A kind of functional non-woven fabric chip of tripolite loading paclitaxel
Technical field
The present invention relates to disposable sanitary articles field, particularly relate to a kind of tripolite loading paclitaxel functional non-woven fabric
Chip.
Background technology
Paclitaxel in Ramulus et folium taxi cuspidatae Extract has the active anticancer of uniqueness, and in 1992, U.S. FDA passed through paclitaxel
Certification as PTS.
Paclitaxel is polymerized by promotion, prevention microtubule depolymerization, thus the division of anticancer.Can dissolve in blood vessel simultaneously
Metabolism of lipid and cholesterol, allow erythrocyte carry more oxygen and nutrient to whole body, for hypertension. hyperlipidemia. hyperglycemia
Regulation effect is had etc. disease.
Paclitaxel is as cancer patient's standard chemotherapeutic agents, and it is big that it exists side effect, is only suitable for use during chemotherapy, additionally
Chemotherapy stage terminates, and medicine is the most just stopped using.Recently as being found of other medical values of paclitaxel, begin with people's research
The application of its Transdermal absorption, as the effective measures reducing toxic and side effects.The side effect that paclitaxel injection is common: 80%
User can lose hair, the user of 18.2% has pain reaction, and the most special body constitution (hypertension, diabetes, Peptic Ulcers) exists
Use paclitaxel injection can produce super anaphylaxis, cause using.
Transdermal drug delivery system is a kind of technical scheme being totally different from conventional administration mode, the minimizing people of energy amplitude peak
The side reaction of body, single-dose amount is few simultaneously, and administration time is long, and side effect is little, is more suitable for daily nursing health care and uses.Transdermal
Being administered completely can be without the solubilizing agent of paclitaxel: polyoxyethylene castor oil, directly reduces because using polyoxyethylene caster
The human body side reaction that oil causes.
Although transdermal administration can be substantially reduced side reaction, but as how can be controlled speed. stable to internal defeated
Send paclitaxel, same particular importance.Find that kieselguhr has meaning especially for the transporting velocity of stability contorting paclitaxel under study for action
Justice, has no special event both at home and abroad.
Research is a kind of easy to use, and the tripolite loading paclitaxel functional non-woven fabric chip that Transdermal absorption is administered just has important
Meaning.
Summary of the invention
The present invention is the daily use in order to solve paclitaxel, promotes the Transdermal absorption of paclitaxel, it is to avoid the poison of paclitaxel
Side effect.The open a kind of tripolite loading paclitaxel functional non-woven fabric chip of the present invention, it be pure viscose fiber spun lacing without
Spin a kind of paste of coating on cloth.Then cutting in flakes by this non-woven fabrics by required specification, this paclitaxel diatom functional chip is born
It is loaded on surface layer or the sublevel of disposable sanitary articles, is pasted on human body, there is health care and improve the effect of body immunity,
Also having the effect of easing pain and diminishing inflammation, prevention and daily nursing for cancer, particularly breast carcinoma have positive effect simultaneously.
The technical scheme is that: mix up paste by formula, paste formulation forms: paclitaxel 0.005-0.05%,
Kieselguhr 5-20%, menthol 0.05-0.5%, stearic acid 1-10%, glycerol 1-5%,
Lanoline 0.5-5%, liquid paraffin 1-10%, octadecanol 0.2-2%, triethanolamine 0.5-5%, deionized water surplus.
The present invention paste modulation uniformly after, by being (10-30) with pure viscose fiber spun-laced nonwoven fabric mass ratio:
(90-70) coat on pure viscose fiber spun-laced nonwoven fabric.
The tripolite loading paclitaxel functional non-woven fabric chip of the present invention is cut into tablet by different product specification, negative
It is loaded in disposable sanitary articles surface or sublevel can obtain the disposable sanitary articles containing paclitaxel diatom function, for human body
Nursing.
Tripolite loading paclitaxel functional non-woven fabric chip dies is cut into roundel, and on breast pad production line, PUR is fixed
It is positioned at breast pad surface, paclitaxel diatom breast pad can be produced, for chest health;By slitting for paclitaxel functional chip
Shape thing, on production line of toilet napkin, PUR is positioned sanitary towel's surface layer or sublevel, can produce paclitaxel diatom function and defend
Raw towel, keeps healthy for reproductive system.
The invention has the beneficial effects as follows, use menthol, stearic acid, glycerol, lanoline, liquid paraffin, mixing of octadecanol
Close dissolution system and dissolve paclitaxel;Being dissolved by mixed system, stable by tripolite loading, after adding pure water, paclitaxel is same
Sample keeps stable, does not separate out.Whole paste is designed as lipophilic ulsions, beneficially paclitaxel infiltration.Simultaneously in order to controlled
Release, uses kieselguhr as taxadol slow release controlling agent.By kieselguhr controlled release paclitaxel, improve relaxing of skin feel
Adaptive, it is to avoid zest.
In order to verify that the present invention reduces the toxic and side effects of product, by " disinfection technology standard ", New Zealand TWO is used to do
Patch zest is tested, and patch area 2.5 centimetres * 2.5 centimetres, 1 hour .24 hour .48 hour testing time, test result is such as
Following table.
Test result, the paclitaxel diatom functional chip nonirritant of the present invention.
In order to verify the stable controlled velocity of tripolite loading paclitaxel functional non-woven fabric chip of the present invention, use New Zealand
TWO is cooked the test of patch infiltration rate, patch area 2.5 centimetres * 2.5 centimetres, test 15 minutes, 1 hour, 4 hours, 12 little
Time, 24 hours, the content of paclitaxel in the tripolite loading paclitaxel functional non-woven fabric chip in patch after 48 hours, by purple
Remain the change of content of taxol after the Transdermal absorption of China fir alcohol, draw the rate of release change of paclitaxel.Content of taxol is tested
Method HPLC(high performance liquid chromatography).Option A mastic formula is added without kieselguhr, quantity deionized water polishing, adjust glutinous
Spend basically identical with option b.Option b mastic formula adds kieselguhr.
Test result such as following table.
Test result, paclitaxel in the tripolite loading paclitaxel functional non-woven fabric chip of option b (addition kieselguhr)
Rate of release is more steady.Option A is distinguished the most over the course of 15 mins, after 1 hour, after 4 hours, after 12 hours, after 24 hours, and 48 hours
Rear paclitaxel Transdermal absorption 5.88%, 11.27%, 18.64%, 33.82%, 53.43%, 58.82%.And option b is respectively at 15 points
Zhong Hou, after 1 hour, after 4 hours, after 12 hours, after 24 hours, paclitaxel Transdermal absorption 4.41%, 7.35% after 48 hours,
15.7%, 29.9%, 45.59%, 57.35%.Add the kieselguhr infiltration rate for control paclitaxel, particularly control the initial stage
Infiltration rate, has obvious effect, reaches the purpose steadily discharged, and to the later stage, nor affects on the total amount of Transdermal absorption.
Detailed description of the invention
Embodiment 1
5.94 kilograms of stearic acid, 2.47 kg of glycerin, 0.99 kilogram of Pilus Caprae seu Ovis is added in 50 liters of rustless steel chuck heating and stirring pots
Fat, 6.93 kg liquid paraffin, 0.99 kilogram of octadecanol, open stirring paddle, 60 degrees Celsius 30 minutes.It is subsequently adding menthol
1.1 kilograms, paclitaxel 0.01 kilogram, 60 degrees Celsius 30 minutes.Adding 10 kilograms of kieselguhr, stirring is cooled to 45 degrees Celsius.
Discharging, rolls one time with three-roller.Transfer the material in 150 liters of dispersion cylinder the most again, open high speed dispersor, dispersion limit, limit
Add the mixed liquor being made up of 69.59 kilograms of deionized waters and 1.98 kilograms of triethanolamine, feed complete, disperse 15 minutes, go out
Material, produces the paste being coated with.
Preparing 500 kilograms of pure viscose fiber spun laced fabrics, fabric width 1 meter, grammes per square metre 80 grams/m, by every square metre of non-woven fabrics
20 grams of pastes of upper coating, complete coating on circular screen printer.Obtain a kind of tripolite loading paclitaxel functional non-woven fabric core
Sheet.
On breast pad production line, tripolite loading paclitaxel functional non-woven fabric chip dies is cut into the disk of 13 centimetres, heat
The melten gel back side is positioned breast pad surface, thus obtains a kind of breast pad containing paclitaxel diatom function.
Embodiment 2
3.10 kilograms of stearic acid, 1.15 kg of glycerin, 1.80 kilograms of Pilus Caprae seu Oviss are added in 20 liters of rustless steel chuck heating and stirring pots
Fat, 3.00 kg liquid paraffin, 0.55 kilogram of octadecanol, open stirring paddle, 60 degrees Celsius 30 minutes.It is subsequently adding menthol
0.50 kilogram, paclitaxel 0.03 kilogram, 60 degrees Celsius 30 minutes.Adding 6 kilograms of kieselguhr, stirring is cooled to 45 degrees Celsius.
Discharging, rolls one time with three-roller.Transfer the material in 150 liters of dispersion cylinder the most again, open high speed dispersor, dispersion limit, limit
Add the mixed liquor being made up of 82.87 kilograms of deionized waters and 1.00 kilograms of triethanolamine, feed complete, disperse 15 minutes, go out
Material, produces the paste being coated with.
Preparing 500 kilograms of pure viscose fiber spun laced fabrics, fabric width 1 meter, grammes per square metre 60 grams/m, by every square metre of non-woven fabrics
10 grams of pastes of upper coating, complete coating on circular screen printer.Obtain a kind of tripolite loading paclitaxel functional non-woven fabric core
Sheet.
On production line of toilet napkin, will be containing the tripolite loading paclitaxel crosscutting one-tenth of functional non-woven fabric chip 3 centimetres * 8 lis
The rectangle tablet of rice, the PUR back side is positioned sanitary towel's sublevel, thus obtains a kind of containing paclitaxel diatom function
Sanitary towel.
Embodiment 3
6.00 kilograms of stearic acid, 2.35 kg of glycerin, 0.70 kilogram of Pilus Caprae seu Ovis is added in 50 liters of rustless steel chuck heating and stirring pots
Fat, 3.00 kg liquid paraffin, 0.55 kilogram of octadecanol, open stirring paddle, 60 degrees Celsius 30 minutes.It is subsequently adding menthol
1.20 kilograms, paclitaxel 0.04 kilogram, 60 degrees Celsius 30 minutes.Adding 12 kilograms of kieselguhr, it is Celsius that stirring is cooled to 45
Degree.Discharging, a piece of with three-roller rolling.Transfer the material in 150 liters of dispersion cylinder the most again, open high speed dispersor, while divide
Dissipate limit and add the mixed liquor being made up of 72.66 kilograms of deionized waters and 1.50 kilograms of triethanolamine, feed complete, disperse 15 points
Clock, discharging, produce the paste being coated with.
Preparing 500 kilograms of pure viscose fiber spun laced fabrics, fabric width 1 meter, grammes per square metre 60 grams/m, by every square metre of non-woven fabrics
15 grams of pastes of upper coating, complete coating on circular screen printer.Obtain a kind of tripolite loading paclitaxel functional non-woven fabric core
Sheet.
On breast pad production line, will be containing the tripolite loading paclitaxel crosscutting one-tenth of functional non-woven fabric chip 3 centimetres * 3 centimetres
Square tablet, the PUR back side is positioned the sublevel of breast pad, thus obtains a kind of breast containing paclitaxel diatom function
Pad.