CN106350308B - 一种用于清洁金属和瓷器的盐复合物及对金属和瓷器进行清洁的方法 - Google Patents
一种用于清洁金属和瓷器的盐复合物及对金属和瓷器进行清洁的方法 Download PDFInfo
- Publication number
- CN106350308B CN106350308B CN201610721773.8A CN201610721773A CN106350308B CN 106350308 B CN106350308 B CN 106350308B CN 201610721773 A CN201610721773 A CN 201610721773A CN 106350308 B CN106350308 B CN 106350308B
- Authority
- CN
- China
- Prior art keywords
- porcelain
- metal
- cleaning
- parts
- salt composite
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
本发明提供一种用于清洁金属和瓷器的盐复合物及对金属和瓷器进行清洁的方法，所述盐复合物包括如下重量份的组分：50~70份粗盐、15~35份氨基磺酸、5~10份柠檬酸钠和1~8份柠檬酸，所述方法采用所述用于清洁金属和瓷器的盐复合物对金属和瓷器进行清洗。采用本发明盐复合物对金属和瓷器进行清洗，可以深层清除金属、瓷器表面的污渍和锈斑，且不会对金属和瓷器造成腐蚀，避免了金属出现裂纹断裂和瓷器表面被腐蚀情况的发生，使用本发明盐复合物清洁后的金属和瓷器还能长效保证不易沾染污渍和生锈，对金属和瓷器具有保护功效。
Description
技术领域
本发明属于清洁剂技术领域，具体涉及一种用于清洁金属和瓷器的盐复合物及对金属和瓷器进行清洁的方法。
背景技术
金属因为易与空气中的氧气发生反应，进而容易出现生锈的现象，造成金属表面锈迹斑斑，严重影响了使用质感和美观。瓷器中有很多细微的小孔，这些小孔在瓷器的使用过程中容易吸收瓷器中承装物质的颜色和成分，进而容易造成瓷器中形成很多无法清洗去除的污渍，且瓷器表面的釉在使用过程中也会受到外界的湿度、温度和光照紫外线的影响，进而容易使瓷器表面的釉脱色或脱落，进而使瓷器本身更容易暴露在外界环境中。
基于此，现有技术开发了清洁剂用于清洁金属和瓷器，但现有的清洗剂采用的酸类清洗成分多对金属和瓷器具有强腐蚀作用，会与金属发生反应生成氢，并将产生的氢扩散到金属的晶格空隙中，使金属容易出现裂纹，且还会与瓷器中的碳酸钙等成分发生反应，使瓷器中产生更多细小的微孔，导致瓷器的整体质量变差，容易破碎，这些细小的微孔也更容易吸收有色物质，使清洗后的瓷器在后期使用中更容易吸附污渍。此外，现有的清洁剂仅为了取得即时清洁效果，并不具有保护清洁后的物品不再容易生锈或沾染污渍的功能。综上可以看出，现有的金属和瓷器的清洁产品具有一定的不足之处。
发明内容
针对现有技术存在的上述不足，本发明要解决的技术问题是：针对现有的清洗剂容易腐蚀金属和瓷器，使金属容易出现裂纹，瓷器产生更多细小微孔导致瓷器整体质量变差，且不具有保护清洁后的物品不再容易生锈或沾染污渍的技术问题，而提供一种不会对金属和瓷器造成腐蚀，且能够长效保持清洁后物品不再生锈或沾染污渍的用于清洁金属和瓷器的盐复合物及对金属和瓷器进行清洁的方法。
为了解决上述技术问题，本发明采用如下技术方案：一种用于清洁金属和瓷器的盐复合物，包括如下重量份的组分：50~70份粗盐、15~35份氨基磺酸、5~10份柠檬酸钠和1~8份柠檬酸。采用本发明盐复合物时，可以利用粗盐的磨砂和吸附作用对金属和瓷器表面的污渍进行清除和吸附，且粗盐还对金属、瓷器表面的细菌具有消杀作用，有效保证清洁后的产品表面菌群总数减少，不会存在有致病菌，且更为关键的是本发明特别针对现有技术清洁剂中使用的酸容易与金属发生反应生成氢，进而导致金属容易生成裂纹，或其中的酸容易与瓷器中的碳酸钙等成分反应，使瓷器中孔隙增多、质量变差的技术问题，特别通过研究发现，采用氨基磺酸与柠檬酸进行复配作为酸性清洁成分，可以在保证酸对金属、瓷器表面的污渍进行有效清洁的同时，不会对金属造成腐蚀和使金属表面产生裂纹，也不会与瓷器中的碳酸钙等成分发生反应，不会使瓷器中的空洞变多，也不会腐蚀瓷器表面的釉质，在清洁同时没有对瓷器和金属造成硬性伤害，有效延长了瓷器和金属的使用期限。
进一步，还包括2~5份扁桃酸和3~8份五倍子酸。通过扁桃酸、五倍子酸、氨基磺酸和柠檬酸的协同配伍作用，还可以对金属表面的氧化锈斑以及瓷器表面的有色污渍进行深度清洗，使清洗后的金属表面光滑，清洗后的瓷器没有局部色斑，清洁效果更佳。
进一步，还包括4~9份水性聚氨酯。本发明通过复配水性聚氨酯可以用来填补金属和瓷器表面已经存在的裂纹，使修补后的金属和瓷器表面光滑无缺口，有效避免了因存在裂纹而导致金属和瓷器断裂现象的发生，且添加的水性聚氨酯还能一定程度地隔绝空气和金属瓷器，减少外界环境对金属、瓷器造成的不良影响。
作为优化，还包括2~7份魔芋糖蛋白；所述魔芋糖蛋白采用如下方法制得：
1）将魔芋清洗、去皮，于60~80℃下干燥8~12h后进行粉碎，得到魔芋粉；
2）将步骤1）所述魔芋粉与Na2HPO4-NaH2PO4缓冲溶液以1 g：200~400 mL的质量体积比混合，于50~70℃浸提2~4 h后，取浸提液过滤，收集清液；
3）将步骤2）收集的所述清液与乙醇按照1:2~4的体积比混合并于室温下静置5~8h后，收集沉淀；
4）用水清洗沉淀至少两次，将清洗后的沉淀于60~80℃下干燥6~8 h，得到所述魔芋糖蛋白。
本发明还特别针对现有技术中清洁剂仅具有即时清洁效果，而不能长效保证瓷器和金属不再生锈或沾染污渍的技术问题，通过研究发现通过复配魔芋糖蛋白可以在瓷器和金属的表面形成一层保护膜，可以将金属和瓷器与外界环境隔绝开，进而避免了空气和水汽直接与金属反应而形成锈斑，也避免了外界环境对瓷器造成影响而造成的瓷器组织破坏和变黄的问题；且添加的魔芋糖蛋白还具有一定的抑菌作用，可以避免金属和瓷器表面生长霉菌和青苔。
作为又一优化，步骤2）中采用pH6.0~7.2的Na2HPO4-NaH2PO4缓冲溶液。采用这样pH范围的缓冲溶液可以避免因pH不合适而使糖蛋白活性失效的问题，进而有效保证制得的糖蛋白能够在物品表面形成保护膜。
作为再一优化，步骤2）中将步骤1）所述魔芋粉与Na2HPO4-NaH2PO4缓冲溶液以1 g：200~400 mL的质量体积比混合均匀，于50~70℃下超声浸提2~4 h，其中，所述超声的功率为300~450 W。采用超声波进行提取，可以使提取效率更高，提取出更多的魔芋糖蛋白，使生产成本降低。
一种对金属和瓷器进行清洗的方法，采用所述用于清洁金属和瓷器的盐复合物对金属和瓷器进行清洗。采用本发明盐复合物对金属和瓷器进行清洗，可以深层清除金属、瓷器表面的污渍和锈斑，且不会对金属和瓷器造成腐蚀，避免了金属出现裂纹断裂和瓷器表面被腐蚀情况的发生，使用本发明盐复合物清洁后的金属和瓷器还能长效保证不易沾染物资和生锈，对金属和瓷器具有保护功效。
作为优化，将所述用于清洁金属和瓷器的盐复合物与水按照1g：10~50 mL的质量体积比混合配制成清洁液，采用所述清洁液对金属和瓷器进行清洗。将本方面盐复合物配成水溶液后，再付金属和瓷器进行清洗，可以使复合物的清除效果更好，清洁效果更优异。
相比现有技术，本发明具有如下有益效果：采用本发明盐复合物时可以深层清除金属、瓷器表面的污渍和锈斑，且更为关键的是采用本发明盐复合物的配方可以在保证酸对金属、瓷器表面的污渍进行有效清洁的同时，不会对金属造成腐蚀和使金属表面产生裂纹，也不会与瓷器中的碳酸钙等成分发生反应，不会使瓷器中的空洞变多，也不会腐蚀瓷器表面的釉质，在清洁同时没有对瓷器和金属造成硬性伤害，有效延长了瓷器和金属的使用期限。此外，本发明配方中组分来源广泛，价格较为低廉，已被广大厂家所接受采用，具有良好的市场应用前景。
具体实施方式
下面结合具体实施例对本发明作进一步详细说明。本实施案例在以本发明技术为前提下进行实施，现给出详细的实施方式和具体的操作过程来说明本发明具有创造性，但本发明的保护范围不限于以下的实施例。
实施例1
一种用于清洁金属和瓷器的盐复合物，包括如下重量份的组分：50份粗盐、15份氨基磺酸、5份柠檬酸钠、1份柠檬酸、2份扁桃酸和3份五倍子酸。
采用本实施例盐复合物对金属和瓷器进行清洗，结果显示清洁后的金属表面无污渍、具有明显的金属光泽，清洁没有使金属表面出现裂纹，清洁后的瓷器由黄色恢复到本色，且清洁没有使瓷器出现脱色、釉质脱落的现象，在保证良好清洁效果的同时，避免了对金属和瓷器造成伤害。
实施例2
一种用于清洁金属和瓷器的盐复合物，包括如下重量份的组分：60份粗盐、25份氨基磺酸、8份柠檬酸钠、5份柠檬酸、4份扁桃酸、5份五倍子酸和7份水性聚氨酯。
采用本实施例盐复合物对金属和瓷器进行清洗，结果显示清洁后的金属表面无污渍和锈斑、具有明显的金属光泽，清洁没有使金属表面出现裂纹，还对原有已存在金属表面裂纹进行了填补，使金属的表面光滑，避免了原存在的金属裂纹带来的金属断裂风险；清洁后的瓷器由黄色恢复到本色且没有局部有色色斑沉淀存在，清洁没有使瓷器出现脱色、釉质脱落的现象，且对瓷器原先表面存在的孔隙进行了修补，保证了瓷器表面的光滑完整，在保证良好清洁效果的同时，避免了对金属和瓷器造成伤害。
实施例3
一种用于清洁金属和瓷器的盐复合物，包括如下重量份的组分：70份粗盐、35份氨基磺酸、10份柠檬酸钠、8份柠檬酸、5份扁桃酸、8份五倍子酸、9份水性聚氨酯和2份魔芋糖蛋白；所述魔芋糖蛋白采用如下方法制得：
1）将魔芋清洗、去皮，于60℃下干燥8h后进行粉碎，得到魔芋粉；
2）将步骤1）所述魔芋粉与pH7.0的Na2HPO4-NaH2PO4缓冲溶液以1 g：200 mL的质量体积比混合，于50℃超声浸提2 h后，取浸提液过滤，收集清液；其中，所述超声的功率为300W；
3）将步骤2）收集的所述清液与乙醇按照1:2的体积比混合并于室温下静置5h后，收集沉淀；
4）用水清洗沉淀至少两次，将清洗后的沉淀于60℃下干燥8 h，得到所述魔芋糖蛋白。
采用本实施例盐复合物对金属和瓷器进行清洗，结果显示清洁后的金属表面无污渍和锈斑、具有明显的金属光泽，清洁没有使金属表面出现裂纹，还对原有已存在金属表面裂纹进行了填补，使金属的表面光滑，避免了原存在的金属裂纹带来的金属断裂风险；清洁后的瓷器由黄色恢复到本色且没有局部有色色斑沉淀存在，清洁没有使瓷器出现脱色、釉质脱落的现象，且对瓷器原先表面存在的孔隙进行了修补，保证了瓷器表面的光滑完整，在保证良好清洁效果的同时，避免了对金属和瓷器造成伤害。采用本实施例清洁还可以在金属和瓷器的表面带来一层保护层，用以隔绝外界环境直接与金属和瓷器接触，可以长效保证金属和瓷器不再被污染而沾染污渍或与氧气发生反应造成生锈。
最后说明的是，以上实施例仅用以说明本发明的技术方案而非限制，尽管参照较佳实施例对本发明进行了详细说明，本领域的普通技术人员应当理解，可以对本发明的技术方案进行修改或者等同替换，而不脱离本发明技术方案的宗旨和范围，其均应涵盖在本发明的权利要求范围当中。
Claims (6)
1.一种用于清洁金属和瓷器的盐复合物，其特征在于，包括如下重量份的组分：50~70份粗盐、15~35份氨基磺酸、5~10份柠檬酸钠、1~8份柠檬酸、2~5份扁桃酸、3~8份五倍子酸、4~9份水性聚氨酯和2~7份魔芋糖蛋白。
2.根据权利要求1所述用于清洁金属和瓷器的盐复合物，其特征在于，所述魔芋糖蛋白采用如下方法制得：
1）将魔芋清洗、去皮，于60~80℃下干燥8~12h后，进行粉碎得到魔芋粉；
2）将步骤1）所述魔芋粉与Na2HPO4-NaH2PO4缓冲溶液以1g：200~400mL的质量体积比混合均匀，于50~70℃浸提2~4 h后，取浸提液过滤，收集清液；
3）将步骤2）收集的所述清液与乙醇按照1:2~4的体积比混合并于室温下静置5~8h后，收集沉淀；
4）用水清洗沉淀至少两次，将清洗后的沉淀于60~80℃下干燥6~8h，得到所述魔芋糖蛋白。
3.根据权利要求2所述用于清洁金属和瓷器的盐复合物，其特征在于，步骤2）中采用pH为6.0~7.2的Na2HPO4-NaH2PO4缓冲溶液。
4.根据权利要求2所述用于清洁金属和瓷器的盐复合物，其特征在于，步骤2）中将步骤1）所述魔芋粉与Na2HPO4-NaH2PO4缓冲溶液以1g：200~400 mL的质量体积比混合均匀，于50~70℃下超声浸提2~4h，其中，所述超声的功率为300~450 W。
5.一种对金属和瓷器进行清洗的方法，其特征在于，采用权利要求1~4任一所述用于清洁金属和瓷器的盐复合物对金属和瓷器进行清洗。
6.根据权利要求5所述对金属和瓷器进行清洗的方法，其特征在于，将所述用于清洁金属和瓷器的盐复合物与水按照1g：10~50mL的质量体积比混合配制成清洁液，采用所述清洁液对金属和瓷器进行清洗。