CN107603722A - A kind of cutting fluid and preparation method thereof - Google Patents
A kind of cutting fluid and preparation method thereof Download PDFInfo
- Publication number
- CN107603722A CN107603722A CN201711004801.5A CN201711004801A CN107603722A CN 107603722 A CN107603722 A CN 107603722A CN 201711004801 A CN201711004801 A CN 201711004801A CN 107603722 A CN107603722 A CN 107603722A
- Authority
- CN
- China
- Prior art keywords
- parts
- cutting fluid
- water
- raw material
- defoamer
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The present invention relates to cutting fluid field, more particularly to a kind of cylinder jacket lathe machining cutting fluid and preparation method thereof, it is made up of the raw material of following parts by weight：35 45 parts of water, 15 25 parts of castor oil, 37 parts of polysorbas20,25 parts of defoamer, 37 parts of BTA, 14 parts of preservative, 10 25 parts of octyl phenol, 14 parts of ethylenediamine tetra-acetic acid, 37 parts of polyethylene glycol 400 bilaurate, 37 parts of trihydroxy ethylamine oleate soap；The technique includes electrical heating reaction, water circulation cooling and precipitation step, the cutting fluid and integrates lubrication, antirust and clean, and greasy property is good, rustless property is high, without stickum, cleaning performance is good, while not grease clothing, do not injure human muscle and skin, environmental pollution is small, and the preparation method step is simple, easy to operate, obtained cutting fluid performance is optimal, and practicality is stronger.
Description
Technical field
The present invention relates to cutting fluid field, more particularly to a kind of cylinder jacket lathe machining cutting fluid and its making side
Method.
Background technology
Usually require to use cutting fluid when machining cylinder jacket lathe and be lubricated effect, but in actual processing mistake
Journey, cutting fluid only serve lubrication, and cylinder jacket lathe machine also needs to add antirust agent progress antirust, in addition, existing cutting
Liquid poorly water-soluble, mostly oil-soluble, easy grease clothing, contain in cutting fluid with corrosive material, easily injure human body flesh
Meat, cleaning is difficult, and recovery during factory's blowdown to cutting fluid is difficult, complicated, and cost is high, and because containing cutting fluid in blowdown water
Easily environment is polluted.
The content of the invention
For cutting fluid rust-preventing characteristic present in prior art is poor, cleaning is difficult, easy grease clothing, blowdown water is easily right
The defects of environment pollutes, and a kind of cutting fluid and preparation method thereof is provided, the cutting fluid collects lubrication, antirust and cleaned in one
Body, greasy property is good, and rustless property is high, and without stickum, cleaning performance is good, while not grease clothing, does not injure human body flesh
Meat and skin, environmental pollution is small, and the preparation method step is simple, easy to operate, and obtained cutting fluid performance is optimal, practicality compared with
By force.
The technical proposal of the invention is realized in this way：A kind of cutting fluid, it is made up of the raw material of following parts by weight：Water
35-45 parts, castor oil 15-25 parts, Tween-20 3-7 parts, defoamer 2-5 parts, BTA 3-7 parts, preservative 1-4 parts,
The 2-5 parts of octyl phenol -10, ethylenediamine tetra-acetic acid 1-4 parts, polyethylene glycol 400 bilaurate 3-7 parts, triethanolamine oleate
Soap 3-7 parts.
Preferably, the cutting fluid is made up of the raw material of following parts by weight：Water 38-42 parts, castor oil 17-22 parts, tween-
20 4-6 parts, defoamer 3-4 parts, BTA 4-6 parts, preservative 2-3 parts, the 3-4 parts of octyl phenol -10, ethylenediamine tetraacetic
Acetic acid 2-3 parts, polyethylene glycol 400 bilaurate 4-6 parts, trihydroxy ethylamine oleate soap 4-6 parts.
Preferably, the cutting fluid is made up of the raw material of following parts by weight：40 parts of water, 20 parts of castor oil, Tween-20 5
Part, 3 parts of defoamer, 5 parts of BTA, 3 parts of preservative, -10 3 parts of octyl phenol, 2 parts of ethylenediamine tetra-acetic acid, poly- second two
5 parts of 400 bilaurate of alcohol, 5 parts of trihydroxy ethylamine oleate soap.
A kind of method for preparing cutting fluid, comprises the following steps：
（1）Weigh raw material
Following raw material is weighed by following parts by weight：Water 35-45 parts, castor oil 15-25 parts, Tween-20 3-7 parts, defoamer 2-
5 parts, BTA 3-7 parts, preservative 1-4 parts, the 2-5 parts of octyl phenol -10, ethylenediamine tetra-acetic acid 1-4 parts, poly- second two
The bilaurate 3-7 parts of alcohol 400, trihydroxy ethylamine oleate soap 3-7 parts；
（2）By step（1）In the water that weighs insert in electrical heating retort, by electrical heating retort electrified regulation to 75-85 DEG C,
Sequentially add step（1）In weigh castor oil, Tween-20, defoamer, BTA, preservative, octyl phenol -10,
Ethylenediamine tetra-acetic acid, polyethylene glycol 400 bilaurate and trihydroxy ethylamine oleate soap, it is stirred while addition, stirring speed
Spend for 100-200r/min, raw material is decomposed in the presence of catalyst, until temperature stop when reaching 125-135 DEG C plus
Heat, heating continue to stir 25-35min after stopping；
（3）By step（2）The material obtained after middle reaction is delivered to water circulation cooling tank, opens the cooling water of water circulation cooling tank
Being cooled down, and start to stir, mixing speed is 100-200 r/min, the material in water circulation cooling tank is cooled to normal temperature,
Stop stirring, the material after cooling is delivered to finished product settling tank, material stands 2-3 months in finished product settling tank.
Preferably, step（2）In electrical heating retort be powered after heating-up temperature be 80 DEG C.
Preferably, step（2）Middle temperature stops heating when reaching 130 DEG C, heating continues to stir 30min after stopping, i.e., anti-
It should complete.
The present invention has advantages below：1st, cutting fluid of the invention integrates lubricity, rustless property and clean-up performance；
2nd, cutting fluid lubrication performance of the invention is good, when the cutting fluid using the present invention machines to cylinder jacket lathe, that is, saves cutter head,
And the workpiece cleanliness processed and brightness are high；3rd, cutting fluid good antirust property of the invention is longer than ancient antirust time；
4th, cutting fluid cleaning performance of the invention is good, and cutting fluid is free of stickum, and working fluid has played cleaning and made in process of production
With making workpiece clean, bright；5th, cutting fluid of the invention not grease clothing, does not injure human muscle and skin, of the invention cuts
Cutting the raw material used in liquid does not have the corrosive compound of any band, harmless, environmentally safe；6th, making of the invention
Technique includes the steps such as electrical heating reaction, water circulation cooling and sedimentation, and technique is simple, easy to operate, obtained cutting fluid performance
Most preferably.
Tween-20, it is a kind of surfactant, is yellow or amber clear and bright oily liquids, there is special foul smell
With faint bitter taste.Relative density 1.01, boiling point>100 DEG C, 321 DEG C of flash-point, refractive index 1.472, viscosity (25 DEG C) 0.25~
0.40Pa·s.Contain more hydrophilic radical in molecule, can be miscible with water, ethanol, methanol and ethyl acetate, insoluble in liquid
Shape paraffin, expressed oi and ligroin, 1 part of this product are dissolved in 130 portions of cottonseed oils and 200 parts of toluene, 5% aqueous solution pH5~7.
HLB value is 16.7.It is a kind of macromolecular, existing hydrophilic part on molecule, has the part of oleophylic again, so can promote plant
The undissolvable macromolecular in water is absorbed, can also help moisture through some containing the high biomembrane of fat.Conventional nonionic
Detergent.For Tween 80 and the double mixing for removing water sorbitol monooleate of a part of polyoxyethylene
Thing.
Octyl phenol -10, i.e. OP-10, CAS numberings are 9041-29-6, and a kind of industrial chemicals, composition is alkyl phenol polyoxy second
Alkene ether, there is excellent level dyeing, emulsification, wetting, diffusion, antistatic behaviour, outward appearance：White and milky pastel, dissolubility：
It is soluble in water, pH value（1% aqueous）：6-7, HLB value：14.5 cloud point：61-67℃.
Polyethylene glycol 400 bilaurate, it is to be formed with polyethylene glycol and laurate esterification, is oil soluble emulsifying agent, it is molten
In a variety of organic solvents such as ethanol, isopropanol, toluene, it is scattered in hot water, there is scattered, emulsification, shading, solubilising, thickening property
Energy.
Tween and diethylamine tetraacethyl are catalyst in the cutting fluid raw material of the present invention, make cutting liquid product by chemical reaction
Main component includes lubrication and the higher material of rustless property.
Embodiment
Embodiments of the present invention are described further with reference to embodiment.
Embodiment 1：A kind of cutting fluid, it is made up of the raw material of following weight：Water 35Kg, the Kg of castor oil 15, Tween-20 3
Kg, the Kg of defoamer 2, the Kg of BTA 3, the Kg of preservative 1, octyl phenol -10 2 Kg, the Kg of ethylenediamine tetra-acetic acid 1,
The Kg of polyethylene glycol 400 bilaurate 3, the Kg of trihydroxy ethylamine oleate soap 3.
A kind of preparation method of cutting fluid, comprises the following steps：
（1）Weigh raw material
Following raw material is weighed by following parts by weight：Water 35Kg, the Kg of castor oil 15, the Kg of Tween-20 3, the Kg of defoamer 2, benzene
And the Kg of triazole 3, the Kg of preservative 1, octyl phenol -10 2 Kg, the Kg of ethylenediamine tetra-acetic acid 1, the bimonthly osmanthus of polyethylene glycol 400
The Kg of acid esters 3, the Kg of trihydroxy ethylamine oleate soap 3；
（2）By step（1）In the water that weighs insert in electrical heating retort, by electrical heating retort electrified regulation to 75 DEG C, according to
Secondary addition step（1）In weigh castor oil, Tween-20, defoamer, BTA, preservative, octyl phenol -10, second
Ethylenediamine tetraacetic acid (EDTA), polyethylene glycol 400 bilaurate and trihydroxy ethylamine oleate soap, it is stirred while addition, mixing speed
For 100r/min, raw material is set to be decomposed in the presence of catalyst, until temperature stops heating when reaching 125 DEG C, heating stops
Continue to stir 25min after only, i.e. reaction is completed；
（3）By step（2）The material obtained after the completion of middle reaction is delivered to water circulation cooling tank, opens the cold of water circulation cooling tank
But water is cooled down, and starts stirring, and mixing speed is 100 r/min, the material in water circulation cooling tank is cooled to normal temperature,
Stop stirring, the material after cooling is delivered to finished product settling tank, material stands 2 months in finished product settling tank.
Embodiment 2：A kind of cutting fluid, it is made up of the raw material of following weight：Water 45Kg, the Kg of castor oil 25, Tween-20 7
Kg, the Kg of defoamer 5, the Kg of BTA 7, the Kg of preservative 4, octyl phenol -10 5 Kg, the Kg of ethylenediamine tetra-acetic acid 4,
The Kg of polyethylene glycol 400 bilaurate 7, the Kg of trihydroxy ethylamine oleate soap 7.
A kind of method for preparing cutting fluid, comprises the following steps：
（1）Weigh raw material
Following raw material is weighed by following parts by weight：Water 45Kg, the Kg of castor oil 25, the Kg of Tween-20 7, the Kg of defoamer 5, benzene
And the Kg of triazole 7, the Kg of preservative 4, octyl phenol -10 5 Kg, the Kg of ethylenediamine tetra-acetic acid 4, the bimonthly osmanthus of polyethylene glycol 400
The Kg of acid esters 7, the Kg of trihydroxy ethylamine oleate soap 7；
（2）By step（1）In the water that weighs insert in electrical heating retort, by electrical heating retort electrified regulation to 85 DEG C, according to
Secondary addition step（1）In weigh castor oil, Tween-20, defoamer, BTA, preservative, octyl phenol -10, second
Ethylenediamine tetraacetic acid (EDTA), polyethylene glycol 400 bilaurate and trihydroxy ethylamine oleate soap, start stirring, mixing speed while addition
For 200r/min, raw material is set to be decomposed in the presence of catalyst, until temperature stops heating when reaching 135 DEG C, heating stops
Continue to stir 35min after only, i.e. reaction is completed；
（3）By step（2）The material obtained after the completion of middle reaction is delivered to water circulation cooling tank, opens the cold of water circulation cooling tank
But water is cooled down, and starts stirring, and mixing speed is 200 r/min, the material in water circulation cooling tank is cooled to normal temperature,
Stop stirring, the material after cooling is delivered to finished product settling tank, material stands 3 months in finished product settling tank.
Embodiment 3：A kind of cutting fluid, it is made up of the raw material of following weight：The Kg of water 35, the Kg of castor oil 25, Tween-20 7
Kg, the Kg of defoamer 2, the Kg of BTA 7, the Kg of preservative 1, octyl phenol -10 5 Kg, the Kg of ethylenediamine tetra-acetic acid 1,
The Kg of polyethylene glycol 400 bilaurate 7, the Kg of trihydroxy ethylamine oleate soap 3；
A kind of method for preparing cutting fluid, comprises the following steps：
（1）Weigh raw material
Following raw material is weighed by following parts by weight：The Kg of water 35, the Kg of castor oil 25, the Kg of Tween-20 7, the Kg of defoamer 2, benzene
And the Kg of triazole 7, the Kg of preservative 1, octyl phenol -10 5 Kg, the Kg of ethylenediamine tetra-acetic acid 1, the bimonthly osmanthus of polyethylene glycol 400
The Kg of acid esters 7, the Kg of trihydroxy ethylamine oleate soap 3；
（2）By step（1）In the water that weighs insert in electrical heating retort, by electrical heating retort electrified regulation to 75 DEG C, according to
Secondary addition step（1）In weigh castor oil, Tween-20, defoamer, BTA, preservative, octyl phenol -10, second
Ethylenediamine tetraacetic acid (EDTA), polyethylene glycol 400 bilaurate and trihydroxy ethylamine oleate soap, start stirring, mixing speed while addition
For 200r/min, raw material is set to be decomposed in the presence of catalyst, until temperature stops heating when reaching 125 DEG C, heating stops
Continue to stir 35min after only, i.e. reaction is completed；
（3）By step（2）The material obtained after the completion of middle reaction is delivered to water circulation cooling tank, opens the cold of water circulation cooling tank
But water is cooled down, and starts stirring, and mixing speed is 100 r/min, the material in water circulation cooling tank is cooled to normal temperature,
Stop stirring, the material after cooling is delivered to finished product settling tank, material stands 3 months in finished product settling tank.
Embodiment 4：A kind of cutting fluid, it is made up of the raw material of following weight：The Kg of water 38, the Kg of castor oil 17, Tween-20 4
Kg, the Kg of defoamer 3, the Kg of BTA 4, the Kg of preservative 2, octyl phenol -10 3 Kg, the Kg of ethylenediamine tetra-acetic acid 2,
The Kg of polyethylene glycol 400 bilaurate 4, the Kg of trihydroxy ethylamine oleate soap 4；
A kind of method for preparing cutting fluid, comprises the following steps：
（1）Weigh raw material
Following raw material is weighed by following parts by weight：The Kg of water 38, the Kg of castor oil 17, the Kg of Tween-20 4, the Kg of defoamer 3, benzene
And the Kg of triazole 4, the Kg of preservative 2, octyl phenol -10 3 Kg, the Kg of ethylenediamine tetra-acetic acid 2, the bimonthly osmanthus of polyethylene glycol 400
The Kg of acid esters 4, the Kg of trihydroxy ethylamine oleate soap 4；
（2）By step（1）In the water that weighs insert in electrical heating retort, by electrical heating retort electrified regulation to 78 DEG C, according to
Secondary addition step（1）In weigh castor oil, Tween-20, defoamer, BTA, preservative, octyl phenol -10, second
Ethylenediamine tetraacetic acid (EDTA), polyethylene glycol 400 bilaurate and trihydroxy ethylamine oleate soap, start stirring, mixing speed while addition
For 120r/min, raw material is set to be decomposed in the presence of catalyst, until temperature stops heating when reaching 128 DEG C, heating stops
Continue to stir 28min after only, i.e. reaction is completed；
（3）By step（2）The material obtained after the completion of middle reaction is delivered to water circulation cooling tank, opens the cold of water circulation cooling tank
But water is cooled down, and starts stirring, and mixing speed is 120 r/min, the material in water circulation cooling tank is cooled to normal temperature,
Stop stirring, the material after cooling is delivered to finished product settling tank, material stands 2 months in finished product settling tank.
Embodiment 5：A kind of cutting fluid, it is made up of the raw material of following weight：The Kg of water 42, the Kg of castor oil 22, Tween-20 6
Kg, the Kg of defoamer 4, the Kg of BTA 6, the Kg of preservative 3, octyl phenol -10 4 Kg, the Kg of ethylenediamine tetra-acetic acid 3,
The Kg of polyethylene glycol 400 bilaurate 6, the Kg of trihydroxy ethylamine oleate soap 6；
A kind of method for preparing cutting fluid, comprises the following steps：
（1）Weigh raw material
Following raw material is weighed by following parts by weight：The Kg of water 42, the Kg of castor oil 22, the Kg of Tween-20 6, the Kg of defoamer 4, benzene
And the Kg of triazole 6, the Kg of preservative 3, octyl phenol -10 4 Kg, the Kg of ethylenediamine tetra-acetic acid 3, the bimonthly osmanthus of polyethylene glycol 400
The Kg of acid esters 6, the Kg of trihydroxy ethylamine oleate soap 6；
（2）By step（1）In the water that weighs insert in electrical heating retort, by electrical heating retort electrified regulation to 82 DEG C, according to
Secondary addition step（1）In weigh castor oil, Tween-20, defoamer, BTA, preservative, octyl phenol -10, second
Ethylenediamine tetraacetic acid (EDTA), polyethylene glycol 400 bilaurate and trihydroxy ethylamine oleate soap, start stirring, mixing speed while addition
For 180r/min, raw material is set to be decomposed in the presence of catalyst, until temperature stops heating when reaching 132 DEG C, heating stops
Continue to stir 32min after only, i.e. reaction is completed；
（3）By step（2）The material obtained after the completion of middle reaction is delivered to water circulation cooling tank, opens the cold of water circulation cooling tank
But water is cooled down, and starts stirring, mixing speed 180r/min, the material in water circulation cooling tank is cooled to normal temperature,
Stop stirring, the material after cooling is delivered to finished product settling tank, material stands 3 months in finished product settling tank.
Embodiment 6：A kind of cutting fluid, it is made up of the raw material of following weight：The Kg of water 38, the Kg of castor oil 22, Tween-20 4
Kg, the Kg of defoamer 4, the Kg of BTA 4, the Kg of preservative 3, octyl phenol -10 3 Kg, the Kg of ethylenediamine tetra-acetic acid 3,
The Kg of polyethylene glycol 400 bilaurate 4, the Kg of trihydroxy ethylamine oleate soap 6；
A kind of method for preparing cutting fluid, comprises the following steps：
（1）Weigh raw material
Following raw material is weighed by following parts by weight：The Kg of water 38, the Kg of castor oil 22, the Kg of Tween-20 4, the Kg of defoamer 4, benzene
And the Kg of triazole 4, the Kg of preservative 3, octyl phenol -10 3 Kg, the Kg of ethylenediamine tetra-acetic acid 3, the bimonthly osmanthus of polyethylene glycol 400
The Kg of acid esters 4, the Kg of trihydroxy ethylamine oleate soap 6；
（2）By step（1）In the water that weighs insert in electrical heating retort, by electrical heating retort electrified regulation to 78 DEG C, according to
Secondary addition step（1）In weigh castor oil, Tween-20, defoamer, BTA, preservative, octyl phenol -10, second
Ethylenediamine tetraacetic acid (EDTA), polyethylene glycol 400 bilaurate and trihydroxy ethylamine oleate soap, start stirring, mixing speed while addition
For 150r/min, raw material is set to be decomposed in the presence of catalyst, until temperature stops heating when reaching 128 DEG C, heating stops
Continue to stir 28min after only, i.e. reaction is completed；
（3）By step（2）The material obtained after the completion of middle reaction is delivered to water circulation cooling tank, opens the cold of water circulation cooling tank
But water is cooled down, and starts stirring, and mixing speed is 150 r/min, the material in water circulation cooling tank is cooled to normal temperature,
Stop stirring, the material after cooling is delivered to finished product settling tank, material stands 3 months in finished product settling tank.
Embodiment 7：A kind of cutting fluid, it is made up of the raw material of following weight：It is made up of the raw material of following weight：The Kg of water 40,
The Kg of castor oil 20, the Kg of Tween-20 5, the Kg of defoamer 3, the Kg of BTA 5, the Kg of preservative 3, octyl phenol -10 3
Kg, the Kg of ethylenediamine tetra-acetic acid 2, the Kg of polyethylene glycol 400 bilaurate 5, the Kg of trihydroxy ethylamine oleate soap 5.
A kind of method for preparing cutting fluid, comprises the following steps：
（1）Weigh raw material
Following raw material is weighed by following parts by weight：The Kg of water 40, the Kg of castor oil 20, the Kg of Tween-20 5, the Kg of defoamer 3, benzene
And the Kg of triazole 5, the Kg of preservative 3, octyl phenol -10 3 Kg, the Kg of ethylenediamine tetra-acetic acid 2, the bimonthly osmanthus of polyethylene glycol 400
The Kg of acid esters 5, the Kg of trihydroxy ethylamine oleate soap 5；
（2）By step（1）In the water that weighs insert in electrical heating retort, by electrical heating retort electrified regulation to 80 DEG C, according to
Secondary addition step（1）In weigh castor oil, Tween-20, defoamer, BTA, preservative, octyl phenol -10, second
Ethylenediamine tetraacetic acid (EDTA), polyethylene glycol 400 bilaurate and trihydroxy ethylamine oleate soap, start stirring, mixing speed while addition
For 150r/min, raw material is set to be decomposed in the presence of catalyst, until temperature stops heating when reaching 130 DEG C, heating stops
Continue to stir 30min after only, i.e. reaction is completed；
（3）By step（2）The material obtained after the completion of middle reaction is delivered to water circulation cooling tank, opens the cold of water circulation cooling tank
But water is cooled down, and starts stirring, and mixing speed is 150 r/min, the material in water circulation cooling tank is cooled to normal temperature,
Stop stirring, the material after cooling is delivered to finished product settling tank, material stands 3 months in finished product settling tank.
In above example, embodiment 7 is most preferred embodiment.The cutting fluid of the present invention is compared with traditional cutting fluid, antirust
Performance is 3-5 times of traditional product, and greasy property is high, and rust-proof effect is high, and cleaning performance is good, not greasy dirt, does not encroach on human skin, nothing
Peculiar smell.
After the cutting fluid tentatively attempted using the present invention through Luoyang internal combustion engine part company, user provides following make
With effect content：
Luoyang internal combustion engine part company is the cylinder jacket enterprise for producing one of automobile engine " heart " core component, is being processed
During dry liner steyr, i.e., the finish of cutting-tool's used life and work pieces process face is improved, is reduced again
The deformation of thin-wall workpiece, higher requirement of just having deducted a percentage the cutting fluid of lathe, using the cutting fluid for contrasting several brands
Afterwards, it is believed that water-base cutting fluid mobility of the invention and rate of heat exchange are higher, and permeability is more preferable, to the cooling effect of blade compared with
Good, so that the cutting-tool's used life such as CBN significantly improves, while cools down fully, the thin-walled deflection of dry cylinder liner is also smaller,
Ensure that the mass-temperature of product, in addition using the cutting fluid of the present invention after, to the lacquer painting of lathe without any corrosion phenomenon, and show
The cutting fluid for other brands having can have certain corrosion to the lacquer painting of lathe in use, while can be to operating personnel
Skin damages, and the cutting fluid of the present invention is completely absent corrosion phenomenon after, and it is attractive in appearance not influence lathe, and to operation
The skin of personnel is also without any injury.
In addition, traditional oil base grinding fluid is replaced using the cutting fluid of the present invention, due to the dry cylinder liner of user's production
Key equipment be to be introduced from certain German renowned company, the equipment represents world-class level, therefore user sets to this
Standby attention and treasure that degree is very high, the replacement to the grinding fluid of this equipment is also very prudent, because applicant's early stage is to this
The experiment that the cutting fluid of invention carries out for many years is attempted, and user is relatively trusted the honing mass ratio of the cutting fluid of the present invention, is used
The maximum cutting fluid that is experienced as is very low as grinding fluid use cost afterwards, stable performance, and honing steady quality is reliable.
User is also used by the use of the cutting fluid of the present invention as cleaning fluid, by being contrasted with the cleaning fluid of a variety of brands,
It was found that the cutting fluid of the present invention is used as cleaning fluid, cleaning performance is good, and steady quality, cost is low, to the skin of operating personnel without times
What is injured.
Claims (6)
- A kind of 1. cutting fluid, it is characterised in that：It is made up of the raw material of following parts by weight：Water 35-45 parts, castor oil 15-25 parts, Tween-20 3-7 parts, defoamer 2-5 parts, BTA 3-7 parts, preservative 1-4 parts, the 2-5 parts of octyl phenol -10, second Ethylenediamine tetraacetic acid (EDTA) 1-4 parts, polyethylene glycol 400 bilaurate 3-7 parts, trihydroxy ethylamine oleate soap 3-7 parts.
- 2. cutting fluid according to claim 1, it is characterised in that：It is made up of the raw material of following parts by weight：Water 38-42 Part, castor oil 17-22 parts, Tween-20 4-6 parts, defoamer 3-4 parts, BTA 4-6 parts, preservative 2-3 parts, octyl The 3-4 parts of phenol -10, ethylenediamine tetra-acetic acid 2-3 parts, polyethylene glycol 400 bilaurate 4-6 parts, trihydroxy ethylamine oleate soap 4-6 Part.
- 3. cutting fluid according to claim 1, it is characterised in that：It is made up of the raw material of following parts by weight：40 parts of water, castor 20 parts of sesame oil, 5 parts of Tween-20,3 parts of defoamer, 5 parts of BTA, 3 parts of preservative, -10 3 parts of octyl phenol, second two 2 parts of amine tetraacethyl, 5 parts of polyethylene glycol 400 bilaurate, 5 parts of trihydroxy ethylamine oleate soap.
- A kind of 4. method for preparing cutting fluid according to claim 1, it is characterised in that：Comprise the following steps：（1）Weigh raw materialFollowing raw material is weighed by following parts by weight：Water 35-45 parts, castor oil 15-25 parts, Tween-20 3-7 parts, defoamer 2- 5 parts, BTA 3-7 parts, preservative 1-4 parts, the 2-5 parts of octyl phenol -10, ethylenediamine tetra-acetic acid 1-4 parts, poly- second two The bilaurate 3-7 parts of alcohol 400, trihydroxy ethylamine oleate soap 3-7 parts；（2）By step（1）In the water that weighs insert in electrical heating retort, by electrical heating retort electrified regulation to 75-85 DEG C, Sequentially add step（1）In weigh castor oil, Tween-20, defoamer, BTA, preservative, octyl phenol -10, Ethylenediamine tetra-acetic acid, polyethylene glycol 400 bilaurate and trihydroxy ethylamine oleate soap, it is stirred while addition, stirring speed Spend for 100-200r/min, raw material is decomposed in the presence of catalyst, until temperature stop when reaching 125-135 DEG C plus Heat, heating continue to stir 25-35min after stopping；（3）By step（2）The material obtained after middle reaction is delivered to water circulation cooling tank, opens the cooling water of water circulation cooling tank Being cooled down, and start to stir, mixing speed is 100-200 r/min, the material in water circulation cooling tank is cooled to normal temperature, Stop stirring, the material after cooling is delivered to finished product settling tank, material stands 2-3 months in finished product settling tank.
- 5. the method according to claim 4 for preparing cutting fluid, it is characterised in that：Step（2）In electrical heating retort Heating-up temperature is 80 DEG C after energization.
- 6. the method according to claim 4 for preparing cutting fluid, it is characterised in that：Step（2）When middle temperature reaches 130 DEG C Stop heating, heating continues to stir 30min after stopping, i.e. reaction is completed.