CN106634704A - Anti-allergic medical pressure-sensitive adhesive and preparation process thereof - Google Patents
Anti-allergic medical pressure-sensitive adhesive and preparation process thereof Download PDFInfo
- Publication number
- CN106634704A CN106634704A CN201611118873.8A CN201611118873A CN106634704A CN 106634704 A CN106634704 A CN 106634704A CN 201611118873 A CN201611118873 A CN 201611118873A CN 106634704 A CN106634704 A CN 106634704A
- Authority
- CN
- China
- Prior art keywords
- parts
- sensitive adhesive
- medical pressure
- pressure sensitive
- antiallergy
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention discloses an anti-allergic medical pressure-sensitive adhesive and a preparation process thereof. The pressure-sensitive adhesive is prepared from the following raw materials: polyisobutene, isodecyl acrylate, acrylate-hydroxy ester, glycidyl methacrylate, alpha-cyanoacrylate, dithiothreitol, buckwheat-flavonoids, Tween 80, pyrithione zinc, L-serine benzyl ester, hydrogenated butadiene-acrylonitrile rubber, mandelic acid, menthol, peach gum, hydroxypropyl-beta-cyclodextrin, vitamin E, an initiator and plasticiser. The medical pressure-sensitive adhesive prepared by the invention presents a higher moisture-vapor transmission rate and moderate viscosity, can be used for repeatedly removing a label for more than 5 times, is flexible to use, has good compatibility with the skin, and has no stimulation to the skin and no allergic phenomenon, the experience effect of a patient is better, and the applied range is wide.
Description
Technical field
The invention belongs to medical material tech field, and in particular to a kind of antiallergy medical pressure sensitive adhesive and its preparation technology.
Background technology
Pressure sensitive adhesive be used to needing in the various applications being adhered on skin, such as medical adhesive tape, wound or surgical dressing, use
In the thick and heavy dressing of apparatus or comparison such as remaining needle, ductus venosus are fixed on skin yet with the flat of skin surface
Whole degree and hair, secretion, cuticular presence, surface property, the mechanical property of skin especially dynamic mechanical with
The difference of other materials is bigger, makes pressure sensitive adhesive increasingly complex with the bond properties problem of skin.Generally for increase pressure sensitive adhesive with
The cementitiousness of skin, reduces alice and obscission, and some tackifier are often added in pressure sensitive adhesive, but some are viscosified
The membership that adds of agent causes allergic, and in addition the breathable moisture permeability of conventional pressure sensitive adhesive is not good, is unfavorable for skin perspiration.Therefore,
In order to obtain more preferable using effect and range of application, need pressure sensitive adhesive to have preferable compatibility with skin, possess sufficiently high
Steam penetrability and gentle viscosity, and can repeatedly take off patch and use.
The content of the invention
For this purpose, the present invention provides a kind of antiallergy medical pressure sensitive adhesive and its preparation technology, solve at least one in prior art
Plant technical problem.
For this purpose, the present invention provides a kind of antiallergy medical pressure sensitive adhesive, it is prepared by the raw material of following weight portion：Poly- isobutyl
Alkene 34-45 parts, isodecyl acrylate 12-22 parts, crylic acid hydroxy ester 6-15 parts, GMA 3-9 parts, a-
Cyanoacrylate 2-5 parts, dithiothreitol (DTT) 1-6 parts, buckwheat flavone 2-5 parts, Tween 80 1-3 parts, pyrithione zinc 1-4 parts, L-
Serine benzyl ester 2-6 part, hydrogenated nitrile-butadiene rubber 5-9 parts, mandelic acid 2-7 parts, menthol 3-6 parts, peach gum 5-12 parts, hydroxypropyl-
Beta-schardinger dextrin 4-8 parts, vitamin E 1.2-3 parts, initiator 0.6-1.8 parts, plasticizer 1.4-2.2 parts.
An embodiment of the invention, wherein, the initiator is benzoyl peroxide or tetramethylethylenediamine
Or dimethoxybenzoin.
An embodiment of the invention, wherein, the plasticizer is glycerine, sorbierite, mannose or poly- second two
Alcohol.
An embodiment of the invention, wherein, it is prepared by the raw material of following weight portion：Polyisobutene 36-
43 parts, isodecyl acrylate 14-21 parts, crylic acid hydroxy ester 7.5-13 parts, GMA 3.5-8 parts, a-
Cyanoacrylate 2.4-4.6 parts, dithiothreitol (DTT) 1.2-5.6 parts, buckwheat flavone 2.4-4.5 parts, Tween 80 1.4-2.5 parts,
Pyrithione zinc 1.8-3.2 parts, Serine benzyl ester 2.7-5 part, hydrogenated nitrile-butadiene rubber 5.2-7.5 parts, mandelic acid 2.4-6.3 parts,
Menthol 3.4-5.8 parts, peach gum 5.5-10 parts, HP-β-CD 4.2-7.6 parts, vitamin E 1.5-2.8 parts, initiation
Agent 0.8-1.5 parts, plasticizer 1.6-2.1 parts.
For this purpose, the present invention provides a kind of preparation technology of antiallergy medical pressure sensitive adhesive, including following preparation process：
Step 1）Hydrogenated nitrile-butadiene rubber, Serine benzyl ester and a- cyanoacrylates are well mixed, then at 110-140 DEG C
At a temperature of banburying 4-10 minutes；
Step 2）Isodecyl acrylate, crylic acid hydroxy ester and GMA are added, is well mixed, Ran Hou
Banburying 7-15 minutes at a temperature of 110-140 DEG C；
Step 3）Room temperature is cooled to, is crushed standby；
Step 4）Polyisobutene, dithiothreitol (DTT) and mandelic acid are added in reactor, 160-190 DEG C is first heated to, 20- is stirred
40min, is subsequently adding initiator, plasticizer and step 3）In crushed material, 190-230 DEG C is warming up to, in 500-1000r/min
Rotating speed under stir 15-30min；
Step 5）Remaining material is added, at 150-180 DEG C, to stir 1-3 hours under the rotating speed of 200-800r/min, is cooled to
Room temperature, you can.
An embodiment of the invention, wherein, the step 1）In at a temperature of 120 DEG C banburying 6 minutes；It is described
Step 2）In at a temperature of 135 DEG C banburying 12 minutes.
An embodiment of the invention, wherein, the step 3）In be crushed to 200-400 mesh.
An embodiment of the invention, wherein, the step 4）It is middle to be first heated to 175 DEG C, stir 35min；Institute
State step 4）In be warming up to 210 DEG C, stir 25min under the rotating speed of 800r/min.
An embodiment of the invention, wherein, the step 5）At 165 DEG C, with the rotating speed of 500r/min
Stirring 3 hours.
Beneficial effects of the present invention are：
The peel strength of medical pressure sensitive adhesive prepared by the present invention at 25 DEG C reaches 11.8-13.4N, and moisture transmission is 604-634
g/m2/ 24h, the higher moisture transmission of display and gentle viscosity, and the number of times that can be noticed repeatedly is more than 5 times, uses flexibly,
It is good with the compatibility of skin, it is non-stimulated to skin and without allergic phenomena, Patient Experience effect preferably, applied range.
Specific embodiment
With reference to embodiment, the present invention is described in further detail.Following examples are used to illustrate the present invention, but not
For limiting the scope of the present invention.
Embodiment 1
A kind of antiallergy medical pressure sensitive adhesive, is prepared by the raw material of following weight portion：34 parts of polyisobutene, isodecyl acrylate
12 parts, 6 parts of crylic acid hydroxy ester, 3 parts of GMA, 2 parts of a- cyanoacrylates, 1 part of dithiothreitol (DTT),
2 parts of buckwheat flavone, 1 part of Tween 80,1 part of pyrithione zinc, 2 parts of Serine benzyl ester, 5 parts of hydrogenated nitrile-butadiene rubber, 2 parts of mandelic acid,
3 parts of menthol, 5 parts of peach gum, 4 parts of HP-β-CD, 1.2 parts of vitamin E, 0.6 part of initiator, 1.4 parts of plasticizer.
Wherein, the initiator is benzoyl peroxide.
Wherein, the plasticizer is glycerine.
A kind of preparation technology of antiallergy medical pressure sensitive adhesive, including following preparation process：
Step 1）Hydrogenated nitrile-butadiene rubber, Serine benzyl ester and a- cyanoacrylates are well mixed, then in 110 DEG C of temperature
Lower banburying 4 minutes；
Step 2）Isodecyl acrylate, crylic acid hydroxy ester and GMA are added, is well mixed, Ran Hou
Banburying 7 minutes at a temperature of 140 DEG C；
Step 3）Room temperature is cooled to, 200-400 mesh is crushed to, it is standby；
Step 4）Polyisobutene, dithiothreitol (DTT) and mandelic acid are added in reactor, 160 DEG C are first heated to, 20min is stirred,
It is subsequently adding initiator, plasticizer and step 3）In crushed material, be warming up to 190 DEG C, under the rotating speed of 500r/min stir
15min；
Step 5）Remaining material is added, at 150 DEG C, to stir 1 hour under the rotating speed of 200r/min, room temperature is cooled to, you can.
Embodiment 2
A kind of antiallergy medical pressure sensitive adhesive, is prepared by the raw material of following weight portion：45 parts of polyisobutene, isodecyl acrylate
22 parts, 15 parts of crylic acid hydroxy ester, GMA 3-9 parts, 5 parts of a- cyanoacrylates, dithiothreitol (DTT) 6
Part, 5 parts of buckwheat flavone, 3 parts of Tween 80,4 parts of pyrithione zinc, 6 parts of Serine benzyl ester, 9 parts of hydrogenated nitrile-butadiene rubber, mandelic acid 7
Part, 6 parts of menthol, 12 parts of peach gum, 8 parts of HP-β-CD, 3 parts of vitamin E, 1.8 parts of initiator, 2.2 parts of plasticizer.
Wherein, the initiator is tetramethylethylenediamine.
Wherein, the plasticizer is sorbierite.
A kind of preparation technology of antiallergy medical pressure sensitive adhesive, including following preparation process：
Step 1）Hydrogenated nitrile-butadiene rubber, Serine benzyl ester and a- cyanoacrylates are well mixed, then in 140 DEG C of temperature
Lower banburying 10 minutes；
Step 2）Isodecyl acrylate, crylic acid hydroxy ester and GMA are added, is well mixed, Ran Hou
Banburying 7 minutes at a temperature of 140 DEG C；
Step 3）Room temperature is cooled to, 200-400 mesh is crushed to, it is standby；
Step 4）Polyisobutene, dithiothreitol (DTT) and mandelic acid are added in reactor, 190 DEG C are first heated to, 40min is stirred,
It is subsequently adding initiator, plasticizer and step 3）In crushed material, be warming up to 230 DEG C, under the rotating speed of 1000r/min stir
30min；
Step 5）Remaining material is added, at 180 DEG C, to stir 3 hours under the rotating speed of 800r/min, room temperature is cooled to, you can.
Embodiment 3
A kind of antiallergy medical pressure sensitive adhesive, is prepared by the raw material of following weight portion：36 parts of polyisobutene, isodecyl acrylate
14 parts, 7.5 parts of crylic acid hydroxy ester, 3.5 parts of GMA, 2.4 parts of a- cyanoacrylates, two sulphur threoses
1.2 parts of alcohol, 2.4 parts of buckwheat flavone, 1.4 parts of Tween 80,1.8 parts of pyrithione zinc, 2.7 parts of Serine benzyl ester, hydrogenated butyronitrile rubber
5.2 parts of glue, 2.4 parts of mandelic acid, 3.4 parts of menthol, 5.5 parts of peach gum, 4.2 parts of HP-β-CD, 1.5 parts of vitamin E,
0.8 part of initiator, 1.6 parts of plasticizer.
Wherein, the initiator is dimethoxybenzoin.
Wherein, the plasticizer is mannose.
A kind of preparation technology of antiallergy medical pressure sensitive adhesive, including following preparation process：
Step 1）Hydrogenated nitrile-butadiene rubber, Serine benzyl ester and a- cyanoacrylates are well mixed, then in 120 DEG C of temperature
Lower banburying 8 minutes；
Step 2）Isodecyl acrylate, crylic acid hydroxy ester and GMA are added, is well mixed, Ran Hou
Banburying 10 minutes at a temperature of 135 DEG C；
Step 3）Room temperature is cooled to, 200-400 mesh is crushed to, it is standby；
Step 4）Polyisobutene, dithiothreitol (DTT) and mandelic acid are added in reactor, 175 DEG C are first heated to, 35min is stirred,
It is subsequently adding initiator, plasticizer and step 3）In crushed material, be warming up to 210 DEG C, under the rotating speed of 700r/min stir
20min；
Step 5）Remaining material is added, at 170 DEG C, to stir 2 hours under the rotating speed of 650r/min, room temperature is cooled to, you can.
Embodiment 4
A kind of antiallergy medical pressure sensitive adhesive, is prepared by the raw material of following weight portion：43 parts of polyisobutene, isodecyl acrylate
21 parts, 13 parts of crylic acid hydroxy ester, 8 parts of GMA, 4.6 parts of a- cyanoacrylates, dithiothreitol (DTT)
5.6 parts, 4.5 parts of buckwheat flavone, 2.5 parts of Tween 80,3.2 parts of pyrithione zinc, 5 parts of Serine benzyl ester, hydrogenated nitrile-butadiene rubber
7.5 parts, 6.3 parts of mandelic acid, 5.8 parts of menthol, 10 parts of peach gum, 7.6 parts of HP-β-CD, 2.8 parts of vitamin E, draw
Send out 1.5 parts of agent, 2.1 parts of plasticizer.
Wherein, the initiator is tetramethylethylenediamine.
Wherein, the plasticizer is polyethylene glycol.
A kind of preparation technology of antiallergy medical pressure sensitive adhesive, including following preparation process：
Step 1）Hydrogenated nitrile-butadiene rubber, Serine benzyl ester and a- cyanoacrylates are well mixed, then in 130 DEG C of temperature
Lower banburying 5 minutes；
Step 2）Isodecyl acrylate, crylic acid hydroxy ester and GMA are added, is well mixed, Ran Hou
Banburying 14 minutes at a temperature of 120 DEG C；
Step 3）Room temperature is cooled to, 200-400 mesh is crushed to, it is standby；
Step 4）Polyisobutene, dithiothreitol (DTT) and mandelic acid are added in reactor, 185 DEG C are first heated to, 35min is stirred,
It is subsequently adding initiator, plasticizer and step 3）In crushed material, be warming up to 210 DEG C, under the rotating speed of 800r/min stir
20min；
Step 5）Remaining material is added, at 170 DEG C, to stir 3 hours under the rotating speed of 550r/min, room temperature is cooled to, you can.
Embodiment 5
A kind of antiallergy medical pressure sensitive adhesive, is prepared by the raw material of following weight portion：40 parts of polyisobutene, isodecyl acrylate
18 parts, 10.2 parts of crylic acid hydroxy ester, 5.7 parts of GMA, 3.5 parts of a- cyanoacrylates, two sulphur Soviet Union
3.4 parts of sugar alcohol, 3.5 parts of buckwheat flavone, 2 parts of Tween 80,2.5 parts of pyrithione zinc, 3.8 parts of Serine benzyl ester, hydrogenated butyronitrile rubber
6.3 parts of glue, 4.1 parts of mandelic acid, 4 parts of menthol, 7.5 parts of peach gum, 5.8 parts of HP-β-CD, 2 parts of vitamin E, initiation
1.1 parts of agent, 1.8 parts of plasticizer.
Wherein, the initiator is dimethoxybenzoin.
Wherein, the plasticizer is mannose.
A kind of preparation technology of antiallergy medical pressure sensitive adhesive, including following preparation process：
Step 1）Hydrogenated nitrile-butadiene rubber, Serine benzyl ester and a- cyanoacrylates are well mixed, then in 120 DEG C of temperature
Lower banburying 6 minutes；
Step 2）Isodecyl acrylate, crylic acid hydroxy ester and GMA are added, is well mixed, Ran Hou
Banburying 12 minutes at a temperature of 135 DEG C；
Step 3）Room temperature is cooled to, 200-400 mesh is crushed to, it is standby；
Step 4）Polyisobutene, dithiothreitol (DTT) and mandelic acid are added in reactor, 175 DEG C are first heated to, 35min is stirred,
It is subsequently adding initiator, plasticizer and step 3）In crushed material, be warming up to 210 DEG C, under the rotating speed of 800r/min stir
25min；
Step 5）Remaining material is added, at 165 DEG C, to stir 3 hours under the rotating speed of 500r/min, room temperature is cooled to, you can.
Comparative example 1
It is in place of this comparative example and the difference of embodiment 1：Not comprising a- cyanoacrylates, buckwheat flavone and menthol.
Comparative example 2
It is in place of this comparative example and the difference of embodiment 1：Not comprising vitamin E, mandelic acid and Serine benzyl ester.
To the pressure-sensitive adhesives prepared by above example and comparative example on polyurethane film, dry glue thickness is 25 micro-
Rice, tests its gas permeability at 25 DEG C, is then affixed to test its peel strength on skin, and observes its service condition, its test
As a result it is as shown in the table：
| Numbering | Peel strength/N | Moisture transmission/g/m2/24h | Whether sensitization | Skin irritation index | Patch number of times can repeatedly be taken off |
| Embodiment 1 | 11.8 | 604 | It is no | 0 | 5-6 |
| Embodiment 2 | 12.3 | 616 | It is no | 0 | 4-5 |
| Embodiment 3 | 12.9 | 623 | It is no | 0 | 5-6 |
| Embodiment 4 | 13.1 | 628 | It is no | 0 | 6-7 |
| Embodiment 5 | 13.4 | 634 | It is no | 0 | 6-7 |
| Comparative example 1 | 9.6 | 577 | It is no | 0 | 2-3 |
| Comparative example 2 | 8.9 | 583 | Slightly | 0 | 3-4 |
Test from more than, the peel strength of medical pressure sensitive adhesive prepared by the present invention at 25 DEG C reaches 11.8-13.4N, moisture
Transmitance is 604-634 g/m2/ 24h, the higher moisture transmission of display and gentle viscosity, and the number of times that can be noticed repeatedly
It is good with the compatibility of skin using flexible more than 5 times, it is non-stimulated to skin and without allergic phenomena, Patient Experience effect preferably,
Applied range.
Claims (9)
1. a kind of antiallergy medical pressure sensitive adhesive, it is characterised in that be prepared by the raw material of following weight portion：Polyisobutene 34-
45 parts, isodecyl acrylate 12-22 parts, crylic acid hydroxy ester 6-15 parts, GMA 3-9 parts, a- cyano group
Acrylate 2-5 parts, dithiothreitol (DTT) 1-6 parts, buckwheat flavone 2-5 parts, Tween 80 1-3 parts, pyrithione zinc 1-4 parts, L- silk ammonia
Acid benzyl ester 2-6 parts, hydrogenated nitrile-butadiene rubber 5-9 parts, mandelic acid 2-7 parts, menthol 3-6 parts, peach gum 5-12 parts, hydroxy propyl-Beta-ring
Dextrin 4-8 parts, vitamin E 1.2-3 parts, initiator 0.6-1.8 parts, plasticizer 1.4-2.2 parts.
2. a kind of antiallergy medical pressure sensitive adhesive according to claim 1, it is characterised in that the initiator is benzoyl peroxide
Formyl or tetramethylethylenediamine or dimethoxybenzoin.
3. a kind of antiallergy medical pressure sensitive adhesive according to claim 1, it is characterised in that the plasticizer is glycerine, mountain
Pears alcohol, mannose or polyethylene glycol.
4. a kind of antiallergy medical pressure sensitive adhesive according to claim 1, it is characterised in that by the raw material of following weight portion
It is prepared：Polyisobutene 36-43 parts, isodecyl acrylate 14-21 parts, crylic acid hydroxy ester 7.5-13 parts, methacrylic acid
Ethylene oxidic ester 3.5-8 parts, a- cyanoacrylate 2.4-4.6 parts, dithiothreitol (DTT) 1.2-5.6 parts, buckwheat flavone 2.4-4.5
Part, Tween 80 1.4-2.5 parts, pyrithione zinc 1.8-3.2 parts, Serine benzyl ester 2.7-5 part, hydrogenated nitrile-butadiene rubber 5.2-7.5
Part, mandelic acid 2.4-6.3 parts, menthol 3.4-5.8 parts, peach gum 5.5-10 parts, HP-β-CD 4.2-7.6 parts, dimension life
Plain E 1.5-2.8 parts, initiator 0.8-1.5 parts, plasticizer 1.6-2.1 parts.
5. according to a kind of preparation technology of the arbitrary described antiallergy medical pressure sensitive adhesive of claim 1-4, it is characterised in that include
Following preparation process：
Step 1）Hydrogenated nitrile-butadiene rubber, Serine benzyl ester and a- cyanoacrylates are well mixed, then at 110-140 DEG C
At a temperature of banburying 4-10 minutes；
Step 2）Isodecyl acrylate, crylic acid hydroxy ester and GMA are added, is well mixed, Ran Hou
Banburying 7-15 minutes at a temperature of 110-140 DEG C；
Step 3）Room temperature is cooled to, is crushed standby；
Step 4）Polyisobutene, dithiothreitol (DTT) and mandelic acid are added in reactor, 160-190 DEG C is first heated to, 20- is stirred
40min, is subsequently adding initiator, plasticizer and step 3）In crushed material, 190-230 DEG C is warming up to, in 500-1000r/min
Rotating speed under stir 15-30min；
Step 5）Remaining material is added, at 150-180 DEG C, to stir 1-3 hours under the rotating speed of 200-800r/min, is cooled to
Room temperature, you can.
6. a kind of preparation technology of antiallergy medical pressure sensitive adhesive according to claim 5, it is characterised in that the step 1）
In at a temperature of 120 DEG C banburying 6 minutes；The step 2）In at a temperature of 135 DEG C banburying 12 minutes.
7. a kind of preparation technology of antiallergy medical pressure sensitive adhesive according to claim 5, it is characterised in that the step 3）
In be crushed to 200-400 mesh.
8. a kind of preparation technology of antiallergy medical pressure sensitive adhesive according to claim 5, it is characterised in that the step 4）
It is middle to be first heated to 175 DEG C, stir 35min；The step 4）In be warming up to 210 DEG C, under the rotating speed of 800r/min stir
25min。
9. a kind of preparation technology of antiallergy medical pressure sensitive adhesive according to claim 5, it is characterised in that the step 5）
At 165 DEG C, to stir 3 hours under the rotating speed of 500r/min.