CN1685099A - Spun-bonded nonwoven fabric and sanitary supplies - Google Patents

Abstract

A spun-bonded nonwoven fabric constituted of a web of continuous filaments of thermoplastic synthetic fibers, the structure of which fabric is set by a pattern composed of areas which are produced by partially fusing the fibers by hot pressing and pierce through the fabric and concavely and convexly embossed patterns on the surfaces of the fabric which patterns are composed of high-density concave and convex areas of unbonded fibers respectively and the bulkiness of which fabric is 100 to 400 % in terms of the ratio of the thickness of the fabric inclusive of the convexly embossed pattern surface to the thickness of the low-density areas of the fabric. The application of a hydrophilic agent to the nonwoven fabric gives sanitary supplies such as disposable diaper.

Description

Spunbond class nonwoven fabric and hygienic material

Technical field

The present invention relates to spunbond class nonwoven fabric, be particularly related to the depression that nonwoven fabric construct forms by the discontinuous decorative pattern of part hot pressing welding with by the high-density region of non-binding fiber or fixing, the soft and bulk spunbond class nonwoven fabric of embossing decorative pattern of projection, disposable hygienic material and be used for the nonwoven fabric of the improvement of a hygienic material.

Background technology

Employed hygienic material such as diaper, physiological napkin is generally by the leak-stopping that is known as " standing gather " the floral motif formations such as (カ Off) that sees through urine, excremental top layer, absorber, has the backing layer of water proofing property and utilize water proofing property.Soft feeling and the productivity, price equal angles of the employed material of these hygienic materials during from thin, powerful, contact skin used nonwoven fabric mostly.

A kind of as hygienic material, the top layer of disposable diaper is owing to be directly to contact with skin, so when requiring it to have soft sense of touch, also require the moment permeability of urine etc. strong, return wet less and higher repeatedly saturating urine the durability liquid permeability can etc.

Use now the nonwoven fabric of the fiber that composite short fiber etc. is bulk with hot blast or part hot pressing welding.Though but this nonwoven fabric that connects with hot blast has bulkiness and resiliency, but the weight of the unit are of nonwoven fabric need be uprised in order to obtain sufficient resiliency, and its surface is made of composite fibre, and nonwoven fabric construct is fixed by the welding of hot blast, so nonwoven fabric is comparatively thick and stiff, sense of touch is very hard.

And, the point of staple fibre part hot pressing welding is glued the powerful less of formula nonwoven fabric, thinner thickness, the fibre end that can produce staple fibre stimulates the problem of skin.

On the other hand, the nonwoven fabric of spun-bond process manufacturing is with the hot pressing welding of long filament mesh portions ground, and carries out hydrophilicity-imparting treatment as required, so have higher productivity, brute force is also bigger, and sense of touch is soft.But because shape, the arrangement of fiber compared with staple fiber nonwoven fabric, it is the plane generally speaking, and the liquid permeability, to return performance such as moist abundant inadequately.As known the comprising of the method for the bulkiness of improving spun-bonded non-woven fabrics: be connected with the absorbency core, the superficial layer that lamination is made of the upper and lower forms the method (spy opens flat 6-304203 communique) of the perforate catheter of recess by this upper strata; Thereby the net that biconstitutent fibres such as core-sheath-type composite fibre or parallel composite fiber constitute is carried out heat embossing processing to be given and keeps concavo-convex method (spy opens flat 11-286863 communique); Thereby to the net that biconstitutent fibres such as core-sheath-type composite fibre or parallel composite fiber constitute carry out heat embossing processing give concavo-convex, with the method (spy opens flat 11-347062 communique) of membranaceousization of protuberance summit of concavo-convex figuration etc.But these methods are perforate or the fixing method of figuration, nonwoven fabric shortcoming flexibility.

The invention of putting down in writing in the related special public clear 63-17944 communique of the inventor's invention is a nonwoven fabric that a kind of long filament net by fineness 0.5d-5d constitutes, that have part joint portion and non-binding property deformation of unevenness.But this invention is the fiber of crooked non-binding property part, carries out embossing, and rubs fiber and make it technology bulk, softnessization, does not relate to for characteristics such as the necessary liquid permeabilities of hygienic material.

Standing gather on the other hand about hygienic material, particularly leak-stopping is with floral motif, backing layer etc., use the lamination nonwoven fabric as the nonwoven fabric with water proofing property, wherein lamination long filament net and meltblown fibers utilize the former brute force and the latter's fine spreadability, water proofing property two specific characters.

Therefore this lamination nonwoven fabric is compared with existing monofilament net, has spreadability preferably, can realize its function under the situation of the weight of lower unit are.Though have long fibre net, the form of the paper of meltblown fiber web becomes stronger, and bonding along with meltblown fiber web, has the harder sense of touch as paper, particularly along with the weight step-down of unit are, the tendency that becomes thin nonwoven fabric is arranged.

As the improvement method of bulkiness, known comprises: be connected with the absorbency core, the superficial layer that lamination is made of the upper and lower forms the method (spy opens flat 6-304203 communique) of the perforate catheter of recess by this upper strata; The nonwoven fabric that biconstitutent fibres such as core-sheath-type composite fibre or parallel composite fiber are constituted carries out heat embossing processing and gives, keeps concavo-convex method (spy opens flat 11-286863 communique); The nonwoven fabric that biconstitutent fibres such as core-sheath-type composite fibre or parallel composite fiber are constituted carry out heat embossing processing and give concavo-convex, with the method (spy opens flat 11-347062 communique) of membranaceousization of protuberance summit of concavo-convex figuration etc.But these methods are perforate or the fixing method of figuration, nonwoven fabric shortcoming flexibility.

The related patent application of the inventor's invention is announced in the communique (special public clear 63-17944 communique) and is disclosed that a kind of long filament net by fineness 0.5d-5d constitutes, as to have part joint portion and non-binding property deformation of unevenness nonwoven fabric.But do not put down in writing the content of using meltblown fiber web in the above-mentioned patent announcement communique, the cohesiveness that does not disclose meltblown fiber web shown in the present is improved effect.

Summary of the invention

The object of the present invention is to provide a kind of can solve above-mentioned problem, as can be used for making bulk, soft-touch, have high water-permeability, return wet less, the spunbond class nonwoven fabric of the improvement of the hygienic material of powerful good disposable diaper etc.

The present invention also aims to,, provide a kind of hygienic material of spunbond class nonwoven fabric of improvement by the spun-bond process that can make than high productivity.

The basic comprising of the nonwoven fabric among the present invention is: a kind of spunbond class nonwoven fabric, be that net with thermoplastic synthetic fiber's continuous filament yarn is the nonwoven fabric that main body constitutes, it is characterized in that, positive and negative and the incorporate part hot pressing welding zone of fiber decorative pattern of the structure of nonwoven fabric by connecting nonwoven fabric, and the depression decorative pattern that on two faces of nonwoven fabric structure, constitutes by the high-density region of non-binding fiber or protruding pattern and be fixed, be more than 100% by the thickness of the shared nonwoven fabric of the non-binding fiber density regions of nonwoven fabric structure and the bulk rate that the ratio of the thickness of the nonwoven fabric of the face of the protruding embossing decorative pattern that contains nonwoven fabric is represented.

One of preferred basic mode of spunbond class nonwoven fabric of the present invention is: adopt the nonwoven fabric structure to the additional layer of meltblown fibers of thermoplasticity synthetic fiber filament layer.

Promptly, can further improve as the desired bulkiness of hygienic material by following spunbond class nonwoven fabric, key propertys such as flexibility: a kind of spunbond class nonwoven fabric, form by composite web, this composite web is by one deck thermoplastic synthetic fiber continuous filament yarn net at least and one deck meltblown fiber web layer is long-pending at least forms, positive and negative and the incorporate part hot pressing welding zone of fiber decorative pattern of the structure of nonwoven fabric by connecting nonwoven fabric, and the depression embossing that on two faces of nonwoven fabric structure, constitutes by the high-density region of non-binding fiber or protruding pattern and be fixed, be more than 100% by the thickness of the shared nonwoven fabric of the non-binding fiber density regions of nonwoven fabric structure and the bulk rate that the ratio of the thickness of the nonwoven fabric of the face of the protruding embossing decorative pattern that contains nonwoven fabric is represented.

Essential structure such as Fig. 1 of spunbond class nonwoven fabric of the present invention (1) schematically illustrate.Shown in Fig. 1 (I), Fig. 1 (III), nonwoven fabric structure reaches (B) depression embossing or the protruding pattern that the high-density region by non-binding fiber constitutes by (A) part hot pressing welding zone of fiber decorative pattern (the following portion of hot weld portion that only is called sometimes) and is fixed.(A) shown in Fig. 1 and (B) decorative pattern are the decorative patterns that schematically illustrates, and actual decorative pattern can be changed (A) and shape (B) and spacing simultaneously.And, the continuous independently respectively or discontinuous positive and negative that is configured in the nonwoven fabric structure of each decorative pattern (A) and (B).And, nonwoven fabric structure and above-mentioned (A) and/or (B) be connected, and contain the density regions of (C) non-binding fiber.(A) part hot pressing welding zone of fiber decorative pattern here is applied in by heat embossing, (B) depression embossing or the protruding pattern that is made of the high-density region of non-binding fiber is the embossing decorative pattern that is applied under the temperature of low temperature or not welding fiber, be on nonwoven fabric (the 1st face) and below (the 2nd face) with the decorative pattern of opposite direction embossing (with reference to Fig. 1 (III), Fig. 2-Fig. 4).A concrete example of spunbond class nonwoven fabric of the present invention as shown in Figure 7.Can see the nonwoven fabric structure that has formed (A), (B) and embossing decorative pattern (C) among Fig. 7 (I).Fig. 8 (I) is the example of of the present invention spunbond class nonwoven fabric that contains the lamination of meltblown fiber web, and is the same with the example of Fig. 7, can see the nonwoven fabric structure that has formed (A), (B) and decorative pattern (C).Can be well understood to the concrete form of the fixture construction that contains above-mentioned (A), (B) and nonwoven fabric structure of the present invention (C) by above-mentioned Fig. 7 and Fig. 8.

In spunbond class nonwoven fabric of the present invention, bulk rate is represented (with reference to Fig. 1 (III)) with the thickness (a) of the shared nonwoven fabric of the density regions of the non-binding fiber of nonwoven fabric structure and the ratio of the thickness (b) of the nonwoven fabric of the face of the protruding embossing decorative pattern that contains nonwoven fabric, the value of promptly following formula calculating gained.

Bulk rate (%)=(b/a) * 100

The thickness of the density regions of the non-binding fiber here (a) is to carry out the preceding thickness of embossing processing under the low temperature, and therefore bulk rate also can be calculated according to the thickness difference before and after the concavo-convex processing.Bulk rate is very important for the flexibility of determining nonwoven fabric, this means that the concavo-convex processing under the low temperature has applied kneading action to the nonwoven fabric structure.

Further, spunbond class nonwoven fabric of the present invention mainly contains hydrophilic agent in the high-density region (B) of non-binding fiber, therefore can with the nonwoven fabric improvement for can satisfy simultaneously as the performance of hygienic material bulk, soft, permeable, return four characteristics such as wet.

Below the present invention is discussed in detail.

As the fiber that constitutes spunbond class nonwoven fabric of the present invention, TPO fibers such as polypropylene, polyethylene or its copolymer the water-retaining property lower one face of fiber self, return moist good, polyester fibers such as polyethylene terephthalate, polybutylene terephthalate (PBT), polytrimethylene terephthalate (PTT) or its copolymer are preferable aspect waist strength, dry feeling, polyamide-based fibers such as nylon 6,66,610,12 or its copolymer then can obtain to have aspect the nonwoven fabric of stable flexibility preferable.Also can be with these composite fibres, blended fiber as required and have other specific function fibers and mix.

Nonwoven fabric need reply when the surface by urine when soaking, the brute force of the body kinematics phase when perhaps using, and, preferably make net, and connecting and nonwoven fabric that the spun-bond process that forms is made with continuous long fiber (long filament) from productive angle.The nonwoven fabric that spun-bond process is made has practical intensity owing to fibre length is long, aeration is better, and different when making with wet method or dry method, need not finish processing etc., therefore fiber can utilize character such as the distinctive WATER REPELLENCY of fiber directly by sheetization (シ one トization).

Fibroreticulate connection in the nonwoven fabric structure, the sense of touch for the intensity that keeps nonwoven fabric and flexibility, fiber self preferably adopts part hot pressing burning-on method to connect.Hot pressing welding area occupation ratio in the part hot pressing welding is from keeping the angle of intensity, flexibility, preferred 5-40%, further preferred 5-25%.Part hot pressing welding is except utilizing ultrasonic bonding machine etc., also can utilize between the heat embossing roller that is heated to be below the fusing point that constitutes fiber and be undertaken by modes such as nets, so, integrated in the table of nonwoven fabric structure, for example pin mark shape, rectangular-shaped etc. the decorative pattern that drifts along are dispersed on whole of nonwoven fabric.Certainly this hot pressing weld portion is pressed sticking membranaceous part, the peculiar sense of touch of fiber that its peripheral fiber has use.

The nonwoven fabric that only utilizes this part hot pressing welding to make, according to fiber formation, embossing shape, configuration, its thickness changes, and thickness is not very big in the no crimped fibre of common circular cross-section fiber.Particularly in the common net with the spun-bond process manufacturing, the arrangement of the fiber when it forms is the plane, and is not bulk.

In addition, part hot pressing welding is meant, by heat with pressure and in the part that part is connected, under the temperature below the fusing point of formation fiber, partly exerts pressure and forms with embossing decorative pattern shape.With in the above welding of melting temperature and to be configured as the fiber of film different, be " film " part that connects when keeping fiber shape, in order to be called part hot pressing welding with partly distinguishing by the concavo-convex high density that is processed to form of non-binding property.

As mentioned above, spunbond class nonwoven fabric of the present invention is in showing by part hot pressing welding in the incorporate nonwoven fabric, form following nonwoven fabric structure: the recess that in a face, has the high-density region of the non-binding fiber different with the decorative pattern of hot pressing weld portion, the protuberance that in opposite face, has the high-density region of non-binding fiber, therefore the nonwoven fabric structure is integrated in the quilt table by the part hot pressing weld portion of scattering, other parts are by the projection or the depression embossing decorative pattern of the high-density region of non-binding fiber, and the different zone of these two fibre densities of the density regions of non-binding fiber constitutes, they are subjected to the breaking effect of low temperature embossing shaping processing respectively and form the structure that fiber self is easy to move, and have therefore formed to have flexible touch, and bulk nonwoven fabric structure.

The high-density region of non-binding fiber is meant the zone shown in the B of Fig. 1 to Fig. 3, it is the zone of fusion or connection not between the fiber, be by the compression of concavo-convex processing with the jog of knurling rolls, fiber is compressed the also high zone of fiber of density of densification, and for example the words of showing with corpus fibrosum integration counting rate meter are scopes of 15-35%.And in the present invention, the area occupation ratio of the high-density region of non-binding fiber is 5-50%, preferred 5-25%.Part hot pressing weld portion is calculated according to the shape of the embossing decorative pattern of hot pressing welding.The nonwoven fabric of test material is enlarged at microscopically, according to welding and be the profile of membranaceous part, measure its size, spacing, try to achieve its area, and calculate the area occupation ratio that accounts for the test material entire area.

The density regions of non-binding fiber is meant the zone shown in the C of Fig. 1, be equivalent to not carry out fiber welding or connection and be not subjected to the compressed portion of concavo-convex processing with knurling rolls, comparing fiber with the high-density region of non-binding fiber does not have densification, roughly has the zone of the preceding fiber collection density of concavo-convex processing.Therefore, the fiber of this density regions has bulkiness, has the free degree of motion, and has the sense of touch of the original softness of fiber.For example, the corpus fibrosum integration rate of the density regions of non-binding fiber is in the scope of 5-15%.The area of the high-density region of non-binding fiber is at extruding embossing decorative pattern and in the high-density region of the fiber that forms, choose and constitute the track that fiber is extruded disconnection or part distortion, try to achieve its area, and calculate area occupation ratio with respect to the test material entire area.The fiber shape of the high-density region of non-binding fiber only comprises that constituting fiber has the fiber of contraction or be out of shape few fiber.

The high-density region thinner thickness and the fiber of non-binding fiber are intensive, then be rich in hydrophilic agent with what hydrophilic agent was handled in high-density region, so the permeability of liquid are better, outer surface smoother, and the sense of touch of dry and comfortable softness is arranged.

The density regions of non-binding property and high-density region thicker, the set density of fiber is less, and is soft and bulk, and the permeability of liquid is good, also has barrier action for returning of liquid is wet, and having preferably, liquid returns moist (wet back).

The sectional view of above-mentioned effect with reference to Fig. 1-Fig. 3 described.Fig. 1-Fig. 3 describes with understandable schematic diagram the structural feature of nonwoven fabric of the present invention.

(A) part hot pressing weld portion is the zone of having an effect in order to keep the whole brute force of nonwoven fabric, has suitable area occupation ratio.

(B) non-binding property high-density region is the B zone, has from the outstanding shape in the surface of nonwoven fabric, therefore has the effect that makes nonwoven fabric integral body become bulk.And owing to be rich in hydrophilic agent in this B zone, have the hydrophily that significantly improves this part, and improve the effect of the permeability of the liquid that passes through this B zone.

(C) non-binding property density regions is the C zone, and its effect is that the free degree of fiber is uprised, and flexibility is good, and gives soft sense of touch.And the C zone has barrier action for liquid from returning of absorber by leavening effect, can improve return moist.

And, have with the border of B on be easy to crooked effect.So, as feature of the present invention, (A), (B) and (C) each zone have above-mentioned effect respectively, thereby have the effect of suitable hygienic material on the whole.

Nonwoven fabric among the present invention is with the use composite fibre shown in the existing technology, by being connected and harder, the rough nonwoven fabric that forms of welding such as hot blast processing is diverse.

Among the present invention, have the fibrage that part is out of shape (stretching, extension) by granting non-binding property and deformation of unevenness to fibrage, can being made into, so its shock-absorbing capacity is better, when applying load, is difficult for compressed characteristic so have with free degree.Therefore, even under the condition of load, also be bulk, and be porous, so in a single day liquid is easy to soak into (saturating liquid speed is fast), and sees through, absorbed liquid is difficult to return wet.

The deformation of unevenness that nonwoven fabric in the present invention applies is and the decorative pattern of the joint portion of part the combination partly depression or the bulging deformation of inconsistent arbitrary shape, the shape of recess or protuberance, size, the depth are relevant with the decorative pattern that combines, and are very important for the flexibility effect.

The shape of recess or protuberance for example is continuous connection or the discrete shape that is configured to straight line, curve, corner angle, circle, pear-skin texture pattern shape etc., and from the flexibility effect, effect was best when the depth of recess or protuberance was approximately the degree of depth of 0.2-5mm.And discrete protuberance adds size preferred 0.1-5mm, the perhaps preferred 0.5-5mm of the spacing of recess or protuberance of pressure surface.

Fig. 1 is the schematic diagram of the overall plan view structure of nonwoven fabric of the present invention.Fig. 2 and Fig. 3 are the exemplary plot that applies the embossing of angular to nonwoven fabric.Fig. 2 and Fig. 3 are two examples of the decorative pattern of non-binding concavo-convex processing, in the drawings, have omitted the decorative pattern and the distribution thereof of hot pressing weld portion.

For example, as shown in Figure 3, be scattered with the embossing decorative pattern of protuberance and in high-density region, form the recess of discontinuous distribution by extruding.And as shown in Figure 2, by the continuous embossing decorative pattern of crush lobes, be under the continuum of states at high-density region, non-press section becomes the state of fibrage projection.The distortion spacing that links decorative pattern is dependent on its decorative pattern, but preferred 1-5mm, the size of recess is preferred wide to be line or the some wire of 0.02-3mm.

Utilize leavening effect to increase thickness by high-density region is set, the bulkiness of nonwoven fabric structure is improved, along with the varied in thickness of load cloth is few.The inventor finds that the concentration of hydrophilic agent becomes big in the high-density region of non-binding fiber after nonwoven fabric applies hydrophilic agent.

If the nonwoven fabric apparent thickness greatly then its softness,, then can obtain the careful fiber thoughts and feelings of texture if the size of the spacing of deformation of unevenness and recess is not made thickness too big.

The bulk rate of the nonwoven fabric among the present invention is more than 100%, preferred 105-400%, further preferred 110-300%, preferred especially 120-200%.When bulk rate is higher, along with descending, load thickness also can diminish, and the resiliency of nonwoven fabric is improved.

Varied in thickness such as the Fig. 5, shown in Figure 6 of spunbond class nonwoven fabric among the present invention to load.We can say that the spunbond class nonwoven fabric among the present invention is all bigger, bulk to its thickness of various loads, better to the compression property of load.When therefore the spunbond class nonwoven fabric among the present invention for example uses as the top layer of disposable diaper, can not reduce by thickness, and in the use of diaper, soft, bulk characteristic lasting effect is also fine along with the process of service time.And, under the state of net the decline of thickness few, from the returning of absorber,, therefore can obtain good effect for liquid because bulk rate is higher.

Apply the method for the protruding embossing decorative pattern of the depression of spun-bonded non-woven fabrics or non-binding fiber, for example generally have depression, projection or ridge design on the surface, between the roller that both overlap just, between roller that has ridge design on the surface and pliability roller, push, perhaps carry out the processing between the plate, also has following method as specific process:, carry out the embossing of wrinkling shape having between the roller of close gap in certain proportion with cloth overfeeding forcibly.

Fig. 4 has respectively between two rollers of circular ridge design and coincidence just by the surface, thereby applies the example of deformation of unevenness.

It should be noted especially in the condition of embossing when handling temperature and to nonwoven fabric institute applied pressure.Temperature during processing is that normal temperature gets final product, and makes embossing be easy to carry out thereby also can heat as required to plastify, and perhaps under the purpose that improves morphological stability, improves temperature and handle in the scope of the combination that does not produce fiber, typing.For example, under the situation of polypropylene non-woven fabric, preferred 30-110 ℃ scope.The embossing processing pressure is different and different according to temperature, will be set at the pressure that can fully carry out embossing certainly.Owing to carry out embossing, the fibre section of compressed part can deform, and by this part deformation effect, can produce better flexibility, also is very effective so further apply HIGH PRESSURE TREATMENT in addition.The condition that temporary transient fixing and hot pressing welding between the fiber of compression unit certainly, must employing take place.For example under the situation of polyacrylic nonwoven fabric, the scope of preferred 20-150kg/cm.

In spunbond class nonwoven fabric of the present invention, the preferred high-density region recess of the non-binding fiber that embossing forms on a face of nonwoven fabric, high-density fiber formation protuberance by non-binding property on its reverse side.For example, when on a face, forming the high-density region of continuous recess,, be preferably formed the convex shape more outstanding than other zones for high-density region on another side becomes protuberance.It is very important that this point is applied to hydrophilic agent on the specific position when the apparent thickness with nonwoven fabric integral body is made as more than the thickness of net.

The hydrophilic treatment of spunbond class nonwoven fabric of the present invention is used the hydrophilic agent solution of common dilution, can adopt existing methods such as infusion method, spray-on process, coating process (roller coat, gravure coating, mould are coated with etc.).Nonwoven fabric uses drying devices such as hot blast, hot-rolling to carry out drying after applying hydrophilic agent.

In hydrophilicity-imparting treatment, in the part beyond the high-density region that is applied in earlier and its, it is different distributing the adhering to of finishing agent.When applying finishing agent, liquid partly reaches more coarse part in the low-density of fiber and looks that content is more, and along with the drying of nonwoven fabric, liquid moves to and is easy to dry part.Therefore, the high-density region of non-binding fiber is when the thinner thickness of nonwoven fabric, and adhering to of finishing agent is more, liquid be easy to by.And the liquid that sees through so leave absorbed layer, is difficult to return wet because density regions is not easy to be compressed and is bulk.So, hydrophilic agent becomes and mainly is rich in high-density region in non-binding fiber, spunbond class nonwoven fabric of the present invention can obtain distinctive liquid transmitance raising, return the effect that moist raising and liquid flow improve.

Before hydrophilicity-imparting treatment, preferably carry out corona treatment, plasma treatment etc., can improve the hydrophiling degree.Processing such as corona treatment can be to handle as the generality that is used to improve wet characteristic etc. of the pre-treatment of printing, for example between sparking electrode and treatment tube, provide RF power and make it discharge by high frequency generation oscillator etc., with nonwoven fabric by handling therebetween.The surface tension of treated side is according to the difference of the wettability of necessity and treatment conditions and difference, and preferably setting and making surface tension is the discharging condition of 37-40mN/m.In addition, when applying Corona discharge Treatment, because the wettability difference of nonwoven fabric self is regulated the applied amount of hydrophilic agent certainly in order to obtain necessary performance.When the surface tension of nonwoven fabric was the scope of 37-40mN/m, the compatibility between the surface fiber of hydrophilic agent and nonwoven fabric was improved significantly, and can apply hydrophilic agent under low concentration equably.In the present invention, applying preferably of hydrophilic agent carried out after the concavo-convex processing of non-binding zone of fiber, uses what problem that also do not have in concavo-convex first being processed.

When the present invention who handles through hydrophilic agent is used for spunbond class nonwoven fabric hygienic material, certainly according to difference as the characteristic levels of hygienic material purpose, and select performance or the using method applied, but also with the table of nonwoven fabric in sense of touch different relevant.Though the fiber high-density region in the embossed concave, convex decorative pattern is not connected to each other, but compare fixing with other, so when being used as the top layer of diaper, preferred mode is: absorber one side that is configured to the reverse side that does not directly contact with skin in the face of nonwoven fabric, when paying attention to hydrophily, high-density region is configured in the one side that contacts with skin on top layer.

Spunbond class nonwoven fabric among the present invention uses the laminate mode more than two layers in the structure of nonwoven fabric, above-mentioned laminate more than two layers by at least one layer filament net and at least one deck meltblown web lamination form.

In this case, the fiber that is used for nonwoven fabric can use above-mentioned fibrous material.Also can use these composite fibres, blended fiber as required and have the mixture of the fiber of other specific functions.Even also be effectively at the different material of interlayer between the long filament net, and the long filament net material different with meltblown fiber web is also passable.Polyester fiber, polyamide-based fiber etc. have and the material of the compatibility of the water angle from WATER REPELLENCY, need to handle by waterproofing agent, water repellents such as silicon class, fluorine class or wax classes as required or add, to improve.

Nonwoven fabric need have the brute force of the body kinematics in the time of can corresponding using etc., from productive angle, preferably,, it forms nonwoven fabric by being carried out continuous connection by at least one layer filament net and the long-pending laminate more than two layers that forms of one deck meltblown fiber web layer at least.This lamination structure can only be the lamination of long filament net and meltblown fiber web, but in order to remedy the more weak meltblown fiber web of surface strength, the material of meltblown fiber web layer that used between the long filament stratum reticulare lamination usually, and each layer is set at multilayer is favourable.And also can be the material that each net is connected the back lamination.

The long filament that constitutes spunbond class nonwoven fabric is 0.5-5dtex, has practical intensity owing to fibre length is long, aeration is good, and it is different during with wet method or dry method manufacturing, not carrying out fiber such as finish processing is direct sheetization (シ one トization), therefore can utilize character such as the distinctive WATER REPELLENCY of fiber.

The public clear 56-3351 communique of meltblown fiber web such as spy, USP3,978,185, USP3,825,380 etc. described, formed by the fine fibre of 1-6 μ m, has spreadability preferably, for example has in polypropylene material and better refuse water, waterproof effect.Because meltblown fiber web is fine fibre, crystalline orientation is lower, therefore than long filament Netease in connection.Even but connect when reverse side, when using separately its brute force also a little less than, become as the harder material of the sense of touch of paper.Therefore, by lamination meltblown web and long filament net, can remedy each shortcoming, the brute force on actual the use is bigger, and spreadability, WATER REPELLENCY, water proofing property are better.

The connection of net, fixing for the sense of touch of the intensity that keeps nonwoven fabric and flexibility, fiber self, preferably uses the part hot pressing welding of heat embossing roller to connect.Hot pressing welding area occupation ratio in the part hot pressing welding is from keeping the angle of intensity, flexibility, preferred 5-40%, further preferred 5-25%.Part hot pressing welding can be crossed between the heating knurling rolls by the ultrasonic method or with Netcom and be carried out, and so, becomes integratedly in the table, and the styles that drift along such as pin mark shape, ellipticity, diamond shaped, rectangle are dispersed on whole of nonwoven fabric.Certainly the hot pressing weld is crimped, and is membranaceous, but its peripheral fiber, particularly long filament net keep the distinctive sense of touch of fiber of use.

In the condition that connects the long filament stratum reticulare, meltblown fiber web layer is extremely very thin, and the characteristic when forming according to its fiber becomes sense of touch as paper by heating, and nonwoven fabric integral body becomes the material with the same hardness of paper.And, having carried out the difference of the nonwoven fabric of part hot pressing welding according to fiber formation, embossing shape, configuration, its thickness changes, and produces the distinctive connection effect of meltblown fiber web layer, and the thickness attenuation does not have bulk.As bulk improvement method, there are perforate and the fixing method of figuration described in existing technology, but it is not as the present invention, will be by at least one layer filament net and the long-pending laminate more than two layers that constitutes of one deck meltblown fiber web layer is integrated in showing by being dispersed in lip-deep discrete part hot pressing weld portion at least, and the nonwoven fabric that the obtains deformation of unevenness by non-binding property obtained bulkiness or flexibility, and do not improve the connection effect of meltblown fiber web layer yet.

The design of lamination meltblown fiber web main points of the present invention down are in the nonwoven fabric structure: for will by at least one layer filament net and at least one deck meltblown fiber web layer amass the laminate more than two layers that constitutes by be dispersed in lip-deep discrete part hot pressing weld portion show in incorporate nonwoven fabric, further apply the processing of non-binding deformation of unevenness by embossing processing etc., thereby integrated in the pars fibrosa ground of the hot pressing weld portion of the scattering knot combined statement, the fiber of the non-binding property jog of other parts has the flexible touch of fiber self.

In meltblown fiber web layer, also different even how much have the connection effect with the hot pressing weld portion, be the temporary transient state that connects, be diverse with composite fibre by harder, the rough material that the heat treatment welding that is used to be connected forms.And, make it to become the fibrage of part distortion (stretching, extension) by the deformation of unevenness power that applies non-binding property to fiber, thereby can obtain sufficient bulkiness with free degree.When applying load, different with original fibrage, have the characteristic that is not easy to compress.That is, occur being easy to crooked lines, have flexibility, bulkiness (thickness).

Fig. 6 is in embodiment 8 and the comparative example 8, with respect to the varied in thickness curve of the nonwoven fabric of loading.In the present invention, also being not easy to compressed characteristic even have the load of applying, is also can not produce the nonwoven fabric that bulkiness reduces for load.

The embossing decorative pattern in the high-density fiber zone that is made of non-binding fiber that the spunbond class nonwoven fabric among the present invention is applied is and the decorative pattern of the joint portion of part the combination partly depression or the bulging deformation of the non-binding property of inconsistent arbitrary shape, and shape, size, the depth of depression or projection and the association that combines decorative pattern are very important for the flexibility effect.For example, shape can be straight line, curve, corner angle, circle, pear-skin texture pattern shape, other connections or discrete shape, but from the angle of flexibility effect, preferably the degree of depth of depression or projection is 0.2-5mm, and concavo-convex dark more effect is good more.

The preferred 0.1-5mm of the size that adds pressure surface of discrete decorative pattern, and the preferred 0.5-5mm of the spacing of recess or protuberance.In the decorative pattern of Fig. 1 (I), Fig. 3, extruding is scattered with the embossing decorative pattern of protuberance and forms the recess of discontinuous distribution in high-density region.And, the extruding of the continuous embossing decorative pattern of the protruding pattern by Fig. 2, Fig. 4, the recess of high-density region becomes the state that the fibrage of non-press section increases under continuum of states.The preferred 1-5mm of distortion spacing that continuous embossing decorative pattern produces, line or the dotted line of the preferred 0.02-3mm of big or small width of recess.

Be provided with in the spunbond class nonwoven fabric of embossing ridge design at these, part hot pressing weld portion is passed through and the inconsistent decorative pattern of embossing ridge design part, is configured to the high-density region of non-binding fiber, the density regions of non-binding fiber (with reference to the C of Fig. 1-4).

The area occupation ratio of the concavo-convex press section of non-binding fiber high-density region is from obtaining the angle of good flexibility, fiber sense of touch, preferred 5-40%, further preferred 5-25%.If consider actual use, that yes is big more soft more for apparent thickness, but the size of distortion spacing, recess can obtain fine and close effect when not too big, preferred more than 100% in the bulk rate of the front and back that apply the distortion of non-binding property, further preferred more than 105%, preferred especially more than 130%.

The method that applies depression or protruding pattern generally has: for example surface that processes the spunbond class nonwoven fabric that applies with heat embossing in the portion of hot welding has depression, projection or concavo-convex style, between the chimeric just roller of both sides, between pliability rollers such as the roller that has depression, protruding style on the surface and paper bowl, rubber rollers, resin roll, push, perhaps between plate, handle.Also has following method as specific process:, carry out the embossing of wrinkling shape having between the roller of close gap in certain proportion with cloth overfeeding forcibly.

It should be noted especially in the condition of embossing when handling temperature and to cloth institute applied pressure.Particularly in the mode of the nonwoven fabric that contains layer of meltblown fibers of the present invention, compare, be easy to receive deformation effect with the nonwoven fabric that only has only the long filament net.Therefore, on flexibility, can suppress the connection effect of layer of meltblown fibers,, preferably set lowlyer, can suitably set according to fibrous material so processing temperature is compared separately with the long filament net.For example, when being material with the polypropylene, be preferably set to the temperature below 60 ℃, further preferred below 50 ℃, it also is effective carrying out positive cooling as required.

On the other hand, also can under the scope of the combination that fiber does not take place, typing, improve temperature and plastify and make embossing be easy to carry out, and keep the stability of form.Pressure during processing is different and different according to temperature, can be set at the pressure that fully is out of shape.In addition, by the fibre section generation distortion of the compressed part of additional deformation, in order to obtain flexibility preferably, it also is effective further carrying out HIGH PRESSURE TREATMENT.Certainly need give one's full attention to temporary transient fixing, the hot pressing welding of the fiber that compression unit can not take place.

As optimal way of the present invention, a preferred face is the high-density region of the protuberance that is extruded, and opposite face forms highdensity recess.That is, when for example on a face, forming continuous portion's (high-density region), become protuberance, preferably make it become the state more outstanding than other zones in order on another side, to make this high-density region.The apparent thickness that makes nonwoven fabric integral body is for having great importance more than the thickness of netting.Do not form by such high density～density regions, therefore the whole thickening of cloth or be easy to bending by bending force becomes soft material with connecting, has the thing of thin, plane and the diverse sense of touch of paper.In order to strengthen such treatment effect, can carry out multilayer and handle.

According to the necessity of nonwoven fabric of the present invention, also can apply various finishing agents such as antistatic agent, softener, hydrophilic agent, lubricant.

When spunbond class nonwoven fabric of the present invention is used for hygienic material, according to the characteristic levels as the purpose of hygienic material, performance that selection should apply or using method.Also need to consider the difference of the sense of touch in the table of nonwoven fabric.That is,, compare with other and fix, therefore preferably this face is configured in direct side that contacts with skin, perhaps consider the utilization of protuberance and be configured though the high-density region that is extruded does not connect.

Concavo-convex processing under the low temperature among the present invention is sayed preferably from economic angle and carry out on-line machining in the manufacturing process of spunbond class nonwoven fabric, also can import to the production of diaper, the part of processing line, carries out off-line processing.

Description of drawings

Fig. 1 (I) is the schematic diagram of the planar configuration of spunbond class nonwoven fabric of the present invention, Fig. 1 (II) is that the nonwoven fabric structure only is fixed by part hot pressing welding zone of fiber decorative pattern, the non-binding zone of fiber of nonwoven cloth cover does not apply the schematic cross-section of the spunbond class nonwoven fabric of concavo-convex processing, and Fig. 1 (III) is the schematic diagram of the cross-sectional configuration of spunbond class nonwoven fabric of the present invention.

Fig. 2 be the continuous connection in spunbond class nonwoven fabric of the present invention non-binding fiber high-density region the depression carreau, be on first of nonwoven fabric structure, be provided with in the checked embodiment of depression of continuous connection, omitted the illustrated schematic diagram of part hot pressing welding zone of fiber decorative pattern.

Among Fig. 3, the high-density region of non-binding fiber depression decorative pattern has constituted discrete spunbond class nonwoven fabric of the present invention, with the same diagram of omitting hot pressing welding zone of fiber decorative pattern of example of Fig. 2.

Among Fig. 4, the high-density region of the non-binding fiber that is provided with in succession depression tortoise plastron decorative pattern has constituted spunbond class nonwoven fabric of the present invention continuously, with the same diagram of omitting hot pressing welding zone of fiber decorative pattern of example of Fig. 2.

Fig. 5 is that spunbond class nonwoven fabric in embodiments of the invention 1 and comparative example 1,5 and 6 is under various loads and the schematic diagram of the relation of thickness.

Fig. 6 is the thickness comparison diagram of spunbond class nonwoven fabric under various loads of embodiments of the invention 8 and comparative example 8.

Fig. 7 (I) is the organigram as the spun-bonded non-woven fabrics of an example of the present invention, and Fig. 7 (2) is the expanded view at the microphotograph of the structure of the spun-bonded non-woven fabrics before concavo-convex processing is implemented in the zone of the non-binding fiber of Fig. 7 (1).

Fig. 8 (I) be as adding of another example the organigram of of the present invention spunbond class nonwoven fabric of meltblown fiber web, Fig. 8 (II) is the expanded view of microphotograph of the structure of the spunbond class nonwoven fabric before the non-binding zone of fiber of Fig. 8 (I) is used concavo-convex processing.

The specific embodiment

Reaching comparative example by the following examples is further detailed the present invention.

At first measuring method, appraisal procedure are described.

(1) weight of the unit are of nonwoven fabric

Choose the square nonwoven fabric of polylith 10cm, its weight is with every 1m ²Weight represent.

(2) thickness of nonwoven fabric

The electric industry in mountain (strain) is made in the use, elasticity of compression testing machine E-2 type, at 4cm ²The mensuration area in, with 1.3,10,37.5,50,100g/cm ²Each load measure down.

(3) the bulk rate of nonwoven fabric

Apply the thickness (10g/cm of the nonwoven fabric before and after the high-density region of non-binding fiber of the present invention ²Load is down) rate of change as bulk rate.

Stress when (4) brute force of nonwoven fabric and 5% is extended

With the omnipotent puller system that the test film of wide 3cm, long 20cm uses Shimadzu Seisakusho Ltd.'s (strain) to make, carry out the tension test that anchor clamps width 100mm, test speed 300m/ divide, the stress when measuring vertical, horizontal intensity and 5% elongation.

(5) the crooked pliability of nonwoven fabric

As the index of expression flexibility, represent with the crooked pliability that following method is measured.

Measuring method is, the end residue 1cm with a direction of measurement of test material presses down with the scale full duration on right angle orientation test material, and the additional crease in the other end of test material forming under the state that encircles, is placed on the end that is pressed down by scale.The end of one side that will press down with scale is with under the subordinate state of pressing, on one side on test material slide scale, mobile in ring on one side.

The point that extends with ring under the reaction force of test material is as terminal point, arrive length till ring one side end from this point as critical length (mm), represents with the mean value in showing.Short more soft more.

(6) the measurement face of water permeability

Water permeability is that nonwoven fabric is used as the top layer of disposable hygienic material, will be used for the measurement face of a side on surface as water permeability." top " or " following " shown in " water permeability measurement face " hurdle of table 1 represents to be used for the characteristic of a surperficial side respectively.

(7) moment permeable speed

10 pages of overlapping toilet papers are arranged on the measuring appliance as absorber (hole of diameter 25mm are set in central authorities during about 800g, 10cm are square, the utensil that two electrodes is set and is connected to its central authorities) with timer, measurement be with test cloth 10cm square (more than) be arranged between absorber and the measuring appliance, from 1 (0.1cc/ drips) normal saline solution that drips the device that drips of the top 15mm of cloth.Begin to measuring with electrode, as permeable speed of moment (second) from dripping by the time till the end of cloth surface.

(8) the permeable speed of 5cc (second/5cc), return wet amount (g)

For the characteristic that makes absorber keeps certain, as absorber with specific filter paper (EatonDikeman society makes " 939 " 10cm square * 3 overlapping) be placed on measuring appliance (with the moment in (6) permeable velocity meter the same) below.On this absorber, place test cloth (10cm is square).At first, from the drip artificial urine of 5cc of top 25mm, artificial urine is the material that adds tween and be adjusted to 45 ± 3 dyne/cm (mN/m) in normal saline solution, and the speed of dripping is 3.3 seconds/25cc.Time till finishing by the cloth surface from beginning to drip measures with electrode, as the permeable speed of 5cc (second/5cc).

Then directly append artificial urine, keep certain in order to make the amount of liquid that contains in the absorber, making whole amount of liquid is about 4 times of absorber weight.Apply three minutes the square load of 800g/10cm from test cloth in this state, the liquid distribution in the absorber is necessarily changed.Then, at test overlapping load weighted filter paper (Eaton Dikeman society makes " 631 " 12.5cm square * 2) that shifts to an earlier date on the cloth, the 3600g/10cm that applies two minutes rapidly square (be equivalent to apply on infant's the diaper load), the weight of measuring filter paper increases, as returning wet amount (g).

(9) liquid flow

On the tilting tables of 45 degree, place 10 toilet papers, be close to test cloth thereon, drip the drip normal saline solution of 1 (0.1cc/ drips) of device from the top 15mm of cloth as absorber.Measurement begins to by the length of flow till finishing, as liquid flow (mm) from the cloth surface portion of dripping.

(10) durable permeable transmitance

Place 10 toilet papers in the plane as absorber, be close to test cloth thereon.Drip the drip normal saline solution of 1 (0.1cc/ drips) of device from the top 15mm of cloth.With two seconds with interior absorbed the liquid that drips be considered as see through.After dry tack free, drip 1 once again in identical position, carry out the test second time.The complex phase of laying equal stress on action is together tested for the third time.Test at 10 to 40 places to the identical test material, will be through counting with respect to several ratio of dripping as durable permeable transmitance (%).

(11) fineness

Diameter to the fiber that constitutes nonwoven fabric is measured with microscope (the キ one high magnification microscope VH-8000 of エ Application ス society), as the fineness (dtex: weight that long filament 10000m long) represent of circular cross-section fiber according to the density calculation of fibre-forming polymer.In addition, the fineness of meltblown fiber web is represented with fibre diameter.

(12) the gentle softening rate of nonwoven fabric

Rate of change (before the handling back/processings) conduct that applies the pliability longitudinally before and after the high-density region of the non-binding fiber of the present invention softening rate that softens.The more little soft effect of this softness counting rate meter registration value is big more.

(13) water pressure resistance

The fine and closely woven degree of expression nonwoven fabric, the yardstick of water proofing property are represented with water pressure resistance.Select test material sheet (20cm is square), measure according to JIS-L-1092.

(embodiment 1, embodiment 2)

With the polypropylene (MFR=40 that measures under the condition of the table 1 of JIS-K7210) that contains titanium oxide as raw material, the long fiber that will melt extrude from the nozzle of circular section cools off on one side near spinning mouthful from the side, with air inhale traction such as silk device and pull device draw on one side.Pull after strand that device comes out opened fibre by Charging system from traction, collect on the mobile wire netting conveyer as net.

This Netcom is crossed between the knurling rolls/plain-barreled roll that is heated to 135 ℃, carry out part hot pressing welding with 45 ° of the circle inclinations of diameter 0.43mm, the needle point decorative pattern (area occupation ratio about 7%) that the indentation of inclination spacing 1.5mm is arranged, thereby acquisition has the nonwoven fabric of the distribution decorative pattern of pin mark.

The formation fiber of the spun-bonded non-woven fabrics that is obtained is the circular section silk of 2.8dtex (embodiment 1) and 2.0dtex (embodiment 2), and the long-pending rate of part hot pressing face of weld is 70%, and the weight of unit are is respectively 20g/m ²

Is that 0.9mm, live width are that the cellular decorative pattern (depression tortoise plastron decorative pattern: with reference to Fig. 4) of the continuous wire of 0.1mm (presses down area occupation ratio 12.5% with this nonwoven fabric by 1 limit, the vertical 2.8mm of decorative pattern spacing, laterally 3.2mm, dark 0.7mm) knurling rolls (100 ℃) and case hardness 50 spend between the rubber rollers of (JIS-A hardness), with embossing under the line pressure 100kg/cm.The tortoise plastron periphery is pressed down, thus the nonwoven fabric that acquisition has softness high-density region, the central portion projection.

Is the hydrophilic agent 0.45wt% that activating agent was constituted of main body modulation to this nonwoven fabric with block polymer polyethers, the polyethers sex change siloxanes that the gravure mode applies with the polyethylene glycol propylene glycol, as the hygienic material nonwoven fabric.The Performance Evaluation result of nonwoven fabric is shown in table 1,2.

To be configured to skin face one side on top layer as the density regions (embossed depression decorative pattern face) of the non-binding fiber on the surface of this nonwoven fabric, the disposable diaper of manufacturing is compared with the diaper that is made of existing nonwoven fabric, fibrage projection between the high-density region, comparatively soft, and returning moist improving, is the dry and comfortable nonwoven fabric with flexible touch.The embodiment 2 of thin dtex is objects with flexibility Paint Gloss.

(embodiment 3, embodiment 4)

Except with non-binding property press down the embossing decorative pattern with opposite with embodiment 1 discontinuous as the protruding tortoise plastron decorative pattern that scatters (on one side 0.45mm, press down area occupation ratio 25%, the vertical 2.8mm of decorative pattern spacing, horizontal 3.2mm, dark 0.6mm) outside, other are all identical with embodiment 1, thereby the weight that obtains 2.8dtex, unit are is 20g/m ²Nonwoven fabric of the present invention.The assessment result of nonwoven fabric is shown in table 1,2.

With this nonwoven fabric as the top layer, skin one side that the continuous projection (surface of nonwoven fabric) of the density regions of nonwoven fabric is used for the top layer in embodiment 3 is used for the top layer with discrete depression decorative pattern face of the high-density region at the back side of nonwoven fabric on the contrary and makes disposable diaper in embodiment 4.The same with embodiment, to compare with existing nonwoven fabric, better softness is returned moist also good.And putting upside down as top layer (embodiment 4) in the table with this nonwoven fabric is the object of high-density region with the point-like projection, is the object that also has dry and comfortable sense of touch except smooth surface.

(embodiment 5)

Except with the embossing decorative pattern of non-binding property as the depression carreau of discontinuous distribution (on one side 0.3mm * 0.7mm, press down area occupation ratio 22%, dark 0.6mm) and by outside sentencing with the combination that contains the checked roller that caves in of this decorative pattern coupling, other are all identical with embodiment 1, thereby the weight that obtains 2.0dtex, unit are is 18g/m ²Nonwoven fabric of the present invention.The assessment result of nonwoven fabric is shown in table 1,2.

The face (surface of nonwoven fabric) of the continuous projection of the density regions of this nonwoven fabric is made disposable diaper towards the skin face on top layer.The same with embodiment 1, compare with existing nonwoven fabric, better aspect flexibility, and have the good wet performance that returns.

(embodiment 6 and 7)

Before applying hydrophilic agent, carry out corona treatment, is the corona treatment condition that to carry out discharge capacity under the atmosphere of 22 ℃ of room temperatures be 30W? branch/m ²(discharge degree 2.2W/cm ²) discharge, consequently the surface tension of nonwoven fabric is 37mN/m, except considering that improving wettability by corona treatment adheres to the hydrophilic agent of 0.3wt%, equally with embodiment 1 and embodiment 3 make hygienic material nonwoven fabric of the present invention, thus acquisition embodiment 6 and 7.The disposable hygienic material that the nonwoven fabric that obtains uses as the top layer is compared with the material that constitutes with existing nonwoven fabric, comparatively soft, adhering to of hydrophilic agent is less, but the same with embodiment 1 and 3 have a good water permeability, the aspect that finishing agent is less can obtain good nonwoven fabric dry and comfortable, that have soft sense of touch.

(comparative example 1,2,3 and 4)

To in embodiment 1,2,5 and 7, not carry out non-binding property respectively and press down, and the situation that has applied hydrophilic agent as a comparative example 1,2,3 and 4.

(comparative example 5,6)

As the comparison on top layer, use the staple fibre point connection nonwoven fabric (19g/m that is actually used as the top layer of commercially available diaper ²: comparative example 5), two composition staple fibre hot blast connects nonwoven fabric (89g/m ²: comparative example 6), its result is shown in table 1 and table 2.

Table 1

	Material	Fineness (dtex)	Concavo-convex processing embossing decorative pattern	Nonwoven fabric		Part hot pressing face of weld amasss rate %	Recess or protuberance area occupation ratio %	Corona treatment	Hydrophilic agent adheres to	Top layer skin face one side	Water permeability is measured face	Weight (the g/m of the unit are of nonwoven fabric 2)	The thickness of the nonwoven fabric under the various loads					The bulk rate (%) of nonwoven fabric
																			Above (table)	Below (lining)	??1.3g ??/cm 2	??10g ??/cm 2	??37.5g/c ??m 2	??50g/c ??m 2	??100g/c ??m 2
				Embodiment 1	????PP								???2.8	Depression tortoise plastron decorative pattern	Low-density projection (discontinuous)	High density projection (continuously)	??7									??12.5	Do not have	Have	Table	Table	????20	??0.36	??0.26	??0.21	??0.19	??0.16	??124
Embodiment 2	????PP	???2.0	Depression tortoise plastron decorative pattern			Low-density projection (discontinuous)	High density projection (continuously)	??7	??12.5	Do not have	Have	Table						Table	????20	??0.33	??0.22	??0.17	??0.16	???0.14	??116
				Embodiment 3	????PP								???2.8	Projection tortoise plastron decorative pattern	Low-density projection (continuously)	High density projection (discontinuous)	??7									??25	Do not have	Have	Table	Table	????20	??0.35	??0.23	??0.17	??0.16	????0.12	??110
Embodiment 4	????PP	???2.8	Projection tortoise plastron decorative pattern			Low-density projection (continuously)	High density projection (discontinuous)	??7	??25	Do not have	Have	In						In	????20	??0.32	??0.21	??0.17	??0.16	??0.13	??111
				Embodiment 5	????PP								???2.0	The projection carreau	Low-density projection (continuously)	High density projection (discontinuous)	??7									??22	Do not have	Have	Table	Table	????18	??0.31	??0.24	??0.19	??0.15	??0.13	??133
Embodiment 6	????PP	???2.8	Depression tortoise plastron decorative pattern			Low-density projection (discontinuous)	High density projection (continuously)	??7	??12.5	Have	Have	Table						Table	????20	??-	??0.26	??-	??-	??-	??124
				Embodiment 7	????PP								???2.8	Depression tortoise plastron decorative pattern	Low-density projection (continuously)	High density projection (discontinuous)	??7									??25	Have	Have	Table	Table	????20	??-	??0.23	??-	??-	??-	??110
				Comparative example 1	????PP								???2.8														Do not have	Have		?-	????20	??0.29	??0.21	??0.17	??0.15	??0.12	??-
Comparative example 2	????PP	???2.0								Do not have	Have							?-	????18	??0.25	??0.19	??0.15	??0.14	??0.12	??-
				Comparative example 3	????PP								???2.0														Do not have	Have		?-	????18	??0.23	??0.18	??0.14	??0.13	??0.12	??-
Comparative example 4	????PP	???2.8								Have	Have							?-	????20	??-	??0.21	??-	??-	?-	??-
				Comparative example 5	????PP								???(2.2)														Do not have	Have		?-	????19	??0.27	??0.16	??0.13	??0.12	??0.11	??-
Comparative example 6	????PP/PE	???(2.3)								Do not have	Have							?-	????18	??0.61	??0.28	??0.18	??0.17	??0.12	??-

Table 2

	The TENSILE STRENGTH of nonwoven fabric (N/3cm is wide)		Stress (N/3cm is wide) during nonwoven fabric 5% elongation		Nonwoven fabric flexibility (mm)		Water permeability							Remarks
															Vertical	Horizontal	Vertical	Horizontal	Vertical	Horizontal	Moment permeable (second)	5cc permeable (second)	Return wet (g)	Liquid flow (mm)	Durable permeable (transmitance)
	1 time	2 times	3 times
				Embodiment 1	??28.9	????7.7	??12.5	????1.3	??78	????47	??0.12	???3.0	???0.6												??26	????100	????100	????60
Embodiment 2	??28.5	????7.2	??12.0											????1.3	??76	????50	??0.12	???3.1	???0.8	??28	????100	????100	????60
				Embodiment 3	??28.3	????6.8	??11.6	????1.1	??79	????49	??0.11	???3.2	???0.8												??30	????100	????100	????60
Embodiment 4	??28.8	????7.5	??11.5											????1.3	??77	????46	??0.11	???3.2	???0.8	??27	????100	????100	????60
				Embodiment 5	??27.1	????6.5	??11.0	????1.1	??78	????50	??0.11	???3.2	???0.9												??28	????100	????100	????60
Embodiment 6	??-	????-	??-											????-	??-	????-	??0.12	???3.2	???0.9	??21	????100	????100	????80
				Embodiment 7	??-	????-	??-	????-	??-	????-	??0.11	???3.5	???0.7												??27	????100	????100	????60
				Comparative example 1	??32.6	????7.6	??13.3	????1.5	??87	????57	??0.13	???3.2	???1.0												??34	????100	????100	????40
Comparative example 2	??31.9	????7.4	??15.3											????1.5	??85	????52	??0.13	???3.2	???1.3	??36	????100	????100	????40
				Comparative example 3	??29.9	????7.1	??12.8	????1.4	??83	????50	??0.13	???3.3	???1.3												??35	????100	????100	????40
Comparative example 4	??-	????-	??-											????-	??-	????-	??0.11	???3.2	???1.7	??22	????100	????100	????70
				Comparative example 5	??-	????-	??-	????-	??-	????-	??0.24	???2.8	???0.5												??30	????100	????0	????0	Staple fibre point connects
Comparative example 6	??-	????-	??-											????-	??-	????-	??0.10	???2.7	???0.1	??20	????100	????40	????0	The staple fibre hot blast is sticking

Can find from the result of table 1 and table 2: the nonwoven fabric the embodiment is compared with the nonwoven fabric in the comparative example, be bulk, varied in thickness during load is less, has flexibility, and moment water permeability, return aspect the water permeabilities such as moist, liquid fluidity, permeable durability better.

Hygienic material among the present invention shown in table 1 and the table 2 has good bulkiness with nonwoven fabric, and bulk rate is more than 110%, and varied in thickness is less when load, and is better, soft to the compressibility of load, has good water permeability, permeable durability simultaneously.

(embodiment 8, embodiment 9)

,, inhale traction such as a device on one side with air and pull device and draw as raw material with polypropylene (MFR=40 that measures under the condition of the table 1 of JIS-K7210) one side the long fiber that will melt extrude from the nozzle of circular section cools off near spinning mouthful from the side.Pull after strand that device comes out opened fibre by Charging system from traction, (2.8dtex (embodiment 8) and 1.2dtex (embodiment 9) are respectively 6.5g/m as the long filament net ²) collect on the mobile wire netting conveyer.

Two of this online laminations be raw material with polypropylene (MFR=700 that measures under the condition of the table 1 of JIS-K7210), (fine footpath is 1.8 μ m, 1g/m to be blown into the net of the meltblown fibers mode of high pressure-temperature wind near the slit two at the delivery nozzle ²).Further the long filament net of lamination collection thereon and above-mentioned the same making makes lamination net (15g/m ²).This Netcom is crossed between the knurling rolls/plain-barreled roll that is heated to be 130 ℃, is 0.36mm by the about 0.9mm of major diameter, the about 0.5mm of minor axis, area ²Oval decorative pattern tilt 30 °, have between the knurling rolls of the heating that is configured to vertical about 3mm, horizontal decorative pattern for the jagged oblique decorative pattern of 1.7m (crimping area occupation ratio 15%), carry out part hot pressing welding, thereby obtain to have the nonwoven fabric of the diffusing some style (tiltedly decorative pattern) of oval point-like.

Is that 0.9mm, live width are that the cellular decorative pattern (depression tortoise plastron decorative pattern) of the continuous wire of 0.1mm (presses down area occupation ratio 12.5% with this nonwoven fabric by 1 limit, between the rubber rollers of knurling rolls (40 ℃) dark 0.7mm) and case hardness 50 degree (JIS-A hardness), with embossing under the line pressure 100kg/cm.The tortoise plastron periphery is pressed down, thus the nonwoven fabric that acquisition has softness high-density region, the central portion projection.The Performance Evaluation result of nonwoven fabric is shown in table 1 and table 2.The fineness of long filament net is that the nonwoven fabric of 1.2dtex (embodiment 9) is soft more nonwoven fabric except the smooth sense of touch of surface fiber.

These nonwoven fabric are compared with the existing disposable diaper that nonwoven fabric constituted that does not carry out the softnessization processing as the disposable diaper of standing gather manufacturing, soft, and have good thickness.And, to the little porous PE film of this nonwoven fabric lamination as the disposable diaper of backing layer have the existing lamination nonwoven fabric that does not carry out the softnessization processing the soft-touch and actual use that can't obtain go up full intensity, have stronger surface strength.

(embodiment 10, embodiment 11)

In order to obtain non-binding property deformation of unevenness, the tortoise plastron protruding pattern of embossing decorative pattern as the discontinuous distribution opposite with embodiment 8 (0.45mm, press down area occupation ratio 25%, dark 0.6mm) on one side will be pressed down, in addition all the same with embodiment 8, the weight that can obtain unit are is 15g/cm ²(embodiment 10) and 17g/cm ²The nonwoven fabric of (embodiment 11).The Performance Evaluation result of nonwoven fabric is shown in table 3 and table 4.

With this nonwoven fabric is that standing gather is made disposable diaper.The same with embodiment 8, compare with the existing diaper that nonwoven fabric constituted that does not carry out the softnessization processing, better softness, and solid sense is better.And, put upside down in the table with this nonwoven fabric, be the object of the high-density region point-like projection of non-binding fiber with little porous PE film lamination as the object of backing layer, except smooth surface is dry and comfortable, also have good sense of touch.

(embodiment 12)

In order to obtain non-binding property deformation of unevenness, the protruding carreau of embossing decorative pattern as discontinuous distribution (0.3mm * 0.7mm, press down area occupation ratio 22%, dark 0.6mm) on one side will be pressed down, by have and the combination of the checked roller of depression that this decorative pattern is chimeric between, in addition the same with embodiment 8, the weight that can obtain unit are is 15g/cm ²Nonwoven fabric.The Performance Evaluation result of nonwoven fabric is shown in table 3 and table 4.

The little porous PE film of this nonwoven fabric lamination is used as backing layer, made disposable diaper.The same with embodiment 8, to compare with existing nonwoven fabric, flexibility is higher, has better thickness sense.

(embodiment 13)

In order to obtain non-binding property deformation of unevenness, with press down the embossing decorative pattern as continuous oblique line protruding pattern (on one side 0.2mm, at interval 0.5mm, press down area occupation ratio 29%, dark 0.6mm), and by and case hardness 60 spend between the combination of rubber rollers of (JIS-A hardness), thick 15mm, in addition all identical with embodiment 8, thus the weight that obtains unit are is 17g/m ²Nonwoven fabric.The assessment result of nonwoven fabric is shown in table 3 and table 4.

This nonwoven fabric has oblique flexibility, compares with the nonwoven fabric before carrying out the softnessization processing, and flexibility is higher, has thickness sense preferably.

(embodiment 14)

Except the polypropylene (MFR=40 that measures under the condition of the table 1 of JIS-K7210) of raw polymer uses long filament net (1.8dtex, 6.5g/m as polypropylene random copolymer (PE3%, MFR=35) ²) in addition, other are all the same with embodiment 8, the weight that can obtain unit are is 15g/m ²Nonwoven fabric.The Performance Evaluation result of nonwoven fabric is shown in table 3 and table 4.

The surface touch of this nonwoven fabric has the same submissive sense of polyethylene, compares with the nonwoven fabric before carrying out soft treatment, has better flexibility, and good thickness sense.

(embodiment 15)

Except in embodiment 8, the long filament stratum reticulare of a face being made as 1.2dtex (3.3g/m in the outside ²) net be made as 2.8dtex (3.3g/m in the inboard ²) net beyond, other are the same with embodiment 8, the weight that can obtain unit are is 15g/m ²Nonwoven fabric.The nonwoven fabric that obtains is the nonwoven fabric that superficial layer is smooth, have the thickness sense.

(embodiment 16, embodiment 1 7)

The raw polymer that the long filament net is used uses polyethylene terephthalate (viscosities il sp/C=0.75) and nylon 6 (relative viscosity η rel=2.7), meltblown fibers uses polyethylene terephthalate (viscosities il sp/C=0.42) and nylon 6 (relative viscosity η rel=2.3), long filament net (2.0dtex, 8.3g/m respectively with polymer ²), (fine footpath is PET=2.4 μ m, 3.4g/m respectively for meltblown fiber web ², N6=1.6 μ m, 3.4g/m ²), by knitting between order embossing decorative pattern (0.5mm is square, crimping area occupation ratio 15%) knurling rolls/plain-barreled roll, the net of polyethylene terephthalate long filament under 205 ℃, the long filament net of nylon 6 carries out part hot pressing welding under 186 degree, the same with embodiment 8 in addition, the weight that can obtain unit are is respectively 20g/m ²Nonwoven fabric.The Performance Evaluation result of nonwoven fabric is shown in table 3 and table 4.

These nonwoven fabric are compared with the various preceding nonwoven fabric of softnessization processing that carry out, and have better flexibility, and its effect of polyester non-woven fabric in the good thickness sense, particularly embodiment 16 are more remarkable.

These nonwoven fabric not only can be used for hygienic material, also can be used for packaging material, printing material, simple dress material etc., have unexistent flexibility in the existing nonwoven fabric.

(comparison array 8-14)

With nonwoven fabric before the concavo-convex softnessization processing of non-binding property of embodiment 8,9,11,14,15,16 and 17 correspondences respectively as separately comparative example 8,9,10,11,12,13 and 14, its characteristic is shown in table 3,4.

Table 3

	Constitute fiber				The formation F of nonwoven fabric: long filament M: melt and spray	The thermocompression bonded embossing	Concavo-convex processing embossing decorative pattern	Nonwoven fabric		Measurement face	Portion of hot weld portion area occupation ratio %	The area occupation ratio of recess or protuberance
													Long filament		Melt and spray
	Material	Fineness (dtex)	Material	Fineness (μ m)
													Above (table)	Below (lining)
								Embodiment 8	?PP						?2.8	?PP	?1.8	?F/M/M/F	Oblique decorative pattern	Depression tortoise plastron decorative pattern	Low-density projection (discontinuous)	High density projection (continuously)	Table	15	?12.5
Embodiment 9	?PP	?1.2	?PP	?1.8	?F/M/M/F	Oblique decorative pattern	Depression tortoise plastron decorative pattern			Low-density projection (discontinuous)	High density projection (continuously)	Table	15	?12.5
								Embodiment 10	?PP						?2.8	?PP	?1.8	?F/M/M/F	Oblique decorative pattern	Projection tortoise plastron decorative pattern	Low-density projection (continuously)	High density projection (discontinuous)	Table	15	?25
Embodiment 11	?PP	?2.8	?PP	?1.8	?F/M/M/F	Oblique decorative pattern	Projection tortoise plastron decorative pattern			Low-density projection (continuously)	High density projection (discontinuous)	Table	15	?25
								Embodiment 12	?PP						?2.8	?PP	?1.8	?F/M/M/F	Oblique decorative pattern	The projection carreau	Low-density projection (continuously)	High density projection (discontinuous)	Table	15	?22
Embodiment 13	?PP	?2.8	?PP	?1.8	?F/M/M/F	Oblique decorative pattern	Projection oblique line decorative pattern			Low-density projection (continuously)	High density projection (discontinuous)	Table	15	?29
								Embodiment 14	?RCP						?1.8	?PP	?1.8	?F/M/F	Pin mark	Depression tortoise plastron decorative pattern	Low-density projection (discontinuous)	High density projection (continuously)	Table	15	?12.5
Embodiment 15	?PP	?1.2/2. ?8	?PP	?1.8	?F/M/M/F	Oblique decorative pattern	Depression tortoise plastron decorative pattern			Low-density projection (discontinuous)	High density projection (continuously)	Table	15	?12.5
								Embodiment 16	?PET						?2.0	?PET	?2.4	?F/M/F	Weave pattern	Depression tortoise plastron decorative pattern	Low-density projection (discontinuous)	High density projection (continuously)	Table	15	?15
Embodiment 17	?N6	?2.0	?N6	?1.6	?F/M/F	Weave pattern	Depression tortoise plastron decorative pattern			Low-density projection (discontinuous)	High density projection (continuously)	Table	15	?15
Comparative example 8	?PP	?2.8	?PP	?1.8	?F/M/M/F	Oblique decorative pattern	-					-
								Comparative example 9	?PP						?1.2	?PP	?1.8	?F/M/M/F	Oblique decorative pattern	-			-
Comparative example 10	?PP	?2.8	?PP	?1.8	?F/M/M/F	Oblique decorative pattern	-					-
								Comparative example 11	?RCP						?1.8	?PP	?1.8	?F/M/F	Pin mark	-			-
Comparative example 12	?PP	?1.2/2. ?8	?PP	?1.8	?F/M/M/F	Oblique decorative pattern	-					-
								Comparative example 13	?PET						?2.0	?PET	?2.4	?F/M/F	Weave pattern	-			-
Comparative example 14	?N6	?2.0	?N6	?1.6	?F/M/F	Weave pattern	-					-

Table 4

	Weight (the g/m of the unit are of nonwoven fabric 2)	The thickness of the nonwoven fabric under the various loads (μ m)					The bulk rate (%) of nonwoven fabric	The TENSILE STRENGTH of nonwoven fabric (N/3cm is wide)		Stress (N/3cm is wide) when nonwoven fabric 5% stretches		The water pressure resistance of nonwoven fabric (mb)	Nonwoven fabric flexibility mm		Gentle softening rate %
																?1.3g/cm 2	?10g/cm 2	?37.5g/cm 2	?50g/cm 2	?100g/cm 2
		Vertical	Horizontal	Vertical	Horizontal	Vertical															Horizontal
								Embodiment 8	?15	?268	?189		?149	?138								?119	?119	?12.2	?7.4	?5.6	?2.1	?15	?58	?42	?84
Embodiment 9	?15	?266	?178	?140	?131	?112	?115					?18.2			?7.7	?6.1	?2.1	?15	?57	?41	?76
								Embodiment 10	?15	?266	?174		?135	?129								?105	?109	?13.1	?7.5	?5.3	?1.4	?13	?58	?42	?84
Embodiment 11	?17	?-	?184	?-	?-	?-	?115					?22.8			?7.0	?6.8	?1.5	?16	?65	?45	?75
								Embodiment 12	?15	?241	?173		?131	?130								?109	?109	?13.0	?7.7	?5.9	?1.8	?14	?59	?43	?86
Embodiment 13	?17	?-	?185	?-	?-	?-	?116					?13.3			?7.5	?6.1	?1.6	?16	?61	?43	?88
								Embodiment 14	?16	?-	?188		?-	?-								?-	?121	?12.0	?5.3	?4.4	?1.3	?13	?59	?40	?87
Embodiment 15	?15	?-	?185	?-	?-	?-	?121					?16.5			?7.2	?6.2	?1.4	?15	?59	?43	?86
								Embodiment 16	?20	?-	?162		?-	?-								?-	?157	?48.3	?18.1	?13.3	?5.8	?-	?103	?62	?76
Embodiment 17	?20	?-	?159	?-	?-	?-	?135					?53.0			?14.1	?8.1	?2.4	?-	?54	?35	?87
Comparative example 8	?15	?224	?159	?133	?124	?109	?-					?14.9			?9.1	?7.1	?2.7	?18	?69	?44
								Comparative example 9	?15	?220	?155		?129	?119								?109	?-	?19.4	?8.3	?7.8	?2.8	?24	?75	?47
Comparative example 10	?17	?-	?160	?-	?-	?-	?-					?19.8			?7.8	?8.5	?1.8	?16	?87	?49
								Comparative example 11	?16	?-	?156		?-	?-								?-	?-	?12.3	?5.6	?4.7	?1.4	?19	?68	?43
Comparative example 12	?15	?-	?153	?-	?-	?-	?-					?17.4			?8.0	?7.5	?2.3	?22	?69	?45
								Comparative example 13	?20	?-	?103		?-	?-								?-	?-	?53.0	?19.0	?28.8	?11.3	?-	?135	?87
Comparative example 14	?20	?-	?118	?-	?-	?-	?-					?55.6			?13.6	?15.2	?4.3	?-	?62	?39

Can find from the result shown in table 3 and the table 4: the object the embodiment is aspects such as stress, flexibility outstanding than in the comparative example all when bulk rate, TENSILE STRENGTH, elongation.

The bulk rate of spunbond class nonwoven fabric of the present invention is good, softness and intensity are better, is applicable to the hygienic material nonwoven fabric.Spunbond class nonwoven fabric of the present invention is further by mainly containing hydrophilic agent in (B) zone, therefore can satisfy simultaneously bulk rate as the performance of hygienic material, softness, permeable, return four characteristics such as wet.

Claims (23)

1. spunbond class nonwoven fabric, it is the nonwoven fabric that the net by thermoplastic synthetic fiber's continuous filament yarn constitutes, it is characterized in that: the structure of nonwoven fabric by between the table the inside that connects nonwoven fabric and incorporate part hot pressing welding zone of fiber decorative pattern, and the depression decorative pattern or the protruding pattern that on two faces of nonwoven fabric structure, constitute by the high-density region of non-binding fiber be fixed, be more than 100% by the thickness of the shared nonwoven fabric of the density regions of nonwoven fabric structure and the bulk rate that the ratio of the thickness of the nonwoven fabric of the face of the protruding embossing decorative pattern that contains nonwoven fabric is represented.

2. spunbond class nonwoven fabric according to claim 1 is characterized in that the high-density region of non-binding fiber disposes continuously.

3. spunbond class nonwoven fabric according to claim 1 and 2 is characterized in that, the discontinuous dispersion of the high-density region of non-binding fiber exists.

4. according to any described spunbond class nonwoven fabric of claim 1-3, it is characterized in that bulk rate is 105-400%.

5. according to any described spunbond class nonwoven fabric of claim 1-4, it is characterized in that the area occupation ratio of part hot pressing welding zone of fiber decorative pattern is 5-40%, the area occupation ratio of the depression of the high-density region of non-binding fiber or protruding pattern portion is 5-40%.

6. spunbond class nonwoven fabric, form by composite web, this composite web is by one deck thermoplastic synthetic fiber continuous filament yarn net at least and one deck meltblown fiber web layer is long-pending at least forms, this nonwoven fabric is characterised in that, the structure of nonwoven fabric is incorporate part hot pressing welding zone of fiber decorative pattern by the table the inside that connects nonwoven fabric, and the depression embossing that on two faces of nonwoven fabric structure, constitutes by the high-density region of non-binding fiber or protruding pattern and be fixed, be more than 100% by the thickness of the shared nonwoven fabric of the density regions of nonwoven fabric structure and the bulk rate that the ratio of the thickness of the nonwoven fabric of the face of the protruding embossing decorative pattern that contains nonwoven fabric is represented.

7. spunbond class nonwoven fabric according to claim 6 is characterized in that the high-density region of non-binding fiber disposes continuously.

8. according to claim 6 or 7 described spunbond class nonwoven fabric, it is characterized in that the discontinuous dispersion of the high-density region of non-binding fiber exists.

9. according to any described spunbond class nonwoven fabric of claim 6-8, it is characterized in that bulk rate is 105-400%.

10. according to any described spunbond class nonwoven fabric of claim 6-9, it is characterized in that the area occupation ratio of part hot pressing welding zone of fiber decorative pattern is 5-40%, the depression decorative pattern of the high-density region of non-binding fiber or the area occupation ratio of protruding pattern portion are 5-40%.

11. spunbond class nonwoven fabric hygienic material, it is the nonwoven fabric that the net by thermoplastic synthetic fiber's continuous filament yarn constitutes, it is characterized in that: the structure of nonwoven fabric is incorporate part hot pressing welding zone of fiber decorative pattern by the table the inside that connects nonwoven fabric, and the depression decorative pattern that on two faces of nonwoven fabric structure, constitutes or protruding pattern and be fixed by the high-density region of non-binding fiber, the bulk rate of being represented by the thickness of the shared nonwoven fabric of the density regions of nonwoven fabric structure and the ratio of the thickness of the nonwoven fabric of the face of the protruding embossing decorative pattern that contains nonwoven fabric is more than 100%, and has applied hydrophilic agent.

12. hygienic material according to claim 11 is characterized in that with spunbond class nonwoven fabric hydrophilic agent mainly is included in the high-density region of non-binding fiber.

13., it is characterized in that bulk rate is 105-400% according to claim 11 or 12 described spunbond class nonwoven fabric.

14. according to any described spunbond class nonwoven fabric of claim 11-13, it is characterized in that the area occupation ratio of part hot pressing welding zone of fiber decorative pattern is 5-40%, the decorative pattern recess of the high-density region of above-mentioned non-binding fiber or the area occupation ratio of protuberance are 5-40%.

15., it is characterized in that spunbond class nonwoven fabric hygienic material has been applied in hydrophilic agent according to any described spunbond class nonwoven fabric of claim 11-14 after implementing corona discharge.

16. spunbond class nonwoven fabric hygienic material, form by composite web, this composite web is by one deck thermoplastic synthetic fiber continuous filament yarn net at least and one deck meltblown fiber web layer is long-pending at least forms, it is characterized in that, the structure of nonwoven fabric is by the part hot pressing welding zone of fiber decorative pattern inside the table that connects nonwoven fabric, and the depression embossing that on two faces of nonwoven fabric structure, constitutes by the high-density region of non-binding fiber or protruding pattern and be fixed, be more than 100% by the thickness of the shared nonwoven fabric of the density regions of nonwoven fabric structure and the bulk rate that the ratio of the thickness of the nonwoven fabric of the face of the protruding embossing decorative pattern that contains nonwoven fabric is represented.

17. spunbond class nonwoven fabric hygienic material according to claim 16 is characterized in that hydrophilic agent mainly is included in the high-density region of non-binding fiber.

18. require 16 or 17 described spunbond class nonwoven fabric hygienic materials according to claim, it is characterized in that bulk rate is 105-400%.

19. according to any described spunbond class nonwoven fabric hygienic material of claim 16-18, it is characterized in that, the area occupation ratio of part hot pressing welding zone of fiber decorative pattern is 5-40%, and the decorative pattern recess of the high-density region of non-binding fiber or the area occupation ratio of protuberance are 5-40%.

20., it is characterized in that in spunbond class nonwoven fabric hygienic material, nonwoven fabric has been applied in hydrophilic agent after implementing Corona discharge Treatment according to any described spunbond class nonwoven fabric hygienic material of claim 16-19.

21. spunbond class nonwoven fabric disposable hygienic material, it is characterized in that, in any described spunbond class nonwoven fabric hygienic material of claim 11-20, the face with the depression of high-density region of non-binding fiber of this nonwoven fabric or protruding pattern is used for the surface on top layer.

22. a disposable hygienic material is characterized in that, in any described spunbond class nonwoven fabric hygienic material of claim 11-20, the face with the depression of high-density region of non-binding fiber of this nonwoven fabric or protruding pattern uses as the reverse side on top layer.

23. a disposable hygienic material is characterized in that, any described spunbond class nonwoven fabric of claim 6-10 is used for standing gather portion and/or backing layer.