DE3829328C1

DE3829328C1 - Coating composition for preventing asbestos fibre pollution from asbestos/binder building material

Info

Publication number: DE3829328C1
Application number: DE19883829328
Authority: DE
Inventors: Wolfgang Dipl.-Chem. Dr. 1000 Berlin De Ortlepp
Original assignee: Individual
Current assignee: Individual
Priority date: 1988-08-30
Filing date: 1988-08-30
Publication date: 1989-12-07

Abstract

The invention relates to the use of a composition prepared using alginic acid and/or water-soluble salts thereof for the additional treatment of asbestos-containing building materials such as spray asbestos, asbestos cement or the like, to avoid or reduce asbestos fibre pollution in the surrounding air. Further additives used are fibre materials, such as cellulose fibres, to increase the mechanical stability of the coating and flame retardants, such as mica, perlite, vermiculite and also water-soluble polymer dispersions.

Description

Die Erfindung betrifft ein Beschichtungsmittel für die nach trägliche Behandlung asbesthaltiger Baustoffe, wie Spritzas best, Asbestzement, Asbestsilicaten usw. mit einer wäßrigen Lösung von Alginsäure und/oder deren wasserlöslichen Salzen, insbesondere Alkalisalzen, und Zusätzen, wie wasserlöslichen Polymerdispersionen, Fasern und Brandschutzmitteln.The invention relates to a coating composition for the inert treatment of building materials containing asbestos, such as sprays best, asbestos cement, asbestos silicates etc. with an aqueous Solution of alginic acid and / or its water-soluble salts, especially alkali salts, and additives such as water-soluble Polymer dispersions, fibers and fire retardants.

Erfindungsgemäße Aufgabe ist die chemische Bindung insbeson dere der in anorganischen Bindemitteln und in Asbesttestfasern vorhandenen Calciumionen, um somit die Verfestigung der Bin demittelzusammensetzung und die feste Einbindung von Asbest fasern zu erreichen.The object of the invention is chemical bonding in particular that of inorganic binders and asbestos test fibers existing calcium ions, in order to solidify the bin composition of agents and the permanent integration of asbestos to reach fibers.

Hierdurch sollen die Asbestfaserimmissionen aus asbesthaltigen Baustoffen in der Umgebungsluft verhindert oder zumindest auf einen zulässigen Immissionswert herabgesetzt werden.As a result, the asbestos fiber emissions from asbestos-containing Prevents or at least prevents building materials in the ambient air a permissible immission value can be reduced.

Die Lösung der gestellten Aufgabe folgt den Kennzeichen und Merkmalen der Patentansprüche, deren Grundlage unter Berück sichtigung des zum Anmeldezeitpunkt bekannten Standes der Technik nachfolgend erläutert wird.The solution to the task follows the marks and Features of the claims, the basis of which inspection of the status of the at the time of registration Technology is explained below.

Faserverstärkte hydraulische Bindemittelwerkstoffe, besonders mit Asbestfasern bewehrte Zement- und Silicatbaustoffe, sind seit langem bekannt und haben in den vergangenen Jahren im Bauwesen vielfältige und weitverbreitete Anwendung gefunden.Fiber reinforced hydraulic binder materials, especially cement and silicate building materials reinforced with asbestos fibers has been known for a long time and has Construction found diverse and widespread application.

Nachteil der mit Asbestfasern hergestellten Baustoffe ist, daß gesundheitsschädliche Faserstoffe dann in die Umgebungs luft freigesetzt werden, wenn unbeschichtete Baustoffe durch Witterungseinflüsse oder andere Einwirkungen erodiert und die asbesthaltigen Baustoffoberflächen auf diese Weise frei gelegt werden. Schädliche Asbestimmissionen treten vor allem auch da auf, wo - so zum Beispiel bei der nachträglichen Beschichtung an sich nicht ausreichend feuerwiderstands fähiger Werkstoffe - Spritzasbest, eine nur wenig Bindemittel enthaltende Asbestfasermischung für die Verkleidung von Stahl trägern, Stahlblechlüftungsschächten und haustechnischen Anlagen, wie Be- und Entlüftungsleitungen, sowie von In stallationsschächten eingesetzt worden sind.The disadvantage of building materials made with asbestos fibers is that harmful fibers then into the environment air released when uncoated building materials through Weather influences or other influences are eroded and the asbestos-containing building material surfaces free in this way be placed. Above all, harmful asbestos emissions occur also where - for example in the case of the subsequent Coating itself insufficient fire resistance capable materials - sprayed asbestos, a little binder Containing asbestos fiber mixture for the cladding of steel beams, sheet steel ventilation shafts and building services Plants, such as ventilation lines, as well as from In installation shafts have been used.

In den vielen Fällen ist die Sanierung solcher Bauschadens fälle durch Entfernen der eingebauten asbesthaltigen Bau stoffe oder sogar der Abriß ganzer Bauwerke oder umfangreicher Bauwerksteile notwendig.In many cases, the renovation of such building damage cases by removing the built-in asbestos-containing construction fabrics or even the demolition of entire buildings or extensive ones Building parts necessary.

Eine nachträgliche Beschichtung oder Imprägnierung asbest haltiger Baustoffe ist wohl bekannt und grundsätzlich im Zuge der Sanierung von Schadensfällen auch möglich, jedoch sind die hierfür nach bisherigem Stand der Technik bekannten Beschichtungsmittel, besonders für die Behandlung innen liegender Be- und Entlüftungsleitungen, Wand- und Decken konstruktionen sowie Installationsschächte nicht geeignet.A subsequent coating or impregnation of asbestos containing building materials is well known and basically in In the course of the repair of damage cases also possible, however are those known for this in the prior art Coating agent, especially for indoor treatment horizontal ventilation and ventilation pipes, walls and ceilings constructions and installation shafts not suitable.

Denn die für eine nachträgliche, dauerhafte Oberflächenbehand lung am besten geeigneten lösemittelhaltigen Anstrichmittel scheiden aus, weil von ihnen bei Verwendung im Gebäudeinnern langzeitig Schadstoffe emittiert werden und zudem durch das Lösemittel gummi- oder kunststoffhaltige Bauwerksteile, so auch Kabelisolierungen in Installationsschächten u. ä., angegriffen bzw. zerstört oder sogar zündfähige Luft-Löse mittel-Konzentrationen erreicht werden können. In explosions gefährdeten Baubereichen bzw. Bauwerksteilen verbietet sich die Verwendung solcher Anstrichmittel ohnehin. Because for a subsequent, permanent surface treatment most suitable solvent-based paint are excluded because of them when used inside the building long-term pollutants are emitted and also by the solvent rubber or plastic building parts, so also cable insulation in installation shafts u. Ä., attacked or destroyed or even ignitable air release medium concentrations can be achieved. In explosions Building areas or parts of buildings at risk are prohibited the use of such paints anyway.

Auch lösemittelfreie Wasserlacke sind, abgesehen von ihrer geringeren Haltbarkeit, weniger geeignet, da diese Weichmacher und andere organische Zusätze enthalten, die ähnliche nachtei lige Auswirkungen wie lösemittelhaltige Beschichtungssysteme haben können.Solvent-free water-based paints are also, apart from their less durability, less suitable as this plasticizer and other organic additives containing similar disadvantages effects such as solvent-based coating systems can have.

Silicatlösungen, wie Wasserglas, scheiden zumeist wegen ihrer hohen Alkalität und möglicher Korrosion, insbesondere metallischer Bauwerksteile oder auch der im Anwendungsbe reich liegenden Glasflächen, bei ihrer Verwendung aus.Silicate solutions, such as water glass, mostly differ due to their high alkalinity and possible corrosion, in particular metallic building parts or also in the application area rich lying glass surfaces, when using them.

Alginsäure oder deren Derivate sind als Zusatzmittel zur Verbesserung der Verarbeitungseigenschaften von Zement- bzw. Betonmischungen bereits vorgeschlagen worden (siehe TIZ-Zbl. 1960, H. 10, Seite 246 und DE-OS 32 34 663). Auch ist aus AT-PS 3 59 417 und CH-PS 6 45 605 bekannt, polymere Verbindun gen, wie Polysaccharide, Polyacrylamid, hydraulischen Bindemittelmischungen zuzusetzen.Alginic acid or its derivatives are used as additives for Improving the processing properties of cement or Concrete mixtures have already been proposed (see TIZ Zbl. 1960, H. 10, page 246 and DE-OS 32 34 663). Is also out AT-PS 3 59 417 and CH-PS 6 45 605 known polymeric compounds gene such as polysaccharides, polyacrylamide, hydraulic Add binder mixtures.

Es hat sich nun im Zuge von Untersuchungen überraschend ge zeigt, daß das erfindungsgemäß vorgeschlagene Mittel als Zu satzmittel für die nachträgliche Behandlung asbesthaltiger Baustoffe zur Vermeidung von Asbestfaserimmissionen besonders gut geeignet ist.It has now surprisingly turned out in the course of investigations shows that the agent proposed according to the invention as Zu Substitute for the subsequent treatment of asbestos-containing Building materials to avoid asbestos fiber emissions especially is well suited.

Die Verwendung von Alginsäure- oder Alginatlösungen als Beschichtungsmittel für asbesthaltige Baustoffe zur Bindung gesundheitsschädlicher Asbestfasern ist bisher noch nicht vorgeschlagen worden.The use of alginic acid or alginate solutions as Coating agent for asbestos-containing building materials for binding Asbestos fibers are not yet harmful to health been proposed.

Die erfindungsgemäße Zusammensetzung zeichnet sich gegen über bekannten Beschichtungsmitteln auch dadurch aus, daß sie am Verwendungsort besonderen Anforderungen, wie zum Bei spiel hinsichtlich des Brandschutzes der damit zu behandelnden Bauteile, mit entsprechenden Zusatzmitteln, wie Glimmer, Per lit oder dergleichen, gut angepaßt werden kann.The composition according to the invention stands out over known coating agents also characterized in that they have special requirements at the place of use, such as game regarding the fire protection of those to be treated Components with appropriate additives, such as mica, per lit or the like, can be adapted well.

Durch den Zusatz von Faserstoffen, wie Cellulosefasern, wird die mechanische Stabilität der Beschichtung und de ren Haftfestigkeit auf dem Untergrund verbessert.By adding fibrous materials such as cellulose fibers, the mechanical stability of the coating and de Ren adhesive strength on the surface improved.

Ein weiterer Vorteil ist, daß Alginsäure und deren Salze gesundheitlich unbedenklich sind und deshalb in sensiblen Bauwerks- bzw. Sanierungsbereichen, wie Krankenhäusern, Lebensmittelbetrieben usw., gut verwendet werden können.Another advantage is that alginic acid and its salts are harmless to health and therefore sensitive Building or renovation areas, such as hospitals, Food businesses, etc., can be used well.

Aus der Vielzahl möglicher Zusammensetzungen und Anwendungen der erfindungsgemäßen Zusammensetzung wird nachstehend ein Beispiel gegeben:From the multitude of possible compositions and applications the composition of the invention is shown below Given an example:

example

1-25 Gewichtsteile Natriumalginat, 0 bis 0,5 Gewichtsteile Cellulosefasern, wie Baumwollfasern, 0 bis 0,8 Gewichtsteile Portlandzement werden in einem Mischbehälter unter Verwendung eines hochtourigen Flügelmischers gemischt und nach zwei bis 5 Minuten unmittelbar auf die damit zu behandelnden Bauwerksteile - ggf. unter Verwendung einer hochviskose Mischungen verspritzenden Torkretvorrichtung - gebracht.1-25 parts by weight of sodium alginate, 0 to 0.5 parts by weight Cellulose fibers such as cotton fibers, 0 to 0.8 parts by weight Portland cement is used in a mixing tank of a high-speed wing mixer and mixed after two up to 5 minutes immediately on the patients to be treated with it Building parts - if necessary using a highly viscous Mixture splashing gate chime device - brought.

Claims

1. Coating agent for asbestos-containing building materials, characterized in that it contains a solution of alginic acid and / or its water-soluble salts, the organic and / or inorganic polymer dispersions, fibrous materials and fire retardants are added.

2. Coating composition according to claim 1, characterized ge indicates that it contains water-soluble polymer dispersions, cellulosic fibers as well as pearlite, mica and / or Contains vermiculite as an additive.