CN108611855A - A kind of antibacterial rapid-curing cutback clothing fabric preparation method - Google Patents
A kind of antibacterial rapid-curing cutback clothing fabric preparation method Download PDFInfo
- Publication number
- CN108611855A CN108611855A CN201810526729.0A CN201810526729A CN108611855A CN 108611855 A CN108611855 A CN 108611855A CN 201810526729 A CN201810526729 A CN 201810526729A CN 108611855 A CN108611855 A CN 108611855A
- Authority
- CN
- China
- Prior art keywords
- parts
- curing cutback
- fabric
- antibacterial
- rapid
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Withdrawn
Abstract
A kind of antibacterial rapid-curing cutback clothing fabric preparation method, includes the following steps：（1）By parts by weight, which be 20 30 parts of polyester filament fibers, 10 20 parts of flax fibers, 5 10 parts of cotton fibers are blended is made fabric；（2）By parts by weight be after 20 28 parts of chitins, 10 18 parts of chitosans, 6 10 parts of polyvinylpyrrolidones, 37 parts of softening agents, 6 10 parts of polyvinyl alcohol emulsions, 30 36 parts of deionized waters are uniformly mixed and to adjust its pH value be 5.8 6.4 to get antimicrobial form hydrophilic finiss liquid；（3）It is 60 80 DEG C to maintain temperature, will walk above-mentioned fabric and impregnate 30 40min in above-mentioned antimicrobial form hydrophilic finiss liquid, then after being dehydrated, and dries 20 25min at a temperature of 90 95 DEG C, obtains the antibacterial rapid-curing cutback clothing fabric.Beneficial effects of the present invention are：（1）Antibacterial rapid-curing cutback clothing fabric made from the preparation method not only have the effect of it is good perspire, also there is good antibacterial effect, while durable antibacterial effect is long；（2）The preparation method is simple, at low cost, pollution-free, to producers without noxious odor.
Description
Technical field
The invention belongs to outdoor wear production fields, and in particular to a kind of antibacterial rapid-curing cutback clothing fabric preparation method.
Background technology
Outdoor wear can be mainly divided into three kinds of underwear, heat preservation layer and coat.Outdoor environment is complicated and changeable, severe to resist
The injury of Environmental insults protects body heat not scattered and disappeared and be quickly discharged generated sweat when movement, is climbing the mountain, climbing
When rock and other outdoor sports, it should accomplish to be layered dressing.So-called layering dressing refers to wearing different materials in movement outdoors
The clothes of matter, to adapt to the various Changes in weather in field to being influenced caused by human body, for example (,) it is clothing of charging, fleece clothing, warming
Clothing, sun-proof clothing, rapid-curing cutback clothing etc..
It climbs the mountain, the coat of outdoor sports generally refers to the clothes of charge garment, combat trousers, parka etc, main work(
It can be waterproof, windproof, anti-tear.With the development of science and technology, to have developed the waterproofs such as GORE-TEX, FIRST-TEX saturating for clothing of charging
The fabric of gas.Its principle is under filminess, and the hole diameter on surface is exactly between hydrone and steam molecule, steam
Molecule can pass through, and hydrone is then blocked, to achieve the effect that waterproof and breathable.
Rapid-curing cutback clothing is exactly the dry faster clothes of ratio, compared with the clothing of hair quality or cotton, in the identical feelings of external condition
Under condition, it is easier to moisture evaporation be gone out, do faster.It is not that sweat but is promptly transferred to by sweat absorption
The surface of clothes, by air circulation by evaporation of perspiration, to achieve the purpose that rapid-curing cutback, the rate of drying ratio of general rapid-curing cutback clothing
Cotton fabric wants fast 50%.
Rapid-curing cutback clothing is that the requirement of outdoor use environment is answered to generate.Under normal circumstances, it can be put on when spring and summer replaces
Rapid-curing cutback clothing, at this time they facilitate than thick and heavy charge garment, it is much practical.The major function of rapid-curing cutback clothing is quickly to arrange
Sweat, that is, the sweat gone out on skin absorbed rapidly, is spread, and evaporation rate is accelerated by enlarged-area as far as possible.
Ordinary movement dress is worn, takes exercise and is transferred to resting state after perspiring at once, it can be sick because of the variation of human body temperature.
And can to dissipate wet and warmth retention property good for rapid-curing cutback clothing, is conducive to keep dry skin salubrious.It is important to mention when doing outdoor sports, speed
Drying can play better effect at windproof, rain-proof, damp proof aspect.
Quick-drying shell fabric using microporous membrane principle is extremely common on the market.Its rapid-curing cutback principle is situated between using micropore size
Thin film between hydrone, air molecule maximum gauge and the minimum diameter of water droplet molecule, then again by film with it is outer
Layer fabric is compound, and then just have the effect of waterproof and breathable this is somewhat similar to the principle of GORE-TEX for fabric, using this original
The fabric of reason, what is played a role is the film that carries micropore, it had both played the role of spill resistant and has also acted as ventilative effect, no
Pipe is to utilize microporous membrane principle or other principle, is all the different chemical fiber plus material of fiber in fact.
Due to perspiring best results when rapid-curing cutback clothing is personal to be worn, so being also easy that bacterium, existing rapid-curing cutback clothing can be grown
It is less desirable in antibiosis effect although relatively good in terms of perspiring effect.
Invention content
Purpose of the invention is to overcome the shortcomings in the prior art, provides a kind of antibacterial rapid-curing cutback clothing fabric preparation side
Method.
In order to solve the above technical problems, the technical scheme is that：
A kind of antibacterial rapid-curing cutback clothing fabric preparation method, includes the following steps：（1）It is that 20-30 parts of polyester filaments are fine by parts by weight
Dimension, 10-20 parts of flax fibers, 5-10 parts of cotton fibers are blended that fabric is made；（2）It is 20-28 parts of chitins, 10- by parts by weight
18 parts of chitosans, 6-10 parts of polyvinylpyrrolidones, 3-7 parts of softening agents, 6-10 parts of polyvinyl alcohol emulsions, 30-36 parts of deionizations
After water is uniformly mixed and adjust its pH value be 5.8-6.4 to get antimicrobial form hydrophilic finiss liquid；（3）Maintenance temperature is 60-
80 DEG C, by step（1）The fabric of gained is in step（2）30-40min is impregnated in the antimicrobial form hydrophilic finiss liquid of middle gained, then is taken off
After water, 20-25min is dried at a temperature of 90-95 DEG C, obtains the antibacterial rapid-curing cutback clothing fabric.
Preferably, the softening agent is hydroxypropyl chitosan.
Beneficial effects of the present invention are：（1）Antibacterial rapid-curing cutback clothing fabric made from the preparation method not only has good row
The effect of sweat also has good antibacterial effect, while durable antibacterial effect is long；（2）The preparation method is simple, at low cost,
It is pollution-free, to producers without noxious odor.
Specific implementation mode
The effect of to make to structure feature of the invention and being reached, has a better understanding and awareness, to preferable
Embodiment cooperation detailed description, is described as follows：
Embodiment 1
A kind of antibacterial rapid-curing cutback clothing fabric preparation method, includes the following steps：（1）Be 20 parts of polyester filament fibers by parts by weight,
10 parts of flax fibers, 5 parts of cotton fibers are blended that fabric is made；（2）By parts by weight be 20 parts of chitins, 10 parts of chitosans, 6 parts it is poly-
After vinylpyrrolidone, 3 parts of softening agents, 6 parts of polyvinyl alcohol emulsions, 30 parts of deionized waters are uniformly mixed and adjust its PH
Value is for 5.8 to get antimicrobial form hydrophilic finiss liquid；（3）It is 60 DEG C to maintain temperature, by step（1）The fabric of gained is in step（2）In
30min is impregnated in the antimicrobial form hydrophilic finiss liquid of gained, then after being dehydrated, 20min is dried at a temperature of 90 DEG C, obtains the antibacterial speed
Drying fabric.
Wherein, the softening agent is hydroxypropyl chitosan.
Embodiment 2
A kind of antibacterial rapid-curing cutback clothing fabric preparation method, includes the following steps：（1）Be 30 parts of polyester filament fibers by parts by weight,
20 parts of flax fibers, 10 parts of cotton fibers are blended that fabric is made；（2）By parts by weight be 28 parts of chitins, 18 parts of chitosans, 10 parts
After polyvinylpyrrolidone, 7 parts of softening agents, 10 parts of polyvinyl alcohol emulsions, 36 parts of deionized waters are uniformly mixed and adjust
Its pH value is 6.4 to get antimicrobial form hydrophilic finiss liquid；（3）It is 80 DEG C to maintain temperature, by step（1）The fabric of gained is in step
（2）40min is impregnated in the antimicrobial form hydrophilic finiss liquid of middle gained, then after being dehydrated, 25min is dried at a temperature of 95 DEG C, obtained described
Antibacterial rapid-curing cutback clothing fabric.
Wherein, the softening agent is hydroxypropyl chitosan.
Embodiment 3
A kind of antibacterial rapid-curing cutback clothing fabric preparation method, includes the following steps：（1）Be 25 parts of polyester filament fibers by parts by weight,
15 parts of flax fibers, 7 parts of cotton fibers are blended that fabric is made；（2）By parts by weight be 24 parts of chitins, 14 parts of chitosans, 8 parts it is poly-
After vinylpyrrolidone, 5 parts of softening agents, 8 parts of polyvinyl alcohol emulsions, 33 parts of deionized waters are uniformly mixed and adjust its PH
Value is for 6.3 to get antimicrobial form hydrophilic finiss liquid；（3）It is 70 DEG C to maintain temperature, by step（1）The fabric of gained is in step（2）In
35min is impregnated in the antimicrobial form hydrophilic finiss liquid of gained, then after being dehydrated, 22min is dried at a temperature of 93 DEG C, obtains the antibacterial speed
Drying fabric.
Wherein, the softening agent is hydroxypropyl chitosan.
Beneficial effects of the present invention are：（1）Antibacterial rapid-curing cutback clothing fabric made from the preparation method not only has good row
The effect of sweat also has good antibacterial effect, while durable antibacterial effect is long；（2）The preparation method is simple, at low cost,
It is pollution-free, to producers without noxious odor.
The basic principles, main features and advantages of the present invention have been shown and described above.The technology of the industry
Personnel are it should be appreciated that the present invention is not limited to the above embodiments, and what is described in the above embodiment and the description is only the present invention
Principle, various changes and improvements may be made to the invention without departing from the spirit and scope of the present invention, these variation and
Improvement is both fallen in the range of claimed invention.The present invention claims protection domain by appended claims and its
Equivalent defines.
Claims (2)
1. a kind of antibacterial rapid-curing cutback clothing fabric preparation method, it is characterised in that：Include the following steps：（1）It is 20-30 by parts by weight
Part polyester filament fiber, 10-20 parts of flax fibers, 5-10 parts of cotton fibers are blended that fabric is made；（2）It is 20-28 by parts by weight
Part chitin, 10-18 parts of chitosans, 6-10 parts of polyvinylpyrrolidones, 3-7 parts of softening agents, 6-10 parts of polyvinyl alcohol emulsions,
After 30-36 parts of deionized waters are uniformly mixed and adjust its pH value be 5.8-6.4 to get antimicrobial form hydrophilic finiss liquid；（3）
It is 60-80 DEG C to maintain temperature, by step（1）The fabric of gained is in step（2）It is impregnated in the antimicrobial form hydrophilic finiss liquid of middle gained
30-40min, then after being dehydrated, dry 20-25min at a temperature of 90-95 DEG C, obtain the antibacterial rapid-curing cutback clothing fabric.
2. a kind of antibacterial rapid-curing cutback clothing fabric preparation method according to claim 1, it is characterised in that：The softening agent is hydroxyl
Propyl chitosan.