CN106995303A - A kind of bamboo and woods fiber plate and preparation method thereof - Google Patents
A kind of bamboo and woods fiber plate and preparation method thereof Download PDFInfo
- Publication number
- CN106995303A CN106995303A CN201610048375.4A CN201610048375A CN106995303A CN 106995303 A CN106995303 A CN 106995303A CN 201610048375 A CN201610048375 A CN 201610048375A CN 106995303 A CN106995303 A CN 106995303A
- Authority
- CN
- China
- Prior art keywords
- parts
- bamboo
- wood
- adhesive
- fibred
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of bamboo and woods fiber plate and preparation method thereof, 12~18 parts with bamboo fibre of 45~55 parts of wood-fibred uniformly mixes drying, adds 5~7 parts of 20~27 parts of magnesia and magnesium chloride, adds 0.05~0.2 part of 4~6 parts of adhesive and tourmaline powder, mixing, extrusion forming is produced.The bamboo and woods fiber plate density that the present invention is obtained is 880~920kg/m3, water content is not higher than 8%；More than B1 grades of fire-protection rating, expansion rate of water absorption is not higher than 2 ‰, and good properties, machinability is good, nonpoisonous and tasteless, safety and Health, environmental protection；And the easy cost of preparation technology is low, application prospect is extensive.
Description
Technical field
The present invention relates to a kind of bamboo and woods fiber plate and preparation method thereof.
Background technology
Bamboo and woods fiber plate has turned into the ideal material that Modern Decorative is fitted up, and it is using increasingly extensive.Bamboo and woods fiber plate is based on wood and bamboo
Want raw material to be made, as the demand of bamboo and woods fiber plate is increasing, can consume in substantial amounts of bamboo wood resources, and its production technology
Organic adhesion agent can be used unavoidably, in the production and use process can the harmful substance such as release formaldehyde, phenol, to the producer and use
The physical and mental health of person brings adverse effect, inadequate environment protection health.
The content of the invention
It is an object of the invention to overcome the deficiencies in the prior art part, there is provided a kind of bamboo and woods fiber plate and preparation method thereof, the bamboo
Wood-fiber board good properties, machinability is good, nonpoisonous and tasteless, safety and Health, environmental protection；And the easy cost of preparation technology is low,
Application prospect is extensive.
One of the technical solution adopted for the present invention to solve the technical problems is：
A kind of preparation method of bamboo and woods fiber plate, including：
1) following each component according to the mass fraction, is weighed：45~55 parts of wood-fibred, 12~18 parts of bamboo fibre, magnesia 20~
27 parts, 5~7 parts of magnesium chloride, 4~6 parts of adhesive, 0.05~0.2 part of tourmaline powder；
2) above-mentioned wood-fibred is uniformly mixed with bamboo fibre, drying to water content is not higher than 10%；
3) in step 2) above-mentioned magnesia and magnesium chloride are added in obtained mixture, uniform mixing；
4) in step 3) above-mentioned adhesive is added in obtained mixture, above-mentioned tourmaline powder is added immediately after, is well mixed；
5) by step 4) obtained mixture is placed in 100~120 DEG C, under 450~550 tons of pressure, is press-formed 20~30min,
The bamboo and woods fiber plate is produced, density is 880~920kg/m3, water content is not higher than 8%；More than B1 grades of fire-protection rating, water suction
Expansion rate is not higher than 2 ‰.
In one embodiment：：The step 1) in each group be divided into：50 parts of wood-fibred, 15 parts of bamboo fibre, 24 parts of magnesia, chlorine
Change 6 parts of magnesium, 5 parts of adhesive, 0.1 part of tourmaline powder.
In one embodiment：The step 1) in each group be divided into：48 parts of wood-fibred, 16 parts of bamboo fibre, 22 parts of magnesia, chlorination
6 parts of magnesium, 5 parts of adhesive, 0.08 part of tourmaline powder.
In one embodiment：The step 1) in each group be divided into：53 parts of wood-fibred, 13 parts of bamboo fibre, 26 parts of magnesia, chlorination
5.5 parts of magnesium, 5.5 parts of adhesive, 0.15 part of tourmaline powder.
In one embodiment：The step 1) in each group be divided into：46 parts of wood-fibred, 17 parts of bamboo fibre, 21 parts of magnesia, chlorination
6.5 parts of magnesium, 4.5 parts of adhesive, 0.1 part of tourmaline powder.
In one embodiment：The step 1) in each group be divided into：55 parts of wood-fibred, 12 parts of bamboo fibre, 27 parts of magnesia, chlorination
5 parts of magnesium, 6 parts of adhesive, 0.2 part of tourmaline powder.
In one embodiment：The step 1) in each group be divided into：45 parts of wood-fibred, 18 parts of bamboo fibre, 20 parts of magnesia, chlorination
7 parts of magnesium, 4 parts of adhesive, 0.05 part of tourmaline powder.
In one embodiment：The wood-fibred is flat or graininess, and the length of flat wood-fibred is 0.5~10mm, and width is
10~50 μm, thickness is no more than 10 μm；The bamboo fibre is flat, and its length is 5~20mm, and width is 5~30 μm,
Thickness is no more than 10 μm.
In one embodiment：The adhesive is plant albumin glue adhesive.
The two of the technical solution adopted for the present invention to solve the technical problems are：
A kind of bamboo and woods fiber plate, the bamboo and woods fiber plate according to the mass fraction, including 45~55 parts of wood-fibred, bamboo fibre 12~18
Part, 20~27 parts of magnesia, 5~7 parts of magnesium chloride, 4~6 parts of adhesive, 0.05~0.2 part of tourmaline powder；The wood-fibred
For flat or graininess, the length of flat wood-fibred is 0.5~10mm, and width is 10~50 μm, and thickness is no more than 10 μm；
The bamboo fibre is flat, and its length is 5~20mm, and width is 5~30 μm, and thickness is no more than 10 μm；It is described gluing
Agent is plant albumin glue adhesive；The bamboo and woods fiber plate density is 880~920kg/m3, water content is not higher than 8%；Fire-protection rating B1
More than level, expansion rate of water absorption is not higher than 2 ‰.
The technical program is compared with background technology, and it has the following advantages that：
The bamboo and woods fiber plate of the present invention, substitutes wood-fibred and bamboo fibre using the part such as magnesia and magnesium chloride, reduces bamboo wood resources
Consumption, be conducive to environmental protection；Adhesive uses the plant albumin glue adhesive of nonhazardous, it is to avoid the harmful substance such as formaldehyde, phenol
Release, it is nonpoisonous and tasteless, it is nonirritant, it is safer；Tourmaline composition is additionally added, sustainable release anion can not only
Air is purified, dedusting, taste removal, be also advantageous for user physically and mentally healthy；Cooperated by each component, obtained bamboo and wood
Fiberboard density is 880~920kg/m3, water content is not higher than 8%；More than B1 grades of fire-protection rating, expansion rate of water absorption is not higher than 2 ‰,
Good properties, machinability is good；And required equipment simple economy, preparation technology is easy, and cost is low, and energy consumption is small；Suitable for building
The multiple fields such as material, ornament materials, application prospect is extensive.
Embodiment
Present disclosure is illustrated below by embodiment：
Embodiment 1
A kind of bamboo and woods fiber plate, its according to the mass fraction, including 50 parts of wood-fibred, 15 parts of bamboo fibre, 24 parts of magnesia, chlorine
Change 6 parts of magnesium, 5 parts of adhesive, 0.1 part of tourmaline powder；It is prepared by the following method：
1) following each component according to the mass fraction, is weighed：Wood-fibred 50kg, bamboo fibre 15kg, magnesia 24kg, magnesium chloride
6kg, adhesive 5kg, tourmaline powder 0.1kg；The wood-fibred is flat wood-fibred, and its length is 0.5~10mm, wide
Spend for 10~50 μm, thickness is no more than 10 μm；The bamboo fibre is flat bamboo fibre, and its length is 5~20mm, width
For 5~30 μm, thickness is no more than 10 μm；The adhesive is plant albumin glue adhesive, such as soybean albumen adhesive, wheat
Protein adhesive etc.；
2) above-mentioned wood-fibred and bamboo fibre are broken into fine powder, uniform mixing, drying to water content is not higher than 10%；
3) in step 2) above-mentioned magnesia and magnesium chloride are added in obtained mixture, uniform mixing；
4) in step 3) above-mentioned adhesive is added in obtained mixture, above-mentioned tourmaline powder is added immediately after, is well mixed；
5) by step 4) obtained mixture is placed in 110 DEG C, under 500 tons of pressure, and 25min is press-formed, the bamboo and wood is produced
Fiberboard, density is 900kg/m, water content 7.2%；More than B1 grades of fire-protection rating, expansion rate of water absorption 1.5 ‰.
Embodiment 2
A kind of bamboo and woods fiber plate, its according to the mass fraction, including 48 parts of wood-fibred, 16 parts of bamboo fibre, 22 parts of magnesia, chlorine
Change 6 parts of magnesium, 5 parts of adhesive, 0.08 part of tourmaline powder；It is prepared by the following method：
1) following each component according to the mass fraction, is weighed：Wood-fibred 48kg, bamboo fibre 16kg, magnesia 22kg, magnesium chloride
6kg, adhesive 5kg, tourmaline powder 0.08kg；The wood-fibred is graininess；The bamboo fibre is flat bamboo fibre, its
Length is 5~20mm, and width is 5~30 μm, and thickness is no more than 10 μm；The adhesive is plant albumin glue adhesive, example
Such as soybean albumen adhesive, wheat gluten adhesive；
2) above-mentioned wood-fibred and bamboo fibre are broken into fine powder, uniform mixing, drying to water content is not higher than 10%；
3) in step 2) above-mentioned magnesia and magnesium chloride are added in obtained mixture, uniform mixing；
4) in step 3) above-mentioned adhesive is added in obtained mixture, above-mentioned tourmaline powder is added immediately after, is well mixed；
5) by step 4) obtained mixture is placed in 110 DEG C, under 500 tons of pressure, and 25min is press-formed, the bamboo and wood is produced
Fiberboard, density is 893kg/m, water content 7.6%；More than B1 grades of fire-protection rating, expansion rate of water absorption 1.8 ‰.
Embodiment 3
A kind of bamboo and woods fiber plate, its according to the mass fraction, including 53 parts of wood-fibred, 13 parts of bamboo fibre, 26 parts of magnesia, chlorine
Change 5.5 parts of magnesium, 5.5 parts of adhesive, 0.15 part of tourmaline powder；It is prepared by the following method：
1) following each component according to the mass fraction, is weighed：Wood-fibred 53kg, bamboo fibre 13kg, magnesia 26kg, magnesium chloride
5.5kg, adhesive 5.5kg, tourmaline powder 0.15kg；The wood-fibred is flat wood-fibred, and its length is 0.5~10mm,
Width is 10~50 μm, and thickness is no more than 10 μm；The bamboo fibre is flat bamboo fibre, and its length is 5~20mm, wide
Spend for 5~30 μm, thickness is no more than 10 μm；The adhesive is plant albumin glue adhesive, such as soybean albumen adhesive, small
Aleuronat adhesive etc.；
2) above-mentioned wood-fibred and bamboo fibre are broken into fine powder, uniform mixing, drying to water content is not higher than 10%；
3) in step 2) above-mentioned magnesia and magnesium chloride are added in obtained mixture, uniform mixing；
4) in step 3) above-mentioned adhesive is added in obtained mixture, above-mentioned tourmaline powder is added immediately after, is well mixed；
5) by step 4) obtained mixture is placed in 110 DEG C, under 500 tons of pressure, and 25min is press-formed, the bamboo and wood is produced
Fiberboard, density is 905kg/m, water content 7.3%；More than B1 grades of fire-protection rating, expansion rate of water absorption 1.9 ‰.
Embodiment 4
A kind of bamboo and woods fiber plate, its according to the mass fraction, including 46 parts of wood-fibred, 17 parts of bamboo fibre, 21 parts of magnesia, chlorine
Change 6.5 parts of magnesium, 4.5 parts of adhesive, 0.1 part of tourmaline powder；It is prepared by the following method：
1) following each component according to the mass fraction, is weighed：Wood-fibred 46kg, bamboo fibre 17kg, magnesia 21kg, magnesium chloride
6.5kg, adhesive 4.5kg, tourmaline powder 0.1kg；The wood-fibred is flat wood-fibred, and its length is 0.5~10mm,
Width is 10~50 μm, and thickness is no more than 10 μm；The bamboo fibre is flat bamboo fibre, and its length is 5~20mm, wide
Spend for 5~30 μm, thickness is no more than 10 μm；The adhesive is plant albumin glue adhesive, such as soybean albumen adhesive, small
Aleuronat adhesive etc.；
2) above-mentioned wood-fibred and bamboo fibre are broken into fine powder, uniform mixing, drying to water content is not higher than 10%；
3) in step 2) above-mentioned magnesia and magnesium chloride are added in obtained mixture, uniform mixing；
4) in step 3) above-mentioned adhesive is added in obtained mixture, above-mentioned tourmaline powder is added immediately after, is well mixed；
5) by step 4) obtained mixture is placed in 110 DEG C, under 500 tons of pressure, and 25min is press-formed, the bamboo and wood is produced
Fiberboard, density is 908kg/m, water content 7.7%；More than B1 grades of fire-protection rating, expansion rate of water absorption 1.7 ‰.
Embodiment 5
A kind of bamboo and woods fiber plate, its according to the mass fraction, including 55 parts of wood-fibred, 12 parts of bamboo fibre, 27 parts of magnesia, chlorine
Change 5 parts of magnesium, 6 parts of adhesive, 0.2 part of tourmaline powder；It is prepared by the following method：
1) following each component according to the mass fraction, is weighed：Wood-fibred 55kg, bamboo fibre 12kg, magnesia 27kg, magnesium chloride
5kg, adhesive 6kg, tourmaline powder 0.2kg；The wood-fibred is graininess；The bamboo fibre is flat bamboo fibre, its
Length is 5~20mm, and width is 5~30 μm, and thickness is no more than 10 μm；The adhesive is plant albumin glue adhesive, example
Such as soybean albumen adhesive, wheat gluten adhesive；
2) above-mentioned wood-fibred and bamboo fibre are broken into fine powder, uniform mixing, drying to water content is not higher than 10%；
3) in step 2) above-mentioned magnesia and magnesium chloride are added in obtained mixture, uniform mixing；
4) in step 3) above-mentioned adhesive is added in obtained mixture, above-mentioned tourmaline powder is added immediately after, is well mixed；
5) by step 4) obtained mixture is placed in 110 DEG C, under 500 tons of pressure, and 25min is press-formed, the bamboo and wood is produced
Fiberboard, density is 882kg/m, water content 6.9%；More than B1 grades of fire-protection rating, expansion rate of water absorption 1.8 ‰.
Embodiment 6
A kind of bamboo and woods fiber plate, its according to the mass fraction, including 45 parts of wood-fibred, 18 parts of bamboo fibre, 20 parts of magnesia, chlorine
Change 7 parts of magnesium, 4 parts of adhesive, 0.05 part of tourmaline powder；It is prepared by the following method：
1) following each component according to the mass fraction, is weighed：Wood-fibred 45kg, bamboo fibre 18kg, magnesia 20kg, magnesium chloride
7kg, adhesive 4kg, tourmaline powder 0.05kg；The wood-fibred is flat wood-fibred, and its length is 0.5~10mm, wide
Spend for 10~50 μm, thickness is no more than 10 μm；The bamboo fibre is flat bamboo fibre, and its length is 5~20mm, width
For 5~30 μm, thickness is no more than 10 μm；The adhesive is plant albumin glue adhesive, such as soybean albumen adhesive, wheat
Protein adhesive etc.；
2) above-mentioned wood-fibred and bamboo fibre are broken into fine powder, uniform mixing, drying to water content is not higher than 10%；
3) in step 2) above-mentioned magnesia and magnesium chloride are added in obtained mixture, uniform mixing；
4) in step 3) above-mentioned adhesive is added in obtained mixture, above-mentioned tourmaline powder is added immediately after, is well mixed；
5) by step 4) obtained mixture is placed in 110 DEG C, under 500 tons of pressure, and 25min is press-formed, the bamboo and wood is produced
Fiberboard, density is 917kg/m, water content 7.2%；More than B1 grades of fire-protection rating, expansion rate of water absorption 1.5 ‰.
Skilled person will appreciate that, when the technical parameter of the present invention changes in following scope, it is contemplated that obtain and above-mentioned reality
Apply the same or like technique effect of example：
A kind of bamboo and woods fiber plate, the bamboo and woods fiber plate according to the mass fraction, including 45~55 parts of wood-fibred, bamboo fibre 12~18
Part, 20~27 parts of magnesia, 5~7 parts of magnesium chloride, 4~6 parts of adhesive, 0.05~0.2 part of tourmaline powder.
The preparation method of above-mentioned bamboo and woods fiber plate includes：
1) following each component according to the mass fraction, is weighed：45~55 parts of wood-fibred, 12~18 parts of bamboo fibre, magnesia 20~
27 parts, 5~7 parts of magnesium chloride, 4~6 parts of adhesive, 0.05~0.2 part of tourmaline powder；
2) above-mentioned wood-fibred is uniformly mixed with bamboo fibre, drying to water content is not higher than 10%；
3) in step 2) above-mentioned magnesia and magnesium chloride are added in obtained mixture, uniform mixing；
4) in step 3) above-mentioned adhesive is added in obtained mixture, above-mentioned tourmaline powder is added immediately after, is well mixed；
5) by step 4) obtained mixture is placed in 100~120 DEG C, under 450~550 tons of pressure, is press-formed 20~30min,
The bamboo and woods fiber plate is produced, density is 880~920kg/m3, water content is not higher than 8%；More than B1 grades of fire-protection rating, water suction
Expansion rate is not higher than 2 ‰.
The wood-fibred is flat or graininess, and the length of flat wood-fibred is 0.5~10mm, and width is 10~50 μm,
Thickness is no more than 10 μm；The bamboo fibre is flat, and its length is 5~20mm, and width is 5~30 μm, and thickness does not surpass
Cross 10 μm.
The adhesive is plant albumin glue adhesive.
It is described above, only present pre-ferred embodiments, therefore the scope that the present invention is implemented can not be limited according to this, i.e., according to the present invention
The equivalent changes and modifications that the scope of the claims and description are made, all should still belong in the range of the present invention covers.
Claims (10)
1. a kind of preparation method of bamboo and woods fiber plate, it is characterised in that：Including：
1) following each component according to the mass fraction, is weighed：45~55 parts of wood-fibred, 12~18 parts of bamboo fibre, magnesia 20~
27 parts, 5~7 parts of magnesium chloride, 4~6 parts of adhesive, 0.05~0.2 part of tourmaline powder；
2) above-mentioned wood-fibred is uniformly mixed with bamboo fibre, drying to water content is not higher than 10%；
3) in step 2) above-mentioned magnesia and magnesium chloride are added in obtained mixture, uniform mixing；
4) in step 3) above-mentioned adhesive is added in obtained mixture, above-mentioned tourmaline powder is added immediately after, and mixing is equal
It is even；
5) by step 4) obtained mixture is placed in 100~120 DEG C, under 450~550 tons of pressure, is press-formed 20~30min,
The bamboo and woods fiber plate is produced, density is 880~920kg/m3, water content is not higher than 8%；More than B1 grades of fire-protection rating, inhales
Water expansion rate is not higher than 2 ‰.
2. the preparation method of bamboo and woods fiber plate according to claim 1, it is characterised in that：The step 1) in each component
For：50 parts of wood-fibred, 15 parts of bamboo fibre, 24 parts of magnesia, 6 parts of magnesium chloride, 5 parts of adhesive, tourmaline powder 0.1
Part.
3. the preparation method of bamboo and woods fiber plate according to claim 1, it is characterised in that：The step 1) in each component
For：48 parts of wood-fibred, 16 parts of bamboo fibre, 22 parts of magnesia, 6 parts of magnesium chloride, 5 parts of adhesive, tourmaline powder 0.08
Part.
4. the preparation method of bamboo and woods fiber plate according to claim 1, it is characterised in that：The step 1) in each component
For：53 parts of wood-fibred, 13 parts of bamboo fibre, 26 parts of magnesia, 5.5 parts of magnesium chloride, 5.5 parts of adhesive, tourmaline powder
0.15 part.
5. the preparation method of bamboo and woods fiber plate according to claim 1, it is characterised in that：The step 1) in each component
For：46 parts of wood-fibred, 17 parts of bamboo fibre, 21 parts of magnesia, 6.5 parts of magnesium chloride, 4.5 parts of adhesive, tourmaline powder
0.1 part.
6. the preparation method of bamboo and woods fiber plate according to claim 1, it is characterised in that：The step 1) in each component
For：55 parts of wood-fibred, 12 parts of bamboo fibre, 27 parts of magnesia, 5 parts of magnesium chloride, 6 parts of adhesive, tourmaline powder 0.2
Part.
7. the preparation method of bamboo and woods fiber plate according to claim 1, it is characterised in that：The step 1) in each component
For：45 parts of wood-fibred, 18 parts of bamboo fibre, 20 parts of magnesia, 7 parts of magnesium chloride, 4 parts of adhesive, tourmaline powder 0.05
Part.
8. the preparation method of bamboo and woods fiber plate according to any one of claim 1 to 7, it is characterised in that：The wood is fine
Tie up as flat or graininess, the length of flat wood-fibred is 0.5~10mm, and width is 10~50 μm, and thickness is no more than
10μm；The bamboo fibre is flat, and its length is 5~20mm, and width is 5~30 μm, and thickness is no more than 10 μm.
9. the preparation method of bamboo and woods fiber plate according to any one of claim 1 to 7, it is characterised in that：It is described gluing
Agent is plant albumin glue adhesive.
10. a kind of bamboo and woods fiber plate, it is characterised in that：The bamboo and woods fiber plate according to the mass fraction, including wood-fibred 45~55
Part, 12~18 parts of bamboo fibre, 20~27 parts of magnesia, 5~7 parts of magnesium chloride, 4~6 parts of adhesive, tourmaline powder 0.05~
0.2 part；The wood-fibred is flat or graininess, and the length of flat wood-fibred is 0.5~10mm, and width is 10~50
μm, thickness is no more than 10 μm；The bamboo fibre is flat, and its length is 5~20mm, and width is 5~30 μm, thick
Degree is no more than 10 μm；The adhesive is plant albumin glue adhesive；The bamboo and woods fiber plate density is 880~920kg/m3, contain
Water is not higher than 8%；More than B1 grades of fire-protection rating, expansion rate of water absorption is not higher than 2 ‰.