JP2000212547A - Water repellent soilproof agent - Google Patents

Water repellent soilproof agent

Info

Publication number
JP2000212547A
JP2000212547A JP11015772A JP1577299A JP2000212547A JP 2000212547 A JP2000212547 A JP 2000212547A JP 11015772 A JP11015772 A JP 11015772A JP 1577299 A JP1577299 A JP 1577299A JP 2000212547 A JP2000212547 A JP 2000212547A
Authority
JP
Japan
Prior art keywords
water
repellent
polytetrafluoroethylene
agent
wax
Prior art date
Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
Granted
Application number
JP11015772A
Other languages
Japanese (ja)
Other versions
JP4860018B2 (en
Inventor
Shogo Shinohara
生悟 篠原
Okinobu Okamura
起宜 岡村
Current Assignee (The listed assignees may be inaccurate. Google has not performed a legal analysis and makes no representation or warranty as to the accuracy of the list.)
Taiho Kogyo Co Ltd
Original Assignee
Taiho Kogyo Co Ltd
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Taiho Kogyo Co Ltd filed Critical Taiho Kogyo Co Ltd
Priority to JP01577299A priority Critical patent/JP4860018B2/en
Publication of JP2000212547A publication Critical patent/JP2000212547A/en
Application granted granted Critical
Publication of JP4860018B2 publication Critical patent/JP4860018B2/en
Anticipated expiration legal-status Critical
Expired - Fee Related legal-status Critical Current

Abstract

PROBLEM TO BE SOLVED: To obtain a water repellent soilproof agent excellent in workability during application and capable of forming a film excellent in water repellency and soilproof properties. SOLUTION: This water repellent soilproof agent comprises a polytetrafluoroethylene having 1,000-100,000 molecular weight, a spherical organic powder made of a melamine-based synthetic resin, an acryl-based synthetic resin, a silicone resin or a polyethylene resin, a silicone oil, a hydrocarbon-based solvent and a wax. The said polytetrafluoroethylene and the spherical organic powder are dispersed in the said hydrocarbon-based solvent.

Description

【発明の詳細な説明】DETAILED DESCRIPTION OF THE INVENTION

【0001】[0001]

【発明の属する技術分野】本発明は、撥水防汚処理剤に
関し、具体的には、塗装面に撥水性及び防汚性を付与す
る撥水防汚処理剤に関し、特に自動車等の車両、航空
機、事務用家具、及びビル外装等における塗装面に、長
期間に亘って撥水性及び防汚性を付与する撥水防汚処理
剤に関する。
BACKGROUND OF THE INVENTION 1. Field of the Invention The present invention relates to a water-repellent and antifouling agent, and more particularly to a water-repellent and antifouling agent for imparting water repellency and antifouling property to a painted surface. The present invention relates to a water-repellent and antifouling agent that imparts water repellency and antifouling properties to office furniture, painted surfaces of building exteriors, and the like over a long period of time.

【0002】[0002]

【従来の技術及び発明が解決しようとする課題】自動車
等の車両の塗装面に保護被膜を形成し、撥水性、艶、及
び汚染防止効果などの特性を付与する処理剤としては、
従来からカーワックスがよく知られていた。
2. Description of the Related Art As a treatment agent for forming a protective film on a painted surface of a vehicle such as an automobile and imparting properties such as water repellency, luster, and pollution prevention effect,
Conventionally, car wax has been well known.

【0003】カーワックスの配合成分には各社それぞれ
のノウハウがあるが、塗装面を保護し、塗装面に艶を与
える艶出し成分等を包含するワックス成分と、シリコン
オイル等を主成分とし、これに炭化水素及び水などの分
散剤、界面活性剤、並びに研磨剤等が配合されたカーワ
ックスが一般的であった。
[0003] The compounding ingredients of car wax include the know-how of each company. However, a wax component including a polishing component that protects the painted surface and gives a gloss to the painted surface, and a silicone oil and the like as main components are used. In general, a car wax mixed with a dispersant such as hydrocarbon and water, a surfactant, an abrasive, and the like has been generally used.

【0004】しかし、前記カーワックスはシリコーンオ
イルを主成分としているので、前記カーワックスにおい
て塗装面上における撥水性と防汚性とを両立させること
は極めて困難であった。即ち、従来のカーワックスにお
いては、撥水性の良いものは防汚性に劣り、したがって
このようなカーワックスで処理した塗装面においては、
水洗いによって汚れを落とすことが困難であった。一
方、防汚性の良いカーワックスによって処理した塗装面
は、水洗いによって容易に汚れを洗い落とすことが可能
であったが、撥水性に劣る傾向があった。
However, since the car wax contains silicone oil as a main component, it has been extremely difficult for the car wax to achieve both water repellency and antifouling property on a painted surface. That is, in the conventional car wax, those having good water repellency are inferior in antifouling properties, and therefore, on the painted surface treated with such car wax,
It was difficult to remove dirt by washing with water. On the other hand, the painted surface treated with car wax having a good antifouling property could easily wash off dirt by washing with water, but tended to have poor water repellency.

【0005】一方、ポリテトラフルオロエチレンのよう
なフッ素樹脂を主成分とするカーワックスが、特開昭64
-38480号公報、特開平6-25609号、及び特開平9-235506
号等において提案されている。
On the other hand, car wax mainly containing a fluororesin such as polytetrafluoroethylene is disclosed in
-38480, JP-A-6-25609, and JP-A-9-235506
No. has been proposed.

【0006】前記特開昭64-38480号公報においては、分
子量1,000〜100,000の低分子量ポリテトラ
フルオロエチレンと、塗装面に撥水性等を付与するカル
ナバ蝋等の塗装面保護剤と、前記低分子量ポリテトラフ
ルオロエチレン及び前記塗装面保護剤を所定の剤型に調
剤する工業用ナフサ等の分散媒とを含有するコーティン
グ処理剤が提案されている。
Japanese Patent Application Laid-Open No. 64-38480 discloses a low molecular weight polytetrafluoroethylene having a molecular weight of 1,000 to 100,000 and a coating surface protective agent such as carnauba wax which imparts water repellency to the coated surface. A coating agent containing the low molecular weight polytetrafluoroethylene and a dispersion medium such as industrial naphtha for dispensing the coated surface protective agent into a predetermined dosage form has been proposed.

【0007】特開平6-25609号公報においては、溶媒に
溶解又は膨潤させたポリテトラフルオロエチレンとシリ
コーン微粒子とポリエチレン微粒子等とを含有する自動
車の塗装用保護撥水剤が提案されている。
Japanese Patent Application Laid-Open No. 6-25609 proposes a protective water repellent for automotive coating containing polytetrafluoroethylene, silicone fine particles, polyethylene fine particles and the like dissolved or swelled in a solvent.

【0008】特開平9-235506号公報においては、平均分
子量が1,000〜100,000のポリテトラフルオ
ロエチレンとフルオロシリコーン化合物とを含む塗装面
コーティング処理用組成物が提案されている。
Japanese Patent Application Laid-Open No. 9-235506 proposes a coating surface coating composition containing polytetrafluoroethylene having an average molecular weight of 1,000 to 100,000 and a fluorosilicone compound.

【0009】自動車の車体表面にカーワックスを塗布す
る際には、通常、カーワックスを塗布後、暫く放置して
カーワックスの層を乾燥させる。そして前記カーワック
スが乾燥した後、車体表面をタオル等によって拭き、過
剰なカーワックスを除去する。この車体表面をタオル等
によって拭く工程を、通常「拭き上げ」と称する。カー
ワックスには、前記拭き上げが容易に行えることも要求
される。
When car wax is applied to the surface of an automobile body, the car wax is usually applied and then left for a while to dry the car wax layer. After the car wax has dried, the car body surface is wiped with a towel or the like to remove excess car wax. This step of wiping the body surface with a towel or the like is usually referred to as “wiping up”. Car wax is also required to be easily wiped.

【0010】しかし、前記コーティング処理剤、塗装用
保護剤、及び塗装面コーティング処理用組成物(以下
「前記コーティング処理剤等」ということがある。)の
いずれにも含有されている低分子量ポリテトラフルオロ
エチレンは、防水性及び防汚性には優れているが、塗装
面に過剰に付着した場合に容易には拭き取ることができ
ない。
However, the low-molecular-weight polytetrafluoroethylene contained in any of the above-mentioned coating agent, coating protective agent, and coating surface coating composition (hereinafter sometimes referred to as “the above-mentioned coating agent”). Fluoroethylene is excellent in waterproofness and antifouling properties, but cannot be easily wiped off when excessively adhered to a painted surface.

【0011】したがって、前記コーティング処理剤等の
ように大量にポリテトラフルオロエチレンを配合したカ
ーワックスにおいては、拭き上げ性を改善する目的で、
シリコンオイル、フルオロシリコーン油、及びフッ素系
オイル等のオイル成分を大量に配合することが一般に行
われてきた。
Therefore, in the case of a car wax containing a large amount of polytetrafluoroethylene, such as the above-mentioned coating agent, in order to improve wiping properties,
It has been common practice to blend large amounts of oil components such as silicone oil, fluorosilicone oil, and fluorine-based oil.

【0012】しかし、一般に、カーワックスに前記オイ
ル成分を大量に配合すると、塗膜表面に形成された保護
被膜の撥水性及び防汚性が低下する傾向がある。よっ
て、前記コーティング処理剤等においては、ポリテトラ
フルオロエチレンの特徴である防水性及び防汚性等が十
分に発揮されないことが多かった。
However, in general, when a large amount of the oil component is added to car wax, the water repellency and the antifouling property of the protective film formed on the surface of the coating film tend to decrease. Therefore, in many cases, the coating agent and the like do not sufficiently exhibit the waterproofness and antifouling properties, etc., characteristic of polytetrafluoroethylene.

【0013】本発明は、塗布時における作業性に優れ、
更に、自動車車体等の塗装面に塗布することにより、長
期間に亘って、優れた撥水性、及び優れた防汚性、即ち
耐汚染性(汚れ難さ、汚れの落ち易さ)を有する被膜を
形成することのできる撥水防汚処理剤を提供することを
目的とする。
The present invention is excellent in workability at the time of coating,
Furthermore, a coating film having excellent water repellency and excellent antifouling property, that is, antifouling property (difficulty of soiling, easy of soiling) over a long period of time by being applied to a painted surface such as an automobile body. It is an object of the present invention to provide a water-repellent and antifouling agent capable of forming a water repellent.

【0014】[0014]

【課題を解決するための手段】前記課題を解決すること
を目的とする撥水防汚処理剤は、分子量が1,000〜
100,000であるポリテトラフルオロエチレンと、
メラミン系合成樹脂、アクリル系合成樹脂、シリコーン
樹脂、及びポリエチレン樹脂から選択された1以上の合
成樹脂を含有する球状有機パウダーと、シリコーンオイ
ルと、炭化水素系溶剤と、ワックス類とを含有し、前記
ポリテトラフルオロエチレンと前記球状有機パウダーと
が前記炭化水素系溶剤中に分散してなることを特徴とす
る撥水防汚処理剤である。
The water-repellent and antifouling agent for solving the above-mentioned problems has a molecular weight of 1,000 to 1,000.
100,000 polytetrafluoroethylene;
Melamine-based synthetic resin, acrylic-based synthetic resin, silicone resin, and spherical organic powder containing one or more synthetic resins selected from polyethylene resin, silicone oil, hydrocarbon-based solvent, and waxes, The polytetrafluoroethylene and the spherical organic powder are dispersed in the hydrocarbon-based solvent.

【0015】前記撥水防汚処理剤の好ましい態様として
は、例えば、 ・ポリテトラフルオロエチレンの含有量が0.5〜50
重量%である撥水防汚処理剤、 ・球状有機パウダーの含有量が0.5〜20重量%であ
る撥水防汚処理剤、 ・炭化水素溶剤の含有量が30〜97重量%である撥水
防汚処理剤、 ・シリコーンオイルの含有量が0.1〜5重量%である
撥水防汚処理剤、及び ・ワックス類の含有量が1.0〜10重量%である撥水
防汚処理剤 を挙げることができる。
Preferred embodiments of the water-repellent / soil-repellent treatment agent include, for example: a polytetrafluoroethylene content of 0.5 to 50;
A water-repellent antifouling agent having a content of spherical organic powder of 0.5 to 20% by weight; a water-repellent antifouling agent having a content of hydrocarbon solvent of 30 to 97% by weight. A soil repellent, a water-repellent antifouling agent having a silicone oil content of 0.1 to 5% by weight, and a water repellent antifouling agent having a wax content of 1.0 to 10% by weight. be able to.

【0016】[0016]

【発明の実施の形態】(1)各成分についての説明 以下、本発明の撥水防汚処理剤において用いられるポリ
テトラフルオロエチレン、球状有機パウダー、炭化水素
系溶剤、シリコーンオイル、及びワックス類について詳
細に説明する。
DESCRIPTION OF THE PREFERRED EMBODIMENTS (1) Description of each component The polytetrafluoroethylene, spherical organic powder, hydrocarbon solvent, silicone oil, and wax used in the water-repellent and antifouling agent of the present invention will be described in detail below. Will be described.

【0017】(1−1)ポリテトラフルオロエチレン 本発明において用いられるポリテトラフルオロエチレン
としては、四フッ化エチレンを従来公知の方法に従って
重合して得られるポリマー、及び四フッ化エチレンを主
成分とするモノマー組成物を従来公知の方法に従って重
合して得られるポリマーを挙げることができる。
(1-1) Polytetrafluoroethylene As the polytetrafluoroethylene used in the present invention, a polymer obtained by polymerizing ethylene tetrafluoride according to a conventionally known method, and a polymer mainly containing ethylene tetrafluoride And a polymer obtained by polymerizing the monomer composition according to a conventionally known method.

【0018】前記モノマー組成物における四フッ化エチ
レン以外のモノマーとしては、パーフルオロプロピレ
ン、パーフルオロビニルエーテル、モノクロロトリフル
オロエチレン、及びフッ化ビニリデン等のフッ素原子を
含有するフッ素系モノマー、並びにエチレン等の共重合
モノマーを挙げることができる。前記共重合モノマーの
含有量は、前記モノマー組成物全体の10重量%以下で
あることが好ましい。尚、共重合モノマーを2種類以上
含有する場合には、前記共重合モノマーの含有量の合計
が、前記モノマー組成物全体の10重量%以下であるこ
とが好ましい。
The monomers other than ethylene tetrafluoride in the monomer composition include fluorine-containing monomers such as perfluoropropylene, perfluorovinyl ether, monochlorotrifluoroethylene and vinylidene fluoride, and fluorine-containing monomers such as ethylene. Copolymerization monomers can be mentioned. The content of the copolymerized monomer is preferably 10% by weight or less based on the entire monomer composition. When two or more copolymerizable monomers are contained, the total content of the copolymerizable monomers is preferably 10% by weight or less based on the entire monomer composition.

【0019】前記ポリテトラフルオロエチレンの分子量
は、1,000〜100,000の範囲であり、好まし
くは1,000〜25,000の範囲である。分子量が
1,000未満であるポリテトラフルオロエチレンは、
昇華性及び揮発性を有することがあるので、前記ポリテ
トラフルオロエチレンを用いた場合には、長期間持続す
る撥水性及び防汚性が得られないことがある。一方、分
子量が100,000を超えるポリテトラフルオロエチ
レンは、塗装面への密着性が不足するので塗装面に定着
しないことがあり、したがって前記ポリテトラフルオロ
エチレンを用いた場合には、撥水防汚処理剤にポリテト
ラフルオロエチレンを添加した効果が得られないことが
ある。
The molecular weight of the polytetrafluoroethylene is in the range of 1,000 to 100,000, preferably in the range of 1,000 to 25,000. Polytetrafluoroethylene having a molecular weight of less than 1,000 is
Since polytetrafluoroethylene may be sublimable and volatile, long-lasting water repellency and stain resistance may not be obtained when polytetrafluoroethylene is used. On the other hand, polytetrafluoroethylene having a molecular weight exceeding 100,000 does not adhere to the painted surface because of insufficient adhesion to the painted surface, and thus may not be fixed on the painted surface. The effect of adding polytetrafluoroethylene to the treating agent may not be obtained.

【0020】前記ポリテトラフルオロエチレンは、通
常、適宜の分散媒に分散された分散液の形態で、本発明
の撥水防汚処理剤の調製に用いられるが、粉末の形態
で、本発明の撥水防汚処理剤の調製に用いることもでき
る。
The above-mentioned polytetrafluoroethylene is usually used in the preparation of the water-repellent and antifouling agent of the present invention in the form of a dispersion dispersed in an appropriate dispersion medium. It can also be used for the preparation of a water stain control agent.

【0021】前記ポリテトラフルオロエチレンが、分散
液の形態で本発明の撥水防汚処理剤の調製に用いられる
場合には、ポリテトラフルオロエチレン分散液として
は、例えば、フロン系溶剤又はケロシン中にポリテトラ
フルオロエチレン粉末を分散させた分散液等を用いるこ
とができる。
When the polytetrafluoroethylene is used in the form of a dispersion in the preparation of the water-repellent and antifouling agent of the present invention, the polytetrafluoroethylene dispersion may be, for example, a fluorocarbon solvent or kerosene. A dispersion or the like in which polytetrafluoroethylene powder is dispersed can be used.

【0022】前記ポリテトラフルオロエチレン粉末とし
ては、例えば、平均粒径が0.1〜100μm以下であ
るポリテトラフルオロエチレン粒子を挙げることができ
る。但し、前記ポリテトラフルオロエチレン粒子の粒径
は、100μmを超えないことが、前記フロン系溶剤及
び後述する炭化水素系溶剤への分散性の点から好まし
い。
Examples of the polytetrafluoroethylene powder include polytetrafluoroethylene particles having an average particle size of 0.1 to 100 μm or less. However, it is preferable that the particle diameter of the polytetrafluoroethylene particles does not exceed 100 μm from the viewpoint of dispersibility in the fluorocarbon solvent and a hydrocarbon solvent described below.

【0023】前記フロン系溶剤としては、フロンR−1
13(HCFC−141b)、フロンR−11、HCF
C−225、及びフロンR−112等の、塩素原子及び
臭素原子の少なくとも一方とフッ素原子とを有するハロ
ゲン化脂肪族炭化水素化合物を挙げることができる。但
し、脂肪族炭化水素の水素原子が全てフッ素原子によっ
て置換された構造を有するパーフルオロカーボン等、ポ
リテトラフルオロエチレンを溶解又は膨潤させる溶剤
は、好ましくない。
As the chlorofluorocarbon-based solvent, chlorofluorocarbon R-1
13 (HCFC-141b), Freon R-11, HCF
Examples thereof include halogenated aliphatic hydrocarbon compounds having at least one of a chlorine atom and a bromine atom and a fluorine atom, such as C-225 and Freon R-112. However, a solvent that dissolves or swells polytetrafluoroethylene, such as perfluorocarbon having a structure in which all hydrogen atoms of an aliphatic hydrocarbon are replaced by fluorine atoms, is not preferable.

【0024】前記ポリテトラフルオロエチレンの分散液
中におけるポリテトラフルオロエチレン粉末の濃度は、
前記分散液全体に対して通常10〜30重量%であり、
好ましくは10〜25重量%である。
The concentration of the polytetrafluoroethylene powder in the polytetrafluoroethylene dispersion is as follows:
It is usually 10 to 30% by weight based on the entire dispersion,
Preferably it is 10 to 25% by weight.

【0025】前記ポリテトラフルオロエチレンの分散液
の例としては、例えば、旭硝子(株)製の「AG Lu
b」(商品名)、デュポン社製の「KRYTOX D
F」(商品名)、同「VYDAXフロロテロマー」(商
品名)、同「バイダックスAR」(商品名)、及びダイ
キン工業(株)製「ルブロン」(商品名)等を挙げるこ
とができる。
Examples of the polytetrafluoroethylene dispersion include "AG Lu" manufactured by Asahi Glass Co., Ltd.
b ”(trade name),“ KRYTOX D ”manufactured by DuPont
F "(trade name)," VYDAX fluorotelomer "(trade name)," Vidax AR "(trade name), and" Lubron "(trade name) manufactured by Daikin Industries, Ltd.

【0026】前記ポリテトラフルオロエチレンが、粉末
の形態で、分散液の形態で本発明の撥水防汚処理剤の調
製に用いられる場合には、前記ポリテトラフルオロエチ
レン粉末としては、前記ポリテトラフルオロエチレンの
分散液のところで述べたポリテトラフルオロエチレン粉
末と同様の粉末を用いることができる。 (1−2)球状有機パウダー 本発明の撥水防汚処理剤における球状有機パウダーは、
メラミン系合成樹脂、アクリル系合成樹脂、シリコーン
樹脂、及びポリエチレン樹脂から選択された1以上の合
成樹脂を含有する。前記球状有機パウダーにおける前記
合成樹脂の含有量は、通常80重量%以上であり、好ま
しくは90重量%であり、特に好ましくは95重量%以
上である。
When the polytetrafluoroethylene is used in the form of a powder or a dispersion in the preparation of the water-repellent / soil-repellent treatment agent of the present invention, the polytetrafluoroethylene powder may be the polytetrafluoroethylene. Powders similar to the polytetrafluoroethylene powder described for the ethylene dispersion can be used. (1-2) Spherical organic powder The spherical organic powder in the water-repellent and antifouling treatment agent of the present invention includes:
It contains at least one synthetic resin selected from a melamine synthetic resin, an acrylic synthetic resin, a silicone resin, and a polyethylene resin. The content of the synthetic resin in the spherical organic powder is usually 80% by weight or more, preferably 90% by weight, and particularly preferably 95% by weight or more.

【0027】メラミン系合成樹脂としては、例えば、メ
ラミン類と低級アルデヒド類とを重縮合させて得られる
メラミン類・低級アルデヒド樹脂をあげることができ
る。
Examples of the melamine-based synthetic resin include melamine-lower aldehyde resins obtained by polycondensing melamines and lower aldehydes.

【0028】前記メラミン類としては、メラミン、アセ
トグアナミン、及びベンゾグアナミン等を挙げることが
できる。
Examples of the melamines include melamine, acetoguanamine, and benzoguanamine.

【0029】前記低級アルデヒド類としては、ホルムア
ルデヒド、アセトアルデヒド、パラホルムアルデヒド、
パラアセトアルデヒド、及びトリオキサン等を挙げるこ
とができる。
The lower aldehydes include formaldehyde, acetaldehyde, paraformaldehyde,
Examples include paraacetaldehyde and trioxane.

【0030】前記メラミン類・低級アルデヒド樹脂とし
ては、具体的にはメラミンホルムアルデヒド樹脂、アセ
トグアナミンホルムアルデヒド樹脂、及びベンゾグアナ
ミンホルムアルデヒド樹脂等を挙げることができる。
Specific examples of the melamine / lower aldehyde resin include melamine formaldehyde resin, acetoguanamine formaldehyde resin, and benzoguanamine formaldehyde resin.

【0031】前記アクリル系合成樹脂としては、例えば
(メタ)アクリル酸エステル重合体、ヒドロキシ基、ア
ミノ基、及びカルボキシル基等の官能基を有するアクリ
ル系樹脂である官能性アクリル樹脂、並びに前記官能性
アクリル樹脂を架橋した架橋型アクリル樹脂等を挙げる
ことができる。尚、本明細書において、「(メタ)アク
リル」は、メタクリルとアクリルとの両方を意味する。
Examples of the acrylic synthetic resin include a functional acrylic resin which is an acrylic resin having a functional group such as a (meth) acrylic acid ester polymer, a hydroxy group, an amino group, and a carboxyl group; A crosslinked acrylic resin obtained by crosslinking an acrylic resin can be used. In addition, in this specification, "(meth) acryl" means both methacryl and acryl.

【0032】(メタ)アクリル酸エステル重合体として
は、(メタ)アクリル酸メチル、(メタ)アクリル酸エ
チル、(メタ)アクリル酸プロピル、(メタ)アクリル
酸ブチル、(メタ)アクリル酸イソブチル、(メタ)ア
クリル酸ヘキシル、及び(メタ)アクリル酸エチルヘキ
シル等から選択される(メタ)アクリル酸エステルの単
独重合体及び共重合体を挙げることができる。
The (meth) acrylate polymers include methyl (meth) acrylate, ethyl (meth) acrylate, propyl (meth) acrylate, butyl (meth) acrylate, isobutyl (meth) acrylate, Homopolymers and copolymers of (meth) acrylates selected from hexyl (meth) acrylate, ethylhexyl (meth) acrylate and the like can be mentioned.

【0033】前記官能性アクリル樹脂としては、(メ
タ)アクリル酸ヒドロキシエチル、(メタ)アクリル酸
ヒドロキシプロピル、(メタ)アクリル酸、(メタ)ア
クリル酸アミド、及び(メタ)アクリル酸グリシジル等
の官能基を有する官能性アクリルモノマーの重合体、前
記官能性アクリルモノマーと(メタ)アクリル酸エステ
ルとの共重合体、前記官能性アクリルモノマーとスチレ
ンとの共重合体、並びに前記官能性アクリルモノマーと
(メタ)アクリル酸エステルとスチレンとの共重合体等
を挙げることができる。
Examples of the functional acrylic resin include hydroxyethyl (meth) acrylate, hydroxypropyl (meth) acrylate, (meth) acrylic acid, (meth) acrylamide, and glycidyl (meth) acrylate. A polymer of a functional acrylic monomer having a group, a copolymer of the functional acrylic monomer and a (meth) acrylate, a copolymer of the functional acrylic monomer and styrene, and a polymer of the functional acrylic monomer ( A copolymer of (meth) acrylic acid ester and styrene can be exemplified.

【0034】前記架橋型アクリル樹脂としては、例え
ば、前記官能性アクリル樹脂を、ホスゲン、ジイソシア
ネート化合物、マレイン酸、フマル酸、フタル酸、イタ
コン酸、シトラコン酸、及びジビニルベンゼン等の適宜
の架橋剤、熱、電子線、可視光線、紫外線、並びに放射
線等の手段の内、少なくとも1つの手段によって架橋し
た樹脂を挙げることができる。
As the cross-linkable acrylic resin, for example, an appropriate cross-linking agent such as phosgene, a diisocyanate compound, maleic acid, fumaric acid, phthalic acid, itaconic acid, citraconic acid, and divinylbenzene may be used. Examples of the resin include a resin crosslinked by at least one of means such as heat, electron beam, visible light, ultraviolet light, and radiation.

【0035】前記シリコーン樹脂を含有する球状有機パ
ウダーとしては、直鎖状のジメチルポリシロキサンを架
橋した構造を有するシリコーンゴムの微粉末であるシリ
コーンゴムパウダー、シロキサン結合が三次元網目状に
架橋した構造を有するポリオルガノシルセスキオキサン
硬化物等の粉末であるシリコーンレジンパウダー、シリ
コーンゴムパウダーの表面をシリコーンレジンで被覆し
た球状粉末であるシリコーン複合パウダー、及び球状の
アモルファスシリカの表面をシリコーンにより疎水化処
理したシリカ微粉末である疎水性シリカパウダー等を挙
げることができる。
Examples of the spherical organic powder containing the silicone resin include silicone rubber powder, which is a fine powder of silicone rubber having a crosslinked linear dimethylpolysiloxane, and a structure in which siloxane bonds are crosslinked in a three-dimensional network. Resin powder which is a powder of a cured polyorganosilsesquioxane having a silicone resin, silicone composite powder which is a spherical powder in which the surface of a silicone rubber powder is coated with a silicone resin, and hydrophobicizing the surface of a spherical amorphous silica with silicone Hydrophobic silica powder, which is a treated silica fine powder, may be mentioned.

【0036】前記ポリエチレン樹脂を含有する球状有機
パウダーとしては、例えば、ポリエチレン樹脂を流動浸
漬法、粉末回転成形法、及び化学粉砕法等の方法により
処理して得られる微粉末等を挙げることができる。
Examples of the spherical organic powder containing the polyethylene resin include fine powders obtained by treating the polyethylene resin by a method such as a fluid immersion method, a powder rotational molding method, and a chemical pulverization method. .

【0037】前記球状有機パウダーの平均粒径は、通常
1〜20μmの範囲であり、好ましくは1〜11μmの
範囲である。前記範囲の平均粒径を有する球状有機パウ
ダーを用いることにより、本発明の撥水防汚処理剤に、
特に良好な作業性、並びに長期間持続する撥水性及び防
汚性を付与することができる。
The average particle size of the spherical organic powder is usually in the range of 1 to 20 μm, preferably in the range of 1 to 11 μm. By using a spherical organic powder having an average particle size in the above range, to the water-repellent antifouling treatment agent of the present invention,
Particularly good workability and long-lasting water repellency and antifouling properties can be imparted.

【0038】本発明の撥水防汚処理剤における球状有機
パウダーには、真球状の形状を有する粒子の他、実質的
に球状の形状を有する粒子も含まれる。ここで、「実質
的に球状の形状」は、電子顕微鏡及び光学顕微鏡等の拡
大観察手段を用いて形状を観察したときにほぼ球状であ
ると観察される程度に球形に近い形状を意味する。前記
「実質的に球状の形状」としては、具体的には、前記拡
大観察手段を用いて形状を観察したときにほぼ球状であ
ると観察される程度に球形に近い回転楕円体、卵形、及
び西洋梨型等の回転体状の形状等を挙げることができ
る。
The spherical organic powder in the water-repellent and antifouling agent of the present invention includes, in addition to particles having a true spherical shape, particles having a substantially spherical shape. Here, the “substantially spherical shape” means a shape that is almost spherical to such an extent that it is observed to be substantially spherical when the shape is observed using a magnifying observation means such as an electron microscope and an optical microscope. As the "substantially spherical shape", specifically, a spheroid, oval, nearly spherical to the extent that it is observed to be substantially spherical when observing the shape using the magnifying observation means And a shape of a rotating body such as a pear type.

【0039】前記球状有機パウダーの例としては、具体
的には、(株)日本触媒製の商品名「エポスター」(メ
ラミンホルムアルデヒド樹脂及びベンゾグアナミンホル
ムアルデヒド樹脂)、及び綜研化学(株)製の商品名
「MRシリーズ」(架橋アクリル樹脂)、東芝シリコー
ン(株)の商品名「トスパール」(シリコーン樹脂)、
東レ・ダウコーニング・シリコーン(株)の商品名「ト
レフィル」(シリコーン樹脂)、信越シリコン(株)の
商品名「KMPシリーズ」(シリコーン樹脂、シリコー
ンゴム)、及び住友精化(株)の商品名「フロービー
ズ」(ポリエチレン樹脂)等を挙げることができる。
Specific examples of the spherical organic powder include "Eposter" (melamine formaldehyde resin and benzoguanamine formaldehyde resin) manufactured by Nippon Shokubai Co., Ltd., and "Eposter" manufactured by Soken Chemical Co., Ltd. MR series "(crosslinked acrylic resin), Toshiba Silicone Co., Ltd. product name" Tospearl "(silicone resin),
Toray Dow Corning Silicone Co., Ltd. product name "Trefil" (silicone resin), Shin-Etsu Silicone Co., Ltd. product name "KMP series" (silicone resin, silicone rubber), and Sumitomo Seika Co., Ltd. product name "Flow beads" (polyethylene resin) and the like can be mentioned.

【0040】(1−3)炭化水素系溶剤 本発明の撥水防汚処理剤において、炭化水素系溶剤は、
前記ポリテトラフルオロエチレン及び球状有機パウダー
が分散する分散媒としての機能を有している。
(1-3) Hydrocarbon Solvent In the water repellent / fouling / treating agent of the present invention, the hydrocarbon solvent is
It has a function as a dispersion medium in which the polytetrafluoroethylene and the spherical organic powder are dispersed.

【0041】したがって、前記ポリテトラフルオロエチ
レン及び球状有機パウダーを実質的に溶解させず、又膨
潤させない炭化水素系の溶剤は、本発明の撥水防汚処理
剤における炭化水素系溶剤として用いることができる。
ここで、文言「実質的に溶解させず、又膨潤させない」
は、前記ポリテトラフルオロエチレン及び球状有機パウ
ダーを前記炭化水素系溶剤に分散したときに、前記ポリ
テトラフルオロエチレン及び球状有機パウダーが、前記
炭化水素系溶剤に溶解せず、更に、肉眼、拡大鏡、及び
顕微鏡等の観察手段による観察によって確認できる程度
には前記炭化水素系溶剤によって膨潤しないことを意味
する。
Therefore, a hydrocarbon solvent which does not substantially dissolve or swell the polytetrafluoroethylene and the spherical organic powder can be used as the hydrocarbon solvent in the water-repellent and antifouling agent of the present invention. .
Here, the phrase "does not substantially dissolve or swell"
When the polytetrafluoroethylene and the spherical organic powder are dispersed in the hydrocarbon-based solvent, the polytetrafluoroethylene and the spherical organic powder do not dissolve in the hydrocarbon-based solvent. And does not swell with the hydrocarbon-based solvent to the extent that it can be confirmed by observation with an observation means such as a microscope.

【0042】前記炭化水素系溶剤としては、例えば脂肪
族炭化水素系溶剤、芳香族炭化水素系溶剤、及び石油系
溶剤等を挙げることができる。
Examples of the hydrocarbon solvents include aliphatic hydrocarbon solvents, aromatic hydrocarbon solvents, and petroleum solvents.

【0043】前記脂肪族炭化水素系溶剤としては、ペン
タン、ヘキサン、ヘプタン、オクタン、イソオクタン、
ノナン、デカン、ウンデカン、及びドデカン等の直鎖状
脂肪族炭化水素、2ーメチルブタン、2ーメチルペンタ
ン、2,3−ジメチルブタン、2,2−ジメチルブタ
ン、2,2,3−トリメチルペンタン、及び2,2,5
−トリメチルヘキサン等の分岐鎖状脂肪族炭化水素、並
びにシクロペンタン、シクロヘキサン、メチルシクロヘ
キサン、メチルシクロペンタン、エチルシクロヘキサ
ン、p−メンタン、及びデカリン等の脂環式炭化水素を
挙げることができる。
Examples of the aliphatic hydrocarbon solvents include pentane, hexane, heptane, octane, isooctane,
Linear aliphatic hydrocarbons such as nonane, decane, undecane, and dodecane, 2-methylbutane, 2-methylpentane, 2,3-dimethylbutane, 2,2-dimethylbutane, 2,2,3-trimethylpentane, and 2, 2,5
-Branched aliphatic hydrocarbons such as trimethylhexane, and alicyclic hydrocarbons such as cyclopentane, cyclohexane, methylcyclohexane, methylcyclopentane, ethylcyclohexane, p-menthane, and decalin.

【0044】前記芳香族炭化水素系溶剤の例としては、
ベンゼン、トルエン、p−キシレン、o−キシレン、m
−キシレン、エチルベンゼン、クメン、n−ブチルベン
ゼン、sec−ブチルベンゼン、tert−ブチルベン
ゼン、p−シメン、メシチレン、テトラリン、シクロヘ
キシルベンゼン、o−ジエチルベンゼン、m−ジエチル
ベンゼン、p−ジエチルベンゼン、ペンチルベンゼン、
ジペンチルベンゼン、及びドデシルベンゼン等を挙げる
ことができる。
Examples of the aromatic hydrocarbon solvent include:
Benzene, toluene, p-xylene, o-xylene, m
-Xylene, ethylbenzene, cumene, n-butylbenzene, sec-butylbenzene, tert-butylbenzene, p-cymene, mesitylene, tetralin, cyclohexylbenzene, o-diethylbenzene, m-diethylbenzene, p-diethylbenzene, pentylbenzene,
Examples thereof include dipentylbenzene and dodecylbenzene.

【0045】前記石油系溶剤としては、例えば30〜3
00℃の範囲の沸点を有する石油系溶剤を挙げることが
でき、具体的には、石油エーテル、石油ベンジン、石油
ナフサ、リグロイン、工業ガソリン、ケロシン、及びソ
ルベントナフサ等を挙げることができる。
As the petroleum solvent, for example, 30 to 3
Petroleum solvents having a boiling point in the range of 00 ° C. can be mentioned, and specific examples thereof include petroleum ether, petroleum benzene, petroleum naphtha, ligroin, industrial gasoline, kerosene, and solvent naphtha.

【0046】前記炭化水素系溶剤としては、前記石油系
溶剤が、安価であり、臭気及び毒性が少なく、更に、後
述するシリコーンオイル及びワックス類を良く溶解する
故に好ましく、前記石油系溶剤の内、特に、石油エーテ
ル、石油ベンジン、石油ナフサ、リグロイン、及びソル
ベントナフサ等が好ましい。
As the hydrocarbon solvent, the petroleum solvent is preferable because it is inexpensive, has low odor and toxicity, and further dissolves well the silicone oils and waxes described later. Particularly, petroleum ether, petroleum benzine, petroleum naphtha, ligroin, and solvent naphtha are preferable.

【0047】(1−4)シリコーンオイル シリコーンオイルとしては、常温で液状である液状シリ
コーンを挙げることができ、具体的には、室温(例えば
25℃)で0.65〜1,000,000cStの粘度
を有する液状シリコーンを挙げることができる。
(1-4) Silicone Oil Examples of the silicone oil include liquid silicone which is liquid at room temperature, and specifically, 0.65 to 1,000,000 cSt at room temperature (for example, 25 ° C.). A liquid silicone having a viscosity can be used.

【0048】前記液状シリコーンとしては、ジメチルシ
リコーンオイル、メチルフェニルシリコーンオイル、メ
チル水素シリコーンオイル、及び変性シリコーンオイル
等を挙げることができる。
Examples of the liquid silicone include dimethyl silicone oil, methylphenyl silicone oil, methyl hydrogen silicone oil, and modified silicone oil.

【0049】前記変性シリコーンオイルとしては、ジメ
チルシリコーンオイルのメチル基の少なくとも一部が、
例えばポリオキシアルキレン基、長鎖アルキル基、フロ
ロアルキル基、クロロフェニル基、アミノ基、アミノ基
含有アルキル基、エポキシ基、エポキシ基含有アルキル
基、メルカプト基、メルカプト含有アルキル基、カルボ
キシル基、カルボキシル基含有基、高級脂肪酸残基、及
びビニル基からなる群から選択された1種以上の基によ
って置換されたシリコーンオイル等を挙げることができ
る。
As the modified silicone oil, at least a part of the methyl groups of the dimethyl silicone oil is
For example, polyoxyalkylene group, long chain alkyl group, fluoroalkyl group, chlorophenyl group, amino group, amino group-containing alkyl group, epoxy group, epoxy group-containing alkyl group, mercapto group, mercapto-containing alkyl group, carboxyl group, carboxyl group-containing And a silicone oil substituted by at least one group selected from the group consisting of a group, a higher fatty acid residue, and a vinyl group.

【0050】(1−5)ワックス類 本発明の撥水防汚材に用いられるワックス類としては、
植物系ワックス、動物系ワックス、鉱物系ワックス、合
成ワックス、及びワックス様物等を挙げることができ
る。
(1-5) Waxes The waxes used in the water-repellent and antifouling material of the present invention include:
Vegetable waxes, animal waxes, mineral waxes, synthetic waxes, and wax-like substances can be exemplified.

【0051】前記植物系ワックスとしては、例えばカル
ナウバワックス、キャンデリラワックス、ライスワック
ス、及び木蝋等を挙げることができる。
Examples of the vegetable wax include carnauba wax, candelilla wax, rice wax, and wood wax.

【0052】前記動物系ワックスとしては、蜜蝋、鯨
蝋、ラノリン、ラノリン誘導体、牛脂、及び豚脂等を挙
げることができる。
Examples of the animal wax include beeswax, spermaceti, lanolin, lanolin derivatives, tallow and lard.

【0053】前記鉱物系ワックスとしては、パラフィ
ン、ワセリン、オゾケライト、セレシン、及びマイクロ
クリスタリンワックス等を挙げることができる。
Examples of the mineral wax include paraffin, vaseline, ozokerite, ceresin, and microcrystalline wax.

【0054】前記合成ワックスとしては、ポリエチレン
ワックス、ポリプロピレンワックス、α−オレフィンワ
ックス、合成脂肪酸と高級アルコールとのエステル、合
成脂肪酸グリセリド、酸化パラフィン、酸化マイクロク
リスタリンワックス、並びにオレフィンと、無水マレイ
ン酸、アクリル酸、及び酢酸ビニルからなる群から選択
された1又は2以上のモノマーとの共重合体を挙げるこ
とができる。
Examples of the synthetic wax include polyethylene wax, polypropylene wax, α-olefin wax, ester of synthetic fatty acid and higher alcohol, synthetic fatty acid glyceride, paraffin oxide, microcrystalline oxide wax, olefin, maleic anhydride, acrylic Copolymers with one or more monomers selected from the group consisting of acids and vinyl acetate can be mentioned.

【0055】ワックス様物としては、高級脂肪酸、合成
脂肪酸、高級アルコール、硬化油、脂肪酸アミド、金属
石鹸、及びポリエーテル等を挙げることができる。
Examples of the wax-like substance include higher fatty acids, synthetic fatty acids, higher alcohols, hardened oils, fatty acid amides, metal soaps, and polyethers.

【0056】(2)各成分の配合量 ポリテトラフルオロエチレン、球状有機パウダー、炭化
水素系溶剤、シリコーンオイル、及びワックス類の配合
量は以下の通りである。
(2) Compounding Amount of Each Component The compounding amounts of polytetrafluoroethylene, spherical organic powder, hydrocarbon solvent, silicone oil, and wax are as follows.

【0057】ポリテトラフルオロエチレンの配合量は、
撥水防汚処理剤の全体に対して通常0.5〜50重量%
の範囲であり、好ましくは1〜30重量%の範囲であ
る。
The blending amount of polytetrafluoroethylene is
Usually 0.5 to 50% by weight based on the total weight of the water repellent / antifouling agent
And preferably in the range of 1 to 30% by weight.

【0058】本発明の撥水防汚処理剤においてポリテト
ラフルオロエチレンの配合量が前記範囲であれば、塗布
後の拭き上げが容易であり、高い撥水性と防汚性とを有
する被膜を付与する撥水防汚処理剤が得られる。
When the compounding amount of polytetrafluoroethylene in the water-repellent / soil-repelling agent of the present invention is within the above range, it is easy to wipe off after application and a film having high water repellency and antifouling property is provided. A water-repellent and stain-proofing agent is obtained.

【0059】尚、前記ポリテトラフルオロエチレンを分
散液の形態で配合する場合には、撥水防汚処理剤全体に
対するポリテトラフルオロエチレン粉末の量が前記割合
になるように前記分散液を配合することが好ましい。
When the polytetrafluoroethylene is blended in the form of a dispersion, the dispersion should be blended so that the amount of the polytetrafluoroethylene powder with respect to the entire water-repellent and antifouling agent is in the above-mentioned ratio. Is preferred.

【0060】球状有機パウダーの配合量は、撥水防汚処
理剤の全体に対して通常0.5〜20重量%の範囲であ
り、好ましくは1〜15重量%の範囲である。球状有機
パウダーの配合量が前記範囲であれば、特に長期間持続
する撥水性及び防汚性を付与する撥水防汚処理剤が得ら
れる。又、前記球状有機パウダーの配合割合が前記範囲
内であれば、前記撥水防汚処理剤の塗布時及び拭き上げ
時の作業性が大幅に向上する。
The compounding amount of the spherical organic powder is usually in the range of 0.5 to 20% by weight, preferably in the range of 1 to 15% by weight, based on the whole water-repellent and antifouling agent. When the compounding amount of the spherical organic powder is within the above range, a water-repellent and antifouling agent which imparts water repellency and antifouling property that is particularly long-lasting can be obtained. Further, when the compounding ratio of the spherical organic powder is within the above range, the workability at the time of applying and wiping the water repellent / soil repellent is greatly improved.

【0061】前記炭化水素系溶剤の配合量は、撥水防汚
処理剤全体に対して通常30〜97重量%の範囲であ
り、好ましくは50〜85重量%の範囲である。
The amount of the hydrocarbon solvent is usually in the range of 30 to 97% by weight, preferably 50 to 85% by weight, based on the total amount of the water-repellent and antifouling agent.

【0062】シリコーンオイルの含有量は、通常0.1
〜5重量%であり、好ましくは0.5〜4重量%であ
る。そして、ワックス類の含有量は、通常1〜10重量
%であり、好ましくは2〜7重量%である。シリコーン
オイル及びワックス類を前記範囲の含有量で含有する撥
水防汚処理剤は、自動車等の塗装面等に極めて美麗な艶
を付与する上、伸びが良い点で好ましい。
The content of silicone oil is usually 0.1
-5% by weight, preferably 0.5-4% by weight. The content of the wax is usually 1 to 10% by weight, preferably 2 to 7% by weight. The water-repellent and antifouling agent containing the silicone oil and the wax in the above-mentioned ranges is preferable in that it imparts a very beautiful luster to a painted surface of an automobile or the like and has good elongation.

【0063】(3)その他の成分 本発明の撥水防汚処理剤には、前記ポリテトラフルオロ
エチレン、前記球状有機パウダー、前記炭化水素系溶
剤、前記シリコーンオイル、及び前記ワックス類に加え
て、艶出し剤、樹脂類、界面活性剤、研磨剤、及び増粘
剤の内、少なくとも1つを配合することができる。
(3) Other Components In addition to the polytetrafluoroethylene, the spherical organic powder, the hydrocarbon-based solvent, the silicone oil, and the waxes, the water-repellent and stain-proofing agent of the present invention includes a luster. At least one of a dispensing agent, a resin, a surfactant, an abrasive, and a thickener can be blended.

【0064】樹脂類としては、石油樹脂、メタクリル樹
脂、樹脂ワニス、テルペン樹脂、ロジンガム、及びコー
パル等を挙げることができる。
Examples of the resin include petroleum resin, methacrylic resin, resin varnish, terpene resin, rosin gum, copal and the like.

【0065】界面活性剤としては、非イオン界面活性
剤、陰イオン面活性剤、陽イオン界面活性剤、両性界面
活性剤、及びフッ素系界面活性剤等を挙げることができ
る。尚、本発明の撥水防汚処理剤において前記界面活性
剤を配合する場合には、前記界面活性剤に加えて更に水
を配合することにより、エマルションの形態を有する撥
水防汚処理剤を調製することができる。
Examples of the surfactant include a nonionic surfactant, an anionic surfactant, a cationic surfactant, an amphoteric surfactant, and a fluorine-based surfactant. When the surfactant is blended in the water-repellent antifouling agent of the present invention, a water-repellent antifouling agent having an emulsion form is prepared by further mixing water in addition to the surfactant. be able to.

【0066】研磨剤としては、シリカ、カオリン、珪藻
土、ゼオライト、炭酸カルシウム、アルミナ、水酸化ア
ルミニウム、酸化セリウム、及び酸化マグネシウム等を
挙げることができる。
Examples of the abrasive include silica, kaolin, diatomaceous earth, zeolite, calcium carbonate, alumina, aluminum hydroxide, cerium oxide, and magnesium oxide.

【0067】粉体としては、無機粉体及び合成樹脂粉体
を挙げることができる。無機粉体としては、例えば微粉
末シリカ及び微粉末アルミナ等を挙げることができ、合
成樹脂粉体としては、ポリオレフィン粉末、ポリテトラ
フルオロエチレン粉末、及びシリコーン樹脂粉末等を挙
げることができる。尚、前記粉体は不定形であってもよ
い。
Examples of the powder include an inorganic powder and a synthetic resin powder. Examples of the inorganic powder include fine powder silica and fine powder alumina, and examples of the synthetic resin powder include polyolefin powder, polytetrafluoroethylene powder, and silicone resin powder. Incidentally, the powder may be in an irregular shape.

【0068】増粘剤としては、無機増粘剤、セルロース
誘導体系増粘剤、澱粉誘導体系増粘剤、合成増粘剤、植
物性増粘剤、及び動物性増粘剤等を挙げることができ
る。
Examples of the thickener include an inorganic thickener, a cellulose derivative thickener, a starch derivative thickener, a synthetic thickener, a vegetable thickener, and an animal thickener. it can.

【0069】前記無機増粘剤としては、例えばベントナ
イト、モンモリロナイト、及び雲母等の粘土鉱物等を挙
げることができる。
Examples of the inorganic thickener include clay minerals such as bentonite, montmorillonite, and mica.

【0070】前記セルロース誘導体系増粘剤としては、
カルボキシメチルセルロース、メチルセルロース、及び
エチルセルロース等を挙げることができる。
The cellulose derivative-based thickeners include:
Examples thereof include carboxymethyl cellulose, methyl cellulose, and ethyl cellulose.

【0071】前記澱粉誘導体系増粘剤としては、可溶性
澱粉、カルボキシメチル澱粉、及びジアルデヒド澱粉等
を挙げることができる。
Examples of the starch derivative-based thickener include soluble starch, carboxymethyl starch, and dialdehyde starch.

【0072】合成増粘剤としては、例えばポリビニルア
ルコール、ポリアクリル酸塩、及び水溶性ポリアクリル
共重合体等を挙げることができる。
Examples of the synthetic thickener include polyvinyl alcohol, polyacrylate, and a water-soluble polyacryl copolymer.

【0073】植物性増粘剤としては、ガラクタン、トラ
ガカントガム、アラビアガム、カラヤガム、キサンタン
ガム、ローカストビーンガム、タラガム、タマリンドガ
ム、クインスシードガム、ペクチン質多糖類、寒天、カ
ラギーナン、アルギン酸ナトリウム、及びシクロデキス
トリン等の、植物の分泌物、種子からの抽出物、及び海
藻等に由来する増粘剤を挙げることができる。
Examples of the vegetable thickener include galactan, tragacanth gum, gum arabic, karaya gum, xanthan gum, locust bean gum, tara gum, tamarind gum, quince seed gum, pectic polysaccharide, agar, carrageenan, sodium alginate, and cyclodextrin. And the like, and secretions of plants, extracts from seeds, and thickeners derived from seaweed and the like.

【0074】動物性増粘剤としては、ゼラチン、カゼイ
ン、コラーゲン、キチン、及びキトサン等の、動物の
筋、骨格、及び外骨格等に由来する増粘剤を挙げること
ができる。
Examples of animal thickeners include thickeners derived from animal muscle, skeleton, exoskeleton and the like, such as gelatin, casein, collagen, chitin, and chitosan.

【0075】前記艶出し剤、樹脂類、界面活性剤、研磨
剤、粉体、及び増粘剤等(以下「その他の成分」という
ことがある。)の種類及び配合量は、例えば前記撥水防
汚処理剤の形態、及び前記撥水防汚処理剤に要求される
性能に応じて自由に選択される。但し、前記その他の成
分を過剰に配合すると、撥水性及び防汚性の高い被膜が
得られない可能性があるから、前記その他の成分の配合
量は、前記撥水防汚処理剤全体に対して合計で20重量
%を超えないことが好ましく、特に10重量%以下の範
囲が好ましい。
The types and amounts of the above-mentioned polishes, resins, surfactants, abrasives, powders, thickeners and the like (hereinafter sometimes referred to as “other components”) are determined, for example, by the water-repellent protection. It is freely selected according to the form of the soil treatment agent and the performance required of the water-repellent and soil-resistant treatment agent. However, if the other components are excessively mixed, there is a possibility that a film having high water repellency and antifouling property may not be obtained, so the amount of the other components is based on the entire water repellent and antifouling agent. It is preferable that the total amount does not exceed 20% by weight, and particularly a range of 10% by weight or less.

【0076】(4)本発明の撥水防汚処理剤の調製方法 本発明の撥水防汚処理剤の調製において、ポリテトラフ
ルオロエチレン、球状有機パウダー、炭化水素系溶剤、
シリコーンオイル、及びワックス類の配合順序には特に
制限はない。
(4) Method for Preparing Water-Repellent / Soil-Repellent Treatment Agent of the Present Invention In preparing the water-repellent / soil-repellent treatment agent of the present invention, polytetrafluoroethylene, spherical organic powder, hydrocarbon solvent
There are no particular restrictions on the order in which the silicone oil and waxes are compounded.

【0077】前記ポリテトラフルオロエチレンについて
は、前述のように分散液の形態で配合してもよく、又、
粉末の形態で配合してもよい。
The polytetrafluoroethylene may be blended in the form of a dispersion as described above.
You may mix | blend in the form of a powder.

【0078】前記ポリテトラフルオロエチレンを分散液
の形態で配合する撥水防汚処理剤の調製方法としては、
例えば、前記炭化水素系溶剤にワックス類を溶解させ、
得られた溶液に、前記ポリテトラフルオロエチレンの分
散液と、球状有機パウダーと、シリコーンオイルとを配
合する方法等を挙げることができる。
The method for preparing the water-repellent / soil-repellent treatment agent containing the above-mentioned polytetrafluoroethylene in the form of a dispersion liquid is as follows.
For example, a wax is dissolved in the hydrocarbon solvent,
A method of blending the obtained solution with the dispersion of polytetrafluoroethylene, the spherical organic powder, and the silicone oil can be used.

【0079】前記方法において、前記炭化水素系溶剤に
ワックス類を溶解させた溶液に、ポリテトラフルオロエ
チレンの分散液と、球状有機パウダーと、シリコーンオ
イルとを配合する順序には特に制限はない。したがっ
て、ポリテトラフルオロエチレンの分散液と、球状有機
パウダーと、シリコーンオイルとを前記溶液に同時に配
合しても良く、前記溶液に先ずテトラフルオロエチレン
の分散液を配合し、次いで球状有機パウダーを配合し、
最後にシリコーンオイルを配合しても良い。
In the above method, there is no particular limitation on the order in which the dispersion of polytetrafluoroethylene, the spherical organic powder, and the silicone oil are mixed with the solution in which the wax is dissolved in the hydrocarbon solvent. Therefore, a dispersion of polytetrafluoroethylene, a spherical organic powder, and a silicone oil may be simultaneously blended into the solution, and a tetrafluoroethylene dispersion is blended into the solution first, and then a spherical organic powder is blended. And
Finally, silicone oil may be blended.

【0080】ポリテトラフルオロエチレンを分散液の形
態で配合する撥水防汚処理剤の調製方法としては、他
に、前記ポリテトラフルオロエチレンの分散液と、球状
有機パウダーと、炭化水素系溶剤と、シリコーンオイル
と、ワックス類とを同時に混合する方法等を挙げること
ができる。
As a method for preparing a water-repellent / soil-repellent treating agent in which polytetrafluoroethylene is blended in the form of a dispersion, other than the above, a dispersion of polytetrafluoroethylene, a spherical organic powder, a hydrocarbon solvent, A method in which silicone oil and waxes are mixed at the same time can be used.

【0081】一方、前記ポリテトラフルオロエチレンを
粉末の形態で配合する撥水防汚処理剤の調製方法として
は、例えば、前記炭化水素系溶剤に最初に前記ワックス
類を溶解させ、得られた溶液に、前記ポリテトラフルオ
ロエチレンの粉末と、球状有機パウダーと、シリコーン
オイルとを配合する方法を挙げることができる。
On the other hand, as a method for preparing a water-repellent / fouling-treating agent containing the polytetrafluoroethylene in the form of a powder, for example, the waxes are first dissolved in the hydrocarbon-based solvent, and the resulting solution is added to the solution. And a method of blending the polytetrafluoroethylene powder, the spherical organic powder, and the silicone oil.

【0082】前記方法においては、炭化水素系溶剤にワ
ックス類を溶解させた溶液に、ポリテトラフルオロエチ
レンの粉末と、球状有機パウダーと、シリコーンオイル
とを配合する順序には特に制限はない。前記溶液に、前
記ポリテトラフルオロエチレンの粉末と、前記球状有機
パウダーと、前記シリコーンオイルとを同時に配合して
もよく、前記溶液に、先ず前記ポリテトラフルオロエチ
レンの粉末を懸濁させ、次いで前記球状有機パウダーを
懸濁させ、最後に前記シリコーンオイルを配合してもよ
い。
In the above method, there is no particular limitation on the order in which the polytetrafluoroethylene powder, the spherical organic powder, and the silicone oil are mixed with the solution in which the wax is dissolved in the hydrocarbon solvent. In the solution, the polytetrafluoroethylene powder, the spherical organic powder, and the silicone oil may be simultaneously compounded.In the solution, the polytetrafluoroethylene powder is first suspended, and then the The spherical organic powder may be suspended, and finally, the silicone oil may be blended.

【0083】ポリテトラフルオロエチレンを粉末の形態
で配合する撥水防汚処理剤の調製方法としては、他に、
前記炭化水素系溶剤に最初にポリテトラフルオロエチレ
ンの粉末を分散させ、次いで球状有機パウダーを分散さ
せ、次いで、シリコーンオイル、及びワックス類を配合
する方法を挙げることができる。
As a method for preparing a water-repellent / fouling / treating agent containing polytetrafluoroethylene in the form of powder,
A method of first dispersing polytetrafluoroethylene powder in the hydrocarbon-based solvent, then dispersing the spherical organic powder, and then blending silicone oil and waxes can be mentioned.

【0084】前記ポリテトラフルオロエチレンを粉末の
形態で配合する撥水防汚処理剤の調製方法としては、更
に、ポリテトラフルオロエチレンの粉末と球状有機パウ
ダーとを乾燥状態において予め混合し、得られた混合物
を炭化水素系溶剤中に分散し、得られた分散液にシリコ
ーンオイル及びワックス類を配合する方法、及び炭化水
素系溶剤中に最初に球状有機パウダーを分散させ、次い
で前記ポリテトラフルオロエチレンを分散させ、得られ
た分散液にシリコーンオイル及びワックス類を配合する
方法等を挙げることができる。
As a method for preparing a water-repellent / soil-repelling agent containing the above-mentioned polytetrafluoroethylene in the form of a powder, a polytetrafluoroethylene powder and a spherical organic powder were further mixed in advance in a dry state. Dispersing the mixture in a hydrocarbon solvent, a method of blending silicone oil and waxes in the resulting dispersion, and first dispersing the spherical organic powder in the hydrocarbon solvent, then the polytetrafluoroethylene Dispersion and a method of blending silicone oil and wax with the obtained dispersion can be mentioned.

【0085】撥水防汚処理剤に前記その他の成分を配合
する場合には、前記その他の成分をどの時点で配合して
もよい。
When the above-mentioned other components are added to the water-repellent / antifouling agent, the other components may be added at any time.

【0086】したがって、炭化水素系溶剤にワックス類
を溶解させた溶液に、ポリテトラフルオロエチレンの粉
末又は分散液と、球状有機パウダーと、シリコーンオイ
ルとを同時に配合する場合には、前記その他の成分を、
前記各成分を配合するのと同時に前記溶液に配合するこ
とができる。
Therefore, when a powder or dispersion of polytetrafluoroethylene, a spherical organic powder, and silicone oil are simultaneously added to a solution in which waxes are dissolved in a hydrocarbon solvent, the above-mentioned other components are used. To
The respective components can be simultaneously added to the solution at the same time.

【0087】一方、炭化水素系溶剤にワックス類を溶解
させた溶液に、ポリテトラフルオロエチレンの粉末又は
分散液と、球状有機パウダーと、シリコーンオイルとを
この順序にしたがって配合する場合には、その他の成分
を、ポリテトラフルオロエチレンの粉末又は分散液を配
合する前又は後に配合しても良く、球状有機パウダーを
配合した後に配合してもよく、又、シリコーンオイルを
配合した後、即ち最後に配合しても良い。
On the other hand, when a powder or dispersion of polytetrafluoroethylene, a spherical organic powder, and silicone oil are mixed in this order in a solution in which waxes are dissolved in a hydrocarbon solvent, May be blended before or after blending the polytetrafluoroethylene powder or dispersion, may be blended after blending the spherical organic powder, or after blending the silicone oil, that is, finally You may mix.

【0088】撥水防汚処理剤の調製は、常温で行っても
良く、加熱下で行っても良い。ここで、「常温で行う」
は、系を加熱することなく前記撥水防汚処理剤の調製を
行うことを意味する。但し、撥水防汚処理剤の調製を
「常温で行う」場合においても、ワックス類を予め炭化
水素系溶剤に溶解させてから残りの成分を配合する場合
には、前記ワックス類の融点まで加熱した炭化水素系溶
剤に前記ワックス類を溶解させ、得られた溶液を室温ま
で冷却して、この溶液に残りの成分を配合することがで
きる。
The preparation of the water-repellent / soil-repellent treating agent may be carried out at normal temperature or under heating. Here, "perform at room temperature"
Means that the water-repellent and antifouling agent is prepared without heating the system. However, even when the preparation of the water-repellent and antifouling agent is performed “at room temperature”, when the waxes are previously dissolved in a hydrocarbon solvent and the remaining components are blended, the wax is heated to the melting point of the waxes. The waxes are dissolved in a hydrocarbon solvent, the resulting solution is cooled to room temperature, and the remaining components can be added to the solution.

【0089】(5)本発明の撥水防汚処理剤の使用方法 本発明の撥水防汚処理剤は、従来のカーワックスを塗布
する際の手順と同様の手順に従って使用することができ
る。
(5) Method of Using the Water-Repellent / Soil-Repellent Treatment Agent of the Present Invention The water-repellent / soil-repellent treatment agent of the present invention can be used in accordance with the same procedure as that for applying a conventional car wax.

【0090】例えば、本発明の撥水防汚処理剤を自動車
の車体に塗布する場合には、前記撥水防汚処理剤をスポ
ンジ又は雑巾等に付着させて、前記スポンジ又は雑巾で
自動車等の塗装面を軽く擦ることにより前記撥水防汚処
理剤を塗布することができる。そして、塗布された撥水
防汚処理剤を自然乾燥させ、最後に車体表面を拭き上げ
て過剰な撥水防汚処理剤を拭き取ることにより、前記車
体表面に撥水性及び防汚性に優れた被膜が形成される。
For example, when the water-repellent and stain-proofing agent of the present invention is applied to the body of an automobile, the water-repellent and stain-proofing agent is attached to a sponge or a cloth, and the sponge or the cloth is used to paint the surface of an automobile or the like. By lightly rubbing, the water-repellent and antifouling agent can be applied. Then, the applied water-repellent and antifouling agent is naturally dried, and finally, the body surface is wiped up and excess water-repellent and antifouling agent is wiped off, whereby a film having excellent water-repellent and antifouling properties is formed on the body surface. It is formed.

【0091】[0091]

【発明の作用】本発明の撥水防汚処理剤には、ポリテト
ラフルオロエチレンに加えて球状有機パウダーが配合さ
れている。よって前記撥水防汚処理剤においては、艶出
し剤等の油状成分の配合量を従来のカーワックス等より
も大幅に少なくすることができ、場合によっては前記油
状成分の配合が不要になる。したがって、前記撥水防汚
処理剤により塗装面に形成される被膜は、高い防汚性を
有している。
The water-repellent and antifouling agent of the present invention contains a spherical organic powder in addition to polytetrafluoroethylene. Therefore, in the water-repellent and antifouling agent, the amount of the oil component such as a polishing agent can be greatly reduced as compared with the conventional car wax, and in some cases, the oil component becomes unnecessary. Therefore, the coating film formed on the painted surface by the water-repellent / antifouling agent has high antifouling properties.

【0092】前記撥水防汚処理剤の被膜が乾燥すると、
前記撥水防汚処理剤中の球状有機パウダーがポリテトラ
フルオロエチレンの被膜に取り込まれる。よって、前記
拭き上げ作業の際には、前記球状有機パウダーがポリテ
トラフルオロエチレン被膜中において恰もボールベアリ
ングのように転がると考えられる。故に、本発明の撥水
防汚処理剤においては、前記油状成分の配合量が少ない
か又は前記油状成分を殆ど若しくは全く含有しないにも
かかわらず、乾燥後の拭き上げ作業が極めて容易であ
り、清潔なタオルで1回拭き上げる程度で、過剰な撥水
防汚処理剤の層を除去することができる。
When the coating of the water-repellent and antifouling agent is dried,
The spherical organic powder in the water-repellent and antifouling agent is incorporated into the polytetrafluoroethylene coating. Therefore, it is considered that the spherical organic powder rolls like a ball bearing in the polytetrafluoroethylene coating during the wiping operation. Therefore, in the water-repellent and antifouling treatment agent of the present invention, the wiping operation after drying is extremely easy and the cleanliness is high even though the amount of the oil component is small or contains little or no oil component. It is possible to remove an excessive layer of the water-repellent and antifouling agent by wiping it once with a simple towel.

【0093】加えて、本発明の撥水防汚処理剤において
は、前述のように、球状有機パウダーがポリテトラフル
オロエチレンの被膜に取り込まれた構造の被膜が形成さ
れる故に、ポリテトラフルオロエチレン単独の場合より
も更に高度の撥水・防汚効果が得られると考えられる。
In addition, in the water-repellent and antifouling agent of the present invention, as described above, since a film having a structure in which the spherical organic powder is incorporated into the film of polytetrafluoroethylene is formed, polytetrafluoroethylene alone is used. It is considered that a higher degree of water repellency and antifouling effect can be obtained than in the case of

【0094】更に、本発明の撥水防汚処理剤には、シリ
コーンオイル及びワックス類が配合されている。よっ
て、この撥水防汚処理剤を自動車等の塗装面に塗布し、
拭き上げると、前記塗装面における微細な傷は、前記シ
リコーンオイル及びワックス類によって埋められるか
ら、前記塗装面は平滑な光沢面になると考えられる。し
たがって、この撥水防汚処理剤により、自動車等の塗装
面に極めて美麗な艶が付与されると考えられる。
Further, the water-repellent and antifouling agent of the present invention contains a silicone oil and a wax. Therefore, this water-repellent antifouling agent is applied to a painted surface of an automobile or the like,
When wiped up, fine scratches on the painted surface are filled with the silicone oil and waxes, so the painted surface is considered to be a smooth glossy surface. Therefore, it is considered that this water-repellent and stain-proofing agent imparts an extremely beautiful luster to a painted surface of an automobile or the like.

【0095】[0095]

【実施例】以下、実施例を用い、本発明をより具体的に
説明する。以下「%」は、重量%を意味する。
The present invention will be described more specifically below with reference to examples. Hereinafter, "%" means% by weight.

【0096】<1.撥水防汚処理剤の調製> (実施例1)カルナウバワックス(加藤洋行(株)製、
融点83℃)5重量%を、前記カルナウバワックスの融
点と同じ温度に加熱したナフサNo.5(エクソン化学
(株)製、沸点154〜197℃)53重量%に攪拌し
ながら溶解させた。前記ナフサNo.5にカルナウバワ
ックスを溶解させた後、前記溶液を攪拌しながら室温ま
で冷却した。前記カルナウバワックスの溶液を室温まで
冷却した後、この溶液に、シリコーンオイルとしてTS
F451(東芝シリコーン(株)製、ジメチルシリコー
ンオイル、粘度2cSt)2%、球状有機パウダーとし
てエポスターS−12(商品名)((株)日本触媒製、
球状メラミンホルムアルデヒド縮合物、平均粒径1.2
μm)10%、及びポリテトラフルオロエチレンとして
KRYTOX DF(商品名)(デュポン社製、分子量
3,300、固形分量が15重量%になるようにHCF
C−141b中に分散)30重量%を添加し、常温で攪
拌して撥水防汚処理剤を調製した。得られた撥水防汚処
理剤は、均一な分散液であった。
<1. Preparation of water-repellent and antifouling agent> (Example 1) Carnauba wax (manufactured by Kato Yoko Co., Ltd.)
5% by weight of Naphtha No. 1 was heated to the same temperature as the melting point of the carnauba wax. 5 (manufactured by Exxon Chemical Co., Ltd., boiling point: 154 to 197 ° C.). The naphtha no. After dissolving carnauba wax in 5, the solution was cooled to room temperature while stirring. After the carnauba wax solution was cooled to room temperature, TS solution was added to the solution as silicone oil.
F451 (manufactured by Toshiba Silicone Co., Ltd., dimethyl silicone oil, viscosity 2 cSt) 2%, as a spherical organic powder, Eposter S-12 (trade name) (manufactured by Nippon Shokubai Co., Ltd.
Spherical melamine formaldehyde condensate, average particle size 1.2
μm) 10%, and KRYTOX DF (trade name) as a polytetrafluoroethylene (manufactured by DuPont, HCF such that the molecular weight is 3,300 and the solid content is 15% by weight).
30% by weight (dispersed in C-141b) and stirred at room temperature to prepare a water-repellent and stain-proofing agent. The resulting water-repellent and antifouling agent was a uniform dispersion.

【0097】(実施例2)前記カルナウバワックス5重
量%を、前記カルナウバワックスの融点と同じ温度に加
熱した33重量%のナフサNo.5に攪拌しながら溶解
させた。前記ナフサNo.5にカルナウバワックスを溶
解させた後、前記溶液を攪拌しながら室温まで冷却し
た。前記カルナウバワックスの溶液を室温まで冷却した
後、この溶液に、前記TSF451を2%、エポスター
S−12を10%、及び前記KRYTOX DFの50
重量%を添加し、常温で攪拌して撥水防汚処理剤を調製
した。得られた撥水防汚処理剤は、均一な分散液であっ
た。
(Example 2) Naphtha No. 33% by weight was prepared by heating 5% by weight of the carnauba wax to the same temperature as the melting point of the carnauba wax. 5 with stirring. The naphtha no. After dissolving carnauba wax in 5, the solution was cooled to room temperature while stirring. After cooling the carnauba wax solution to room temperature, the solution contained 2% TSF451, 10% Eposter S-12, and 50% KRYTOX DF.
% By weight and stirred at room temperature to prepare a water-repellent and antifouling agent. The resulting water-repellent and antifouling agent was a uniform dispersion.

【0098】(実施例3)カルナウバワックス5重量%
を、前記カルナウバワックスの融点と同じ温度に加熱し
た54重量%のナフサNo.5に、攪拌しながら溶解さ
せた。前記ナフサNo.5にカルナウバワックスを溶解
させた後、前記溶液を攪拌しながら室温まで冷却した。
前記カルナウバワックスの溶液を室温まで冷却した後、
この溶液に、前記TSF451(粘度1,000cS
t)を1%、前記エポスターS−12を10%、前記K
RYTOX DFを30重量%添加し、常温で攪拌して
撥水防汚処理剤を調製した。前記撥水防汚処理剤は均一
な分散液であった。
(Example 3) Carnauba wax 5% by weight
Was heated to the same temperature as the melting point of the carnauba wax. 5 with stirring. The naphtha no. After dissolving carnauba wax in 5, the solution was cooled to room temperature while stirring.
After cooling the carnauba wax solution to room temperature,
The TSF451 (viscosity of 1,000 cS) was added to this solution.
t) is 1%, the eposter S-12 is 10%, the K
RYTOX DF was added at 30% by weight, and stirred at room temperature to prepare a water-repellent and antifouling agent. The water-repellent and antifouling agent was a uniform dispersion.

【0099】(実施例4)カルナウバワックス5重量%
を、前記カルナウバワックスの融点と同じ温度に加熱し
た42重量%のナフサNo.5に、攪拌しながら溶解さ
せた。前記ナフサNo.5にカルナウバワックスを溶解
させた後、前記溶液を攪拌しながら室温まで冷却した。
前記カルナウバワックスの溶液を室温まで冷却した後、
この溶液に、樹脂類としてTSF451(粘度2cS
t)を2%、球状有機パウダーとしてMR−7G(商品
名)(綜研化学(株)製、球状架橋アクリル樹脂、平均
粒径3〜10μm)10%、及びポリテトラフルオロエ
チレンとしてAG Lub−G(商品名)(旭硝子
(株)製、分子量4,000、固形分11%をHCFC
ー225に分散)41重量%を添加し、常温で攪拌して
撥水防汚処理剤を調製した。得られた撥水防汚処理剤
は、均一な分散液であった。
(Example 4) Carnauba wax 5% by weight
Was heated to the same temperature as the melting point of the carnauba wax. 5 with stirring. The naphtha no. After dissolving carnauba wax in 5, the solution was cooled to room temperature while stirring.
After cooling the carnauba wax solution to room temperature,
TSF451 (viscosity 2 cS)
t) of 2%, 10% of MR-7G (trade name) (manufactured by Soken Chemical Co., Ltd., spherical crosslinked acrylic resin, average particle size of 3 to 10 μm) as spherical organic powder, and AG Lub-G as polytetrafluoroethylene. (Trade name) (manufactured by Asahi Glass Co., Ltd., molecular weight 4,000, solid content 11%, HCFC
(Dispersed in -225) and stirred at room temperature to prepare a water-repellent and antifouling agent. The resulting water-repellent and antifouling agent was a uniform dispersion.

【0100】(実施例5)前記カルナウバワックス5重
量%を、前記カルナウバワックスの融点と同じ温度に加
熱した42重量%のナフサNo.5に攪拌しながら溶解
させた。前記ナフサNo.5にカルナウバワックスを溶
解させた後、前記溶液を攪拌しながら室温まで冷却し
た。前記カルナウバワックスの溶液を室温まで冷却した
後、この溶液に、前記TSF451を2%、トレフィル
E−605(東レ・ダウコーニング・シリコーン(株)
製、球状シリコンゴム、平均粒径2μm)を10%、及
び前記AG Lub−Gの41重量%を添加し、均一な
分散液状の撥水防汚処理剤を調製した。
Example 5 5% by weight of the carnauba wax was heated to the same temperature as the melting point of the carnauba wax. 5 with stirring. The naphtha no. After dissolving carnauba wax in 5, the solution was cooled to room temperature while stirring. After cooling the carnauba wax solution to room temperature, 2% of the TSF451 was added to this solution, and Trefil E-605 (Dow Corning Toray Silicone Co., Ltd.) was used.
And spherical silicon rubber (average particle size: 2 μm), 10%, and 41% by weight of the AG Lub-G were added to prepare a uniform dispersion liquid water-repellent and antifouling agent.

【0101】(実施例6)前記カルナウバワックス5重
量%を、前記カルナウバワックスの融点と同じ温度に加
熱した38重量%のナフサNo.5に攪拌しながら溶解
させた。前記ナフサNo.5にカルナウバワックスを溶
解させた後、前記溶液を攪拌しながら室温まで冷却し
た。前記カルナウバワックスの溶液を室温まで冷却した
後、この溶液に、前記TSF451を2%、KMP−5
90(信越シリコン(株)製、球状シリコン樹脂、平均
粒径2μm)を10%、及びルブロンLDE−3(ダイ
キン工業(株)製、ポリテトラフルオロエチレン、分子
量10,000、固形分10%をケロシン及びHCFC
−141bに分散)の45重量%を添加し、均一な分散
液状の撥水防汚処理剤を調製した。
Example 6 38% by weight of naphtha No. 1 obtained by heating 5% by weight of the carnauba wax to the same temperature as the melting point of the carnauba wax. 5 with stirring. The naphtha no. After dissolving carnauba wax in 5, the solution was cooled to room temperature while stirring. After cooling the carnauba wax solution to room temperature, 2% of the TSF451 was added to the solution, and KMP-5 was added.
90 (Shin-Etsu Silicon Co., Ltd., spherical silicone resin, average particle size 2 μm) 10%, and Lubron LDE-3 (Daikin Industries, Ltd., polytetrafluoroethylene, molecular weight 10,000, solid content 10%) Kerosene and HCFC
(Dispersed in -141b) to prepare a uniformly dispersed liquid water-repellent and stain-proofing agent.

【0102】(実施例7)前記カルナウバワックス5重
量%を、前記カルナウバワックスの融点と同じ温度に加
熱した38重量%のナフサNo.5に攪拌しながら溶解
させた。前記ナフサNo.5にカルナウバワックスを溶
解させた後、前記溶液を攪拌しながら室温まで冷却し
た。前記カルナウバワックスの溶液を室温まで冷却した
後、この溶液に、前記TSF451を2%、フロービー
ズLE−1080(住友精化(株)製、球状低密度ポリ
エチレン、平均粒径6±1μm)を10%、及び前記ル
ブロンLDE−3の45重量%を添加し、均一な分散液
状の撥水防汚処理剤を調製した。
(Example 7) 38% by weight of naphtha No. 1 obtained by heating 5% by weight of the carnauba wax to the same temperature as the melting point of the carnauba wax. 5 with stirring. The naphtha no. After dissolving carnauba wax in 5, the solution was cooled to room temperature while stirring. After cooling the carnauba wax solution to room temperature, 2% of the TSF451 and flow beads LE-1080 (manufactured by Sumitomo Seika Co., Ltd., spherical low-density polyethylene, average particle size 6 ± 1 μm) were added to the solution. 10% and 45% by weight of the above-mentioned Lubron LDE-3 were added to prepare a uniform dispersion liquid repellent / waterproofing agent.

【0103】(比較例1)前記カルナウバワックス5重
量%を、前記カルナウバワックスの融点と同じ温度に加
熱した53重量%のナフサNo.5に攪拌しながら溶解
させた。前記ナフサNo.5にカルナウバワックスを溶
解させた後、前記溶液を攪拌しながら室温まで冷却し
た。前記カルナウバワックスの溶液を室温まで冷却した
後、この溶液に、前記TSF451(粘度2cSt)を
2重量%、本発明における球状有機パウダーに代えて、
不定形のポリエチレン微粉末であるPW2010(東洋
ペトロライト(株)製、平均粒径5.9μm)を10重
量%、及び前記KRYTOXDFの30重量%を添加
し、常温で攪拌して撥水防汚処理剤を調製した。得られ
た撥水防汚処理剤は、均一な分散液であった。
(Comparative Example 1) 5% by weight of the carnauba wax was heated to the same temperature as the melting point of the carnauba wax. 5 with stirring. The naphtha no. After dissolving carnauba wax in 5, the solution was cooled to room temperature while stirring. After cooling the carnauba wax solution to room temperature, 2 wt% of the TSF451 (viscosity 2 cSt) was added to this solution instead of the spherical organic powder in the present invention,
10% by weight of amorphous polyethylene fine powder PW2010 (manufactured by Toyo Petrolite Co., Ltd., average particle size of 5.9 μm) and 30% by weight of the KRYTOXDF were added, and the mixture was stirred at room temperature to perform water-repellent and stain-proof treatment. An agent was prepared. The resulting water-repellent and antifouling agent was a uniform dispersion.

【0104】(比較例2)前記カルナウバワックス5重
量%を、前記カルナウバワックスの融点と同じ温度に加
熱した63重量%のナフサNo.5に攪拌しながら溶解
させた。前記ナフサNo.5にカルナウバワックスを溶
解させた後、前記溶液を攪拌しながら室温まで冷却し
た。前記カルナウバワックスの溶液を室温まで冷却した
後、この溶液に、前記TSF451(粘度2cSt)を
2重量%、及び前記KRYTOX DFの30重量%を
添加し、常温で攪拌して撥水防汚処理剤を調製した。得
られた撥水防汚処理剤は、均一な分散液であった。
(Comparative Example 2) Naphtha No. of 63% by weight was prepared by heating 5% by weight of the carnauba wax to the same temperature as the melting point of the carnauba wax. 5 with stirring. The naphtha no. After dissolving carnauba wax in 5, the solution was cooled to room temperature while stirring. After cooling the carnauba wax solution to room temperature, 2% by weight of the TSF451 (viscosity: 2 cSt) and 30% by weight of the KRYTOX DF were added to the solution, and the mixture was stirred at room temperature and stirred at room temperature. Was prepared. The resulting water-repellent and antifouling agent was a uniform dispersion.

【0105】(比較例3)前記カルナウバワックス5重
量%を、前記カルナウバワックスの融点と同じ温度に加
熱した57重量%のナフサNo.5に攪拌しながら溶解
させた。前記ナフサNo.5にカルナウバワックスを溶
解させた後、前記溶液を攪拌しながら室温まで冷却し
た。前記カルナウバワックスの溶液を室温まで冷却した
後、この溶液に、前記TSF451(粘度1,000c
St)を8重量%、及び前記KRYTOX DFの30
重量%を添加し、常温で攪拌して撥水防汚処理剤を調製
した。得られた撥水防汚処理剤は、均一な分散液であっ
た。
(Comparative Example 3) 5% by weight of the carnauba wax was heated to the same temperature as the melting point of the carnauba wax. 5 with stirring. The naphtha no. After dissolving carnauba wax in 5, the solution was cooled to room temperature while stirring. After cooling the carnauba wax solution to room temperature, the solution was added to the TSF451 (viscosity of 1,000 c).
8% by weight of St) and 30 of the KRYTOX DF
% By weight and stirred at room temperature to prepare a water-repellent and antifouling agent. The resulting water-repellent and antifouling agent was a uniform dispersion.

【0106】(比較例4)前記カルナウバワックス5重
量%を、前記カルナウバワックスの融点と同じ温度に加
熱した57重量%のナフサNo.5に攪拌しながら溶解
させた。前記ナフサNo.5にカルナウバワックスを溶
解させた後、前記溶液を攪拌しながら室温まで冷却し
た。前記カルナウバワックスの溶液を室温まで冷却した
後、この溶液に、前記TSF451(粘度2cSt)を
8重量%、及び前記KRYTOX DFの30重量%を
添加し、常温で攪拌して撥水防汚処理剤を調製した。得
られた撥水防汚処理剤は、均一な分散液であった。
(Comparative Example 4) 5% by weight of the carnauba wax was heated to the same temperature as the melting point of the carnauba wax. 5 with stirring. The naphtha no. After dissolving carnauba wax in 5, the solution was cooled to room temperature while stirring. After cooling the carnauba wax solution to room temperature, 8 wt% of the TSF451 (viscosity: 2 cSt) and 30 wt% of the KRYTOX DF are added to the solution, and the mixture is stirred at room temperature and stirred at room temperature. Was prepared. The resulting water-repellent and antifouling agent was a uniform dispersion.

【0107】<2.撥水防汚処理剤の評価>前記実施例
1〜7及び比較例1〜4の撥水防汚処理剤について、以
下の方法にしたがって撥水性能及び防汚性能を評価し
た。
<2. Evaluation of water-repellent and antifouling agent> The water-repellent and antifouling agent of Examples 1 to 7 and Comparative Examples 1 to 4 were evaluated for water-repellent performance and antifouling performance according to the following methods.

【0108】2−1 試験方法 平成6年式の日産ADバン、平成3年式の日産サニー、
及び平成7年式の三菱FTOのそれぞれのボンネット部
分と屋根部とを洗車した。洗車後、トラップ粘土を用い
て前記3台の自動車の塗装面に残っていた鉄粉等を除去
し、クリーナーワックスとバフとを使用して前記塗装面
に残っていた水垢を除去した。更に、前記ボンネット部
と屋根部とをナフサNo.5で脱脂し、塗装面上に残存
していたワックス分を除去した。
2-1 Test Method Nissan AD van of 1994, Nissan Sunny of 1991,
And the car hood and roof of the 1995 Mitsubishi FTO. After washing the car, iron powder and the like remaining on the painted surfaces of the three automobiles were removed using trap clay, and scales remaining on the painted surfaces were removed using a cleaner wax and a buff. Further, the bonnet part and the roof part are designated by Naphtha No. 5 and the wax remaining on the painted surface was removed.

【0109】前記3台の自動車のボンネット部と屋根部
とをそれぞれマスキングテープで9の区画に分割し、前
記9区画の内1区画を空試験用として残し、残り8区画
に、前記実施例1〜7及び比較例1〜4の撥水防汚処理
剤を通常のワックスがけの要領で塗布した。尚、異なる
区画には異なる撥水防汚処理剤を塗布した。前記8区画
に撥水防汚処理剤を塗布した後、各区画について拭き上
げを行い、後述する基準に従って前記各撥水防汚処理剤
の作業性について評価した。
The hood portion and the roof portion of each of the three automobiles were divided into nine sections by using a masking tape, and one of the nine sections was left for a blank test, and the remaining eight sections were used in the first embodiment. To 7 and Comparative Examples 1 to 4 were applied in the same manner as ordinary waxing. Note that different water-repellent and stain-proofing agents were applied to different sections. After applying the water-repellent and stain-proofing agent to the eight sections, each section was wiped off, and the workability of each of the water-repellent and stain-proofing agents was evaluated according to the criteria described later.

【0110】前記3台の自動車のボンネット及び屋根に
おける9区画をそれぞれ拭き上げた後、前記3台の自動
車のマスキングテープを剥がし、前記3台の自動車を屋
外に駐車した。
After wiping the nine compartments of the hood and roof of each of the three automobiles, the masking tapes of the three automobiles were peeled off, and the three automobiles were parked outdoors.

【0111】前記撥水防汚処理剤を塗布後、1ヶ月後及
び3ヶ月後に、前記3台の自動車を洗車し、前記3台の
自動車のそれぞれにおける9区画について、洗車後の水
の引き具合即ち水引性、洗車後の撥水性、及び洗車後の
汚染率を評価した。
One and three months after the application of the water-repellent and antifouling agent, the three automobiles were washed, and nine compartments in each of the three automobiles were subjected to water washing after washing. The water pulling property, the water repellency after car washing, and the contamination rate after car washing were evaluated.

【0112】2−2 評価方法・評価基準 (a) 作業性 選択済みの清浄なタオルを三つ折りにして、前記9区画
のそれぞれについてワックスを拭き取った。前記区画の
それぞれについて、三つ折りにしたタオルの1面を用い
た。作業性、即ち拭き取り性については、以下の基準に
従って評価した。
2-2 Evaluation Method and Evaluation Criteria (a) Workability The selected clean towel was folded in three, and the wax was wiped off in each of the nine sections. For each of the compartments, one side of a trifolded towel was used. Workability, that is, wiping property was evaluated according to the following criteria.

【0113】○:1〜2回タオルで拭くと乾燥した撥水
防汚処理剤が拭き取れる。 △:3〜5回タオルで拭くと乾燥したワックスが拭き取
れる。 ×:5回以上タオルで拭かないと乾燥したワックスが拭
き取れない。
:: The dried water-repellent and antifouling agent can be wiped off by wiping with a towel once or twice. Δ: Dry wax can be wiped off by wiping with a towel three to five times. X: The dried wax cannot be removed unless it is wiped with a towel five or more times.

【0114】(b) 洗車後の水引性 1ヶ月後及び3ヶ月後に、前記3台の自動車のボンネッ
ト及び屋根を、スポンジと水道水とにより洗車後、前記
ボンネットと屋根とにおける撥水防汚処理剤塗布面に水
道水をかけ、前記表面における水道水の引き具合を目視
によって観察することにより水引性を評価した。水引性
の評価は以下の基準に基づいて行った。
(B) Water drainage after car washing One month and three months later, the bonnet and roof of the three automobiles were washed with sponge and tap water, and then the water-repellent and stain-proofing agent on the bonnet and roof was removed. Tap water was applied to the application surface, and the degree of water withdrawal on the surface was visually observed to evaluate the water drawability. The evaluation of water drawability was performed based on the following criteria.

【0115】◎:水が塗装面に乗らない。 ○:水が1〜2秒程で塗装面から引く。 △:水が5秒程で塗装面から引く。 ×:水が塗装面から引かない。A: Water does not get on the painted surface. :: Water is drawn from the painted surface in about 1 to 2 seconds. Δ: Water is pulled from the painted surface in about 5 seconds. ×: Water does not drain from the painted surface.

【0116】(c) 洗車後の撥水性 1ヶ月後及び3ヶ月後に洗車を行った後、塗装面に残っ
ている水を清浄なタオルで拭き取り、トリガーポンプに
よって前記塗装面に水を噴射し、水滴の状態を観察して
洗車後の撥水性を評価した。撥水性の評価は以下の基準
によって行った。
(C) Water repellency after car washing After one month and three months after car washing, water remaining on the painted surface was wiped off with a clean towel, and water was sprayed on the painted surface by a trigger pump. The state of water droplets was observed to evaluate the water repellency after car washing. The evaluation of water repellency was performed according to the following criteria.

【0117】◎:水滴が球状であり、前記塗装面上を転
がりだす。 ○:水滴が球状である。 △:水滴が楕円状である。 ×:水滴がアメーバ状である。
A: Water droplets are spherical and roll on the painted surface. :: Water droplets are spherical. Δ: Water droplet is elliptical. ×: Water droplets are amoebic.

【0118】(d) 洗車後の汚染率 1ヶ月後及び3ヶ月後に洗車を行った後、前記3台の自
動車におけるそれぞれの区画につき、カラーアナライザ
TC−1800(東京電色(株))により、白色度を測
定した。尚、水垢除去後撥水防汚処理剤を塗布する前に
おける前記3台の車の白色度は、以下の通りであった。
(D) Pollution rate after car washing After washing one month and three months later, each section of the three cars was analyzed by a color analyzer TC-1800 (Tokyo Denshoku Co., Ltd.). The whiteness was measured. The whiteness of the three cars before the application of the water-repellent and antifouling agent after descaling was as follows.

【0119】日産ADバン:47.4 日産サニー :57.8 三菱FTO :60.4Nissan AD Van: 47.4 Nissan Sunny: 57.8 Mitsubishi FTO: 60.4

【0120】汚染率は、以下の式The contamination rate is calculated by the following equation.

【数1】[100−(洗車後の白色度/水垢除去直後の
白色度)]×100 によって評価した。尚、前記汚染率は前記3台の自動車
について測定した汚染率の平均である。
[Equation 1] [100− (whiteness after car washing / whiteness immediately after descaling)] × 100. The pollution rate is an average of the pollution rates measured for the three vehicles.

【0121】尚、以下の基準に従って汚染度を評価し
た。
The degree of contamination was evaluated according to the following criteria.

【0122】 ◎: 0≦汚染率< 2.0 …肉眼では汚れが判らない。 ○: 2.0≦汚染率<10.0 …少し汚れている。 △:10.0≦汚染率<15.0 …汚れている。 ×:15.0≦汚染率 …酷く汚れている。◎: 0 ≦ contamination rate <2.0 ... No dirt is visible to the naked eye. :: 2.0 ≦ contamination rate <10.0 ... Slightly dirty. Δ: 10.0 ≦ contamination rate <15.0: Stained. ×: 15.0 ≦ contamination rate: Very dirty.

【0123】<3.結果>前記実施例1〜7 及び比較
例1〜4の撥水防汚処理剤について、作業性、並びに洗
車後の水引性、撥水性、及び汚染率の評価結果を以下の
表1及び表2に示す。
<3. Results> For the water-repellent and antifouling agents of Examples 1 to 7 and Comparative Examples 1 to 4, the evaluation results of workability, water-repellency, water-repellency, and contamination rate after car washing are shown in Tables 1 and 2 below. Show.

【0124】[0124]

【表1】 [Table 1]

【0125】[0125]

【表2】 [Table 2]

【0126】前記表1及び表2に示されているように、
実施例1〜7の撥水防汚処理剤を塗装した塗装面におい
ては、何れも乾燥後タオルで1〜2回擦るだけで撥水防
汚処理剤を拭き取ることができた。したがって、実施例
1〜7の撥水防汚処理剤は、何れも良好な作業性を有す
ることが判った。
As shown in Tables 1 and 2,
On the painted surfaces coated with the water-repellent and stain-proofing agents of Examples 1 to 7, the water-repellent and stain-proofing agents could be wiped off only by rubbing with a towel once or twice after drying. Therefore, it was found that each of the water-repellent and stain-proofing agents of Examples 1 to 7 had good workability.

【0127】前記実施例1〜7 の撥水防汚処理剤の
内、球状有機パウダーとしてメラミンホルムアルデヒド
樹脂を用いた実施例1〜3の撥水防汚処理剤において
は、塗布後1ヶ月を経過した塗装面は、洗車後において
も水道水が1〜2秒で引いていく程の高い水引性を示
し、更に、洗車後の塗装面上に噴射した水道水が球状に
なって転がり落ちる程の極めて高い撥水性を示した。
Among the water-repellent and antifouling agents of Examples 1 to 7, the water-repellent and antifouling agents of Examples 1 to 3 using melamine formaldehyde resin as the spherical organic powder were coated one month after application. The surface shows a high water-drawing property so that the tap water can be drawn in 1-2 seconds even after the car wash, and is extremely high enough that the tap water sprayed on the painted surface after the car wash rolls down in a spherical shape It showed water repellency.

【0128】前記塗装面は、塗布後3ヶ月を経過した後
においても、塗布後1ヶ月後の塗布面と同様の高い水引
性を示し、又、水道水が球状になる程の高い撥水性を示
した。
The coated surface shows the same high water-repellency even after 3 months from the application as the coated surface one month after the application, and has a high water repellency such that the tap water becomes spherical. Indicated.

【0129】球状有機パウダーとして、実施例1〜3に
おけるメラミンホルムアルデヒド樹脂の球状パウダーに
代えて、架橋アクリル樹脂、シリコーン樹脂、又はポリ
エチレン樹脂の球状パウダーを用いた撥水防汚処理剤に
関する実施例4〜7においては、塗装面は、更に高い水
引性及び撥水性を示した。即ち、実施例4〜7の撥水処
理剤を用いた場合には、塗布後1ヶ月及び3ヶ月の何れ
においても、洗車後の塗装面は、水が直ちに引く程の高
い水引性、及び噴射した水が球状になり直ちに転がりだ
す程の高い撥水性を示した。
Examples 4 to 5 relating to a water-repellent and antifouling treatment agent using a spherical powder of a crosslinked acrylic resin, a silicone resin or a polyethylene resin instead of the spherical powder of melamine formaldehyde resin in Examples 1 to 3 as the spherical organic powder. In No. 7, the painted surface showed even higher water-drawing and water-repellent properties. That is, when the water-repellent treatment agents of Examples 4 to 7 were used, the painted surface after car washing had a high water-drawing property such that water immediately drained and sprayed, both at one month and three months after application. The water thus obtained became spherical and showed high water repellency enough to start rolling immediately.

【0130】塗装面の汚れ難さ即ち防汚性については、
実施例1〜7の何れの撥水防汚処理剤を塗布した塗装面
においても、塗布後1ヶ月経過時及び3ヶ月経過時にお
ける洗車後の汚染率は2%以下であり、洗車後の塗装面
において肉眼で汚れを認めることができなかった。この
ことから、前記実施例1〜7の撥水防汚処理剤を塗布し
た塗装面は、長期間に亘って高い防汚性を有することが
判った。
Regarding the difficulty of soiling the painted surface, that is, the antifouling property,
Regarding the painted surface to which any of the water-repellent and antifouling treatment agents of Examples 1 to 7 was applied, the contamination rate after 1 month and 3 months after application was 2% or less, and the painted surface after car washing. No dirt could be recognized with the naked eye. From this, it was found that the coated surfaces to which the water repellent and antifouling agents of Examples 1 to 7 were applied had high antifouling properties over a long period of time.

【0131】これに対して、球状有機パウダーに代えて
不定形のポリエチレン粉末であるPWパウダーを配合し
た比較例1の撥水防汚処理剤においては、タオルで3〜
5回擦らなければ撥水防汚処理剤を完全に拭き取ること
ができなかった。又、球状有機パウダーもPWパウダー
も配合しなかった比較例2の撥水防汚処理剤において
は、5回以上タオルで塗装面を擦っても塗装面上の撥水
防汚処理剤を拭き取ることができなかった。
On the other hand, in the water-repellent and stain-proofing agent of Comparative Example 1 in which PW powder which is an amorphous polyethylene powder was blended in place of the spherical organic powder, 3 to 10
The water-repellent and antifouling agent could not be completely wiped off unless rubbed five times. Further, in the water-repellent and stain-proofing agent of Comparative Example 2 in which neither the spherical organic powder nor the PW powder was blended, the water-repellent and stain-proofing agent on the painted surface could be wiped off even if the painted surface was rubbed with a towel five times or more. Did not.

【0132】又、比較例1〜4の撥水防汚処理剤を塗布
した塗装面は、塗布後1ヶ月もすると、水引性及び撥水
性が著しく劣化した。又、前記PWパウダーなどの不定
形の粒子を配合した比較例1の撥水防汚処理剤、及び粘
度が1000cStである高粘度シリコーン油を8重量
%と大量に配合した比較例3の撥水防汚処理剤において
は、塗布後3ヶ月もすると、塗装面が著しく汚れ、水道
水とスポンジとによる洗車程度では汚れを落とすことが
困難であることが判った。
The coated surfaces coated with the water-repellent and stain-proofing agents of Comparative Examples 1 to 4 were significantly deteriorated in water drainage and water repellency even one month after the application. Further, the water-repellent and soil-repellent treatment agent of Comparative Example 1 in which irregular particles such as the PW powder were blended, and the water-repellent and soil-repellent agent of Comparative Example 3 in which a high-viscosity silicone oil having a viscosity of 1000 cSt was blended in a large amount of 8% by weight. In the case of the treating agent, it was found that the painted surface was significantly stained three months after the application, and it was difficult to remove the stain only with a car wash using tap water and sponge.

【0133】[0133]

【発明の効果】本発明によれば、作業性が高く、更に長
期間に亘って優れた撥水性及び防汚性を有する被膜を形
成する撥水防汚処理剤が提供される。
According to the present invention, there is provided a water-repellent and antifouling agent which forms a film having high workability and excellent water repellency and antifouling properties over a long period of time.

【0134】本発明によれば、更に、自動車、事務用家
具家具、及び航空機等の金属製品の塗装面、並びに木製
家具等の表面に容易に塗布でき、拭き上げ時の作業性が
良く、加えて長期間持続する撥水性、水引性、及び防汚
性を付与する撥水防汚処理剤が提供される。
According to the present invention, it can be easily applied to the painted surface of metal products such as automobiles, office furniture, and aircraft, and the surface of wooden furniture and the like. The present invention provides a water-repellent and antifouling agent which imparts water repellency, water-repellency, and antifouling properties that last for a long period of time.

【0135】本発明によれば、更に、塗布時の伸びに優
れ、自動車、事務用家具家具、及び航空機等の金属製品
の塗装面、並びに木製家具等の表面に、極めて美麗で深
みのある艶を付与する撥水防汚処理剤が提供される。
According to the present invention, furthermore, it is excellent in elongation at the time of application, and has a very beautiful and deep gloss on the painted surface of metal products such as automobiles, office furniture and aircraft, and the surface of wooden furniture. Is provided.

フロントページの続き Fターム(参考) 4H020 BA02 BA06 BA12 BA32 4J038 BA212 CB021 CD121 CG141 DA161 DL031 DL032 KA06 MA02 MA07 MA10 MA14 NA05 NA07 Continued on the front page F term (reference) 4H020 BA02 BA06 BA12 BA32 4J038 BA212 CB021 CD121 CG141 DA161 DL031 DL032 KA06 MA02 MA07 MA10 MA14 NA05 NA07

Claims (6)

【特許請求の範囲】[Claims] 【請求項1】 分子量が1,000〜100,000
であるポリテトラフルオロエチレンと、メラミン系合成
樹脂、アクリル系合成樹脂、シリコーン樹脂、及びポリ
エチレン樹脂から選択された1以上の合成樹脂を含有す
る球状有機パウダーと、シリコーンオイルと、炭化水素
系溶剤と、ワックス類とを含有し、前記ポリテトラフル
オロエチレンと前記球状有機パウダーとが前記石油系溶
剤中に分散してなることを特徴とする撥水防汚処理剤。
(1) a molecular weight of 1,000 to 100,000;
And polytetrafluoroethylene, a melamine-based synthetic resin, an acrylic-based synthetic resin, a silicone resin, and a spherical organic powder containing one or more synthetic resins selected from polyethylene resins, a silicone oil, and a hydrocarbon-based solvent. And a wax, and wherein the polytetrafluoroethylene and the spherical organic powder are dispersed in the petroleum-based solvent.
【請求項2】 前記請求項1におけるポリテトラフル
オロエチレンの含有量が0.5〜50重量%である請求
項1に記載の撥水防汚処理剤。
2. The water-repellent and antifouling agent according to claim 1, wherein the content of polytetrafluoroethylene in the above item 1 is 0.5 to 50% by weight.
【請求項3】 前記請求項1における球状有機パウダ
ーの含有量が0.5〜20重量%である請求項1又は2
に記載の撥水防汚処理剤。
3. The method according to claim 1, wherein the content of the spherical organic powder is 0.5 to 20% by weight.
3. The water-repellent and antifouling agent according to 1.
【請求項4】 前記請求項1における炭化水素系溶剤
の含有量が30〜97重量%である請求項1〜3の何れ
か1項に記載の撥水防汚処理剤。
4. The water-repellent and stain-proofing agent according to claim 1, wherein the content of the hydrocarbon solvent in the above item 1 is 30 to 97% by weight.
【請求項5】 前記請求項1におけるシリコーンオイ
ルの含有量が0.1〜5重量%である請求項1〜4の何
れか1項に記載の撥水防汚処理剤。
5. The water-repellent and antifouling agent according to claim 1, wherein the content of the silicone oil in the above item 1 is 0.1 to 5% by weight.
【請求項6】 前記請求項1におけるワックス類の含
有量が1〜10重量%である請求項1〜5の何れか1項
に記載の撥水防汚処理剤。
6. The water-repellent and antifouling agent according to claim 1, wherein the content of the wax in the above item 1 is 1 to 10% by weight.
JP01577299A 1999-01-25 1999-01-25 Water repellent antifouling agent Expired - Fee Related JP4860018B2 (en)