WO1997026377A1 - Procede de laminage a chaud de feuillards d'acier - Google Patents

Procede de laminage a chaud de feuillards d'acier Download PDF

Info

Publication number
WO1997026377A1
WO1997026377A1 PCT/EP1997/000107 EP9700107W WO9726377A1 WO 1997026377 A1 WO1997026377 A1 WO 1997026377A1 EP 9700107 W EP9700107 W EP 9700107W WO 9726377 A1 WO9726377 A1 WO 9726377A1
Authority
WO
WIPO (PCT)
Prior art keywords
strip
temperature
ferrite
steel
rolled
Prior art date
Application number
PCT/EP1997/000107
Other languages
German (de)
English (en)
Inventor
Manfred Espenhahn
Rudolf Kawalla
Hans Pircher
Waldemar Wolpert
Original Assignee
Thyssen Stahl Ag
Priority date (The priority date is an assumption and is not a legal conclusion. Google has not performed a legal analysis and makes no representation as to the accuracy of the date listed.)
Filing date
Publication date
Application filed by Thyssen Stahl Ag filed Critical Thyssen Stahl Ag
Priority to AU14408/97A priority Critical patent/AU1440897A/en
Priority to JP9525663A priority patent/JP2000503345A/ja
Priority to EP97901001A priority patent/EP0873428A1/fr
Publication of WO1997026377A1 publication Critical patent/WO1997026377A1/fr

Abstract

L'invention concerne un procédé de laminage à chaud de feuillards constitués d'un acier non allié ou faiblement allié, en particulier un acier à teneur en carbone très basse, à teneur en carbone ultra basse et exempt d'interstitiels, dans un groupe finisseur à plusieurs plages. Ledit procédé commence à une température comprise dans la plage austénitique de l'acier et se termine à une température comprise dans la plage ferritique de l'acier. La transformation structurale de l'acier est terminée par refroidissement du feuillard entre des cages du groupe finisseur. L'invention se caractérise en ce que le feuillard est laminé dans sa phase austénitique de façon à prendre une épaisseur intermédiaire comprise entre 2 et 12 millimètres, puis est refroidi pour prendre l'état ferritique en une seule étape de refroidissement, et ensuite laminé à sa dimension définitive en phase ferritique.
PCT/EP1997/000107 1996-01-14 1997-01-11 Procede de laminage a chaud de feuillards d'acier WO1997026377A1 (fr)

Priority Applications (3)

Application Number Priority Date Filing Date Title
AU14408/97A AU1440897A (en) 1996-01-14 1997-01-11 Process for the hot rolling of steel bands
JP9525663A JP2000503345A (ja) 1996-01-14 1997-01-11 鋼帯の熱間圧延方法
EP97901001A EP0873428A1 (fr) 1996-01-14 1997-01-11 Procede de laminage a chaud de feuillards d'acier

Applications Claiming Priority (2)

Application Number Priority Date Filing Date Title
DE19600990A DE19600990C2 (de) 1996-01-14 1996-01-14 Verfahren zum Warmwalzen von Stahlbändern
DE19600990.1 1996-01-14

Publications (1)

Publication Number Publication Date
WO1997026377A1 true WO1997026377A1 (fr) 1997-07-24

Family

ID=7782645

Family Applications (1)

Application Number Title Priority Date Filing Date
PCT/EP1997/000107 WO1997026377A1 (fr) 1996-01-14 1997-01-11 Procede de laminage a chaud de feuillards d'acier

Country Status (8)

Country Link
EP (1) EP0873428A1 (fr)
JP (1) JP2000503345A (fr)
KR (1) KR19990077215A (fr)
AU (1) AU1440897A (fr)
CA (1) CA2242728A1 (fr)
DE (1) DE19600990C2 (fr)
MX (1) MX9805594A (fr)
WO (1) WO1997026377A1 (fr)

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US6503339B1 (en) 1998-02-20 2003-01-07 Thyssen Krupp Stahl Ag Method for producing non-grain oriented magnetic sheet steel

Families Citing this family (14)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
NL1003293C2 (nl) * 1996-06-07 1997-12-10 Hoogovens Staal Bv Werkwijze en inrichting voor het vervaardigen van een stalen band.
NL1007739C2 (nl) * 1997-12-08 1999-06-09 Hoogovens Staal Bv Werkwijze en inrichting voor het vervaardigen van een stalen band met hoge sterkte.
DE19632448A1 (de) * 1996-08-05 1998-02-12 Mannesmann Ag Verfahren und Anlage zur Herstellung von Band aus niedriggekohlten und ultraniedriggekohlten Stählen
TR199901967T2 (xx) * 1996-12-19 2000-07-21 Hoogovens Staal Bv. Bir �elik �erit veya sac haz�rlamak i�in i�lem ve tertibat.
DE19712616C2 (de) * 1997-03-26 1999-07-15 Thyssen Stahl Ag Warmwalzen von Stahlband
NL1007731C2 (nl) * 1997-12-08 1999-06-09 Hoogovens Staal Bv Werkwijze en inrichting voor het vervaardigen van een ferritisch gewalste stalen band.
DE19758108C1 (de) * 1997-12-17 1999-01-14 Mannesmann Ag Produktionsverfahren und -anlage zur endlosen Erzeugung von warmgewalzten dünnen Flachprodukten
WO1999050463A1 (fr) * 1998-03-27 1999-10-07 Corus Staal Bv Procede de production d'un acier de formage ayant de bonnes caracteristiques de formage et acier de formage a basse teneur en carbone
IT1303873B1 (it) * 1998-11-26 2001-03-01 Demag Italimpianti Spa Laminatoio a caldo per nastri sottili
DE19858073C2 (de) * 1998-12-16 2003-04-24 Max Planck Inst Eisenforschung Verfahren zur Erzeugung von dünnen Warmbändern aus Stahl mit verbesserter Tiefziehfähigkeit
BE1012462A3 (fr) * 1999-02-05 2000-11-07 Centre Rech Metallurgique Procede de fabrication d'une bande d'acier laminee a chaud pour emboutissage.
ITRM20060262A1 (it) * 2006-05-17 2007-11-18 Ct Sviluppo Materiali Spa Procedimento per la produzione di nastri di acciaio al carbonio a grano fine e nastri cosi ottenibili
AT509707B1 (de) 2010-05-04 2011-11-15 Siemens Vai Metals Tech Gmbh Verfahren zum warmwalzen von stahlbändern und warmwalzstrasse
EP4364867A1 (fr) 2022-11-04 2024-05-08 Primetals Technologies Austria GmbH Laminage d'acier avec détection technique de mesure de la conversion de phase

Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
BE807881R (fr) * 1973-11-27 1974-05-27 Centre Rech Metallurgique Procede pour la fabrication de toles pour emboutissage
LU78401A1 (fr) * 1977-10-27 1979-06-01 Centre Rech Metallurgique Procede de fabrication d'un acier formable a froid
BE901292A (fr) * 1984-12-17 1985-06-17 Centre Rech Metallurgique Procede de laminage controle d'un produit epais.
EP0306076A1 (fr) * 1987-09-01 1989-03-08 Hoogovens Groep B.V. Fabrication de bandes d'acier formables
EP0524162A2 (fr) * 1991-07-17 1993-01-20 CENTRE DE RECHERCHES METALLURGIQUES CENTRUM VOOR RESEARCH IN DE METALLURGIE Association sans but lucratif Procédé de fabrication d'une bande mince en acier doux
WO1993021351A1 (fr) * 1991-02-08 1993-10-28 Mcgill University Aciers depourvus d'elements interstitiels

Family Cites Families (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
NL9100911A (nl) * 1991-03-22 1992-10-16 Hoogovens Groep Bv Inrichting en werkwijze voor het vervaardigen van warmgewalst staal.

Patent Citations (6)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
BE807881R (fr) * 1973-11-27 1974-05-27 Centre Rech Metallurgique Procede pour la fabrication de toles pour emboutissage
LU78401A1 (fr) * 1977-10-27 1979-06-01 Centre Rech Metallurgique Procede de fabrication d'un acier formable a froid
BE901292A (fr) * 1984-12-17 1985-06-17 Centre Rech Metallurgique Procede de laminage controle d'un produit epais.
EP0306076A1 (fr) * 1987-09-01 1989-03-08 Hoogovens Groep B.V. Fabrication de bandes d'acier formables
WO1993021351A1 (fr) * 1991-02-08 1993-10-28 Mcgill University Aciers depourvus d'elements interstitiels
EP0524162A2 (fr) * 1991-07-17 1993-01-20 CENTRE DE RECHERCHES METALLURGIQUES CENTRUM VOOR RESEARCH IN DE METALLURGIE Association sans but lucratif Procédé de fabrication d'une bande mince en acier doux

Non-Patent Citations (1)

* Cited by examiner, † Cited by third party
Title
MESSIEN P: "LAMINAGE FERRITIQUE DE BANDES A CHAUD MINCES EN ACIER DOUX *", CAHIERS D'INFORMATIONS TECHNIQUES DE LA REVUE DE METALLURGIE, vol. 88, no. 5, 1 May 1991 (1991-05-01), pages 433 - 442, XP000249515 *

Cited By (1)

* Cited by examiner, † Cited by third party
Publication number Priority date Publication date Assignee Title
US6503339B1 (en) 1998-02-20 2003-01-07 Thyssen Krupp Stahl Ag Method for producing non-grain oriented magnetic sheet steel

Also Published As

Publication number Publication date
CA2242728A1 (fr) 1997-07-24
DE19600990C2 (de) 1997-12-18
EP0873428A1 (fr) 1998-10-28
KR19990077215A (ko) 1999-10-25
DE19600990A1 (de) 1997-07-17
MX9805594A (es) 1998-10-31
JP2000503345A (ja) 2000-03-21
AU1440897A (en) 1997-08-11

Similar Documents

Publication Publication Date Title
EP1469954B2 (fr) Procede de production de feuillard lamine a chaud a partir d'aciers austenitiques inoxydables
EP0771596B1 (fr) Installation pour laminer à chaud des bandes en continu ou en discontinu
DE69202088T2 (de) Vorrichtung und Verfahren zur Herstellung von warmgewalztem Stahl.
EP0804300B1 (fr) Procede et dispositif de production d'une feuille d'acier presentant les proprietes d'un produit lamine a froid
EP0761326B1 (fr) Installation pour la production d'une bande mince laminée à chaud
EP1305122A1 (fr) Procede et installation de fabrication de produits plats minces
DE19600990C2 (de) Verfahren zum Warmwalzen von Stahlbändern
WO2007048497A1 (fr) Procede de fabrication d’une tole chaude presentant une structure multiphase
EP0666122A1 (fr) Procédé et installation pour la fabrication de bandes d'acier laminées à chaud à partir d'ébauches coulées en continu
DE10060948C2 (de) Verfahren zum Erzeugen eines Warmbandes aus einem einen hohen Mangan-Gehalt aufweisenden Stahl
WO2000065103A2 (fr) Procede de production d'une tole magnetique a grains non orientes
EP4003623A1 (fr) Fabrication d'une bande d'acier pouvant être emboutie dans une installation combinée de coulée et de laminage
DE4041206C2 (de) Verfahren und Anlage zur Herstellung von warmgewalztem Stahlband, insbesondere für Edelstähle aus stranggegossenem Vormaterial
EP1192287B1 (fr) Procede de production de tole electrique a grains non orientes
DE19520832A1 (de) Verfahren und Vorrichtung zur Herstellung von Stahlband mit Kaltwalzeigenschaften
EP1440173B1 (fr) Feuillard d'acier lamine a chaud prevu pour produire du feuillard magnetique a grains non orientes et procede approprie pour le produire
EP1633894B1 (fr) Procede et installation pour produire un feuillard lamine a chaud a structure biphasee
DE3116419C2 (de) Verfahren zur Herstellung eines kornorientierten, elektromagnetischen Siliciumstahlbandes
DE4009860C2 (de) Verfahren und Anlage zur Herstellung von warmgewalztem Stahlband, insbesondere für Edelstähle, aus bandförmig stranggegossenem Vormaterial
DE3518925A1 (de) Verfahren zum kontrollierten stab- und drahtwalzen legierter staehle
EP3206808B1 (fr) Installation et procédé de fabrication de tôles fortes
DE19512953A1 (de) Verfahren und Vorrichtung zur Herstellung von warmgewalztem Stahlband
EP1038978B1 (fr) Procédé pour produire une bande laminée à chaud
EP0823294A1 (fr) Procédé de fabrication d'une bande en acier basse et ultra basse de teneur en carbon
EP0970256B1 (fr) Laminage a chaud de feuillard d'acier

Legal Events

Date Code Title Description
AK Designated states

Kind code of ref document: A1

Designated state(s): AU CA JP KR MX US

AL Designated countries for regional patents

Kind code of ref document: A1

Designated state(s): AT BE CH DE DK ES FI FR GB GR IE IT LU MC NL PT SE

DFPE Request for preliminary examination filed prior to expiration of 19th month from priority date (pct application filed before 20040101)
121 Ep: the epo has been informed by wipo that ep was designated in this application
WWE Wipo information: entry into national phase

Ref document number: 1997901001

Country of ref document: EP

ENP Entry into the national phase

Ref document number: 2242728

Country of ref document: CA

Ref country code: CA

Ref document number: 2242728

Kind code of ref document: A

Format of ref document f/p: F

WWE Wipo information: entry into national phase

Ref document number: PA/a/1998/005594

Country of ref document: MX

WWE Wipo information: entry into national phase

Ref document number: 1019980705357

Country of ref document: KR

WWP Wipo information: published in national office

Ref document number: 1997901001

Country of ref document: EP

WWP Wipo information: published in national office

Ref document number: 1019980705357

Country of ref document: KR

WWR Wipo information: refused in national office

Ref document number: 1997901001

Country of ref document: EP

WWW Wipo information: withdrawn in national office

Ref document number: 1997901001

Country of ref document: EP

WWW Wipo information: withdrawn in national office

Ref document number: 1019980705357

Country of ref document: KR