DE102007041378A1 - Handling reversible printing forme for the wet offset method involves subjecting surface of printing forme to solution of inorganic acid and/or short-chain organic acid and/or solution or dispersion of one or more metal soaps - Google Patents
Handling reversible printing forme for the wet offset method involves subjecting surface of printing forme to solution of inorganic acid and/or short-chain organic acid and/or solution or dispersion of one or more metal soaps Download PDFInfo
- Publication number
- DE102007041378A1 DE102007041378A1 DE102007041378A DE102007041378A DE102007041378A1 DE 102007041378 A1 DE102007041378 A1 DE 102007041378A1 DE 102007041378 A DE102007041378 A DE 102007041378A DE 102007041378 A DE102007041378 A DE 102007041378A DE 102007041378 A1 DE102007041378 A1 DE 102007041378A1
- Authority
- DE
- Germany
- Prior art keywords
- solution
- water
- acid
- group
- printing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
Description
Die Erfindung betrifft ein Verfahren zur Behandlung einer reversiblen Druckform für das Nass-Offsetverfahren nach dem Oberbegriff des 1. Anspruchs.The The invention relates to a method for treating a reversible Printing form for the wet offset method according to the preamble of the 1st claim.
Im
Die
in
Dieser
hydrophobe Zustand ist bei diesen Schichten nicht allein durch die
Wirkung der eingesetzten organischen Verbindungen erreichbar. Um bei
den schaltbaren Schichten nach
Ein weiterer Nachteil dieser Schichten ist die für einige Einsatzgebiete nicht ausreichende maximale Hydrophobie, die durch einen relativ niedrigen maximalen Wasserrandwinkei von ca. 50° gekennzeichnet ist. Das kann insbesondere beim Einsatz von Oberflächen mit erhöhter Rauheit zu einer nicht ausreichenden Wasserabweisung führen, da bei rauen Schichten aufgrund der Oberflächenstruktur eine erhöhte Neigung zur Wasserbenetzung besteht, die durch die Hydrophobie der Oberfläche kompensiert werden muss.One Another disadvantage of these layers is that for some applications insufficient maximum hydrophobicity by a relative low maximum Wasserrandwinkei of about 50 ° is. This can be especially true when using surfaces with increased roughness to an insufficient water repellency lead, because with rough layers due to the surface structure there is an increased tendency for water wetting by the hydrophobicity of the surface must be compensated.
Die oben aufgeführten bekannten Verfahren zum Behandeln von reversiblen Druckformen sind auf die Erzeugung eines stabilen hydrophoben Zustandes der gesamten Druckform gerichtet. Auf die vollständig hydrophobierte Druckform werden die Bildinformationen eingeschrieben, indem entsprechende Bereiche mittels lokaler Energieeinwirkung in den hydrophilen Zustand überführt werden. Im Anschluss an die Bebilderung erfolgt der Druckvorgang. Die hydrophilen Bereiche werden im Offset-Prozess mit Feuchtmittel benetzt, um eine Farbabweisung in diesen Bereichen zu erreichen.The listed above known methods for treating Reversible printing plates are designed to produce a stable hydrophobic Condition of the entire printing form directed. On the complete hydrophobized printing form, the image information is written in, by corresponding areas by means of local energy in the hydrophilic state. In connection the printing is done on the artwork. The hydrophilic areas are wetted with fountain solution in the offset process for a color rejection to achieve in these areas.
Es hat sich gezeigt, dass auf die oben beschriebene Art und Weise unter Nutzung von reversiblen Druckformen auf Basis von mit TiO2 und anderen oxidischen Materialien beschichteten Oberflächen kein Druckprozess mit befriedigender Qualität ausgeführt werden kann, da die auf diesen Druckformen hergestellten hydrophilen Bereiche nicht ausreichend farbabweisend sind.It has been found that in the manner described above using reversible printing plates based on surfaces coated with TiO 2 and other oxidic materials, no printing process can be carried out with satisfactory quality, since the hydrophilic areas produced on these printing plates are not sufficiently ink-repellent are.
Aus
der
Nachteilig an dieser vorgeschlagenen Lösung ist, dass die dadurch erlangte Verstärkung oder Stabilisierung der Hydrophilie auch hier nicht ausreichend ist, um die einem Druckbild mit sehr hohen Qualitätsansprüchen genügende Farbabweisung zu erzielen.adversely At this proposed solution is that by the obtained reinforcement or stabilization of the hydrophilicity even here is not enough to give a printed image with a lot high quality standards sufficient color rejection to achieve.
Aufgabe der vorliegenden Erfindung ist es deshalb, ein Verfahren zum Behandeln einer wiederbeschreibbaren Druckform zu entwickeln, bei der die Hydrophilie der im Ergebnis der Bebilderung erzeugten hydrophilierten Bereiche der Druckform in einem der Bebilderung folgenden Verfahrensschritt verstärkt und stabilisiert wird.task Therefore, the present invention is a method for treating to develop a rewritable printing form, in which the hydrophilicity the hydrophilized areas produced as a result of the imaging the printing plate in one of the imaging following process step strengthened and stabilized.
Erfindungsgemäß wird diese Aufgabe durch ein Verfahren mit den Merkmalen des 1. Anspruchs gelöst.According to the invention this object is achieved by a method having the features of the first claim.
Der Erfindungsgedanke besteht darin, dass die Farbabweisung der auf den reversiblen Druckformen bei der Bebilderung erzeugten hydrophilen Bereiche entscheidend verbessert werden kann, wenn diese vor dem Druckprozess einer Lösung einer geeigneten anorganischen Säure und/oder einer kurzkettigen organischen Säure ausgesetzt werden. Statt dieser Lösung oder auch zusätzlich zu dieser können diese Bereiche auch mit einer Lösung von einer oder mehreren Metallseifen in mindestens einem mit Wasser mischbaren Lösungsmittel in Kontakt gebracht werden.Of the Invention idea is that the color rejection on the reversible printing forms produced in the imaging hydrophilic Areas can be decisively improved if these are before the Printing process of a solution of a suitable inorganic Acid and / or a short-chain organic acid get abandoned. Instead of this solution or in addition These areas can also have a solution to this one or more metal soaps in at least one with water mixable solvents are brought into contact.
Bei dieser Säure kann es sich zum Beispiel um Ameisensäure, Essigsäure, Propionsäure, Acrylsäure oder Methacrylsäure handeln. Es sind aber auch einfache anorganische Säuren, wie z. B. Phosphorsäure, einsetzbar. Der Effekt kann noch verstärkt werden, wenn die Lösung eine geringe Menge eines hydrophilen Polymers, z. B. einer Polysäure oder eines Polyalkohols, enthält. Besonders vorteilhaft ist es, wenn das hydrophile Polymer eine Molmasse von über 10 000 g/Mol aufweist.at this acid may be, for example, formic acid, Acetic acid, propionic acid, acrylic acid or methacrylic acid. But they are also simple inorganic acids, such as. B. phosphoric acid, used. The effect can be amplified if the solution contains a small amount of a hydrophilic polymer, z. As a polyacid or a polyhydric alcohol contains. It is particularly advantageous if the hydrophilic polymer has a molecular weight of over 10,000 g / mole.
Bei herkömmlichen Offsetdruckverfahren besitzt die Oberfläche der Druckform eine Rauheit bzw. eine Porosität, die dazu geeignet ist, durch die Wirkung von Kapillarkräf ten Feuchtmittel zu binden. Das ist zum Beispiel bei anodisch oxidierten Aluminiumplatten der Fall. Eine solche Oberflächenbeschaffenheit kann ebenfalls im erfindungsgemäßen Verfahren genutzt werden. Es hat sich gezeigt, dass Druckformoberflächen mit einer mittleren Rautiefe im Bereich von 1 bis 6 μm besonders geeignet sind, um die Wirkung der erfindungsgemäßen Methode vorteilhaft zu unterstützen.at conventional offset printing process has the surface the printing form a roughness or porosity, the is suitable, by the action of Kapillarkräf th dampening solution to bind. This is for example with anodized aluminum plates the case. Such a surface finish can also be used in the process according to the invention. It has been shown that printing surface with a average surface roughness in the range of 1 to 6 microns particularly are suitable to the effect of the invention Favorable method to support.
Die Erfindung soll nachfolgend an Hand von Ausführungsbeispielen näher erläutert werden.The Invention will be described below with reference to exemplary embodiments be explained in more detail.
Hierzu wird ein anodisiertes Aluminiumblech als Druckformvorläufer mittels Plasmaspritzen mit TiO2 beschichtet. Anschließend wird mittels Laminar-Flow Coating ein TiO2-Sol aufgebracht, das nach einem bekannten Verfahren aus Titanisopropoxid durch Hydrolyse und partielle Kondensation hergestellt wurde. Anschließend erfolgt eine Temperung für 2 Stunden bei 550°C. Die getemperte Schicht ist dann hydrophil und hat einen Wasserrandwinkel von 0°.For this purpose, an anodized aluminum sheet is coated as a printing form precursor by means of plasma spraying with TiO 2 . Subsequently, a TiO 2 sol is applied by laminar flow coating, which was prepared by a known method of titanium isopropoxide by hydrolysis and partial condensation. This is followed by an annealing for 2 hours at 550 ° C. The tempered layer is then hydrophilic and has a water edge angle of 0 °.
Die so erhaltene Schicht wird mit einer Lösung von 1% Hexadecyltrimethoxysilan in Hexan benetzt und getrocknet. Nach dem Trocknen ist die Oberfläche der Druckformen hydrophob und weist einen Wasserrandwinkel von 130° auf. Die Oberfläche der Druckformen ist auf eine mittlere Rautiefe von mehr als 1 μm und weniger als 6 μm eingestellt.The The layer thus obtained is treated with a solution of 1% hexadecyltrimethoxysilane wetted in hexane and dried. After drying, the surface is the printing forms hydrophobic and has a water edge angle of 130 °. The surface of the printing plates is on an average surface roughness set more than 1 micron and less than 6 microns.
Die so hergestellte Druckform kann nun bebildert werden.The thus prepared printing form can now be imaged.
Um die entsprechenden Bildinformationen zu vermitteln, erfolgt eine lokale Bestrahlung der Schicht. Das geschieht durch UV-Laserimpulsen mit einer Intensität unterhalb der Ablationsschwelle. Die Laserbestrahlung erfolgt so, dass damit die Flächen abgerastert werden, auf der die Entstehung von hydropphilen Bereichen gewünscht ist. Nach der Laserbestrahlung liegt der Wasserrandwinkel auf den bestrahlten Flächen bei 0°.Around to convey the appropriate image information, there is a local irradiation of the layer. This is done by UV laser pulses with an intensity below the ablation threshold. The laser irradiation is done so that the surfaces are scanned, wished on the emergence of hydrophilic areas is. After the laser irradiation the water edge angle is on the irradiated areas at 0 °.
Anschließend wird die gesamte Oberfläche der Druckform mit einer anorganischen Säure und/oder einer kurzkettigen organischen Säure in Kontakt gebracht. Im Ausführungsbeispiel wird hier eine 0,5%ige wässrige Lösung von Polyacrylsäure mit einer Molmasse von 20 000 g/mol, die 0,1% Acrylsäure enthält, verwendet.Subsequently The entire surface of the printing plate is mixed with an inorganic one Acid and / or a short-chain organic acid brought into contact. In the embodiment here is a 0.5% aqueous solution of polyacrylic acid with a molecular weight of 20,000 g / mol containing 0.1% of acrylic acid, used.
Der Kontakt der Druckformoberfläche mit der Lösung von Polyacrylsäure und Acrylsäure kann hergestellt werden, indem die Druckformoberfläche mit der Lösung überspült wird. Weiterhin ist es möglich, die Druckform in diese Lösung zu tauchen oder die Druckformoberfläche mit der Lösung zu besprühen. Eine weitere Möglichkeit besteht darin, die Lösung mittels einer Walze auf die Oberfläche der Druckform aufzubringen.The contact of the printing form surface with the solution of polyacrylic acid and acrylic acid can be prepared by flushing the printing plate surface with the solution. Furthermore, it is possible to dip the printing plate in this solution or to spray the printing plate surface with the solution. Another possibility is to apply the solution by means of a roller to the surface of the printing plate.
Erfolgt die Bebilderung in der Druckmaschine, scheiden einige Verfahren aus. Vorteilhafterweise wird dann die Lösung aufgesprüht oder mit einer Walze aufgebracht.He follows the imaging in the printing press, divorce some procedures out. Advantageously, the solution is then sprayed on or applied with a roller.
Im Anschluss an die Behandlung der Druckformoberfläche mit der Lösung von Polyacrylsäure und Acrylsäure ist es vorteilhaft, die verbleibenden Reste der Lösung von der Druckformoberfläche zu beseitigen. Das kann durch Überspülen mit Wasser geschehen.in the Following the treatment of the printing surface with the solution of polyacrylic acid and acrylic acid it is beneficial to use the remaining remnants of the solution from the printing surface to eliminate. That can be done by overflowing to happen with water.
Statt Acrylsäure können auch andere kurzkettige Säuren, wie z. B. Ameisensäure, Essigsäure, Propionsäure oder Methacrylsäure als verdünnte Lösungen verwendet werden. Ebenso ist es möglich, eine anorganische Säure wie Phosphorsäure als verdünnte Lösung anzuwenden.Instead of Acrylic acid can also be other short chain acids, such as For example, formic acid, acetic acid, propionic acid or methacrylic acid as dilute solutions be used. It is also possible to use an inorganic one Acid such as phosphoric acid as diluted Apply solution.
Bei einer Ausführung der Erfindung kann in die zur Spülung der Druckform verwendete, eine anorganische Säure oder einer kurzkettigen organischen Säure enthaltende Lösung ein wasserlösliches oder in Wasser dispergierbares Polymer eingebracht werden. Dieses wird in einer Molmasse von größer 10 000 g/mol eingesetzt.at an embodiment of the invention can in the flushing the printing plate used, an inorganic acid or a short-chain organic acid-containing solution a water-soluble or water-dispersible polymer be introduced. This is in a molecular weight of greater than 10 000 g / mol used.
Es ist auch möglich, hier eine Polysäure, ein Salz einer Polysäure, ein Copolymer von mindestens zwei hydrophilen Verbindungen oder ein Copolymer von mindestens einer hydrophilen und mindestens einer hydrophoben Verbindung oder einen Polyalkohol einzusetzen.It is also possible, here a polyacid, a salt a polyacid, a copolymer of at least two hydrophilic ones Compounds or a copolymer of at least one hydrophilic and at least one hydrophobic compound or a polyalcohol use.
Das hier einsetzbare Polymer kann auch solche funktionelle Gruppen wie die Carbonylgruppe, die Thiocarbonylgruppe, die Carboxylgruppe, die Thiocarboxylgruppe, die Alkoxygruppe, die Hydroxygruppe, die Phosphatgruppe, die Phosphonogruppe, die Aminogruppe, die Amidogruppe, die Sulfatgruppe, oder die Sulfonylgruppe enthalten.The here applicable polymer can also be such functional groups as the carbonyl group, the thiocarbonyl group, the carboxyl group, the thiocarboxyl group, the alkoxy group, the hydroxy group, the Phosphate group, the phosphono group, the amino group, the amido group, the sulphate group, or the sulphonyl group.
Erfindungsgemäß einsetzbare Polymere sind zum Beispiel: Polyethylenoxid, Polyvinylpyridin, Polyvinylpyrrolidon, Polyacrylssäure, Polyethylenglykolacrylate, wie Alkoxypoiyethylenglykolmono(meth)acrylate, Vinylalkohol- und Vinyletherpolymere, Acrylonitril-Methylacrylat-Copolymer, Acrylonitril-Styrol-Copolymer, Polydecylacrylat, Polyacrylsäure-Maleinsäure-Copolymer, Poly(ethylen-co-vinylacetat), Polyethylenimin, Polyethylenpiperidin oder Polyethylenglykol.Usable according to the invention Polymers are, for example: polyethylene oxide, polyvinylpyridine, polyvinylpyrrolidone, Polyacrylic acid, polyethylene glycol acrylates, such as alkoxy polyethylene glycol mono (meth) acrylates, Vinyl alcohol and vinyl ether polymers, acrylonitrile-methyl acrylate copolymer, Acrylonitrile-styrene copolymer, polydecyl acrylate, polyacrylic acid-maleic acid copolymer, Poly (ethylene-co-vinyl acetate), polyethyleneimine, polyethylene piperidine or polyethylene glycol.
Anwendbare Polymere können auch aus folgenden Verbindungen aufgebaut sein: Acrylsäure, Methacrylsäure, Glycidylmethacrylat, Acrylamid, Dimethylacrylamid, Acrylonitril, Methacrylamid, Methacryloyloxyethylisocyanat, Maleinsäure, Maleinsäureanhydrid,, Acrylamidomethylpropansulfonsäure und deren Salze, Acrylsäurehydroxyethylester, Acrylsäureethylester, Vinylimidazol oder Hydroxypropylmethacrylat.applicable Polymers can also be made up of the following compounds be: acrylic acid, methacrylic acid, glycidyl methacrylate, Acrylamide, dimethylacrylamide, acrylonitrile, methacrylamide, methacryloyloxyethylisocyanate, Maleic acid, maleic anhydride, acrylamidomethylpropanesulfonic acid and salts thereof, hydroxyethyl acrylate, ethyl acrylate, Vinylimidazole or hydroxypropyl methacrylate.
In einer weiteren Ausführung der Erfindung erhält diese säurehaltige Lösung einen Zusatz einer Lösung oder Dispersion von einer oder mehreren Metallseifen in mindestens einem mit Wasser mischbaren Lösungsmittel. Bei den Metallseifen handelt es sich um mindestens eine der folgenden Verbindungen: Salze der Metalle Al, Ba, Ca, Cd, Co, Cr, Cu, Fe, Li, Mg, Mn, Ni, Pb, Sn, Sr, Zn mit Fett-, Harz- u. Naphthensäuren.In obtains a further embodiment of the invention this acidic solution is an addition of a solution or dispersion of one or more metal soaps in at least a water-miscible solvent. At the metal soaps it is at least one of the following compounds: salts of the metals Al, Ba, Ca, Cd, Co, Cr, Cu, Fe, Li, Mg, Mn, Ni, Pb, Sn, Sr, Zn with grease, resin u. Naphthenic acids.
Bei der Verarbeitung ist zu beachten, dass die Metallseifen zwischen 15 u. 200°C schmelzen und meist kolloides Verhalten und Grenzflächenaktivität zeigen. Ihre Löslichkeit in Wasser ist gering, dagegen lösen sie sich zum Teil gut in Fetten u. fetten Ölen. Unter Einwirkung von Wasser erfolgt meist zunächst eine Quellung zu einem Gel.at the processing is to be noted that the metal soaps between 15 u. 200 ° C melt and mostly colloidal behavior and Show interface activity. Your solubility in water is low, but they partly dissolve well in fats u. fat oils. Under the influence of water takes place usually first a swelling to a gel.
Bei dem mit Wasser mischbaren Lösungsmittel kann es sich zum Beispiel um ein- oder mehrwertige Alkohole handeln.at the water-miscible solvent may be Example to deal with monohydric or polyhydric alcohols.
Als Beispiele für den Einsatz mehrwertiger Alkohole werden hier Diole vorgeschlagen, wobei sich hier Ethylenglykol (1,2-Ethandiol), Propylenglykol (1,2-Propandiol), Butylenglykol (1,4-Butandiol) anbieten. Andere geeignete mehrwertige Alkohole sind dreiwertigen Alkohole, wie zum Beispiel das Glycerin (Propan-1,2,3-triol) oder Isomere von Propantriol, wie das Propan-1,1,2-triol.When Examples of the use of polyhydric alcohols will be here proposed diols, which here ethylene glycol (1,2-ethanediol), Propylene glycol (1,2-propanediol), butylene glycol (1,4-butanediol) offer. Other suitable polyhydric alcohols are trihydric alcohols, such as the glycerin (propane-1,2,3-triol) or isomers of propanetriol, such as the propane-1,1,2-triol.
Es können aber auch andere mit Wasser mischbare Lösungsmittel, wie zum Beispiel Tetrahydrofuran, eingesetzt werden.It but also other water-miscible solvents, such as tetrahydrofuran used.
Eine weitere Möglichkeit besteht darin, von Alkoholen abgeleitete Verbindungen als mit Wasser mischbare Lösungsmittel zur Anwendung zu bringen. Als derartige Verbindungen können Ester, Ether oder Polyalkohole eingesetzt werden.A Another possibility is derived from alcohols Compounds as water-miscible solvents for Application. As such compounds can Esters, ethers or polyalcohols are used.
Als weitere Lösungsmittel sind Glykole und/oder von Glykolen abgeleitete Verbindungen geeignet. Beispiele für Verbindungen, die sich von den Glykolen ableiten, sind Glykolether, Glykolester und Polyglykole.When other solvents are glycols and / or glycols derived compounds suitable. Examples of connections, which are derived from the glycols are glycol ethers, glycol esters and polyglycols.
In einer weiteren Ausführung der Erfindung wird auf die anorganischen Säure oder einer kurzkettigen organischen Säure verzichtet. Die angewandte Lösung enthält dann ausschließlich einer oder mehrerer der oben beschrieben Metallseifen.In Another embodiment of the invention is based on the inorganic Acid or a short-chain organic acid waived. The applied solution then contains excluding one or more of those described above Metal soaps.
Die Wirkung des Zusatzes einer Lösung von einer oder mehreren Metallseifen in mehrwertigen Alkohole und in von mehrwertigen Alkoholen abgeleiteten Verbindungen beruht wahrscheinlich in der Anlagerung der Metallseife an die hydrophoben Bereiche der Druckplatte, wodurch es zur Stabilisierung und Verstärkung der hydrophoben Eigenschaften der Druckformoberfläche in diesen Bereichen kommt.The Effect of adding a solution of one or more Metal soaps in polyhydric alcohols and in polyhydric alcohols derived compounds is likely due to attachment the metal soap to the hydrophobic areas of the printing plate, thereby it stabilizes and enhances hydrophobic properties the printing form surface comes in these areas.
In einer vorteilhaften Ausführung des erfindungsgemäßen Verfahrens besteht dieser Zusatz aus einer Lösung von 1 g Cu-Naphtenat in 10 g Dipropylenglykol, wobei 1 Teil dieses Zusatzes mit 10 Teilen einer 0,5%igen wässrigen Lösung von Polyacrylsäure mit einer Molmasse von 20000 g/mol, die 0,1% Acrylsäure enthält, vermischt wurde.In an advantageous embodiment of the invention Method, this addition consists of a solution of 1 g of copper naphthenate in 10 g of dipropylene glycol, with 1 part of this additive with 10 parts of a 0.5% aqueous solution of polyacrylic acid with a molecular weight of 20,000 g / mol, containing 0.1% of acrylic acid was mixed.
Die so vorbereiteten Druckformen werden auf einen geeigneten Träger, also zum Beispiel den Plattenzylinder einer Bogenoffset-Druckmaschine aufgespannt und im Druckprozess unter Verwendung von Wasser als Befeuchtungsmittel eingesetzt.The prepared printing forms are placed on a suitable support, So, for example, clamped the plate cylinder a sheetfed offset printing press and in the printing process using water as a humectant used.
Die Regenerierung der Druckformen erfolgt (nach der Reinigung der Druckform) mittels Bestrahlung der gesamten Oberfläche mit fokussierter IR-Strahlung, wodurch die Temperatur im obersten Bereich der wiederbeschreibbaren Schicht kurzzeitig ca. 500°C erreicht. Die so behandelte Oberfläche weist einen Wasserrandwinkel von 0° auf.The Regeneration of the printing plates takes place (after cleaning the printing form) by irradiating the entire surface with focused IR radiation, causing the temperature in the top of the rewritable Layer briefly reached about 500 ° C. The so treated Surface has a water edge angle of 0 °.
Nach erneuter Befeuchtung mit einer Lösung von 1% Hexadecyltrimethylsilan in Hexan und anschließender Trocknung kann die Druckform wieder bebildert, erfindungsgemäß mit der oben beschriebenen Lösung behandelt und wiederum im Druckprozess verwendet werden.To rewetting with a solution of 1% hexadecyltrimethylsilane in hexane and subsequent drying, the printing plate imaged again, according to the invention with the above treated solution and again in the printing process be used.
ZITATE ENTHALTEN IN DER BESCHREIBUNGQUOTES INCLUDE IN THE DESCRIPTION
Diese Liste der vom Anmelder aufgeführten Dokumente wurde automatisiert erzeugt und ist ausschließlich zur besseren Information des Lesers aufgenommen. Die Liste ist nicht Bestandteil der deutschen Patent- bzw. Gebrauchsmusteranmeldung. Das DPMA übernimmt keinerlei Haftung für etwaige Fehler oder Auslassungen.This list The documents listed by the applicant have been automated generated and is solely for better information recorded by the reader. The list is not part of the German Patent or utility model application. The DPMA takes over no liability for any errors or omissions.
Zitierte PatentliteraturCited patent literature
- - US 6564713 [0002] - US 6564713 [0002]
- - EP 1020304 A2 [0003, 0003, 0004] - EP 1020304 A2 [0003, 0003, 0004]
- - EP 1375136 A1 [0008] EP 1375136 A1 [0008]
Claims (19)