WO2018150950A1 - 光学材料用組成物 - Google Patents

光学材料用組成物 Download PDF

Info

Publication number
WO2018150950A1
WO2018150950A1 PCT/JP2018/004014 JP2018004014W WO2018150950A1 WO 2018150950 A1 WO2018150950 A1 WO 2018150950A1 JP 2018004014 W JP2018004014 W JP 2018004014W WO 2018150950 A1 WO2018150950 A1 WO 2018150950A1
Authority
WO
WIPO (PCT)
Prior art keywords
composition
compound
mass
optical
optical material
Prior art date
Application number
PCT/JP2018/004014
Other languages
English (en)
French (fr)
Inventor
慶彦 西森
陽介 今川
紘平 竹村
堀越　裕
山本　良亮
Original Assignee
三菱瓦斯化学株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 三菱瓦斯化学株式会社 filed Critical 三菱瓦斯化学株式会社
Priority to CN201880007583.7A priority Critical patent/CN110198969B/zh
Priority to EP18754376.4A priority patent/EP3584269B1/en
Priority to JP2018568127A priority patent/JP7014188B2/ja
Priority to US16/483,542 priority patent/US10982094B2/en
Priority to KR1020197023309A priority patent/KR102464231B1/ko
Publication of WO2018150950A1 publication Critical patent/WO2018150950A1/ja

Abstract

広範な物性を持つ光学材料を設計可能となる光学材料用組成物を提供する。本発明の光学材料用組成物は、下記式（１）で表される化合物（Ａ）、１，２，３，５，６－ペンタチエパン（ｂ）、及び必要に応じて下記式（２）で表される化合物（Ｂ）を含有し、化合物（Ｂ）の含有量が、組成物総量に対して、０～３０質量％である。 （式中、ｍは０～４の整数を示し、ｎは０～２の整数を示す。）

Description

光学材料用組成物
　本発明は、プラスチックレンズ、プリズム、光ファイバー、情報記録基盤、フィルター、及び、接着剤等の光学部品、中でも眼鏡用プラスチックレンズ等の光学レンズに用いられる光学材料用組成物に関するものである。
　光学材料、中でも眼鏡レンズに要求されるプラスチック材料の主な性能は、耐熱性、低比重、高透明性および低黄色度、ならびに高屈折率および高アッベ数などの光学性能であり、近年、高屈折率と高アッベ数を達成する為にポリエピスルフィド化合物を含有する光学材料用重合性組成物が提案されている（特許文献１～３）。
　また、眼鏡レンズ等の光学レンズには意匠性、耐久性、及び光学特性の向上を目的として、染色、ハードコート、及び、反射防止コートが施される。それらを施す工程において光学材料は高温にさらされ、熱変形に起因する問題が起こることがある。そのため光学材料の耐熱性の向上が望まれている。光学材料の高屈折率化や色調安定性を向上する目的で光学材料用組成物に種々のコモノマーの添加が行われている。
　しかしながら、コモノマーの添加によって重合後に得られる光学材料の架橋密度が低下して耐熱性が悪化する傾向があり、耐熱性の面からコモノマーの添加量が限られ、光学材料の特性の向上可能な範囲が限定されてしまう課題がある。基準となる耐熱性を向上することでコモノマーの添加許容量を増加させ、広範な物性を持つ光学材料を設計可能となる光学材料用組成物が望まれる。
特開平１０－２９８２８７号公報 特開２００１－００２９３３号公報 特開２０１０－２４２０９３号公報
　耐熱性を向上した、広範な物性を持つ光学材料を設計可能となる光学材料用組成物を提供することが望まれている。
　本発明者らは、下記式（１）で表される化合物を含有する特定の組成物により広範な物性を持つ光学材料を設計可能であることを見出した。すなわち、本発明は以下の通りである。
［１］　下記式（１）で表される化合物（Ａ）、１，２，３，５，６－ペンタチエパン（ｂ）、及び必要に応じて下記式（２）で表される化合物（Ｂ）を含有し、
　化合物（Ｂ）の含有量が、組成物総量に対して、０～３０質量％である、光学材料用組成物。
Figure JPOXMLDOC01-appb-C000002
 （式中、ｍは０～４の整数を示し、ｎは０～２の整数を示す。）
［２］　化合物（Ａ）の含有量が、組成物総量に対して、２０～８０質量％である、［１］に記載の光学材料用組成物。
［３］　さらにポリチオール（ａ）を含有する、［１］または［２］に記載の組成物。
［４］　ポリチオール（ａ）は、１，２，６，７－テトラメルカプト－４－チアへプタン、メタンジチオール、（スルファニルメチルジスルファニル）メタンチオール、ビス（２－メルカプトエチル）スルフィド、２，５－ビス（メルカプトメチル）－１，４－ジチアン、１，２－ビス（２－メルカプトエチルチオ）－３－メルカプトプロパン、４，８－ジメルカプトメチル－１，１１－ジメルカプト－３，６，９－トリチアウンデカン、４，７－ジメルカプトメチル－１，１１－ジメルカプト－３，６，９－トリチアウンデカン、５，７－ジメルカプトメチル－１，１１－ジメルカプト－３，６，９－トリチアウンデカン、１，１，３，３－テトラキス（メルカプトメチルチオ）プロパン、テトラメルカプトペンタエリスリトール、１，３－ビス（メルカプトメチル）ベンゼン、１，４－ビス（メルカプトメチル）ベンゼン、及びチイランメタンチオールから選択される少なくとも１種である、［３］に記載の組成物。
［５］　さらに硫黄を含有する、［１］～［４］のいずれかに記載の組成物。
［６］　化合物（Ａ）と化合物（Ｂ）の質量比が４５：５５～１００：０である、［１］～［５］に記載の組成物。
［７］　化合物（Ａ）と１，２，３，５，６－ペンタチエパン（ｂ）の質量比が２５：７５～９５：５である、［１］～［６］に記載の組成物。
［８］　１，２，３，５，６－ペンタチエパン（ｂ）の含有量が、組成物総量に対して、５～７０質量％である、［１］～［７］のいずれかに記載の組成物。
［９］　組成物総量に対して、
　化合物（Ａ）　　　　　　　　　　　　　　　　２０～８０質量％；
　１，２，３，５，６－ペンタチエパン（ｂ）　　　５～７０質量％；
　化合物（Ｂ）　　　　　　　　　　　　　　　　　０～３０質量％；
　ポリチオール（ａ）　　　　　　　　　　　　　　０～１０質量％；及び
　硫黄　　　　　　　　　　　　　　　　　　　　　０～２５質量％；
を含有する、［１］～［８］のいずれかに記載の組成物。
［９ａ］　組成物総量に対して、
　化合物（Ａ）　　　　　　　　　　　　　　　　２０～８０質量％；
　１，２，３，５，６－ペンタチエパン（ｂ）　　　５～７０質量％；
　化合物（Ｂ）　　　　　　　　　　　　　　　　　０～３０質量％；
　ポリチオール（ａ）　　　　　　　　　　　　　　０～１０質量％；
　硫黄　　　　　　　　　　　　　　　　　　　　　０～２５質量％；
　重合触媒　　　　　　　　　　　　　　　　　　　０～１０質量％；及び
　重合調整剤　　　　　　　　　　　　　　　　　　０～５質量％
を含有する［１］～［９］のいずれかに記載の組成物。
［１０］　前記組成物を硬化させた際の２５℃でのｅ線での屈折率が１．７５以上である、［１］～［９］、［９ａ］のいずれかに記載の組成物。
［１１］［１］～［１０］、［９ａ］のいずれかに記載の組成物を硬化した光学材料。
［１２］［１１］に記載の光学材料を含む光学レンズ。
　本発明の光学材料用組成物は以下の一以上の効果を有する。
　（１）本発明の光学材料用組成物を用いることで耐熱性が向上し、コモノマーの添加許容量を増加させ、広範な物性を持つ光学材料を設計可能となる。
　（２）優れた耐熱性および高屈折率を有する光学材料が得られ得る。
　以下、本発明について実施形態及び例示物等を示して詳細に説明するが、本発明は以下に示す実施形態及び例示物等に限定されるものではなく、本発明の要旨を逸脱しない範囲において任意に変更して実施できる。
　本発明の一形態は、下記式（１）で表される化合物（Ａ）、１，２，３，５，６－ペンタチエパン（ｂ）、及び必要に応じて下記式（２）で表される化合物（Ｂ）を含有し、
　化合物（Ｂ）の含有量が、組成物総量に対して、０～３０質量％である、光学材料用組成物に関する。
Figure JPOXMLDOC01-appb-C000003
 （式中、ｍは０～４の整数を示し、ｎは０～２の整数を示す。）
　以下、各構成要素について詳細に説明する。
［化合物（Ａ）］
　化合物（Ａ）は、下記式（１）で表される４つのチオエポキシ基を有するチオエーテル化合物であり、光学材料の屈折率と耐熱性を高める効果がある。
Figure JPOXMLDOC01-appb-C000004
 　この化合物の入手方法は特に限定されないが、例えば、テトラメルカプトペンタエリスリトールを原料として特開平０９－１１０９７９記載の方法にて合成可能であり好適に用いることができる。
　光学材料用組成物中の化合物（Ａ）の割合は、組成物総量に対して、０．１～９９．５質量％であり、好ましくは３～９０質量％、より好ましくは５～９０質量％、さらに好ましくは１０～９０質量％、一層好ましくは２０～９０質量％であり、特に好ましくは２０～８０質量％であり、最も好ましくは２０～５０質量％である。この範囲にあることで、十分な耐熱性向上効果を得ることができる。
［ポリチオール（ａ）］
　光学材料用組成物は必要に応じてポリチオール（ａ）を含んでもよい。ポリチオール（ａ）は、１分子あたりメルカプト基を２つ以上有するチオール化合物である。ポリチオール（ａ）は本発明の光学材料用組成物から得られる樹脂の加熱時の色調を改善させる効果がある。
　本発明において使用されるポリチオールは特に限定されないが、色調改善効果が高いことから、好ましい具体例として、１，２，６，７－テトラメルカプト－４－チアへプタン、メタンジチオール、（スルファニルメチルジスルファニル）メタンチオール、ビス（２－メルカプトエチル）スルフィド、２，５－ビス（メルカプトメチル）－１，４－ジチアン、１，２－ビス（２－メルカプトエチルチオ）－３－メルカプトプロパン、４，８－ジメルカプトメチル－１，１１－ジメルカプト－３，６，９－トリチアウンデカン、４，７－ジメルカプトメチル－１，１１－ジメルカプト－３，６，９－トリチアウンデカン、５，７－ジメルカプトメチル－１，１１－ジメルカプト－３，６，９－トリチアウンデカン、１，１，３，３－テトラキス（メルカプトメチルチオ）プロパン、テトラメルカプトペンタエリスリトール、１，３－ビス（メルカプトメチル）ベンゼン、１，４－ビス（メルカプトメチル）ベンゼン、及びチイランメタンチオールが挙げられ、特にビス（２－メルカプトエチル）スルフィド、１，２，６，７－テトラメルカプト－４－チアへプタンが好ましく、１，２，６，７－テトラメルカプト－４－チアへプタンが最も好ましい。これらは市販品や公知の方法により合成した物が使用可能であり、また２種以上を併用することができる。これらは市販品や公知の方法により合成した物が使用可能であり、また２種以上を併用することができる。
　光学材料用組成物においてポリチオール（ａ）の割合は、組成物総量に対して、好ましくは０～２５質量％（例えば０．１～２５質量％）、より好ましくは０～２０質量％（例えば０．５～２０質量％）であり、さらに好ましくは０～１０質量％（例えば０．５～１０質量％）であり、特に好ましくは０～５質量％（例えば０．５～５質量％）である。この範囲にあることで、色調安定効果と耐熱性とのバランスがよくなる。
［１，２，３，５，６－ペンタチエパン（ｂ）］
　１，２，３，５，６－ペンタチエパン（ｂ）は、下記式（ｂ）で表される化合物であり、本発明の光学材料用組成物から得られる光学材料（樹脂）の屈折率を向上させる効果がある。
Figure JPOXMLDOC01-appb-C000005
 　１，２，３，５，６－ペンタチエパン（ｂ）の入手方法は特に制限されない。市販品を用いてもよく、原油や動植物等の天然物から採取抽出しても、又公知の方法で合成してもかまわない。
　合成法の一例としては、Ｎ．　Ｔａｋｅｄａ等，Ｂｕｌｌ．Ｃｈｅｍ．Ｓｏｃ．Ｊｐｎ．，６８，２７５７（１９９５）、Ｆ．Ｆｅｈｅｒら，Ａｎｇｅｗ．Ｃｈｅｍ．Ｉｎｔ．Ｅｄ．，７，３０１（１９６８）、Ｇ．Ｗ．Ｋｕｔｎｅｙら，Ｃａｎ．Ｊ．Ｃｈｅｍ，５８，１２３３（１９８０）等に記載の方法が挙げられる。
　光学材料用組成物において１，２，３，５，６－ペンタチエパン（ｂ）を使用する場合の割合は、組成物総量に対して、好ましくは５～７０質量％であり、より好ましくは５～５０質量％である。この範囲にあることで、屈折率向上と光学材料の透明性とを両立できる。
　化合物（Ａ）と１，２，３，５，６－ペンタチエパン（ｂ）との質量比（化合物（Ａ）：１，２，３，５，６－ペンタチエパン（ｂ））は、２５：７５～９５：５であることが好ましい。この範囲にあることで、高い屈折率と優れた色調とを両立し得る。
［化合物（Ｂ）］
　光学材料用組成物は必要に応じて化合物（Ｂ）を含んでもよい。化合物（Ｂ）は、下記式（２）で表される、２つのエピスルフィド基を有するエピスルフィド化合物である。化合物（Ｂ）は化合物（Ａ）と共重合可能であり、化合物（Ａ）とともに用いることで硬化反応性を高める効果がある。
Figure JPOXMLDOC01-appb-C000006
 （式中、ｍは０～４の整数を示し、ｎは０～２の整数を示す。）
　中でもビス（β－エピチオプロピル）スルフィドおよびビス（β－エピチオプロピル）ジスルフィドが好ましく、ビス（β－エピチオプロピル）スルフィドが特に好ましい。ビス（β－エピチオプロピル）スルフィドは上記式（２）においてｍ＝ｎ＝０の化合物に相当し、ビス（β－エピチオプロピル）ジスルフィドは上記式（２）においてｍ＝０かつｎ＝１である化合物に相当する。
　光学材料用組成物中の化合物（Ｂ）の含有量は、組成物総量に対して、０～３０質量％であり、より好ましくは０～２５質量％である。この範囲にあることで、優れた色調を確保しつつ、硬化反応性を向上し得る。
　化合物（Ａ）と化合物（Ｂ）のと質量比（化合物（Ａ）：化合物（Ｂ））は、４５：５５～１００：０であることが好ましく、５０：５０～１００：０であることがより好ましい。この範囲にあることで、高い屈折率と優れた色調とを両立し得る。
［硫黄］
　光学材料用組成物は必要に応じて硫黄を含んでもよい。硫黄は本発明の光学材料用組成物から得られる光学材料（樹脂）の屈折率を向上させる効果がある。
　本発明で用いる硫黄の形状はいかなる形状でもかまわない。具体的には、硫黄としては、微粉硫黄、コロイド硫黄、沈降硫黄、結晶硫黄、昇華硫黄等が挙げられ、溶解速度の観点から好ましくは、粒子の細かい微粉硫黄である。
　本発明に用いる硫黄の粒径（直径）は１０メッシュより小さいことが好ましい。硫黄の粒径が１０メッシュより大きい場合、硫黄が完全に溶解しにくい。硫黄の粒径は、３０メッシュより小さいことがより好ましく、６０メッシュより小さいことが最も好ましい。
　本発明に用いる硫黄の純度は、好ましくは９８％以上であり、より好ましくは９９．０％以上であり、さらに好ましくは９９．５％以上であり、最も好ましくは９９．９％以上である。硫黄の純度が９８％以上であると、９８％未満である場合に比べて、得られる光学材料の色調がより改善する。
　上記条件を満たす硫黄は、市販品を容易に入手可能であり、好適に用いることができる。
　光学材料用組成物において硫黄の割合は、組成物総量に対して、０～４０質量％（例えば１～４０質量％）であり、好ましくは０～３０質量％（例えば５～３０質量％、１０～３０質量％）、より好ましくは０～２５質量％（例えば５～２５質量％）であり、特に好ましくは０～２０質量％（例えば５～２０質量％）である。この範囲にあることで、屈折率向上効果と溶解性のバランスに優れるためである。
　好ましい光学材料用組成物の組成の一例は、以下の通りである。
　組成物総量に対して、
　化合物（Ａ）　　　　　　　　　　　　　　　　２０～８０質量％（より好ましくは２０～５０質量％）；
　１，２，３，５，６－ペンタチエパン（ｂ）　　　５～７０質量％（より好ましくは５～５０質量％）；
　化合物（Ｂ）　　　　　　　　　　　　　　　　　０～３０質量％（より好ましくは０～２５質量％）；
　ポリチオール（ａ）　　　　　　　　　　　　　　０～１０質量％（より好ましくは０～５質量％）；及び
　硫黄　　　　　　　　　　　　　　　　　　　　　０～２５質量％（より好ましくは０～２０質量％）；
を含有する光学材料用組成物。
　好ましい光学材料用組成物の組成の他の一例は、以下の通りである。
　組成物総量に対して、
　化合物（Ａ）　　　　　　　　　　　　　　　　２０～８０質量％（より好ましくは２０～５０質量％）；
　１，２，３，５，６－ペンタチエパン（ｂ）　　　５～７０質量％（より好ましくは５～５０質量％）；
　化合物（Ｂ）　　　　　　　　　　　　　　　　　０～３０質量％（より好ましくは０～２５質量％）；
　ポリチオール（ａ）　　　　　　　　　　　　　　０～１０質量％（より好ましくは０～５質量％）；
　硫黄　　　　　　　　　　　　　　　　　　　　　０～２５質量％（より好ましくは０～２０質量％）；
　重合触媒　　　　　　　　　　　　　　　　　　　０～１０質量％（より好ましくは０．０００１～１０質量％）；及び
　重合調整剤　　　　　　　　　　　　　　　　　　０～５質量％（より好ましくは０．０００１～５．０質量％）
を含有する光学材料用組成物。
　［その他の成分］
　また、本発明の光学材料用組成物は、化合物（Ａ）と共重合可能な他の重合性化合物を含んでも良い。
　他の重合性化合物としては、化合物（Ａ）および化合物（Ｂ）以外のエピスルフィド化合物、ビニル化合物、メタクリル化合物、アクリル化合物、及びアリル化合物が挙げられる。
　他の重合性化合物の添加量は、本発明の効果を阻害しない範囲であれば特に制限されず、例えば、組成物総量に対して、０～３０質量％である。
　また、耐酸化性、耐候性、染色性、強度及び屈折率等の各種性能改良を目的として、各種性能改良剤として、本発明の組成成分（組成成分を予備重合反応させて得られる重合物を含む）の一部もしくは全部と反応可能な化合物を添加して、重合硬化する事も可能である。
　このような組成成分の一部もしくは全部と反応可能な化合物の具体例としては、エポキシ化合物類、イソ（チオ）シアネート類、カルボン酸類、カルボン酸無水物類、フェノール類、アミン類、ビニル化合物類、アリル化合物類、アクリル化合物類、及びメタクリル化合物類が挙げられる。これらの化合物の添加量は、本発明の効果を阻害しない範囲であれば特に制限されず、例えば、組成物総量に対して、０～１０質量％である。
　また、重合硬化のために光学材料用組成物は重合触媒および／または重合調節剤を含んでもよい。
　一形態の光学材料用組成物は重合触媒をさらに含む。
　重合触媒としては、例えば、アミン類、ホスフィン類、第４級アンモニウム塩類、第４級ホスホニウム塩類、第３級スルホニウム塩類、第２級ヨードニウム塩類、鉱酸類、ルイス酸類、有機酸類、ケイ酸類、四フッ化ホウ酸類、過酸化物、アゾ化系合物、アルデヒドとアンモニア系化合物の縮合物、グアニジン類、チオ尿素類、チアゾール類、スルフェンアミド類、チウラム類、ジチオカルバミン酸塩類、キサントゲン酸塩類、酸性リン酸エステル類等を挙げることができる。好ましくは、アミン類、ホスフィン類、第４級アンモニウム塩類、第４級ホスホニウム塩類である。重合触媒は単独でも２種類以上を混合して使用してもかまわない。
　重合触媒の添加量は、特に制限されず、例えば、組成物総量に対して、０．０００１～１０質量％である。
　一形態の光学材料用組成物は重合調整剤をさらに含む。
　重合調整剤は、長期周期律表における第１３～１６族のハロゲン化物を挙げることができる。これらのうち好ましいものは、ケイ素、ゲルマニウム、スズ、アンチモンのハロゲン化物であり、より好ましいものはアルキル基を有するゲルマニウム、スズ、アンチモンの塩化物である。重合調整剤は単独でも２種類以上を混合して使用してもかまわない。
　重合調整剤の添加量は、特に制限されず、例えば、組成物総量に対して、０．０００１～５．０質量％である。
　また、公知の酸化防止剤、ブルーイング剤、紫外線吸収剤、消臭剤、密着性改善剤及び離型性改善剤等の添加剤を添加することもできる。これらの添加剤の量は、本発明の効果を阻害しない範囲であれば特に制限されず、例えば、組成物総量に対して、０～１０質量％である。
［光学材料用組成物］
　本発明の光学材料用組成物は、化合物（Ａ）、１，２，３，５，６－ペンタチエパン（ｂ）、及び、必要に応じて、化合物（Ｂ）、ポリチオール（ａ）、硫黄、及びその他の成分を均一な状態に混合することにより調製される。
［光学材料用組成物の硬化］
　光学材料用組成物はモールド等の型に注型し、重合させることで光学材料とすることができる。光学材料用重合性組成物をモールドに注入する前にあらかじめ脱気処理を行うことは、光学材料の高度な透明性を達成する面から好ましい。
　本発明の光学材料用組成物の注型に際し、０．１～５μｍ程度の孔径のフィルター等で不純物を濾過し除去することは、本発明の光学材料の品質を高める点から好ましい。
　本発明の光学材料用組成物の重合（硬化）は通常以下の条件で行われる。
　硬化時間は通常１～１００時間であり、硬化温度は通常－１０℃～１４０℃である。重合（硬化）は所定の重合温度で所定時間保持する工程、０．１℃～１００℃／ｈの昇温を行う工程、０．１℃～１００℃／ｈの降温を行う工程によって、又はこれらの工程を組み合わせて行う。なお、硬化時間とは昇温過程・降温過程等を含めた重合硬化時間をいい、所定の重合(硬化)温度で保持する工程に加えて、所定の重合(硬化)温度へと昇温・冷却する工程を含む。
　また、硬化終了後、得られた光学材料を５０～１５０℃の温度で１０分～５時間程度アニール処理を行うことは、本発明の光学材料の歪を除くために好ましい。さらに得られた光学材料に対して、必要に応じて染色、ハードコート、耐衝撃性コート、反射防止、防曇性付与等の表面処理を行ってもよい。
　上記のとおり、上記光学材料用組成物を重合硬化することで光学材料を製造することができる。本発明は、上記光学材料用組成物を重合硬化することを含む光学材料の製造方法をも包含するものである。
　さらに、上記光学材料用組成物を硬化して得られる光学材料（成形体；硬化物；硬化樹脂）もまた、本発明に包含される。
　本発明の光学材料用組成物は、化合物（Ａ）および１，２，３，５，６－ペンタチエパン（ｂ）を含有することで優れた耐熱性を達成でき、その他のコモノマーの添加による耐熱性低下の影響を低減できる。したがって、光学材料用組成物に種々のコモノマーを配合し、かつ、その配合量を増加させることが可能であり、これにより広範な物性を持つ光学材料の設計が可能となる。
　特に、本発明の一実施形態の光学材料用組成物は、優れた耐熱性および高屈折率を有する光学材料を与えることができる。
　光学材料用組成物を硬化させた際の光学材料の屈折率は、１．７０以上であることが好ましく、１．７５以上であることがより好ましく、１．７８以上であることが特に好ましい。屈折率は屈折率計により測定することができ、２５℃、ｅ線（波長５４６．１ｎｍ）で測定した値である。
　光学材料の耐熱性としては、光学材料を昇温した際に軟化点が存在しないか、あるいは軟化点が、５０℃以上であることが好ましく、５５℃以上がより好ましい。軟化点はＴＭＡ（熱機械分析）により測定できる。ＴＭＡ曲線の温度微分曲線であるＤＴＭＡのピーク値が小さいほど熱による軟化が起こりにくいため好ましく、ＤＴＭＡのピーク値が、２μｍ／℃以下であることが好ましい。
　本発明の光学材料は、例えば、光学部材、機械部品材料、電気・電子部品材料、自動車部品材料、土木建築材料、成形材料等の他、塗料や接着剤の材料等の各種用途に有用である。中でも、光学材料、例えば、眼鏡レンズ、（デジタル）カメラ用撮像レンズ、光ビーム集光レンズ、光拡散用レンズ等のレンズ、ＬＥＤ用封止材、光学用接着剤、光伝送用接合材料、光ファイバー、プリズム、フィルター、回折格子、ウォッチガラス、表示装置用のカバーガラス等の透明ガラスやカバーガラス等の光学用途；ＬＣＤや有機ＥＬやＰＤＰ等の表示素子用基板、カラーフィルター用基板、タッチパネル用基板、情報記録基板、ディスプレイバックライト、導光板、ディスプレイ保護膜、反射防止フィルム、防曇フィルム等のコーティング剤（コーティング膜）などの表示デバイス用途等が好適である。上記光学材料としては、特に、光学レンズ、プリズム、光ファイバー、情報記録基盤、フィルター等の光学材料、中でも光学レンズが好適である。
　本発明の光学材料用組成物を用いて製造される光学レンズは、安定性、色相、透明性などに優れるため、望遠鏡、双眼鏡、テレビプロジェクター等、従来、高価な高屈折率ガラスレンズが用いられていた分野に用いることができ、極めて有用である。必要に応じて、非球面レンズの形で用いることが好ましい。
　以下、実施例により本発明を具体的に説明するが、本発明の効果を奏する限りにおいて適宜実施形態を変更することができる。
　光学材料の分析・評価は以下の方法で行った。
［光学材料の屈折率］
　光学材料の屈折率はデジタル精密屈折率計（株式会社島津製作所製、ＫＰＲ－２０００）を用い、２５℃におけるｅ線の屈折率を測定した。
［光学材料の耐熱性評価］
　サンプルを厚さ３ｍｍに切り出し、０．５ｍｍφのピンに５０ｇの荷重を与え、１０℃／分で昇温してＴＭＡ測定（セイコーインスツルメンツ製、ＴＭＡ／ＳＳ６１００）を行って、得られたＴＭＡ曲線の温度微分曲線であるＤＴＭＡのピーク温度、及びピーク値により評価を行った。
　このピーク値が小さいほど熱による軟化が起こりにくく耐熱性が高いと評価される。特にピーク値が負、またはピークが無い場合は軟化点無しとした。
［合成例１］
　テトラキス（β－エピチオプロピルチオメチル）メタン（化合物Ａ１）の合成
　テトラメルカプトペンタエリスリトール１０．０ｇ（０．０５０ｍｏｌ）にメタノール５０ｍＬを加え、５℃に冷却した。その溶液に４８％水酸化ナトリウム水溶液０．４２ｇ（０．００４９ｍｏｌ）を加えた後、溶液を１５℃以下に保ちながらエピクロロヒドリン２０．３ｇ（０．２２ｍｏｌ）を滴下した。滴下終了後、更に１時間５℃で撹拌を行った。
　その後、溶液を５℃に冷却しつつ、４８％水酸化ナトリウム水溶液１６．３ｇ（０．２０ｍｏｌ）をメタノール２０ｍＬに溶かした溶液を滴下した。滴下終了後更に２時間撹拌を行い、トルエン１００ｍＬおよび水１００ｍＬを加えた。トルエン層を３回水洗し、溶媒を留去してテトラキス（β－エポキシプロピルチオメチル）メタン２０．１ｇ（０．０４７ｍｏｌ）を得た。
　得られたテトラキス（β－エポキシプロピルチオメチル）メタン２０．１ｇ（０．０４７ｍｏｌ）にトルエン１００ｍＬ、メタノール１００ｍＬ、無水酢酸１．２４ｇ（０．０１２ｍｏｌ）、およびチオ尿素３０．５ｇ（０．４０ｍｏｌ）を加えて、２０℃で２４時間撹拌を行った。その後、トルエン４００ｍＬおよび５％硫酸４００ｍＬを加えてトルエン層を３回水洗し、溶媒を留去することで１６．８ｇのテトラキス（β－エピチオプロピルチオメチル）メタンの粗製物を得た。粗製物を更にシリカゲルカラム精製を行うことで１１．２ｇ（０．０２３ｍｏｌ）のテトラキス（β－エピチオプロピルチオメチル）メタン（以下、化合物Ａ１と称する）を得た。
　以下の実験で用いた化合物Ａ１はこの方法で合成したものである。
［実施例１］
　化合物（Ａ）であるテトラキス（β－エピチオプロピルチオメチル）メタン（化合物Ａ１）６５質量部、１，２，３，５，６－ペンタチエパン（ｂ）（以下、単に「ペンタチエパン（ｂ）」と称する）３５質量部、及び重合触媒としてテトラ－ｎ－ブチルホスホニウムブロマイド０．０２質量部及び重合調整剤としてジ－ｎ－ブチルスズジクロライド０．０５質量部を混合しながら真空脱気を行い、光学材料用組成物を得た。
　得られた光学材料用組成物を３０℃で１０時間加熱し、１００℃まで１０時間かけて昇温させ、最後に１００℃で５時間加熱し、重合硬化させた。放冷後、１２０℃で３０分アニール処理を行った。得られた光学材料の評価を表１にまとめた。
［実施例２～１２、比較例１～４］
　表１に示される組成に従い、実施例１と同様の操作を行うことにより、光学材料を得た。
　得られた光学材料の評価を表１にまとめた。
Figure JPOXMLDOC01-appb-T000007
　なお、表中の数値は、組成物中の化合物の含有量（質量部）を示す。また、表中の数値と併記したａ１～ａ３およびＢ１、Ｂ２の表記は使用した化合物を示す。表中の化合物としては、以下のものを使用した。
Ａ１：テトラキス（β－エピチオプロピルチオメチル）メタン
ａ１：ビス（２－メルカプトエチル）スルフィド
ａ２：１，３－ビス（メルカプトメチル）ベンゼン
ａ３：１，２，６，７－テトラメルカプト－４－チアへプタン
Ｂ１：ビス（β－エピチオプロピル）スルフィド
Ｂ２：ビス（β－エピチオプロピル）ジスルフィド
 
　なお、化合物ａ３は、例えば、特開２００５－２６３７９１号記載の方法で合成可能である。
　上記表１から、式（１）で表される化合物（Ａ）および１，２，３，５，６－ペンタチエパン（ｂ）、ならびに必要に応じてポリチオール（ａ）および硫黄を含む光学材料用組成物を用いた場合（実施例１～４）には、高い屈折率と優れた耐熱性を有する光学材料が得られることが確認される。
　また、所定量化合物（Ｂ）をさらに含む場合（実施例５～１２）にも、高い屈折率と優れた耐熱性を有する光学材料が得られることが確認される。
　特に、化合物（Ａ）、化合物（Ｂ）、１，２，３，５，６－ペンタチエパン（ｂ）、ポリチオール（ａ）および硫黄を所定量配合した実施例８～１２では、１．７９を超える高い屈折率及び優れた耐熱性が達成できたことが確認される。
　一方、化合物（Ａ）を含まない比較例１～３や化合物（Ｂ）の含有量が３０質量％を超える比較例４では、耐熱性に劣ることが確認される。
　本発明の光学材料用組成物を重合硬化した硬化物は、プラスチックレンズ、プリズム、光ファイバー、情報記録基盤、フィルター、及び、接着剤などの光学材料として好適に用いることができる。
 

Claims (12)

  1. 　下記式（１）で表される化合物（Ａ）、１，２，３，５，６－ペンタチエパン（ｂ）、及び必要に応じて下記式（２）で表される化合物（Ｂ）を含有し、
    　化合物（Ｂ）の含有量が、組成物総量に対して、０～３０質量％である、光学材料用組成物。
    Figure JPOXMLDOC01-appb-C000001
     （式中、ｍは０～４の整数を示し、ｎは０～２の整数を示す。）
  2. 　化合物（Ａ）の含有量が、組成物総量に対して、２０～８０質量％である、請求項１に記載の光学材料用組成物。
  3. 　さらにポリチオール（ａ）を含有する、請求項１または２に記載の組成物。
  4. 　ポリチオール（ａ）は、１，２，６，７－テトラメルカプト－４－チアへプタン、メタンジチオール、（スルファニルメチルジスルファニル）メタンチオール、ビス（２－メルカプトエチル）スルフィド、２，５－ビス（メルカプトメチル）－１，４－ジチアン、１，２－ビス（２－メルカプトエチルチオ）－３－メルカプトプロパン、４，８－ジメルカプトメチル－１，１１－ジメルカプト－３，６，９－トリチアウンデカン、４，７－ジメルカプトメチル－１，１１－ジメルカプト－３，６，９－トリチアウンデカン、５，７－ジメルカプトメチル－１，１１－ジメルカプト－３，６，９－トリチアウンデカン、１，１，３，３－テトラキス（メルカプトメチルチオ）プロパン、テトラメルカプトペンタエリスリトール、１，３－ビス（メルカプトメチル）ベンゼン、１，４－ビス（メルカプトメチル）ベンゼン、及びチイランメタンチオールから選択される少なくとも１種である、請求項３に記載の組成物。
  5. 　さらに硫黄を含有する、請求項１～４のいずれか一項に記載の組成物。
  6. 　化合物（Ａ）と化合物（Ｂ）の質量比が４５：５５～１００：０である、請求項１～５のいずれか一項に記載の組成物。
  7. 　化合物（Ａ）と１，２，３，５，６－ペンタチエパン（ｂ）の質量比が２５：７５～９５：５である、請求項１～６のいずれか一項に記載の組成物。
  8. 　１，２，３，５，６－ペンタチエパン（ｂ）の含有量が、組成物総量に対して、５～７０質量％である、請求項１～７のいずれか一項に記載の組成物。
  9. 　組成物総量に対して、
    　化合物（Ａ）　　　　　　　　　　　　　　　２０～８０質量％；
    　１，２，３，５，６－ペンタチエパン（ｂ）　　５～７０質量％；
    　化合物（Ｂ）　　　　　　　　　　　　　　　　０～３０質量％；
    　ポリチオール（ａ）　　　　　　　　　　　　　０～１０質量％；及び
    　硫黄　　　　　　　　　　　　　　　　　　　　０～２５質量％；
    を含有する、請求項１～８のいずれか一項に記載の組成物。
  10. 　前記組成物を硬化させた際の２５℃でのｅ線での屈折率が１．７５以上である、請求項１～９のいずれか一項に記載の組成物。
  11. 　請求項１～１０のいずれか一項に記載の組成物を硬化した光学材料。
  12. 　請求項１１に記載の光学材料を含む光学レンズ。
PCT/JP2018/004014 2017-02-17 2018-02-06 光学材料用組成物 WO2018150950A1 (ja)