, and the image quality is lowered. On the other hand, if it is less than the lower limit, there is a reflection of a fluorescent lamp and the antiglare property is poor.

  The specific conditions of the minimum reflectance and the maximum reflectance of the antireflection film here are as follows: the surface reflection spectrum at a wavelength of 400 to 700 nm is (1) the minimum reflectance is 0.6% or more and 2.0% or less. Yes, (3) The maximum reflectance is 3.5% or less, and (3) the difference between the maximum reflectance and the minimum reflectance is 2.5% or less, and the three conditions are satisfied simultaneously. That is, in order to obtain an antireflection effect effective in the visible light region, the maximum reflectance of the surface reflection spectrum that can be placed at a wavelength of 400 to 700 nm needs to be 3.5% or less. In order to prevent the reflected color from having a specific color tone, the minimum reflectance is 0.6% or more and 2.0% or less, and the difference between the maximum reflectance and the minimum reflectance is 2.5. % Or less is necessary. More preferably, in addition to satisfying the condition (1) of the surface reflection spectrum that can be placed at a wavelength of 500 to 700 nm, (2) the maximum reflectance is 2.2% or less, and (3) the maximum reflectance and the minimum reflectance The condition is that the difference is 1.5% or less. The reflectance measuring method here is as defined later.

  The antireflection film of the present invention requires that at least two layers of the A layer and the B layer are laminated on at least one surface of the base film, and the A layer having a higher refractive index than the B layer is close to the base film. It is necessary to laminate in position. If the order of lamination is different, it will not function as an antireflection film.

  In addition, another layer may be provided between the A layer and the base film, between the A layer and the B layer, and between the B layer and the surface, as long as the antireflection function is not hindered. From the viewpoint of productivity including color tone and cost, it is preferable that the A layer is provided on the base film and the B layer is provided thereon. The refractive index measurement method here is as defined later.

  The A layer of the present invention needs to have a thickness of 0.3 μm or more, a refractive index of 1.62 or less, and higher than the B layer. When the refractive index of the A layer is higher than 1.62, the maximum reflectance exceeds 3.5%, the reflected light in a specific wavelength region becomes relatively strong, and a neutral color tone cannot be realized. If the refractive index of the A layer is lower than that of the B layer, it will not function as an antireflection film. Further, the refractive index of the A layer is preferably 1.48 or more in order to suppress an increase in the minimum reflectance.

  If the film thickness of this A layer is less than 0.3 μm, the difference between the maximum reflectance and the minimum reflectance in the 400 to 700 nm region becomes large, and it becomes difficult to obtain a neutral color tone.

  As a composition for forming the refractive index of the A layer in a layer having a refractive index of 1.62 or less, various resin components may be one component system or mixed to be any multi-component resin component. Any composition such as a mixture of additives such as pigments and metal oxide fine particles in an arbitrary ratio may be used, but when an antireflection film is attached to the image display surface or the surface of the front plate to form an image display device In order to prevent dust from adhering to the surface, a composition containing a conductive component in the A layer is preferable.

  As the resin component constituting the A layer, a resin component such as an acrylic resin, a urethane resin, a melamine resin, an organic silicate compound, a silicone resin, a phosphorus-containing resin, a sulfide-containing resin, or a halogen-containing resin can be used alone or Although a mixed system can be used, it is particularly preferable to use a silicone resin and an acrylic resin from the viewpoints of hardness and durability. Furthermore, from the viewpoint of curability, flexibility, and productivity, an acrylic resin is preferable, and an active ray curable acrylic resin or a thermosetting acrylic resin is more preferable. Particularly preferably, among such acrylic resins, the (meth) acrylate-based resin is easily radically polymerized by irradiation with actinic rays, and may have an effect of improving the solvent resistance and hardness of the formed film. Most preferably, a (meth) acrylate resin having a (meth) acryloyl group composed of two or more polyfunctional (meth) acrylate compounds in the molecule may improve solvent resistance. For example, as such (meth) acrylate resin, pentaerythritol tri (meth) acrylate, trimethylolpropane tri (meth) acrylate, glycerol tri (meth) acrylate, ethylene-modified trimethylolpropane tri (meth) acrylate, tris- ( 2-hydroxyethyl) -isocyanuric acid ester tri (meth) acrylate such as tri (meth) acrylate, pentaerythritol tetra (meth) acrylate, dipentaerythritol penta (meth) acrylate, dipentaerythritol hexa (meth) acrylate, etc. Tetrafunctional or higher functional (meth) acrylates may be mentioned.

  In order to improve the dispersibility of the particles, a (meth) acrylate compound (monomer) having an acidic functional group such as a carboxyl group, a phosphate group, or a sulfonate group can be used for the resin component of the A layer. . Specifically, as the acidic functional group-containing monomer, unsaturated carboxylic acid such as acrylic acid, methacrylic acid, crotonic acid, 2- (meth) acryloyloxyethyl succinic acid, 2- (meth) acryloyloxyethylphthalic acid, Examples thereof include phosphoric acid (meth) acrylic acid esters such as mono (2- (meth) acryloyloxyethyl) acid phosphate and diphenyl-2- (meth) acryloyloxyethyl phosphate, and 2-sulfoester (meth) acrylate. In addition, a (meth) acrylate compound having a polar bond such as an amide bond, a urethane bond, or an ether bond can be used. Furthermore, a resin having a urethane bond, such as a urethane (meth) acrylate oligomer, is particularly preferable because of its high polarity and good particle dispersibility.

  In forming the A layer in the present invention, an initiator may be used to advance curing of the applied binder component. As the initiator, the applied binder component initiates or accelerates polymerization and / or crosslinking reaction by radical reaction, anion reaction, cation reaction, etc., and various conventionally known photopolymerization initiators can be used. is there. Specific examples of such photopolymerization initiators include sulfides such as sodium methyldithiocarbamate sulfide, diphenyl monosulfide, dibenzothiazoyl monosulfide and disulfide, thioxanthone, 2-ethylthioxanthone, 2-chlorothioxanthone, Thioxanthone derivatives such as 2,4-diethylthioxanthone, azo compounds such as hydrazone and azobisisobutyronitrile, diazo compounds such as benzenediazonium salt, benzoin, benzoin methyl ether, benzoin ethyl ether, benzophenone, dimethylaminobenzophenone Michler's ketone, benzylanthraquinone, t-butylanthraquinone, 2-methylanthraquinone, 2-ethylanthraquinone, 2-aminoanthraquinone, Aromatic carbonyl compounds such as chloroanthraquinone, dialkylaminobenzoic acid esters such as methyl p-dimethylaminobenzoate, ethyl p-dimethylaminobenzoate, butyl D-dimethylaminobenzoate, isopropyl p-diethylaminobenzoate, and benzoyl Peroxides such as peroxide, di-t-butyl peroxide, dicumyl peroxide, cumene hydroperoxide, and the like, 9-phenylacridine, 9-p-methoxyphenylacridine, 9-acetylaminoacridine, benzacridine, etc. Acridine derivatives, phenazine derivatives such as 9,10-dimethylbenzphenazine, 9-methylbenzphenazine, 10-methoxybenzphenazine, 6,4 ′, 4 ″ -trimethoxy-2,3-diphenylquinoxaline, etc. Quinoxaline derivatives, 2,4,5-triphenylimidazolyl dimer, 2-nitrofluorene, 2,4,6-triphenylpyrylium tetrafluoride salt, 2,4,6-tris (trichloromethyl) -1,3,5-triazine, 3,3′-carbonylbiscoumarin, thiomichler ketone, 2,4,6-trimethylbenzoyldiphenylphosphine oxide, oligo (2-hydroxy-2-methyl-1- (4 -(1-methylvinyl) phenyl) propanone, 2-benzyl-2-dimethylamino-1- (4-morpholinophenyl) -butanone and the like.

  Moreover, when forming A layer by this invention, in order to prevent the fall of the sensitivity of the said initiator by oxygen inhibition, you may coexist an amine compound with a photoinitiator. Such an amine compound is not particularly limited as long as it is a non-volatile compound such as an aliphatic amine compound or an aromatic amine compound. For example, triethanolamine, methyldiethanolamine and the like are suitable.

  The amount of the photopolymerization initiator is usually 0.1 to 20 parts by mass, preferably 1.0 to 15.0 parts by mass with respect to 100 parts by mass of the binder component. If it is less than 0.1 parts by mass, photopolymerization is slow, and it tends to require long-time light irradiation in order to satisfy hardness and scratch resistance, and sometimes tends to be uncured. On the other hand, when it exceeds 20 mass parts, functions, such as electroconductivity of a coating film, abrasion resistance, a weather resistance, will fall easily.

  The conductive component that is preferably contained in the layer A is effectively used within the range of no problem, such as conductive oxide fine particles, inorganic salt chelates, and organic salts, but has low humidity dependency and processing conditions. It is preferable to use conductive oxide fine particles from the viewpoint of small fluctuation due to the above.

  In the present invention, the conductive particles refer to metal fine particles or conductive metal oxide fine particles. Among these, metal oxide fine particles are preferable because of their high transparency. As the metal oxide fine particles, tin-containing antimony oxide particles (ATO), zinc-containing antimony oxide particles, tin-containing indium oxide particles (ITO), zinc oxide / aluminum oxide particles, antimony oxide particles, and the like are particularly preferable, and tin-containing particles are more preferable. Indium oxide particles (ITO) and tin-containing antimony oxide particles (ATO).

  As the conductive particles, particles having an average primary particle diameter (sphere equivalent diameter measured by the BET method) of 0.5 μm or less are preferably used, more preferably 0.001 to 0.3 μm, still more preferably. Has a particle diameter of 0.005 to 0.2 μm.

  It is preferable that content of electroconductive particle is 50 mass% or less with respect to A layer. If it exceeds 50% by mass, various physical and chemical strengths of the film may be deteriorated.

  In order to obtain a specific range of haze in the reflective film of the present invention, it is preferable to have antiglare properties. The means for imparting antiglare properties is not particularly limited. For example, a method of roughening the surface of the base film by a method such as sand blasting, embossing roll, chemical etching, etc., forming A layer and B layer on the roughened surface, giving fine irregularities, transfer by mold Examples thereof include a method of giving fine irregularities on the surface of the A layer by a method, a method of forming fine irregularities by dispersing fine particles in the A layer or the B layer, and the like. In particular, a method of containing mat particles having an average particle diameter of 0.1 to 10.0 μm in the A layer is preferably used for forming the antiglare property. As the mat particles, silica particles, particles of inorganic compounds such as titanium oxide and alumina, resin particles such as crosslinked acrylic particles, crosslinked styrene particles, melamine resin particles, and benzoguanamine resin particles are preferably used.

  As such matte particles, particles having an average particle diameter (sphere equivalent diameter (defined by JIS Z8819-1) measured by the BET method shown in JIS R1626) of 0.1 to 10.0 μm are preferably used. However, more preferably, those having a particle diameter of 0.5 to 5.0 μm, more preferably 1.0 to 4.0 μm are used. When the average particle diameter is 5.0 μm or less, the whiteness of the formed film (A layer) is suppressed, so that transparency is obtained, and when it is 0.5 μm or more, antiglare properties are obtained. Since it is obtained, it is preferable. Moreover, it is preferable that content of this mat particle | grain with respect to the whole A layer is 30 mass% or less. It is preferable that the content of the particles is 30% by mass or less because various physical and chemical strengths of the obtained film are good and the haze value becomes a desired value and transparency is obtained.

  The A layer of the present invention may further contain various additives such as a polymerization inhibitor, a curing catalyst, an antioxidant, a dispersant, etc., if necessary. When laminating | stacking, it is preferable from the point which improves the abrasion resistance of the surface of this reflection film that an organic substituent containing alkoxysilane compound is included.

Examples of such organic substituent-containing alkoxysilane compounds include alkyl groups, fluoroalkyl groups, phenyl groups, vinyl groups, epoxy groups, styryl groups, methacryloxy groups, acryloxy groups, amino groups, ureido groups, chloropropyl groups, mercapto groups. Silane coupling agents having organic substituents such as sulfide groups, isocyanate groups, isocyanurate groups, etc., hydrolysates of these silane coupling agents, alkoxysilane compounds produced by condensation of the same or different silane coupling agents, Organic substituent-containing alkoxysilane compound composed of the above-mentioned silane coupling agent and an alkoxysilane compound obtained by condensing an alkoxysilane compound not containing an organic substituent, and further containing organic substituents reacted with various chlorosilanes, hydrosilanes, and silazanes. Alkoxy Lan compounds, mixed systems of these in any proportion, etc. are used, but are preferably used, but in particular, vinyl group, epoxy group, methacryloxy group, acryloxy group, amino group, ureido group, chloropropyl group, mercapto group, sulfide An alkoxysilane compound containing a group, an isocyanate group or the like is preferable from the viewpoint of reactivity, and an alkoxysilane compound having a kinematic viscosity of 5 mm ² / s (25 ° C.) or more is more preferable because of high reactivity per content.

  As content, it is preferable that it is 50 mass parts or less per 100 mass parts of resin components of A layer, when suppressing a raise of a surface resistance value, More preferably, it is 20 mass parts or less.

  In the present invention, the constituents of the A layer can further contain an organic metal compound such as a conductive polymer such as polypyrrole, polyaniline and polythiophene, a metal alcoholate and a chelate compound for the purpose of imparting conductivity. In addition, for the purpose of improving the surface hardness, the constituents of this A layer are alkyl silicates and hydrolysates thereof, colloidal silica, dry silica, wet silica, inorganic particles such as titanium oxide, and colloidally dispersed silica fine particles. Etc. can be further contained.

In order to provide a desired level of antistatic property by the A layer of the present invention, the surface resistivity of the A layer measured by the method shown in JIS K6911 should be 1 × 10 ¹² Ω / □ or less. More preferably, it is 1 × 10 ¹¹ Ω / □ or less.

  The layer A in the present invention is a layer having a total light transmittance of preferably 40% or more, more preferably 60% or more, from the viewpoint of sharpness and transparency.

  In the present invention, “... (Meta) acrylic ...” is an abbreviation of “... acrylic ... or meta acrylic ...”.

  In the present invention, the B layer has a refractive index lower than that of the A layer and is 1.42 or less. That is, when the refractive index is higher than the A layer, it does not function as an antireflection film, and when the refractive index is higher than 1.42, both the maximum reflectance and the minimum reflectance of the surface reflection spectrum at a wavelength of 400 to 700 nm are increased, which is favorable. Antireflection performance is not obtained.

  In order to make the layer B have a refractive index of 1.42 or less, adopting a constitution mainly composed of a siloxane polymer combined with silica-based fine particles can reduce the refractive index and scratch resistance. From this point, it is preferably adopted. In other words, as the configuration in which the surface reflection spectrum at the wavelength of 400 to 700 nm according to the present invention satisfies the maximum reflectance and the minimum reflectance for satisfying all of the following three conditions, the conditions and configuration of the A layer are also included. In addition, it is particularly preferable to employ such a B layer configuration.

The term “bond” as used herein means a state in which the silica component of the silica-based fine particles and the siloxane polymer in the matrix are reacted and homogenized.
A siloxane polymer bonded to silica-based fine particles forms a silanol compound once by a known hydrolysis reaction with a polyfunctional silane compound in a solvent in the presence of the silica-based fine particles using an acid catalyst. It can be obtained by utilizing a condensation reaction.

  The polyfunctional silane compound preferably includes a polyfunctional fluorine-containing silane compound from the viewpoint of low refractive index and antifouling properties, and includes trifluoromethylmethoxysilane, trifluoromethylethoxysilane, and trifluoropropyltrimethoxy. Trifunctional fluorine-containing silane compounds such as silane, trifluoropropyltriethoxysilane, heptadecafluorodecyltrimethoxysilane, tridecafluorooctyltrimethoxysilane, heptadecafluorodecyltriethoxysilane, tridecafluorooctyltriethoxysilane, Examples include bifunctional fluorine-containing silane compounds such as heptadecafluorodecylmethyldimethoxysilane, all of which are preferably used. From the viewpoint of surface hardness, trifluoromethylmethoxysilane, trifluoro Chill silane, trifluoropropyl trimethoxy silane, trifluoropropyl triethoxy silane, more preferably.

  Examples of such polyfunctional fluorine-free silane compounds include vinyltrimethoxysilane, vinyltriethoxysilane, 3-methacryloxypropyltrimethoxysilane, 3-methacryloxypropyltriethoxysilane, methyltrimethoxysilane, and methyltriethoxy. Silane, hexyltrimethoxysilane, octadecyltrimethoxysilane, octadecyltriethoxysilane, phenyltrimethoxysilane, phenyltriethoxysilane, 3-aminopropyltriethoxysilane, N- (2-aminoethyl) -3-aminopropyltrimethoxy Trifunctional silanes such as silane, 3-chloropropyltrimethoxysilane, 3- (N, N-diglycidyl) aminopropyltrimethoxysilane, 3-glycidoxysipropyltrimethoxysilane Compound, dimethyldimethoxysilane, dimethyldiethoxysilane, diphenyldimethoxysilane, diphenyldiethoxysilane, methylphenyldimethoxysilane, methylvinyldimethoxysilane, methylvinyldiethoxysilane, 3-glycidoxypropylmethyldimethoxysilane, 3-amino Propylmethyldimethoxysilane, N- (2-aminoethyl) -3-aminopropylmethyldimethoxysilane, 3-chloropropylmethyldimethoxysilane, 3-chloropropylmethyldiethoxysilane, cyclohexylmethyldimethoxysilane, 3-methacryloxypropyldimethoxy Bifunctional silane compounds such as silane and octadecylmethyldimethoxysilane, tetrafunctional silane compounds such as tetramethoxysilane and tetraethoxysilane, etc. All of these are preferably used. From the viewpoint of surface hardness, vinyltrimethoxysilane, 3-methacryloxypropyltrimethoxysilane, methyltrimethoxysilane, methyltriethoxysilane, phenyltrimethoxysilane, and phenyltriethoxysilane are preferable. More preferable.

  Further, the silica fine particles are preferably silica-based fine particles having an average particle diameter of 1 nm to 200 nm, and particularly preferably an average particle diameter of 1 nm to 70 nm. When the average particle diameter is less than 1 nm, the bond with the matrix material becomes insufficient and the hardness may be lowered. On the other hand, if the average particle diameter exceeds 200 nm, the generation of voids between particles caused by introducing a large amount of particles is reduced, and the effect of lowering the refractive index may not be sufficiently exhibited. Further, among these silica-based fine particles, those having a structure having a cavity inside are particularly preferably used in order to lower the refractive index.

  Examples of such silica-based fine particles having cavities therein include silica-based fine particles having a hollow portion surrounded by an outer shell, porous silica-based fine particles having a large number of hollow portions, and the like. As such an example, for example, it can be produced by the method disclosed in Japanese Patent No. 3272111, and the volume occupied by the cavities inside the fine particles, that is, the porosity of the fine particles is preferably 5% or more, more preferably 30% or more. preferable. Further, the refractive index of the fine particles themselves is preferably 1.20 to 1.40, more preferably 1.20 to 1.35. Although a method of measuring the refractive index is described later, it can also be measured by a method disclosed in Japanese Patent Laid-Open No. 2001-233611. Examples of such silica-based fine particles include those disclosed in Japanese Patent Application Laid-Open No. 2001-233611, and those commercially available such as Japanese Patent No. 3272111.

  Acid catalysts used for the hydrolysis reaction include acid catalysts such as formic acid, oxalic acid, hydrochloric acid, sulfuric acid, acetic acid, trifluoroacetic acid, phosphoric acid, polyphosphoric acid, polyvalent carboxylic acid or anhydrides thereof, and ion exchange resins. It is done.

  In particular, formic acid and acetic acid are preferably used as catalysts from the viewpoint of improving the hardness of the transparent coating.

  The preferred addition amount is preferably 0.05% by mass to 10% by mass, particularly preferably 0.1% by mass to 5% by mass, based on the total silane compound content used in the synthesis of the siloxane polymer (a). It is. If the amount of the acid catalyst is less than 0.05% by mass, the hydrolysis reaction may not proceed sufficiently. Moreover, when it exceeds 10 mass%, there exists a possibility that a hydrolysis reaction may run away.

In the hydrolysis reaction, it is preferable to perform the reaction in a solvent because the control of the reaction is easy, and the solvent used is preferably an organic solvent. For example, alcohols such as ethanol, propanol, butanol, 3-methyl-3-methoxy-1-butanol; glycols such as ethylene glycol, propylene glycol; ethylene glycol monomethyl ether, propylene glycol monomethyl ether, propylene glycol monobutyl ether, diethyl Ethers such as ether; ketones such as methyl isobutyl ketone and diisobutyl ketone; amides such as dimethylformamide and dimethylacetamide; acetates such as ethyl acetate, ethyl cellosolve acetate, 3-methyl-3-methoxy-1-butanol acetate ; In addition to aromatic or aliphatic hydrocarbons such as toluene, xylene, hexane, cyclohexane, γ-butyrolactone, N-methyl 2-pyrrolidone, dimethyl sulfoxide and the like. The amount of the solvent is preferably added in the range of 50% by mass to 500% by mass, particularly preferably 80% by mass to 200% by mass, based on the total silane compound content used in the synthesis of the siloxane polymer (a). % Range. If it is less than 50% by mass, the reaction may run away and gel. On the other hand, if it exceeds 500 mass%, hydrolysis may not proceed.
Moreover, as water used for a hydrolysis, ion-exchange water is preferable. The amount of water can be arbitrarily selected, but it is preferably used in the range of 1.0 to 4.0 mol with respect to 1 mol of silane.

  The hydrolysis reaction is preferably performed at room temperature to 55 ° C by adding the acid catalyst and water in the solvent to the silane compound.

  As the conditions for the condensation reaction for obtaining the siloxane polymer (a) of the present invention, it is preferable to carry out the reaction under reflux for 1 to 100 hours after hydrolysis to obtain a silanol compound. In addition, in order to increase the degree of polymerization of the siloxane polymer, it is possible to reheat or add a base catalyst.

In the antireflection film of the present invention, as described above, the product of the refractive index and the thickness of the B layer is the target beam (under the condition that the refractive index and the thickness of the A layer are 1.62 or less and 0.3 μm or more, respectively. It is preferable that the wavelength is 1/4 of the wavelength of normal visible light. Accordingly, in the B layer, it is preferable that the product of the thickness d and the refractive index n of each layer is four times in the wavelength range of 400 to 700 nm. The relationship between the refractive index n and the thickness d in the B layer is expressed by the following formula ( The minimum reflectance of the surface reflection spectrum at a wavelength of 400 to 700 nm is 0.6% or more and 2.0% or less, and the maximum reflectance is 3.5% or less. In addition, it is preferable for the difference between the maximum reflectance and the minimum reflectance to be 2.5% or less.
n · d = λ / 4 Formula (1)
(Here, λ is the wavelength range of visible light and is usually in the range of 380 nm ≦ λ ≦ 780 nm).

  As the base film in the present invention, a film that can be formed by melt film formation or solution film formation is preferably used. Specific examples thereof include films made of polyester, polyolefin, polyamide, polyphenylene sulfide, acetate, polycarbonate, acrylic resin, and the like. Among these, a film made of a thermoplastic resin excellent in transparency, mechanical strength, dimensional stability and the like is particularly preferable. Since it is preferable that the light transmittance is high for use in an image display device, a film made of at least one selected from polyester, acetate and acrylic resin is preferable. From the viewpoint of transparency and mechanical properties, a film made of polyester is particularly preferably used.

  For example, the total light transmittance indicated by JIS K7361-1 of the base film is preferably 40% or more, more preferably 60% or more.

  Examples of the polyester preferably used in the present invention include polyethylene terephthalate, polyethylene naphthalate, polypropylene terephthalate, polybutylene terephthalate, and polypropylene naphthalate. Two or more of these may be mixed. In addition, these may be a polyester copolymerized with other dicarboxylic acid components and diol components, but the copolymerization ratio is preferably 25% or more in the degree of crystallinity in a film in which crystal orientation is completed. More preferably, the range is 30% or more, and more preferably 35% or more. When the crystallinity is less than 25%, dimensional stability and mechanical strength tend to be insufficient. The crystallinity can be measured by a method described in “Practical Spectroscopy Series (3) Raman Spectroscopy” issued by IPC Corporation.

  When the above-described polyester is used, its intrinsic viscosity (measured in o-chlorophenol at 25 ° C. according to JIS K7367) is preferably 0.4 to 1.2 dl / g, more preferably 0.5 to 0.8 dl / g. When the intrinsic viscosity is less than 0.4 dl / g, the mechanical strength is insufficient, which is not preferable. Further, even if the intrinsic viscosity exceeds this preferable range, not only is the quality excessive, but also the operability during film production is deteriorated, which is economically undesirable.

  Examples of the acetate include triacetyl cellulose, and examples of the acrylic resin include polymethyl methacrylate.

  The base film used in the present invention may be a composite film having a laminated structure of two or more layers. As the composite film, for example, a composite film that is substantially free of particles in the inner layer portion and provided with a layer containing particles in the surface layer portion, has coarse particles in the inner layer portion, and fine particles in the surface layer portion. And a composite film having a layer in which the inner layer portion contains fine bubbles. In the composite film, the polymer constituting the inner layer portion and the surface layer portion may be a chemically different polymer or the same kind of polymer.

  The base film in the present invention has sufficient thermal stability of the film, particularly dimensional stability and mechanical strength, and from the viewpoint of improving the flatness, in the state where the hard coat layer is provided, biaxial stretching is performed. A crystal-oriented film is preferred. The crystal orientation by biaxial stretching means that the thermoplastic film before unstretched, that is, before the crystal orientation is completed, is preferably stretched about 2.5 to 5 times in the longitudinal direction and the width direction, respectively, and then heat-treated. The crystal orientation is completed by the above, and it indicates a biaxial orientation pattern by wide-angle X-ray diffraction.

  The thickness of the base film used in the present invention is appropriately selected according to the use for which the hard coat film of the present invention is used. From the viewpoint of mechanical strength and handling properties, it is preferably 10 to 500 μm, more Preferably it is 20-300 micrometers.

  The base film of the present invention may contain various additives, resin compositions, cross-linking agents and the like within a range that does not impair the effects of the present invention. For example, antioxidants, heat stabilizers, UV absorbers, organic and inorganic particles, pigments, dyes, antistatic agents, nucleating agents, acrylic resins, polyester resins, urethane resins, polyolefin resins, polycarbonate resins, alkyd resins, epoxy resins , Urea resin, phenol resin, silicone resin, rubber resin, wax composition, melamine crosslinking agent, oxazoline crosslinking agent, methylolated, alkylolized urea crosslinking agent, acrylamide, polyamide, epoxy resin, isocyanate compound , Aziridine compounds, various silane coupling agents, various titanate coupling agents, and the like.

  Among these, when inorganic particles such as silica, colloidal silica, alumina, alumina sol, kaolin, talc, mica, calcium carbonate, barium sulfate, carbon black, zeolite, titanium oxide, and metal fine powder are added, it is easy to slip. This is particularly preferable since the property and scratch resistance are improved. The average particle size of the inorganic particles is preferably 0.005 to 5 μm, more preferably about 0.05 to 1 μm. The particle diameter here is a value obtained using a laser diffraction particle size distribution measuring apparatus. The average particle size is 50% distributed particle size. The 50% distribution particle size refers to the particle size where the particle size distribution is 50%. Moreover, the addition amount of inorganic particles is 0.05 to 20 parts by mass, preferably 0.1 to 10 parts by mass in 100 parts by mass of the base film.

The base film of the present invention preferably has a configuration in which an easy-adhesion layer is provided on at least one surface for the purpose of improving the adhesion, in order to improve the adhesion with a layer laminated on the easy-adhesion layer. The easy adhesion layer preferably has a refractive index of 1.52 to 1.66, and moreover, (refractive index of the easy adhesion layer) = {(refractive index of the base film) × (laminated on the easy adhesion layer). It is preferable that the refractive index of the layer)} ^1/2 ± 0.02 is satisfied because interference fringes generated when laminated on the easy-adhesion layer are reduced. The easy-adhesion layer is not particularly limited as long as it has excellent adhesion to the layer laminated on the easy-adhesion layer and has the above refractive index, but is generally a water-dispersible polyester resin, water-dispersibility A polyurethane resin is preferably used. Moreover, the easy-adhesion layer is applied in the middle of the film forming process, and a method of forming simultaneously with the film forming is preferably used, and the thickness thereof is 0.08 to 0.20 μm.

The antireflection film in the present invention is usually often installed and used on the outermost surface of a display. In that case, the scratch resistance is preferably grade 3 or higher because it is difficult to damage the film when dust or the like adhering to the surface of the film is wiped off with a cloth. Preferably it is quaternary or higher. Scratch resistance was measured by visually observing the surface of the antireflection film side surface after applying a load of 250 g to # 0000 steel wool and reciprocating 10 times at a stroke width of 10 cm and a speed of 30 mm / sec. The method of scratching is evaluated in the following five stages.
5th grade: No scratches.
Fourth grade: 1 to 5 scratches.
3rd grade: 6 to 10 scratches.
Second grade: 11 or more scratches.
First grade: Countless scratches on the entire surface.

  Next, although the manufacturing method of the antireflection film of this invention is demonstrated, it is not limited to this.

  FIG. 1 is a schematic cross-sectional view showing an example of a preferred embodiment of the antireflection film of the present invention. On the base film (a), an antireflection layer (d) composed of an A layer (b) and a B layer (c) is laminated, and the base film (a) is opposite to the antireflection layer (d). The near-infrared absorption layer (e) and the adhesive layer (f) are laminated on the surface.

  As a method of providing the A layer (b) and the B layer (c), a method of directly laminating on a base film by coating, a method of laminating a layer formed on another base material on a base film, etc. Any method may be used, but it is preferable to employ a method of directly laminating on a base film by coating from the viewpoint of production stability at an appropriate film thickness and cost.

  Examples of the coating method include various coating methods such as reverse coating method, gravure coating method, rod coating method, bar coating method, die coating method, spray coating method, and the like. In forming the layer, a reverse coating method, particularly a reverse coating using a small-diameter gravure roll is preferable from the viewpoint of coating accuracy.

  Moreover, when applying the A layer (b) and the B layer (c), it is preferable to prepare a coating solution in which the above components are dispersed with a solvent, and apply, dry and cure. Such a solvent is applied or printed. Conventionally known various organic solvents can be used as long as they are blended for improving workability and can dissolve the resin component. In particular, in the present invention, an organic solvent having a boiling point of 60 to 180 ° C. is preferable from the viewpoints of viscosity stability and drying property of the composition. Specific examples of such organic solvents include methanol, ethanol, isopropyl alcohol, n-butanol, tert-butanol, ethylene glycol monomethyl ether, 1-methoxy-2-propanol, propylene glycol monomethyl ether, propylene glycol mono Preferable examples include ethyl ether, cyclohexanone, butyl acetate, isopropyl acetone, methyl ethyl ketone, methyl isobutyl ketone, diacetyl acetone, and acetyl acetone. These may be used alone or in combination of two or more.

  When preparing the coating solution used for forming the A layer (b), the amount of the organic solvent may be blended in an arbitrary amount so that the composition has a viscosity with good workability according to the coating means and the printing means. The solid content concentration of the composition is usually 60% by mass or less, preferably 50% by mass or less. As the preparation of the composition for forming a photocurable film of the present invention, any method can be adopted. Usually, conductive particles and / or mat particles are added to a solution in which a resin component is dissolved in an organic solvent. A method of dispersing by a paint shaker, a dispersing machine such as a ball mill, a sand mill, a three roll, an attritor, a homomixer, etc., and then adding a photopolymerization initiator and dissolving uniformly is suitable. Furthermore, when adding additives, such as the said alkoxysilane compound, adding immediately before application | coating is preferable.

  Examples of the actinic rays used in the present invention include electromagnetic waves that polymerize acrylic vinyl groups such as ultraviolet rays, electron beams, and radiation (α rays, β rays, γ rays, etc.). It is preferable. As the ultraviolet ray source, an ultraviolet fluorescent lamp, a low-pressure mercury lamp, a high-pressure mercury lamp, an ultra-high pressure mercury lamp, a xenon lamp, a carbon arc lamp, or the like can be used. Moreover, when irradiating actinic radiation, if it irradiates under a low oxygen concentration, it can harden | cure efficiently.

  The coating liquid used for forming the B layer (c) of the present invention is preferably composed of the siloxane polymer as a main component, diluted with a solvent by adding a curing agent or the like, and the content of the solvent is used during the synthesis of the siloxane polymer. It is preferable to add in the range of 1300 mass% to 9900 mass%, particularly preferably in the range of 1500 mass% to 6000 mass% with respect to the total silane compound content. If the amount is less than 1300% by mass and exceeds 9900% by mass, it becomes difficult to form a transparent film having a predetermined film thickness.

  Examples of the curing agent include titanium, zirconium, aluminum, and magnesium. Among these, for the purpose of lowering the refractive index, aluminum-based and magnesium-based curing agents having a low refractive index are preferable. These curing agents can be easily obtained by reacting a metal alkoxide with a chelating agent. Examples of chelating agents include β-diketones such as acetylacetone, benzoylacetone, and dibenzoylmethane; β-keto acid esters such as ethyl acetoacetate and ethyl benzoylacetate.

  Preferable specific examples of the metal group chelate compound include ethyl acetoacetate aluminum diisopropylate, aluminum tris (ethyl acetoacetate), alkyl acetoacetate aluminum diisopropylate, aluminum monoacetylacetate bis (ethyl acetoacetate), aluminum tris Aluminum chelate compounds such as (acetylacetonate), magnesium chelate compounds such as ethyl acetoacetate magnesium monoisopropylate, magnesium bis (ethylacetoacetate), alkyl acetoacetate magnesium monosopropylate, magnesium bis (acetylacetonate) It is done. Of these, aluminum tris (acetylacetonate), aluminum tris (ethyl acetoacetate), magnesium bis (acetylacetonate), and magnesium bis (ethyl acetoacetate) are preferable, considering storage stability and availability. Then, aluminum tris (acetylacetonate) and aluminum tris (ethylacetoacetate) are particularly preferable. The amount of the metal chelate compound to be added is preferably 0.1% by mass to 10% by mass, particularly preferably 1% by mass, based on the total silane compound content used in the synthesis of the siloxane polymer (a). % To 6% by mass. When the amount introduced is less than 0.1% by mass, curing becomes insufficient, and when a transparent film is formed, the hardness decreases. On the other hand, when it exceeds 10% by mass, the curing becomes sufficient and the hardness of the transparent film is improved, but the refractive index is also improved, which is not preferable.

  In the antireflection film of the present invention, a near-infrared absorbing layer (e) can be provided on the surface opposite to the surface having the antireflection layer (d) of the base film (a). The near-infrared absorbing layer can be used without any particular limitation, such as those obtained by dispersing a near-infrared absorbing dye in a polymer resin, or provided with a near-infrared absorbing dye alone.

  As the near infrared absorbing dye, for example, a diimonium salt compound, a fluorine-containing phthalocyanine compound, a thionickel complex compound, an aminium compound, a cyanine compound, an azo compound, a polymethine compound, a quinone compound, a diphenylmethane compound, A triphenylmethane type compound, a mercaptonaphthol type compound, etc. are mentioned, Any of a single type or a mixed type can be used conveniently.

  When the near-infrared absorbing dye is dispersed in a polymer resin, examples of the polymer resin include polyester-based, acrylic-based, cellulose-based, polyethylene-based, polypropylene-based, polyolefin-based, polyvinyl chloride-based, polycarbonate, and phenol-based resins. Urethane resins and the like can be used, and any of them can be suitably used. It is preferable to contain a UV absorber such as benzophenone or benzotriazole in order to suppress deterioration of light resistance of the near infrared absorbing dye. Moreover, it is preferable to disperse | distribute 1-10 mass parts near-infrared absorption pigment | dye with respect to 100 mass parts of polymeric resins.

  In the antireflection film of the present invention, an adhesive layer (f) can be provided on the surface opposite to the surface having the antireflection layer (d) of the base film (a). The adhesive layer (f) is not particularly limited as long as it can adhere two objects by its adhesive action. As the pressure-sensitive adhesive for forming the pressure-sensitive adhesive layer (f), rubber, vinyl polymerization, condensation polymerization, thermosetting resin, silicone, and the like can be used. Among these, examples of the rubber-based adhesive include butadiene-styrene copolymer system (SBR), butadiene-acrylonitrile copolymer system (NBR), chloroprene polymer system, and isobutylene-isoprene copolymer system (butyl rubber). it can. Examples of the vinyl polymerization-based pressure-sensitive adhesive include acrylic resin-based, styrene resin-based, vinyl acetate-ethylene copolymer system, and vinyl chloride-vinyl acetate copolymer system. Examples of the condensation polymerization pressure-sensitive adhesive include a polyester resin system. Examples of the thermosetting resin adhesive include epoxy resin, urethane resin, formalin resin, and the like. These resins may be used alone or in combination of two or more.

  Furthermore, as the pressure-sensitive adhesive, either a solvent-type pressure-sensitive adhesive or a solventless pressure-sensitive adhesive can be used. Formation of the pressure-sensitive adhesive layer (f) is carried out using a conventional technique such as coating using the pressure-sensitive adhesive as described above. Further, a colorant may be contained in the adhesive layer (f). This is easily achieved by mixing and using a colorant such as a pigment or dye in the adhesive. When it contains a colorant, it is desirable that the light transmittance at 550 nm is in the range of 40 to 80% as a laminated film.

  Since the antireflection film of the present invention has high surface hardness and scratch resistance, it can be used in a wide range of applications. For example, it can be applied to the surface of membrane switches, curved mirrors, rearview mirrors, goggles, window glass, posters, advertising towers, nameplates and instrument covers, and other various commercial displays. Especially for image display members such as liquid crystal display (LCD), plasma display panel (PDP), electroluminescence display (ELD), cathode ray tube display (CRT), portable digital assistant (PDA), adhesive layer or adhesive layer The image display device can be attached to the surface of the image display surface and / or the front plate thereof via the.

[Characteristic measurement method and effect evaluation method]
The characteristic measurement method and effect evaluation method in the present invention are defined as follows.

(1) Scratch resistance: Steel wool hardness evaluation Scratch resistance was rubbed 10 times at a stroke width of 10 cm and a speed of 30 mm / sec by applying a load of 250 g to # 0000 steel wool on the antireflection surface of the antireflection film. Then, the surface was observed visually and how to get a damage | wound was evaluated in the following five steps.
5th grade: No scratches.
Fourth grade: 1 to 5 scratches.
3rd grade: 6 to 10 scratches.
Second grade: 11 or more scratches.
First grade: Countless scratches on the entire surface.

(2) Haze measurement Based on JIS K7136, it measured using the Nippon Denshoku Industries Co., Ltd. haze meter.

(3) Evaluation of surface resistance value (antistatic property) The antireflection film was sampled into a square of 100 mm × 100 mm, pretreated by the method shown in JIS K6911, and HIRESTA UP (MCP-HT450 manufactured by Mitsubishi Yuka Co., Ltd.). : According to JIS K6911), the surface resistance value was measured.

(4) Reflectance measurement The surface opposite to the measurement surface (the surface on which the antireflection layer is provided) is uniform with 320-400 water-resistant sandpaper so that the 60 ° C. gloss (JIS Z 8741) is 10 or less. After roughening, the black paint was applied and colored so that the visible light transmittance was 5% or less. Using a spectrophotometer (UV-3150) manufactured by Shimadzu Corporation, the absolute reflection spectrum in the wavelength region of 380 nm to 800 nm was measured at an incident angle of 5 degrees from the measurement surface, and the reflectance at wavelengths of 400 nm and 700 nm The minimum reflectance in the region of 400 nm to 700 nm was determined. When the measured reflection spectrum has undulations, the respective reflectances were obtained from curves connecting intermediate points between undulation peaks (maximum points) and valleys (minimum points).

(5) Refractive index measurement About the coating film formed with the spin coater on the silicon wafer, the refractive index of 633 nm was measured with the phase difference measuring apparatus (Nikon Co., Ltd. product: NPDM-1000).

(6) Anti-glare property A fluorescent lamp (8000 cd / cm ² ) is projected from a distance of 30 cm away on the surface of the prepared anti-reflection film provided with an anti-reflection layer, and the degree of the reflected image is expressed by the following 3 Rated by stage.
○ The outline of the fluorescent lamp is almost unknown.
△ The fluorescent lamp is blurred, but the outline is clear.
× The fluorescent light is clearly visible.

(7) Character visibility When the produced antireflection film is placed at a distance of 10 cm on paper printed with a font size of 10.5 points (surface opposite to the surface provided with the antireflection layer) The ease of seeing the transparently visible characters was evaluated in the following three stages.
○ Characters are clearly identified.
△ Characters look blurry but can be read.
× Characters are blurred and cannot be read.

  Next, although this invention is demonstrated based on an Example, this invention is not necessarily limited to these.

(Preparation of layer B paint-1)
A silica slurry comprising 144 parts by mass of porous silica particles having an outer shell with a primary particle diameter of 50 nm (porosity 40%) and 560 parts by mass of isopropyl alcohol was prepared, and 219 parts by mass of methyltrimethoxysilane, 3, 3, 3- 158 parts by mass of trifluoropropyltrimethoxysilane, 704 parts by mass of the above silica slurry, and 713 parts by mass of polypropylene glycol monoethyl ether are mixed with stirring, and 1 part by mass of phosphoric acid and 130 parts by mass of water are mixed at 30 ° C. ± 10 ° C. Hydrolysis was performed for 60 minutes with stirring, and the temperature was raised to 80 ° C. ± 5 ° C. and polymerization was performed with stirring for 60 minutes to obtain a silica particle-containing polymer.

  Next, 1200 parts by mass of this silica particle-containing polymer and 5244 parts by mass of isopropyl alcohol were stirred and mixed, then 15 parts by mass of acetoxyaluminum as a curing catalyst was added and stirred again to prepare a paint having a refractive index of 1.35. .

(Preparation of layer B paint-2)
Silica fine particle sol (trade name: IPA-ST, manufactured by Nissan Chemical Industries, Ltd., solid content: 30%) dispersed in isopropyl alcohol having a particle diameter of 12 nm and having no cavities, has a primary particle diameter of 50 nm. In the same manner as in the preparation of the B-layer paint-1, except that the silica slurry is composed of 144 parts by mass of porous silica particles (porosity 40%) and 560 parts by mass of isopropyl alcohol. A silica particle-containing polymer was obtained.

  Next, after 1200 parts by mass of this silica particle-containing polymer and 5466 parts by mass of isopropyl alcohol were mixed with stirring, 15 parts by mass of acetoxyaluminum was added as a curing catalyst and mixed again with stirring to prepare a paint having a refractive index of 1.38. .

(Preparation of organic substituent-containing alkoxysilane compound)
138 parts by mass of methyltrimethoxysilane, 236 parts by mass of 3-glycidoxypropyltrimethoxysilane and 120 parts by mass of isopropyl alcohol were mixed with stirring, and 1.7 parts by mass of formic acid and 72 parts by mass of water were blended, Hydrolyze with stirring at 10 ° C for 30 minutes, further raise the temperature to 80 ° C ± 5 ° C, polymerize with stirring for 60 minutes, cool to room temperature, and then distill off the solvent to remove methyl group and epoxy group-containing alkoxysilane A compound was obtained. The kinematic viscosity was 45 mm ² / s at 25 ° C.

Example 1
On the easy-adhesion surface of a commercially available optically-adhesive polyester film for optical use (Lumirror (registered trademark) QT63 manufactured by Toray Industries Inc., thickness 100 μm), 25% by mass of antimony-containing tin oxide fine particles having an average particle diameter of about 10 nm and silica having an average particle diameter of 1.4 μm Paint containing 10% by mass of particles (Silo Hovic 100: manufactured by Fuji Silysia Chemical Co., Ltd.) and polyfunctional acrylate (Seika Beam PET-AS-41: refractive index 1.53 manufactured by Dainichi Seika Co., Ltd.) and “containing organic substituents” The alkoxysilane compound obtained in “Preparation of alkoxysilane compound” was mixed at a mass ratio of 33: 1, and the stirred coating solution was applied with a small-diameter gravure coater, dried at 90 ° C., and then irradiated with ultraviolet rays of 400 mJ / cm ^2. Then, an A layer having a thickness of about 3 μm was provided. Next, on this A layer, the paint prepared in the “adjustment of B layer paint-1” is applied with a small diameter gravure coater, dried and cured at 130 ° C., and the B layer having a thickness of about 0.1 μm. An antireflection film was produced.

  The evaluation results of the obtained antireflection film are shown in Table 1 (scratch resistance, haze, surface resistance value, antiglare property, character visibility) and Table 2 (maximum reflectance at wavelengths of 400 to 700 nm and 500 to 700 nm, minimum). Reflectance, difference between maximum reflectance and minimum reflectance).

(Example 2)
For layer A, paint containing 20% by mass of antimony-containing tin oxide fine particles having a primary particle size of 30 nm, 10% by mass of crosslinked polystyrene fine particles having an average particle size of 2 μm (manufactured by Soken Chemical) and polyfunctional acrylate (manufactured by Nippon Kayaku Co., Ltd.) An antireflection film was produced in the same manner as in Example 1 except that KAS-565M-30A: refractive index 1.53) was used.

  The evaluation results of the obtained antireflection film are shown in Table 1 (scratch resistance, haze, surface resistance value, antiglare property, character visibility) and Table 2 (maximum reflectance at wavelengths of 400 to 700 nm and 500 to 700 nm, minimum). Reflectance, difference between maximum reflectance and minimum reflectance).

(Example 3)
Regarding the B layer, an antireflection film was produced in the same manner as in Example 1 except that the coating prepared in “Adjustment of the B layer coating-2” was used.

  The evaluation results of the obtained antireflection film are shown in Table 1 (scratch resistance, haze, surface resistance value, antiglare property, character visibility) and Table 2 (maximum reflectance at wavelengths of 400 to 700 nm and 500 to 700 nm, minimum). Reflectance, difference between maximum reflectance and minimum reflectance).

Example 4
For layer B, a paint containing a fluorine-containing copolymer (fluoroolefin / vinyl ether copolymer) (manufactured by JSR Corporation, JN-7215: refractive index 1.42) is used and dried and cured at 150 ° C. Except for this, an antireflection film was produced in the same manner as in Example 1.

  The evaluation results of the obtained antireflection film are shown in Table 1 (scratch resistance, haze, surface resistance value) and Table 2 (maximum reflectance, minimum reflectance, maximum reflectance and minimum reflectance at wavelengths of 400 to 700 nm and 500 to 700 nm). Reflectance difference).

  As shown in Tables 1 and 2, the antireflective films of the examples have an antireflective layer that is compatible with both reflectivity and scratch resistance, and also has excellent anti-glare properties and letter visibility.

(Comparative Example 1)
Regarding the A layer, an antireflection film was produced in the same manner as in Example 1 except that 40% by mass of the matte particles were added.

  The evaluation results of the obtained antireflection film are shown in Table 1 (scratch resistance, haze, surface resistance value, antiglare property, character visibility) and Table 2 (maximum reflectance at wavelengths of 400 to 700 nm and 500 to 700 nm, minimum). Reflectance, difference between maximum reflectance and minimum reflectance).

(Comparative Example 2)
Regarding the A layer, an antireflection film was produced in the same manner as in Example 1 except that no mat particles were added.

  The evaluation results of the obtained antireflection film are shown in Table 1 (scratch resistance, haze, surface resistance value, antiglare property, character visibility) and Table 2 (maximum reflectance at wavelengths of 400 to 700 nm and 500 to 700 nm, minimum). Reflectance, difference between maximum reflectance and minimum reflectance).

(Comparative Example 3)
For layer B, a silicone hard coat agent (AY-150 manufactured by Toray Dow Corning Silicone Co., Ltd .: refractive index 1.44) is used as a paint, dried at 80 ° C., and then irradiated with ultraviolet rays 400 mj / cm ² to be cured. An antireflection film was produced in the same manner as in Example 1 except that a B layer having a thickness of about 0.1 μm was provided. The evaluation results of the obtained antireflection film are shown in Table 1 (scratch resistance, haze, surface resistance value, antiglare property, character visibility) and Table 2 (maximum reflectance at wavelengths of 400 to 700 nm and 500 to 700 nm, minimum). Reflectance, difference between maximum reflectance and minimum reflectance).

  As shown in Tables 1 and 2, the anti-reflection film of the comparative example has a high haze in the comparative example 1 and thus has a poor anti-glare property although the anti-glare property is inferior. In the comparative example 2, the anti-glare property is inferior. It can be seen that an antireflection layer having a neutral color cannot be obtained.

(Example 7)
Two types of near-infrared absorbing dyes (diimonium salt type: IRG-022, manufactured by Nippon Kayaku Co., Ltd., phthalocyanine type) are provided on the surface of the antireflection film obtained in Example 1 on which the antireflection layer (d) is not provided. : Nippon Shokubai Co., Ltd. EEX COLOR 810K) 2 parts by mass, 1 part by mass, and acrylic resin (Mitsubishi Rayon Co., Ltd. Dianar BR-80) 100 parts by mass provided a near infrared absorption layer. . Furthermore, on this near-infrared absorbing layer, a dye having an absorption maximum at a wavelength of 595 nm and a dye for correcting the chromaticity of white light are mixed with an adhesive AGR-100 (manufactured by Nippon Kayaku Co., Ltd.) to form an adhesive layer. After being provided and bonded to glass, it was cured with an ultraviolet irradiation amount of 1000 mJ / cm ² to obtain a front protective plate for plasma display.

(Example 8)
The front protective plate for the plasma display panel of Example 7 was set on the front surface of the plasma display panel. A plasma display with less reflection and neutral reflection color was obtained.

  According to the present invention, since the antireflection film of the present invention has antiglare properties, suppresses glare on the screen, has low surface reflectance, and has a neutral color, for example, a large screen such as a plasma display. It is suitable as an antireflection film applied to the front surface of flat TVs and the front surface of liquid crystal televisions.

It is the figure which represented typically the cross section which shows an example of the antireflection film of this invention.

Explanation of symbols

1: B layer (c)
2: A layer (b)
3: Substrate film (a)
4: Near-infrared absorbing layer (e)
5: Adhesive layer (f)
6: Antireflection layer (d)

Claims (15)

At least one of the A layer having a film thickness of 0.3 μm or more and a refractive index of 1.62 or less and the B layer having a refractive index lower than that of the A layer and 1.42 or less on at least one surface of the base film Two layers are antireflection films laminated at a position where the A layer is closer to the base film than the B layer, and the haze of the antireflection film is 1.6 to 30.0% and the wavelength is 400 An antireflection film whose surface reflection spectrum (defined in the text) at ˜700 nm satisfies all the following three conditions.
(1) The minimum reflectance is 0.6% or more and 2.0% or less,
(2) The maximum reflectance is 3.5% or less,
(3) The difference between the maximum reflectance and the minimum reflectance is 2.5% or less.   The antireflection film according to claim 1, wherein the B layer is mainly composed of a siloxane polymer bonded to silica-based fine particles.   The antireflection film according to claim 2, wherein the silica-based fine particles have cavities therein.   The antireflection film according to claim 2 or 3, wherein the siloxane polymer contains a polyfunctional fluorine-containing silane compound.   The antireflective film according to claim 1, wherein the refractive index of the A layer is 1.48 or more and 1.62 or less.   The reflection according to claim 1, wherein the A layer contains conductive metal oxide fine particles, and the content of the conductive metal oxide fine particles is 50% by mass or less with respect to the A layer. Prevention film.   The A layer contains mat particles having an average particle diameter of 0.1 to 10.0 µm, and the mat particle content is 30% by mass or less based on the A layer. The antireflection film as described.   The antireflection film according to claim 1, wherein the B layer is laminated on the A layer.   The antireflection film according to claim 1, wherein the layer A contains an organic substituent-containing alkoxysilane compound.   The organic substituent-containing alkoxysilane compound is at least one selected from the group consisting of vinyl groups, epoxy groups, methacryloxy groups, acryloxy groups, amino groups, ureido groups, chloropropyl groups, mercapto groups, sulfide groups, and isocyanate groups. The antireflection film according to claim 9, comprising: The antireflection film according to claim 9 or 10, wherein the organic substituent-containing alkoxysilane compound is a condensate having a kinematic viscosity of 5 mm ² / s (25 ° C) or more.   The antireflection film according to any one of claims 1 to 11, wherein the surface of the antireflection film has a scratch resistance of 3 or more (defined in the text). The antireflection film according to claim 1, wherein the antireflection film has a surface resistance value of 1 × 10 ¹² Ω or less.   The antireflection film according to claim 1, wherein the base film is made of at least one selected from the group consisting of a polyester resin, an acetate resin, and an acrylic resin.   An image display device, wherein the antireflection film according to claim 1 is adhered to an image display surface or a surface of a front plate.