CA2631354A1 - Slip-cling stretch film - Google Patents
Slip-cling stretch film Download PDFInfo
- Publication number
- CA2631354A1 CA2631354A1 CA 2631354 CA2631354A CA2631354A1 CA 2631354 A1 CA2631354 A1 CA 2631354A1 CA 2631354 CA2631354 CA 2631354 CA 2631354 A CA2631354 A CA 2631354A CA 2631354 A1 CA2631354 A1 CA 2631354A1
- Authority
- CA
- Canada
- Prior art keywords
- layer
- multilayer film
- weight
- density polyethylene
- cling
- Prior art date
- Legal status (The legal status is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the status listed.)
- Abandoned
Abstract
A multilayer stretch film having a high slip surface and an aggressive cling surface for wrapping items or loads for ease of transport is disclosed. In one embodiment, there is disclosed a multilayer film comprises a first surface having a coefficient of friction at least less than about 0.9, comprising at least polypropylene and high-density polyethylene, a second surface having a cling force to the first surface at least greater than about 5 g/in, comprising at least a styrenic block copolymer, and a core layer, positioned between the first surface and the second surface, comprising at least linear low-density polyethylene or its blend.
Description
SLIP-CLING STRETCH FILM
CROSS-REFERENCE TO RELATED APPLICATIONS
[0001] This application is a continuation-in-part of United States Patent Application Serial No. 11/941,425, filed on November 16, 2007, which is a continuation-in-part of United States Patent Application Serial No. 11/763,639, filed on June 15, 2007, each of which is incorporated herein by reference in its entirety.
BACKGROUND OF THE INVENTION
Field of the Invention [0002] Embodiments of the present invention generally relate to a multilayer stretch film. More specifically, embodiments of the present invention relate to a multilayer stretch film having a high slip surface and an aggressive cling surface for wrapping items or loads for ease of transport.
Description of the Related Art [0003] The use of thermoplastic stretch wrap films for the over-wrap packaging of goods, and in particular, large rolls of paper or carpet, is a commercially significant application of polymer film. Monolayer stretch wrap films have identical surfaces on both sides, while multilayer stretch films can have a non-cling surface and a cling surface. The non-cling surface generally does not cling to itself and prevents adjoining wrapped goods from sticking to one another. The cling surface enables the film to stick to itself to prevent unwrapping during transport. However, as the non-cling surface decreases in coefficient of friction, the cling surface must increase its cling aggressiveness to enable the film to stick to itself when wrapped around goods.
CROSS-REFERENCE TO RELATED APPLICATIONS
[0001] This application is a continuation-in-part of United States Patent Application Serial No. 11/941,425, filed on November 16, 2007, which is a continuation-in-part of United States Patent Application Serial No. 11/763,639, filed on June 15, 2007, each of which is incorporated herein by reference in its entirety.
BACKGROUND OF THE INVENTION
Field of the Invention [0002] Embodiments of the present invention generally relate to a multilayer stretch film. More specifically, embodiments of the present invention relate to a multilayer stretch film having a high slip surface and an aggressive cling surface for wrapping items or loads for ease of transport.
Description of the Related Art [0003] The use of thermoplastic stretch wrap films for the over-wrap packaging of goods, and in particular, large rolls of paper or carpet, is a commercially significant application of polymer film. Monolayer stretch wrap films have identical surfaces on both sides, while multilayer stretch films can have a non-cling surface and a cling surface. The non-cling surface generally does not cling to itself and prevents adjoining wrapped goods from sticking to one another. The cling surface enables the film to stick to itself to prevent unwrapping during transport. However, as the non-cling surface decreases in coefficient of friction, the cling surface must increase its cling aggressiveness to enable the film to stick to itself when wrapped around goods.
[0004] Thus, there is a need for an improved slip-cling stretch film having a high slip surface and an aggressive cling surface.
18089_1 SUMMARY OF THE INVENTION
18089_1 SUMMARY OF THE INVENTION
[0005] Embodiments of the present invention relate to a multilayer stretch film having a high slip surface and an aggressive cling surface for wrapping items or loads for ease of transport.
[0006] In one embodiment, a multilayer film comprises a slip layer comprising at least polypropylene and high-density polyethylene blend, a cling layer comprising at least a styrenic block copolymer, and an intermediary layer comprising at least linear low-density polyethylene resin or its blend.
[0007] In another embodiment of the present invention, a multilayer film comprises a first surface having a coefficient of friction at least less than about 0.9, comprising at least polypropylene and high-densily polyethylene, a second surface having a cling force to the first surface at least greater than about 5 g/in, comprising at least a styrenic block copolymer, and a core layer, positioned between the first surface and the second surface, comprising at least linear low-density polyethylene resin.
BRIEF DESCRIPTION OF THE DRAWING
BRIEF DESCRIPTION OF THE DRAWING
[0008] So the manner in which the above recited features of the present invention can be understood in detail, a more particular description of embodiments of the present invention, briefly summarized above, may be had by reference to an embodiment, which is illustrated in the appended drawing. It is to be noted, however, the appended drawing illustrates only a typical embodiment of embodiments encompassed within the scope of the present invention, and, therefore, is not to be considered limiting, for the present invention may admit to other equally effective embodiments, wherein:
[0009] Figure 1 depicts a cross-sectional view of a film in accordance with one embodiment of the present invention.
18089_1 [0010] The headings used herein are for organizational purposes only and are not meant to be used to limit the scope of the description or the claims. As used throughout this application, the word "may" is used in a permissive sense (i.e., meaning having the potential to), rather than the mandatory sense (i.e., meaning must).
Similarly, the words "include", "including", and "includes" mean including but not limited to. To facilitate understanding, like reference numerals have been used, where possible, to designate like elements common to the figure.
DETAILED DESCRIPTION OF THE INVENTION
18089_1 [0010] The headings used herein are for organizational purposes only and are not meant to be used to limit the scope of the description or the claims. As used throughout this application, the word "may" is used in a permissive sense (i.e., meaning having the potential to), rather than the mandatory sense (i.e., meaning must).
Similarly, the words "include", "including", and "includes" mean including but not limited to. To facilitate understanding, like reference numerals have been used, where possible, to designate like elements common to the figure.
DETAILED DESCRIPTION OF THE INVENTION
[0011] Figure 1 depicts a cross-sectional view of a film in accordance with one embodiment of the present invention. The film 100 generally comprises a slip layer 102, a cling layer 104, and at least one intermediaiy layer 106 (also referred to herein as a "core" layer) positioned between the two surface layers. The slip layer 102 comprises between about 5% by weight and about 20% by weight of the film 100. The cling layer 104 comprises between about 3% by weight and about 20% by weight of the film 100. In many of the embodiments, the balance of the film 100 is the intermediary layer 106.
[0012] The slip layer 102 generally comprises a polymer composition yielding a low coefficient of friction. The coefficient of friction of the slip layer 102 is at least less than about 0.9. In one embodiment, the coefficient of friction of the slip layer 102 is about 0.5.
[0013] The slip layer 102 generally comprises a polypropylene (PP) and high-density polyethylene (HDPE) composition. The PP may be provided in a range of about 60% by weight to about 99% by weight, and the balance of the composition comprises HDPE.
In one embodiment, the PP is provided in about 80% by weight and the HDPE is provided in about 20% by weight of the slip layer 102. In another embodiment, the PP
is provided in about 75% to about 95% by weight, the HDPE is provided in about 5% to 18089_1 about 25% by weight, and the balance comprises at least one resin or additive, such as abrasion-resistant resins, colorants, stabilizers, UV absorbers, and the like.
In one embodiment, the PP is provided in about 80% by weight and the HDPE is provided in about 20% by weight of the slip layer 102. In another embodiment, the PP
is provided in about 75% to about 95% by weight, the HDPE is provided in about 5% to 18089_1 about 25% by weight, and the balance comprises at least one resin or additive, such as abrasion-resistant resins, colorants, stabilizers, UV absorbers, and the like.
[0014] In one exemplary embodiment, the PP is a polypropylene copolymer plastic material commercially available from Basell Polyolefins of Hoofddorp, The Netherlands, under the name Basell Pro-fax SA861. The PP has a density of about 0.900 g/cm3, and a mass-flow rate (MFR) of about 6.50 g/10 min, as determined by ASTM
test methods D792 and D1238, respectively.
test methods D792 and D1238, respectively.
[0015] In another exemplary embodiment, the HDPE is a high-density polyethylene plastic material, commercially available from the Westlake Chemical Corporation of Houslon, '1'exas, ui ler llte naine Westlake HDPE HC 6008. The HDPE has a density of about 0.962 g/cm3, and a MFR of about 8.2 g/10 min, as determined by ASTM test methods D1505 and D1238, respectively.
[0016] The cling layer 104 generally comprises a polymer composition yielding a high cling. The cling force of the cling layer 104 to the slip layer 102, when wrapped around a good or load, is at least greater than about 5 g/in. In one embodiment, the cling force of the cling layer 104 to slip layer 102 is about 50 g/in.
[0017] The cling layer 104 generally comprises a styrenic block copolymer (SBC).
The SBC may be provided in a range of about 50% by weight to about 100% by weight.
In one embodiment, the SBC is provided in about 100% by weight of the slip layer 102.
In another embodiment, the SBC is provided in about 50% to about 95% by weight, and the balance comprises at least an additional resin or additive, such as UV
protective additives, puncture resistant resins, and the like.
The SBC may be provided in a range of about 50% by weight to about 100% by weight.
In one embodiment, the SBC is provided in about 100% by weight of the slip layer 102.
In another embodiment, the SBC is provided in about 50% to about 95% by weight, and the balance comprises at least an additional resin or additive, such as UV
protective additives, puncture resistant resins, and the like.
[0018] In one exemplary embodiment, the SBC is a styrenic block copolymer material commercially available from Kraton Polymers LLC of Houston, Texas, under the name Kraton MD6718 Compound. The SBC has a density of about 0.9 g/ cm3, and a MFR of between about 2 g/10 min and about 25 g/10 min.
[0019] The cling layer 104 may further comprise additional resins and additives. In one embodiment, the cling layer 104 comprises a puncture-resistant resin. In another embodiment, the cling layer 104 may also comprise a low-density polyethylene (LDPE) resin having a density of between about 0.91 g/ cm3 and 0.94 g/ cm3, a LLDPE
resin having a density of between about 0.915 g/cm3 and 0.925 g/cm3, or a very low-density polyethylene (VLDPE) resin having a density of between about 0.88 g/cm3 and 0.915 g/cm3.
resin having a density of between about 0.915 g/cm3 and 0.925 g/cm3, or a very low-density polyethylene (VLDPE) resin having a density of between about 0.88 g/cm3 and 0.915 g/cm3.
[0020] In another embodiment of the present invention, the cling layer 104 may additionally comprise an ethylene-octene copolymer resin having a density between about 0.850 g/cm3 and about 0.900 g/cm3. In an exemplary embodiment, the ethylene-octene copolymer is a copolymer, commercially available from the Dow Chemical Company of Midland, Michigan, under the name Dow Affinity KC-8852. The ethylene-octene copolymer has a density of about 0.875 g/cm3 and a MFR of about 3.0 g/10 min, as determined by ASTM test methods D792 and D1238, respectively.
[0021] Further examples of useful cling additives include polyisobutylenes (PIB) having a number average molecular weight in the range from about 1,000-3,000, preferably about 1,200-1,800, as measured by vapor phase osmometry, amorphous atactic polypropylenes, e.g., those having an average molecular weight of about 2,000, and polyterpenes. Examples of cling-enhancing resins include, but are not limited to, ethylene-vinyl acetate (EVA) copolymers containing from about 5% to about 15%
by weight copolymerized vinyl acetate and VLDPE resins having densities from 0.88 g/cm3 to 0.912 g/cm3 and melt indexes from 0.5 g/10 min to 10 g/10 min. The optional cling additives may be present in the cling layer 104 in a concentration of from about 0.5% by weight to about 10% by weight of the cling layer 104 composition.
18089_1 [0022] Optionally, in some embodiments, polyethylene resins are utilized in the cling layer 104, and are further blended with minor amounts, e.g., up to about 20% by weight total, of one or more other suitable resins to achieve a desired range of physical and/or mechanical properties in the film product. For example, suitable resins such as ethyl vinyl acetate copolymer, and LLDPE resins may be useful when blended with the cling layer 104. In many embodiments, conventional film additives such as antioxidants, UV stabilizers, pigments, dyes, etc., are utilized in the cling layer 104 of the film 100.
by weight copolymerized vinyl acetate and VLDPE resins having densities from 0.88 g/cm3 to 0.912 g/cm3 and melt indexes from 0.5 g/10 min to 10 g/10 min. The optional cling additives may be present in the cling layer 104 in a concentration of from about 0.5% by weight to about 10% by weight of the cling layer 104 composition.
18089_1 [0022] Optionally, in some embodiments, polyethylene resins are utilized in the cling layer 104, and are further blended with minor amounts, e.g., up to about 20% by weight total, of one or more other suitable resins to achieve a desired range of physical and/or mechanical properties in the film product. For example, suitable resins such as ethyl vinyl acetate copolymer, and LLDPE resins may be useful when blended with the cling layer 104. In many embodiments, conventional film additives such as antioxidants, UV stabilizers, pigments, dyes, etc., are utilized in the cling layer 104 of the film 100.
[0023] The intermediary layer 106 generally comprises one or more layers of polymeric compositions yielding necessary mechanical properties of the film 100, such as extensibility, load containment, tear and puncture resistance, and the like. In one embodiment, the intermediary layer 106 comprises a linear low-density polyethylene (LLDPE). In another embodiment, the intermediary layer 106 further comprises a white pigment such as titanium dioxide.
[0024] The LLDPE may be provided in a range of between about 50% and 100% by weight. In particular embodiments, the titanium dioxide may be provided between about 0.1% to about 5% by weight. In one embodiment, the LLDPE is provided in about 98% by weight, and the titanium dioxide is provided in about 2% by weight of the intermediary layer 106. In another embodiment, the composition may additionally comprise conventional additives, resins, and the like, to provide the desired performance characteristics.
[0025] In one exemplary embodiment, the LLDPE is a linear low-density polyethylene material commercially available from Dow Chemical Company of Midland, Michigan, under the name Dowlex 2045G. The LLDPE has a density of about 0.920 g/cm3 and a MFR of about 1.0 g/10 min, as measured by ASTM D792 and D1238, respectively. In another exemplary embodiment, the LLDPE is a linear low-density 18089_1 polyethylene material commercially available from Dow Chemical Company of Midland, Michigan, under the name Tuflin HSE-7002. The titanium dioxide is provided as an element of a white concentrate. In one embodiment, the titanium dioxide is contained within a white concentrate from Ampacet Corporation of Tarrytown, New York, under the name Ampacet White 110359-C.
[0026] Alternative embodiments of the present invention provide an intermediary layer 106 comprising at least two or more individual layers. It is understood that embodiments of the present invention may comprise as many individual layers in the intermediary layer 106 as necessary or feasible to achieve desired material properties in a film 100. For example, at least one embodiment of the present invention provides a three-layer film having a single intermediary layer, whereas an alternative embodiment provides for up to a fourteen layer film, having twelve individual layers in the intermediary layer. Additional embodiments provide for any number of layers contained within the range of the above-disclosed embodiments, as well as any number of layers feasible within the scope of the embodiments of the present invention.
[0027] The individual layers of the intermediary layer 106 may comprise various optional material compositions. Such materials include, but are not limited to, any feasible grade of LLDPE, metallocene-catalyzed LLDPE, Low-Density Polyethylene (LDPE), Mid-Density Polyethylene (MDPE), High-Density Polyethylene (HDPE), or Polypropylene (PP), including homopolymers, copolymers or blends of the above.
[0028] In one embodiment, the intermediary layer 106 comprises three layers 108, 110, 112. In one such embodiment, the three layers comprise an A-B-A
structure, wherein A is a layer of LLDPE and wherein B is a layer of LLDPE and a white concentrate.
structure, wherein A is a layer of LLDPE and wherein B is a layer of LLDPE and a white concentrate.
[0029] In one embodiment of the present invention, a multilayer film comprises a slip layer comprising a polypropylene copolymer and high-density polyethylene blend, 18089_1 a cling layer comprising a styrenic block copolymer and ethylene-octene copolymer blend, and an intermediary layer comprising at least three individual layers, comprising at least two layers of linear low-density polyethylene, and a layer of a linear low-density polyethylene and additive blend.
[0030] Additives and/or resins may be provided in the intermediary layer 106, such as those discussed above with respect to the slip layer 102 and the cling layer 104.
Additional resins include polyolefin homopolymers and copolymers suitable for enhancement of mechanical properties such as tensile strength, elongation at break, tear and puncture resistance.
[00311 In order to ensure the film 100 meets the desired parameters in accordance with embodiments of the present invention, testing may be done to determine its physical properties. A parameter used to analyze the performance of such films is the force required to stretch the film to a desired percentage of its original length. This force is indicative of the load retention characteristics of the film. The films of embodiments of the present invention generally have a force to stretch the film to 100%
of at least about 5 pli (pounds per linear inch). In many embodiments, the films generally have tensile strength of at least about 5000 psi and elongation to break of at least about 400%, as determined by ASTM D882.
[0032] Generally, embodiments of the film 100 are constructed according to conventional practices. The film 100 may be manufactured utilizing blown-film or cast-film co-extrusion. In one embodiment, a cast-film manufacturing process provides resin materials are heated to their molten state, and their viscosities are coordinated to prepare multilayer films in a uniform manner. The molten materials are conveyed to a co-extrusion adapter that combines the molten materials to form a multilayer co-extruded structure. The layered polymeric material is transferred through an extrusion die opened to a predetermined gap commonly in the range of between about 0.05 in 18089_1 (0.13 cm) and 0.012 in (0.03 cm). The material is then drawn down to the intended gauge thickness by means of a primary chill or casting roll maintained at between about 50 F to about 130 F. Typical draw down ratios range from between about 5:1 to about 40:1.
[0033] The overall thickness of the stretch wrap film can vary widely according to end use specifications, but is generally in the range of the typical thicknesses for stretch wrap films. In one embodiment of the present invention, the overall film 100 thickness is between about 0.012 mm to about 0.125 mm. In one embodiment, the film 100 thickness is about 0.025 mm.
[0034] Once manufactured, in some embodiments, the slip layer 102 and/or the cling layer 104 of the film can be post-formation treated by implementing operations such as corona discharge, chemical treatment, flame treatment, etc., to modify the printability or ink receptivity of the surface(s) or to impart other desirable characteristics thereto.
[0035] In accordance with embodiments of the invention, the film may be provided in a non-stretched, i.e., unoriented, or merely a modestly stretched state prior to use.
The film 100 is capable of being stretched from at least between about 40% and 400%
during a final goods wrapping step.
[0036] In accordance with embodiments of the present invention, the film shp properties are unexpectedly improved as the film is stretched. These advantageous results may be a proximate result of the specific PP and HDPE compositions utilized in the slip layer with several embodiments of the present invention.
Specifically, as the film is stretched, microscopic patterns appear on the slip layer film surface reducing film smoothness as well as the contact area. As a result, the slip surface of the described embodiments visibly loses its relatively glossy appearance when the film is stretched to about 100%. In one example, the static COF changed from about 0.65 before a stretch to 18089_i about 0.49 after the stretch. As is understood by those of ordinary skill in the art, low friction is advantageous for ease of moving and for reduction of possible damage to items wrapped in a film in accordance with embodiments of the present invention.
[0037] While the foregoing is directed to embodiments of the present invention, other and further embodiments of the invention may be devised without departing from the basic scope thereof.
18089_1
Additional resins include polyolefin homopolymers and copolymers suitable for enhancement of mechanical properties such as tensile strength, elongation at break, tear and puncture resistance.
[00311 In order to ensure the film 100 meets the desired parameters in accordance with embodiments of the present invention, testing may be done to determine its physical properties. A parameter used to analyze the performance of such films is the force required to stretch the film to a desired percentage of its original length. This force is indicative of the load retention characteristics of the film. The films of embodiments of the present invention generally have a force to stretch the film to 100%
of at least about 5 pli (pounds per linear inch). In many embodiments, the films generally have tensile strength of at least about 5000 psi and elongation to break of at least about 400%, as determined by ASTM D882.
[0032] Generally, embodiments of the film 100 are constructed according to conventional practices. The film 100 may be manufactured utilizing blown-film or cast-film co-extrusion. In one embodiment, a cast-film manufacturing process provides resin materials are heated to their molten state, and their viscosities are coordinated to prepare multilayer films in a uniform manner. The molten materials are conveyed to a co-extrusion adapter that combines the molten materials to form a multilayer co-extruded structure. The layered polymeric material is transferred through an extrusion die opened to a predetermined gap commonly in the range of between about 0.05 in 18089_1 (0.13 cm) and 0.012 in (0.03 cm). The material is then drawn down to the intended gauge thickness by means of a primary chill or casting roll maintained at between about 50 F to about 130 F. Typical draw down ratios range from between about 5:1 to about 40:1.
[0033] The overall thickness of the stretch wrap film can vary widely according to end use specifications, but is generally in the range of the typical thicknesses for stretch wrap films. In one embodiment of the present invention, the overall film 100 thickness is between about 0.012 mm to about 0.125 mm. In one embodiment, the film 100 thickness is about 0.025 mm.
[0034] Once manufactured, in some embodiments, the slip layer 102 and/or the cling layer 104 of the film can be post-formation treated by implementing operations such as corona discharge, chemical treatment, flame treatment, etc., to modify the printability or ink receptivity of the surface(s) or to impart other desirable characteristics thereto.
[0035] In accordance with embodiments of the invention, the film may be provided in a non-stretched, i.e., unoriented, or merely a modestly stretched state prior to use.
The film 100 is capable of being stretched from at least between about 40% and 400%
during a final goods wrapping step.
[0036] In accordance with embodiments of the present invention, the film shp properties are unexpectedly improved as the film is stretched. These advantageous results may be a proximate result of the specific PP and HDPE compositions utilized in the slip layer with several embodiments of the present invention.
Specifically, as the film is stretched, microscopic patterns appear on the slip layer film surface reducing film smoothness as well as the contact area. As a result, the slip surface of the described embodiments visibly loses its relatively glossy appearance when the film is stretched to about 100%. In one example, the static COF changed from about 0.65 before a stretch to 18089_i about 0.49 after the stretch. As is understood by those of ordinary skill in the art, low friction is advantageous for ease of moving and for reduction of possible damage to items wrapped in a film in accordance with embodiments of the present invention.
[0037] While the foregoing is directed to embodiments of the present invention, other and further embodiments of the invention may be devised without departing from the basic scope thereof.
18089_1
Claims (28)
1. A multilayer film comprising:
a slip layer comprising at least a polypropylene copolymer and high-density polyethylene blend;
a cling layer comprising at least a styrenic block copolymer; and an intermediary layer comprising a plurality of individual layers;
wherein at least one layer of the intermediary layer comprises linear low-density polyethylene resin or its blend.
a slip layer comprising at least a polypropylene copolymer and high-density polyethylene blend;
a cling layer comprising at least a styrenic block copolymer; and an intermediary layer comprising a plurality of individual layers;
wherein at least one layer of the intermediary layer comprises linear low-density polyethylene resin or its blend.
2. The multilayer film of claim 1, wherein at least one layer of the intermediary layer comprises titanium dioxide.
3. The multilayer film of claim 1, wherein the multilayer film comprises the slip layer in between about 5% to about 20% by weight, the cling layer in between about 3%
to about 20% by weight, and the intermediary layer in between about 60% to about 90%
by weight.
to about 20% by weight, and the intermediary layer in between about 60% to about 90%
by weight.
4. The multilayer film of claim 3, wherein the multilayer film comprises the slip layer in about 15% by weight, the cling layer in about 7% by weight, and the intermediary layer in about 78% by weight.
5. The multilayer film of claim 1, wherein the slip layer has a coefficient of friction between about 0.3 to about 0.9, and wherein the cling layer has a cling force to the slip layer between about 5 g/in to about 80 g/in.
6. The multilayer film of claim 5, wherein the slip layer has a coefficient of friction of about 0.5, and wherein the cling layer has a cling force to the slip layer of about 50 g/in.
7. The multilayer film of claim 1, wherein the slip layer comprises between about 70% and about 99% by weight polypropylene and between about 1% to about 30% by weight high-density polyethylene.
8. The multilayer film of claim 7, wherein slip layer comprises about 80% by weight polypropylene and about 20% by weight high-density polyethylene.
9. The multilayer film of claim 1, wherein the intermediary layer comprises between about 50% and 100% by weight linear low-density polyethylene.
10. The multilayer film of claim 9, wherein the intermediary layer further comprises between about 0.1% to about 5% by weight titanium dioxide.
11. The multilayer film of claim 10, wherein the intermediary layer comprises about 98% by weight linear low-density polyethylene and about 2% by weight titanium dioxide.
12. The multilayer film of claim 1, wherein the multilayer film can withstand a force stretch the film to about 400% at about 5000 psi.
13. The multilayer film of claim 1, wherein the overall multilayer film thickness is between about 0.012 mm to about 0.125 mm.
14. The multilayer film of claim 13, wherein the overall multilayer film thickness is about 0.025 mm.
15. The multilayer film of claim 1, wherein the at least three individual layers each comprise a material selected from the group consisting of linear low-density 18089_1 polyethylene, metallocene-catalyzed low-density polyethylene, low-density polyethylene, mid-density polyethylene, high-density polyethylene, polypropylene, and any homopolymers, copolymers or blend thereof.
16. The multilayer film of claim 1, wherein the intermediary layer further comprises at least an additive.
17. The multilayer film of claim 1, wherein the cling layer further comprises at least an additive.
18. The multilayer film of claim 1, wherein the cling layer further comprises an ethylene-octene copolymer.
19. A multilayer film comprising:
a first surface having a coefficient of friction at least less than about 0.9, comprising at least a polypropylene copolymer and high-density polyethylene;
a second surface having a cling force to the first surface at least greater than about 5 g/in, comprising at least a styrenic block copolymer; and a core layer, positioned between the first surface and the second surface, comprising a plurality layers;
wherein at least one layer of the intermediary layer comprises linear low-density polyethylene resin or its blend.
a first surface having a coefficient of friction at least less than about 0.9, comprising at least a polypropylene copolymer and high-density polyethylene;
a second surface having a cling force to the first surface at least greater than about 5 g/in, comprising at least a styrenic block copolymer; and a core layer, positioned between the first surface and the second surface, comprising a plurality layers;
wherein at least one layer of the intermediary layer comprises linear low-density polyethylene resin or its blend.
20. The multilayer film of claim 19, wherein the coefficient of friction of the first surface is about 0.5, and wherein the cling force of the second surface to the first surface is about 50 g/ in.
21. The multilayer film of claim 19, wherein the multilayer film comprises the first layer in between about 5% to about 20% by weight, the second layer in between about 3% to about 20% by weight, and the core layer in between about 60% to about 90% by weight.
22. The multilayer film of claim 19, wherein the multilayer film comprises the first layer in about 15% by weight, the second layer in about 7% by weight, and the core layer in about 78% by weight.
23. The multilayer film of claim 19, wherein the first layer comprises between about 75% and about 99% by weight polypropylene and between about 1% to about 25% by weight high-density polyethylene.
24. The multilayer film of claim 23, wherein first layer comprises about 80%
by weight polypropylene and about 20% by weight high-density polyethylene.
by weight polypropylene and about 20% by weight high-density polyethylene.
25. The multilayer film of claim 19, wherein the second layer comprises between about 80% and 100% by weight of a styrenic block copolymer.
26. The multilayer film of claim 19, wherein the core layer comprises between about 50% and 100% by weight linear low-density polyethylene.
27. The multilayer film of claim 26, wherein the core layer further comprises between about 0.1% to about 5% by weight titanium dioxide.
28. A multilayer film comprising:
a slip layer comprising a polypropylene copolymer and high-density polyethylene blend;
a cling layer comprising a styrenic block copolymer and ethylene-octene copolymer blend; and an intermediary layer comprising at least three individual layers, comprising:
at least two layers of linear low-density polyethylene; and a layer of a linear low-density polyethylene and additive blend.
a slip layer comprising a polypropylene copolymer and high-density polyethylene blend;
a cling layer comprising a styrenic block copolymer and ethylene-octene copolymer blend; and an intermediary layer comprising at least three individual layers, comprising:
at least two layers of linear low-density polyethylene; and a layer of a linear low-density polyethylene and additive blend.