CN104005039B - A kind of aluminum alloy mould cleaning agent and preparation method thereof - Google Patents
A kind of aluminum alloy mould cleaning agent and preparation method thereof Download PDFInfo
- Publication number
- CN104005039B CN104005039B CN201410225673.7A CN201410225673A CN104005039B CN 104005039 B CN104005039 B CN 104005039B CN 201410225673 A CN201410225673 A CN 201410225673A CN 104005039 B CN104005039 B CN 104005039B
- Authority
- CN
- China
- Prior art keywords
- cleaning agent
- aluminum alloy
- alloy mould
- preparation
- surfactant
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Active
Abstract
A kind of aluminum alloy mould cleaning agent of the present invention and preparation method thereof, described cleaning agent is composed of the following components according to mass percent: ten disulfobenzene sodium sulfonate 6-12%, surfactant 5-15%, NaOH 40-50%, natrium carbonicum calcinatum 10-20%, natrium citricum 8-15%, sodium metasilicate 5-8%, defoamer 1-2%, by the preparation method of science, the aluminum alloy mould cleaning agent obtaining, pollute and have powerful clean ability for the oil film easily causing on aluminium alloy, be 98% to the washing power of oil film, price economy, indices meets national requirements for environmental protection, to human body skin without harm, corrosion-free to aluminum alloy mould, can improving product quality and die life.
Description
Technical field
The invention belongs to cleaning agent and manufacture field, be specifically related to a kind of aluminum alloy mould cleaning agent and preparation method thereof.
Background technology
In household electrical appliances, automobile industry Mould Machining enterprise, the material of most economical material benefit is aluminium alloy, aluminium, and aluminium alloy conducts heat, quality is light, be the good base material of processing mold, due to the optimization and upgrading of automobile industry inside in recent years, constantly stimulate the growth to mould demand. Auto industry is for China; also grow the stage in development; above-mentioned under the drive of above trend; the advantage that China's Die Industry is developed is very obvious; but aluminum alloy mould in use, often have pollution, particularly greasy dirt that greasy dirt, foreign material cause and easily form oil film in aluminum alloy surface and be attached to surface and form colour film; time has been grown and can form irreversible erosion to aluminum alloy surface, has a strong impact on product quality and die life.
Summary of the invention
For addressing the above problem, the invention discloses a kind of aluminum alloy mould cleaning agent and preparation method thereof, the washing power of oil film is 98%, corrosion-free to aluminum alloy mould, price economy, environment-protecting asepsis.
For achieving the above object, technical scheme of the present invention is as follows:
A kind of aluminum alloy mould cleaning agent, it is characterized in that: described cleaning agent is composed of the following components according to mass percent: ten disulfobenzene sodium sulfonate 6-12%, surfactant 5-15%, NaOH 40-50%, natrium carbonicum calcinatum 10-20%, natrium citricum 8-15%, sodium metasilicate 5-8%, defoamer 1-2%.
As a modification of the present invention, the component that described surfactant is following mass percent is prepared from by chemical reaction: diethanol amine 60-80%; 4-chloromethyl pyridine hydrochloride 20-40%.
As a modification of the present invention, the preparation method of described surfactant is: by after the diethanol amine of said components and the mixing of 4-chloromethyl pyridine hydrochloride, be under agitation heated to 60-80 DEG C, then stir insulation 2 hours.
As a modification of the present invention, described defoamer is Polyether Modified Polysiloxanes Defoaming Agent.
A preparation method for aluminum alloy mould cleaning agent, is characterized in that: comprise the following steps:
(1) make surfactant;
(2) surfactant of making is added in reactor, then add ten disulfobenzene sodium sulfonates, NaOH, natrium carbonicum calcinatum, natrium citricum, sodium metasilicate, closing presure still stirs 0.5-2 hour under 110Kpa air pressure, normal temperature;
(3) add under defoamer normal temperature and pressure and stir 10-20 minute;
(4) mixture is put into evaporimeter, revolution distillation 3-6 hour, extracts supernatant, puts into filtering centrifuge centrifugal under 1200 revolutions per seconds, obtains cleaning agent.
The invention has the beneficial effects as follows:
A kind of aluminum alloy mould cleaning agent of the present invention and preparation method, pollute and have powerful clean ability for the oil film easily causing on aluminium alloy, be 98% to the washing power of oil film, price economy, indices meets national requirements for environmental protection, without harm, corrosion-free to aluminum alloy mould to human body skin, can improving product quality and die life.
Detailed description of the invention
Embodiment 1
A kind of aluminum alloy mould cleaning agent, described cleaning agent is composed of the following components according to mass percent: ten disulfobenzene sodium sulfonates 9%, surfactant 12%, NaOH 48%, natrium carbonicum calcinatum 12%, natrium citricum 12%, sodium metasilicate 6%, defoamer 1%.
Surfactant is that the component of following mass percent is prepared from by chemical reaction: diethanol amine 75%; 4-chloromethyl pyridine hydrochloride 25%, the preparation method of described surfactant is: by after diethanol amine and the mixing of 4-chloromethyl pyridine hydrochloride, be under agitation heated to 75 DEG C, then stir insulation 2 hours.
Described defoamer is Polyether Modified Polysiloxanes Defoaming Agent.
A preparation method for aluminum alloy mould cleaning agent, comprises the following steps:
(1) make according to the method described above surfactant;
(2) surfactant of making is added in reactor, then add ten disulfobenzene sodium sulfonates, NaOH, natrium carbonicum calcinatum, natrium citricum, sodium metasilicate, closing presure still stirs 1.5 hours under 110Kpa air pressure, normal temperature;
(3) add under defoamer normal temperature and pressure and stir 10 minutes;
(4) mixture is put into evaporimeter, revolution distillation 5 hours, extracts supernatant, puts into filtering centrifuge centrifugal under 1200 revolutions per seconds, obtains cleaning agent.
When use, cleaning agent and water are according to the dilution proportion of 1:30, and oil film is with serious pollution can be diluted according to 1:25, when used winter, the solution having diluted suitably can be heated to 10-20 DEG C of use, better effects if.
Using a kind of aluminum alloy mould cleaning agent described in the present embodiment, is 98% to the washing power of oil film, and aluminum alloy mould is corrosion-free, and indices meets national requirements for environmental protection, to human body skin without harm.
Embodiment 2
A kind of aluminum alloy mould cleaning agent, described cleaning agent is composed of the following components according to mass percent: ten disulfobenzene sodium sulfonates 10%, surfactant 12%, NaOH 44%, natrium carbonicum calcinatum 14%, natrium citricum 10%, sodium metasilicate 8%, defoamer 2%.
Surfactant is that the component of following mass percent is prepared from by chemical reaction: diethanol amine 80%; 4-chloromethyl pyridine hydrochloride 20%, the preparation method of described surfactant is: by after diethanol amine and the mixing of 4-chloromethyl pyridine hydrochloride, be under agitation heated to 70 DEG C, then stir insulation 2 hours.
Described defoamer is Polyether Modified Polysiloxanes Defoaming Agent.
A preparation method for aluminum alloy mould cleaning agent, comprises the following steps:
(1) make according to the method described above surfactant;
(2) surfactant of making is added in reactor, then add ten disulfobenzene sodium sulfonates, NaOH, natrium carbonicum calcinatum, natrium citricum, sodium metasilicate, closing presure still stirs 1 hour under 110Kpa air pressure, normal temperature;
(3) add under defoamer normal temperature and pressure and stir 15 minutes;
(4) mixture is put into evaporimeter, revolution distillation 6 hours, extracts supernatant, puts into filtering centrifuge centrifugal under 1200 revolutions per seconds, obtains cleaning agent.
When use, cleaning agent and water are according to the dilution proportion of 1:30, and oil film is with serious pollution can be diluted according to 1:25, when used winter, the solution having diluted suitably can be heated to 10-20 DEG C of use, better effects if.
Using a kind of aluminum alloy mould cleaning agent described in the present embodiment, is 97% to the washing power of oil film, and aluminum alloy mould is corrosion-free, and indices meets national requirements for environmental protection, to human body skin without harm.
The disclosed technological means of the present invention program is not limited only to the disclosed technological means of above-mentioned embodiment, also comprises the technical scheme being made up of above technical characterictic.
Claims (2)
1. an aluminum alloy mould cleaning agent, it is characterized in that: described cleaning agent is composed of the following components according to mass percent: ten disulfobenzene sodium sulfonate 6-12%, surfactant 5-15%, NaOH 40-50%, natrium carbonicum calcinatum 10-20%, natrium citricum 8-15%, sodium metasilicate 5-8%, defoamer 1-2%, the component that described surfactant is following mass percent is prepared from by chemical reaction: diethanol amine 60-80%; 4-chloromethyl pyridine hydrochloride 20-40%. The preparation method of described surfactant is: by after diethanol amine and the mixing of 4-chloromethyl pyridine hydrochloride, be under agitation heated to 60-80 DEG C, then stir insulation 2 hours.
2. a kind of aluminum alloy mould cleaning agent according to claim 1, is characterized in that: described defoamer is Polyether Modified Polysiloxanes Defoaming Agent.