WO2023157195A1 - ダイシングダイボンディングフィルム、及び、半導体装置を製造する方法 - Google Patents

ダイシングダイボンディングフィルム、及び、半導体装置を製造する方法 Download PDF

Info

Publication number
WO2023157195A1
WO2023157195A1 PCT/JP2022/006459 JP2022006459W WO2023157195A1 WO 2023157195 A1 WO2023157195 A1 WO 2023157195A1 JP 2022006459 W JP2022006459 W JP 2022006459W WO 2023157195 A1 WO2023157195 A1 WO 2023157195A1
Authority
WO
WIPO (PCT)
Prior art keywords
die bonding
bonding film
film
dicing
adhesive layer
Prior art date
Application number
PCT/JP2022/006459
Other languages
English (en)
French (fr)
Inventor
強 田澤
尚弘 木村
和弘 山本
有輝啓 岩永
Original Assignee
株式会社レゾナック
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 株式会社レゾナック filed Critical 株式会社レゾナック
Priority to PCT/JP2022/006459 priority Critical patent/WO2023157195A1/ja
Priority to KR1020247027295A priority patent/KR20240151766A/ko
Priority to CN202380020759.3A priority patent/CN118661243A/zh
Priority to PCT/JP2023/005056 priority patent/WO2023157847A1/ja
Priority to JP2023538017A priority patent/JPWO2023157847A1/ja
Priority to TW112105490A priority patent/TW202340410A/zh
Publication of WO2023157195A1 publication Critical patent/WO2023157195A1/ja

Abstract

ダイボンディングフィルムと、ダイボンディングフィルムに貼り合せられた粘着剤層を有するダイシングフィルムとを備えるダイシングダイボンディングフィルムが開示される。接着剤層の厚みが１０μｍ以下である。粘着剤層の厚みが１０μｍ未満である。ダイシングフィルムが基材フィルムを更に有していてもよく、基材フィルム上に粘着剤層が設けられていてもよい。

Description

ダイシングダイボンディングフィルム、及び、半導体装置を製造する方法
　本開示は、ダイシングダイボンディングフィルム、及び、これを用いて半導体装置を製造する方法に関する。
　半導体ウェハをダイシングにより分割する工程の間、半導体ウェハを固定するために利用されるダイシングフィルムと、チップとチップとの間又はチップと基板との間を接着するダイボンディングフィルムとが一体化されたダイシングダイボンディングフィルム（半導体加工用テープ）が、半導体装置の製造のために用いられることがある（例えば、特許文献１、２）。ダイシングダイボンディングフィルムを構成するダイボンディングフィルムは、一般に数十μｍ程度の厚みを有することが多い。
特許第６５３５１１７号公報 特許第６９２８８５２号公報
　半導体パッケージにおけるチップの積層数の増加、及びチップの薄化に伴って、１０μｍ以下の厚みを有する、極めて薄いダイボンディングフィルムの適用が望まれている。ところが、ダイボンディングフィルムが１０μｍ以下の厚みまで薄くなると、ダイシングダイボンディングフィルムを伸張させることを含む方法により半導体ウェハを分割する工程において、ダイボンディングフィルムが分断され難いことがあることが明らかとなった。ダイボンディングフィルムが容易に分断されないと、個片化されたダイボンディングフィルムが付着したチップをピックアップすることが困難となり、半導体製造の歩留まりの低下に繋がり得る。
　本開示の一側面は、１０μｍ以下の厚みを有するダイボンディングフィルムを有するダイシングダイボンディングフィルムに関して、ダイシングダイボンディングフィルムを伸張させることを含む方法により半導体ウェハを分割する工程におけるダイボンディングフィルムの分断性を改善することに関する。
　本開示の一側面は、ダイボンディングフィルムと、前記ダイボンディングフィルムに貼り合せられた粘着剤層を有するダイシングフィルムとを備えるダイシングダイボンディングフィルムに関する。前記ダイボンディングフィルムの厚みが１０μｍ以下であり、前記粘着剤層の厚みが１０μｍ未満である。
　本開示の別の一側面は、前記ダイシングダイボンディングフィルムの前記ダイボンディングフィルムを半導体ウェハに貼り付けることと、前記ダイシングダイボンディングフィルムを伸張させることを含む方法により前記半導体ウェハ及び前記ダイボンディングフィルムを分割し、それにより、チップ及び個片化された前記ダイボンディングフィルムを有するダイボンディングフィルム付きチップを前記粘着剤層上に形成することと、を含む、半導体装置を製造する方法に関する。
　１０μｍ以下の厚みを有するダイボンディングフィルムを有するダイシングダイボンディングフィルムに関して、ダイシングダイボンディングフィルムを伸張させることを含む方法により半導体ウェハを分割する工程におけるダイボンディングフィルムの分断性を改善することができる。
ダイシングダイボンディングフィルムの一例を示す平面図及び断面図である。 半導体装置を製造する方法の一例を示す工程図である。 半導体装置を製造する方法の一例を示す工程図である。
　本発明は以下に説明される例に限定されない。以下の説明において、各構成要素（ステップ等も含む）は、特に明示した場合を除き、必須ではない。各図における構成要素の大きさは概念的なものであり、構成要素間の大きさの相対的な関係は各図に示されたものに限定されない。本開示における数値及びその範囲は、本発明を制限するものではない。本明細書において「～」を用いて示された数値範囲は、「～」の前後に記載される数値をそれぞれ最小値及び最大値として含む範囲を示す。本明細書中に段階的に記載されている数値範囲において、一つの数値範囲で記載された上限値又は下限値は、他の段階的な記載の数値範囲の上限値又は下限値に置き換えてもよい。本明細書中に記載されている数値範囲において、その数値範囲の上限値又は下限値は、実施例に示されている値に置き換えてもよい。
　本明細書において、（メタ）アクリレートは、アクリレート又はそれに対応するメタクリレートを意味する。（メタ）アクリロイル基、（メタ）アクリル共重合体等の他の類似表現についても同様である。本明細書に例示される各成分及び材料は、特に断らない限り、１種を単独で使用してもよく、２種以上を併用して使用してもよい。
　図１の（ａ）は、ダイシングダイボンディングフィルムの一例を示す平面図であり、図１の（ｂ）は図１の（ａ）のＢ－Ｂ線に沿う断面図である。図１に示されるダイシングダイボンディングフィルム１０は、ダイボンディングフィルム１と、ダイボンディングフィルム１に貼り合せられた粘着剤層２を有するダイシングフィルム５とから構成される。ダイシングフィルム５は、基材フィルム３を有しており、基材フィルム３上に粘着剤層２が設けられている。図１には、ダイボンディングフィルム１が貼り付けられた半導体ウェハＷａも示されている。
　ダイボンディングフィルム１は、チップを他のチップ又は基板と接着するための接着剤フィルムであり、ダイアタッチフィルム（ＤＡＦ）と称されることもある。図１に例示されるダイボンディングフィルム１は、半導体ウェハＷａの主面全体を覆う円形の主面を有する。
　ダイボンディングフィルム１は、１０μｍ以下の厚みを有することができる。ダイボンディングフィルム１の厚みが１０μｍ以下であることは、例えば多層のチップを有する薄い半導体パッケージの製造のために有利である。ダイボンディングフィルム１の厚みは、９μｍ以下、８μｍ以下又は７μｍ以下であってもよく、１μｍ以上、２μｍ以上、３μｍ以上、４μｍ以上、又は５μｍ以上であってもよい。
　ダイボンディングフィルム１は、チップの接着のために通常用いられる接着剤から形成されたフィルムであることができる。ダイボンディングフィルム１は熱硬化性接着剤であってもよい。ダイボンディングフィルム１を構成する熱硬化性接着剤は、例えば、高分子量樹脂成分と、熱硬化性成分とを含む。
　ダイボンディングフィルム１に含まれ得る高分子量樹脂成分は、例えば、アクリルゴム、ポリイミド、及びフェノキシ樹脂からなる群から選ばれる少なくとも１種の樹脂を含んでもよい。高分子量樹脂成分がエポキシ基等の反応性基を有していてもよい。高分子量樹脂成分の重量平均分子量（ＧＰＣ法による標準ポリスチレン換算値）が、１０万～３００万であってもよい。高分子量樹脂成分の含有量が、ダイボンディングフィルム１の全体質量１００質量部に対して３０～８０質量部であってもよい。
　ダイボンディングフィルム１に含まれ得る熱硬化性成分は、自己重合及び／又は硬化剤との反応により架橋構造を形成する反応性基を有する化合物である。熱硬化性成分は、例えば、エポキシ樹脂、ビスマレイミド樹脂、トリアジン樹脂、及びフェノール樹脂からなる群から選ばれる少なくとも１種を含んでもよい。熱硬化性成分の含有量が、ダイボンディングフィルム１の量１００質量部に対して１～３０質量部であってもよい。
　ダイボンディングフィルム１を構成する熱硬化性接着剤は、必要により他の成分を含んでもよい。他の成分の例としては、熱硬化性成分と反応する硬化剤、熱硬化性成分と硬化剤との反応を促進する硬化促進剤、カップリング剤（例えばシランカップリング剤）、及びフィラー（例えばシリカ）が挙げられる。
　ダイシングフィルム５は、矩形の主面を有する基材フィルム３と、基材フィルム３上に設けられた粘着剤層２とを有する。粘着剤層２は、基材フィルム３に接する主面２ａ、及びダイボンディングフィルム１と接する主面２ｂとを有する。粘着剤層２の主面２ａ，２ｂは、ダイボンディングフィルム１の主面全体を覆うサイズの円形の面であることができる。
　粘着剤層２は、１０μｍ未満の厚みを有してもよい。粘着剤層２の厚みが１０μｍ未満であると、１０μｍ以下の厚みを有するダイボンディングフィルム１が、ダイシングダイボンディングフィルム１０を伸張させることを含む方法により半導体ウェハＷａを分割する工程において特に容易に分断される。また、ダイボンディングフィルム１の厚みが１０μｍ以下である場合、粘着剤層２の厚みが１０μｍ未満であっても、半導体ウェハＷａの分割によって形成されたチップが飛散することが十分に抑制される。同様の観点から、粘着剤層２の厚みが９μｍ以下、８μｍ以下、７μｍ以下、６μｍ以下、５μｍ以下、４μｍ以下、又は３μｍ以下であってもよい。粘着剤層２の厚みが０．５μｍ以上、１μｍ以上、又は２μｍ以上であってもよい。
　粘着剤層２は、ダイシングフィルムにおいて通常用いられる粘着剤によって形成された層であることができる。粘着剤層２を構成する粘着剤は、感圧型粘着剤又は紫外線硬化型粘着剤であってもよい。紫外線硬化型粘着剤は、紫外線照射によって粘着性が低下する性質を有する粘着剤である。紫外線硬化型粘着剤を用いると、例えばダイボンディングフィルムが付着したチップをピックアップする前に、紫外線照射により粘着剤層２の粘着力を低下させることができる。紫外線硬化型粘着剤は、例えば、（メタ）アクリロイル基を有するアクリル樹脂を含んでいてもよい。アクリル樹脂が水酸基を有していてもよい。アクリル樹脂は、（メタ）アクリロイル酸エステルをモノマー単位として含む重合体である。紫外線硬化型粘着剤は、必要により、光重合開始剤、及び架橋剤（例えばポリイソシアネート化合物）等の他の成分を更に含んでもよい。架橋剤は、アクリル樹脂と反応する反応性基を有する化合物であり、その例としてはポリイソシアネート化合物が挙げられる。
　ダイボンディングフィルム１に対する粘着剤層２のピール強度が高いことは、半導体ウェハＷａの分割によってチップを形成する工程において、チップの飛散の抑制、及びダイボンディングフィルム１の粘着剤層２からの剥離の抑制に寄与する。係る観点から、例えば、ダイボンディングフィルム１に対する粘着剤層２の３０°ピール強度が６．０Ｎ／２５ｍｍ以上であってもよい。３０°ピール強度は、粘着剤層２をダイボンディングフィルム１の主面に対して３０°の方向に向けて引き剥がしたときの応力から求められるピール強度である。３０°ピール強度の測定方法の詳細は、後述の実施例において説明される。粘着剤層２が紫外線硬化型粘着剤によって形成されている場合、紫外線照射前の粘着剤層２が示す３０°ピール強度が６．０Ｎ／２５ｍｍ以上であってもよい。ダイボンディングフィルム１に対する粘着剤層２の３０°ピール強度（紫外線照射前の３０°ピール強度）が、２０Ｎ／２５ｍｍ以下、１７．５Ｎ／２５ｍｍ以下、又は１５Ｎ／２５ｍｍ以下であってもよい。
　ダイシングフィルム５を構成する基材フィルム３は、ダイシングダイボンディングフィルムを伸張させることを含む方法により半導体ウェハを分割する工程において通常用いられるダイシングダイボンディングフィルムを構成する基材フィルムから、選択することができる。基材フィルム３は樹脂フィルムであってもよく、例えば、ポリエステル（ポリエチレンテレフタレート（ＰＥＴ）、ポリブチレンテレフタレート、ポリエチレンナフタレート等）、ポリオレフィン（ポリエチレンフィルム、ポリプロピレン等）、ポリカーボネート、ポリアミド、ポリイミド、ポリアミドイミド、ポリエーテルイミド、ポリエーテルスルフィド、ポリエーテルスルホン、ポリエーテルケトン、ポリフェニレンエーテル、及びポリフェニレンスルフィドから選ばれる樹脂を含む樹脂フィルムであってもよい。基材フィルム３は、単層フィルムであってもよく、二種以上のフィルムから構成される多層フィルムであってもよい。基材フィルム３の厚みは、例えば、１０μｍ以上、１５μｍ以上、又は２０μｍ以上であってもよく、２００μｍ以下、１７５μｍ以下又は１５０μｍ以下であってもよい。
　図１に例示される基材フィルム３は矩形の主面を有するが、基材フィルム３の形状はこれに限定されない。基材フィルム３が長尺のフィルムであってもよい。長尺の１枚の基材フィルム３上に複数の粘着剤層２が配置されていてもよい。
　図２及び図３は、以上例示されたダイシングダイボンディングフィルムを用いて半導体装置を製造する方法の一例を示す工程図である。図２及び図３に示される方法は、ダイシングダイボンディングフィルム１０のダイボンディングフィルム１を半導体ウェハＷａに貼り付けることと、ダイシングダイボンディングフィルム１０を伸張させることを含む方法により、半導体ウェハＷａ及びダイボンディングフィルム１を分割し、それにより、チップＣ及び個片化されたダイボンディングフィルム１ａを有する複数のダイボンディングフィルム付きチップ３０を粘着剤層２上に形成することと、ダイシングフィルム５を加熱により収縮させることと、ダイボンディングフィルム付きチップ３０をピックアップすることとを含む。
　半導体ウェハＷａは、２つの主面Ｆ１及びＦ２を有する。例えば、主面Ｆ１が回路面で、主面Ｆ２が回路面の反対側の裏面であってもよい。半導体ウェハＷａがシリコンウェハであってもよい。ステルスダイシング法により半導体ウェハＷａを分割する場合、ダイボンディングフィルム１が貼り付けられる前に、半導体ウェハＷａにレーザ光を照射して、切断予定ラインに沿う改質層を形成してもよい。その後、半導体ウェハＷａに対してバックグラインディング及びポリッシングの処理をしてもよい。
　図２の（ａ）の例の場合、半導体ウェハＷａの主面Ｆ２にダイボンディングフィルム１が接する向きで、ダイボンディングフィルム１が半導体ウェハＷａに貼り付けられる。更に、粘着剤層２のダイボンディングフィルム１側の主面２ｂに対して、半導体ウェハＷａを囲むようにダイシングリングＤＲが貼り付けられる。
　その後、図２の（ｂ）に示されるように、低温条件下で、ダイシングフィルム５のダイシングリングＤＲの内側の領域をリングＲａで突き上げることによって、ダイシングフィルム５を伸張させる。このときの温度は例えば－１５～０℃であってもよい。ステルスダイシング法の場合、ダイシングフィルム５の伸張により、半導体ウェハＷａ及びダイボンディングフィルム１が半導体ウェハＷａ内の改質層に沿って分断される。この分断により、半導体ウェハＷａが複数のチップＣに分割され、ダイボンディングフィルム１が個々のチップＣに付着する個片化された部分１ａに分割される。すなわち、チップＣ及び個片化されたダイボンディングフィルム１ａを有する、ダイボンディングフィルム付きチップ３０が粘着剤層２上に形成される。
　リングＲａが下げられた後、図３の（ａ）に示されるように、ダイシングフィルム５のうちダイシングリングＤＲとダイボンディングフィルム付きチップ３０との間の領域がヒータＨによって加熱される。加熱された部分のダイシングフィルム５の収縮により、ダイボンディングフィルム付きチップ３０同士の間隔を更に広げることができる。
　必要に応じて紫外線照射によって粘着剤層２の粘着力を低下させた後、図３の（ｂ）に示されるように、突き上げ冶具４２によって突き上げられた個々のダイボンディングフィルム付きチップ３０が、吸引コレット４４によりピックアップされる。ピックアップされたダイボンディングフィルム付きチップ３０は、回路基板又は他のチップに圧着されてもよい。
　本発明は以下の実施例に限定されない。特に記述がない限り、使用された材料は全て試薬として入手されたものである。
実施例１
１．アクリル樹脂の合成
　スリーワンモータ、撹拌翼及び窒素導入管が備え付けられた容量２０００ｍｌのフラスコに以下の成分を入れ、反応液を形成した。
・酢酸エチル（溶剤）：６３５ｇ
・２－エチルヘキシルアクリレート：３９５ｇ
・２－ヒドロキシエチルアクリレート：１００ｇ
・メタクリル酸：５ｇ
・アゾビスイソブチロニトリル：０．２ｇ
　十分に均一になるまで反応液を撹拌した後、流量５００ｍＬ／分の窒素ガスによる６０分間のバブリングにより、系中の溶存酸素を取り除いた。反応液を１時間かけて７８℃まで昇温し、同温度で６時間、重合反応を進行させた。次いで、反応液を、スリーワンモータ、撹拌翼及び窒素導入管が備え付けられた容量２０００ｍＬの加圧釜に移した。加圧窯内で、圧力０．２８ＭＰａの雰囲気下、１２０℃に４．５時間、反応液を加温した。その後、生成した重合体を含む反応液を室温（２５℃、以下同様）まで冷却した。
　反応液に酢酸エチル４９０ｇを加えて反応液を撹拌した。次いで、メトキノン（重合禁止剤）０．０２５ｇ、及びジオクチルスズジラウレート（ウレタン化触媒）０．１０ｇを添加した。更に２－メタクリロイルオキシエチルイソシアネート（昭和電工株式会社製、カレンズＭＯＩ（商品名））８１ｇを反応液に加え、７０℃で６時間、反応液を加熱することにより、重合体と２－メタクリロイルオキシエチルイソシアネートとの反応を進行させた。反応液を室温に冷却した後、酢酸エチルを加え、メタクリロイルオキシ基及び水酸基を有するアクリル樹脂を濃度３５質量％で含むアクリル樹脂溶液を得た。
　得られたアクリル樹脂溶液を６０℃で一晩真空乾燥し、残った固形分を全自動元素分析装置（エレメンタール社製、商品名：ｖａｒｉｏＥＬ）にて元素分析した。元素分析から得られた窒素含有量から、アクリル樹脂１ｇ当たりに導入された２－メタアクリロイルオキシエチル基の量を算出したところ、０．８９ｍｍｏｌ／ｇであった。
　アクリル樹脂のＧＰＣ測定により、アクリル樹脂の重量平均分子量（標準ポリスチレン換算値）を求めた。ＧＰＣ測定のために、東ソー株式会社製のＳＤ－８０２２／ＤＰ－８０２０／ＲＩ－８０２０を使用した。カラムとして昭和電工マテリアルズ株式会社のＧｅｌｐａｃｋ　ＧＬ－Ａ１５０－Ｓ／ＧＬ－Ａ１６０－Ｓを用いた。溶離液としてテトラヒドロフランを用いた。アクリル樹脂の重量平均分子量は３５万であった。
２．ダイシングフィルム
　以下の成分を混合することで、紫外線硬化型の粘着剤層を形成するためのワニス（溶剤以外の成分の濃度：２５質量％）を調製した。アクリル樹脂は「１．アクリル樹脂の合成」において合成されたものである。「固形分」は溶剤以外の成分の量を意味する。
・アクリル樹脂：１００質量部（固形分）
・光重合開始剤（１－ヒドロキシシクロヘキシルフェニルケトン、チバスペシャリティケミカルズ株式会社製、イルガキュア１８４、「イルガキュア」は登録商標）：２．０質量部
・架橋剤（多官能イソシアネート、日本ポリウレタン工業株式会社製、コロネートＬ、固形分７５％）：４．１質量部（固形分）
・酢酸エチル（溶剤）
　離型面を有するポリエチレンテレフタレートフィルム（幅４５０ｍｍ、長さ５００ｍｍ、厚さ３８μｍ）をカバーフィルムとして準備した。カバーフィルムの離型面に、アプリケータを用いてワニスを塗布し、塗膜を８０℃で５分間乾燥した。これにより、カバーフィルムと、その上に形成された粘着剤層（厚さ２μｍ）とからなる積層フィルムを得た。
　コロナ処理が施された面を有するポリオレフィンフィルム（幅４５０ｍｍ、長さ５００ｍｍ、厚さ１００μｍ）を基材フィルムとして準備した。以下、基材フィルムの長手方向をＭＤ方向といい、ＭＤ方向に垂直な方向をＴＤ方向という。この基材フィルムを、コロナ処理が施された面が粘着剤層と接する向きで、上記積層フィルムの粘着剤層に室温にて貼り合わせた。次いで、全体をゴムロールで押圧することで、基材フィルムを粘着剤層に密着させた。基材フィルム、粘着剤層及びカバーフィルムを有するダイシングフィルムを室温で３日間放置した。
３．ダイボンディングフィルム
　以下の成分、及びシクロヘキサノンを含む混合物を、攪拌してからビーズミルを用いて９０分混練した。
・エポキシ樹脂（Ｎ５００Ｐ－１０（商品名）、ＤＩＣ株式会社、クレゾールノボラック型エポキシ樹脂、エポキシ当量２００、分子量９８０、軟化点８５℃）：５５質量部
・フェノール樹脂（ＭＥＨ－７８００Ｍ（商品名）、明和化成株式会社製、水酸基当量１７５）：４５質量部
・シランカップリング剤１（ＮＵＣ　Ａ－１８９（商品名）、日本ユニカー株式会社製、γ－メルカプトプロピルトリメトキシシラン）：１．７質量部
・シランカップリング剤２（ＮＵＣＡ－１１６０（商品名）、日本ユニカー株式会社製、γ－ウレイドプロピルトリエトキシシラン）：０．２質量部
・フィラー（アエロジルＲ９７２（商品名）、日本アエロジル株式会社製、シリカ、平均粒径０．０１６μｍ）：３２質量部
　「アエロジルＲ９７２」は、有機基（例えば、メチル基）を表面に有するシリカ粒子である。
　混練後の混合物に以下の成分を加え、混合物を更に撹拌した。その後、真空脱気することによって、ダイボンディングフィルム形成用のワニスを得た。
・エポキシ基を有するアクリルゴム（ＨＴＲ－８６０Ｐ－３（商品名）、ナガセケムテックス株式会社製、グリシジルアクリレート又はグリシジルメタクリレートの含有量：３質量％、重量平均分子量：８０万）：２８０質量部
・硬化促進剤（キュアゾール２ＰＺ－ＣＮ（商品名）、「キュアゾール」は登録商標、四国化成工業株式会社製、１－シアノエチル－２－フェニルイミダゾール）：０．５質量部
　離型面を有するポリエチレンテレフタレートフィルム（厚さ３５μｍ）をキャリアフィルムとして準備した。キャリアフィルムの離型面に、ダイボンディングフィルム形成用のワニスを塗布し、塗膜を１４０℃で５分間加熱乾燥した。これにより、キャリアフィルムと、その上に形成されたＢステージ状態のダイボンディングフィルム（厚さ７μｍ）とからなる積層フィルムを得た。
４．ダイシングダイボンディングフィルムの作製
　ダイボンディングフィルムを有する積層フィルムを、円形（直径：３１２ｍｍ）にカットした。円形のダイボンディングフィルムに対して、カバーフィルムを剥離したダイシングフィルムを、粘着剤層がダイボンディングフィルムに接する向きで貼り付けた。形成された積層体を室温で１日放置した。その後、ダイシングフィルムのうちダイボンディングフィルムに貼り合せられた部分の外側をカットし、円形のダイボンディングフィルムと、ダイボンディングフィルムを覆い、ダイボンディングフィルムからはみ出した部分を有する円形（直径：３７０ｍｍ）のダイシングフィルムとを有するダイシングダイボンディングフィルムを得た。同様の操作により、後述の種々の評価試験に供するための複数のダイシングダイボンディングフィルムを作製した。
実施例２、３及び比較例１～３
　粘着剤層の厚さを表１に示されるとおりに変更したこと以外は実施例１と同様にして、複数のダイシングダイボンディングフィルムを作製した。
参考例１～３
　ダイボンディングフィルムの厚さを２０μｍに変更し、粘着剤層の厚さを表１に示されるとおりに変更したこと以外は実施例１と同様にして、複数のダイシングダイボンディングフィルムを作製した。
５．評価
（１）ダイボンディングフィルムに対する粘着剤層の粘着力（３０°ピール強度）
　各ダイシングダイボンディングフィルムから、幅２５ｍｍ及び長さ１００ｍｍのサイズを有する測定試料（粘着剤層及び接着剤層からなる積層体）を切り出した。各測定試料に対して、照度１００ｍＷ／ｃｍ２、照射量１５０ｍＪ／ｃｍ２の条件で紫外線（ＵＶ）を照射した。紫外線照射前と紫外線照射後の測定試料について、ダイボンディングフィルムから剥離角度３０°で粘着剤層を引き剥がしたときのピール強度（３０°ピール強度）を測定した。引張速度は６０ｍｍ／分であった。測定試料は、温度２３℃、相対湿度４０％の環境下で保存し、同環境で３０°ピール強度を測定した。
（２）プロセス性評価
（ｉ）ダイシング試験
　シリコンウェハ（直径：１２インチ、厚さ：７７５μｍ）の表面に保護テープを貼り付けた。シリコンウェハの保護テープ側及びその反対側の面に対して以下のステルスダイシング条件でレーザ光を照射することによって、ステルスダイシングのための改質層を、互いに直交する複数の直線から構成される切断予定ラインに沿ってシリコンウェハ内部に形成した。
ステルスダイシング条件：
・ステルスダイシング装置：ＤＦＬ７３６１（株式会社ディスコ製）
・レーザ発振器型式：半導体レーザ励起Ｑスイッチ固体レーザ
・波長：１３４２ｎｍ
・周波数：６０ｋＨｚ
・出力：０．８Ｗ
・パス数：２
・チップサイズ：３ｍｍ×１２ｍｍ
・ダイシング速度：８００ｍｍ／秒
　シリコンウェハの保護テープとは反対側の面を、グラインダポリッシャ装置（ＤＧＰ８７６１、株式会社ディスコ製）を用いて、シリコンウェハの厚さが３０μｍになるまで研磨した。シリコンウェハの研磨された面を、ダイシングダイボンディングフィルムのダイボンディングフィルムに以下の条件で貼り付けた。このとき、シリコンウェハの改質層の方向が、ダイシングダイボンディングフィルムの基材フィルムのＭＤ方向及びＴＤ方向に沿うように貼り付けの向きを調整した。更に、ダイボンディングフィルムからはみ出した部分の粘着剤層をダイシングリングに貼り付けた。その後、シリコンウェハから保護テープを剥離した。
貼付条件：
・貼付装置：ＤＦＭ２８００（株式会社ディスコ製）
・貼付温度：６５℃
・貼付速度：１０ｍｍ／ｓ
・貼付テンションレベル：レベル７
　次いで、ダイセパレータ（ＤＤＳ２３００、株式会社ディスコ製）を使用した以下の条件の冷却エキスパンドにより、ダイシングダイボンディングフィルムを伸張させ、それによりシリコンウェハ及びダイボンディングフィルムを分割した。その後、ダイシングフィルムを以下の条件の加熱により収縮させた。
冷却エキスパンド条件：
・冷却温度：０℃
・冷却時間：１２０秒
・突上げ量：１０ｍｍ
・突上げ速度：１２０ｍｍ／秒
・突上げ後の保持時間：１０秒
加熱条件：
・ヒータ温度：２５０℃
・ヒータ回転速度：１０°／秒
・突上げ量：８ｍｍ
・テープ冷却待ち時間：１０秒
　ダイシングフィルムの収縮の後、粘着剤層に対して以下の条件で紫外線を照射し、それにより粘着剤層の粘着力を低下させた。
紫外線照射条件：
・紫外線の照度：１００ｍＷ／ｃｍ２
・紫外線の照射量：１５０ｍＪ／ｃｍ２
（ｉｉ）プロセス性
保持性
　ダイシング試験の過程で、チップが飛散する現象の有無、及び、シリコンウェハからはみ出した部分の接着剤層と粘着剤層の間の剥離の有無を確認した。以下の基準で保持性を評価した。
Ａ：チップの飛散無し、且つ、接着剤層と粘着剤層の界面の剥離無し
Ｂ：チップの飛散無し、接着剤層と粘着剤層との界面の剥離有り
Ｃ：チップの飛散有り
分断性
　隣り合うチップの間のダイボンディングフィルムを全て観察し、ダイボンディングフィルムが分断されていない箇所の数に基づいて、分断性を以下の基準で評価した。
Ａ：０
Ｂ：１以上１０未満
Ｃ：１０以上
カーフ幅
　隣り合うチップの間に形成された、格子状の間隙の幅（カーフ幅）を顕微鏡観察により測定した。シリコンウェハの外周に相当する部分を４等分する４つの位置それぞれの近傍における２箇所、及び、シリコンウェハの中央部の１箇所において、チップ周囲のＭＤ方向又はＴＤ方向に沿う間隙のカーフ幅を測定した。合計９箇所において測定されたＭＤ方向又はＴＤ方向に沿う間隙のカーフ幅の平均値を求めた。
ピックアップ性
　保持性、分断性及びカーフ幅の評価の後、以下の条件で１００個のダイボンディングフィルム付きチップをピックアップした。
ピックアップ条件：
・ダイボンダ装置：ＤＢ８３０－Ｐ（ファスフォードテクノロジ株式会社製）
・突上げピン：ＥＪＥＣＴＯＲ　ＮＥＥＤＬＥ　ＳＥＮ２－８３－０５（直径：０．７ｍｍ、先端形状：半径３５０μｍの半球、マイクロメカニクス社製）
・突き上げ高さ：２５０μｍ
・突き上げ速度：１ｍｍ／秒
・突上げピン数：８本
　ピックアップの成功率に基づいて、以下の基準でピックアップ性を評価した。Ａ：１００％
Ｂ：８０％以上１００％未満
Ｃ：６０％以上８０％未満
Figure JPOXMLDOC01-appb-T000001
　表１に評価結果が示される。参考例１～３のようにダイボンディングフィルムの厚みが２０μｍである場合、粘着剤層の厚さが薄くなると、ダイシングの過程においてダイボンディングフィルムの剥離が生じ易くなる傾向がある。ところが、実施例１～３及び比較例１～３のようにダイボンディングフィルムの厚さが１０μｍ以下である場合、粘着剤層が薄くなってもダイシングの過程における良好な保持性が維持されることが確認された。更に、実施例１～３のように粘着剤層の厚さが１０μｍ未満であると、ダイボンディングフィルムの分断性が改善されることも確認された。加えて、粘着剤層が薄くなると大きなカーフ幅が確保され易いことも確認された。
　１…ダイボンディングフィルム、１ａ…個片化されたダイボンディングフィルム、２…粘着剤層、３…基材フィルム、５…ダイシングフィルム、１０…ダイシングダイボンディングフィルム、３０…ダイボンディングフィルム付きチップ、Ｃ…チップ、Ｗａ…半導体ウェハ。

Claims (5)

  1. 　ダイボンディングフィルムと、
    　前記ダイボンディングフィルムに貼り合せられた粘着剤層を有するダイシングフィルムと、
    を備え、
    　前記ダイボンディングフィルムの厚みが１０μｍ以下であり、
    　前記粘着剤層の厚みが１０μｍ未満である、
    ダイシングダイボンディングフィルム。
  2. 　前記ダイボンディングフィルムに対する前記粘着剤層の３０°ピール強度が６．０Ｎ／２５ｍｍ以上である、請求項１に記載のダイシングダイボンディングフィルム。
  3. 　前記ダイシングフィルムが基材フィルムを更に有し、前記基材フィルム上に前記粘着剤層が設けられている、請求項１又は２に記載のダイシングダイボンディングフィルム。
  4. 　請求項１～３のいずれか一項に記載のダイシングダイボンディングフィルムの前記ダイボンディングフィルムを半導体ウェハに貼り付けることと、
    　前記ダイシングダイボンディングフィルムを伸張させることを含む方法により前記半導体ウェハ及び前記ダイボンディングフィルムを分割し、それにより、チップ及び個片化された前記ダイボンディングフィルムを有するダイボンディングフィルム付きチップを前記粘着剤層上に形成することと、
    を含む、半導体装置を製造する方法。
  5. 　前記半導体ウェハ及び前記ダイボンディングフィルムを分割する方法がステルスダイシング法である、請求項４に記載の方法。
PCT/JP2022/006459 2022-02-17 2022-02-17 ダイシングダイボンディングフィルム、及び、半導体装置を製造する方法 WO2023157195A1 (ja)