CN112192699A - Bamboo-wood fiber board production process - Google Patents
Bamboo-wood fiber board production process Download PDFInfo
- Publication number
- CN112192699A CN112192699A CN202011040942.4A CN202011040942A CN112192699A CN 112192699 A CN112192699 A CN 112192699A CN 202011040942 A CN202011040942 A CN 202011040942A CN 112192699 A CN112192699 A CN 112192699A
- Authority
- CN
- China
- Prior art keywords
- parts
- bamboo
- uniformly mixing
- fiber
- hot pressing
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a bamboo-wood fiber board production process, which comprises the following steps: 1) selecting materials: bamboo fiber, wood fiber, glass fiber, paraffin emulsion, adhesive and tourmaline powder; 2) uniformly mixing bamboo fibers and wood fibers and then drying; 3) adding glass fiber in the step 2), and fully and uniformly mixing; 4) adding the paraffin emulsion into the mixture obtained in the step 3), and fully and uniformly mixing; 5) adding an adhesive in the step 4), and fully and uniformly mixing; 6) adding tourmaline powder into the mixture obtained in the step 5), and fully and uniformly mixing; 7) putting the mixture obtained in the step 6) into a hot press to form a plate blank and carrying out hot press molding; 8) and 7) stopping heating after the hot pressing time is finished, and keeping the original hot pressing pressure until the hot pressing pressure is naturally cooled to obtain the finished bamboo-wood fiber board. Compared with the prior art, the invention has the advantages that: the environment-friendly waterproof plate is environment-friendly and non-toxic, and has the advantages of firm and durable plate body, good bending resistance and compression resistance and good waterproof and moistureproof effects.
Description
Technical Field
The invention relates to the technical field of lubricating oil, in particular to a bamboo-wood fiberboard production process.
Background
The bamboo-wood fiber integrated wall material is manufactured by adopting an extrusion process, so that the color, the size and the shape of a product can be controlled according to needs, customization according to needs is really realized, the use cost is reduced to the maximum extent, forest resources are saved, the bamboo-wood fiber integrated wall material has an outstanding environment-friendly function and can be recycled, the whole house integrally-mounted bamboo-wood fiber integrated wall can be installed in a horizontal mode, a vertical mode, an inclined mode and the like according to personal preference, the socket, buckle and wedge type design is adopted, different types of products can be matched with one another for installation and use, a larger imagination space is provided for the individualized design of a designer, in addition, the processing method is the same as that of solid wood, and the bamboo-wood fiber integrated wall material can be sawed, nailed and planed without painting, can be installed and used immediately, and common woodworkers.
The existing fiberboard product has the problems of poor overall quality of the fiberboard body, poor compactness of the fiberboard body, local cracks of the fiberboard body and poor damp-proof and water-proof effects, and in addition, organic adhesives can be used in the production process, so that harmful substances such as formaldehyde, phenol and the like can be released in the production and use processes, adverse effects are brought to physical and mental health of producers and users, and certain potential safety hazards in environmental protection still exist.
Disclosure of Invention
The invention aims to solve the problems in the prior art, and further provides a bamboo-wood fiberboard production process which is environment-friendly, non-toxic, firm and durable in board body, good in bending resistance and compression resistance and good in waterproof and moistureproof effects.
The purpose of the invention is realized by the following technical scheme:
a bamboo-wood fiber board production process comprises the following steps:
1) weighing the following components in parts by weight: 13-16 parts of bamboo fiber, 45-60 parts of wood fiber, 9-13 parts of glass fiber, 6-9 parts of paraffin emulsion, 6-9 parts of adhesive and 0.5-1 part of tourmaline powder;
2) uniformly mixing the bamboo fibers and the wood fibers in the step 1) and drying;
3) adding the glass fiber obtained in the step 1) into the mixture obtained in the step 2), and fully and uniformly mixing;
4) adding the paraffin emulsion in the step 1) into the mixture obtained in the step 3), and fully and uniformly mixing;
5) adding the adhesive in the step 1) into the mixture obtained in the step 4), and fully and uniformly mixing;
6) adding the tourmaline powder obtained in the step 1) into the mixture obtained in the step 5), and fully and uniformly mixing;
7) placing the mixture obtained in 6) into a hot press, forming a slab and hot-pressing, wherein: the hot pressing temperature is 120-180 ℃, the hot pressing time is 22-28 min, and the hot pressing pressure is 30-100 kg/cm;
8) and 7) stopping heating after the hot pressing time is finished, and keeping the original hot pressing pressure until the hot pressing pressure is naturally cooled to obtain the finished bamboo-wood fiber board.
Further, the adhesive in 1) is a plant adhesive.
Further, in 1), the components in parts by weight are as follows: 15 parts of bamboo fiber, 50 parts of wood fiber, 11 parts of glass fiber, 7 parts of paraffin emulsion, 7 parts of adhesive and 0.8 part of tourmaline powder.
Further, in 1), the components in parts by weight are as follows: 13 parts of bamboo fiber, 52 parts of wood fiber, 9 parts of glass fiber, 7 parts of paraffin emulsion, 7 parts of adhesive and 0.8 part of tourmaline powder.
Further, in 1), the components in parts by weight are as follows: 16 parts of bamboo fiber, 48 parts of wood fiber, 13 parts of glass fiber, 8 parts of paraffin emulsion, 8 parts of adhesive and 0.8 part of tourmaline powder.
Compared with the prior art, the invention has the advantages that:
reasonable bamboo-wood fiber collocation proportion adds the bending resistance compressive property of right amount of glass fiber increase plate body, choose for use the plant gluing agent, avoid the existence of toxic gas, accomplish environmental protection safety in production and use, through adding right amount of paraffin emulsion, can increase the waterproof performance of finished product panel and improve panel surface finish, the tourmaline powder of adding at last increases the environmental protection performance of finished product panel, utilize the characteristic of tourmaline powder to play the effect of release air anion and far infrared, effective purification installation service environment.
Detailed Description
Example one
A bamboo-wood fiber board production process comprises the following steps:
1) weighing the following components in parts by weight: 15 parts of bamboo fiber, 50 parts of wood fiber, 11 parts of glass fiber, 7 parts of paraffin emulsion, 7 parts of adhesive and 0.8 part of tourmaline powder;
2) uniformly mixing the bamboo fibers and the wood fibers in the step 1) and drying;
3) adding the glass fiber obtained in the step 1) into the mixture obtained in the step 2), and fully and uniformly mixing;
4) adding the paraffin emulsion in the step 1) into the mixture obtained in the step 3), and fully and uniformly mixing;
5) adding the adhesive in the step 1) into the mixture obtained in the step 4), and fully and uniformly mixing;
6) adding the tourmaline powder obtained in the step 1) into the mixture obtained in the step 5), and fully and uniformly mixing;
7) placing the mixture obtained in 6) into a hot press, forming a slab and hot-pressing, wherein: the hot pressing temperature is 120-180 ℃, the hot pressing time is 22-28 min, and the hot pressing pressure is 30-100 kg/cm;
8) and 7) stopping heating after the hot pressing time is finished, and keeping the original hot pressing pressure until the hot pressing pressure is naturally cooled to obtain the finished bamboo-wood fiber board.
Example two
A bamboo-wood fiber board production process comprises the following steps:
1) weighing the following components in parts by weight: 13 parts of bamboo fiber, 52 parts of wood fiber, 9 parts of glass fiber, 7 parts of paraffin emulsion, 7 parts of adhesive and 0.8 part of tourmaline powder;
2) uniformly mixing the bamboo fibers and the wood fibers in the step 1) and drying;
3) adding the glass fiber obtained in the step 1) into the mixture obtained in the step 2), and fully and uniformly mixing;
4) adding the paraffin emulsion in the step 1) into the mixture obtained in the step 3), and fully and uniformly mixing;
5) adding the adhesive in the step 1) into the mixture obtained in the step 4), and fully and uniformly mixing;
6) adding the tourmaline powder obtained in the step 1) into the mixture obtained in the step 5), and fully and uniformly mixing;
7) placing the mixture obtained in 6) into a hot press, forming a slab and hot-pressing, wherein: the hot pressing temperature is 120-180 ℃, the hot pressing time is 22-28 min, and the hot pressing pressure is 30-100 kg/cm;
8) and 7) stopping heating after the hot pressing time is finished, and keeping the original hot pressing pressure until the hot pressing pressure is naturally cooled to obtain the finished bamboo-wood fiber board.
EXAMPLE III
A bamboo-wood fiber board production process comprises the following steps:
1) weighing the following components in parts by weight: 16 parts of bamboo fiber, 48 parts of wood fiber, 13 parts of glass fiber, 8 parts of paraffin emulsion, 8 parts of adhesive and 0.8 part of tourmaline powder;
2) uniformly mixing the bamboo fibers and the wood fibers in the step 1) and drying;
3) adding the glass fiber obtained in the step 1) into the mixture obtained in the step 2), and fully and uniformly mixing;
4) adding the paraffin emulsion in the step 1) into the mixture obtained in the step 3), and fully and uniformly mixing;
5) adding the adhesive in the step 1) into the mixture obtained in the step 4), and fully and uniformly mixing;
6) adding the tourmaline powder obtained in the step 1) into the mixture obtained in the step 5), and fully and uniformly mixing;
7) placing the mixture obtained in 6) into a hot press, forming a slab and hot-pressing, wherein: the hot pressing temperature is 120-180 ℃, the hot pressing time is 22-28 min, and the hot pressing pressure is 30-100 kg/cm;
8) and 7) stopping heating after the hot pressing time is finished, and keeping the original hot pressing pressure until the hot pressing pressure is naturally cooled to obtain the finished bamboo-wood fiber board.
Claims (5)
1. The production process of the bamboo-wood fiber board is characterized by comprising the following steps:
1) weighing the following components in parts by weight: 13-16 parts of bamboo fiber, 45-60 parts of wood fiber, 9-13 parts of glass fiber, 6-9 parts of paraffin emulsion, 6-9 parts of adhesive and 0.5-1 part of tourmaline powder;
2) uniformly mixing the bamboo fibers and the wood fibers in the step 1) and drying;
3) adding the glass fiber obtained in the step 1) into the mixture obtained in the step 2), and fully and uniformly mixing;
4) adding the paraffin emulsion in the step 1) into the mixture obtained in the step 3), and fully and uniformly mixing;
5) adding the adhesive in the step 1) into the mixture obtained in the step 4), and fully and uniformly mixing;
6) adding the tourmaline powder obtained in the step 1) into the mixture obtained in the step 5), and fully and uniformly mixing;
7) placing the mixture obtained in 6) into a hot press, forming a slab and hot-pressing, wherein: the hot pressing temperature is 120-180 ℃, the hot pressing time is 22-28 min, and the hot pressing pressure is 30-100 kg/cm;
8) and 7) stopping heating after the hot pressing time is finished, and keeping the original hot pressing pressure until the hot pressing pressure is naturally cooled to obtain the finished bamboo-wood fiber board.
2. The bamboo-wood fiberboard production process of claim 1, wherein the adhesive in 1) is a plant adhesive.
3. The bamboo-wood fiber board production process according to claim 1, wherein 1) comprises the following components in parts by mass: 15 parts of bamboo fiber, 50 parts of wood fiber, 11 parts of glass fiber, 7 parts of paraffin emulsion, 7 parts of adhesive and 0.8 part of tourmaline powder.
4. The bamboo-wood fiber board production process according to claim 1, wherein 1) comprises the following components in parts by mass: 13 parts of bamboo fiber, 52 parts of wood fiber, 9 parts of glass fiber, 7 parts of paraffin emulsion, 7 parts of adhesive and 0.8 part of tourmaline powder.
5. The bamboo-wood fiber board production process according to claim 1, wherein 1) comprises the following components in parts by mass: 16 parts of bamboo fiber, 48 parts of wood fiber, 13 parts of glass fiber, 8 parts of paraffin emulsion, 8 parts of adhesive and 0.8 part of tourmaline powder.