WO2015068282A1 - Encre pour l'impression par jet d'encre absorbant le rayonnement infrarouge - Google Patents

Encre pour l'impression par jet d'encre absorbant le rayonnement infrarouge Download PDF

Info

Publication number
WO2015068282A1
WO2015068282A1 PCT/JP2013/080328 JP2013080328W WO2015068282A1 WO 2015068282 A1 WO2015068282 A1 WO 2015068282A1 JP 2013080328 W JP2013080328 W JP 2013080328W WO 2015068282 A1 WO2015068282 A1 WO 2015068282A1
Authority
WO
WIPO (PCT)
Prior art keywords
ink
antimony
tin oxide
doped tin
infrared
Prior art date
Application number
PCT/JP2013/080328
Other languages
English (en)
Japanese (ja)
Inventor
文人 小林
芝岡　良昭
博昭 島根
渉 吉住
正太 川▲崎▼
Original Assignee
共同印刷株式会社
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by 共同印刷株式会社 filed Critical 共同印刷株式会社
Priority to PCT/JP2013/080328 priority Critical patent/WO2015068282A1/fr
Publication of WO2015068282A1 publication Critical patent/WO2015068282A1/fr

Abstract

L'invention porte sur une encre pour l'impression par jet d'encre absorbant le rayonnement infrarouge, comprenant de l'oxyde d'étain dopé par de l'antimoine et un véhicule. L'oxyde d'étain dopé par de l'antimoine comprend de l'oxyde d'étain et de l'oxyde d'antimoine et satisfait aux conditions (a) et/ou (b) : (a) la largeur à mi-hauteur (∆2θ) d'un pic au voisinage de 2θ=27˚ obtenu à partir d'une mesure de diffraction des rayons X est inférieure ou égale à 0,30 ; et/ou (b) la teneur en oxyde d'antimoine est de 0,5 à 10,0 % en poids par rapport au poids de l'oxyde d'étain dopé par de l'antimoine et le degré de cristallisation, c'est-à-dire une valeur obtenue par division, par la largeur à mi-hauteur (∆2θ), de la valeur maximale du pic au voisinage de 2θ=27˚ obtenu à partir de la mesure de diffraction des rayons X, est d'au moins 58 427.
PCT/JP2013/080328 2013-11-08 2013-11-08 Encre pour l'impression par jet d'encre absorbant le rayonnement infrarouge WO2015068282A1 (fr)

Priority Applications (1)

Application Number Priority Date Filing Date Title
PCT/JP2013/080328 WO2015068282A1 (fr) 2013-11-08 2013-11-08 Encre pour l'impression par jet d'encre absorbant le rayonnement infrarouge

Applications Claiming Priority (1)

Application Number Priority Date Filing Date Title
PCT/JP2013/080328 WO2015068282A1 (fr) 2013-11-08 2013-11-08 Encre pour l'impression par jet d'encre absorbant le rayonnement infrarouge

Publications (1)

Publication Number Publication Date
WO2015068282A1 true WO2015068282A1 (fr) 2015-05-14

Family

ID=53041083

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/JP2013/080328 WO2015068282A1 (fr) 2013-11-08 2013-11-08 Encre pour l'impression par jet d'encre absorbant le rayonnement infrarouge

Country Status (1)

Country Link
WO (1) WO2015068282A1 (fr)

Cited By (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2017132048A (ja) * 2016-01-25 2017-08-03 セイコーエプソン株式会社 前処理液、油性インクジェット記録用インクセット及び油性インクジェット記録方法
JP2019077797A (ja) * 2017-10-25 2019-05-23 ゼネラル株式会社 インクジェットインクとそれを用いた半立体画像の形成方法
WO2020066388A1 (fr) * 2018-09-28 2020-04-02 富士フイルム株式会社 Procédé d'impression à jet d'encre
WO2022004524A1 (fr) * 2020-06-29 2022-01-06 共同印刷株式会社 Encre durcissable aux rayons ultraviolets absorbant les rayons infrarouges et produit imprimé absorbant les rayons infrarouges
WO2022136211A1 (fr) * 2020-12-21 2022-06-30 Agfa-Gevaert Nv Encre pour jet d'encre absorbant le proche infrarouge, procédé d'enregistrement
WO2022163499A1 (fr) * 2021-01-29 2022-08-04 共同印刷株式会社 Encre durcissable aux ultraviolets absorbant les infrarouges et matière imprimée absorbant les infrarouges

Citations (12)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH08337500A (ja) * 1995-04-10 1996-12-24 Sumitomo Chem Co Ltd 酸化スズウィスカおよびその製造方法
JPH10316425A (ja) * 1997-05-12 1998-12-02 Tokuyama Corp 球状複合酸化錫粉末の製造方法
JP2003176132A (ja) * 2001-09-28 2003-06-24 Sumitomo Metal Mining Co Ltd 日射遮蔽用アンチモン錫酸化物粒子および日射遮蔽膜形成用塗布液ならびに日射遮蔽膜
JP2005531661A (ja) * 2002-06-28 2005-10-20 メルク　パテント　ゲゼルシャフト　ミット　ベシュレンクテル　ハフトング 表面コーティング系および印刷インクの硬化および乾燥
JP2009057441A (ja) * 2007-08-31 2009-03-19 Kyodo Printing Co Ltd インキ組成物
JP2009114298A (ja) * 2007-11-06 2009-05-28 Brother Ind Ltd 水系インクジェット記録用赤外吸収インク、インクジェット記録方法及びインクジェット記録装置
JP2010006999A (ja) * 2008-06-29 2010-01-14 Kyodo Printing Co Ltd 偽造防止用赤外線吸収インキ
JP2010084079A (ja) * 2008-10-01 2010-04-15 Kyodo Printing Co Ltd 偽造防止用赤外線吸収インキ及び印刷物
WO2013146937A1 (fr) * 2012-03-28 2013-10-03 共同印刷株式会社 Support d'impression filigrané pour prévention des contrefaçons
WO2013147033A1 (fr) * 2012-03-29 2013-10-03 三菱マテリアル株式会社 Matière de coupure du rayonnement infrarouge
WO2013147029A1 (fr) * 2012-03-29 2013-10-03 三菱マテリアル株式会社 Poudre d'oxyde d'étain dopée à l'antimoine et son procédé de fabrication
WO2013168812A1 (fr) * 2012-05-11 2013-11-14 共同印刷株式会社 Oxyde d'étain dopé à l'antimoine, pigment apte à absorber le rayonnement infrarouge, encre apte à absorber le rayonnement infrarouge, matière imprimée et procédé de fabrication d'un oxyde d'étain dopé à l'antimoine

Patent Citations (12)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JPH08337500A (ja) * 1995-04-10 1996-12-24 Sumitomo Chem Co Ltd 酸化スズウィスカおよびその製造方法
JPH10316425A (ja) * 1997-05-12 1998-12-02 Tokuyama Corp 球状複合酸化錫粉末の製造方法
JP2003176132A (ja) * 2001-09-28 2003-06-24 Sumitomo Metal Mining Co Ltd 日射遮蔽用アンチモン錫酸化物粒子および日射遮蔽膜形成用塗布液ならびに日射遮蔽膜
JP2005531661A (ja) * 2002-06-28 2005-10-20 メルク　パテント　ゲゼルシャフト　ミット　ベシュレンクテル　ハフトング 表面コーティング系および印刷インクの硬化および乾燥
JP2009057441A (ja) * 2007-08-31 2009-03-19 Kyodo Printing Co Ltd インキ組成物
JP2009114298A (ja) * 2007-11-06 2009-05-28 Brother Ind Ltd 水系インクジェット記録用赤外吸収インク、インクジェット記録方法及びインクジェット記録装置
JP2010006999A (ja) * 2008-06-29 2010-01-14 Kyodo Printing Co Ltd 偽造防止用赤外線吸収インキ
JP2010084079A (ja) * 2008-10-01 2010-04-15 Kyodo Printing Co Ltd 偽造防止用赤外線吸収インキ及び印刷物
WO2013146937A1 (fr) * 2012-03-28 2013-10-03 共同印刷株式会社 Support d'impression filigrané pour prévention des contrefaçons
WO2013147033A1 (fr) * 2012-03-29 2013-10-03 三菱マテリアル株式会社 Matière de coupure du rayonnement infrarouge
WO2013147029A1 (fr) * 2012-03-29 2013-10-03 三菱マテリアル株式会社 Poudre d'oxyde d'étain dopée à l'antimoine et son procédé de fabrication
WO2013168812A1 (fr) * 2012-05-11 2013-11-14 共同印刷株式会社 Oxyde d'étain dopé à l'antimoine, pigment apte à absorber le rayonnement infrarouge, encre apte à absorber le rayonnement infrarouge, matière imprimée et procédé de fabrication d'un oxyde d'étain dopé à l'antimoine

Cited By (12)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
JP2017132048A (ja) * 2016-01-25 2017-08-03 セイコーエプソン株式会社 前処理液、油性インクジェット記録用インクセット及び油性インクジェット記録方法
JP2019077797A (ja) * 2017-10-25 2019-05-23 ゼネラル株式会社 インクジェットインクとそれを用いた半立体画像の形成方法
WO2020066388A1 (fr) * 2018-09-28 2020-04-02 富士フイルム株式会社 Procédé d'impression à jet d'encre
JPWO2020066388A1 (ja) * 2018-09-28 2021-08-30 富士フイルム株式会社 インクジェット記録方法
JP7065994B2 (ja) 2018-09-28 2022-05-12 富士フイルム株式会社 インクジェット記録方法
US12097714B2 (en) 2018-09-28 2024-09-24 Fujifilm Corporation Ink jet recording method
WO2022004524A1 (fr) * 2020-06-29 2022-01-06 共同印刷株式会社 Encre durcissable aux rayons ultraviolets absorbant les rayons infrarouges et produit imprimé absorbant les rayons infrarouges
JP2022010821A (ja) * 2020-06-29 2022-01-17 共同印刷株式会社 赤外線吸収性紫外線硬化型インク及び赤外線吸収性印刷物
WO2022136211A1 (fr) * 2020-12-21 2022-06-30 Agfa-Gevaert Nv Encre pour jet d'encre absorbant le proche infrarouge, procédé d'enregistrement
CN116635490A (zh) * 2020-12-21 2023-08-22 爱克发-格法特公司 Nir吸收喷墨油墨、记录的方法
WO2022163499A1 (fr) * 2021-01-29 2022-08-04 共同印刷株式会社 Encre durcissable aux ultraviolets absorbant les infrarouges et matière imprimée absorbant les infrarouges
CN116829656A (zh) * 2021-01-29 2023-09-29 共同印刷株式会社 红外线吸收性紫外线固化型墨和红外线吸收性印刷物

Similar Documents

Publication Publication Date Title
WO2015068282A1 (fr) Encre pour l'impression par jet d'encre absorbant le rayonnement infrarouge
US11613638B2 (en) Three-dimensional printing
EP1036831B1 (fr) Composition d'encre photodurcissable pour l'enregistrement par jet d'encre et procédé d'enregistrement par jet d'encre utilisant cette composition
US10174217B2 (en) Ink, ink stored container, image forming method, liquid discharging apparatus, and image
US20100289859A1 (en) Surface-treated pigment, ink composition, and ink-jet recording method
US20130135384A1 (en) Photocurable ink composition for ink jet recording
WO2016018306A1 (fr) Composition d'encre et fluide fixateur de pré-traitement
WO2019199328A1 (fr) Impression tridimensionnelle
JP2014070185A (ja) 画像形成方法
AU2018289672B2 (en) Counterfeit-preventing ink composition, counterfeit-preventing ink, printed article for counterfeit prevention, and method for producing counterfeit-preventing ink composition
WO2015068292A1 (fr) Article imprimé
JP2007231214A (ja) カプセル化樹脂粒子
US11479682B2 (en) Three-dimensional printing
JP5455818B2 (ja) インク組成物、インクセット及び画像形成方法
WO2015068290A1 (fr) Encre pour impression en creux absorbant les infrarouges
WO2019156655A1 (fr) Méthode d'impression en trois dimensions
JP6319642B1 (ja) 水性顔料分散体及び水性顔料分散体の製造方法
WO2015068281A1 (fr) Encre pour sérigraphie à absorption dans l'infrarouge
WO2019156656A1 (fr) Compositions d'impression tridimensionnelle
EP3733793B1 (fr) Procédé de production d'une dispersion aqueuse pigmentaire
TW201518125A (zh) 印刷物
WO2015068291A1 (fr) Article imprimé
JP2021187089A (ja) 画像形成方法、画像形成装置及び画像記録物
TW201518424A (zh) 紅外線吸收性噴墨印刷墨
WO2015068280A1 (fr) Encre d'héliogravure absorbant les infrarouges

Legal Events

Date Code Title Description
121 Ep: the epo has been informed by wipo that ep was designated in this application

Ref document number: 13896917

Country of ref document: EP

Kind code of ref document: A1

NENP Non-entry into the national phase

Ref country code: DE

122 Ep: pct application non-entry in european phase

Ref document number: 13896917

Country of ref document: EP