CN105238970B - A kind of aluminium alloy of high-strength high-tractility - Google Patents
A kind of aluminium alloy of high-strength high-tractility Download PDFInfo
- Publication number
- CN105238970B CN105238970B CN201510792711.1A CN201510792711A CN105238970B CN 105238970 B CN105238970 B CN 105238970B CN 201510792711 A CN201510792711 A CN 201510792711A CN 105238970 B CN105238970 B CN 105238970B
- Authority
- CN
- China
- Prior art keywords
- aluminium alloy
- present
- tractility
- strength
- surplus
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
The invention discloses the aluminium alloy of a kind of high-strength high-tractility, being grouped into according to the one-tenth of mass percent by following: Si 5 ~ 5.5%, Mg 0.02 ~ 0.08%, Fe 0.6 ~ 0.7%, Bi 0.5 ~ 0.55%, W 0.05 ~ 0.08%, Ti 0.02 ~ 0.09%, surplus is Al.The present invention based on Al Si alloy, add appropriate Mg, Fe, Bi, W, Ti, making the high comprehensive performance of the present invention: under room temperature, tensile strength is between 450 ~ 520MPa, yield strength is 285 ~ 375MPa, and Brinell hardness is 135 ~ 160, percentage elongation is 15.8 ~ 18.8%, wear rate 1.15*10‑9~1.82*10‑9 g·mm‑1·N‑1.Ensure that the present invention has higher tensile strength and yield strength.
Description
Technical field
The present invention relates to field of aluminum alloys, the aluminium alloy of a kind of high-strength high-tractility.
Background technology
Aluminium alloy owing to having the features such as high intensity, high tenacity, light structures, corrosion-resistant, processability good, is easily recycled,
It it is metal material that modern society is pursued, most promising.It is widely used in the civilian and armies such as traffic, building materials, Aeronautics and Astronautics
Work field, has irreplaceable important function in national economy and national defense construction.Development of the West Regions, modern railway transportation,
Under the application backgrounds such as bridge, large span, high load, extra-high type building window and curtain wall need one to have higher-strength and good
The material of good elongation percentage, 6061 aluminium alloy processing characteristicies and elongation percentage etc. can not meet this requirement.ALcoa company of the U.S.
Once preparing 6013 aluminium alloys, this aluminium alloy has higher intensity and good corrosion resistance.But owing to 6013 aluminium alloys extend
Rate is low, processing characteristics is not good enough, so its application is constantly subjected to limit.
Summary of the invention
It is an object of the invention to provide the aluminium alloy of the high-strength high-tractility of a kind of low cost, good combination property, with
The problem solving to propose in above-mentioned background technology.
For achieving the above object, the present invention provides following technical scheme:
The aluminium alloy of a kind of high-strength high-tractility, is grouped into according to the one-tenth of mass percent by following: Si 5 ~ 5.5%,
Mg 0.02 ~ 0.08%, Fe 0.6 ~ 0.7%, Bi 0.5 ~ 0.55%, W 0.05 ~ 0.08%, Ti 0.02 ~ 0.09%, surplus is Al.
As the further scheme of the present invention: the aluminium alloy of described high-strength high-tractility, by following according to percent mass
The one-tenth of ratio is grouped into: Si 5.2 ~ 5.3%, Mg 0.04 ~ 0.06%, Fe 0.63 ~ 0.67%, Bi 0.52 ~ 0.54%, W 0.06 ~
0.07%, Ti 0.05 ~ 0.07%, surplus is Al.
As the further scheme of the present invention: the aluminium alloy of described high-strength high-tractility, by following according to percent mass
The one-tenth of ratio is grouped into: Si 5.25%, Mg 0.05%, Fe 0.65%, Bi 0.53%, W 0.065%, Ti 0.06%, and surplus is Al.
Compared with prior art, the invention has the beneficial effects as follows:
The present invention based on Al-Si alloy, add appropriate Mg, Fe, Bi, W, Ti so that the combination property of the present invention is excellent
Good: under room temperature, tensile strength is between 450 ~ 520MPa, yield strength is 285 ~ 375MPa, and Brinell hardness is 135 ~ 160, elongation
Rate is 15.8 ~ 18.8%, wear rate 1.15*10-9~1.82*10-9 g·mm-1·N-1.Ensure that the present invention has higher tension
Intensity and yield strength.Owing to the casting temperature of aluminium alloy is low, extrusion technique comparative maturity, continuous extrausion process can be used to prepare,
Thus production cost is relatively low.
Detailed description of the invention
Below in conjunction with the embodiment of the present invention, the technical scheme in the embodiment of the present invention is clearly and completely described,
Obviously, described embodiment is only a part of embodiment of the present invention rather than whole embodiments.Based in the present invention
Embodiment, the every other embodiment that those of ordinary skill in the art are obtained under not making creative work premise, all
Belong to the scope of protection of the invention.
Embodiment 1
In the embodiment of the present invention, the aluminium alloy of a kind of high-strength high-tractility, by the following composition according to mass percent
Composition: Si 5%, Mg 0.02%, Fe 0.6%, Bi 0.5%, W 0.05%, Ti 0.02%, surplus is Al.
Embodiment 2
In the embodiment of the present invention, the aluminium alloy of a kind of high-strength high-tractility, by the following composition according to mass percent
Composition: Si 5.5%, Mg 0.08%, Fe 0.7%, Bi 0.55%, W 0.08%, Ti 0.09%, surplus is Al.
Embodiment 3
In the embodiment of the present invention, the aluminium alloy of a kind of high-strength high-tractility, by the following composition according to mass percent
Composition: Si 5.2%, Mg 0.04%, Fe 0.63%, Bi 0.52%, W 0.06%, Ti 0.05%, surplus is Al.
Embodiment 4
In the embodiment of the present invention, the aluminium alloy of a kind of high-strength high-tractility, by the following composition according to mass percent
Composition: Si 5.3%, Mg 0.06%, Fe 0.67%, Bi 0.54%, W 0.07%, Ti 0.07%, surplus is Al.
Embodiment 5
In the embodiment of the present invention, the aluminium alloy of a kind of high-strength high-tractility, by the following composition according to mass percent
Composition: Si 5.25%, Mg 0.05%, Fe 0.65%, Bi 0.53%, W 0.065%, Ti 0.06%, surplus is Al.
The preparation method of described aluminium alloy, including following operating procedure: by aluminium ingot, magnesium ingot, Si additive, Fe additive,
Bi additive, W additive, Ti additive shove charge add heat fusing；Add and smelt flux refine；The melt obtained is carried out pre-place
Reason；Then melting online treatment is carried out；Filter；Casting；Homogenizing；Cooling finally gives aluminium alloy.
The aluminium alloy capability testing result of each embodiment is as shown in table 1.
Table 1
It is obvious to a person skilled in the art that the invention is not restricted to the details of above-mentioned one exemplary embodiment, Er Qie
In the case of the spirit or essential attributes of the present invention, it is possible to realize the present invention in other specific forms.Therefore, no matter
From the point of view of which point, all should regard embodiment as exemplary, and be nonrestrictive, the scope of the present invention is by appended power
Profit requires rather than described above limits, it is intended that all by fall in the implication of equivalency and scope of claim
Change is included in the present invention.
Although moreover, it will be appreciated that this specification is been described by according to embodiment, but the most each embodiment only wraps
Containing an independent technical scheme, this narrating mode of description is only that for clarity sake those skilled in the art should
Description can also be formed those skilled in the art through appropriately combined as an entirety, the technical scheme in each embodiment
May be appreciated other embodiments.
Claims (3)
1. the aluminium alloy of a high-strength high-tractility, it is characterised in that be grouped into according to the one-tenth of mass percent by following:
Si 5 ~ 5.5%, Mg 0.02 ~ 0.08%, Fe 0.6 ~ 0.7%, Bi 0.5 ~ 0.55%, W 0.05 ~ 0.08%, Ti 0.02 ~ 0.09%,
Surplus is Al.
The aluminium alloy of high-strength high-tractility the most according to claim 1, it is characterised in that by following according to quality hundred
The one-tenth of proportion by subtraction is grouped into: Si 5.2 ~ 5.3%, Mg 0.04 ~ 0.06%, Fe 0.63 ~ 0.67%, Bi 0.52 ~ 0.54%, W 0.06 ~
0.07%, Ti 0.05 ~ 0.07%, surplus is Al.
The aluminium alloy of high-strength high-tractility the most according to claim 2, it is characterised in that by following according to quality hundred
The one-tenth of proportion by subtraction is grouped into: Si 5.25%, Mg 0.05%, Fe 0.65%, Bi 0.53%, W 0.065%, Ti 0.06%, and surplus is
Al。