CN106046543A - PP wood-plastic ground heating floor material and preparation method thereof - Google Patents
PP wood-plastic ground heating floor material and preparation method thereof Download PDFInfo
- Publication number
- CN106046543A CN106046543A CN201610501641.4A CN201610501641A CN106046543A CN 106046543 A CN106046543 A CN 106046543A CN 201610501641 A CN201610501641 A CN 201610501641A CN 106046543 A CN106046543 A CN 106046543A
- Authority
- CN
- China
- Prior art keywords
- wood
- parts
- ground heating
- heating floor
- floor material
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Pending
Abstract
The invention provides a PP wood-plastic ground heating floor material and a preparation method thereof. The PP wood-plastic ground heating floor material is mainly prepared from the following raw materials: 100 parts of PP resin powder, 55-80 parts of poplar powder of 80 meshes, 40-60 parts of Al(OH)3, 5-6 parts of a silane coupling agent, 2-3 parts of barium stearate, 1.5-3 parts of zinc borate, 0.5-1.5 parts of an antioxidant, 0.2-0.5 part of acrylic acid (AA), 0.2-0.5 part of titanium dioxide and 1-2 parts of polyethylene wax. The invention further provides a preparation method of the PP wood-plastic ground heating floor material. With the combination of the formula and the preparation method, the problems that a conventional floor heating plate which is made of a wood-plastic material is generally poor in mechanical properties, thermal resistance and aging resistance can be solved.
Description
Technical field
The invention belongs to heating materials technical field, be specifically related to a kind of PP wood and mould ground heating floor material and preparation side thereof
Method.
Background technology
Ground heating floor refers to be applicable to the floor of low temperature hydraulic floor heating (abbreviation floor heating).Need to possess good breathability
And while heat sinking function, possess thermostability and the feature of environmental protection.Ground heating floor optimal pavement material at present is solid wooden compound floor, but
This floor needs to use a large amount of adhesive and paint in process of production, and both materials can discharge a large amount of formaldehyde.Current is general
Although the floor that wooden supporter moulding material makes accomplished content of formaldehyde far below Standard, but when using as ground heating floor its
Mechanical property, heat resistance, resistance to ag(e)ing all have problems.
Summary of the invention
The technical problem to be solved is to provide a kind of PP wood to mould ground heating floor material and preparation method thereof, energy
Enough solving the floor heating floor that current Wood-plastic material makes, mechanical property, heat resistance and resistance to ag(e)ing are the most poor
Problem.
In the present invention, " consumption ", " part " are all quality criterias, and the amount of each component is all on the basis of 100 parts of PP resins.
For solving above-mentioned existing technical problem, the present invention uses following scheme:
Ground heating floor material moulded by a kind of PP wood, mainly includes that following raw material is made: PP resin-oatmeal 100 parts, 80 mesh Poplar Powders
55-80 part, Al (OH)3 40-60 part, silane coupler 5-6 part, barium stearate 2-3 part, Firebrake ZB 1.5-3 part, antioxidant
0.5-1.5 part, acrylic acid (AA) 0.2-0.5 part, titanium dioxide 0.2-0.5, Tissuemat E 1-2 part.
As preferably, described 80 mesh Poplar Powder water content ＜ 2wt%.
As preferably, described antioxidant uses antioxidant 1076, and it is mainly composed of β-(3,5-di-t-butyl-4-hydroxyls
Base phenyl)-propanoic acid positive octadecanol ester.
The preparation method of ground heating floor material moulded by this PP wood, comprises the following steps:
(1) according to proportioning raw materials, PP resin-oatmeal, 80 mesh Poplar Powders, silane coupler, barium stearate are added in blender mixed
Closing, rotating speed is 450 revs/min, and the time is 8-10 minute, and temperature is 90 DEG C, obtains mixture standby；
(2) batch mixing step (1) obtained, adds Al (OH)3, Firebrake ZB, antioxidant, acrylic acid (AA), titanium dioxide, poly-second
Alkene wax continues stirring, and rotating speed is 1200 revs/min, and the time is 10-12 minute, and temperature is 115 DEG C, obtains mixture standby；
(3) pelletize is carried out at a temperature of the mixture obtained in step (2) being joined comminutor 130 DEG C, by cold for the pellet obtained
But, after, obtain a kind of PP wood and mould ground heating floor material former material granule；
(4) the granular Wood-plastic material obtained in step (3) being passed through extruding production line, extrusion temperature controls at 165 DEG C-185 DEG C
Between, ground heating floor material moulded by the PP wood that extruding production line makes different size according to difform mould.
The invention have benefit that: the present invention uses technique scheme to provide a kind of PP wood to mould ground heating floor material
And preparation method thereof, it is possible to solve the floor heating floor that current Wood-plastic material makes, mechanical property, heat resistance and resistance to always
The problem that the property changed is the most poor.
Detailed description of the invention
The present invention is described in detail, in illustrative examples and the explanation of this present invention below in conjunction with specific embodiment
It is used for explaining the present invention, but not as a limitation of the invention.
Embodiment 1
Ground heating floor material moulded by a kind of PP wood, mainly includes that following raw material is made: PP resin-oatmeal 100 parts, 80 mesh Poplar Powders
55 parts, Al (OH)3 40 parts, silane coupler 5 parts, barium stearate 2 parts, Firebrake ZB 1.5 parts, antioxidant 1 part, acrylic acid (AA)
0.2 part, titanium dioxide 0.2, Tissuemat E 1 part；Described 80 mesh Poplar Powder water content ＜ 2wt%；Described antioxidant uses antioxidant
1076, it is mainly composed of β-(3,5-di-tert-butyl-hydroxy phenyl)-propanoic acid positive octadecanol ester.
The preparation method of ground heating floor material moulded by this PP wood, comprises the following steps:
(1) according to proportioning raw materials, PP resin-oatmeal, 80 mesh Poplar Powders, silane coupler, barium stearate are added in blender mixed
Closing, rotating speed is 450 revs/min, and the time is 8 minutes, and temperature is 90 DEG C, obtains mixture standby；
(2) batch mixing step (1) obtained, adds Al (OH)3, Firebrake ZB, antioxidant, acrylic acid (AA), titanium dioxide, poly-second
Alkene wax continues stirring, and rotating speed is 1200 revs/min, and the time is 10 minutes, and temperature is 115 DEG C, obtains mixture standby；
(3) pelletize is carried out at a temperature of the mixture obtained in step (2) being joined comminutor 130 DEG C, by cold for the pellet obtained
But, after, obtain a kind of PP wood and mould ground heating floor material former material granule；
(4) the granular Wood-plastic material obtained in step (3) being passed through extruding production line, extrusion temperature controls at 165 DEG C-185 DEG C
Between, ground heating floor material moulded by the PP wood that extruding production line makes different size according to difform mould.
Embodiment 2
Ground heating floor material moulded by a kind of PP wood, mainly includes that following raw material is made: PP resin-oatmeal 100 parts, 80 mesh Poplar Powders
70 parts, Al (OH)3 50 parts, silane coupler 6 parts, barium stearate 2.5 parts, Firebrake ZB 2 parts, antioxidant 1 part, acrylic acid (AA)
0.4 part, titanium dioxide 0.3, Tissuemat E 1.5 parts；Described 80 mesh Poplar Powder water content ＜ 2wt%；Described antioxidant uses antioxygen
Agent 1076, it is mainly composed of β-(3,5-di-tert-butyl-hydroxy phenyl)-propanoic acid positive octadecanol ester.
The preparation method of ground heating floor material moulded by this PP wood, comprises the following steps:
(1) according to proportioning raw materials, PP resin-oatmeal, 80 mesh Poplar Powders, silane coupler, barium stearate are added in blender mixed
Closing, rotating speed is 450 revs/min, and the time is 9 minutes, and temperature is 90 DEG C, obtains mixture standby；
(2) batch mixing step (1) obtained, adds Al (OH)3, Firebrake ZB, antioxidant, acrylic acid (AA), titanium dioxide, poly-second
Alkene wax continues stirring, and rotating speed is 1200 revs/min, and the time is 11 minutes, and temperature is 115 DEG C, obtains mixture standby；
(3) pelletize is carried out at a temperature of the mixture obtained in step (2) being joined comminutor 130 DEG C, by cold for the pellet obtained
But, after, obtain a kind of PP wood and mould ground heating floor material former material granule；
(4) the granular Wood-plastic material obtained in step (3) being passed through extruding production line, extrusion temperature controls at 165 DEG C-185 DEG C
Between, ground heating floor material moulded by the PP wood that extruding production line makes different size according to difform mould.
Embodiment 3
Ground heating floor material moulded by a kind of PP wood, mainly includes that following raw material is made: PP resin-oatmeal 100 parts, 80 mesh Poplar Powders
80 parts, Al (OH)3 60 parts, silane coupler 6 parts, barium stearate 3 parts, Firebrake ZB 3 parts, antioxidant 1.5 parts, acrylic acid (AA)
0.5 part, titanium dioxide 0.5, Tissuemat E 2 parts；Described 80 mesh Poplar Powder water content ＜ 2wt%；Described antioxidant uses antioxidant
1076, it is mainly composed of β-(3,5-di-tert-butyl-hydroxy phenyl)-propanoic acid positive octadecanol ester.
The preparation method of ground heating floor material moulded by this PP wood, comprises the following steps:
(1) according to proportioning raw materials, PP resin-oatmeal, 80 mesh Poplar Powders, silane coupler, barium stearate are added in blender mixed
Closing, rotating speed is 450 revs/min, and the time is 10 minutes, and temperature is 90 DEG C, obtains mixture standby；
(2) batch mixing step (1) obtained, adds Al (OH)3, Firebrake ZB, antioxidant, acrylic acid (AA), titanium dioxide, poly-second
Alkene wax continues stirring, and rotating speed is 1200 revs/min, and the time is 12 minutes, and temperature is 115 DEG C, obtains mixture standby；
(3) pelletize is carried out at a temperature of the mixture obtained in step (2) being joined comminutor 130 DEG C, by cold for the pellet obtained
But, after, obtain a kind of PP wood and mould ground heating floor material former material granule；
(4) the granular Wood-plastic material obtained in step (3) being passed through extruding production line, extrusion temperature controls at 165 DEG C-185 DEG C
Between, ground heating floor material moulded by the PP wood that extruding production line makes different size according to difform mould.
The principle of above-described embodiment only illustrative present invention and effect thereof, not for limiting the present invention.Any ripe
Above-described embodiment all can be modified under the spirit and the scope of the present invention or change by the personage knowing this technology.Cause
This, have usually intellectual such as complete with institute under technological thought without departing from disclosed spirit in art
All equivalences become are modified or change, and must be contained by the claim of the present invention.
Claims (2)
1. ground heating floor material and preparation method thereof moulded by a PP wood, it is characterised in that mainly include that following raw material is made:
PP resin-oatmeal 100 parts, 80 mesh Poplar Powder 55-80 parts, Al (OH)3 40-60 part, silane coupler 5-6 part, barium stearate 2-3 part,
Firebrake ZB 1.5-3 part, antioxidant 0.5-1.5 part, acrylic acid (AA) 0.2-0.5 part, titanium dioxide 0.2-0.5, Tissuemat E 1-2
Part；Described 80 mesh Poplar Powder water content ＜ 2wt%；Described antioxidant uses antioxidant 1076, and it is mainly composed of β-(3,5-
Di-tert-butyl-hydroxy phenyl)-propanoic acid positive octadecanol ester.
The preparation method of ground heating floor material moulded by PP wood the most according to claim 1, it is characterised in that include following step
Rapid:
(1) according to proportioning raw materials, PP resin-oatmeal, 80 mesh Poplar Powders, silane coupler, barium stearate are added in blender mixed
Closing, rotating speed is 450 revs/min, and the time is 8-10 minute, and temperature is 90 DEG C, obtains mixture standby；
(2) batch mixing step (1) obtained, adds Al (OH)3, Firebrake ZB, antioxidant, acrylic acid (AA), titanium dioxide, poly-second
Alkene wax continues stirring, and rotating speed is 1200 revs/min, and the time is 10-12 minute, and temperature is 115 DEG C, obtains mixture standby；
(3) pelletize is carried out at a temperature of the mixture obtained in step (2) being joined comminutor 130 DEG C, by cold for the pellet obtained
But, after, obtain a kind of PP wood and mould ground heating floor material former material granule；
(4) the granular Wood-plastic material obtained in step (3) being passed through extruding production line, extrusion temperature controls at 165 DEG C-185 DEG C
Between, extruding production line makes the ABS Wood-plastic material of different size according to difform mould.