WO2017056511A1 - Procédé de production d'une poudre d'acier allié destinée à la métallurgie des poudres - Google Patents

Procédé de production d'une poudre d'acier allié destinée à la métallurgie des poudres Download PDF

Info

Publication number
WO2017056511A1
WO2017056511A1 PCT/JP2016/004440 JP2016004440W WO2017056511A1 WO 2017056511 A1 WO2017056511 A1 WO 2017056511A1 JP 2016004440 W JP2016004440 W JP 2016004440W WO 2017056511 A1 WO2017056511 A1 WO 2017056511A1
Authority
WO
WIPO (PCT)
Prior art keywords
powder
gas
alloy steel
iron
based powder
Prior art date
Application number
PCT/JP2016/004440
Other languages
English (en)
Japanese (ja)
Inventor
小林　聡雄
中村　尚道
伊都也 佐藤
Original Assignee
Ｊｆｅスチール株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Ｊｆｅスチール株式会社 filed Critical Ｊｆｅスチール株式会社
Priority to KR1020187003334A priority Critical patent/KR102022946B1/ko
Priority to JP2017500093A priority patent/JP6112282B1/ja
Publication of WO2017056511A1 publication Critical patent/WO2017056511A1/fr

Abstract

La présente invention concerne un procédé de production d'une poudre d'acier allié destinée à la métallurgie des poudres. Le procédé utilise un four à lit mobile et, sans recourir à une analyse de gaz, qui rend nécessaire une maintenance fastidieuse, permet de traiter thermiquement une poudre à base de fer qui contient des éléments pouvant facilement s'oxyder, tels Cr, Mn et V, et de réduire de façon stable la teneur en C et la teneur en O. Un procédé de production d'une poudre d'acier allié destinée à la métallurgie des poudres d'après la présente invention comprend les étapes consistant à : préparer une poudre atomisée à base de fer ayant une composition spécifique ; introduire la poudre atomisée à base de fer dans un four à lit mobile de manière à former une couche de remplissage ayant une épaisseur de d (mm) ; introduire un gaz contenant de l'hydrogène dans le four à lit mobile d'une manière telle que le gaz contenant de l'hydrogène présente une vitesse moyenne de flux de gaz telle que v (mm/s) ; réduire la poudre atomisée à base de fer en la traitant thermiquement dans le four à lit mobile ; et produire une poudre d'acier allié destinée à la métallurgie des poudres, d et v satisfaisant l'expression d/√v ≤ 2,7 (mm1/2∙s1/2).
PCT/JP2016/004440 2015-09-30 2016-09-30 Procédé de production d'une poudre d'acier allié destinée à la métallurgie des poudres WO2017056511A1 (fr)

Priority Applications (2)

Application Number Priority Date Filing Date Title
KR1020187003334A KR102022946B1 (ko) 2015-09-30 2016-09-30 분말 야금용 합금 강분의 제조 방법
JP2017500093A JP6112282B1 (ja) 2015-09-30 2016-09-30 粉末冶金用合金鋼粉の製造方法

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
JP2015-195148 2015-09-30
JP2015195148 2015-09-30

Publications (1)

Publication Number Publication Date
WO2017056511A1 true WO2017056511A1 (fr) 2017-04-06

Family

ID=58423055

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2016/004440 WO2017056511A1 (fr) 2015-09-30 2016-09-30 Procédé de production d'une poudre d'acier allié destinée à la métallurgie des poudres

Country Status (3)

Country Link
JP (1) JP6112282B1 (fr)
KR (1) KR102022946B1 (fr)
WO (1) WO2017056511A1 (fr)

Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH09170002A (ja) * 1995-10-19 1997-06-30 Kawasaki Steel Corp 鉄粉の仕上げ熱処理方法および仕上げ熱処理装置
JP2006016688A (ja) * 2004-05-31 2006-01-19 Jfe Steel Kk 鉄粉の仕上げ熱処理方法および装置

Family Cites Families (10)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPS5125158A (en) 1974-08-26 1976-03-01 Nippon Kuatsu System Co Ryutaijikukeryono ryuryokei
JPS594298B2 (ja) 1977-01-13 1984-01-28 三菱重工業株式会社 包装用容器整形装置
JPS5810962B2 (ja) 1978-10-30 1983-02-28 川崎製鉄株式会社 圧縮性、成形性および熱処理特性に優れる合金鋼粉
JPS6440881A (en) 1987-08-07 1989-02-13 Canon Kk Hologram having protective layer
JP3224417B2 (ja) 1992-02-14 2001-10-29 川崎製鉄株式会社 高強度、高疲労強度および高靱性を有する焼結体用合金鋼粉および焼結体
JP3272886B2 (ja) * 1994-04-15 2002-04-08 川崎製鉄株式会社 高強度焼結体用合金鋼粉および高強度焼結体の製造方法
SE9602835D0 (sv) 1996-07-22 1996-07-22 Hoeganaes Ab Process for the preparation of an iron-based powder
SE9800153D0 (sv) 1998-01-21 1998-01-21 Hoeganaes Ab Low pressure process
TWI368544B (en) * 2006-02-15 2012-07-21 Jfe Steel Corp Iron-based powder mixture and method of manufacturing iron-based compacted body and iron-based sintered body
US20130136646A1 (en) * 2010-06-04 2013-05-30 Hoganas Ab (Publ) Nitrided sintered steels

Patent Citations (2)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH09170002A (ja) * 1995-10-19 1997-06-30 Kawasaki Steel Corp 鉄粉の仕上げ熱処理方法および仕上げ熱処理装置
JP2006016688A (ja) * 2004-05-31 2006-01-19 Jfe Steel Kk 鉄粉の仕上げ熱処理方法および装置

Also Published As

Publication number Publication date
KR20180022994A (ko) 2018-03-06
JPWO2017056511A1 (ja) 2017-10-05
JP6112282B1 (ja) 2017-04-12
KR102022946B1 (ko) 2019-09-19

Similar Documents

Publication Publication Date Title
CN111440987B (zh) 采用短流程生产的抗拉强度≥980MPa淬火配分钢及方法
CN103757530B (zh) 抗拉强度≥1250MPa的薄带连铸经济性超高强捆带及其制造方法
US9815115B2 (en) Finish heat treatment method and finish heat treatment apparatus for iron powder
JP6112280B1 (ja) 粉末冶金用合金鋼粉の製造方法
JP6112283B1 (ja) 粉末冶金用合金鋼粉の製造方法
JP6112281B1 (ja) 粉末冶金用合金鋼粉の製造方法
JP6112282B1 (ja) 粉末冶金用合金鋼粉の製造方法
JP6112277B1 (ja) 粉末冶金用合金鋼粉の製造方法
JP6112278B1 (ja) 粉末冶金用合金鋼粉の製造方法
CN111893390A (zh) 一种性能均匀的宽板幅铁路车辆罐体用薄钢板的生产方法
JPS61110701A (ja) 鉄鋼粉の仕上熱処理方法及びその装置
CN114130820B (zh) 一种车厢用热轧钢板及其制造方法
CN109338221A (zh) 一种挂车车轴管及其生产方法
CN118668127A (zh) 一种高强韧高纯净冷冲模具钢及其制备方法
CN118600322A (zh) 一种高强耐火带式焙烧机台车车体材料及其台车和制备方法
CN116590610A (zh) 一种正火型屈服强度370MPa级压力容器钢板及其制备方法

Legal Events

Date Code Title Description
ENP Entry into the national phase

Ref document number: 2017500093

Country of ref document: JP

Kind code of ref document: A

121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 16850689

Country of ref document: EP

Kind code of ref document: A1

ENP Entry into the national phase

Ref document number: 20187003334

Country of ref document: KR

Kind code of ref document: A

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 16850689

Country of ref document: EP

Kind code of ref document: A1