MA44136B1 - Procédé de production d'une tôle d'acier revêtue de haute résistance présentant une ductilité et une aptitude au formage améliorées, et tôle d'acier revêtue ainsi obtenue - Google Patents

Procédé de production d'une tôle d'acier revêtue de haute résistance présentant une ductilité et une aptitude au formage améliorées, et tôle d'acier revêtue ainsi obtenue

Info

Publication number
MA44136B1
MA44136B1 MA44136A MA44136A MA44136B1 MA 44136 B1 MA44136 B1 MA 44136B1 MA 44136 A MA44136 A MA 44136A MA 44136 A MA44136 A MA 44136A MA 44136 B1 MA44136 B1 MA 44136B1
Authority
MA
Morocco
Prior art keywords
steel sheet
sheet
temperature
equal
coated steel
Prior art date
Application number
MA44136A
Other languages
English (en)
Inventor
Véronique Hebert
Maya Gospodinova
Original Assignee
Arcelormittal
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Arcelormittal filed Critical Arcelormittal
Publication of MA44136B1 publication Critical patent/MA44136B1/fr

Abstract

Cette invention concerne un procédé de production d'une tôle d'acier revêtue présentant une résistance à la traction ts supérieure ou égale à 100 mpa, un allongement total te selon la norme iso 6892-1 supérieur ou égal à 12 %, le produit ts x te de la résistance à la traction par l'allongement total étant supérieur ou égal à 14200 mpa%, et un rapport d'expansion de trou her selon la norme iso 16630:2009 supérieur ou égal à 25 %. Ledit procédé comprend les étapes successives suivantes : la fourniture d'une tôle d'acier laminée à froid, la composition chimique de l'acier comprenant, en % en poids : 0,15 % = c = 0,23 %, 2,0 % = mn = 2,7 %, c + mn/10 = 0,420 %, 0 = cr = 0,40 %, mn + cr = 2,25 %, 0,2 % = si = 1,6 %, 0,02 % = al = 1,2 %, 1,0 % = si + al = 2,2 %, 0 = nb = 0,035 %, 0 = mo = 0,1 %, le reste étant du fe et les inévitables impuretés, le recuit de la tôle d'acier à une température de recuit ta, de manière à obtenir une structure comprenant au moins 65 % d'austénite et au plus 35 % de ferrite intercritique, la trempe de la tôle à partir d'une température d'au moins 600 °c, à une vitesse de refroidissement comprise entre 20 et 50 °c/s, jusqu'à une température de trempe qt de 200 à 270 °c, le chauffage de la tôle jusqu'à une température de ségrégation pt comprise entre 400 et 480 °c et le maintien de la tôle à cette température de ségrégation pt pendant un temps de ségrégation pt compris entre 50 et 250 s., le revêtement par immersion à chaud de la tôle à une température inférieure à 515 °c, le refroidissement de la tôle revêtue à la température ambiante, la tôle d'acier présentant une microstructure constituée, en fraction de surface : de 3 à 15 % d'austénite résiduelle, au moins 30 % de martensite revenue, au plus 5 % de martensite fraîche, au plus 35 % de bainite, la somme des fractions de surface de la martensite revenue, de la martensite fraîche et de la bainite étant comprise entre 55 et 92 %, et entre 5 et 35 % de ferrite.
MA44136A 2015-12-21 2016-12-21 Procédé de production d'une tôle d'acier revêtue de haute résistance présentant une ductilité et une aptitude au formage améliorées, et tôle d'acier revêtue ainsi obtenue MA44136B1 (fr)

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
PCT/IB2015/059840 WO2017109541A1 (fr) 2015-12-21 2015-12-21 Procédé de production d'une tôle d'acier revêtue de haute résistance présentant une ductilité et une aptitude au formage améliorées, et tôle d'acier revêtue ainsi obtenue
PCT/EP2016/082195 WO2017108959A1 (fr) 2015-12-21 2016-12-21 Procédé de production d'une tôle d'acier revêtue de haute résistance présentant une ductilité et une aptitude au formage améliorées, et tôle d'acier revêtue ainsi obtenue

Publications (1)

Publication Number Publication Date
MA44136B1 true MA44136B1 (fr) 2020-04-30

Family

ID=55273297

Family Applications (2)

Application Number Title Priority Date Filing Date
MA44136A MA44136B1 (fr) 2015-12-21 2016-12-21 Procédé de production d'une tôle d'acier revêtue de haute résistance présentant une ductilité et une aptitude au formage améliorées, et tôle d'acier revêtue ainsi obtenue
MA49586A MA49586B1 (fr) 2015-12-21 2016-12-21 Procédé de production d'une feuille d'acier revêtue à haute résistance présentant une ductilité et une aptitude au formage améliorées et feuille d'acier revêtue ainsi obtenue

Family Applications After (1)

Application Number Title Priority Date Filing Date
MA49586A MA49586B1 (fr) 2015-12-21 2016-12-21 Procédé de production d'une feuille d'acier revêtue à haute résistance présentant une ductilité et une aptitude au formage améliorées et feuille d'acier revêtue ainsi obtenue

Country Status (16)

Country Link
US (2) US11827948B2 (fr)
EP (2) EP3394297B1 (fr)
JP (1) JP6946332B2 (fr)
KR (1) KR102618090B1 (fr)
CN (1) CN108431241B (fr)
BR (1) BR112018012538B1 (fr)
CA (1) CA3008069C (fr)
ES (2) ES2885324T3 (fr)
HU (2) HUE049748T4 (fr)
MA (2) MA44136B1 (fr)
MX (1) MX2018007649A (fr)
PL (2) PL3394297T3 (fr)
RU (1) RU2729671C2 (fr)
UA (1) UA123634C2 (fr)
WO (2) WO2017109541A1 (fr)
ZA (1) ZA201803919B (fr)

Families Citing this family (39)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US11318566B2 (en) 2016-08-04 2022-05-03 Honda Motor Co., Ltd. Multi-material component and methods of making thereof
US11339817B2 (en) 2016-08-04 2022-05-24 Honda Motor Co., Ltd. Multi-material component and methods of making thereof
US10640854B2 (en) 2016-08-04 2020-05-05 Honda Motor Co., Ltd. Multi-material component and methods of making thereof
WO2019122964A1 (fr) 2017-12-19 2019-06-27 Arcelormittal Tôle d'acier présentant une ténacité, une ductilité et une résistance excellentes, et son procédé de fabrication
WO2019122961A1 (fr) * 2017-12-19 2019-06-27 Arcelormittal Tôle d'acier à haute résistance et haute aptitude au formage et son procédé de fabrication
KR102276741B1 (ko) * 2018-09-28 2021-07-13 주식회사 포스코 구멍확장성이 높은 고강도 냉연강판, 고강도 용융아연도금강판 및 이들의 제조방법
WO2020067752A1 (fr) 2018-09-28 2020-04-02 주식회사 포스코 Tôle d'acier laminée à froid à haute résistance ayant un rapport d'expansion de trou élevé, tôle d'acier galvanisée à chaud par trempe à haute résistance, et procédés de fabrication associés
WO2020080407A1 (fr) * 2018-10-18 2020-04-23 Ｊｆｅスチール株式会社 Tôle d'acier et son procédé de fabrication
SE542893C2 (en) * 2018-11-30 2020-08-18 Voestalpine Stahl Gmbh A resistance spot welded joint comprising a zinc coated ahss steel sheet
KR102544854B1 (ko) * 2018-11-30 2023-06-19 아르셀러미탈 구멍 확장비가 높은 냉연 어닐링된 강판 및 그 제조 방법
WO2020158065A1 (fr) * 2019-01-30 2020-08-06 Ｊｆｅスチール株式会社 Tôle d'acier haute résistance et procédé de fabrication de celle-ci
US11555234B2 (en) * 2019-04-24 2023-01-17 Nippon Steel Corporation Steel sheet
BR112021021467A2 (pt) * 2019-05-07 2022-01-04 United States Steel Corp Método para produzir um produto de chapa de aço laminada a quente lingotada continuamente de alta resistência, e, produto de chapa de aço laminada lingotado continuamente de alta resistência
WO2020245627A1 (fr) * 2019-06-03 2020-12-10 Arcelormittal Tôle d'acier laminée à froid et revêtue et son procédé de fabrication
ES2911656T3 (es) 2019-06-17 2022-05-20 Tata Steel Ijmuiden Bv Método de tratamiento térmico de un fleje de acero laminado en frío
PT3754037T (pt) 2019-06-17 2022-04-19 Tata Steel Ijmuiden Bv Método de tratamento térmico de uma tira de aço laminada a frio de alta resistência
WO2021020787A1 (fr) * 2019-07-29 2021-02-04 주식회사 포스코 Tôle d'acier à haute résistance et son procédé de fabrication
EP4006192A4 (fr) * 2019-07-29 2022-09-07 Posco Tôle d'acier à résistance élevée et son procédé de fabrication
KR20220013405A (ko) * 2019-07-30 2022-02-04 제이에프이 스틸 가부시키가이샤 고강도 강판 및 그 제조 방법
EP4010505A1 (fr) * 2019-08-07 2022-06-15 United States Steel Corporation Produits en tôle d'acier zinguée à ductilité élevée
CN110964969B (zh) * 2019-11-27 2021-09-21 本钢板材股份有限公司 一种高强度热镀锌淬火配分钢及其生产方法
WO2021116741A1 (fr) * 2019-12-13 2021-06-17 Arcelormittal Tôle d'acier laminée à froid et traitée thermiquement et procédé de fabrication de celle-ci
US20230002846A1 (en) * 2019-12-19 2023-01-05 Nippon Steel Corporation Steel sheet and manufacturing method thereof
WO2021123889A1 (fr) * 2019-12-19 2021-06-24 Arcelormittal Feuille d'acier laminée à chaud et traitée thermiquement et son procédé de fabrication
CN110978673A (zh) * 2019-12-31 2020-04-10 安徽科蓝特铝业有限公司 一种铝合金高空作业平台型材
CN111057973A (zh) * 2019-12-31 2020-04-24 安徽科蓝特铝业有限公司 一种超耐侯拉丝木纹庭院铝合金型材及其加工工艺
US11511375B2 (en) 2020-02-24 2022-11-29 Honda Motor Co., Ltd. Multi component solid solution high-entropy alloys
WO2021176249A1 (fr) * 2020-03-02 2021-09-10 Arcelormittal Tôle d'acier laminée à froid à haute résistance et recuite après galvanisation et son procédé de fabrication
CN111394661B (zh) * 2020-04-30 2021-07-27 西京学院 一种低合金高强韧性马贝复相钢的制备工艺
CN111996467B (zh) * 2020-09-28 2022-05-20 首钢集团有限公司 一种980MPa级镀锌高强钢及其制备方法
SE545210C2 (en) 2020-12-23 2023-05-23 Voestalpine Stahl Gmbh Coiling temperature influenced cold rolled strip or steel
WO2022136689A1 (fr) * 2020-12-23 2022-06-30 Voestalpine Stahl Gmbh Bande ou tôle d'acier revêtu de zinc ou d'alliage de zinc présentant une adhérence au zinc améliorée
CN114807737B (zh) * 2021-01-21 2023-06-13 宝山钢铁股份有限公司 一种热镀锌钢及其制造方法
US20240141467A1 (en) * 2021-03-25 2024-05-02 Nippon Steel Corporation Steel sheet and welded joint
DE102021108448A1 (de) * 2021-04-01 2022-10-06 Salzgitter Flachstahl Gmbh Stahlband aus einem hochfesten Mehrphasenstahl und Verfahren zur Herstellung eines derartigen Stahlbandes
SE545181C2 (en) * 2021-07-20 2023-05-02 Voestalpine Stahl Gmbh High strength cold rolled steel strip sheet for automotive use having good withstandability to retained austentite decomposition
KR20230073569A (ko) * 2021-11-19 2023-05-26 주식회사 포스코 우수한 강도 및 성형성을 갖는 냉연강판 및 그 제조방법
DE102022102418A1 (de) 2022-02-02 2023-08-03 Salzgitter Flachstahl Gmbh Hochfestes schmelztauchbeschichtetes Stahlband mit durch Gefügeumwandlung bewirkter Plastizität und Verfahren zu dessen Herstellung
WO2024121608A1 (fr) * 2022-12-09 2024-06-13 Arcelormittal Tôle d'acier laminée à froid et revêtue et son procédé de fabrication

Family Cites Families (30)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US2664369A (en) * 1951-08-06 1953-12-29 United States Steel Corp Method of softening low-carbon medium-alloy steel
JP3750789B2 (ja) * 1999-11-19 2006-03-01 株式会社神戸製鋼所 延性に優れる溶融亜鉛めっき鋼板およびその製造方法
FR2850671B1 (fr) 2003-02-05 2006-05-19 Usinor Procede de fabrication d'une bande d'acier dual-phase a structure ferrito-martensitique, laminee a froid et bande obtenue
EP2679699A3 (fr) 2005-03-31 2014-08-20 Kabushiki Kaisha Kobe Seiko Sho Feuille d'acier laminée à froid à haute résistance mécanique et pièces d'automobiles en acier ayant d'excellentes propriétés d'adhésion de film de revêtement, maniabilité et résistivité face à la fragilisation par l'hydrogène
AU2008238998B2 (en) 2007-04-11 2011-02-24 Nippon Steel Corporation Hot-dip metal coated high-strength steel sheet for press working excellent in low-temperature toughness and process for production thereof
JP5402007B2 (ja) * 2008-02-08 2014-01-29 Ｊｆｅスチール株式会社 加工性に優れた高強度溶融亜鉛めっき鋼板およびその製造方法
KR100985375B1 (ko) * 2008-05-20 2010-10-04 주식회사 포스코 고강도 고가공성 냉연강판, 용융아연도금강판 및 그제조방법
JP5418047B2 (ja) * 2008-09-10 2014-02-19 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
JP5412182B2 (ja) * 2009-05-29 2014-02-12 株式会社神戸製鋼所 耐水素脆化特性に優れた高強度鋼板
JP5287770B2 (ja) * 2010-03-09 2013-09-11 Ｊｆｅスチール株式会社 高強度鋼板およびその製造方法
MX2013001456A (es) 2010-08-12 2013-04-29 Jfe Steel Corp Lamina de acero laminada en frio, de alta resistencia, que tiene excelente trabajabilidad y resistencia al impacto, y metodo para manufacturar la misma.
JP5719545B2 (ja) * 2010-08-13 2015-05-20 新日鐵住金株式会社 伸びとプレス成形安定性に優れた高強度薄鋼板
PL2617849T3 (pl) * 2010-09-16 2017-07-31 Nippon Steel & Sumitomo Metal Corporation Walcowana na zimno blacha stalowa o dużej wytrzymałości z doskonałą ciągliwością i podatnością na wywijanie kołnierza, ocynkowana blacha stalowa o dużej wytrzymałości, oraz sposób ich wytwarzania
WO2012120020A1 (fr) * 2011-03-07 2012-09-13 Tata Steel Nederland Technology Bv Procédé pour produire un acier formable à haute résistance et acier formable à haute résistance produit par celui-ci
KR101549317B1 (ko) * 2011-03-28 2015-09-01 신닛테츠스미킨 카부시키카이샤 냉연 강판 및 그 제조 방법
JP5825119B2 (ja) 2011-04-25 2015-12-02 Ｊｆｅスチール株式会社 加工性と材質安定性に優れた高強度鋼板およびその製造方法
UA112771C2 (uk) 2011-05-10 2016-10-25 Арселормітталь Інвестігасьон І Десароло Сл Сталевий лист з високою механічною міцністю, пластичністю і формованістю, спосіб виготовлення та застосування таких листів
JP5856002B2 (ja) * 2011-05-12 2016-02-09 Ｊｆｅスチール株式会社 衝突エネルギー吸収能に優れた自動車用衝突エネルギー吸収部材およびその製造方法
TWI467028B (zh) * 2011-09-30 2015-01-01 Nippon Steel & Sumitomo Metal Corp High-strength hot-dip galvanized steel sheet with excellent impact resistance and its manufacturing method and high-strength alloyed hot-dip galvanized steel sheet and manufacturing method thereof
TWI507538B (zh) 2011-09-30 2015-11-11 Nippon Steel & Sumitomo Metal Corp With excellent burn the attachment strength of the hardenable galvannealed steel sheet, a high strength galvannealed steel sheet and manufacturing method, etc.
TWI468534B (zh) 2012-02-08 2015-01-11 Nippon Steel & Sumitomo Metal Corp 高強度冷軋鋼板及其製造方法
EP2631333A1 (fr) 2012-02-24 2013-08-28 Henkel AG & Co. KGaA Prétraitement de surfaces en zinc avant une passivation
JP5764549B2 (ja) * 2012-03-29 2015-08-19 株式会社神戸製鋼所 成形性および形状凍結性に優れた、高強度冷延鋼板、高強度溶融亜鉛めっき鋼板および高強度合金化溶融亜鉛めっき鋼板、ならびにそれらの製造方法
KR102044693B1 (ko) * 2012-03-30 2019-11-14 뵈스트알파인 스탈 게엠베하 고강도 냉연 강판 및 그러한 강판을 생산하는 방법
EP2881481B1 (fr) * 2012-07-31 2019-04-03 JFE Steel Corporation Tôle d'acier galvanisée par immersion à chaud à résistance élevée qui présente une excellente aptitude au moulage et une excellente aptitude à la fixation de formes, ainsi que procédé de fabrication de cette dernière
JP5821911B2 (ja) * 2013-08-09 2015-11-24 Ｊｆｅスチール株式会社 高降伏比高強度冷延鋼板およびその製造方法
WO2015088523A1 (fr) 2013-12-11 2015-06-18 ArcelorMittal Investigación y Desarrollo, S.L. Tôle en acier laminée à froid et recuite
JP6306481B2 (ja) * 2014-03-17 2018-04-04 株式会社神戸製鋼所 延性及び曲げ性に優れた高強度冷延鋼板および高強度溶融亜鉛めっき鋼板、並びにそれらの製造方法
EP3181715B1 (fr) * 2014-10-24 2019-01-02 JFE Steel Corporation Élément de haute résistance formé à chaud à la presse et son procédé de fabrication
WO2017109542A1 (fr) 2015-12-21 2017-06-29 Arcelormittal Procédé de fabrication d'une tôle d'acier à haute résistance présentant une ductilité et une formabilité améliorées et tôle d'acier obtenue par ce procédé

Also Published As

Publication number Publication date
ZA201803919B (en) 2019-02-27
RU2018122448A (ru) 2019-12-25
BR112018012538B1 (pt) 2021-12-28
JP6946332B2 (ja) 2021-10-06
EP3653738B1 (fr) 2021-07-21
PL3653738T3 (pl) 2022-01-03
KR20180095541A (ko) 2018-08-27
MX2018007649A (es) 2018-09-21
EP3653738A1 (fr) 2020-05-20
EP3394297A1 (fr) 2018-10-31
WO2017109541A1 (fr) 2017-06-29
CA3008069A1 (fr) 2017-06-29
CA3008069C (fr) 2023-09-12
RU2018122448A3 (fr) 2020-03-27
UA123634C2 (uk) 2021-05-05
US20230193412A1 (en) 2023-06-22
KR102618090B1 (ko) 2023-12-26
BR112018012538A2 (pt) 2018-12-11
CN108431241B (zh) 2019-12-27
CN108431241A (zh) 2018-08-21
RU2729671C2 (ru) 2020-08-11
MA49586A (fr) 2021-03-24
MA49586B1 (fr) 2021-10-29
ES2885324T3 (es) 2021-12-13
HUE056202T2 (hu) 2022-01-28
EP3394297B1 (fr) 2020-02-12
US11827948B2 (en) 2023-11-28
HUE049748T4 (hu) 2022-02-28
PL3394297T3 (pl) 2020-07-27
WO2017108959A1 (fr) 2017-06-29
HUE049748T2 (hu) 2020-10-28
ES2780927T3 (es) 2020-08-27
JP2019505693A (ja) 2019-02-28
US20200270713A1 (en) 2020-08-27

Similar Documents

Publication Publication Date Title
MA44136B1 (fr) Procédé de production d'une tôle d'acier revêtue de haute résistance présentant une ductilité et une aptitude au formage améliorées, et tôle d'acier revêtue ainsi obtenue
CA3008064C (fr) Procede de fabrication d'une tole d'acier a haute resistance presentant une ductilite et une formabilite ameliorees et tole d'acier obtenue par ce procede
CA3008062C (fr) Procede pour la production d'une tole d'acier a haute resistance ayant une ductilite et une aptitude au formage ameliorees et tole d'acier ainsi obtenue
MA44113B1 (fr) Procédé de production d'une tôle d'acier à haute résistance présentant une résistance et une aptitude au formage améliorées et tôle d'acier à haute résistance ainsi obtenue
EP3564397B1 (fr) Procédé de fabrication d'une tôle d'acier à ultra-haute résistance revêtue et tôle obtenue
CA2954146C (fr) Procede de production d'une tole d'acier revetue a haute resistance presentant une resistance, une ductilite et une aptitude au formage ameliorees
CA2908491A1 (fr) Acier a haute resistance manifestant une bonne ductilite et son procede d'elaboration par traitement de trempe et de partitionnement en bain de zinc
MA44134B1 (fr) Procédé de production d'une tôle d'acier présentant une résistance, une ductilité et une aptitude au formage améliorées
KR102490989B1 (ko) 초고강도 갈바닐링된 강판을 제조하기 위한 방법 및 획득된 갈바닐링된 강판
MA49613B1 (fr) Procédé pour la production d'une tôle d'acier à haute résistance ayant une ductilité, une aptitude au formage et une soudabilité élevées et tôle d'acier ainsi obtenue
US10907232B2 (en) Method for producing a high strength coated steel sheet having improved strength, formability and obtained sheet
KR20190052683A (ko) 망간 함유 평탄 강으로 이루어지는 평탄 강 제품을 제조하는 방법 및 이러한 평탄 강 제품
JP6967628B2 (ja) 超高強度合金化溶融亜鉛めっき鋼板を製造するための方法、及び得られた合金化溶融亜鉛めっき鋼板