CN104045900A - Plastic composite material for tray - Google Patents
Plastic composite material for tray Download PDFInfo
- Publication number
- CN104045900A CN104045900A CN201410282943.8A CN201410282943A CN104045900A CN 104045900 A CN104045900 A CN 104045900A CN 201410282943 A CN201410282943 A CN 201410282943A CN 104045900 A CN104045900 A CN 104045900A
- Authority
- CN
- China
- Prior art keywords
- pallet
- plastics composite
- silane
- parts
- calcium carbonate
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Granted
Abstract
The invention relates to a plastic composite material for a tray and belongs to the technical field of plastic materials. The material provided by the invention has high fracture-resistant and impact-resistant performances, high shore hardness and good mechanical property. The plastic composite material for the tray provided by the invention is mainly prepared from the following components in parts by weight: 70-85 parts of high-density polyethylene or high-density polypropylene, 2.0-3.0 parts of sorbitan monostearate, 0.5-1.0 part of polytetrafluoroethylene, 2.0-5.0 parts of ethylene-methacrylic acid copolymer, 0.5-0.8 part of silane coupling agent, 5.0-10 parts of nano inorganic filler, 10-13 parts of synthesized rubber, 8.0-12 parts of fibers, 2.0-5.0 parts of flame retardant and 1.0-2.0 parts of antioxidant. The composite material has high fracture-resistant and impact-resistant performances and high shore hardness.
Description
Technical field
The present invention relates to a kind of plastics composite for pallet, belong to plastic material technical field.
Background technology
Pallet has another name called pallet, and pallet is that placement for collecting dress, stacking, carrying and transport is as the goods of unit load and the levelling bench arrangement of goods.As with the similar a kind of unit load devices of freight container, pallet has now been widely used in the fields such as production, transport, storage and circulation, is considered to one of two large key innovations in 20th century material flow industry.Pallet, as handling important in Logistics Operation process, storage and transportation equipment, supports the use and in modern logistics, is bringing into play huge effect with fork truck.The benefit that pallet brings to modern logistics industry is mainly reflected in: can realize blocking, standardization and the stdn of article packing, protection article, facilitate logistics and commodity-circulate,
At present, mostly adopt iron, common plastics or Wood-plastic material to make for the production of the material of pallet, and adopt pallet that polyethylene or acrylic plastering make for the advantage such as lightweight, cheapness, there is larger application space.As the making method of the disclosed a kind of continuous glass fibre reinforced thermoplastic plastics pallet of Chinese patent application (publication number: CN103214862A), it mainly adopts polypropylene, glass fibre, oxidation inhibitor and coupling agent raw material.Than common plastics pallet its have that mechanical strength is high, the strong and scrape resistant texts of excellent spring, non-deformability.But the pallet ubiquity resistance to fracture, the poor problem of shock resistance that adopt common plastics to make.
Summary of the invention
The present invention is directed to above problems of the prior art, a kind of plastics composite for pallet is provided, and the technical problem of solution is to realize the pallet that adopts plastics composite of the present invention to make to have resistance to fracture and the high effect of shock resistance, shore hardness and mechanical property.
The object of the invention is to be achieved by the following technical programs, a kind of plastics composite for pallet, this plastics composite is mainly made up of the weight part of following composition:
High density polyethylene(HDPE) or polypropylene: 70～85; : 2.0～3.0; Tetrafluoroethylene: 0.5～1.0; Ethylene-methacrylic acid copolymer: 2.0～5.0; Silane coupling agent: 0.5～0.8; Nanometer inorganic filler: 5.0～10; Synthetic rubber: 10～13; Fiber: 8.0～12; Fire retardant: 2.0～5.0; Antioxidant: 1.0～2.0.
The present invention is for the plastics composite of pallet, taking high density polyethylene(HDPE) or polypropylene as main raw, by adding and tetrafluoroethylene acting in conjunction to improve material in resistance to fracture and shock resistance, make the pallet that adopts plastics composite of the present invention to make there is higher resistance to fracture and shock resistance, but the inventor finds to add after, the shore hardness of matrix material can reduce, shore hardness can only reach 65 left and right, therefore, the present invention is by adding after ethylene-methacrylic acid copolymer and and tetrafluoroethylene compound use, find to there is synergy between them, make on the contrary the shore hardness of material be greatly improved, shore hardness can reach more than 90, and also can further improve resistance to fracture and shock resistance, more than resistance to impact shock can reach 10MPa, simultaneously, by adding after nanometer inorganic filler, synthetic rubber and silane coupling agent compound use, make overall mechanical property can reach requirement, as performances such as tensile strength, elongation at break, flexural strengths, by adding fire retardant and antioxidant, work-ing life and the flame retardant properties that can improve product, can also add the compositions such as pigment in above-mentioned plastics composite.
At the above-mentioned plastics composite for pallet, as preferably, this plastics composite is mainly made up of the weight part of following composition:
High density polyethylene(HDPE) or polypropylene: 75～80; : 2.2～2.8; Tetrafluoroethylene: 0.6～0.8; Ethylene-methacrylic acid copolymer: 3.0～4.0; Silane coupling agent: 0.6～0.7; Nanometer inorganic filler: 6.0～8.0; Synthetic rubber: 11～12; Fiber: 10～11; Fire retardant: 2.0～3.0; Antioxidant: 1.0～1.5.
At the above-mentioned plastics composite for pallet, as preferably, described silane coupling agent is selected from one or more in vinyl trichloro silane, vinyltriethoxysilane, vinyl three (2-methoxy ethoxy) silane, γ-methacryloxypropyl trimethoxy silane, methacryloxypropyl triethoxyl silane, vinyltrimethoxy silane, γ-glycidyl ether oxygen base propyl trimethoxy silicane and γ-mercapto propyl group dimethoxy silane.By adding silane coupling agent can improve plastics composite, can will between nanometer inorganic filler and the interface of organic materials, erect " molecular bridge ", make to improve the consistency between them, improve the performance of plastics composite and increase dispersiveness and the bonding strength of nanometer inorganic filler in high density polyethylene(HDPE) or polypropylene material.As further preferred, described silane coupling agent is the mixture of γ-methacryloxypropyl trimethoxy silane and vinyl three (2-methoxy ethoxy) silane, and the weight ratio of γ-methacryloxypropyl trimethoxy silane and vinyl three (2-methoxy ethoxy) silane is 1:2.4～2.8.
At the above-mentioned plastics composite for pallet, as preferably, described nanometer inorganic filler is selected from one or more in nano silicon, nano barium sulfate, nano titanium oxide or nano-calcium carbonate.Because pigment particles is easily reunited, form macrobead, affect quality product, the inventor finds to add nanometer BaSO in co-mixing system
4with nanometer CaCO
3after two kinds of inorganic nano-fillers, can improve the dispersiveness of pigment in plastics (plastic pallet), and the opacifying power of pigmenting power and goods.As further preferred, in described plastic pallet matrix material, also contain the pigment of 1.0～1.5 weight parts, described pigment is selected from P.R.48:2 pigment (pigment red 4 8:2), P.G.7 pigment (Phthalocyanine Green G) or P.Y180 pigment (Pigment Yellow 73 180), and described inorganic nano-filler is BaSO
4with nanometer CaCO
3mixture.As further preferably, 20%～30% nanometer CaCO for described pigment
3be coated processing, first by 20%～30% nanometer CaCO of pigment weight
3after mixing with pigment, add again in plastics composite, by by pigment and nanometer CaCO
3first carry out blend, can make nanometer CaCO
3be wrapped in the surface of pigment, thereby the color articles power and the opacifying power that make are improved greatly.
At the above-mentioned plastics composite for pallet, as preferably, described synthetic rubber is silicon rubber.Adopt synthetic rubber not only easy to use, and there is oil resistant, acid and alkali-resistance, high temperature resistant, aging-resistant feature, can greatly extend the work-ing life of pallet.
At the above-mentioned plastics composite for pallet, as preferably, described fiber is selected from one or more in glass fibre, staple fibre and mineral fibre.As further preferred, described fiber is glass fibre, glass fibre can and silane coupling agent between play synergy, improve the adhesive strength of glass fibre and organic materials, as the adhesive strength between glass fibre and polyethylene or polypropylene and ethylene-methacrylic acid copolymer, improve consistency, thereby can improve the strength property of matrix material.
At the above-mentioned plastics composite for pallet, as preferably, described fire retardant is selected from one or more in kaolin, calcium carbonate and zinc borate.As further preferred, described fire retardant is the mixture of kaolin and calcium carbonate, and the weight ratio of described kaolin and calcium carbonate is 1:2～3.0.Because calcium carbonate decomposes rear calcium oxide and the carbonic acid gas of forming under hot conditions, the carbonic acid gas of formation can play good flame retardant effect.
At the above-mentioned plastics composite for pallet, described antioxidant adopts the antioxidant of this area routine, does not have special requirement, as adopted antioxidant 1010, antioxidant 168 etc.
In sum, the present invention compared with prior art has the following advantages:
Plastics composite of the present invention is by adding and tetrafluoroethylene acting in conjunction to improve material in resistance to fracture and shock resistance, makes product that matrix material makes after falling, and has higher resistance to fracture and shock resistance; By adding after ethylene-methacrylic acid copolymer and and tetrafluoroethylene compound use, there is synergy, the shore hardness of material can be reached more than 90.
Embodiment
Below by specific embodiment, technical scheme of the present invention is described in further detail, but the present invention is not limited to these embodiment.
Embodiment 1
A kind of plastics composite, it is mainly made up of the weight part of following composition:
High density polyethylene(HDPE): 85; : 3.0; Tetrafluoroethylene: 0.5; Ethylene-methacrylic acid copolymer: 2.0; Silane coupling agent vinyl trichlorosilane: 0.8; Nano titanium oxide: 10; Silicon rubber: 10; Glass fibre: 8.0; Calcium carbonate: 4.0.
Adopt above-mentioned plastics composite, make pallet according to the making method of this area routine.In particular, the making method of the pallet described in the present embodiment is as follows:
Weight part proportioning according to mentioned component takes raw material, and after adding feeding cylinder and mixing, heating and melting, then, injects in closed tray die fast, and through pressurize, injection moulding, die sinking is taken out goods and suitably pruned treating selvedge, obtains plastic pallet.
Embodiment 2
A kind of plastics composite, it is mainly made up of the weight part of following composition:
High density polyethylene(HDPE): 70; : 2.0; Tetrafluoroethylene: 1.0; Ethylene-methacrylic acid copolymer: 5.0; Silane coupling agent γ-methacryloxypropyl trimethoxy silane: 0.5; Nano silicon: 5.0; Synthetic rubber: 13; Glass fibre: 12; Fire retardant kaolin: 2.0; Antioxidant 1010: 2.0.
Adopt above-mentioned plastics composite, make pallet according to the making method of this area routine, the making method of employing is consistent with embodiment 1, repeats no more here.
Embodiment 3
A kind of plastics composite, it is mainly made up of the weight part of following composition:
High density polyethylene(HDPE): 80; : 2.8; Tetrafluoroethylene: 0.8; Ethylene-methacrylic acid copolymer: 4.0; Silane coupling agent γ-glycidyl ether oxygen base propyl trimethoxy silicane: 0.7; Nano-calcium carbonate: 6.0; Silicon rubber: 12; Mineral fibre: 11; Fire retardant: 3.0; Antioxidant 168:1.5.
Adopt above-mentioned plastics composite, make pallet according to the making method of this area routine, the making method of employing is consistent with embodiment 1, repeats no more here.
Embodiment 4
A kind of plastics composite, it is mainly made up of the weight part of following composition:
High density polyethylene(HDPE): 75; : 2.2; Tetrafluoroethylene: 0.6; Ethylene-methacrylic acid copolymer: 3.0; Silane coupling agent vinyl three (2-methoxy ethoxy) silane: 0.6; Nano titanium oxide: 8.0; Silicon rubber: 11; Glass fibre: 10; Fire retardant: 2.0, described fire retardant is the mixture of kaolin and calcium carbonate, and the weight ratio of described kaolin and calcium carbonate is 1:3.0, antioxidant 168:1.0.
Adopt above-mentioned plastics composite, make pallet according to the making method of this area routine, the making method of employing is consistent with embodiment 1, repeats no more here.
Embodiment 5
A kind of plastics composite, it is mainly made up of the weight part of following composition:
Polypropylene: 77; : 2.5; Tetrafluoroethylene: 0.7; Ethylene-methacrylic acid copolymer: 3.5; Silane coupling agent: 0.65, described silane coupling agent is the mixture of γ-methacryloxypropyl trimethoxy silane and vinyl three (2-methoxy ethoxy) silane, and the weight ratio of γ-methacryloxypropyl trimethoxy silane and vinyl three (2-methoxy ethoxy) silane is 1:2.8, nano titanium oxide: 7.0; Silicon rubber: 13; Glass fibre: 10; Fire retardant: 2.0, described fire retardant is the mixture of kaolin and calcium carbonate, and the weight ratio of described kaolin and calcium carbonate is 1:2.0, antioxidant 168:1.0.
Adopt above-mentioned plastics composite, make pallet according to the making method of this area routine, the making method of employing is consistent with embodiment 1, repeats no more here.
Embodiment 6
A kind of plastics composite, it is mainly made up of the weight part of following composition:
High density polyethylene(HDPE) or polypropylene: 80; : 2.0; Tetrafluoroethylene: 0.8; Ethylene-methacrylic acid copolymer: 3.0; Silane coupling agent: 0.6, described silane coupling agent is the mixture of γ-methacryloxypropyl trimethoxy silane and vinyl three (2-methoxy ethoxy) silane, and the weight ratio of γ-methacryloxypropyl trimethoxy silane and vinyl three (2-methoxy ethoxy) silane is 1:2.4, nano silicon: 7.0; Silicon rubber: 12; Glass fibre: 11; Fire retardant: 2.0, described fire retardant is zinc borate, antioxidant 1011:1.0.
Adopt above-mentioned plastics composite, make pallet according to the making method of this area routine, the making method of employing is consistent with embodiment 1, repeats no more here.
Embodiment 7
A kind of plastics composite, it is mainly made up of the weight part of following composition:
High density polyethylene(HDPE): 75; : 2.2; Tetrafluoroethylene: 0.6; Ethylene-methacrylic acid copolymer: 3.0; Silane coupling agent vinyl three (2-methoxy ethoxy) silane: 0.6; Nano-calcium carbonate: 8.0; Silicon rubber: 11; Glass fibre: 10; Fire retardant: 2.0; Pigment: 1.0, described pigment is P.Y180 pigment; Described fire retardant is the mixture of kaolin and calcium carbonate, and the weight ratio of described kaolin and calcium carbonate is 1:3.0, antioxidant 168:1.0.
Above-mentioned pigment can adopt P.R.48:2 pigment or P.G.7 pigment to replace.
Adopt above-mentioned plastics composite, making method according to this area routine is made pallet, in particular, the nano-calcium carbonate and the pigment that first take pigment weight 20%～30% carry out blend processing, make nano-calcium carbonate be wrapped in the surface of pigment, and then the pigment that adopts calcium carbonate processing is added in feeding cylinder and carries out blend with other raw material, after mixing, adopt again the method consistent with embodiment 1, repeat no more here.
Embodiment 8
High density polyethylene(HDPE): 80; : 2.0; Tetrafluoroethylene: 0.8; Ethylene-methacrylic acid copolymer: 4.0; Silane coupling agent vinyl three (2-methoxy ethoxy) silane: 0.8; Nano-calcium carbonate: 5.0; Silicon rubber: 11; Glass fibre: 12; Fire retardant: 3.0; Pigment: 1.5, described pigment is P.Y180 pigment; Described fire retardant is kaolin, antioxidant 168:1.0.
Adopt above-mentioned plastics composite, making method according to this area routine is made pallet, in particular, the nano-calcium carbonate and the pigment that first take pigment weight 20%～30% carry out blend processing, make nano-calcium carbonate be wrapped in the surface of pigment, and then the pigment that adopts calcium carbonate processing is added in feeding cylinder and carries out blend with other raw material, after mixing, adopt again the method consistent with embodiment 1, repeat no more here.
Embodiment 9
High density polyethylene(HDPE): 85; : 2.5; Tetrafluoroethylene: 1.0; Ethylene-methacrylic acid copolymer: 2.0; γ-methacryloxypropyl trimethoxy silane: 0.5; Nano barium carbonate: 6.0; Silicon rubber: 10; Glass fibre: 8.0; Fire retardant: 2.0; Pigment: 1.2, described pigment is P.Y180 pigment; Described fire retardant is kaolin, antioxidant 1010: 1.0.
Adopt above-mentioned plastics composite, making method according to this area routine is made pallet, in particular, the nano-calcium carbonate and the pigment that first take pigment weight 20%～30% carry out blend processing, make nano-calcium carbonate be wrapped in the surface of pigment, and then the pigment that adopts calcium carbonate processing is added in feeding cylinder and carries out blend with other raw material, after mixing, adopt again the method consistent with embodiment 1, repeat no more here.
Comparative example 1
A kind of plastics composite, it is mainly made up of the weight part of following composition:
High density polyethylene(HDPE): 75; Ethylene-methacrylic acid copolymer: 3.0; Silane coupling agent vinyl three (2-methoxy ethoxy) silane: 0.6; Nano titanium oxide: 8.0; Silicon rubber: 11; Glass fibre: 10; Fire retardant: 2.0, described fire retardant is the mixture of kaolin and calcium carbonate, and the weight ratio of described kaolin and calcium carbonate is 1:3.0, antioxidant 168:1.0.
Adopt above-mentioned plastics composite, make pallet according to the making method of this area routine, the making method of employing is consistent with embodiment 1, repeats no more here.
Comparative example 2
A kind of plastics composite, it is mainly made up of the weight part of following composition:
High density polyethylene(HDPE): 75; : 2.2; Tetrafluoroethylene: 0.6; Silane coupling agent vinyl three (2-methoxy ethoxy) silane: 0.6; Nano titanium oxide: 8.0; Silicon rubber: 11; Glass fibre: 10; Fire retardant: 2.0, described fire retardant is the mixture of kaolin and calcium carbonate, and the weight ratio of described kaolin and calcium carbonate is 1:3.0, antioxidant 168:1.0.
Adopt above-mentioned plastics composite, make pallet according to the making method of this area routine, the making method of employing is consistent with embodiment 1, repeats no more here.
The pallet of choosing at random the plastics composite making of above-described embodiment and comparative example carries out performance test, and concrete test result is as shown in table 1 below.
Table 1:
Elongation described in above-mentioned table 1 is elongation at break.Test adopts plastics composite of the present invention to be made into after pallet, by finished product drop shutter test and finished product impact test, adopt the testing method of this area routine, the height of fall that described finished product drop shutter test is finished product is 8 meters, fall 6 times, the pallet that the plastics composite of the present embodiment is made, after drop shutter test, all crack-frees and without damaging phenomenon; Finished product impact test is put down and is crouched in ground by pallet, adopt the weight that quality is 10kg highly freely to fall 6 times at 3 meters, the equal crack-free of pallet and without damaging phenomenon, illustrate that the pallet of the plastics composite making of embodiment of the present invention 1-9 has good resistance to rupture.And the pallet that adopts the plastics composite of comparative example 1 to make adopts above-mentioned same method to carry out after the test of finished product drop shutter test and finished product impact test, finished product drop shutter test and finished product impact test all can only fall just to have for 2 times and break and damage phenomenon.In addition, as can be seen from Table 1, the pallet overall performance that plastics composite of the present invention is made is better, and can find out from reference examples 2, if add and tetrafluoroethylene, and do not add ethylene-methacrylic acid copolymer, shore hardness can only reach 70 left and right, product performance are poor, and the overall performance of product is all relatively poor, also illustrated and between plastics composite of the present invention, there is good synergy, thereby made the pallet that adopts plastics composite of the present invention to make there is good overall performance.First embodiment 7-9 by carrying out blend processing by 20%～30% nano-calcium carbonate and/or barium sulfate and pigment, thereby make nano material be wrapped in surface of pigments, carry out again blend, thereby the tinting strength of the product finally obtaining and opacifying power are greatly improved, compare with conventional method (directly pigment and other composition being mixed together to method) tinting strength and opacifying power and all can improve more than 15%.
Specific embodiment described in the present invention is only to the explanation for example of the present invention's spirit.Those skilled in the art can make various amendments or supplement or adopt similar mode to substitute described specific embodiment, but can't depart from spirit of the present invention or surmount the defined scope of appended claims.
Although the present invention has been made a detailed description and has quoted as proof some specific embodiments, to those skilled in the art, only otherwise it is obvious leaving that the spirit and scope of the present invention can make various changes or revise.
Claims (9)
1. for a plastics composite for pallet, it is characterized in that, this plastics composite is mainly made up of the weight part of following composition:
High density polyethylene(HDPE) or polypropylene: 70～85; : 2.0～3.0; Tetrafluoroethylene: 0.5～1.0; Ethylene-methacrylic acid copolymer: 2.0～5.0; Silane coupling agent: 0.5～0.8; Nanometer inorganic filler: 5.0～10; Synthetic rubber: 10～13; Fiber: 8.0～12; Fire retardant: 0～4.0; Antioxidant: 0～2.0.
2. according to claim 1 for the plastics composite of pallet, it is characterized in that, this plastics composite is mainly made up of the weight part of following composition:
High density polyethylene(HDPE) or polypropylene: 75～80; : 2.2～2.8; Tetrafluoroethylene: 0.6～0.8; Ethylene-methacrylic acid copolymer: 3.0～4.0; Silane coupling agent: 0.6～0.7; Nanometer inorganic filler: 6.0～8.0; Synthetic rubber: 11～12; Fiber: 10～11; Fire retardant: 2.0～3.0; Antioxidant: 1.0～1.5.
3. according to the plastics composite for pallet described in claim 1 or 2, it is characterized in that, described silane coupling agent is selected from one or more in vinyl trichloro silane, vinyltriethoxysilane, vinyl three (2-methoxy ethoxy) silane, γ-methacryloxypropyl trimethoxy silane, methacryloxypropyl triethoxyl silane, vinyltrimethoxy silane, γ-glycidyl ether oxygen base propyl trimethoxy silicane and γ-mercapto propyl group dimethoxy silane.
4. according to claim 3 for the plastics composite of pallet, it is characterized in that, described silane coupling agent is the mixture of γ-methacryloxypropyl trimethoxy silane and vinyl three (2-methoxy ethoxy) silane, and the weight ratio of γ-methacryloxypropyl trimethoxy silane and vinyl three (2-methoxy ethoxy) silane is 1:2.4～2.8.
5. according to claim 4 for the plastics composite of pallet, it is characterized in that, described nanometer inorganic filler is selected from one or more in nano silicon, nano barium sulfate, nano titanium oxide or nano-calcium carbonate.
6. according to the plastics composite for pallet described in claim 1 or 2, it is characterized in that, described synthetic rubber is silicon rubber.
7. according to the plastics composite for pallet described in claim 1 or 2, it is characterized in that, described fiber is selected from one or more in glass fibre, staple fibre and mineral fibre.
8. according to the plastics composite for pallet described in claim 1 or 2, it is characterized in that, described fire retardant is selected from one or more in kaolin, calcium carbonate and zinc borate.
9. according to claim 8 for the plastics composite of pallet, it is characterized in that, described fire retardant is the mixture of kaolin and calcium carbonate, and the weight ratio of described kaolin and calcium carbonate is 1:2.0～3.0.