CN107243576A - A kind of processing method of automobile clutch damping disk(-isc) - Google Patents
A kind of processing method of automobile clutch damping disk(-isc) Download PDFInfo
- Publication number
- CN107243576A CN107243576A CN201710641508.3A CN201710641508A CN107243576A CN 107243576 A CN107243576 A CN 107243576A CN 201710641508 A CN201710641508 A CN 201710641508A CN 107243576 A CN107243576 A CN 107243576A
- Authority
- CN
- China
- Prior art keywords
- workpiece
- punching
- pallet
- mould
- window
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses a kind of processing method of automobile clutch damping disk(-isc), comprise the following steps：（1）Blanking punching mesopore；（2）Rush window；（3）Window shapes；（4）Edge-cutting and hole-punching system.Using the punching after forming of technical solution of the present invention damping disk(-isc), it is to avoid the deformation of circular hole in forming process, as long as punching product mould is qualified, the position degree of product must be qualified；Edge-cutting and hole-punching system uses one set of die simultaneously, saves the trimming in former process, can improve production efficiency.
Description
Technical field
The present invention relates to automobile clutch manufacture field, and in particular to a kind of processing method of automobile clutch damping disk(-isc).
Background technology
In the prior art, to the processing method of automobile clutch damping disk(-isc), as shown in figure 1, comprising the following steps：
（1）Blanking punching mesopore, as shown in Fig. 2 it is specific as follows step by step：
1）Using 3mm thickness 08AL steel plates, positioned with the adjacent right-angle side of billot two, material is put into lower mould by hand steered billot end；
2）Lathe is operated, upper mould is descending, drops out initial workpiece workpiece, positioned with the long straight flange of billot one and last time blanking excircle configuration, according to
It is secondary to drop out 2 ~ 3 workpiece, billot is turned one, remaining workpiece is dropped out, every piece of 3mm × 206mm × 1250mm billot can drop out 6
Individual workpiece, workpiece punching position burr answers fine uniform, without punching defect；
3）Workpiece is unloaded, workpiece, rim charge are distinguished into block pattern row pattern on pallet, and finishes writing Sign Board and is placed on pallet, was produced
Note checking whether screw loosens and whether material leakage is smooth in journey, often process 20 ~ 30 chip removals once；
4）Cleaning is carried out after completion to equipment, mould to oil；
（2）Square hole circular hole is rushed, as shown in figure 3, it is specific as follows step by step：
1）Excircle of workpiece burr downwards, is positioned with inner hole of workpiece and baseplane, puts the workpiece in lower mould；
2）Lathe is operated, upper mould is descending, go out circular hole and square hole to illustrated dimensions requirement, workpiece punching position burr answers tiny
It is even, without punching defect；
3）Workpiece is unloaded, by workpiece block pattern row pattern on pallet, and Sign Board is finished writing and is placed on pallet, inspection is noted in production process
Look into whether screw loosens and whether material leakage is smooth, often process 20 ~ 30 chip removals once；
4）Cleaning is carried out after completion to equipment, mould to oil；
（3）Window is rushed, as shown in figure 4, it is specific as follows step by step：
1）Excircle of workpiece burr downwards, is positioned with any one hole of Φ 8 and mesopore, puts the workpiece in lower mould；
2）Lathe is operated, upper mould is descending, 16 windows are gone out by technical size requirement, workpiece punching position burr answers tiny
It is even, without punching defect；
3）Workpiece is unloaded, by workpiece block pattern row pattern on pallet, and Sign Board is finished writing and is placed on pallet, inspection is noted in production process
Look into whether screw loosens and whether material leakage is smooth, often process 20 ~ 30 chip removals once；
4）Cleaning is carried out after completion to equipment, mould to oil；
（4）Window shapes, as shown in figure 5, it is specific as follows step by step：
1）Excircle of workpiece burr downwards, is positioned with any one Φ 8mm hole and mesopore, puts the workpiece in lower mould；
2）Operate lathe, upper mould is descending, shaping window presses groove by technical size requirements, component shaping position require nothing pull,
The forming defectses such as drawing crack；
3）Workpiece is unloaded, by workpiece block pattern row pattern on pallet, and Sign Board is finished writing and is placed on pallet, inspection is noted in production process
Look into whether screw loosens and whether material leakage is smooth, often process 20 ~ 30 chip removals once；
4）Cleaning is carried out after completion to equipment, mould to oil；
（5）Trimming, as shown in fig. 6, it is specific as follows step by step：
1）It is punched the intraoral chamber of Directional Windows downwards, is positioned with workpiece mesopore and baseplane, put the workpiece in lower mould；
2）Operate lathe, upper mould is descending, workpiece pressed into technical size requirement trimming, workpiece be punched position burr answer fine uniform,
Without punching defect；
3）Workpiece is unloaded, by workpiece block pattern row pattern on pallet, and Sign Board is finished writing and is placed on pallet, inspection is noted in production process
Look into whether screw loosens, often process after a workpiece, clean out the waste material of die surface；
4）Cleaning is carried out after completion to equipment, mould to oil.
Above-mentioned prior art has the disadvantage：In damping disk(-isc) forming process, circular hole is first rushed due to use and reshapes order, damping disk(-isc)
Plastic deformation is easily produced, causes circular hole to deform after forming seriously, position degree is poor, it is impossible to be put into cubing.
The content of the invention
In view of the shortcomings of the prior art, problem solved by the invention is to solve：In damping disk(-isc) forming process, damping disk(-isc) holds
Plastic deformation is also easy to produce, causes circular hole to deform after forming seriously, position degree is poor, it is impossible to be put into cubing problem.
In order to solve the above technical problems, the technical solution adopted by the present invention is a kind of processing side of automobile clutch damping disk(-isc)
Method, comprises the following steps：
（1）Blanking punching mesopore, it is specifically as follows step by step：
1）Using 3mm thickness 08AL steel plates, positioned with the adjacent right-angle side of billot two, material is put into lower mould by hand steered billot end；
2）Lathe is operated, upper mould is descending, drops out initial workpiece workpiece, positioned with the long straight flange of billot one and last time blanking excircle configuration, according to
It is secondary to drop out 2 ~ 3 workpiece, billot is turned one, remaining workpiece is dropped out, every piece of 3mm × 206mm × 1250mm billot can drop out 6
Individual workpiece, workpiece punching position burr answers fine uniform, without punching defect；
3）Workpiece is unloaded, workpiece, rim charge are distinguished into block pattern row pattern on pallet, and finishes writing Sign Board and is placed on pallet, was produced
Note checking whether screw loosens and whether material leakage is smooth in journey, often process 20 ~ 30 chip removals once；
4）Cleaning is carried out after completion to equipment, mould to oil；
（2）Window is rushed, it is specifically as follows step by step：
1）Excircle of workpiece burr downwards, is positioned with mesopore, puts the workpiece in lower mould；
2）Lathe is operated, upper mould is descending, 16 windows are gone out by technical size requirement, workpiece punching position burr answers tiny
It is even, without punching defect；
3）Workpiece is unloaded, by workpiece block pattern row pattern on pallet, and Sign Board is finished writing and is placed on pallet, inspection is noted in production process
Look into whether screw loosens and whether material leakage is smooth, often process 20 ~ 30 chip removals once；
4）Cleaning is carried out after completion to equipment, mould to oil；
（3）Window shapes, and it is specifically as follows step by step：
1）Excircle of workpiece burr downwards, is positioned with any one window and mesopore, puts the workpiece in lower mould；
2）Lathe is operated, upper mould is descending, shaping window, groove is pressed by technical size requirement, component shaping position is required without drawing
The forming defectses such as wound, drawing crack；
3）Workpiece is unloaded, by workpiece block pattern row pattern on pallet, and Sign Board is finished writing and is placed on pallet, inspection is noted in production process
Look into whether screw loosens and whether material leakage is smooth, often process 20 ~ 30 chip removals once；
4）Cleaning is carried out after completion to equipment, mould to oil
（4）Edge-cutting and hole-punching system, it is specifically as follows step by step：
1）It is punched the intraoral chamber of Directional Windows downwards, is positioned with workpiece mesopore and a window, put the workpiece in lower mould；
2）Operate lathe, upper mould is descending, workpiece pressed into technical size requirement trimming, workpiece be punched position burr answer fine uniform,
Without punching defect；
3）Workpiece is unloaded, by workpiece block pattern row pattern on pallet, and Sign Board is finished writing and is placed on pallet, inspection is noted in production process
Look into whether screw loosens, often process after a workpiece, clean out the waste material of die surface；
4）Cleaning is carried out after completion to equipment, mould to oil.
Using the beneficial effect of technical solution of the present invention：Damping disk(-isc) punching after forming, it is to avoid circular hole in forming process
Deformation, as long as punching product mould it is qualified, the position degree of product must be qualified；Edge-cutting and hole-punching system uses one set of die simultaneously,
The trimming in former process is saved, production efficiency can be improved.
Brief description of the drawings
Fig. 1 is prior art schematic flow sheet；
Fig. 2 is prior art blanking punching mesopore process schematic diagram；
Fig. 3 is that prior art rushes square hole circular hole process schematic diagram；
Fig. 4 is that prior art rushes window process schematic diagram；
Fig. 5 is prior art window forming process schematic diagram；
Fig. 6 is prior art trimming process schematic diagram；
Fig. 7 is schematic flow sheet of the present invention；
Fig. 8 is blanking punching mesopore process schematic diagram of the present invention；
Fig. 9 is that the present invention rushes window process schematic diagram；
Figure 10 is window forming process schematic diagram of the present invention；
Figure 11 is edge-cutting and hole-punching system process schematic diagram of the present invention.
Embodiment
The embodiment to the present invention is further described below in conjunction with the accompanying drawings, but is not the limit to the present invention
It is fixed.
Fig. 7 shows the flow chart of the present invention, and a kind of processing method of automobile clutch damping disk(-isc) comprises the following steps：
（1）Blanking punching mesopore, as shown in figure 8, it is specific as follows step by step：
1）Using 3mm thickness 08AL steel plates, positioned with the adjacent right-angle side of billot two, material is put into lower mould by hand steered billot end；
2）Lathe is operated, upper mould is descending, drops out initial workpiece workpiece, positioned with the long straight flange of billot one and last time blanking excircle configuration, according to
It is secondary to drop out 2 ~ 3 workpiece, billot is turned one, remaining workpiece is dropped out, every piece of 3mm × 206mm × 1250mm billot can drop out 6
Individual workpiece, workpiece punching position burr answers fine uniform, without punching defect；
3）Workpiece is unloaded, workpiece, rim charge are distinguished into block pattern row pattern on pallet, and finishes writing Sign Board and is placed on pallet, was produced
Note checking whether screw loosens and whether material leakage is smooth in journey, often process 20 ~ 30 chip removals once；
4）Cleaning is carried out after completion to equipment, mould to oil；
（2）Window is rushed, as shown in figure 9, it is specific as follows step by step：
1）Excircle of workpiece burr downwards, is positioned with mesopore, puts the workpiece in lower mould；
2）Lathe is operated, upper mould is descending, 16 windows are gone out by technical size requirement, workpiece punching position burr answers tiny
It is even, without punching defect；
3）Workpiece is unloaded, by workpiece block pattern row pattern on pallet, and Sign Board is finished writing and is placed on pallet, inspection is noted in production process
Look into whether screw loosens and whether material leakage is smooth, often process 20 ~ 30 chip removals once；
4）Cleaning is carried out after completion to equipment, mould to oil；
（3）Window shapes, and as shown in Figure 10, it is specifically as follows step by step：
1）Excircle of workpiece burr downwards, is positioned with any one window and mesopore, puts the workpiece in lower mould；
2）Lathe is operated, upper mould is descending, shaping window, groove is pressed by technical size requirement, component shaping position is required without drawing
The forming defectses such as wound, drawing crack；
3）Workpiece is unloaded, by workpiece block pattern row pattern on pallet, and Sign Board is finished writing and is placed on pallet, inspection is noted in production process
Look into whether screw loosens and whether material leakage is smooth, often process 20 ~ 30 chip removals once；
4）Cleaning is carried out after completion to equipment, mould to oil
（4）Edge-cutting and hole-punching system, as shown in figure 11, it is specifically as follows step by step：
1）It is punched the intraoral chamber of Directional Windows downwards, is positioned with workpiece mesopore and a window, put the workpiece in lower mould；
2）Operate lathe, upper mould is descending, workpiece pressed into technical size requirement trimming, workpiece be punched position burr answer fine uniform,
Without punching defect；
3）Workpiece is unloaded, by workpiece block pattern row pattern on pallet, and Sign Board is finished writing and is placed on pallet, inspection is noted in production process
Look into whether screw loosens, often process after a workpiece, clean out the waste material of die surface；
4）Cleaning is carried out after completion to equipment, mould to oil.
Using the beneficial effect of technical solution of the present invention：Damping disk(-isc) punching after forming, it is to avoid circular hole in forming process
Deformation, as long as punching product mould it is qualified, the position degree of product must be qualified；Edge-cutting and hole-punching system uses one set of die simultaneously,
The trimming in former process is saved, production efficiency can be improved.
Embodiments of the present invention are made that with detailed description above in association with accompanying drawing, but the present invention be not limited to it is described
Embodiment.To those skilled in the art, without departing from the principles and spirit of the present invention, these are implemented
Mode carries out various change, modification, replacement and modification and still fallen within protection scope of the present invention.
Claims (1)
1. a kind of processing method of automobile clutch damping disk(-isc), it is characterised in that：Comprise the following steps：
（1）Blanking punching mesopore, it is specifically as follows step by step：
1）Using 3mm thickness 08AL steel plates, positioned with the adjacent right-angle side of billot two, material is put into lower mould by hand steered billot end；
2）Lathe is operated, upper mould is descending, drops out initial workpiece workpiece, positioned with the long straight flange of billot one and last time blanking excircle configuration, according to
It is secondary to drop out 2 ~ 3 workpiece, billot is turned one, remaining workpiece is dropped out, every piece of 3mm × 206mm × 1250mm billot can drop out 6
Individual workpiece, workpiece punching position burr answers fine uniform, without punching defect；
3）Workpiece is unloaded, workpiece, rim charge are distinguished into block pattern row pattern on pallet, and finishes writing Sign Board and is placed on pallet, was produced
Note checking whether screw loosens and whether material leakage is smooth in journey, often process 20 ~ 30 chip removals once；
4）Cleaning is carried out after completion to equipment, mould to oil；
（2）Window is rushed, it is specifically as follows step by step：
1）Excircle of workpiece burr downwards, is positioned with mesopore, puts the workpiece in lower mould；
2）Lathe is operated, upper mould is descending, 16 windows are gone out by technical size requirement, workpiece punching position burr answers tiny
It is even, without punching defect；
3）Workpiece is unloaded, by workpiece block pattern row pattern on pallet, and Sign Board is finished writing and is placed on pallet, inspection is noted in production process
Look into whether screw loosens and whether material leakage is smooth, often process 20 ~ 30 chip removals once；
4）Cleaning is carried out after completion to equipment, mould to oil；
（3）Window shapes, and it is specifically as follows step by step：
1）Excircle of workpiece burr downwards, is positioned with any one window and mesopore, puts the workpiece in lower mould；
2）Lathe is operated, upper mould is descending, shaping window, groove is pressed by technical size requirement, component shaping position is required without drawing
The forming defectses such as wound, drawing crack；
3）Workpiece is unloaded, by workpiece block pattern row pattern on pallet, and Sign Board is finished writing and is placed on pallet, inspection is noted in production process
Look into whether screw loosens and whether material leakage is smooth, often process 20 ~ 30 chip removals once；
4）Cleaning is carried out after completion to equipment, mould to oil；
（4）Edge-cutting and hole-punching system, it is specifically as follows step by step：
1）It is punched the intraoral chamber of Directional Windows downwards, is positioned with workpiece mesopore and a window, put the workpiece in lower mould；
2）Operate lathe, upper mould is descending, workpiece pressed into technical size requirement trimming, workpiece be punched position burr answer fine uniform,
Without punching defect；
3）Workpiece is unloaded, by workpiece block pattern row pattern on pallet, and Sign Board is finished writing and is placed on pallet, inspection is noted in production process
Look into whether screw loosens, often process after a workpiece, clean out the waste material of die surface；
4）Cleaning is carried out after completion to equipment, mould to oil.